Formation and structure of a (√19 × √19)R23.4°-Ge/Pt(1 1 1) surface alloy

An ordered (√19 × √19)R23.4°-Ge/Pt(1 1 1) surface alloy can be formed by vapor depositing one-monolayer Ge on a Pt(1 1 1) substrate at room temperature and subsequently annealing at 900-1200 K. The long-range order of this structure was observed by low energy electron diffraction (LEED) and confirmed by scanning tunneling microscopy (STM). The local structure and alloying of vapor-deposited Ge on Pt(1 1 1) at 300 K was investigated by using X-ray Photoelectron Diffraction (XPD) and low energy alkali ion scattering spectroscopy (ALISS). XPS indicates that Ge adatoms are incorporated to form an alloy surface layer at ∼900 K. Results from XPD and ALISS establish that Ge atoms are substitutionally incorporated into the Pt surface layer and reside exclusively in the topmost layer, with excess Ge diffusing deep into the bulk of the crystal. The incorporated Ge atoms at the surface are located very close to substitutional Pt atomic positions, without any corrugation or “buckling”. Temperature Programmed Desorption (TPD) shows that both CO and NO adsorb more weakly on the Ge/Pt(1 1 1) surface alloy compared to that on the clean Pt(1 1 1) surface.     

First-principles study of adsorption and diffusion on Ge/Si(0 0 1)-(2 × 8) and Ge/Si(1 0 5)-(1 × 2) surfaces

Using first-principles total-energy calculations, we have investigated the adsorption and diffusion of Si and Ge adatoms on Ge/Si(0 0 1)-(2 × 8) and Ge/Si(1 0 5)-(1 × 2) surfaces. The dimer vacancy lines on Ge/Si(0 0 1)-(2 × 8) and the alternate S_A and rebonded S_B steps on Ge/Si(1 0 5)-(1 × 2) are found to strongly influence the adatom kinetics. On Ge/Si(0 0 1)-(2 × 8) surface, the fast diffusion path is found to be along the dimer vacancy line (DVL), reversing the diffusion anisotropy on Si(0 0 1). Also, there exists a repulsion between the adatom and the DVL, which is expected to increase the adatom density and hence island nucleation rate in between the DVLs. On Ge/Si(1 0 5)-(1 × 2) surface, the overall diffusion barrier of Si(Ge) along direction is relative fast with a barrier of ∼0.83(0.61) eV, despite of the large surface undulation. This indicates that the adatoms can rapidly diffuse up and down the (1 0 5)-faceted Ge hut island. The diffusion is also almost isotropic along [0 1 0] and directions.     

Germanium growth on Br-terminated Si(1 0 0)

The consequences of Ge deposition on Br-terminated Si(1 0 0) were studied with scanning tunneling microscopy at ambient temperature after annealing at 650 K. One monolayer of Br was sufficient to prevent the formation of Ge huts beyond the critical thickness of 3 ML. This is possible because Br acts as a surfactant whose presence lowered the diffusivity of Ge adatoms. Hindered mobility was manifest at low coverage through the formation of short Ge chains. Further deposition resulted in the extension and connection of the Ge chains and gave rise to the buildup of incomplete layers. The deposition of 7 ML of Ge resulted in a rough surface characterized by irregularly shaped clusters. A short 800 K anneal desorbed the Br and allowed Ge atoms to reorganize into the more energetically favorable “hut” structures produced by conventional Ge overlayer growth on Si(1 0 0).     

Structural analysis of the c(4 × 2) reconstruction in Si(0 0 1) and Ge(0 0 1) surfaces by low-energy electron diffraction

The c(4 × 2) structures in (0 0 1) surfaces of Si and Ge have been studied by low-energy electron diffraction (LEED). Using a proper cleaning method for the Si surface, we were able to observe clear c(4 × 2) LEED patterns up to incident energy of ∼400 eV as well as the Ge surface. Extensive experimental intensity-voltage curves allowed us to optimize the asymmetric dimer model up to the eighth layer (including the dimer layer) in depth in the dynamical LEED calculation. Optimized structural parameters are almost the same for the Si and Ge except for the height of the buckled-up atom of the asymmetric dimer. For the Ge surface, the structural parameters are in excellent agreement with those obtained by a previous theoretical calculation. The tilt angle and bond length of the dimer are 18 ± 1 (19 ± 1)° and 2.4 ± 0.1 (2.5 ± 0.1) Å for the Si(0 0 1) (Ge(0 0 1)), respectively.     

Hydrogen-induced metallization on Ge(1 1 1) c(2 × 8)

We have studied hydrogen adsorption on the Ge(1 1 1) c(2 × 8) surface using scanning tunneling microscopy (STM) and angle-resolved photoelectron spectroscopy (ARPES). We find that atomic hydrogen preferentially adsorbs on rest atom sites. The neighbouring adatoms appear higher in STM images, which clearly indicates a charge transfer from the rest atom states to the adatom states. The surface states near the Fermi-level have been followed by ARPES as function of H exposure. Initially, there is strong emission from the rest atom states but no emission at the Fermi-level which confirms the semiconducting character of the c(2 × 8) surface. With increasing H exposure a structure develops in the close vicinity of the Fermi-level. The energy position clearly indicates a metallic character of the H-adsorbed surface. Since the only change in the STM images is the increased brightness of the adatoms neighbouring a H-terminated rest atom, we identify the emission at the Fermi-level with these adatom states.     

Hydrogen adsorption on GaAs(0 0 1)-c(4 × 4)

Exposure of the As-terminated GaAs(0 0 1)-c(4 × 4) reconstructed surface to atomic hydrogen (H) at different substrate temperatures (50-480 °C) has been studied by reflection high-energy electron diffraction (RHEED) and scanning tunnelling microscopy (STM). Hydrogen exposure at low temperatures (∼50 °C) produces a disordered (1 × 1) surface covered with AsH_x clusters. At higher temperatures (150-400 °C) exposure to hydrogen leads to the formation of mixed c(2 × 2) and c(4 × 2) surface domains with H adsorbed on surface Ga atoms that are exposed due to the H induced loss of As from the surface. At the highest temperature (480 °C) a disordered (2 × 4) reconstruction is formed due to thermal desorption of As from the surface. The results are consistent with the loss of As from the surface, either through direct thermal desorption or as a result of the desorption of volatile compounds which form after reaction with H.     

Relaxations in the 1 × 5 reconstruction of Pt(1 1 0)

Pt(1 1 0) is one of the most closely investigated metal surface structures because it displays a variety of “missing-row” reconstructions, which are only marginally stable. The ground state is usually found to have 1 × 2 translational symmetry, but a 1 × 3 form has also been seen. Between 1 × 2 and 1 × 3, a series of disordered structures has been recorded, which shows a slight preference for 1 × 5 periodicity. Under the preparation conditions used in this study, a stable 1 × 5 structure was found for Pt(1 1 0). Investigation by surface X-ray diffraction has led to a complete three-dimensional structure, which closely resembles an alternation of 1 × 2 and 1 × 3 unit cells. Pt(1 1 0) shows an interesting example of two “homometric” structures that are indistinguishable by diffraction, but are distinguishable by virtue of their subsurface relaxation pattern.     

Simulations of iodine adsorbed Ge(0 0 1) surface and its STM images

A layer of iodine at Ge(0 0 1) surface develops an ordered structure of iodine atoms bound to Ge dimers. Here are discussed atomic structures of Ge(0 0 1) surface covered by 0.25 monolayer of iodine. The p(2×4), p(2×2), c(2×4) and p(1×4) surface structures are found in calculations. The structure with two iodine atoms of the dissociated I₂ molecule adsorbed at both ends of the same germanium dimer is found to be energetically favourable over iodine adsorption at neighbouring dimers. Simulated STM images of the obtained surface structures are presented and compared with experimental data.     

Surface chemistry of NO and NO2 on the Pt(1 1 0)-(1 × 2) surface: A comparative study

The surface chemistry of NO and NO₂ on clean and oxygen-precovered Pt(1 1 0)-(1 × 2) surfaces were investigated by means of high resolution electron energy loss spectroscopy (HREELS), X-ray photoelectron spectroscopy (XPS) and thermal desorption spectroscopy (TDS). At room temperature, NO molecularly adsorbs on Pt(1 1 0), forming linear NO(a) and bridged NO(a). Coverage-dependent repulsive interactions within NO(a) drive the reversible transformation between linear and bridged NO(a). Some NO(a) decomposes upon heating, producing both N₂ and N₂O. For NO adsorption on the oxygen-precovered surface, repulsive interactions exist between precovered oxygen adatoms and NO(a), resulting in more NO(a) desorbing from the surface in the form of linear NO(a). Bridged NO(a) experiences stronger repulsive interactions with precovered oxygen than linear NO(a). The desorption activation energy of bridged NO(a) from oxygen-precovered Pt(1 1 0) is lower than that from clean Pt(1 1 0), but the desorption activation energy of linear NO(a) is not affected by the precovered oxygen. NO₂ decomposes on Pt(1 1 0)-(1 × 2) surface at room temperature. The resulted NO(a) (both linear NO(a) and bridged NO(a)) and O(a) repulsively interact each other. Comparing with NO/Pt(1 1 0), more NO(a) desorbs from NO₂/Pt(1 1 0) as linear NO(a), and both linear NO(a) and bridged NO(a) exhibit lower desorption activation energies. The reaction pathways of NO(a) on Pt(1 1 0), desorption or decomposition, are affected by their repulsive interactions with coexisting oxygen adatoms.     

Ge(5 × 5) as a wetting layer on Si(1 1 1)

Ab initio total energy methods are used to investigate the effects on a Ge(1 1 1)-5 × 5 surface of the lateral compressive stress that would be due to a Si substrate, and the effects of intermixing at the interface with the substrate. The effects of stress due to the lattice mismatch between Si and Ge are studied on a Ge slab by changing the lattice constant in the surface plane from that of experimental bulk diamond Ge to that of Si. When this is done the height difference of the Ge adatoms in the faulted half-cell from those in the unfaulted half is accentuated. Effects on the Ge surface due to the presence of the Si-Ge interface were studied using a thin Ge layer on a Si substrate. The presence of the substrate leads to corrugations with significant height differences appearing among the faulted adatoms. The energetics of intermixing were investigated for Si-Ge single atom interchanges. Additional corrugations resulted from the shortened bondlengths due to the Si impurity in the wetting layer.     

STM observation of initial growth of Sn atoms on Ge(0 0 1) surface

We have studied initial growth of Sn atoms on Ge(0 0 1) surfaces at room temperature and 80 K by scanning tunneling microscopy. For Sn deposition onto the Ge(0 0 1) substrate at room temperature, the Sn atoms form two kinds of one-dimensional structures composed of ad-dimers with different alignment, in the 〈3 1 0〉 and the 〈1 1 0〉 directions, and epitaxial structures. For Sn deposition onto the substrate at 80 K, the population of the dimer chains aligning in the 〈3 1 0〉 direction increases. The diffusion barrier of the Sn adatom on the substrate kinetically determines the population of the dimer chain. We propose that the diffusion barrier height depends on surface strain induced by the adatom. The two kinds of dimer chains appearing on the Ge(0 0 1) and Si(0 0 1) surfaces with adatoms of the group-IV elements are systematically interpreted in terms of the surface strain.     

Vibrational entropy-driven dealloying of Mo(1 0 0) and W(1 0 0) surface alloys

The formation and stability of Cu, Ag and Au-induced c(2 × 2) alloys at the Mo(1 0 0) and W(1 0 0) surfaces have been investigated with low-energy electron microscopy and diffraction. The ordered alloys transform to disordered overlayer structures at elevated temperature. Comparison of the transformation temperatures with energetics obtained from first principles calculations reveals the vibrational entropic contribution to the system free energy that defines alloy thermal stability. Effective Debye temperatures for metal adatoms are determined that exhibit the expected mass and bond strength dependence.     

Perturbation of Ge(1 1 1) and Si(1 1 1)√3α-Sn surfaces by adsorption of dopants

We test the response of the √3 × √3α reconstructions formed by 1/3 monolayer of tin adatoms on silicon and germanium (1 1 1) surfaces upon doping with electrons or holes, using potassium or iodine as probes/perturbers of the initial electronic structures. From detailed synchrotron radiation photoelectron spectroscopy studies we show that doping with either electrons or holes plays a complimentary role on the Si and Ge surfaces and, especially, leads to complete conversion of the Sn 4d two-component spectra into single line shapes. We find that the low binding energy component of the Sn core level for both Si and Ge surfaces corresponds to Sn adatoms with higher electronic charge, than the Sn adatoms that contribute to the core level high binding energy signal. This could be analyzed as Sn adatoms with different valence state.     

Ground-state properties of arsenic deposited on the Ge(0 0 1)(2 × 1) surface

We present results of ab initio calculations of structural, electronic and vibrational properties of the Ge(0 0 1) surface covered with a monolayer of arsenic. The fully occupied π_u bonding and π_g antibonding electronic states due to the As-As dimer formation are quite close in energy and their ordering is same as that found on the Si(0 0 1) surface. Using our calculated atomic and electronic structures, surface lattice dynamics was studied by employing a linear response approach based on density functional perturbation theory. A comparison of the phonon spectrum of the Ge(0 0 1)/As(2 × 1) surface with that of the clean Ge(0 0 1)(2 × 1) surface indicates the presence of several new characteristic phonon modes due to adsorption of As atoms.     

An ab initio-based approach to adsorption-desorption behavior of Si adatoms on GaAs(1 1 1)A-(2 × 2) surfaces

The adsorption-desorption behavior of Si adatoms on GaAs(1 1 1)A-(2 × 2) surfaces is investigated using our ab initio-based approach, in which adsorption and desorption behavior of Si adatoms is described by comparing the calculated desorption energy obtained by total-energy electronic-structure calculations with the chemical potential estimated by quantum statistical mechanics. We find that the Si adsorption at the Ga-vacancy site on the (2 × 2) surfaces with As adatoms occurs less than 1140-1590 K while the adsorption without As adatom does less than 630-900 K. The change in adsorption temperature of Si adatoms by As adatoms is due to self-surfactant effects of As adatoms: the promotion of the Si adsorption triggered by As adatoms is found to be interpreted in terms of the band-energy stabilization. Furthermore, the stable temperature range for Si adsorbed surfaces with As adatoms agrees with the experimental results. The obtained results provide a firm theoretical framework to clarify n-type doping processes during GaAs epitaxial growth.     

Surface structure and phase transition of Ge(1 1 1)-3 × 3-Pb studied by reflection high-energy positron diffraction

We studied the structures and the phase transition of Pb/Ge(1 1 1) surface by using the reflection high-energy positron diffraction. The surface structures at 60 K and 293 K have the 3 × 3 and √3 × √3 periodicities, respectively. The rocking curves measured at both temperatures are nearly the same. This indicates that the equilibrium positions of the surface atoms do not change according to the phase transition. From the analysis of the rocking curve based on the dynamical diffraction theory, we found that at both temperatures the surface structures are composed of the so-called one-up and two-down model. The 3 × 3-√3 × √3 phase transition for the Pb/Ge(1 1 1) surface is interpreted in terms of order-disorder transition.     

Carbon monoxide adsorption on Co deposited Pt(1 0 0)-hex: IRRAS and LEED investigations

Infrared reflection absorption spectroscopy (IRRAS) was used to investigate carbon monoxide (CO) adsorption on Pt(1 0 0) surfaces deposited with Co layers with different thicknesses. Pt(1 0 0) surfaces cleaned in ultrahigh vacuum showed surface reconstruction, i.e., Pt(1 0 0)-hex: two absorption bands ascribable to adsorbed CO on the 1 × 1 surface and hex domains emerge at 2086 and 2074 cm⁻¹, respectively, after 1.0 L CO exposure. Deposition of a 0.3-nm-thick-Co layer on Pt(1 0 0)-hex at 333 K changes the low-energy electron diffraction (LEED) pattern from hex to p(1 × 1), indicating that the deposited Co lifts the reconstruction. The IRRAS spectrum for 1.0-L-CO-exposed Co_0.3 nm/Pt(1 0 0)-hex fabricated at 333 K yields a single absorption band at 2059 cm⁻¹. For Co_0.3 nm/Pt(1 0 0)-hex fabricated at 693 K, the LEED pattern shows a less-contrasted hex and the pattern remains nearly unchanged even after CO exposure of 11 L, although only 1.0 L CO exposure to Pt(1 0 0)-hex lifts the surface reconstruction. A Co_0.3 nm/Pt(1 0 0)-hex surface fabricated at 753 K exhibits an absorption band at 2077 cm⁻¹, which is considered to originate from CO adsorbed on the Pt-enriched surface alloy. Co_0.3 nm/Pt(1 0 0)-hex surfaces fabricated above 773 K show a clear hex-reconstructed LEED pattern, and the frequencies of the adsorbed CO bands are comparable to those of Pt(1 0 0)-hex, indicating that the deposited Co atoms are diffused near the surface region. The outermost surface of the 3.0-nm-thick-Co-deposited Pt(1 0 0)-hex is composed of Pt-Co alloy domains even at a deposition temperature of 873 K. Based on the LEED and IRRAS results, the outermost surface structures of Co_x/Pt(1 0 0)-hex are discussed.     

Tl/Ge(1 0 0) system: Phase formation and phase transitions

Using scanning tunneling microscopy, phase formation and temperature-driven phase transitions in Tl/Ge(1 0 0) system have been studied. Evolution of Tl overlayer structure has been considered for three temperature ranges, including around room temperature (RT), high-temperature (HT) (350-450 K) and low-temperature (LT) (20-100 K) ranges. Upon RT growth, a 2 × 1-Tl phase develops in submonolayer range and is completed at around 1 ML of Tl. Cooling of the RT-deposited Tl overlayer results in formation of a set of various LT structures. These are 1D chains, 5 × 4-Tl and “stroked” phases observed in submonolayer range and a long-period c(12 × 14)-Tl phase developed at around 1 ML. All transitions between these RT and LT structures are reversible. At doses beyond 1 ML, RT deposition of Tl onto Ge(1 0 0) leads to the growth of second-layer Tl stripes, forming arrays with a 1 × 4 periodicity. Meanwhile, structure of the first layer also changes and it displays a set of various reconstructions, c(2 × 8), c(10 × 6) and c(10 × 7). All these structures remain unchanged upon cooling to LT. Growth at HT as well as heating of RT-deposited Tl overlayer irreversibly produces 3 × 2-Tl phase whose rows become decorated by second-layer Tl stripes at prolonged Tl deposition.     

Photon-induced chemical vapor deposition of molybdenum on Pt(1 1 1)

Temperature-programmed desorption (TPD) and X-ray photoelectron spectroscopy (XPS) have been employed to study the adsorption and photon-induced decomposition of Mo(CO)₆. Mo(CO)₆ adsorbs molecularly on a Pt(1 1 1) surface with weak interaction at 100 K and desorbs intact at 210 K without undergoing thermal decomposition. Adsorbed Mo(CO)₆ undergoes decarbonylation to form surface Mo(CO)_x (x ? 5) under irradiation of ultraviolet light. The Mo(CO)_x species can release further CO ligands to form Mo adatoms with CO desorption at 285 K. In addition, a fraction of the released CO ligands transfers onto the Pt surface and subsequently desorbs at 350-550 K. The resulting Mo layer deposited on the Pt surface is nearly free of contamination by C and O. The deposited Mo adatoms can diffuse into the bulk Pt at temperatures above 1070 K.     

Adsorption of Nd on the Mo(1 1 0) surface

The adsorption of Nd on the Mo(1 1 0) surface has been studied by low energy electron diffraction and Auger electron spectroscopy. It has been found that at low coverages Nd adatoms form a rich amount of dilute (n × 2) commensurate structures, which can be explained as forming zigzag chains oriented along the [1 1 0] direction. Monte Carlo simulations indicate that the formation of the zigzag chain structures is initiated by the indirect lateral interaction between Nd adatoms.