Multistimuli responsive grafted poly(ether tert‐amine) (gPEA): Synthesis,characterization and controlled morphology in aqueous solution

Multistimuli responsive grafted poly(ether tert‐amine) (gPEAs), which were comprised of poly(propylene oxide) (PPO) in backbone and poly(ethylene oxide) (PEO) as grafted chain, were successfully synthesized through nucleophilic addition/ring‐opening reaction of commercial poly(propylene glycol) diglycidyl ether and Jeffamine L100. These gPEAs exhibit very sharp response to temperature, pH and ionic strength with tunable cloud point (CP). The CP of gPEA aqueous solution increases with increasing the PEO content or decreasing pH value, varying from 27 to 77 °C. Compared with linear PEA101, gPEA110 of completely grafted structure in aqueous solution exhibits sharper response to temperature with ΔT around 1 °C. The results obtained from TEM and dynamic light scattering reveal that gPEAs are dispersed as uniform sized nano‐micelles in aqueous at room temperature, which can further aggregate into mesoglobules of complex structure at high temperature (>CP). © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 6353–6361, 2009     

Multistimuli responsive micelles based on well‐defined amphiphilic comb poly(ether amine) (acPEA)

A series of well‐defined amphiphilic comb poly (ether amine)s (acPEAs) were successfully synthesized through nucleophilic addition/ring‐opening reaction of commercial available poly(propylene glycol) (PPO) diglycidyl ether and Jeffamine L100, followed by esterification of hydroxyl groups in backbone by alkyl carboxylic acid with different chain length. acPEAs are comprised of hydrophilic short PEO chains and hydrophobic alkyl chains as comb chains, which are grafted on PPO backbone alternately to form well‐defined structure. With the very low critical micelle concentration (CMC) of around 3.0 × 10^?3 g/L, the obtained acPEAs can self‐assemble into stable nanomicelles, whose aggregation is responsive to temperature, pH, and ionic strength with tunable cloud point (CP). The CP of acPEAs' aqueous solution increases with the decrease of the length of graft alkyl chains, the decrease of pH value, and the decrease of ionic strength. A transition behavior in the responsive aggregation of micelles formed by acPEA8 and acPEA10 in aqueous solution, especially at low pH value (<7.0), was observed, which was also revealed by DLS results. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3468–3475, 2010     

Multistimuli responsive amphiphilic graft poly(ether amine): Synthesis,characterization, and self‐assembly in aqueous solution

We reported that multiresponsive amphiphilic graft poly(ether amine)s (agPEAs) comprised of hydrophilic poly(ethylene oxide) (PEO) and hydrophobic octadecyl alkyl chain as side‐chain were prepared through one‐pot synthesis. In aqueous solution, these obtained agPEAs can self‐assemble into stable nanomicelles, whose aggregation can be controlled by temperature, pH, and ionic strength with tunable cloud point (CP). In the presence of these obtained agPEAs, hydrophobic dye Nile red can be dispersed into aqueous solution and hydrophilic dye methyl orange can be dispersed into nonpolar toluene. The agPEAs are expected to be potential in application such as encapsulation and controlled release of drugs, due to their simple synthesis, amphiphilicity, and multistimuli response. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 327–335, 2010     

Poly(ether tert‐amine): A novel family of multiresponsive polymer

A novel multiresponsive poly(ether tert‐amine) (PEA) was synthesized by nucleophilic addition/ring‐opening reaction of commercial poly(ethylene oxide) (PEO), poly(propylene oxide) (PPO), and di‐epoxy and di‐amine monomer. The process of synthesis was very simple and green in ethanol as reactive media. These PEAs exhibit sharp response to temperature, pH, and ionic strength, with adjustable and sharp phase transitions in the range of 27–100 °C. The lower critical solution temperature (LCST) of PEA's aqueous solution presents a linear relationship to the PEO content (y = 35.7 + x), indicating well‐tunable LCST. The concentration of PEA has no obvious effect on LCST. Therefore, PEA will be potential in applications of drug delivery, separation, and biotechnology. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 1292–1297, 2009     

Synthesis of backbone thermo and pH dual‐responsive hyperbranched poly(amine‐ether)s through proton‐transfer polymerization

Stimuli‐responsive hyperbranched polymers have attracted great attention in recent years because of their wide applications in biomedicine. Through proton‐transfer polymerization of triethanolamine and 1,2,7,8‐diepoxyoctane with the help of potassium hydride, a series of novel backbone thermo and pH dual‐responsive hyperbranched poly(amine‐ether)s were prepared successfully in one‐pot. The degrees of branching of the resulting polymers were at 0.40–0.49. Turbidity measurements revealed that hyperbranched poly(amine‐ether)s exhibited thermo and pH dual‐responsive properties in water. Importantly, these responsivities could be readily adjusted by changing the polymer composition as well as the polymer concentration in aqueous solution. Moreover, in vitro evaluation demonstrated that hyperbranched poly(amine‐ether)s showed low cytotoxicity and efficient cell internalization against NIH 3T3 cell lines. These results suggest that these backbone thermo and pH dual‐responsive hyperbranched poly(amine‐ether)s are promising materials for biomedicine. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Enhanced ionic conductivity in PEO/PMMA glassy miscible blends: Role of nano‐confinement of minority component chains

AC impedance spectroscopy was used to investigate the ionic conductivity of solution cast poly(ethylene oxide) (PEO)/poly(methyl methacrylate) (PMMA) blends doped with lithium perchlorate. At low PEO contents (below overlap weight fraction w^*), ionic conductivities are almost low. This could be due to nearly distant PEO chains in blend, which means ion transportation cannot be performed adequately. However, at weight fractions well above w^*, a significant increase in ionic conductivity was observed. This enhanced ionic conductivity mimics the PEO segmental relaxation in rigid PMMA matrix, which can be attributed to the accelerated motions of confined PEO chains in PMMA matrix. At PEO content higher than 20 wt % the conductivity measured at room temperature drops due to crystallization of PEO. However by increasing temperature to temperatures well above the melting point of PEO, a sudden increase of conductivity was observed which was attributed to phase transition from crystalline to amorphous state. The results indicate that some PEO/PMMA blends with well enough PEO content, which are structurally solid, can be considered as an interesting candidate for usage as solid‐state electrolytes in Lithium batteries. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 2065–2071, 2010     

Thermosensitive behavior of poly(ethylene glycol)/poly(2‐(N,N‐dimethylamino)ethyl methacrylate) double hydrophilic block copolymers

The poly(ethylene glycol)/poly(2‐(N,N‐dimethylamino)ethyl methacrylate) (PEG/PDMAEMA) double hydrophilic block copolymers were synthesized by atom transfer radical polymerization using mPEG‐Br or Br‐PEG‐Br as macroinitiators. The narrow molecular weight distribution of PEG/PDMAEMA block copolymers was identified by gel permeation chromatography results. The thermosensitivity of PEG/PDMAEMA block copolymers in aqueous solution was revealed to depend significantly on pH, ionic strength, chain structure, and concentration of the block copolymers. By optimizing these factors, the cloud point temperature of PEG/PDMAEMA block copolymers can be limited within body temperature range (30–37 °C), which suggests that PEG/PDMAEMA block copolymers could be a good candidate for drug delivery systems. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 503–508, 2010     

Novel temperature‐responsive water‐soluble copolymers based on 2‐hydroxyethylacrylate and vinyl butyl ether and their interactions with poly(carboxylic acids)

Novel water‐soluble amphiphilic copolymers have been synthesized by free radical copolymerization of 2‐hydroxyethylacrylate with vinyl butyl ether. In water these copolymers exhibit lower critical solution temperature, which depends on the content of hydrophobic vinyl butyl ether units. The interaction between these copolymers and poly(acrylic acid) or poly(methacrylic acid) in aqueous solutions results in formation of interpolymer complexes stabilized by hydrogen bonds and hydrophobic interactions. An increase in hydrophobicity of the copolymers leads to the enhancement of their complex formation ability with respect to poly(acrylic acid) and poly(methacrylic acid). Poly(methacrylic acid) forms stronger complexes with the copolymers when compared with poly(acrylic acid). The complexes exhibit dual sensitivity to pH‐ and temperature and this property may be easily adjusted regulating the strength of interaction. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 195–204, 2006     

Dendron‐like poly(ε‐benzyloxycarbonyl‐L‐lysine)/linear PEO block copolymers: Synthesis,physical characterization,self‐assembly,and drug‐release behavior

Dendron‐like poly(ε‐benzyloxycarbonyl‐L ‐lysine)/linear poly(ethylene oxide) block copolymers (i.e., Dm‐PZLys‐b‐PEO, m = 0 and 3; Dm are the propargyl focal point poly(amido amine) dendrons having 2^m primary amine groups) were for the first time synthesized by combining ring‐opening polymerization (ROP) of ε‐benzyloxycarbonyl‐L ‐lysine N‐carboxyanhydride (Z‐Lys‐NCA) and click chemistry, where Dm‐PZLys homopolypeptides were click conjugated with azide‐terminated PEO. Their molecular structures and physical properties were characterized in detail by FTIR, ¹H NMR, gel permeation chromatography, differential scanning calorimetry, polarized optical microscopy, and wide angle X‐ray diffraction. Both homopolypeptides and copolymers presented a liquid crystalline phase transition for PZLys block, and the transition was irreversible. Moreover, the degree of crystallinity of PEO block within linear copolymers decreased from 96.2% to 20.4% with increasing PZLys composition, whereas that within dendritic copolymers decreased to zero. The secondary conformation of PZLys progressively changed from β‐sheet to α‐helix with increasing the chain length. These copolymers self‐assembled into spherical nanoparticles in aqueous solution, and the anticancer drug doxorubicin‐loaded nanoparticles gave a similar morphology compared with their blank counterparts. The drug‐loaded nanoparticles showed a triphasic drug‐release profile at aqueous pH 7.4 or 5.5 and 37 °C and sustained a longer drug‐release period for about 2 months. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis of networked polymers with lithium counter cations from a difunctional epoxide containing poly(ethylene glycol) and an epoxide monomer carrying a lithium sulfonate salt moiety

Poly(ethylene glycol)‐based networked polymers that had lithium sulfonate salt structures on the network were prepared by heating a mixture of poly(ethylene glycol) diglycidyl ether (PEGGE), poly(ethylene glycol) bis(3‐aminopropyl) terminated (PEGBA), and an ionic epoxy monomer, lithium 3‐glycidyloxypropanesulfonate (LiGPS). Flexible self‐standing networked polymer films showed high thermal stability, low crystallinity, low glass transition temperature, and good mechanical strength. The materials were ion conductive at room temperature even under a dry condition, although the ionic conductivity was rather low (10^?6 to 10^?5 S/m). The ionic conductivity increased with the increase in temperature to above 1 × 10^?4 S/m at 90 °C. The film samples became swollen by immersing in propylene carbonate (PC) or PC solution of lithium bis(trifluoromethanesulfonyl)imide (LiTFSI). The samples swollen in PC showed higher ionic conductivity (ca.1 × 10^?3 S/m at room temperature), and the samples swollen in LiTFSI/PC showed much higher ionic conductivity (nearly 1 S/m at room temperature). © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3113–3118, 2010     

Preparation of poly(ethylene oxide)‐block‐poly(isoprene) by nitroxide‐mediated free radical polymerization from PEO macroinitiators

Amphiphilic poly(ethylene oxide)‐block‐poly(isoprene) (PEO‐b‐PI) diblock copolymers were prepared by nitroxide‐mediated polymerization of isoprene from alkoxyamine‐terminal poly(ethylene oxide) (PEO). PEO monomethyl ether (M_n ≈ 5200 g/mol) was functionalized by esterification with 2‐bromopropionyl bromide with subsequent copper‐mediated replacement of the terminal bromine with 2,2,5‐trimethyl‐4‐phenyl‐3‐azahexane‐3‐nitroxide. The resulting PEO‐alkoxyamine macroinitiator was used to initiate polymerization of isoprene in bulk and in solution at 125 °C to yield PEO‐b‐PI block copolymers with narrow molecular weight distributions (M_w/M_n ≤ 1.1). Polymerizations were first order in isoprene through 35% conversion. Micellar aggregates of PEO‐b‐PI in aqueous solution were crosslinked by treatment with a water‐soluble redox initiating system, and persistent micellar structures were observed in the dry state by AFM. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 2977–2984, 2005     

Lead‐sensitive PNIPAM microgels modified with crown ether groups

A series of lead‐sensitive poly(N‐isopropylacrylamide) microgels with pendant crown ether groups were prepared. Their cation‐sensitive behaviors were studied by dynamic light scattering. When ionic strength is not controlled, adding salts causes the microgel particles to deswell. However, when the salt effect is ruled out by keeping a constant ionic strength, adding Pb²⁺ results in much larger swelling. The Pb²⁺‐induced swelling was explained by the formation of host–guest complex between Pb²⁺ and the pendant crown ether groups, which increases the hydrophilicity of the polymer and accordingly the degree of swelling. The lead sensitivity of the microgels increases with increasing crown ether content. For the modified microgel with the highest crown ether content, it swells to ～430% of its original volume at [Pb²⁺] = 10 mM. Other cations also increase the swelling degree of the modified microgels. The extent of the cation‐induced swelling mainly depends on their affinity to the pendant crown ether groups. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 4120–4127, 2010     

The Effects of Salts and Ionic Surfactants on the Micellar Structure of Tri‐Block Copolymer PEO‐PPO‐PEO in Aqueous Solution

The micelles of two poly(ethylene oxide)‐poly(propylene oxide)‐poly(ethylene oxide) (PEO‐PPO‐PEO) block copolymers, P123 and F127 (same mol wt of PPO but different % PEO) in aqueous solution in the absence and presence of salts as well as ionic surfactants were mainly examined by dynamic light scattering (DLS). The study is further supported by cloud point and viscosity measurements. The change in cloud point (CP), as well as the size of micelles in aqueous solution in presence of salts obeys the Hofmeister lyotropic series. Addition of both cationic cetylpyridinium chloride (CPC) and anionic sodium dodecylsulfate (SDS) surfactants in the aqueous solution of P123 show initial decrease of micellar size from 20 nm to nearly 7 nm and then increasing with a double relaxation mode, further in the presence of NaCl this double relaxation mode vanishes. The effect of surfactant on F127, which has much bigger hydrophilic part is different than P123 and have no double relaxation. The relaxation time distributions is obtained using the Laplace inversion routine REPES. Two relaxation modes for P123 are explained on the bases of Pluronic rich mixed micelles containing ionic surfactants and the other smaller, predominantly surfactant rich micelles domains.     

Thermoresponsive copolymers of methacrylic acid and poly(ethylene glycol) methyl ether methacrylate

Copolymers of methacrylic acid (MAA) and poly(ethylene glycol) methyl ether methacrylate (PEGMA) were prepared and their cloud points in aqueous solution were studied as a function of comonomer ratio, solution pH, and presence of hydrophobic comonomers. Under acidic conditions, the cloud point falls below 0 °C for copolymers with between 25% to 60% ether content, because of the formation of hydrophobic H‐bonded ether–acid complexes. The cloud point also decreases with solution pH. For equivalent ether to acid ratios, the cloud point decreases with decreasing PEG chain length, because of the presence of a larger number of hydrophobic methyl and methacrylate groups. Similarly, the cloud point decreases upon incorporation of hydrophobic comonomers such as butyl, lauryl, or glycidyl methacrylates. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 6095–6104, 2005     

Novel temperature‐ and pH‐responsive graft copolymers composed of poly(L‐glutamic acid) and poly(N‐isopropylacrylamide)

A series of novel temperature‐ and pH‐responsive graft copolymers, poly(L ‐glutamic acid)‐g‐poly(N‐isopropylacrylamide), were synthesized by coupling amino‐semitelechelic poly(N‐isopropylacrylamide) with N‐hydroxysuccinimide‐activated poly(L ‐glutamic acid). The graft copolymers and their precursors were characterized, by ESI‐FTICR Mass Spectrum, intrinsic viscosity measurements and proton nuclear magnetic resonance (¹H NMR). The phase‐transition and aggregation behaviors of the graft copolymers in aqueous solutions were investigated by the turbidity measurements and dynamic laser scattering. The solution behavior of the copolymers showed dependence on both temperature and pH. The cloud point (CP) of the copolymer solution at pH 5.0–7.4 was slightly higher than that of the solution of the PNIPAM homopolymer because of the hydrophilic nature of the poly(glutamic acid) (PGA) backbone. The CP markedly decreased when the pH was lowered from 5 to 4.2, caused by the decrease in hydrophilicity of the PGA backbone. At a temperature above the lower critical solution temperature of the PNIPAM chain, the copolymers formed amphiphilic core‐shell aggregates at pH 4.5–7.4 and the particle size was reduced with decreasing pH. In contrast, larger hydrophobic aggregates were formed at pH 4.2. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4140–4150, 2008     

Complex,degradable polyester materials via ketoxime ether‐based functionalization: Amphiphilic,multifunctional graft copolymers and their resulting solution‐state aggregates

Degradable, amphiphilic graft copolymers of poly(ε‐caprolactone)‐graft‐poly(ethylene oxide), PCL‐g‐PEO, were synthesized via a grafting onto strategy taking advantage of the ketones presented along the backbone of the statistical copolymer poly(ε‐caprolactone)‐co‐(2‐oxepane‐1,5‐dione), (PCL‐co‐OPD). Through the formation of stable ketoxime ether linkages, 3 kDa PEO grafts and p‐methoxybenzyl side chains were incorporated onto the polyester backbone with a high degree of fidelity and efficiency, as verified by NMR spectroscopies and GPC analysis (90% grafting efficiency in some cases). The resulting block graft copolymers displayed significant thermal differences, specifically a depression in the observed melting transition temperature, T_m, in comparison with the parent PCL and PEO polymers. These amphiphilic block graft copolymers undergo self‐assembly in aqueous solution with the P(CL‐co‐OPD‐co‐(OPD‐g‐PEO)) polymer forming spherical micelles and a P(CL‐co‐OPD‐co‐(OPD‐g‐PEO)‐co‐(OPD‐g‐pMeOBn)) forming cylindrical or rod‐like micelles, as observed by transmission electron microscopy and atomic force microscopy. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3553–3563, 2010     

Synthesis,characterization, and properties of amphiphilic chitosan copolymers with mixed side chains by click chemistry

Novel amphiphilic chitosan copolymers with mixed side chains of poly(ε‐caprolactone) and poly(ethylene oxide) (CS‐g‐PCL/PEO) were successfully synthesized by “graft to” approach via click chemistry. The melting and crystallization behaviors and crystalline morphology of CS‐g‐PCL/PEO copolymers can be adjusted by the alteration of the feed ratio of PCL and PEO segments. CS‐g‐PCL/PEO copolymers revealed crystalline morphology different from that of linear alkynyl PCL and alkynyl PEO due to the influence of brush structure of copolymers and the mutual influence of PCL and PEO segments. The hydrophilicity of the CS copolymers can be improved and adjusted by the alteration of the composition of PCL and PEO segments. Moreover, the CS copolymers can self‐assemble into spherical micelles in aqueous solution. Investigation shows that the size of the CS copolymer micelles increased with the increase of the content of hydrophobic PCL segments in copolymers, which indicated that the micellar behavior of the copolymers can be controlled by the adjustment of the ratio of PCL and PEO segments in copolymer. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3476–3486, 2010     

Unimolecular micelle derived from hyperbranched polyethylenimine with well‐defined hybrid shell of poly(ethylene oxide) and polystyrene: A versatile nanocapsule

The synthesis and properties of a macromolecular nanocapsule derived from hyperbranched polyethylenimine (HPEI) with well‐defined hybrid shell of poly(ethylene oxide) monomethyl ether (mPEO) and polystyrene (PS) are described. HPEI is treated in sequence with 4‐glycidol‐2,2,6,6‐tetrametyl‐piperidin‐1‐oxyl, succinic anhydride, mPEO, leading to a HPEI derivative compatible with nitroxide‐mediated living radical polymerization of styrene, thus a macromolecular nanocapsule, HPEI@PEO/PS, is available with a well‐defined and tunable hybrid shell of PEO and PS. Within certain PEO/PS ratio, the nanocapsule is soluble in a number of organic solvents as well as in water. The nanocapsule exists as three layer onion‐like particle (HPEI@PS@PEO) in water, whereas in chloroform it exists as a hybrid shell particle (HPEI@PEO/PS), and the particles generally exist in the form of unimolecular micelle. In a biphasic water/chloroform mixture, the nanocapsule can transfer anionic, water‐soluble guest from an aqueous phase to the chloroform phase; while when dissolved in water, the nanocapsule can efficiently capture both ionic and apolar solutes. Release of the guest can occur under the stimulus of pH or the switch of medium. This is the first example of a unimolecular micelle that can simultaneously deliver both polar and apolar guests. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 681–691, 2010     

Synthesis,self‐assembly,drug‐release behavior,and cytotoxicity of triblock and pentablock copolymers composed of poly(ε‐caprolactone), poly(L‐lactide), and poly(ethylene glycol)

Biocompatible and biodegradable ABC and ABCBA triblock and pentablock copolymers composed of poly(ε‐caprolactone) (PCL), poly(L ‐lactide) (PLA), and poly(ethylene glycol) (PEO) with controlled molecular weights and low polydispersities were synthesized by a click conjugation between alkyne‐terminated PCL‐b‐PLA and azide‐terminated PEO. Their molecular structures, physicochemical and self‐assembly properties were thoroughly characterized by means of FT‐IR, ¹H‐NMR, gel permeation chromatography, differential scanning calorimetry, wide‐angle X‐ray diffraction, dynamic light scattering, and transmission electron microscopy. These copolymers formed microphase‐separated crystalline materials in solid state, where the crystallization of PCL block was greatly restricted by both PEO and PLA blocks. These copolymers self‐assembled into starlike and flowerlike micelles with a spherical morphology, and the micelles were stable over 27 days in aqueous solution at 37 °C. The doxorubicin (DOX) drug‐loaded nanoparticles showed a bigger size with a similar spherical morphology compared to blank nanoparticles, demonstrating a biphasic drug‐release profile in buffer solution and at 37 °C. Moreover, the DOX‐loaded nanoparticles fabricated from the pentablock copolymer sustained a longer drug‐release period (25 days) at pH 7.4 than those of the triblock copolymer. The blank nanoparticles showed good cell viability, whereas the DOX‐loaded nanoparticles killed fewer cells than free DOX, suggesting a controlled drug‐release effect. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Precise synthesis of end‐functionalized thermosensitive poly(vinyl ether)s by living cationic polymerization

A series of poly(2‐methoxyethyl vinyl ether)s with narrow molecular weight distributions and with perfectly defined end groups of varying hydrophobicities was successfully synthesized by base‐assisting living cationic polymerization. The end group was shown to greatly affect the temperature‐induced phase separation behavior of aqueous solutions (lower critical solution temperature‐type phase separation) or organic solutions (upper critical solution temperature‐type phase separation) of the polymers. The cloud points were also influenced largely by the molecular weight and concentration of the polymer. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012