Crystal structure of a new synthetic Ca,Li pentaborate: CaLi<Subscript>4</Subscript>[B<Subscript>5</Subscript>O<Subscript>8</Subscript>(OH)<Subscript>2</Subscript>]<Subscript>2</Subscript>

When studying the phase formation in the CaO-Li₂O-B₂O₃-H₂O system, a new Ca,Li pentaborate was synthesized under hydrothermal conditions. The structure of a new compound with the crystallochemical formula CaLi₄[B₅O₈(OH)₂]₂ (sp. gr. Pb2n, a = 8.807(7), b = 9.372(7), c = 8.265(6) Å, V = 682.2(9) ų, Z = 2, d_calcd = 2.43 g/cm³, automated SYNTEX-\(P\bar 1\) diffractometer, 2690 reflections, 2θ/θ scan, λMo) is refined up to R_hkl = 0.0557 in the anisotropic approximation of atomic thermal vibrations with allowance for the localized H atoms. The structure of the Ca,Li pentaborate is formed by (010) open boron—oxygen layers formed by two independent [B₅O₈(OH)₂]^3? pentagroups, with each of them being formed by three B tetrahedra and two B triangles. The structure framework consists of the above boron—oxygen layers bound by isolated Li tetrahedra. The Ca cations are localized in the centers of eight-vertex polyhedra located in the [001] channels of the Li,B,O framework. Comparative crystallochemical analysis of the new Ca,Li pentaborate and Li pentaborate of the composition Li₃[B₅O₈(OH)₂]-II showed that the anionic matrices of both compounds are completely identical, whereas some of the cationic positions are different.     

Crystal structure of the new radical cation salt (<Emphasis Type="Italic">DOET</Emphasis>)<Subscript>4</Subscript>[Fe(CN)<Subscript>5</Subscript>NO]<Subscript>1.25</Subscript>(C<Subscript>6</Subscript>H<Subscript>5</Subscript>Cl)<Subscript>0.75</Subscript>

A new radical cation salt based on 4,5-(1,4-dioxanediyl-2,3-dithio)-4′,5′-ethylenedithiotetrathiafulvalene (DOET) with the photochromic anion [Fe(CN)₅NO]^2?, namely, (DOET)₄[Fe(CN)₅ NO]_1.25(C₆H₅Cl)_0.75, is synthesized. Single crystals of this salt are studied using X-ray diffraction [a = 10.398(2) Å, b = 11.168(2) Å, c = 18.499(4) Å, α = 103.14(3)°, β = 92.80(3)°, γ = 106.02(3)°, V = 1996.3(7) ų, space group \(P\bar 1\), and Z = 1]. In the structure, radical cation layers alternate with anion layers along the c axis. The centrosymmetric dimers are formed by DOET radical cations in the donor layer with packing of the β type. Like the vast majority of DOET-based salts, the new salt possesses semiconductor properties.     

Synthesis and an X-ray diffraction study of Rb<Subscript>2</Subscript>[(UO<Subscript>2</Subscript>)<Subscript>2</Subscript>(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>3</Subscript>]

The synthesis and X-ray diffraction study of compound Rb₂[(UO₂)₂(C₂O₄)₃], which crystallizes in the monoclinic crystal system, are performed. The unit cell parameters are as follows: a = 7.9996(6) Å, b = 8.8259(8) Å, c = 11.3220(7) Å, β = 105.394(2)°, and V = 770.7(1) ų; space group P2₁/n, Z = 2, and R ₁ = 0.0271. [(UO₂)₂(C₂O₄)₃]^2? layers belonging to the AK _0.5 ⁰² T ¹¹ crystal chemical group of uranyl complexes (A = UO ₂ ²⁺ , K ⁰² = C₂O ₄ ^2? , and T ¹¹ = C₂O ₄ ^2? ) are uranium-containing structural units of the crystals. The layers are connected with outer-sphere rubidium cations by electrostatic interactions.     

New type of borophosphate anionic radical in the crystal structure of CsAl<Subscript>2</Subscript>BP<Subscript>6</Subscript>O<Subscript>20</Subscript>

The crystal structure of a new borophosphate CsAl₂BP₆O₂₀ obtained by spontaneous crystallization in a multicomponent Cs–Cu–B–P–O system is determined by X-ray diffraction (a = 11.815(2), b = 10.042(2), and c = 26.630(4) Å; space group Pbca, Z = 8, V = 3159.5(10) ų; R₁ = 0.043). A new type of borophosphate anionic 2D radical characterized by the lowest B: P = 1: 6 ratio and containing P₃O₁₀ phosphate groups is found in the compound. A mixed-type anionic framework consisting of vertex-sharing BO₄ and PO₄ tetrahedra and AlO₆ octahedra is distinguished in the structure. Large cesium atoms are located in the channels of the framework. Topological relationships are revealed between the structures of the CsAl₃(P₃O₁₀)₂ and CsAl₂BP₆O₂₀ phases having different cationic compositions. These compounds can be considered quasi-polytypic phases.     

Refined crystal structure of parakeldyshite and the genetic crystal chemistry of zirconium minerals with [Si<Subscript>2</Subscript>O<Subscript>7</Subscript>] diorthogroups

The structure of the mineral parakeldyshite Na_1.93ZrSi₂O_6.93(OH)_0.07 is refined by X-ray diffraction analysis. The main crystallographic data are as follows: space group P \(\overline 1 \), a = 6.617(2) Å, b = 8.813(1) Å, c = 5.426(1) Å, α = 87.26(3)°, β = 85.68(3)°, γ = 71.45(3)°, and R _F = 0.0153. The initial structural model of this mineral is confirmed. Within this model, the structure of parakeldyshite is based on the heteropolyhedral framework formed by [Si₂O₇] diorthogroups, which are linked together through isolated zirconium octahedra. The fundamental difference between the structure under investigation and the initial structural model is associated with the arrangement of the extraframework cations. A comparative crystal chemical analysis of the zirconium silicates with [Si₂O₇] diorthogroups is performed.     

Na(H<Subscript>2</Subscript>O)[Mn(H<Subscript>2</Subscript>O)<Subscript>2</Subscript>(BP<Subscript>2</Subscript>O<Subscript>8</Subscript>)]: Crystal structure refinement

The crystal structure of synthetic manganese sodium borophosphate hydrate Na(H₂O)[Mn(H₂O)₂(BP₂O₈)] was refined based on X-ray diffraction data. The compound was prepared by soft hydrothermal synthesis in the MnCl₂-Na₃PO₄-B₂O₃-H₂O system. The unit-cell parameters are a= 9.602(1) Å, c= 16.037(3) Å, sp. gr. P6₅22, Z= 6, D _x = 2.57 g/cm³. The water molecules were found to be statistically distributed in the channels of the mixed anionic paraframework consisting of (BO₄) and (PO₄) tetrahedra and [MnO₄(H₂O)₂] octahedra. The hydrogen atoms of the water molecules coordinated to the Mn²⁺ cations were located and their positional and thermal parameters were refined. The crystal-chemical features of borophosphates of the general formula A _x M(H₂O)₂(BP₂O₈)(H₂O) are considered.     

Polymorphism of the borophosphate anion in K(Fe,Al)[BP<Subscript>2</Subscript>O<Subscript>8</Subscript>(OH)] and Rb(Al,Fe)[BP<Subscript>2</Subscript>O<Subscript>8</Subscript>(OH)] crystal structures

The crystal structure of two borophosphates, Rb(Al,Fe)[BP₂O₈(OH)] (a = 9.381(6), b = 8.398(5), c = 9.579(6) Å, β = 102.605(10)°, sp. gr. P2₁/c) and K(Fe,Al)[BP₂O₈(OH)] (a = 5.139(2), b = 8.065(4), c = 8.290(4)Å, α = 86.841(8)°, β = 80.346(8)°, γ = 86.622(8)°, sp. gr. P \(\bar 1\)), obtained by hydrothermal synthesis in the AlCl₃: FeCl₃: K₃PO₄(Rb₃PO₄): B₂O₃: H₂O system has been established using X-ray diffraction (Bruker Smart diffractometer, T = 100 K). Hydrogen atoms are located and their coordinates and thermal parameters are refined. It is shown that the polymorphism of the [BP₂O₈(OH)]^4? borophosphate anion has a morphotropic nature and is related to the substitutions both in the cationic part of the structure and in the octahedral position of the anionic mixed framework. The synthesis of new isotypic triclinic compounds under hydrothermal conditions is predicted.     

Crystal structure and microtwinning of monoclinic La<Subscript>3</Subscript>SbZn<Subscript>3</Subscript>Ge<Subscript>2</Subscript>O<Subscript>14</Subscript> crystals of the langasite family

The crystal structure of monoclinic La₃SbZn₃Ge₂O₁₄ crystals from the langasite family is determined by X-ray diffraction analysis [a = 5.202(1) Å, b = 8.312(1) Å, c = 14.394(2) Å, β = 90.02(1)°, sp. gr. A2, Z = 2, and R/R _w = (5.2/4.6)%]. The structure is a derivative of the Ca₃Ga₂Ge₄O₁₄-type structure (a = 8.069 Å, c = 4.967 Å, sp. gr. P321, Z = 1). The crystal studied is a polysynthetic twin with the twin index n = 2, whose monoclinic components are related by pseudomerohedry by a threefold rotation axis of the supergroup P321.     

Growth and crystal structure of binary molybdate CsFe(MoO<Subscript>4</Subscript>)<Subscript>2</Subscript>

CsFe(MoO₄)₂ single crystals have been grown by solution-melt crystallization with a charge-to-solvent ratio of 1: 3 (with Cs₂Mo₃O₁₀ used as a solvent). The crystal structure of this compound has been refined by X-ray diffraction (X8 APEX automatic diffractometer, MoK _α radiation, 356 F(hkl), R = 0.0178). The trigonal unit cell has the following parameters: a = b = 5.6051(2) Å, c = 8.0118(4) Å, V = 217.985(15) ų, Z = 1, ρ_calc = 3.875 g/cm³, and sp. gr. P \(\bar 3\) m1. The structure is composed of alternating layers of FeO₆ octahedra (with MoO₄ tetrahedra attached by sharing vertices) and CsO₁₂ icosahedra.     

Refinement of the crystal structure of rhombohedral KU<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript> as a representative of orthophosphates with the NaZr<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript> structure

The crystal structure of the high-temperature β modification of synthetic orthophosphate KU₂(PO₄)₃ was refined from powder X-ray diffraction data by the Rietveld method: sp. gr. \(R\bar 3c\), the unit-cell parameters a= 9.113(1) Å and c= 24.997(1) Å. The isotropic refinement converged to R _wp = 6.15, R _B = 2.14, R _F = 3.52, and S = 0.42. It was confirmed that β-KU₂(PO₄)₃ belongs to the structure type of sodium zirconium phosphate containing an actinide atom in a sixfold (octahedral) coordination formed by oxygen atoms, which is unusual for orthophosphates. The principal interatomic distances and bond angles in the structure are reported.     

Novel Polyoxovanadate K<Subscript>2</Subscript>ZnV<Subscript>5</Subscript>O<Subscript>14</Subscript>: Crystal Structure and Peculiarities of Crystal Chemistry

A novel structure type has been established as a result of studying a non-merohedral microtwin of polyoxovanadate (K₂ZnV₅O₁₄) by X-ray diffractometry (R = 0.0595). The new compound, synthesized under hydrothermal conditions in the ZnCl₂–K₂CO₃–V₂O₅–H₂O system, is characterized as follows: a = 8.066(5) Å, b = 8.117(5) Å, c = 9.236(5) Å, β = 105.287(5)°, sp. P2₁/m, Z = 2, ρ_calcd = 3.54 g/cm³. Edge-shared five-core “clusters” consisting of vanadium octahedra, between which ZnO₄ tetrahedra (sharing vertices with octahedra) are located, form two-dimensional two-layer anion packets of the (ZnV₅O₁₄)^2– composition, alternating along the c axis with layers of potassium atoms. Structural peculiarities determine the morphology and color of new-phase crystals.     

Molecular structure of [(C<Subscript>5</Subscript>H<Subscript>5</Subscript>)<Subscript>2</Subscript>(C<Subscript>5</Subscript>H<Subscript>4</Subscript>CH<Subscript>3</Subscript>)(C<Subscript>4</Subscript>H<Subscript>8</Subscript>O)Sm]

The mixed tris-cyclopentadienyl tetrahydrofuranato samarium complex bis-(cyclopentadienyl) methylcyclopentadienyl tetrahydrofuranato samarium (I) was synthesized by reaction of (C₅H₅)₂SmCl with methyl cyclopentadienyl sodium in THF. [(C₅H₅)₂(C₅H₄CH₃)(C₄H₈O)Sm] (I) was characterized by elemental analyses—IR spectra and MS spectra. The structure of [(C₅H₅)₂(C₅H₄CH₃)(C₄H₈O)Sm] (I), which has two slightly different independent molecules per asymmetric unit, has been elucidated through complete X-ray analysis. The crystals are monoclinic, with a = 12.791(3) Å, b = 10.467(2) Å, c = 26.108(5) Å, β = 98.22(2)°, and space group Cc, R = 0.0381 for 2103 observed-reflection with I ≥ 3σ(I).     

Crystal structure of the Ca<Subscript>3</Subscript>TaGa<Subscript>3</Subscript>Si<Subscript>2</Subscript>O<Subscript>14</Subscript> compound

The absolute crystal structure of the Ca₃TaGa₃Si₂O₁₄ piezoelectric compound is refined using X-ray diffraction analysis. The unit cell parameters and final R factors are as follows: a = 8.112(1) Å, c = 4.9862(6) Å, space group P321, Z = 1, R = 0.98%, and R _w = 1.42%. It is shown that the configuration of the absolute crystal structure inherited from the seed material determines the positive sense of the optical activity of the crystal under investigation. The structural and acoustical characteristics of the Ca₃TaGa₃Si₂O₁₄ crystals are compared with those of the La₃Ga₅SiO₁₄ crystals.     

Two-dimensional Supramolecular Architecture of Oxamido-bridged Binuclear Copper(II) Complex Cu<Subscript>2</Subscript>(oxen)(NCS)<Subscript>2</Subscript>(DMF)<Subscript>2</Subscript>

An oxamido-bridged binuclear copper(II) complex, Cu₂(oxen)(NCS)₂(DMF)₂ (1) (H₂oxen = N,N′-bis(2-aminoethyl)oxamide, DMF = dimethylformamide), has been synthesized by the reaction of Cu(oxen) · 2H₂O with CuCl₂ · 2H₂O and KSCN in DMF/CH₃OH solution, and characterized by elementary analysis, FT-IR spectra and X-ray single-crystal diffraction. Structural analysis reveals that complex 1 forms a centrosymmetric binuclear molecule in which an oxamido group in the trans conformation bridges two crystallographically equivalent five-coordinate copper(II) ions with Cu–Cu distance of 5.279(2) Å. The complex molecules are assembled into a novel 2D layer through weak Cu?S interactions (d _Cu–S = 3.341(4) Å) and intermolecular hydrogen bonds. Viewed along the crystallographic b axis, layers display an interesting hydrophobic–hydrophilic–hydrophobic sandwich arrangement, with the hydrophobic layers dominated by dipole interaction of DMF molecules.     

Crystal structure of Rb<Subscript>2</Subscript>Mn<Subscript>3</Subscript>(H<Subscript>2</Subscript>O)<Subscript>2</Subscript>[P<Subscript>2</Subscript>O<Subscript>7</Subscript>]<Subscript>2</Subscript>, a new representative of the family of hydrated diphosphates

The crystal structure of Rb₂Mn₃(H₂O)₂[P₂O₇]₂, a new phase obtained in the form of single crystals under hydrothermal conditions in the MnCl₂–Rb₃PO₄–H₂O system, is determined by X-ray diffraction (Xcalibur-S-CCD diffractometer, R = 0.0270): a = 9.374(2), b = 8.367(2), c = 9.437(2) Å, ß = 99.12(2)°, space group P2₁/c, Z = 2, D_x = 3.27 g/cm³. A correlation between the unit-cell parameters and the size of cations forming the crystal structures of isostructural A₂M₃(H₂O)₂[P₂O₇]₂ diphosphates (A = K, NH₄, Rb, or Na; _M = Mn, Fe, Co, or Ni) is revealed. It is shown that, due to the topological similarity, the structures of diphosphates and orthophosphates of the farringtonite structural type can undergo mutual transformations.     

Crystal structure of Rb<Subscript>2</Subscript>[Ti(VO<Subscript>2</Subscript>)<Subscript>3</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>]

The crystal structure of the new compound Rb₂[Ti(VO₂)₃(PO₄)₃] obtained by hydrothermal synthesis in the RbCl-TiPO₄-V₂O₅-B₂O₃-H₂O system (a = 13.604(2) Å, c = 9.386(2) Å, sp. gr. P6cc, Z = 4, ρ_calcd = 3.32 g/cm³) has been studied by X-ray diffraction (Xcalibur-S-CCD diffractometer, R = 0.038). It is shown that the isotypism of Rb₂[Ti(VO₂)₃(PO₄)₃] and Cs₂[Ti(VO₂)₃(PO₄)₃] is caused by the flexibility of a mixed anionic framework composed of phosphorus tetrahedra, vanadium five-vertex polyhedra, and titanium octahedra (bases of the crystal structures of these compounds). The topological correlations between the structures of titanium-vanadyl phosphates and benitoite and beryl silicates are analyzed.     

Structure and some properties of [UO<Subscript>2</Subscript>(C<Subscript>5</Subscript>H<Subscript>12</Subscript>N<Subscript>2</Subscript>O)<Subscript>5</Subscript>](ClO<Subscript>4</Subscript>)<Subscript>2</Subscript>

Compound [UO₂(C₅H₁₂N₂O)₅](ClO₄)₂ is synthesized and characterized by thermogravimetry, IR spectroscopy, and X-ray diffraction. The compound crystallizes in the monoclinic crystal system; a = 15.2985(9) Å, b = 26.9676(15) Å, c = 20.6962(11) Å, β = 100.697(1)°, space group P2₁/c, Z = 8, and R = 0.0445. Discrete [UO₂(C₅H₁₂N₂O)₅]²⁺ groups belonging to the AM ₅ ¹ crystal chemical group of uranyl complexes (A = UO ₂ ²⁺ and M ¹=C₅H₁₂N₂O) are uranium-containing structural units of the crystals.     

Crystal structure refinement of Sr<Subscript>3</Subscript>TaGa<Subscript>3</Subscript>Si<Subscript>2</Subscript>O<Subscript>14</Subscript>

An accurate X-ray diffraction study of Sr₃TaGa₃Si₂O₁₄ (STGS) crystal (a = 8.3023(10) Å, c = 5.0853(2) Å, sp. gr. P321, Z = 1, R/wR = 0.59/0.52%, 4004 independent reflections) is performed. The use of two independent data sets obtained on diffractometers with point and 2D detectors made it possible to determine the model structure characterized by the best reproducibility of parameters. The ordered distribution of atoms over crystallographic positions and the anharmonic character of displacements of all cations and one oxygen atom are established.     

Synthesis and crystal structure of the [Co<Subscript>2</Subscript>(Nicotinamide)<Subscript>4</Subscript>(C<Subscript>4</Subscript>H<Subscript>9</Subscript>COO)<Subscript>4</Subscript>(H<Subscript>2</Subscript>O)] complex

The [Co₂ L ₄(C₄H₉COO)₄(H₂O)] coordination compound of cobalt(II) valerate with nicotinamide (L) is synthesized and studied by IR spectroscopy. The crystal structure of the synthesized compound is determined. The crystals are triclinic, and the unit cell parameters are as follows: a = 10.2759(10) Å, b = 16.3858(10) Å, c = 16.4262(10) Å, α = 100.538(10)°, β = 101.199(10)°, γ = 90.813 (10)°, Z = 2, and space group P \(\bar 1\). The structural units of the crystal are dimeric molecular complexes in which pairs of cobalt atoms are linked by triple bridges formed by oxygen atoms of two bidentately coordinated valerate anions and a water molecule. The octahedral coordination of each cobalt atom is complemented by the pyridine nitrogen atoms of two nicotinamide ligands and the oxygen atom of the monodentate valerate group. The hydrocarbon chains of the valerate anions are disordered over two or three positions each.     

Growth and structure of La<Subscript>3</Subscript>Zr<Subscript>0.5</Subscript>Ga<Subscript>5</Subscript>Si<Subscript>0.5</Subscript>O<Subscript>14</Subscript> crystals

The complete X-ray structure determination of Czochralski grown La₃Zr_0.5Ga₅Si_0.5O₁₄ single crystals with the Ca₃Ga₂Ge₄O₁₄ structure is performed (sp. gr. P321, a = 8.226(1) Å, c = 5.1374(6) Å, Z = 1, Mo K_α1 radiation, 1920 crystallographically independent reflections, R = 0.0166, R_w = 0.0192). The absolute structure is determined. It is shown that possible transition of some of La atoms (～1.2%) from the 3e to 6g position may give rise to the formation of structural defects.