近年来,全无机卤素钙钛矿CsPbX3(X=Cl,Br,I)因其荧光带宽窄、带隙可调、合成工艺简单以及荧光量子产率(Photoluminescence quantum yield,PLQY)高等优点而被应用于光电器件领域.但相比于PLQY接近于100％的红光与绿光CsPbX3量子点,PLQY低于10％的蓝光量子点光学性能...     

掺杂离子对白色长余辉发光材料Y2O2S:Tb3+, Eu3+,M2+ (M=Mg,Ca, Sr,Ba),Zr4+性能的影响

采用高温固相法制备了白色长余辉发光材料Y₂O₂S:Tb³⁺, Eu³⁺,M²⁺(M=Mg, Ca, Sr, Ba), Zr⁴⁺, 利用X晶体衍射、发光光谱、余辉曲线和热释光曲线等对制备的材料进行表征。结果表明:掺杂离子没有改变样品晶体结构和发射峰的位置,但对其发光强度、余辉时间及陷阱深度有较大的影响。在263 nm紫外光的激发下,469 nm和626 nm的发射分别对应于Eu³⁺的⁵D₂→⁷F₀、⁵D₀→⁷F₂跃迁,544 nm的发射对应于Tb³⁺的⁵D₄→⁷F₅跃迁,主要通过它们的混合产生白光。掺杂不同二价离子样品的余辉性能按Mg²⁺、Sr²⁺、Ca²⁺、Ba²⁺的顺序递减,其中掺杂Mg²⁺的样品,色度坐标为(0.29,0.32),陷阱深度为1.17 eV,余辉时间长达320 s(≥1 mcd/m²),表现出最佳的发光性能。     

甲胺分子的紫外光解离动力学实验研究

在280—287.5 nm区域内,通过实验测定共振增强多光子电离-时间飞行质谱、碎片离子的分质量激发谱以及光强指数等对甲胺分子的光解离通道进行了研究.实验结果证实甲胺分子在单光子能量范围内存在一个电子排斥态,主要的光解离过程为甲胺分子共振吸收1个光子到达该电子排斥态后解离成中性碎片,然后是中性碎片经多光子共振电离形成碎片离子和碎片离子的进一步解离.     

一种LED用红色荧光粉BaZn2(BO3)2：Eu3+的合成与发光性能研究

通过高温固相法制得双峰可调节本征半导体发光BaZn₂（BO₃）₂：Eu³⁺荧光粉,此类荧光粉在300~400 nm的紫外波段有很强的吸收。在375 nm的紫外光激发下,该荧光粉产生了两个宽带的发射峰,分别位于550 nm和615 nm处。并且,在395 nm的紫光激发下,荧光粉会由于Eu³⁺离子的⁵D₀→⁷F₂电偶极跃迁产生一个位于615 nm的强宽发射峰,这表明Eu³⁺离子占据了反演对称中心的位置,取代了BaZn₂（BO₃）₂中部分的Ba²⁺离子。当Eu³⁺的摩尔分数达到10%时,发生浓度猝灭。在不同浓度的Eu³⁺离子的掺杂下,BaZn₂（BO₃）₂：Eu³⁺荧光粉的发光从黄色延伸到红色,实现了荧光粉的色度可调。     

M_2Eu_xLn_(1-x)AlO_5(M=Ca,Sr,Ba,Ln=La,Gd,Lu)红色荧光粉发光性质的研究

用高温固相反应法合成了M_2Eu_xLn_(1-x)AlO_5(M=Ca,Sr,Ba,Ln=La,Lu,Gd)荧光粉,研究了荧光粉的发光性质。在紫外光和近紫外光激发下,样品的发射光谱由Eu~(3+)的5D0→7FJ(J=0,1,2,3,4)特征发射组成。其中Eu3+离子位于590 nm附近的5D0→7F1和位于620 nm附近的5D0→7F2跃迁发射的强度最强。荧光粉的激发光谱都是由O~(2-)-Eu~(3+)电荷迁移带和Eu~(3+)的f-f跃迁构成的。M_2Eu_xLa_(1-x)AlO_5(M=Ca,Sr,Ba)的O2--Eu~(3+)的电荷迁移带的峰位按Ca、Sr、Ba顺序向长波方向移动。研究了用La、Gd和Lu替代M_2Eu_xLn_(1-x)AlO_5中Ln的位置对样品发光的影响。给出了Eu~(3+)浓度对发光强度的影响。分析了M_2Eu_xLn_(1-x)AlO_5和M_2Eu_xLn_(1-x)AlO_5的荧光寿命。     

中等光强纳秒激光电离苯团簇产生多价碳离子的数值模拟和实验研究

飞秒强激光与团簇相互作用产生多价离子的现象已被广泛报道,然而近期多个研究小组发现当功率密度低至1010W/cm2的纳秒激光照射团簇时,同样也观察到了多价离子的存在.虽然可以用"多光子电离引发-逆韧致吸收加热-电子碰撞电离"电离机理对这种现象进行解释,但是缺乏相应的数值模拟.建立了一个简化的数值模型,根据有质动力势Up计算团簇内电子能量,再由Lotz公式计算出相应的电离截面,最后由动力学反应速率方程计算出团簇内多价碳离子随时间的演变.详细分析了团簇尺寸、电子密度等关键参数对多价离子产生的影响.数值模拟结果表明:团簇电离在小于0.7 ns时间尺度内完成,C2+,C3+和C4+多价离子强度达到平衡后,离子相对强度由大到小依次为C2+,C3+,C4+,这与实验结果相一致;多价离子的价态随着团簇尺寸的增加而升高,半径为5.6 nm的苯团簇比半径为3 nm的苯团簇更容易产生高价态的离子,这也与实验结果相一致.     

碱土金属离子对红色长余辉材料Y2O2S：Eu3+, M2+（M=Mg,Ca,Sr,Ba）,Ti4+纳米阵列发光性能的影响

采用溶胶凝胶模板法制备红色长余辉发光材料Y₂O₂S：Eu³⁺,M²⁺（M=Mg,Ca,Sr,Ba）,Ti⁴⁺纳米阵列,利用X射线衍射、扫描电子显微镜和荧光分光光度计、照度计分别研究了不同二价离子掺杂下所合成样品的物相、形貌及发光性能。结果表明：样品排列整齐有序,管径大小统一;不同的二价离子种类没有改变晶体结构和发射峰的位置,但对余辉性能有较大的影响。用324 nm波长光激发样品,由于Eu³⁺的⁵D₀→⁷F₂跃迁,最强的红色发射峰位于626 nm处;不同离子掺杂样品的余辉性能按Ba²⁺、Ca²⁺、Sr²⁺、Mg²⁺的顺序递加,其中二价离子为Mg²⁺ 时,余辉时间长达287 s（≥1 mcd/m²）,表现出最佳的余辉性能。     

ANALYSIS OF F′0+u ION-PAIR STATE OF IODINE

The optical-optical double resonant multiphoton ionization (OODR-MPI) technique and the fluorescent excitation spectroscopy technique have been applied to the study of the F′0⁺_u ion-pair state of iodine. This paper presents OODR-MPI spectrum and fluorescent excitation spectrum of I₂ in the region of 54000-55300cm^-1 by the three-photon resonant, two-photon ionization (1+2+2) and (1+(1+1)+2) processes.     

SrCO3:Mn2+绿色荧光粉的合成和发光性能

采用共沉淀法结合高温固相法,在碳还原气氛下合成了SrCO3:Mn2+绿色荧光粉,用XRD和荧光光谱分别对样品的结构和发光性能进行了表征.XRD结果证实,样品为单一斜方晶系的SrCO3相;荧光光谱检测表明,样品在267nm左右紫外线激发下,产生峰位位于547 nm的明亮绿光,对应于Mn2+的4T1(4G)→6A1(6S)...     

Magnetic properties and composition range of non-stoichiometric m-type hexagonal ferrites prepared by ion exchange

Single crystals of Ba, Sr M-type hexagonal ferrites were prepared by ion exchange in Ba, Sr containing molten salts from single crystals of β″ -ferrites. A fast diffusion of the divalent Ba²⁺, Sr²⁺ is observed leading to a non-stoichiometric M-type ferrite with chemical formula: Ba_1+xFe_10.5Co_0.25O_17+x (0 ≤ x ≤ 0.25). x depending on the exchange reaction time. Saturation magnetization ranges from 19 to 64 emu/g depending on exchange conditions. The Curie temperature is (470 ± 5)°C. An easy axis direction (M_s c) has been determined in all cases. The observed anisotropy is considerably lower than that of M ferrite. The calculated anisotropy constants are, in 10⁶ erg/cm³, K₁ = 0.8 and K₂ = 1.0 at room temperature.     

Optoacoustic study of the infrared multiphoton excitation of ethylene

The optoacoustic effect was used to detect the infrared multiphoton excitation of ethylene as a function of laser wave length and laser energy fluence. The strong absorptions were observed at 949 cm⁻¹, 953 cm⁻¹ and 939 cm⁻¹. The dependence of the energy absorption on the laser energy fluence shows that the absorption at 949 cm⁻¹ is due to the resonance of the single quantum transition whereas the absorptions at 953 cm⁻¹ and 939 cm⁻¹ are due to the resonance of the double quantum transitions. The energy shift of the later transitions was explained in terms of Fermi resonance of the overtones of v₇ and v₈ modes. The onset of highly multiple quantum transitions were observed at high laser energy fluence.     

TWO PHOTONS EXCITED 4d RYDBERG STATE OF AsH3

In this paper, by using resonance enhanced (2+1) multiphoton ionization (REMPI) of AsH₃ and detecting the daughter molecular ions AsH⁺ and As⁺, a long progression discrete structure was obtained from 267 to 291 nm, which obeys the formula ν₀(cm^-1)=68875.3+504.1v′₂+5.26v′²₂. Analysis of the spectrum has revealed that it belongs to 4d Rydberg state transition. Our assignment yields the 4d Rydberg state parameters T_e′=67881.1 cm^-1, ω_e′=495.1 cm^-1 and δ=0.962. Finally the 4d Rydberg state structure of AsH₃ was discussed.     

红色荧光粉MMoO4:Eu3+ (M=Ca,Sr,Ba)的水热合成及光谱性质

采用水热合成法制备了红色荧光粉MMoO4:Eu3+ (M=Ca,Sr,Ba),用XRD、SEM、荧光激发和发射光谱对其物相、形貌以及发光性能进行表征和研究.结果表明,在800℃时可得到MMoO4(M=Ca,Sr,Ba)物相结构,荧光粉粒径小且粒度分布均匀.分别以395 nm的近紫外光和465 nm的蓝光激发样品,MMo...     

(2+2)RESONANCE-ENHANCED MULTIPHOTON IONIZATION-FRAGMENTATION STUDY OF DIMETHYLAMINE

The multiphoton ionization spectra of dimethylamine are given in the 445-470 nm region. A time of flight mass spectrometer was used,and experiment was done under collision free condition. It is found that (2+2) resonance enhanced multiphoton ionization through (n_N,3s) Rydberg state produces parent ions which endure pseudo-α and C—N bond cleavages. The former forms CH₃N⁺H=CH₂ ions,and the latter gives CH₂=N⁺H₂ ions .     

Eu3+．Dy3+,Sm3+掺杂Ca(Sr,Ba)W04的光谱性质

采用共沉淀方法制备了稀土离子Eu3+,Dy3+,Sm3掺杂的Ca(Sr,Ba) WO4发光材料,目的是研究金属阳离子改变对稀土离子发光性质的影响.X射线衍射光谱数据表明,CaWO4、SrWO4、BaWO4都是四方晶系I41/a(88)结构,随着阳离子半径增大,衍射峰向小角移动.不同温度制备的BaWO4样品X射线衍射光谱...     

M2SiO4：Re(M=Mg,Ca,Ba;Re=Ce3+,Tb3+)的发光性能

合成了系列M₂SiO₄:Re(M=Mg,Ca,Ba;Re=Ce³⁺,Tb³⁺)样品,研究了样品在真空紫外区域的激发光谱和发射光谱。从激发谱可以看出:M₂SiO₄:Re(M=Mg,Ca,Ba;Re=Ce³⁺,Tb³⁺)在147,172nm有很强的吸收带。用Mg,Ca完全取代Ba₂SiO₄:Tb³⁺中的Ba,相对应的晶体的晶格参数逐渐增大,晶场的能量逐渐减少,其激发光谱随着碱土离子半径的增加向长波方向移动。在172nm真空紫外光激发下,观察到M₂SiO₄:Re(M=Mg,Ca,Ba;Re=Tb³⁺和M₂SiO₄:Re(M=Mg,Ca,Ba;Re=Ce³⁺,Tb³⁺)特征发射;在真空紫外激发下,随着M₂SiO₄:Re(M=Mg,Ca,Ba;Re=Ce³⁺,Tb³⁺)中Ce³⁺含量的增加,M₂SiO₄:Re的特征发射明显减弱,并分析讨论了相关发光现象的成因。     

长余辉材料Sr2MgSi2O7：Eu2+,Dy3+中稀土离子的发光特性

利用同步辐射光源(德国HASYLAB实验室的SUPERLUMI实验站)和真空紫外激光(157.6nm)对新型蓝光发射长余辉材料Sr₂MgSi₂O₇:Eu²⁺(0.2%),Dy³⁺(8%)进行了光谱研究。在170nm同步辐射光源激发下,观察到对应Eu²⁺:5d-4f跃迁的477nm发射带和对应Dy³⁺:4f-4f跃迁的两组线谱发射,其中只有来自Eu²⁺的5d-4f发射对长余辉光谱有贡献。在157.6nm激光激发下,除了上述发射外,还明显观察到对应Eu³⁺的红色线谱(590,614,626nm)。结合这些光谱特性,对Sr₂MgSi₂O₇:Eu²⁺,Dy³⁺中稀土离子的发光特性以及长余辉发光机理进行了讨论,并提出了Eu²⁺充当空穴陷阱的可能性。     

Ce3+离子激活的SrB4O7的VUV光谱

Ce³⁺只有一个4f电子,具有最简单的4f¹5d⁰基态结构,其激发光谱直接反映了5d轨道的能量状态。由于同一基质晶格相同格位上不同稀土离子受基质晶体场影响相近,所以根据Ce³⁺离子的光谱可以推测和分析其他稀土离子的5d轨道能量,是研究其他稀土离子f-d跃迁的基础。采用高温固相法合成了Ce³⁺离子激活的SrB₄O₇发光体,测定了样品在130~350nm波长范围的激发光谱和相应的发射光谱。指认了VUV激发光谱上Ce³⁺离子的5个4f¹→4f⁰5d¹跃迁激发带,讨论了SrB₄O₇的基质吸收带和Ce³⁺的5d轨道在SrB₄O₇中的晶体场劈裂、5d轨道能级重心及SrB₄O₇:Ce³⁺的发射光谱和Stokes位移。     

近紫外LED用黄色荧光粉Sr3SiO5：Ce3+, Li+的发光特性

采用高温固相法快速降温合成Sr_3-2xSiO₅：xCe³⁺,xLi⁺荧光粉。用X射线衍射仪和荧光分光光度计测试荧光粉的样品结构和发光性能。在1 420 ℃下煅烧得到四方相结构的Sr₃SiO₅：Ce³⁺,Li⁺。样品的激发光谱分布于270~500 nm的波长范围,有两个激发带,峰位分别位于328 nm和410 nm,表明样品可以被近紫外光有效激发。样品的发射光谱分布于420~650 nm,发射峰位于528 nm处。在410 nm左右的近紫外光激发下,宽带发射的峰位于528 nm。Ce³⁺的最佳掺杂量x（Ce³⁺）为0.8%,并且发光强度随掺杂浓度的增加先升高后降低,出现浓度猝灭。根据Dexter能量共振理论,该浓度猝灭的原因是Ce³⁺的电偶极-电偶极相互作用。     

Syntheses of BaCO3 nanostructures by ultrasonic method

BaCO₃ nanostructures were synthesized by the reaction of Ba(CH₃COO)₂ and sodium hydroxide or tetramethylammonium hydroxide (TMAH) by a sonochemical method. Reaction conditions, such as the concentration of the Ba²⁺ ion, aging time and power of the ultrasonic device played important roles in the size, morphology and growth process of the final products. The BaCO₃ nanostructures were characterized by scanning electron microscopy (SEM), X-ray powder diffraction (XRD), and the Infrared spectroscopy (IR).