Structure and properties of star‐shaped solution‐polymerized styrene‐butadiene rubber and its co‐coagulated rubber filled with silica/carbon black‐I: morphological structure and mechanical properties

The morphological structure and mechanical properties of the star‐shaped solution‐polymerized styrene‐butadiene rubber (SSBR) and organically modified nanosilica powder/star‐shaped SSBR co‐coagulated rubber (N‐SSBR) both filled with silica/carbon black (CB) were studied. The results showed that, compared with SSBR, silica powder could be mixed into N‐SSBR much more rapidly, and N‐SSBR/SiO₂ nanocomposite had better filler‐dispersion and processability. N‐SSBR/SiO₂/CB vulcanizates displayed higher glass‐transition temperature and lower peak value of internal friction loss than SSBR/SiO₂/CB vulcanizates. In the N‐SSBR/SiO₂/CB vulcanizates, filler was dispersed in nano‐scale resulting in good mechanical properties. Composites filled with silica/CB doped filler exhibited more excellent mechanical properties than those filled with a single filler because of the better filler‐dispersion and stronger interfacial interaction with macromolecular chains. N‐SSBR/SiO₂/CB vulcanizates exhibited preferable performance in abrasion resistance and higher bound rubber content as the blending ratio of silica to CB was 20:30. Copyright © 2008 John Wiley & Sons, Ltd.     

Insights into the Payne Effect of Carbon Black Filled Styrene-butadiene Rubber Compounds

As a widely used reinforcing filler of rubber, carbon black(CB) often enhances the nonlinear Payne effect and its mechanism still remains controversial. We adopt simultaneous measurement of rheological and electrical behaviors for styrene-butadiene rubber(SBR)/CB compounds and CB gel(CBG) during large deformation/recovery to investigate the contribution of conductive CB network evolution to the Payne effect of the compounds. In the highly filled compounds, the frequency dependence of their strain softening behavior is much more remarkable than that of their CB network breakdown during loading, while during unloading the unrecoverable filler network hardly affects the complete recovery of modulus, both revealing that their Payne effect should be dominated by the disentanglement of SBR matrix. Furthermore,the bound rubber adjacent to CB particles can accelerate the reconstruction of continuous CB network and improve the reversibility of Payne effect. This may provide new insights into the effect of filler network, bound rubber, and free rubber on the Payne effect of CB filled SBR compounds.     

Properties of ethylene propylene diene rubber/white and black filler composites cured by gamma radiation in presence of sorbic acid

The effect of incorporating sorbic acid (SA), an echo-friendly curing agent, and silica or carbon black (CB) filler, as well as gamma irradiation on the physico-chemical, mechanical and thermal properties of ethylene propylene diene monomer rubber (EPDM) was investigated. The results indicated that the developed composites revealed improvement in the studied parameters over the untreated samples. Filler incorporation into rubber matrix has been proven a key factor in enhancing the swelling resistance, tensile strength and thermal properties of the fabricated composites. The improvement in tensile strength and modulus was attributed to better interfacial bonding via SA. Alternatively, a comparison was established between the performance of the white and black fillers. The utmost mechanical performance was reported for the incorporated ratios 10 phr SA and 40 phr white filler into a 50 kGy irradiated composite. Meanwhile, the incorporation of CB yielded better thermally stable composites than those filled with silica at similar conditions.     

Effect of silane coupling agent on the polymer‐filler interaction and mechanical properties of silica‐filled NR

The effects of filler loading and a new silane coupling agent 3‐octanoylthio‐1‐ propyltriethoxysilane (NXT silane) on the polymer‐filler interaction and mechanical properties of silica‐filled and carbon black‐filled natural rubber (NR) compounds were studied. Silica (high dispersion silica7000GR, VN2, and VN3) and carbon black (N330) were used as the fillers, and the loading range was from 0 to 50 phr. The loading of NXT silane was from 0 to 6 phr. Experimental results show that the maximum and minimum torques of silica and carbon black‐filled NR increase with increasing filler loading. With increasing filler loading, the scorch time and optimum cure time decrease for carbon black‐filled NR, but increase for silica‐filled NR. The minimum torque, scorch time, and optimum cure time decrease because of the presence of NXT silane. For the carbon black and silica‐filled NR, the tensile strength and elongation at break have maximum values, but the hardness, M300, M100, and tear strength keep increasing with filler loading. The mechanical properties of silica‐filled NR were improved in the presence of NXT silane. With increasing filler loading, the storage modulus of filled NR increases, but the loss factor decreases. Carbon black shows the strongest polymer‐filler interaction, followed by VN3, 7000GR, and VN2. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 573–584, 2005     

Formation of Network by Carbon Black，Silica and Their Mixing Fillers in Isoprene Rubber北大核心CSCD

The network formed by fillers has great influence on the mechanical properties of rubber materials. To understand the formation of network by carbon black,silica,and carbon black/silica mixing fillers in rubber and its influence on the properties of rubber,isoprene rubber/filler composites with different filler loadings are prepared and their micromorphology,rheological and tensile properties are investigated. It is found that the dispersion of fillers is better in rubber after cure than that in rubber before cure for all three rubber systems,and the filler size of silica is smaller than that of carbon black,but the aggregation is more severe in silica filled rubber system. In mixed filler system,the two fillers tend to aggregate separately, leading to the low modulus at small strain than that in single filler system. With the increase of the filler loading,the tensile strength increases first and then decreases,the elongation at break decreases,and the temperature rise in compression flexometer tests increases. Moreover,the temperature rise in mixed filler system is higher than that in single filler system at high filler loading. © 2022, Science Press (China). All rights reserved.     

Difference in bound rubber formation of silica and carbon black with styrene‐butadiene rubber

Formation of bound rubber is affected by the physical structure and surface chemistry of filler and the property of rubber. Variation of the bound rubber formation in styrene‐butadiene rubber compounds filled with silica and/or carbon black was studied. Influence of temperature on extraction of loosely bound rubber was also investigated. For the both silica and carbon black‐filled compounds, the bound rubber content increases with increase in the silica content ratio. The bound rubber content decreases with increasing the extracting temperature. The loosely bound rubber content of the silica‐filled compound is higher than that of the carbon black‐filled one. Activation energy for the extraction of the unbound and loosely bound rubbers becomes higher as the total filler content increases. The activation energy of the silica‐filled compound is higher (almost double the value) than for the carbon black‐filled one. Copyright­© 2002 John Wiley & Sons, Ltd.     

Influence of filler type and content on properties of styrene‐butadiene rubber (SBR) compound reinforced with carbon black or silica

Rubber compounds are filled with reinforcing fillers to improve their physical properties. Carbon black and silica have different surface chemistries to each other. Differences in properties of carbon black‐ and silica‐reinforced styrene‐butadiene rubber (SBR) compounds were studied. Variation of properties of carbon black‐ or silica‐filled compounds with the filler content was also investigated. The silica‐filled compounds without any coupling agent and dispering agent were prepared to investigate the influence of polar materials‐adsorption on the silica surface. Viscosity and crosslink density increased with increase of the filler content. Hardness, modulus, tensile strength, and wear property were improved more and more by increasing the filler content. Viscosity of the silica‐filled compound was higher than that of the carbon black‐filled one. Cure rate of the silica‐filled compound became slower as the filler content increased, while that of the carbon black‐filled one became faster. Difference in properties between the carbon black‐ and silica‐filled compounds were explained by the poor silica dispersion and the adsorption of cure accelerator on the silica surface. Copyright © 2004 John Wiley & Sons, Ltd.     

Synergistic effect by high specific surface area carbon black as secondary filler in silica reinforced natural rubber tire tread compounds

The partial replacement of silica by high specific surface area and high structure Carbon Black (CB) N134 as secondary filler, keeping the same total filler content at 55 phr, shows a clear synergistic effect on overall performance. At low content of CB, i.e. in the range of 0–36 wt% of CB relative to total filler amount, the Payne effect and tan delta at both 0 °C and 60 °C change marginally, but thereafter gradually increase. Cure times are shortened in the presence of CB, facilitating an increase of productivity. Bound rubber content and mechanical properties show an optimum at 18 wt% of CB relative to total filler amount or at a ratio of silica/CB 45/10 phr. With regard to tire performance as indicated by the laboratory test results, the abrasion resistance, wet grip and ice traction can therefore be enhanced while maintaining the tire rolling resistance at the optimum level for this silica/CB ratio.     

炭黑结合橡胶对天然橡胶性能的影响

本文研究了天然橡胶(NR)与五种不同类型炭黑的结合橡胶对其混炼胶的应力-应变、流变性质等的影响。结果表明,NR与炭黑的结合橡胶量随炭黑结构和表面积增加而增加。结合橡胶的增加使NR在低剪切下的本体粘度、弹性恢复性和强度增加,塑性和粘着性降低;在高剪切下流动性变差,挤出物收缩则有所下降。此外,结合橡胶的增加也增加了硫化胶的交联度,因此模量、硬度和耐磨性提高,抗张强度和伸长率却有所下降。     

Comparison of the mechanical properties at similar hardness level of natural rubber filled with various reinforcing-fillers

Commercially, the alteration of a rubber formulation is usually made in such a way as to keep the hardness of the rubber product constant. This is because a specific hardness of the rubber product sets the limit to its practical applications. Therefore, in this paper, natural rubber (NR) vulcanizates containing various fillers were prepared to have the same hardness level, and their mechanical properties were compared and related to the degree of filler dispersion. The results show that higher amounts of carbon black (CB) and silica are needed for CB- and silica-filled natural rubber vulcanizates to achieve the same hardness value as a NR vulcanizate containing 6 phr of montmorillonite clay. At equal loading of fillers, clay-filled vulcanizate exhibits higher modulus, hardness, tensile strength and compression set, but lower heat build-up resistance and crack growth resistance than those of the vulcanizates containing conventional fillers. For the vulcanizate having the same hardness value, CB-filled vulcanizate gives the better overall mechanical properties followed by the clay-filled and silica-filled vulcanizates, respectively. The explanation is given as the better dispersion of carbon black, as can be seen in the SEM micrograph.     

The effects of a silane coupling agent on curing characteristics and mechanical properties of bamboo fibre filled natural rubber composites

The effects of a silane coupling agent on curing characteristics and mechanical properties of bamboo fibre filled natural rubber composites were studied. Scorch time, t₂ and cure time, t₉₀ of the composites decrease with increasing filler loading and with the presence of a silane coupling agent, Si69. Mooney viscosity also increases with increasing filler loading but at a similar filler loading shows lower value with the presence of Si69. The mechanical properties of composites viz tensile strength, tear strength, hardness and tensile modulus were also improved with the addition of Si69.     

Influences of different dimensional carbon-based nanofillers on fracture and fatigue resistance of natural rubber composites

The dimensions of reinforcing filler is a key factor in influencing the fracture and fatigue of rubbers. Here, the fracture and fatigue resistance of natural rubber (NR) filled with different dimensional carbon-based fillers including zero-dimensional spherical carbon black (CB), one-dimensional fibrous carbon nanotubes (CNTs) and two-dimensional planar graphene oxide (GO) were explored. To obtain equal hardness, a control indicator in the rubber industry, the amounts of CB, CNTs, and GO were 10.7 vol%, 1.2 vol%, and 1.6 vol%, respectively. J-integral and dynamic fatigue tests revealed that NR filled with CB exhibited the best quasi-static fracture resistance and dynamic crack growth resistance. The much higher hysteresis loss of NR filled with CNTs weakened its fatigue resistance. The planar GO played a limited role in preventing crack growth. Furthermore, digital image correlation revealed that NR filled with CB had the highest strain amplification level and area at the crack tip, which dissipated the most local input energy and then improved the fracture and fatigue performance.     

Understanding the reinforcement and dissipation of natural rubber compounds filled with hybrid filler composed of carbon black and silica

The performance of reinforced rubber compounds depends on the filler composition while the reinforcement and dissipation mechanisms still remain unclear.Herein linear and nonlinear dynamic rheological responses of carbon black/silica hybrid filler filling nature rubber compounds are investigated.The rheological contributions of dynamically retarded bulk phase and filler network are revealed to be crucial at high and low frequencies,respectively,and the bulk phase is shown to be of vital importance for the occurrence of nonlinear Payne effect at mediate frequencies.A framework for simultaneously solving reinforcement and dissipation varying with filler composition and content is suggested,providing a new perspective in understanding the filling effect for manufacturing high-performance rubber materials.     

Effect of carbon nanofibers on mechanical and electrical behaviors of acrylonitrile‐butadiene rubber composites

Recently, carbon nanofibers have become an innovative reinforcing filler that has drawn increased attention from researchers. In this work, the reinforcement of acrylonitrile butadiene rubber (NBR) with carbon nanofibers (CNFs) was studied to determine the potential of carbon nanofibers as reinforcing filler in rubber technology. Furthermore, the performance of NBR compounds filled with carbon nanofibers was compared with the composites containing carbon black characterized by spherical particle type. Filler dispersion in elastomer matrix plays an essential role in polymer reinforcement, so we also analyzed the influence of dispersing agents on the performance of NBR composites. We applied several types of dispersing agents: anionic, cationic, nonionic, and ionic liquids. The fillers were characterized by dibutylphtalate absorption analysis, aggregate size, and rheological properties of filler suspensions. The vulcanization kinetics of rubber compounds, crosslink density, mechanical properties, hysteresis, and conductive properties of vulcanizates were also investigated. Moreover, scanning electron microscopy images were used to determine the filler dispersion in the elastomer matrix. The incorporation of the carbon nanofibers has a superior influence on the tensile strength of NBR compared with the samples containing carbon black. It was observed that addition of studied dispersing agents affected the performance of NBR/CNF and NBR/carbon black materials. Especially, the application of nonylphenyl poly(ethylene glycol) ether and 1‐butyl‐3‐methylimidazolium tetrafluoroborate contributed to enhanced mechanical properties and electrical conductivity of NBR/CNF composites.     

Recent developments in rubber processing,leading to new applications such as the “green tyre”

Rubber articles derive most of their mechanical properties from the admixture of reinforcing fillers. Most commonly, carbon black is used as reinforcing filler. If silica is used instead, tyres made with such rubber compounds may exhibit a rolling resistance reduction by ca. 30%, which translates in substantial fuel savings of a car. Such silicas are far more difficult to mix with rubber than carbon black. Coupling agents are used as a surface modification of the filler to enhance compatibility with the polymer. Additionally they improve the ease of mixing with the rubber. The development of proper coupling agents combined with improved mixing techniques has contributed to the final break-through of the silicareinforced “Green Tyre”.     

纳米微晶纤维素对炭黑补强天然橡胶力学性能和动态性能的影响

采用酸水解工业微晶纤维素(MCC)制备纳米微晶纤维素(NCC),将其与天然胶乳共凝沉,混炼时加入炭黑(CB),制备了天然橡胶(NR)/NCC/CB复合材料,研究了NR/NCC/CB和NR/NCC/CB/RH(间苯二酚-六亚甲基四胺络合物)复合材料的力学性能和动态性能,并与NR/CB体系的性能进行对比.结果表明NCC可以均匀分散在天然橡胶基体中,且依拉伸方向取向,随着NCC替代炭黑的份数增加,Payne效应减弱,说明NCC本身并不构成强的填料网络,NR/NCC/CB与NR/CB比较,前者整体的网络化程度减弱,体系的损耗因子变化不大,NCC的加入改善了NR/CB的力学性能和抗屈挠龟裂性能,降低压缩疲劳温升和压缩永久形变,当NCC取代5～20 phr CB后,仍然保持高耐磨炭黑补强天然橡胶的耐磨耗性能.动态力学性能显示NR/NCC/CB的玻璃化转变温度较NR/CB变化不大,0℃的tanδ略有下降的同时60℃的tanδ明显降低.NR/NCC/CB/RH体系的Payne效应较NR/NCC/CB明显减弱,力学性能、抗屈挠龟裂性能和耐磨耗性能进一步改善,体系的压缩疲劳温升和压缩永久形变更小.     

Development of an O-ring from NR/EPDM filled silica/CB hybrid filler for use in a solid oxide fuel cell testing system

This research presents the effects of oxygen pressure and ambient temperatures on the crack behavior of O-rings from a semi-EV of NR/EPDM rubber with silica/CB filler, exposed to the inlet flow and outflow oxygen pressure in a Solid Oxide Fuel Cell (SOFC) environment. Blends of NR/EPDM were prepared with various ratios of silica/CB filler at 00/60, 10/50, 20/40, 30/30, 40/20, 50/10, and 60/00 phr. The fabricated O-ring complied with the standard for O-rings (TIS 2728-2559), with a minimum hardness of 65–75 Shore A, minimum tensile strength of 9 MPa, minimum elongation at break of 200%, and a minimum 100% modulus of 2.7 MPa. The mechanical properties of the compounds were tested, and the appropriate compound was chosen to make the O-rings to test in SOFC. The crack morphology of the fabricated O-rings was investigated and compared with a commercial O-ring after testing in the SOFC. As a result, the compound with silica/CB of 40:20 ratio provided the optimum mechanical properties, and passed the criteria standard of TIS 2728-2559. The mechanical properties of the prepared and commercial O-rings were similar (P-value of commercial with 60/00 = 0.273, 50/10 = 0.273, 40/20 = 0.144, 30/30 = 0.465, 20/40 = 0.465, 10/50 = 1.000 and 00/60 = 0.273; all > 0.05) and and both could still be continued to be used in SOFC despite some inner cracks after 24 h. The price of the prepared O-ring is cheaper than the commercial O-rings due to the low price of NR used in its formulation. Therefore, a prepared O-ring can be used in a SOFC, or other applications due to their mechanical properties and their reasonable price.     

高耐磨低生热NBR/TBIR复合材料的结构与性能

采用高反式-1,4-丁二烯-异戊二烯共聚橡胶(TBIR)对丁腈橡胶(NBR)进行改性, 制备了高耐磨、 低生热输送轮用白炭黑填充的NBR/TBIR橡胶纳米复合材料. 研究了NBR/TBIR橡胶纳米复合材料的交联密度、 物理力学性能及填料分散性, 探讨了材料的结构对性能的影响. 研究结果表明, 与纯NBR相比, NBR/TBIR橡胶纳米复合材料的硫化速率和交联密度随TBIR用量的增加而增大; 在保持NBR硫化胶基本力学性能、 耐老化性能和耐溶剂性能基本不变的前提下, TBIR的加入使NBR/TBIR硫化胶的耐磨性提高15%, 动态压缩生热降低5%, 动态压缩永久变形降低22%, 白炭黑分散水平提高; 与丁腈橡胶/顺丁橡胶[NBR/BR(80/20), 质量份数比]硫化胶相比, NBR/TBIR(80/20, 质量份数比)硫化胶具有更低的动态压缩生热和动态压缩永久变形及更好的填料分散性.     

Filler–polymer interactions in both silica and carbon black‐filled styrene–butadiene rubber compounds

Bound rubber in a filled rubber compound is formed by physical adsorption and chemisorption between the rubber and the filler. Styrene–butadiene rubber (SBR) is composed of four components of styrene, cis‐1,4‐, trans‐1,4‐, and 1,2‐units. Filler–polymer interactions in both silica and carbon black‐filled SBR compounds were studied by analyzing microstructures of the bound rubbers with pyrolysis‐gas chromatography. Differences in the filler–polymer interactions of the styrene, cis‐1,4‐, trans‐1,4‐, and 1,2‐units were investigated. The filler–polymer interactions of the butadiene units were found to be stronger than that of the styrene unit. The interactions of the cis‐1,4‐ and trans‐1,4‐units were stronger with carbon black than with silica, whereas the 1,2‐unit interacted more strongly with silica than with carbon black. © 2001 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 39: 439–445, 2001     

Preparation and mechanical properties of water-dispersible hyperbranched polymer grafted carbon black/natural rubber composites by latex blending method

In order to improve the mechanical properties of rubber-matrix composites, carboxyl-terminated hyperbranched poly (2-hydroxypropane-1,2,3-tricarboxylic acid) grafted carbon black (CB-g-CTHBP) was prepared, and it could be stably dispersed in water for up to 90 days. CB-g-CTHBP dispersion and natural rubber latex were blended to obtain NR/CB-g-CTHBP, and the effect of CB-g-CTHBP content on the mechanical properties of composites was discussed. The results show that the dispersibility and wettability of CB-g-CTHBP to composites are significantly improved after grafting hyperbranched polymer onto the surface. Compared with the composite filled with NR/CB, when the amount of filler is 30 phr, tensile strength, tear strength, and shore A hardness of NR/CB-g-CTHBP increase by 54.78%, 55.13%, and 20.96%, respectively. Moreover, CB-g-CTHBP could disperse more evenly in the natural rubber-matrix, and the interaction between CB-g-CTHBP and rubber-matrix could further enhance in the composite.