Structural and optical properties of ZnO thin films deposited onto ITO/glass substrates

ZnO films were prepared by post deposition thermal oxidation in the ambient atmosphere of metallic Zn films (d = 100–170 nm) vacuum evaporated onto unheated indium tin oxide (ITO)-coated glass substrates. To study the effect of the substrate position during the Zn film deposition on the microstructure and optical properties (transmittance, reflectance and absorbance) of as obtained ZnO films, two set of Zn samples simultaneously deposited onto horizontally and obliquely arranged substrates were prepared. The as obtained ZnO films had a polycrystalline wurtzite structure, those obtained from normally deposited Zn films having a higher c-axis preferred orientation and a lower optical transmittance in the visible wavelength range. The optical band-gap was found to be of 3.14 eV for oxidized normally deposited virgin Zn films and of 3.16 eV for those obliquely deposited.     

Surface morphology of spin-coated As–S–Se chalcogenide thin films

Surface morphology and roughness of amorphous spin-coated As–S–Se chalcogenide thin films were determined using atomic force microscopy. Prepared films were coated from butylamine solutions with thicknesses d ∼ 100 nm and then annealed in a vacuum furnace at 45 °C and 90 °C for 1 h for their stabilization. The root mean square surface roughness analysis of surfaces of as-deposited spin-coated As–S–Se films indicated a very smooth film surface (with R_q values 0.42–0.45 ± 0.2 nm depending on composition). The nanoscale images of as-deposited films confirmed that surface of the films is created by domains with dimensions 20–40 nm, which corresponds to diameters of clusters found in solutions. The domain character of film surfaces gradually disappeared with increasing annealing temperature while the solvent was removed from the films. Middle-infrared transmission spectra recorded a decrease of intensities of vibration bands connected to N–H (at 3367 and 3292 cm⁻¹) and C–H (at 2965, 2935 and 2880 cm⁻¹) stretching vibrations. Temperature regions of solvent evaporation T = 60–90 °C and glass transformation temperatures T_g = 135–150 °C of spin-coated As–S–Se thin films were determined using a modulated differential scanning calorimetry.     

Electrochemical deposition of ZnO film and its photoluminescence properties

ZnO thin films were prepared by the electrochemical deposition method on conductive substrates. The as-deposited film was ZnO crystallites of the wurzite structure highly oriented along the (0 0 2) plane. The specific crystalline morphology may be attributed to the growth mechanism through the orientation attachment mode, which is one of the characteristics peculiar for the present process, because the terrace has been clearly observed in high-resolution AFM images. The film shows high transmittance and an optical band gap energy of 3.3 eV. After annealing in N₂ or Ar, strong green emission was observed, which should be related to the generation of singly ionized oxygen defects. Improving emission intensity further by optimizing the annealing conditions, this method may be promising to replace the traditional method for preparation of ZnO green phosphor.     

ZnO growth on Si with low-temperature ZnO buffer layers by ECR-assisted MBE

High-quality ZnO films were grown on Si(1 0 0) substrates with low-temperature (LT) ZnO buffer layers by an electron cyclotron resonance (ECR)-assisted molecular-beam epitaxy (MBE). In order to investigate the optimized buffer layer temperature, ZnO buffer layers of about 1.1 μm were grown at different growth temperatures of 350, 450 and 550 °C, followed by identical high-temperature (HT) ZnO films with the thickness of 0.7 μm at 550 °C. A ZnO buffer layer with a growth temperature of 450 °C (450 °C-buffer sample) was found to greatly enhance the crystalline quality of the top ZnO film compared to others. The root mean square (RMS) roughness (3.3 nm) of its surface is the smallest, compared to the 350 °C-buffer sample (6.7 nm), the 550 °C-buffer sample (7.4 nm), and the sample without a buffer layer (6.8 nm). X-ray diffraction (XRD), photoluminescence (PL) and Raman scattering measurements were carried out on these samples at room temperature (RT) in order to characterize the crystalline quality of ZnO films. The preferential c-axis orientations of (0 0 2) ZnO were observed in the XRD spectra. The full-width at half-maximum (FWHM) value of the 450 °C-buffer sample was the narrowest as 0.209°, which indicated that the ZnO film with a buffer layer grown at this temperature was better for the subsequent ZnO growth at elevated temperature of 550 °C. Consistent with these results, the 450 °C-buffer sample exhibits the highest intensity and the smallest FWHM (130 meV) of the ultraviolet (UV) emission at 375 nm in the PL spectrum. The ZnO characteristic peak at 438.6 cm⁻¹ was found in Raman scattering spectra for all films with buffers, which is corresponding to the E₂ mode.     

Electrical conductivity and single oscillator model properties of amorphous CuSe semiconductor thin film

The structural, optical dispersion and electrical conductivity properties of the CuSe thin film have been investigated using X-ray diffraction, electrical and optical characterization methods. X-ray diffraction results indicate that CuSe thin film has an amorphous structure. The electrical conductivity of the CuSe film increases with increasing temperature. The activation energy and room temperature conductivity values of the film were found to be 1.32 meV and 3.89 × 10⁻³ S/cm, respectively. The refractive index dispersion of the thin film obeys the single oscillator model and single oscillator parameters were determined. The E_o, n_∞, and S_o values of the CuSe thin film were found to be 5.08 eV, 3.55 and 1.92 × 10¹⁴ m⁻², respectively. The obtained results suggest that CuSe film is an amorphous semiconductor.     

Fabrication and ionic conductivity of amorphous Li–Al–Ti–P–O thin film

Li⁺ ion conducting Li–Al–Ti–P–O thin films were fabricated on ITO-glass substrates at various temperatures from 25 to 400 °C by RF magnetron sputtering method. When the substrate temperature is higher than 300 °C, severe destruction of ITO films were confirmed by XRD (X-ray diffraction) and the abrupt transformation of one semi-circle into two semi-circles on the impedance spectra. These as-deposited Li–Al–Ti–P–O solid state electrolyte thin films have an amorphous structure confirmed by XRD and a single semicircle on the impedance spectra. Good transmission higher than 80% in the visible light range of these electrolyte thin films can fulfill the demand of electro-chromic devices. Field emission scanning electron microscopy and atomic force microscopy showed the denser, smoother and more uniform film structure with the enhanced substrate temperature. Measurements of impedance spectra indicate that the gradual increased conductivity of these Li–Al–Ti–P–O thin films with the elevation of substrate temperature from room temperature to 300 °C is originated from the increase of the pre-exponential factor (σ₀). The largest Li-ion conductivity can come to 2.46 × 10^? 5 S cm^? 1. This inorganic solid lithium ion conductor film will have a potential application as an electrolyte layer in the field such as lithium batteries or all-solid-state EC devices.     

Influence of oxygen partial pressure on the properties of undoped InOx films deposited at room temperature by rf-PERTE

Transparent and conductive/semiconductive undoped indium oxide (InO_x) thin films were deposited at room temperature. The deposition technique used is the radio frequency (rf) plasma enhanced reactive thermal evaporation (rf-PERTE) of indium (In) in the presence of oxygen. The influence of oxygen partial pressure on the properties of these films is presented. The oxygen partial pressure varied between 3 × 10^?2 and 1.3 × 10^?1 Pa. Undoped InO_x films, 100 nm thick, deposited at the oxygen partial pressure of 6 × 10^?2 Pa show a conductive behaviour, exhibit an average visible transmittance of 81%, a band gap around 2.7 eV and an electrical conductivity of about 1100 (Ω cm)^?1. For oxygen pressures greater than 6 × 10^?2 Pa, semiconductive films are obtained, maintaining the visible transmittance. Films deposited at lower pressures are conductive but dark. From XPS data, films deposited at an oxygen partial pressure of 6 × 10^?2 Pa show the highest amount of oxygen in the film surface and the lowest ratio between oxygen in the oxide crystalline and amorphous phases.     

Influence of amorphous buffer layers on the crystallinity of sputter-deposited undoped ZnO films

Undoped ZnO films were deposited by radio frequency (RF) magnetron sputtering on amorphous buffer layers such as SiO_x, SiO_xN_y, and SiN_x prepared by plasma enhanced chemical vapor deposition (PECVD) for dielectric layer in thin film transistor (TFT) application. ZnO was also deposited directly on glass and quartz substrate for comparison. It was found that continuous films were formed in the thickness up to 10 nm on all buffer layers. The crystallinity of ZnO films was improved in the order on quartz>SiO_x >SiO_xN_y>glass>SiN_x according to the investigated intensities of (0 0 2) XRD peaks. The crystallite sizes of ZnO were in the order of SiO_x～glass >SiN_x. Stable XRD parameters of ZnO thin films were obtained to the thickness from 40 to 100 nm grown on SiO_x insulator for TFT application. Investigation of the ZnO thin films by atomic force microscope (AFM) revealed that grain size and roughness obtained on SiN_x were larger than those on SiO_x and glass. Hence, both nucleation and crystallinity of sputtered ZnO thin films remarkably depended on amorphous buffer layers.     

Optical absorption in amorphous InN thin films

Amorphous indium nitride (a-InN) thin films were deposited onto different substrates at temperatures <325 K using RF magnetron sputtering at a rate 0.3–0.4 Å/s. X-ray diffraction patterns reveal that the films grown on the substrates are amorphous. The optical absorption edge, ‘bandgap’ energy, E_g, of a-InN has been determined by spectroscopic ellipsometry over the energy range 0.88–4.1 eV. The absorption coefficient was obtained by the analysis of the measured ellipsometric spectra with the Tauc–Lorentz model. The E_g was determined using the modified Tauc and Cody extrapolations. The corresponding Tauc and Cody optical bandgaps were found to be 1.75 and 1.72 eV, respectively. These values are in excellent agreement with the values of the bandgap energy obtained as fitting parameters in the Tauc–Lorentz model: 1.72 ± 0.006 eV as well as by using spectrophotometry (1.74 eV) and photoluminescence (1.6 eV). The spectral dependence of the polarized absorptivities was also investigated. We found that there was a higher absorptivity for wavelengths <725 nm. This wavelength, ∼725 nm, therefore indicates that the absorption edge for a-InN is about 1.70 eV. Thus, the average value of the measured optical absorption of a-InN film is approximately 1.68 ± 0.071 eV.     

Sol–gel derived highly transparent and conducting yttrium doped ZnO films

This paper reports the structural, electrical and optical properties of Yttrium doped zinc oxide (YZO) thin films deposited on Corning (7059) glass substrates by spin coating technique. A precursor solution of ZnO, 0.2 M in concentration was prepared from zinc acetate dissolved in anhydrous ethanol with diethanolamine as a sol gel stabilizer. Yttrium nitrate hexahydrate (Y₂NO₃ · 6H₂O) was used as the dopant (3 wt%) in the present study. The films of different thickness in the range (200–500 nm) were prepared. The films were annealed in air at 450 °C for 1 h. It was observed that the c-axis orientation improves and the grain size increases as is indicated by an increase in intensity of the (0 0 2) peak and the decrease in the FWHM with the increase of film thickness. The resistivity decreased sharply from 2.8 × 10⁻² to 5.8 × 10⁻³ Ω-cm as the thickness increased from 200 to 500 nm. However, the average transmittance decreased from 87% to 82.6% as the film thickness increased to 500 nm. The lowest sheet resistance of ∼120 Ω/□ was obtained for the 500 nm thick film.     

Absorption and luminescence in amorphous SixGe1-xO2 films fabricated by SPCVD

Optical absorption and photoluminescence of Ge-doped silica films fabricated by the surface-plasma chemical vapor deposition (SPCVD) are studied in the 2–8 eV spectral band. The deposited on silica substrate films of about 10 μm in thickness are composed as x·GeO₂-(1-x)·SiO₂ with x ranging from 0.02 to 1. It is found that all as‐deposited films do not luminesce under the excitation by a KrF (5 eV) excimer laser, thus indicating lack of oxygen deficient centers (ODCs) in them. After subsequent fusion of silicon containing (x < 1) films by a scanning focused CO₂ laser beam absorption band centered at 5 eV as well as two luminescence bands centered at blue (3.1 eV) and UV (4.3 eV) wavelengths arise, highlighting the formation of the ODCs. The excitation of unfused SPCVD films by an ArF (6.4 eV) excimer laser yields a luminescence spectrum with two bands typical for the ODCs, but with a faster decay kinetics. Intensities of these bands grow up with samples cooling down to a temperature of 80–60 K. Unfused films excited by the ArF laser also demonstrate luminescence due to recombination of a trapped charge resulted from the excitation of localized electron states of the glass network. In the unfused GeO₂ film luminescence related to a self-trapped exciton (STE) typical for GeO₂ crystals with α-quartz structure is observed. The observed STE luminescence can be indicative of the crystalline fraction availability in the film. Whereas GeO₂ crystals are known as not containing twofold coordinated germanium, a polycrystalline inclusion in the SPCVD GeO₂ film serves as a factor explaining the absence of any spectroscopic manifestation of this type of defects in it even after fusion. On the other hand, lack of STE luminescence in other unfused films with x < 1 testifies truly amorphous state of the matter in them.     

Amorphous tungsten-doped In2O3 transparent conductive films deposited at room temperature from metallic target

Amorphous tungsten-doped In₂O₃ (IWO) films were deposited from a metallic target by dc magnetron sputtering at room temperature. Both oxygen partial pressure and sputtering power have significant effects on the electrical and optical properties of the films. The as-deposited IWO films with the optimum resistivity of 5.8 × 10^?4 Ω·cm and the average optical transmittance of 92.3% from 400 to 700 nm were obtained at a W content of 1 wt%. The average transmittance in the near infrared region (700–2500 nm) is 84.6–92.8% for amorphous IWO prepared under varied oxygen partial pressure. The mobility of the IWO films reaches its highest value of 30.3 cm² V^?1 s^?1 with the carrier concentration of 1.6 × 10²⁰ cm^?3, confirming their potential application as transparent conductive oxide films in various flexible devices.     

Effect of annealing temperature on the optical and electrical properties of aluminum doped ZnO films

Aluminum doped ZnO thin films were successfully deposited on the silicon substrates by spin coating method. The effects of an annealing temperature on electrical and optical properties were investigated for 1.5 at.% of aluminum. Refractive index profile has been obtained for the film annealed at 350 °C using ellipsometry and it has shown minimum refractive index of 1.95 and maximum value of 2.1. Thickness profile shows quite good uniformity of the film having minimum thickness value of 30.1 nm and maximum value of 34.5 nm. Maximum conductivity value obtained was 4.63 Ω^?1-cm^?1 for the film annealed at 350 °C. Maximum carrier density of 2.20 × 10¹⁷ cm^?3 was deduced from the Hall measurement and Fourier transform infrared spectroscopy clearly reveals major peak at 407 cm^?1 in the spectra associated with the ZnO bond.     

Optical characterization of sputtered amorphous aluminum nitride thin films by spectroscopic ellipsometry

We have measured and analyzed the optical constants and polarized optical properties of amorphous aluminum nitride (a-AlN) thin films deposited by RF reactive magnetron sputtering onto silicon(1 1 1) and glass substrates. The optical constants were obtained by analysis of the measured ellipsometric spectra in the wavelength range 300–1400 nm, using the Cauchy–Urbach model. Refractive indices and extinction coefficients of the films were determined to be in the range 1.80–2.11 and 8.6 × 10⁻³–1.5 × 10⁻⁵, respectively. Analysis of the absorption coefficient, in the wavelength range 200–1400 nm, shows the bandgap of a-AlN thin films to be 5.84 ± 0.05 eV. From the angle dependence of the p-polarized reflectivity we deduce a Brewster angle of 61° and a principal angle of 64°. Measurement of the polarized optical properties reveals a high transmissivity and very low absorptivity for a-AlN films in the visible and near infrared regions. X-ray diffraction analysis confirmed the amorphous nature of the films under study.     

Effect of γ-ray irradiation on structure formation and optical constants of thermally evaporated rhodamine B thin films

Rhodamine B (RhB) is polycrystalline in powder form; it becomes nanocrystalline in thermally evaporated films. Gamma-rays induce nanocrystalline to amorphous transformation of RhB films. The optical constants are independent of film thickness. The type of electronic transition for as-deposited and gamma-ray irradiated RhB film is indirect allowed one. The onset and optical energy gap for as-deposited films are 2 and 3.45 eV, respectively. Exposure to different γ-ray doses did not change the transmittance and reflectance behavior of RhB films. γ-ray irradiation decreases onset and optical energy gap, refractive index and dispersion parameters and increase extinction coefficient, oscillator and electric dipole strengths.     

Effect of vacuum annealing on charge transport and trapping in a-Si1 − xCx:H/c-Si heterostructures

The processes of charge transport and trapping in amorphous Si_1 ? xC_x:H films deposited on crystalline p-type Si wafers and annealed in vacuum in the temperature range 300–650 °C have been evaluated. Current–voltage (I–V), capacitance–voltage (C–V) and admittance–temperature (G–T) characteristics were measured in the temperature range 100–350 K. The spectrum of thermal effusion of hydrogen was measured from room temperature up to 1000 °C.C–V characteristics indicate a slight increase of the dielectric constant k and a large hysteresis after annealing at 450 °C. The hysteresis is believed to be associated with mobile hydrogen effusion from the a-SiC:H film, and it is not seen after a 650 °C anneal. From I–V data the maximum rectification ratio is observed after annealing at 450 °C. Variable-range hopping (VRH) conduction at the Fermi level is found to dominate the forward current of the as-deposited structure. After annealing at 450 °C the forward current can be described by space-charge limited (SCL) mechanisms with trapping at shallow levels with energy of about 0.12 eV. After annealing at 650 °C the process of VRH conduction appears again, but the density of hopping sites is much higher than in the as-grown sample. From admittance spectra, the energy position of respective traps in a-SiC:H is at (E_V + 0.45) eV for as-deposited material and it decreases slightly after vacuum annealing. On the basis of these results, an energy band diagram of the a-Si_1 ? xC_x:H/p-Si structure annealed at 450 °C is proposed.     

Growth temperature induced effects in non-polar a-plane GaN on r-plane sapphire substrate by RF-MBE

Non-polar a-plane GaN films were grown on an r-plane sapphire substrate by plasma assisted molecular beam epitaxy (PAMBE). The effect of growth temperature on structural, morphological and optical properties has been studied. The growth of non-polar a-plane (1 1 ?2 0) orientation of the GaN epilayers were confirmed by high resolution X-ray diffraction (HRXRD) study. The X-ray rocking curve (XRC) full width at half maximum of the (1 1 ?2 0) reflection shows in-plane anisotropic behavior and found to decrease with increase in growth temperature. The atomic force micrograph (AFM) shows island-like growth for the film grown at a lower temperature. Surface roughness has been decreased with increase in growth temperature. Room temperature photoluminescence shows near band edge emission at 3.434–3.442 eV. The film grown at 800 °C shows emission at 2.2 eV, which is attributed to yellow luminescence along with near band edge emission.     

Growth of pure ZnO thin films prepared by chemical spray pyrolysis on silicon

Structural, morphological, optical and electrical properties of ZnO thin films prepared by chemical spray pyrolysis from zinc acetate (Zn(CH₃COO)₂ 2H₂O) aqueous solutions, on polished Si(1 0 0), and fused silica substrates for optical characterization, have been studied in terms of deposition time and substrate temperature. The growth of the films present three regimes depending on the substrate temperature, with increasing, constant and decreasing growth rates at lower, middle, and higher-temperature ranges, respectively. Growth rate higher than 15 nm min⁻¹ can be achieved at T_s=543 K. ZnO film morphological and electrical properties have been related to these growth regimes. The films have been characterized by X-ray diffraction, scanning electron microscopy and X-ray photoelectron spectroscopy.     

InOx semiconductor films deposited on glass substrates for transparent electronics

Transparent undoped semiconductor indium oxide films were deposited by radio frequency (rf) plasma enhanced reactive thermal evaporation (rf-PERTE) of indium at low substrate temperature. It was experimentally verified that the variation of rf power density has a strong influence on the electrical and structural properties of the films. The thickness of the InO_x films is of about 100 nm. Results show that InO_x films show an average visible transmittance of about 85% and energy gap of about 2.6 eV. Structural and electrical conductivity measurements show that films are polycrystalline and there exists a linear variation of conductivity logarithm vs reciprocal of temperature. Electrical conductivity variation of 17.6 to 5.8 × 10⁻³ (Ω cm)⁻¹ for films produced at rf power densities ranging from 3.9 to 78.1 mW cm⁻³ was obtained. This controllable semiconductor behavior can therefore satisfy the requirement of a particular application for these type of films.     

Characteristics of p-type nanocrystalline silicon thin films developed for window layer of solar cells

Different rf-power and chamber pressures have been used to deposit boron doped hydrogenated silicon films by the PECVD method. The optoelectronic and structural properties of the silicon films have been investigated. With the increase of power and pressure the crystallinity of the films increases while the absorption decreases. As a very thin p-layer is needed in p–i–n thin film solar cells the variation of properties with film thickness has been studied. The fraction of crystallinity and thus dark conductivity vary also with the thickness of the film. Conductivity as high as 2.46 S cm⁻¹ has been achieved for 400 Å thin film while for 3000 Å thick film it is 21 S cm⁻¹. Characterization of these films by XRD, Raman Spectroscopy, TEM and SEM indicate that the grain size, crystalline volume fraction as well as the surface morphology of p-layers depend on the deposition conditions as well as on the thickness of the film. Optical band gap varies from 2.19 eV to 2.63 eV. The thin p-type crystalline silicon film with high conductivity and wide band gap prepared under high power and pressure is suitable for application as window layer for Silicon thin film solar cells.