STM studies of cyclohexene hydrogenation/dehydrogenation and its poisoning by carbon monoxide on Pt(1 1 1)

A scanning tunneling microscope that can be operated in ultra high vacuum (<10⁻⁹ Torr) as well as at high pressures (1 − 10³ Torr) has been utilized to study the structures formed by cyclic C₆ hydrocarbons adsorbed on a platinum (1 1 1) crystal surface. Catalytic reactions of cyclohexene were also studied in the presence of hydrogen at pressures (up to 200 mTorr) and 300 K-350 K temperature range. Cyclohexane and cyclohexene produced the same adsorbed structure, which is attributed to the partially dehydrogenated π-allyl (C₆H₉). 1,3-Cyclohexadiene produced structures similar to those produced by benzene. In contrast 1,4-cyclohexadiene forms a structure that we attribute to intact molecular 1,4-cyclohexadiene. During reaction the STM images appear disordered, indicative of rapid diffusion of surface species. Addition of 5 mTorr of CO stops the catalytic activity and forms an ordered structure on the surface.     

Formation and hydrogenation of p(2 × 2)-N on Pt(1 1 1)

The formation of a well-ordered p(2 × 2) overlayer of atomic nitrogen on the Pt(1 1 1) surface and its reaction with hydrogen were characterized with reflection absorption infrared spectroscopy (RAIRS), temperature programmed desorption (TPD), low energy electron diffraction (LEED), Auger electron spectroscopy (AES), and X-ray photoelectron spectroscopy (XPS). The p(2 × 2)-N overlayer is formed by exposure of ammonia to a surface at 85 K that is covered with 0.44 monolayer (ML) of molecular oxygen and then heating to 400 K. The reaction between ammonia and oxygen produces water, which desorbs below 400 K. The only desorption product observed above 400 K is molecular nitrogen, which has a peak desorption temperature of 453 K. The absence of oxygen after the 400 K anneal is confirmed with AES. Although atomic nitrogen can also be produced on the surface through the reaction of ammonia with an atomic, rather than molecular, oxygen overlayer at a saturation coverage of 0.25 ML, the yield of surface nitrogen is significantly less, as indicated by the N₂ TPD peak area. Atomic nitrogen readily reacts with hydrogen to produce the NH species, which is characterized with RAIRS by an intense and narrow (FWHM ∼ 4 cm⁻¹) peak at 3322 cm⁻¹. The areas of the H₂ TPD peak associated with NH dissociation and the XPS N 1s peak associated with the NH species indicate that not all of the surface N atoms can be converted to NH by the methods used here.     

Angular distributions of desorbing N2 in thermal N2O decomposition on Rh(1 0 0)

The angular distribution of desorbing N₂ was studied in the decomposition of N₂O(a) on Rh(1 0 0) at 60-140 K by means of angle-resolved temperature-programmed desorption. N₂ desorption shows two peaks at around 80 K and 110 K. At low N₂O coverage, the former collimates far from the surface normal toward the [0 0 1] direction, whereas at high coverage, the desorption sharply collimates along the surface normal. The adsorption form of N₂O and its dissociation were also examined by DFT-GGA calculations. Dissociating N₂O is proposed to be lying along the [0 0 1] direction at low coverage and to change to an upright form bonding through the terminal oxygen at high coverage.     

Reactivity of 3-hexyne on oxygen modified Ru(0 0 1) surfaces: Observation of oxametallacycles by RAIRS

The chemical behaviour of 3-hexyne on oxygen modified Ru(0 0 1) surfaces has been analysed under ultrahigh-vacuum, using reflection-absorption infrared spectroscopy (RAIRS). The effects of oxygen coverage, 3-hexyne exposure and adsorption temperature were studied. Two modified Ru(0 0 1) surfaces were prepared: Ru(0 0 1)-(2 × 2)-O and Ru(0 0 1)-(2 × 1)-O that correspond to oxygen coverages (θ_O) of 0.25 and 0.5 ML, respectively. The striking result is the direct bonding to an O atom when the modified surfaces are exposed to a very low dose (0.2 L) of 3-hexyne at low temperature (100 K). For θ_O = 0.25 ML, an unsaturated oxametallacycle [Ru-O-C(C₂H₅)C(C₂H₅)-Ru] is proposed, identified by RAIRS for the first time, through the νCC and νCO modes. Further decomposition at 110 K yields smaller oxygenated intermediates, such as acetyl [μ₃-η²(C,O)-CH₃CO], co-adsorbed with a small amount of carbon monoxide and non-dissociated species. The temperature at which a fraction of molecules undergoes complete C-C and C-H bond breaking is thus much lower than on clean Ru(0 0 1). The ultimate decomposition product observed by RAIRS at 220 K is methylidyne [CH]. Another key observation was that the adsorption temperature is not determinant of the reaction route, contrarily to what occurs on clean Ru(0 0 1): even when 3- hexyne strikes the surface at a rather high temperature (220 K), the multiple bond does not break completely. For θ_O = 0.5 ML, a saturated oxametallacycle [Ru-O-CH(C₂H₅)-CH(C₂H₅)-Ru] is also proposed at 100 K, identified by the ν_asO-C-C (at 1043 cm⁻¹) and ν_sO-C-C (at 897 cm⁻¹) modes, showing that some decomposition with C-H bond breaking occurs. For this oxygen coverage, the reaction temperatures are lower, and the intermediate surface species are less stable.     

CO2 adsorption on Cr(1 1 0) and Cr2O3(0 0 0 1)/Cr(1 1 0)

We attempt to correlate qualitatively the surface structure with the chemical activity for a metal surface, Cr(1 1 0), and one of its surface oxides, Cr₂O₃(0 0 0 1)/Cr(1 1 0). The kinetics and dynamics of CO₂ adsorption have been studied by low energy electron diffraction (LEED), Aug er electron spectroscopy (AES), and thermal desorption spectroscopy (TDS), as well as adsorption probability measurements conducted for impact energies of E_i = 0.1-1.1 eV and adsorption temperatures of T_s = 92-135 K. The Cr(1 1 0) surface is characterized by a square shaped LEED pattern, contamination free Cr AES, and a single dominant TDS peak (binding energy E_d = 33.3 kJ/mol, first order pre-exponential 1 × 10¹³ s⁻¹). The oxide exhibits a hexagonal shaped LEED pattern, Cr AES with an additional O-line, and two TDS peaks (E_d = 39.5 and 30.5 kJ/mol). The initial adsorption probability, S₀, is independent of T_s for both systems and decreases exponentially from 0.69 to 0.22 for Cr(1 1 0) with increasing E_i, with S₀ smaller by ∼0.15 for the surface oxide. The coverage dependence of the adsorption probability, S(Θ), at low E_i is approx. independent of coverage (Kisliuk-shape) and increases initially at large E_i with coverage (adsorbate-assisted adsorption). CO₂ physisorbs on both systems and the adsorption is non-activated and precursor mediated. Monte Carlo simulations (MCS) have been used to parameterize the beam scattering data. The coverage dependence of E_d has been obtained by means of a Redhead analysis of the TDS curves.     

Condensation and desorption of nickel tetra-carbonyl on Cu(1 1 0)

The condensation and desorption of nickel tetra-carbonyl (Ni(CO)₄) on Cu(1 1 0) has been studied by thermal desorption spectroscopy. A quite unusual evolution of the desorption spectra is observed. First a desorption peak appears at around 140 K, which disappears with increasing coverage and merges into a clearly separated new desorption peak at around 150 K. This transformation takes place at a coverage of about 10% of a monolayer. It is suggested that the low temperature peak is due to desorption of monomers. With increasing coverage nucleation and growth of multilayer islands starts, from which the desorption energy is higher due to the higher coordination of the carbonyl molecules, compared to that of the monomers. Evaluation of the multilayer desorption spectra yields a desorption energy of 57.9 kJ/mol (0.60 eV) and an unusually high frequency factor of 1.6 × 10¹⁹ s⁻¹.     

Ethylene hydrogenation on Ni(1 0 0) surface

The hydrogenation of ethylene on Ni(1 0 0) surface has been studied by TDS. The decrease in the bonding energy with increasing coverage is revealed for both of adsorbed hydrogen and ethylene by the shift of desorption to lower temperatures. Ethane formation is only observed on the preadsorbed hydrogen coverage exceeding 0.5 monolayer (ML), coupled with the growth of H₂ shoulder peak at lower temperatures. Further increase of H coverage to saturation reduces the bonding energy of subsequently adsorbed ethylene by 15 kJ/mol and decreases the saturation coverage of ethylene to about one-third on the clean surface. This leads to the shift of ethane desorption from 250 to 220 K and an appearance of additional ethane peak at 180 K. The latter ethane formation coincides with the hydrogenation of surface ethyl species derived from ethyl iodide as a precursor. It indicates that the rate of ethyl formation on the surface would be comparable to that of subsequent hydrogen addition to the surface ethyl species in the hydrogenation of ethylene when the preadsorbed hydrogen coverage approaches 1.0 ML.     

The adsorption of and reaction of NO2 on Ag(1 1 1)-p(4 × 4)-O and formation of surface nitrate

The adsorption and reaction of nitrogen dioxide on the Ag(1 1 1)-p(4 × 4)-O surface has been investigated with RAIRS, TPRS and STM. At 300 K NO₂ initially reacts with the oxygen overlayer to form nitrate in p(3 × 3) and p(4 × 4) structures, which convert to a new p(3 × 3) at saturation coverage. Surface pitting during nitrate adsorption is suggestive of the incorporation of silver atoms into the NO₃ structure. With heating NO₃ decomposes into NO₂ and O at 396 K and 497 K, and oxygen desorbs at 578 K.     

Anomalous adsorption of Cs on Pt(1 1 1)

The adsorption of Cs on Pt(1 1 1) surfaces and its reactivity toward oxygen and iodine for coverages θ_Cs?0.15 is reported. These surfaces show unusual “anomalous” behavior compared to higher coverage surfaces. Similar behavior of K on Pt(1 1 1) was previously suggested to involve incorporation of K into the Pt lattice. Despite the larger size of Cs, similar behavior is reported here. Anomalous adsorption is found for coverages lower than 0.15 ML, at which point there is a change in the slope of the work function. Thermal Desorption Spectroscopy (TDS) shows a high-temperature Cs peak at 1135 K, which involves desorption of Cs⁺ from the surface.The anomalous Cs surfaces and their coadsorption with oxygen and iodine are characterized by Auger Electron Spectroscopy (AES), TDS and Low Electron Energy Diffraction (LEED). Iodine adsorption to saturation on Pt(1 1 1)(anom)-Cs give rise to a sharp LEED pattern and a distinctive work function increase. Adsorbed iodine interacts strongly with the Cs and weakens the Cs-Pt bond, leading to desorption of Cs_xI_y clusters at 560 K. Anomalous Cs increases the oxygen coverage over the coverage of 0.25 ML found on clean Pt. However, the Cs-Pt bond is not significantly affected by coadsorbed oxygen, and when oxygen is desorbed the anomalous cesium remains on the surface.     

Formamide reactions on rutile TiO2(0 1 1) surface

The reaction of formamide over the (0 1 1) faceted TiO₂(0 0 1) surface has been studied by Temperature Programmed Desorption (TPD) and X-ray Photoelectron Spectroscopy (XPS). Two main reactions were observed: dehydration to HCN and H₂O and decomposition to NH₃ and CO. The dehydration reaction was found to be three to four times larger than the decomposition at all coverages. Each of these reactions is found to occur in two temperature domains which are dependent upon surface coverage. The low temperature pathway (at about 400 K) is largely insensitive to surface coverage while the high temperature pathway (at about 500 K) shifts to lower temperatures with increasing surface coverage. These two temperature pathways may indicate two adsorption modes of formamide: molecular (via an η¹(O) mode of adsorption) and dissociative (via an η²(O,N) mode of adsorption). C1s and N1s XPS scans indicated the presence of multiple species after formamide absorption at 300 K. These occurred at ca. 288.5 eV (-CONH-) and 285 eV (sp³/sp² C) for the C1s and 400 eV-(NH₂), 398 eV (-NH) and 396 eV (N) for the N1s and result from further reaction of formamide with the surface.     

Adsorption and thermal reaction of short-chain alkanethiols on GaAs(1 0 0)

By means of temperature-programmed desorption (TPD) and X-ray photoemission spectroscopy (XPS) with synchrotron radiation, we investigated the adsorption and thermal decomposition of alkanethiols (RSH, R = CH₃, C₂H₅, and C₄H₉) on a GaAs(1 0 0) surface. All chemisorbed alkanethiols can deprotonate to form thiolates below 300 K via dissociation of the sulfhydryl hydrogen (-SH). Two types of thiolates species are observed on GaAs(1 0 0), according to adsorption on surface Ga and As sites. The thiolates adsorbed on a Ga site preferentially recombine with surface hydrogen to desorb as a molecular thiol at 350-385 K. The thiolate on the As site exhibits greater thermal stability and undergoes mainly dissociation of the C-S bond at ∼520 K, independent of the alkyl chain length. The decomposition of CH₃S either directly desorbs CH₃ or transfers the CH₃ moiety onto the surface. The surface CH₃ further evolves directly from the surface at 665 K. The dissociations of C₂H₅S and C₄H₉S yield surface C₂H₅ and C₄H₉, which further decompose to desorb C₂H₄ and C₄H₈, respectively, via β-hydride elimination. The complete decomposition of alkanethiol leads to the formation of surface S without deposition of carbon. Adsorption of CH₃SSCH₃ results in the formation of surface CH₃S at initial exposures via scission of the S−S bond. Compared with the adsorption of CH₃SH, the CH₃S on the Ga site exhibits greater thermal stability because surface hydrogen is absent. At a high exposure, CH₃SSCH₃ can absorb molecularly on the surface and decompose to desorb CH₃SCH₃ via formation of a CH₃SS intermediate.     

The mechanism of amine formation on Si(1 0 0) activated with chlorine atoms

The dissociation of NH₃ on a Si(1 0 0) surface activated with Cl atoms was investigated using X-ray photoelectron spectroscopy. Gas phase UV-Cl₂ (0.1-10 Torr Cl₂ for 10-600 s under 1000 W Xe lamp illumination) completely replaced the H-termination on aqueous-cleaned Si(1 0 0) with 0.82 ± 0.06 ML of Cl at 298 K. A single spin-orbit split Cl 2p doublet indicated that the Cl atoms were bound to Si dimer atoms, forming silicon monochloride (Cl-Si-Si-Cl). Exposing the Cl-terminated surface at 348 K to NH₃ (1-1000 Torr for 5-60 min) replaced one Cl atom with one N atom up to a coverage of 0.33 ± 0.02 ML. Cl atoms lowered the activation energy barrier for reaction to form a primary amine (Si-NH₂). Oxygen was coadsorbed due to competition by H₂O contamination. The presence of Cl on the surface even after high NH₃ exposures is attributed to site blocking and electrostatic interactions among neighboring Cl-Si-Si-NH₂ moieties. The results demonstrate a low temperature reaction pathway for depositing N-bearing molecules on Si surfaces.     

Adsorption of cyclohexadiene, cyclohexene and cyclohexane on Pt(1 1 1)

The adsorption of 1,3-cyclohexadiene, 1,4-cyclohexadiene, cyclohexene and cyclohexane on Pt(1 1 1) was studied using ab initio density functional theory. For 1,3-cyclohexadiene three adsorption modes were distinguished: bridge 1,2-di-σ/3,4-π, hollow 1,4-di-σ/2,3-π and bridge 1,4-di-σ/2,3-π with adsorption energies of −155, −147 and −75 kJ/mol, respectively. Three stable adsorption modes were also identified for 1,4-cyclohexadiene: bridge quadra-σ, hollow di-σ/π and bridge di-π with adsorption energies of −146 kJ/mol, −142 kJ/mol and −88 kJ/mol, respectively. Cyclohexene was found to adsorb in six modes: 4 di-σ and 2 π-adsorption modes. The preferred configuration was found to be boat di-σ with an adsorption energy of −81 kJ/mol. The three other di-σ adsorption modes have comparable adsorption energies, ranging from −64 to −69 kJ/mol. Molecular strain and CPt bonding energies are used to elucidate stability trends. Cyclohexane is found to adsorb only at the hollow site whereby the axial hydrogen atoms are positioned over surface Pt-atoms with an adsorption energy of −37 kJ/mol. The calculations correctly predict the weakening of the axial CH bonds and provide a possible explanation for the large shift in the vibrational frequencies.     

The catalytic reduction of NO by H2 on Ru(0 0 0 1): Observation of NHads species

Adsorption of NO and the reaction between NO and H₂ were investigated on the Ru(0 0 0 1) surface by X-ray photoelectron spectroscopy (XPS). Surface composition was measured after NO adsorption and after the selective catalytic reduction of nitric oxide with hydrogen in steady-state conditions at 320 K and 390 K in a 30:1 mixture of H₂ and NO (total pressure = 10⁻⁴ mbar). After steady-state NO reduction, molecularly adsorbed NO in both the linear on-top and threefold coordinations, NH_ads and N_ads species were identified by XPS. The coverage of the NH_ads and N_ads species was higher after the reaction at 390 K than the corresponding values at 320 K. Strong destabilisation of N_ads by O_ads was detected. A possible reaction mechanism is discussed.     

Reflection absorption infrared study of the adsorption of dimethylamine on copper (1 1 0) and nickel (1 1 1) surfaces

The adsorption of dimethylamine on Cu(1 1 0) and Ni(1 1 1) has been studied by reflection absorption infrared spectroscopy. For Cu(1 1 0), adsorption was molecular at 80 and 300 K and for submonolayer dimethylamine the appearance of A′ and not A″ modes indicated C_s symmetry. Similar bonding was found for Ni(1 1 1) at 170 K. Annealing the adlayer to 350 K resulted in the formation of a new species on Ni(1 1 1), similar to that which has been identified as methylaminocarbyne on Pt(1 1 1). In contrast only molecular dimethylamine was identified on Cu(1 1 0), with H-bonded interactions at high coverage and a potential surface dimer.     

Catalytic reduction of NO in the presence of benzene on a Pt(3 3 2) surface

The catalytic reduction of NO in the presence of benzene on the surface of Pt(3 3 2) has been studied using Fourier transform infra red reflection-absorption spectroscopy (FTIR-RAS) and thermal desorption spectroscopy (TDS). IR spectra show that while the presence of benzene molecules at low coverage (e.g., following an exposure of just 0.25 L) promotes NO-Pt interaction, the adsorption of NO on Pt(3 3 2) at higher benzene coverages is suppressed. It is also shown that there are no strong interactions between the adsorbed NO molecules and the benzene itself or benzene-derived hydrocarbons, which can lead to the formation of intermediate species that are essential for N₂ production.TDS results show that the adsorbed benzene molecules undergo dehydrogenation accompanied by hydrogen desorption starting at 300 K and achieving a maximum at 394 K. Subsequent dehydrogenation of the benzene-derived hydrocarbons then begins with hydrogen desorption starting at 500 K. N₂ desorption from NO adlayers on clean Pt(3 3 2) surface becomes significant at temperatures higher than 400 K, giving rise to a peak at 465 K. This peak corresponds to N₂ desorption from NO dissociation on step sites. The presence of benzene promotes N₂ desorption, depending on the benzene coverage. When the benzene exposure is 0.25 L, the N₂ desorption peak at 459 K is dramatically increased. Increasing benzene coverage also results in the intensification of N₂ desorption at ∼410 K. At benzene exposures of 2.4 L, N₂ desorption develops as a broad peak with a maximum at ∼439 K.It is concluded that the catalytic reduction of NO by platinum in the presence of benzene proceeds by NO decomposition and subsequent oxygen removal at temperatures lower than 500 K, and NO dissociation is a rate-limiting step. The contribution of benzene to N₂ desorption is mainly attributed to providing a source of H, which quickly reacts with NO-derived atomic O, leaving the surface with more vacant sites for further NO dissociation.     

Growth of Rh nanoclusters on TiO2(1 1 0): XPS and LEIS studies

Rhodium clusters were prepared by evaporation on a nearly stoichiometric TiO₂(1 1 0) surface. The growth of metal nanoparticles, as a function of rhodium coverage, could be followed by monitoring the Rh 3d_5/2 XP peak position and by low energy ion scattering spectroscopy (LEIS). The substrate temperature in the 160-300 K regime during evaporation significantly influences the cluster size, leading to smaller crystallites at low temperature. Annealing the surface results in the agglomeration of rhodium, which commenced at lower temperature for smaller clusters. At high temperatures (∼900 K) encapsulation of rhodium also occurred.     

Characterization of methylidyne on Pt(1 1 1) with infrared spectroscopy

Methylidyne (CH) was prepared on Pt(1 1 1) by three methods: thermal decomposition of diiodomethane (CH₂I₂), ethylene decomposition at temperatures above 450 K, and surface carbon hydrogenation. Methylidyne and its precursors are characterized by reflection absorption infrared spectroscopy (RAIRS). The C-I bond of diiodomethane breaks upon adsorption to produce methylene (CH₂), which decomposes to methylidyne at temperatures above 130 K. Above 200 K, methylidyne is the only hydrocarbon species observed with RAIRS, although reaction channels for the formation of methane (CH₄) and ethylene (C₂H₄) are indicated by temperature programmed desorption (TPD). As is well known from numerous previous studies, ethylene decomposes to ethylidyne (CCH₃) upon exposure to Pt(1 1 1) at 410 K. Upon annealing to 450 K, ethylidyne dissociates through two reaction pathways, dehydrogenation to ethynyl (CCH) and C-C bond scission to methylidyne. Ethylene dehydrogenation on the surface at 750 K and under low ethylene exposures produces surface carbon that can be hydrogenated to methylidyne with C-H and C-D stretch frequencies of 2956 and 2206 cm⁻¹, respectively. Hydrogen co-adsorption on the surface causes these frequencies to shift to higher values. Methylidyne is stable on Pt(1 1 1) to temperatures up to 500 K.     

Comparison of the interaction of Pd with positively and negatively poled LiNbO3(0 0 0 1)

To investigate the possibility of manipulating the surface chemical properties of finely dispersed metal films through ferroelectric polarization, the interaction of palladium with oppositely poled LiNbO₃(0 0 0 1) substrates was characterized. Low energy ion scattering indicated that the Pd tended to form three-dimensional clusters on both positively and negatively poled substrates even at the lowest coverages. X-ray photoelectron spectroscopy (XPS) showed an upward shift in the binding energy of the Pd 3d core levels of 0.9 eV at the lowest Pd coverages, which slowly decayed toward the bulk value with increasing Pd coverage. These shifts were independent of the poling direction of the substrate and similar to those attributed to cluster size effects on inert supports. Thus, the spectroscopic data suggested that Pd does not interact strongly with LiNbO₃ surfaces. The surface chemical properties of the Pd clusters were investigated using CO temperature programmed desorption. On both positively and negatively poled substrates, CO desorption from freshly deposited Pd showed a splitting of the broad 460 K desorption peak characteristic of bulk Pd into distinct peaks at 270 and 490 K as the Pd coverage was decreased below 1.0 ML; behavior that also resembles that seen on inert supports. It was found that a small fraction of the adsorbed CO may dissociate (<2%) for Pd on both positively and negatively poled substrates. The thermal response of the smaller Pd clusters on the LiNbO₃ surfaces, however, was different from that of inert substrates. In a manner similar to Nb₂O₅, when CO desorption experiments were carried out a second time, the adsorption capacity decreased and the higher temperature desorption peak shifted from 490 K to below 450 K. This behavior was independent of the substrate poling direction. Thus, while there was evidence that LiNbO₃ does not behave as a completely inert support, no significant differences between positively and negatively poled surfaces were observed. This lack of sensitivity of the surface properties of the Pd to the poling direction of the substrate is attributed to the three-dimensional Pd clusters being too thick for their surfaces to be influenced by the polarization of the underlying substrate.     

Reaction of water with Ce-Au(1 1 1) and CeOx/Au(1 1 1) surfaces: Photoemission and STM studies

This article reports photoemission and STM studies for the adsorption and dissociation of water on Ce-Au(1 1 1) alloys and CeO_x/Au(1 1 1) surfaces. In general, the adsorption of water at 300 K on disordered Ce-Au(1 1 1) alloys led to O-H bond breaking and the formation of Ce(OH)_x species. Heating to 500-600 K induced the decomposition or disproportionation of the adsorbed OH groups, with the evolution of H₂ and H₂O into gas phase and the formation of Ce₂O₃ islands on the gold substrate. The intrinsic Ce ↔ H₂O interactions were explored by depositing Ce atoms on water multilayers supported on Au(1 1 1). After adsorbing Ce on ice layers at 100 K, the admetal was oxidized immediately to yield Ce³⁺. Heating to room temperature produced finger-like islands of Ce(OH)_x on the gold substrate. The hydroxyl groups dissociated upon additional heating to 500-600 K, leaving Ce₂O₃ particles over the surface. On these systems, water was not able to fully oxidize Ce into CeO₂ under UHV conditions. A complete Ce₂O₃ → CeO₂ transformation was seen upon reaction with O₂. The particles of CeO₂ dispersed on Au(1 1 1) did not interact with water at 300 K or higher temperatures. In this respect, they exhibited the same reactivity as does a periodic CeO₂(1 1 1) surface. On the other hand, the Ce₂O₃/Au(1 1 1) and CeO_2−x/Au(1 1 1) surfaces readily dissociated H₂O at 300-500 K. These systems showed an interesting reactivity for H₂O decomposition. Water decomposed into OH groups on Ce₂O₃/Au(1 1 1) or CeO_2−x/Au(1 1 1) without completely oxidizing Ce³⁺ into Ce⁴⁺. Annealing over 500 K removed the hydroxyl groups leaving behind CeO_2−x/Au(1 1 1) surfaces. In other words, the activity of CeO_x/Au(1 1 1) for water dissociation can be easily recovered. The behavior of gold-ceria catalysts during the water-gas shift reaction is discussed in light of these results.