Preparation of microcrystalline silicon solar cells on microcrystalline silicon carbide window layers grown with HWCVD at low temperature

N-type microcrystalline silicon carbide layers prepared by hot-wire chemical vapor deposition were used as window layers for microcrystalline silicon n–i–p solar cells. The microcrystalline silicon intrinsic and p-layers of the solar cells were prepared with plasma-enhanced chemical vapor deposition at a very high frequency. Amorphous silicon incubation layers were observed at the initial stages of the growth of the microcrystalline silicon intrinsic layer under conditions close to the transition from microcrystalline to amorphous silicon growth. ‘Seed layers’ were developed to improve the nucleation and growth of microcrystalline silicon on the microcrystalline silicon carbide layers. Raman scattering measurement demonstrates that an incorporation of a ‘seed layer’ can drastically increase the crystalline volume fraction of the total absorber layer. Accordingly, the solar cell performance is improved. The correlation between the cell performance and the structural property of the absorber layer is discussed. By optimizing the deposition process, a high short-circuit current density of 26.7 mA/cm² was achieved with an absorber layer thickness of 1 μm, which led to a cell efficiency of 9.2%.     

A simple quality factor for characterization of thin silicon films

Four series of intrinsic thin Si films were prepared by plasma enhanced chemical vapor deposition at standard and high growth rate conditions. We suggest a simple ‘μc-Si:H layer quality factor’ based on the ratio of subgap optical absorption coefficient values: α(1.4 eV)/α(1 eV). This ratio minimizes the light scattering effects for rough films and can serve as a reliable detection of the amorphous/microcrystalline structure transition and also as a figure of merit for the microcrystalline layer. The quality factor is evaluated for series of our samples with well known structure and also compared with samples from other laboratories with different deposition and measurement techniques.     

Influence of crystalline volume fraction on the performance of high mobility microcrystalline silicon thin-film transistors

The influence of the crystalline volume fraction of hydrogenated microcrystalline silicon on the device performance of thin-film transistors fabricated at temperatures below 200 °C was investigated. Transistors employing microcrystalline silicon channel material prepared close to the transition to amorphous growth regime exhibit the highest charge carrier mobilities exceeding 50 cm²/V s. The device parameters like the charge carrier mobility, the threshold voltage and the subthreshold slope will be discussed with respect to the crystalline volume fraction of the intrinsic microcrystalline silicon material.     

Optoelectronic properties of hot-wire silicon layers deposited at 100 °C

Hot-wire chemical vapor deposition is employed for the deposition of amorphous and microcrystalline silicon layers at substrate temperature kept below 100 °C with the aid of active cooling of the substrate holder. The hydrogen dilution is varied in order to investigate films at the amorphous-to-microcrystalline transition. While the amorphous layers can be produced with a reasonably low defect density as deduced from subgap optical absorption spectra and a good photosensitivity, the microcrystalline layers are of a lesser quality, most probably due to a decrease of crystallinity during the film growth. In the amorphous growth regime, the Urbach energy values decrease with increasing hydrogen dilution, reaching a minimum of 67 meV just before the microcrystalline threshold. By varying the total gas pressure, the growth rate of the films is changed. The lowest deposition rate of this study (0.16 nm/s) produced the amorphous sample with the highest photoresponse (1 × 10⁶).     

Crystallinity of the mixed phase silicon thin films by Raman spectroscopy

Raman spectra of the mixed phase silicon films were studied for a sample with transition from amorphous to fully microcrystalline structure using four excitation wavelengths (325, 514.5, 632.8 and 785 nm). Factor analysis showed the presence of two and only two spectrally independent components in the spectra within the range from 250 to 750 cm^?1 for all four excitation wavelengths. The 785 nm excitation was found optimal for crystallinity evaluation and by comparison with surface crystallinity obtained by atomic force microscopy, we have estimated the ratio of integrated Raman cross-sections of microcrystalline and amorphous silicon at this wavelength as y = 0.88 ± 0.05.     

Determination of Raman emission cross-section ratio in hydrogenated microcrystalline silicon

The determination of the crystalline volume fraction from the Raman spectra of microcrystalline silicon involves the knowledge of a material parameter called the Raman emission cross-section ratio y. This value is still debated in the literature. In the present work, the determination of y has been carried out on the basis of quantitative analysis of medium-resolution transmission electron microscopy (TEM) micrographs performed on one layer deposited by very high frequency plasma enhanced chemical vapor deposition (VHF-PECVD) close to the amorphous/microcrystalline transition. Subsequent comparison of these data with the crystallinity as evaluated from measured Raman spectra yields a surprisingly high value of y = 1.7. This result is discussed in relation to previously published values (that range from 0.1 to 0.9).     

Influence of deposition conditions for bottom cell on micromorph tandem device performance

We have realized micromorph tandem solar cells on Asahi U-type TCO-covered glass substrates. The intrinsic layers of both amorphous top cell and microcrystalline bottom cell are grown by very high frequency plasma enhanced chemical vapour deposition (VHF-PECVD) at 100 MHz at low substrate temperature (150 °C). For the bottom cell different growth regimes have been explored by changing both chamber pressure and plasma power. The effect of the structural composition of the microcrystalline absorber layer on the electrical parameters of the device has been investigated. High short circuit current density and constant FF in a wide silane concentration range are obtained when using large power to pressure ratio (0.5 W/Pa). However, low open circuit voltage is generally found in this regime. The largest V_OC values are found at 67 Pa and power to pressure ratio of 0.3 W/Pa, where the highest efficiency (11.1%) is reached. An evaluation of device stability has been done by exposing the tandem solar cells to white light (AM 1.5-like spectrum) for 200 h.     

Properties of thin-film silicon solar cells at very high irradiance

The focussed beam of a low-power helium–neon laser is used to study accelerated light-induced degradation (Staebler–Wronski effect) and high steady-state photocarrier generation rates in amorphous and microcrystalline silicon thin-film solar cells, at up to 13 MW m^? 2 irradiance. Even at these high power densities, COMSOL® simulations indicate that heat diffusion into the substrate, aided by spreading conduction via the Ag back-contact, restricts the temperature rise to less than 14 °C. Short-circuit current may be measured directly, and the I–V characteristic estimated by taking into account shunting by the inactive part of the cell. The improved resistance to degradation of microcrystalline silicon cells is shown to persist to high irradiance. Computer simulations of an amorphous silicon solar cell are presented that are consistent with measured un-degraded and degraded properties, and offer insight into prevailing defect creation processes and carrier recombination mechanisms.     

Properties of thin film silicon,prepared at high growth rate in a wide range of thicknesses

Preparation of thin film silicon at high growth rate is an important target for its application in solar cells. The properties of hydrogenated microcrystalline silicon, prepared with the help of PECVD multi-hole cathode in a high pressure and depletion regime in a wide range of thicknesses are described in detail. We illustrate the surprising result that we can prepare high growth rate microcrystalline silicon from 0.4 up to 30 μm thickness without great peel-off problems. The room temperature dark DC conductivity, as well as the crystallinity, increased up to 5 μm film thickness and then started to decrease again. These results are explained by the initial temperature profiling and a thickness-induced increase of the lateral inhomogeneity.     

Deposition of microcrystalline silicon films at ultrafast rate by using a new microwave induced plasma source

Synthesis of microcrystalline silicon (μc-Si) film at an ultrafast deposition rate over 100 nm/s is achieved from SiH₄ + He by using a high density microwave plasma source even without employing H₂ dilution and substrate heating techniques. Systematic deposition studies show that high SiH₄ flow rate and working pressure increase film deposition rate while high He flow rate decreases the rate. On the other hand, crystallinity of deposited Si film decreases with increasing SiH₄ or He flow rate and working pressure. Enhancements of gas phase and surface reactions during film deposition process are responsible for the achievement of high deposition rate and high film crystallinity.     

Microstructures of high-growth-rate (up to 8.3 nm/s) microcrystalline silicon photovoltaic layers and their influence on the photovoltaic performance of thin-film solar cells

Microstructures of microcrystalline silicon (μc-Si) deposited at a high-growth-rate have been investigated in order to apply to the photovoltaic i-layer. μc-Si films were prepared by very-high-frequency (100 MHz) plasma-enhanced chemical vapor deposition at 180 °C. High growth rates of 3.3–8.3 nm/s have been achieved utilizing high deposition pressures up to 24 Torr and large input powers. Applying μc-Si to n–i–p junction solar cells, as the optimum result in this experimental series, a conversion efficiency of 6.30% (J_SC: 22.1 mA/cm², V_OC: 0.470 V, and FF: 60.7%) has been achieved employing the i-layer deposited at 8.1 nm/s. Raman scattering and X-ray diffraction measurements revealed the crystalline volume fraction of around 50% with the (2 2 0) crystallographic preferential orientation, respectively. The cross-sectional transmission electron microscope image shows densely columnar structure grown directly on the underlying n-layer. These structural features are basically in good agreement those of low-growth-rate μc-Si used for a high efficiency solar cell as previously reported, implying advantages of the use of high pressures with regard to providing the photovoltaic i-layers. Finally, the implication is discussed from the photovoltaic performance as a function of the crystalline volume fraction of i-layer, and current problems in improving the photovoltaic performance are extracted.     

Low concentrator hetero-junction microcrystalline silicon solar cells

Multi-junction silicon-based thin-film solar cells are attractive materials for further cost-reduction and high efficiency. Meanwhile, it is also well considered that a concentrator solar cell is another alternative approach to enhance the conversion efficiency. In concentrator solar cells, the photocurrent linearly increases with the concentration ratio of incident light. At the same time, the open-circuit voltage (V_oc) of solar cells increases logarithmically with the photocurrent. This leads to an increase in efficiency with increasing sunlight intensity.We proposed a novel hetero-junction structure microcrystalline silicon (μc-Si:H) solar cell structure using wide-gap microcrystalline silicon oxide (μc-Si_1 ? xO_x:H) as p-layer and it has some advantages over conventional homo-junction μc-Si:H solar cells under low concentrations. It was observed that wide-gap doped layers can reduce carrier recombination rate especially in p-layer and at the p/i interface and V_oc enhancement with increasing light intensity improves as the band gap of p-layer is increased. Our best solar cell has efficiencies of 9.2% at 1 sun and 10.4% at 11.8 suns. We also investigated the degradation behavior of hetero-junction μc-Si:H solar cells. The degradation in efficiency for this type of solar cell was less than 6%. Therefore, hetero-junction μc-Si:H solar cell is the promising alternative for low-light concentration.     

A narrow process window for the preparation of polytypes of microcrystalline silicon carbide thin films by hot-wire CVD method

Effects of deposition conditions on the structure of microcrystalline silicon carbide (μc-SiC) films prepared by hot-wire chemical vapor deposition (hot-wire CVD) method have been investigated. It is found from X-ray diffraction patterns of the film that a diffraction peak from crystallites from hexagonal polytypes of SiC is observed in addition to those of 3 C-SiC crystallites. This result is obtained in the film under a narrow deposition conditions of SiH₃CH₃ gas pressure of 8 Pa, the H₂ gas pressure of 80–300 Pa and the total gas pressure of 40–300 Pa under fixed substrate and filament temperatures employed in this study. Furthermore, the grain size of hexagonal crystallites (about 20 nm) on c-Si substrates becomes larger than that of 3 C-SiC crystallites (about 10 nm) for the films deposited under the total gas pressure of 36–88 Pa. The fact that microcrystalline hexagonal SiC can be deposited under limited deposition conditions could be interpreted in the context of a result for c-SiC polytypes prepared by thermal CVD method.     

Electron and hole transport in microcrystalline silicon solar cells studied by time-of-flight photocurrent spectroscopy

A photocurrent time-of-flight study of carrier transport in microcrystalline silicon pin diodes prepared over a range of crystallinities is presented. Electron and hole drift mobilities at a crystalline volume fraction >0.35 are typically 3.8 and 1.3 cm²/(V s) respectively at 300 K and a thickness to electric field ratio of 1.8 × 10⁻⁷ cm²/V. A factor of five enhancement in hole mobility over amorphous silicon persists at a crystalline volume fraction as low as 0.1. Current decays are dispersive and mobilities are thermally activated, although detailed field-dependence is still under investigation. Evidence for a sharp fall in the density of states at 0.13 eV above the valence band edge is presented. Similarities in behaviour with certain amorphous and polymorphous silicon samples are identified.     

Optical properties of microcrystalline 3C–SiC:H films measured by resonant photothermal bending spectroscopy

Optical absorption coefficient spectra of hydrogenated microcrystalline cubic silicon carbide (μc-3C–SiC:H) films prepared by Hot-Wire CVD method have been estimated for the first time by resonant photothermal bending spectroscopy (resonant-PBS). The optical bandgap energy and its temperature coefficient of μc-3C–SiC:H film is found to be about 2.2 eV and 2.3 × 10⁻⁴ eV K⁻¹, respectively. The absorption coefficient spectra of localized states, which are related to grain boundaries, do not change by exposure of air and thermal annealing. The localized state of μc-3C–SiC:H has different properties for impurity incorporation compared with that of hydrogenated microcrystalline silicon (μc-Si:H) film.     

Argon-plasma-induced growth of crystalline grains in microcrystalline silicon: Formation mechanism of grains

A thick (∼300 nm) microcrystalline silicon (μc-Si:H) film with a low crystalline volume fraction (∼24%) and a columnar grain size of about 100 nm was exposed to an argon plasma at a substrate temperature of 220 °C after deposition. It is shown that argon plasma treatment significantly enhances film-crystallinity throughout the μc-Si:H layer: over a factor of 2 in crystalline fraction and by a factor of 3 in columnar grain size after a 90-min argon treatment. Based on these experimental results, it is proposed that crystallization of μc-Si:H is likely mediated by the energy transferred from energetic argon atoms.     

Transport properties near the magneto/structural transition of Tb5Si2Ge2

We report high resolution measurements of the electrical resistivity (ρ, dρ/dT) and thermopower (S, dS/dT) measurements near the magnetic and structural transition of the layered Tb₅Si₂Ge₂ compound, which are fairly close but not fully coupled. The analysis of the transport properties confirms a split magneto/structural transition, with T_S ～ 97 K and T_S ～ 107 K for the structural transition (on cooling and heating respectively; 1st-order transition). The magnetic transition occurs only at T_C ～ 112 K and without hysteresis (2nd-order transition). The magnetic critical behavior of resistivity is analyzed, obtaining an almost classical mean field exponent (α ～ 0.59) for T > T_C. For the structural phase, and below T_S, we obtain a rather different exponent (α ～ 1.06).     

Optical and structural proprieties of nc-Si:H prepared by argon diluted silane PECVD

Using argon as a diluent of Silane, hydrogenated amorphous and nanorocrystalline silicon films Si:H were prepared by radio-frequency (13.56 MHz) plasma enhanced chemical vapor deposition (rf-PECVD). The deposition rate and crystallinity varying with the deposition pressure and rf power, were systematically studied. Structural analysis (Raman scattering spectroscopy and X-ray diffraction), combined with optical measurements spectroscopy were used to characterize the films. The argon dilution of silane for all samples studied was 95% by volume, and the substrate temperature was 200 °C. The deposition pressure was varied from 400 mTorr to 1400 mTorr and varying rf power from 50 to 250 W. The structural evolution studies, shows that beyond 200 W of rf power, an amorphous-nanocrystalline transition was observed, with an increase in crystalline fraction by increasing rf power and working pressure. The films were grown at high deposition rates. The deposition rates of the films near the amorphous-nanocrystalline phase transition region were found in the range 6–10 Å/s. A correlation between structural and optical properties has been found and discussed.     

Judd–Ofelt analysis of Nd3+ ions in poly(styrene sulfonate) films

In this work, we present the synthetic route and the optical characterization of poly(styrene sulfonate) (PSS) films doped with Neodymium ions (Nd³⁺). In the synthesis optimization we obtained the maximum incorporation of Nd³⁺ in the matrix about 14.0%. The UV–Vis–NIR curve presents an intense characteristic electronic transition ⁴I_9/2 → ⁴F_5/2 + ²H_9/2 at 800 nm. It was also shown the radiative transition ⁴F_3/2 → ⁴I_11/2 at about 1060 nm. Judd–Ofelt theory was used in order to obtain the near infrared Nd³⁺ radiative transition rate, emission cross-section and radiative lifetime.     

Tracer diffusion of 22Na and 45Ca,ionic conduction and viscosity of two standard soda-lime glasses and their undercooled melts

The tracer diffusivities of ⁴⁵Ca in two different high purity standard soda-lime silica glasses have been measured by the radiotracer method below and above their calorimetric glass transition temperatures. Calorimetric glass transition temperatures (T_g) of 845 K and 867 K have been obtained for standard glasses I and II, respectively, using differential scanning calorimetry (DSC) at a heating rate of 20 K/min. In this paper, we focus on the results of ⁴⁵Ca diffusion and conductivity of the two standard soda-lime glasses and compare them with ²²Na diffusivities also obtained in our laboratory [E.M. Tanguep Njiokep, H. Mehrer, Solid State Ionics 177 (2006) 2839, E.M. Tanguep Njiokep, H. Mehrer, Defect Diffus Forum 237–240 (2005) 282]. The ⁴⁵Ca diffusion coefficients obtained are found to follow the Arrhenius law, both below (Tanguep Njiokep and Mehrer, 2006, 2005) and above T_g. In the Arrhenius diagram a change of slope of the ⁴⁵Ca diffusivities appears at 835 K for standard glass I and at 790 K for standard glass II. At the same time, the ionic conductivities display a change in slope at 790 K and 778 K for standard glasses I and II, respectively. These temperatures are somewhat smaller than the calorimetric glass transition temperatures obtained at a heating rate of 20 K/min. Rather, they appear to be close to values of T_g obtained by extrapolation to a vanishing heating rate (Tanguep Njiokep and Mehrer, 2006). The viscosity diffusion of standard glass I is considerably smaller than the conductivity diffusion coefficient and both tracer diffusivities. In both glasses the ionic conductivity is essentially due to the motion of Na ions. The contribution of Ca ions to the conductivity is negligible.