Short-range order and F ion diffusion inside the Pb1 − xAlxF2 + x solid solution Part II: Al NMR investigation and proposal of clustering process

A ²⁷Al nuclear magnetic resonance (NMR) investigation at room temperature of the Pb_{1 − x}Al_xF_{2 + x} (0 ≤ x ≤ 0.12) solid solution and of the ordered Pb₉Al₂F₂₄ phase is carried out. Two different types of aluminium ions are identified and their ratio is determined as a function of x. A clustering process based on the formation of column clusters, more and more extended when x increases, is proposed on the basis of results issued from the ¹⁹F (Part I) and ²⁷Al NMR investigations.     

Nax/2Bi1−x/2MoxV1−xO4 and Bi1−x/3MoxV1−xO4 New Scheelite-related phases

New Scheelite-related solid solutions of the compositions Na_x/2Bi_1−x/2Mo_xV_1−xO₄ (0≤x≤1) and Bi_1−x/3 Mo_xV_1−xO₄(0≤x≤0.2) have been synthesised by the substitution of Na and Mo at the A and B sites respectively of the ABO₄ type ferroelastic BiVO₄. The phases were characterised using chemical analysis, powder X-ray diffraction, scanning electron microscopy, EDAX, and Raman spectroscopy. While almost a continuous solid solution is obtained for the series Na_x/2Bi_1−x/2Mo_xV_1−xO₄, the absence of Na at the A-site results only in a narrow stability region for the other series, Bi_1−x/3 Mo_xV_1−xO₄ where 0≤x≤0.2. Raman spectra of selected samples at room temperature also suggest that vanadium and molybdenum atoms are disordered at the tetrahedral sites.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

Characterization of nonstoichiometric nickel manganite spinels NixMn3−x□3δ/4O4+δ by temperature programmed reduction

Cation deficient spinels Ni_xMn_3−x□_3δ/4O_4+δ (0≤x≤1) have been prepared by thermal decomposition of mixed oxalates Ni_x/3Mn_(3−x)/3(C₂O₄)·nH₂O in air at 623 K. They have been characterised by temperature programmed reduction (TPR) under H₂, the reaction being followed by gravimetric and powder X-ray diffraction measurements. It has been shown that TPR proceeds in several steps. The first steps correspond to the loss of nonstoichiometric oxygen leading to the formation of a stoichiometric oxide. During the following stages the manganese cations are reduced, causing the spinel structure to be destroyed, and the formation of solid solution of NiO in a cubic MnO. Subsequently, Ni²⁺ cations undergo a reduction to metallic nickel, and, finally, a mixture of nonstoichiometric MnO_1−δ and metallic nickel is formed. These oxides contain a high level of vacancies which vary with the nickel content with a maximum of δ≈1 near x=0.6. This nonstoichiometry is ascribed both to the presence of Ni³⁺ and excess of Mn⁴⁺.     

Ionic conduction properties of layer-type oxides NaxMx/2Ti1−x/2O2 (M=Ni, Co; 0.60≤x≤1.0)

Layer-type oxide Na_xM_x/2^IITi_1−x/2^IVO₂ (M=Co, Ni; 0.60≤x≤1.0) has been prepared by solid state reactions. In both series, two structural variants of type -NaFeO₂ (O3) and β-RbScO₂ (P2) have been obtained consecutively as x decreases with a borderline composition around x_c0.7. With the decrease of x, the ionic conductivity has been found to increase up to 8.4×10⁻² S cm⁻¹ at 770 K (Na_0.67Co_0.33Ti_0.67O₂). Compositions of P2 have been found to exhibit the conductivity values two to five times greater than those of O3, primarily due to the larger rectangular threshold available for the diffusion of Na⁺ ions. Such a structural effect has also been considered to depend on the polarizability of alkali ion. HT-XRD and ²³Na-NMR data of Na_0.67Co_0.33Ti_0.67O₂ strongly suggest that the diffusion of Na⁺ ion is deeply related with the local distortion of trigonal prismatic sites, leading to the change of activation energy around 430 K.     

Structural and lithium intercalation studies of Mn(0.5−x)CaxTi2(PO4)3 phases (0≤x≤0.50)

Materials from the Mn_(0.5−x)Ca_xTi₂(PO₄)₃ (0≤x≤0.50) solid solution were obtained by solid-state reaction in air at 1000 °C. Selected compositions were investigated by powder X-ray diffraction analysis, ³¹P nuclear magnetic resonance (NMR) spectroscopy and electrochemical lithium intercalation. The structure of all samples determined by Rietveld analysis is of the Nasicon type with the R space group. Mn²⁺/Ca²⁺ ions occupy only the M1 sites in the Ti₂(PO₄)₃ framework. The divalent cations are ordered in one of two M1 sites, except for the Mn_0.50Ti₂(PO₄)₃ phase, where a small departure from the ideal order is observed by XRD and ³¹P MAS NMR. The electrochemical behaviour of Mn_0.50Ti₂(PO₄)₃ and Mn_(0.5−x)Ca_xTi₂(PO₄)₃ phases was characterised in Li cells. Two Li ions can be inserted without altering the Ti₂(PO₄)₃ framework. In the 0≤y≤2 range, the OCV curves of Li//Li_yMn_0.50Ti₂(PO₄)₃ cells show two main potential plateaus at 2.90 and 2.50–2.30 V. Comparison between the OCV curves of Li//Li_(1+y)Ti₂(PO₄)₃ and Li//Li_yMn_0.50Ti₂(PO₄)₃ shows that the intercalation occurs first in the unoccupied M1 site of Mn_0.50Ti₂(PO₄)₃ at 2.90 V and then, for compositions y>0.50, at the M2 site (2.50–2.30 V voltage range). The effect of calcium substitution in Mn_0.50Ti₂(PO₄)₃ on the lithium intercalation is also discussed from a structural and kinetic viewpoint. In all systems, the lithium intercalation is associated with a redistribution of the divalent cation over all M1 sites. In the case of Mn_0.50Ti₂(PO₄)₃, the stability of Mn²⁺ either in an octahedral or tetrahedral environment facilitates cationic migration.     

Synthesis and characterization of the Aurivillius phases Bi2 − xPbxSr1 − xNdxNb2O9

The n = 2 Aurivillius phase Bi_{2 − x}Pb_xSr_{1 − x}Nd₂O₉ was successfully synthesized as a ceramic material over the whole range of simultaneous, charge compensated substitution x = 0–1.0. Structural investigations were performed by Rietveld refinement applying different space groups Fmmm and A2₁am, and additionally by X-ray absorption spectroscopy (EXAFS) on the Nd L_III-edge, confirming the accommodation of Nd on the atomic sites of Sr, which implies the substitution of Bi³⁺ by the isoelectronic Pb²⁺. The ferroelectric transition temperature T_c = 270 °C of the substituted powders with x = 0.4 and 1.0 is distinctly reduced compared to the unsubstituted sample with T_c = 450 °C. In temperature resolved powder X-ray diffraction patterns no structural phase transition could be detected.     

Oxygen tracer diffusion in La1 − xSrxCoO3

Tracer diffusion of ¹⁸O in dense, polycrystalline La_1−xSr_xCoO₃ for x = 0.1 has been measured in the temperature range 400 to 600 °C and at 500 °C for x = 0.2 at an oxygen partial pressure of 1 × 10⁵ Pa. Depth profiles were obtained by secondary ion mass spectrometry. The diffusion coefficient for La_0.9Sr_0.1CoO₃ is given by D = (17–247) exp[(−232 ± 8 kJ/mole)/RT] cm²/s. This value is several orders of magnitude lower than D extrapolated from the results for x = 0.2 measured in the 700–900 °C temperature range. One possible explanation for the discrepancy is that the two measurements reflect different diffusion paths. As expected, La_0.8Sr_0.2CoO₃ exhibits a higher diffusivity at 500 °C than does La_0.9Sr_0.1CoO₃.     

Neutron diffraction and IR spectroscopy on mechanically alloyed La-substituted PbWO4

Defect structures of the lanthanum-substituted PbWO₄ prepared by mechanical alloying (MA) were investigated by means of powder neutron diffraction and FT-IR, to compare with that of the oxide ion conductive sintered samples. Neutron diffraction revealed that Pb_1−xLa_xWO_4+x/2 prepared by MA possessed the lead site deficiency in the lattice. In addition, it was also found that occupation factors of the lead site were still smaller than the nominal value even for the mechanically alloyed Pb_1−xLa_2x/3WO₄. The vacancy formation at the lead site of the mechanically alloyed Pb_1−xLa_xWO_4+x/2 was also corroborated from the splitting of the absorption band around 800 cm⁻¹ ascribed to the W–O stretching vibration of WO₄ tetrahedron. At the end of this paper, the formation process of the lead site vacancy was discussed in the sintered Pb_1−xLa_xWO_4+x/2 during milling.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Structural and compositional analysis of InBixAsySb(1−x−y) films grown on GaAs(0 0 1) substrates by liquid phase epitaxy

The growth of epitaxial InBi_xAs_ySb_(1−x−y) layers on highly lattice mis-matched semi-insulating GaAs substrates has been successfully achieved via the traditional liquid phase epitaxy. Orientation and single crystalline nature of the film have been confirmed by X-ray diffraction. Scanning electron micrograph shows abrupt interface at micrometer resolution. Surface composition of Bi(x) and As(y) in the InBi_xAs_ySb_(1−x−y) film was measured using energy dispersive X-ray analysis and found to be 2.5 and 10.5 at.%, respectively, and was further confirmed with X-ray photoelectron spectroscopy. Variation of the composition with depth of the film was studied by removing the layers with low current (20 μA) Ar⁺ etching. It was observed that with successive Ar⁺ etching, In/Sb ratio remained the same, while the As/Sb and Bi/Sb ratios changed slightly with etching time. However after about 5 min etching the As/Sb and Bi/Sb ratios reached constant values. The room temperature band gap of InBi_0.025As_0.105Sb_0.870 was found to be in the range of 0.113–0.120 eV. The measured values of mobility and carrier density at room temperature are 3.1×10⁴ cm² V⁻¹ s⁻¹ and 8.07×10¹⁶ cm⁻³, respectively.     

Influence of Nd substitution on the superconducting properties of ceramics in the 2212 system Bi2−wPbwSr2−xCa1−yNdx+yCu2O8+z

In the system Bi_2−wPb_wSr_2−xCa_1−yNd_x+yCu₂O_8+z different fractions of Nd are substituted on either Sr of Ca sites in order to introduce intrinsic insulating pinning centres. It is shown that a Nd concentration around x or y = 0.2 is likewise favourable with an average Nd---Nd distance in the range of the coherence length in the a, b-plane. However, clear evidence of flux pinning is only present for charge compensation with Pb²⁺. A simultaneous substitution of the Bi-based 2212 superconductor with moderate amounts of Nd³⁺ and Pb²⁺ improves the superconducting properties by strengthening the flux pinning forces.     

Lithium insertion to ReO3-type metastable phase in the Nb2O5–WO3 system

Lithium insertion to distorted ReO₃-type metastable solid solution Nb_xW_1−xO_3−x/2 (0≤x<0.25) has been studied by chemical and electrochemical methods. In the course of lithium insertion into tetragonal compounds, transition to a cubic phase was found to occur in the region where values of y (in Li_yNb_xW_1−xO_3−x/2) fall between 0.2 and 0.3, and the phase transition was found to depend on the conditions of the reaction. Changes in OCV and lattice parameters in tetragonal region (y<0.2) were discussed from the viewpoint of the ordering of lithium ions. Also, the component diffusion coefficient of lithium in tetragonal compounds Li_0.1Nb_xW_1−xO_3−x/2 (0≤x≤0.23) was found to increase with niobium content when x≤0.10, and to saturate at 4×10⁻⁹ cm²/s.     

Crystal structure, electrical and magnetic properties of La1 − xSrxCoO3 − y

The crystal structure and properties of La_{1 − x}Sr_xCoO_{3 − y} with strontium contents ranging from x = 0.1 to x = 0.7 have been studied. The lattice parameters were measured as a function of temperature (4.2–400 K) and the crystal structure was found to change from rhombohedral (at low temperatures and values of x) to cubic. While LaCoO₃ is paramagnetic the oxides in the composition range 0.2 < x < 0.6 are soft ferromagnets. The strontium additions are compensated by the formation of Co⁴⁺ (cobalt ions with one positive effective charge, Co_Co^.) and oxygen vacancies (V_o^..). From the results it is concluded that the relative importance of oxygen vacancies increases with increasing temperature and decreasing oxygen activity. As a result the concentration of electronic charge carriers — and the resultant electrical conductivity — decrease with increasing temperature. The defect structure is discussed and it is concluded that defect associations — probably between oxygen vacancies and strontium ions — and formation of microdomains of perovskite-related phases are important aspects of the overall structure of these perovskite phases.     

Estimation of conductivity parameters in Sr1 − xThxF2 + 2x solid solution with fluorite-type structure

Concentration of nn-dipoles, nnn-dipoles and charge carriers as well as parameters related to their reorientation and mobility have been estimated from an analysis of a.c. conductivity data of polycrystalline samples of the Sr_{1 − x}Th_xF_{2 + 2x} solid solution. The molar fraction of charge carriers has been evaluated as a function of composition. Results obtained confirm, in agreement with the clustering process model, that the (F_i)_m ions responsible for long range motions in Sr_{1 − x}Th_xF_{2 + 2x} are interstitial fluoride ions of F type.     

Material design of new lithium ionic conductor, thio-LISICON, in the Li2S–P2S5 system

A new lithium ionic conductor of the thio-LISICON (LIthium SuperIonic CONductor) family was found in the binary Li₂S–P₂S₅ system; the new solid solution with the composition range 0.0≤x≤0.27 in Li_3+5xP_1−xS₄ was synthesized at 700 °C and characterized by X-ray diffraction measurements. Its electrical and electrochemical properties were studied by ac impedance and cyclic voltammetry measurements, respectively. The solid solution member at x=0.065 in Li_3+5xP_1−xS₄ showed the highest conductivity value of 1.5×10⁻⁴ S cm⁻¹ at 27 °C with negligible electronic conductivity and the activation energy of 22 kJ mol⁻¹ which is characteristic of high ionic conduction state. The extra lithium ions in Li₃PS₄ created by partial substitution of P⁵⁺ for Li⁺ led to the large increase in ionic conductivity. In the solid solution range examined, the minimum conductivity was obtained for the compositions, Li₃PS₄ (x=0.0 in Li_3+5xP_1−xS₄) and Li₄P_0.8S₄ (x=0.2 in Li_3+5xP_1−xS₄); this conductivity behavior is similar to other thio-LISICON family with the general formula, Li_xM_1−yM_y′S₄ (M=Si, Ge, and M′=P, Al, Zn, Ga, Sb). Conduction mechanism and the material design concepts are discussed based on the conduction behavior and the structure considerations.     

Oxygen permeability of La2Cu(Co)O4+δ solid solutions

Formation of the La₂Cu_1−xCo_xO_4+δ solid solutions with orthorhombic K₂NiF₄-type structure was found to be in the range of 0≤x≤0.30 at temperatures above 1270 K. Incorporating cobalt into the copper sublattice of lanthanum cuprate leads to increasing oxygen hyperstoichiometry and decreasing electrical conductivity. Thermal expansion coefficients of the La₂Cu_1−xCo_xO_4+δ (x=0.02–0.30) ceramics at 470–1100 K were calculated from the dilatometric data to vary in the range (12.2–13.2)×10⁻⁶ K⁻¹. Studying the dependence of oxygen permeation fluxes through La₂Cu(Co)O_4+δ on the membrane thickness demonstrated that the oxygen transport at the thickness values below 1 mm is limited by both surface exchange rate and bulk ionic conductivity. Oxygen permeability of the La₂Cu_1−xCo_xO_4+δ solid solutions was ascertained to increase with cobalt concentration at x=0.02–0.10 and to decrease with further dopant additions, indicating a participation of interstitial oxygen in the ionic transport.     

Oxygen diffusion and surface exchange in La1−xSrxFe0.8Cr0.2O3−δ (x=0.2, 0.4 and 0.6)

Oxygen tracer diffusion (D*) and surface exchange rate constant (k*) have been measured, using isotopic exchange and depth profiling by secondary ion mass spectrometry (SIMS), in La_1−xSr_xFe_0.8Cr_0.2O_3−δ (x=0.2, 0.4 and 0.6). Measurements were made as a function of temperature (700–1000 °C) and oxygen partial pressure (0.21–10⁻²¹ atm) in dry oxygen, water vapour and water vapour/hydrogen/nitrogen mixtures. At high oxygen activity, D* was found to increase with increasing temperature and Sr content. The activation energies for D* in air are 2.13 eV (x=0.2), 1.53 eV (x=0.4) and 1.21 eV (x=0.6). As the oxygen activity decreases, D* increases as expected qualitatively from the increase in oxygen vacancy concentration. Under strongly reducing conditions, the measured values of D* at 1000 °C range from 10⁻⁸ cm² s⁻¹ for x=0.2 to 10⁻⁷ cm² s⁻¹ for x=0.4 and 0.6. The activation energies determined at constant H₂O/H₂ ratio are 1.21 eV (x=0.2), 1.59 eV (x=0.4) and 0.82 eV (x=0.6).

The surface exchange rate constant of oxygen for the H₂O molecule is similar in magnitude to that for the O₂ molecule and both increase with increasing Sr concentration.     

Effective Ru moment in RuSr2Eu2−xCexCu2O10 from high-temperature magnetic susceptibility

We have made high-temperature (250 K<T<800 K) DC susceptibility measurements in the compounds RuSr₂Eu_2−xCe_xCu₂O₁₀ for x=0.6,0.8, and 1.0 in order to determine the Ru effective magnetic moment. After carefully subtracting all contributions to the magnetic susceptibility except that of the Ru ions, we have been able to fit the Ru susceptibility with a law χ_Ru=χ₀+C_Ru/(T−Θ_Ru). We have found that the Ru effective moment falls between the values expected for Ru⁵⁺ in spin states and . We have also found a dependence of μ_eff(Ru) and Θ_Ru with the Ce content x.     

Thermodynamic analysis of BaxK1 − xBiO3 using the Eliashberg theory

In order to understand the mechanism that gives rise to superconductivity in the ceramic superconductors of the type Ba_xK_{1 − x}BiO₃, we analyze the thermodynamic properties with the use of the Eliashberg equations. For these calculations we used the electron-phonon spectral density function ²(ω)F(ω), calculated by Shirai et al. [1] from first principles for two different K concentrations, x=0.5 and x=0.7.