Relationship between electronic and crystal structure in Cu–Ni–Co–Mn–O spinels: Part A: Temperature-induced structural transformation

Local atomic and crystal structures around Cu and Mn atoms in Mn_1.68Cu_0.6Ni_0.48Co_0.24O₄ spinel samples fabricated by metal–organic decomposition synthesis at different annealing temperatures were investigated by X-ray absorption fine structure analysis. There are two distinct copper cations, Cu¹⁺ and Cu²⁺, both of which maintain tetrahedral coordination. The bond-length distances are Cu¹⁺–O = 2.00 Å and Cu²⁺–O = 1.80 Å. The manganese cations are for the most part octahedral. The spinels prepared at low temperature (600 °C) contain smaller (Mn⁴⁺–O = 1.88 Å) undistorted MnO₆ octahedrons corresponding to Mn⁴⁺ valence, whereas the manganese octahedrons in high-temperature materials (800 °C and higher) were larger and had a pronounced tetragonal distortion pertaining to Mn³⁺ oxidation state (Mn³⁺–O = 1.93 Å and 2.11 Å). By rising the fabrication temperatures, relative concentration of the species of Mn⁴⁺ and Mn³⁺ varies as a result of the reaction represented by Cu¹⁺ + Mn⁴⁺  Cu²⁺ + Mn³⁺, implying irreversible temperature-induced structural transformation. Atomic coordinates in the low-temperature phase are similar to those found in the ideal cubic spinel with oxygen parameter u = 0.27, whereas local environments of the Cu and Mn atom correspond to the tetragonal CuMn₂O₄ phase (space group I4₁/amd). Unlike in CuMn₂O₄, orientation of the lattice distortions is random, however, the long-range cubic spinel structure is retained at all time.     

Composition and electric field effects on the transport properties of Bi doped chalcogenide glasses thin films

The temperature dependence of the DC electrical conductivity σ_DC was measured in the temperature range from 300–500 K. It was found that there are double activation energies, E_σ, for Ge₂₀Se_80−xBi_x (x=0, 2.5 and 5 at%) films, while there is single activation energy for Ge₂₀Se_72.5Bi_7.5. when incorporation of Bi=7.5 at%, the pre-exponential value σ₀ decreases by about six order of magnitude, the activation energy in the extended states E_σ decreases from 0.96 to 0.09 eV. Also the effect of applied electric field was studied and observed that, activation energy in high temperature region increases with increasing electric field; this behavior can be understood assuming that the contribution to the conductivity activation process is due to conduction in the extended states and also due to hopping in the localized states. With the increasing electric field, as former process, which is having high activation energy, becomes more predominant due to the dumping of the carriers in the extended states, the effective activation energy of the system increases, in spite of the fact that the activation energy of the extended states conduction may remain constant. Finally, the electrical data suggests that the addition of bismuth produces localized states near the conduction band edge so that the electrical transport is due to hopping of electrons after being excited into localized states at the conduction band edge.     

Magnetic properties of Sm–Co–B-based nanocomposite magnets

The magnetic properties of nanocomposite melt-spun magnets with composition Sm_16−xCo_68+xB₁₆ (x=0–10, 2 at% interval) and Sm₈Co_92−yB_y (y=10–18, 2 at% interval) have been studied systematically. Several ribbons were fabricated with a wheel speed of 50 m/s, followed by annealing in the temperature range of 700–800°C for 2.5–40 min. XRD results and magnetization versus temperature curves showed that almost all of the samples were composed of the tetragonal Sm₂Co₁₄B and rhombohedral SmCo₁₂B₆ phases which are not magnetically hard at room temperature. However, a relatively high coercivity in the range of 3.5–5.5 kOe has been obtained in these samples. The highest coercivity of 5.5 kOe and a very promising β value of −0.28%/°C were obtained in Sm₈Co₇₄B₁₈ ribbons annealed at 750°C for 5 min. The high coercivities are attributed to the small grain size of the 2 : 14 : 1 phase, in which the large surface areas enhance its effective anisotropy, and make it uniaxial type.     

Investigation of the static and dynamic magnetic properties of CoFe2O4 nanoparticles

We have investigated the magnetic behavior of cobalt ferrite nanoparticles with a mean diameter of 7.2 nm. AC susceptibility of colloidal cobalt ferrite nanoparticles was measured as a function of temperature T from 2 to 300 K under zero external DC field for frequencies ranging from f=10 to 10,000 Hz. A prominent peak appears in both χ′ and χ″ as a function of T. The peak temperature T₂ of χ″ depends on f following the Vogel–Fulcher law. The particles show superparamagnetic behavior at room temperature, with transition to a blocked state at T_B^m94 K in ZFC and 119 K in AC susceptibility measurements, respectively, which depends on the applied field. The saturation magnetization and the coercivity measured at 4.2 K are 27.3 emu/g and 14.7 kOe, respectively. The particle size distribution was determined by fitting a magnetization curve obtained at 295 K assuming a log-normal size distribution. The interparticle interactions are found to influence the energy barriers yielding an enhancement of the estimated magnetic anisotropy, K=6×10⁶ erg/cm³. Mössbauer spectra obtained at higher temperatures show a gradual collapse of the magnetic hyperfine splitting typical for superparamagnetic relaxation. At 4.2 K, the Mössbauer spectrum was fitted with two magnetic subspectra with internal fields H_int of 490, 470 and 515 kOe, corresponding to Fe³⁺ ions in A and B sites.     

Handling the particle size and distribution of Fe3O4 nanoparticles through ball milling

A series of samples consisting of spinel Fe₃O₄ nanoparticles with controlled particle sizes and increasing concentration has been obtained through ‘mild’ ball milling (BM) experiments by using an organic carrier liquid. We have succeeded in producing quite narrow particle size distributions with mean values d7–10 nm by an appropriate choice of the milling time for each concentration. The method proved to be practical to tailor the final particle size without formation of undesirable phases. All samples showed superparamagnetic behavior at room temperature, with transition to a blocked state at T_B10–20 K. The mean value and distribution width of the size distributions for the three samples studied were obtained from M(H) cycles recorded at T>T_B showing good agreement with X-ray diffraction and electron microscopy results. The effect of increasing interparticle interactions was to shift T_B upwards, as inferred from magnetization measurements. Mössbauer spectra at low temperatures showed no evidence of enhanced spin disorder.     

Enhanced dispersion and stability of gold nanoparticles on stoichiometric and reduced TiO2(1 1 0) surface in the presence of molybdenum

Mo, Au and their coadsorbed layers were produced on nearly stoichiometric and oxygen-deficient titania surfaces by physical vapor deposition (PVD) and characterized by low energy ion scattering (LEIS), X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES) and scanning tunnelling microscopy (STM). The behavior of Au/Mo bimetallic layers was studied at different relative metal coverages and sample temperatures.

STM data indicated clearly that the deposition of Au on the Mo-covered stoichiometric TiO₂(1 1 0) surface results in an enhanced dispersion of gold at 300 K. The mean size of the Au nanoparticles formed at 300 K on the Mo-covered TiO₂(1 1 0) was significantly less than on the Mo-free titania surface (2 ± 0.5 nm and 4 ± 1 nm, respectively). Interestingly, the deposition of Mo at 300 K onto the stoichiometric TiO₂(1 1 0) surface covered by Au nanoparticles of 3–4 nm (0.5 ML) also resulted in an increased dispersity of gold. The driving force for the enhanced wetting at 300 K is that the Au–Mo bond energy is larger than the Au–Au bond energy in 3D gold particles formed on stoichiometric titania. In contrast, 2D gold nanoparticles produced on ion-sputtered titania were not disrupted in the presence of Mo at 300 K, indicating a considerable kinetic hindrance for breaking of the strong Au-TiO_x bond.

The annealing of the coadsorbed layer formed on a strongly reduced surface to 740 K did not cause a decrease in the wetting of titania surface by gold. The preserved dispersion of Au at higher temperatures is attributed to the presence of the oxygen-deficient sites of titania, which were retained through the reaction of molybdenum with the substrate. Our results suggest that using a Mo-load to titania, Au nanoparticles can be produced with high dispersion and high thermal stability, which offers the fabrication of an effective Au catalyst.     

Annealing dependence of magnetic properties in nanostructured Sm0.5Y0.5Co5

Nanocrystalline Sm_0.5Y_0.5Co₅ powders with high coercivity H_C and enhanced remanence M_r were prepared by mechanical milling and subsequent annealing. Annealing temperatures T ranging from 973 to 1173 K, and times t ranging from 1 to 5 min were used. X-ray diffraction (XRD) and DC-magnetization measurements were carried out to study the microstructure and magnetic properties of these samples. XRD patterns demonstrate that the average grain size D of the nanocrystalline powders depends on the annealing temperature T and time t: D ranges from 11 nm (for T=973 K and t=1 min) to 93 nm (for T=1173 K and t=5 min). Magnetic measurements performed at room temperature indicate high coercivity values (H_C>955 kA/m), and enhanced remanence (M_r/M_max>0.5) for all samples. A strong annealing-induced grain size dependence of these magnetic properties was found.     

Crystallization kinetics of the Fe40Ni38Mo4B18 amorphous alloy

X-ray diffraction (XRD) and Mössbauer spectroscopy were used to study the annealing of the Fe₄₀Ni₃₈Mo₄B₁₈ amorphous alloy. The samples were isothermally annealed in the 858–878 K temperature range several times. Two crystalline phases were observed in the annealed samples: FeNi₃ and (Fe, Ni, Mo)₂₃B₆. Preliminary results indicate that assuming a linear relationship between the area under the main XRD peak associated with the FeNi₃ phase and its volume fraction, this can be fitted to a Johnson–Mehl–Avrami equation with an exponent n close to 1.0. Mössbauer results show a broad magnetic hyperfine field distribution in as-received samples and, consistent with XRD results, a sextet attributed to precipitates of FeNi₃ (B_hf=29.5 T) for long annealing times.     

Anomalous magnetic behavior of the Co0.53Ga0.47 spin glass above the freezing temperature

We present here the detailed analysis of the magnetic behavior of the Co_0.53Ga_0.47 alloy, especially at temperatures above the freezing temperature T_f = 10 K. Low field static magnetization measurements were performed by using the SQUID magnetometer in the temperature range 5–65 K and magnetic fields up to 100 Oe. The temperature dependence of the field cooled susceptibility π_FC(T) at T > T_f has an anomaly, which is displayed in the double change of the curvature near T_s = 24 K. The data of magnetization M_FC in an external field H lie on a universal curve M_FC(H/T) at temperatures T_f < T < T_s. The plots of π^-1_FC(T) and non-linear magnetic susceptibility π^nl_FC(T^-3) are linear lines in the temperature range T_f−T_s. The strong deviation of π^-1_FC(T) and π^nl_FC(T^-3) from straight line, taking place at T T_s, indicates that T_s is an upper temperature limit of the classical superparamagnetic behavior with the constant cluster moment. The results suggest that such phenomena may be fairly universal for spin glasses.     

Magnetic properties in BaFe12O19 nanoparticles prepared under a magnetic field

It was observed that the nanocrystallites of BaFe₁₂O₁₉ formed at 140°C under a 0.25 T magnetic field exhibited a higher saturation magnetization (6.1 emu/g at room temperature) than that of the sample (1.1 emu/g) obtained under zero magnetic field. Both of the two approaches yielded plain-like particles with an average particle size of 12 nm. However, the Curie temperature (T_c), a direct measuring of the strength of superexchange interaction of Fe³⁺–O²⁻–Fe³⁺, increased from 410°C for the nanoparticles prepared without an external field applied to 452°C for the particles formed under a 0.25 T magnetic field, which indicates that external magnetic fields can improve the occupancy of magnetic ions and then increase the superexchange interaction. This was confirmed by electron paramagnetic resonance and Mössbauer spectrum analysis. The results present in this paper suggest that in addition to oxygen defects, surface non-magnetic layer and a fraction of finer particles in the superparamagnetic range, cation vacancies should be responsible for the decreasing of saturation magnetization in magnetic nanoparticles.     

Effect of Cu doping in MgB2 superconductor at various processing temperatures

The effects of Cu doping in MgB₂ superconductor has been studied at different processing temperatures. The polycrystalline samples of Mg_1−xCu_xB₂ with x = 0.05 were synthesized through the in-situ solid sate reaction method in argon atmosphere at different temperature range between 800–900 °C. The samples were characterized through X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and low temperature R–T measurement techniques for the phase verification, microstructure and superconducting transition temperature, respectively. The XRD patterns of Mg_1−xCu_xB₂ (x = 0.05) do not exhibit any impurity traces of MgB₄ or MgB₆ and they show the sharp transition in the samples prepared at 850 °C. The onset transition temperature of the prepared samples is around 39 K, which is almost the same as that for the pure MgB₂. This indicates that Cu doping in MgB₂ does not affect the transition temperature. The SEM micrograph of Mg_0.95Cu_0.05B₂ has shown that the sample is dense with grain size smaller than 1 μm.     

Magnetic properties of YCo5 (70%wt)+Y2Co17 (30%wt) nanocomposite powders at low temperatures

Nanostructured YCo₅ (70%wt)+Y₂Co₁₇ (30%wt) composite powders were prepared by mechanical milling and subsequent annealing at 1073 K for 1.5 min. The average grain size D of the YCo₅ and Y₂Co₁₇ phases, obtained from XRD data, was 14 and 12 nm, respectively. The temperature dependence of the magnetic properties was studied by DC magnetization measurements at temperatures T ranging from 3 to 300 K. Hysteresis loops (H_max=70 kOe) show that both the coercivity H_C and the squareness σ_r/σ_max are temperature-dependent. The coercivity increases from 12 kOe at room temperature to 18 kOe at T=3 K. The observed enhanced remanence (σ_r/σ_max>0.5) indicates that a strong exchange coupling is present at all temperatures used in this study. The maximum magnetization σ_max changes little with temperature and has a value of about 70% of the effective saturation magnetization of the title compound.     

Influence of N2:(N2 + Ar) flow ratio and substrate temperature on the properties of zirconium nitride films prepared by reactive dc magnetron sputtering

Preferred crystal orientation and low electrical resistivity are required for ZrN_x films applied in electronic devices. In this paper, effects of N₂:(N₂+Ar) flow ratio (F(N₂)) and substrate temperature on the properties of the films deposited on glass substrate by reactive dc sputtering are investigated. In a wide range of F(N₂) (4–24%), the films show fcc NaCl structure. While for F(N₂) in the ranges of 5–12, 12–24 and >24%, the films show (1 1 1)/(2 0 0), (1 1 1) only and amorphous structures, respectively. The electrical resistivity increases with F(N₂) from 5 to 24%, and can be controlled to some extent by changing the substrate temperature.     

The effect of annealing under hydrostatic pressure on the visible photoluminescence from si-ion implanted SiO2 films

We have studied the influence of the hydrostatic pressure during annealing on the intensity of the visible photoluminescence (PL) from thermally grown SiO₂ films irradiated with Si⁺ ions. Post-implantation anneals have been carried out in an Ar ambient at temperatures T_a of 400°C and 450°C for 10 h and 1130°C for 5 h at hydrostatic pressures of 1 bar–15 kbar. It has been found that the intensity of the 360, 460 and 600 nm PL peaks increases with rising hydrostatic pressure during low-temperature annealing. The intensity of the short-wavelength PL under conditions of hydrostatic pressure continues to rise even at T_a=1130°C. Increasing T_a leads to a shift in the PL spectra towards the ultraviolet range. The results obtained have been interpreted in terms of enhanced, pressure-mediated formation of ≡Si–Si≡ centres and small Si clusters within metastable regions of the ion-implanted SiO₂.     

Structural and electrical properties of crystalline (1−x)Ta2O5−xTiO2 thin films fabricated by metalorganic decomposition

Polycrystalline (1−x)Ta₂O₅−xTiO₂ thin films were formed on Si by metalorganic decomposition (MOD) and annealed at various temperatures. As-deposited films were in the amorphous state and were completely transformed to crystalline after annealing above 600 °C. During crystallization, a thin interfacial SiO₂ layer was formed at the (1−x)Ta₂O₅−xTiO₂/Si interface. Thin films with 0.92Ta₂O₅–0.08TiO₂ composition exhibited superior insulating properties. The measured dielectric constant and dissipation factor at 1 MHz were 9 and 0.015, respectively, for films annealed at 900 °C. The interface trap density was 2.5×10¹¹ cm⁻² eV⁻¹, and flatband voltage was −0.38 V. A charge storage density of 22.8 fC/μm² was obtained at an applied electric field of 3 MV/cm. The leakage current density was lower than 4×10⁻⁹ A/cm² up to an applied electric field of 6 MV/cm.     

Aspects of “low field” magnetotransport in epitaxial thin films of the ferromagnetic metallic oxide SrRuO3

Epitaxial thin films of the conductive ferromagnetic oxide SrRuO₃ were grown on an (0 0 1) SrTiO₃ (STO) substrate by using DC sputtering technique. The magnetic and magnetoresistive properties of the films were measured by applying the magnetic field both perpendicular (out-of-plane) and parallel (in-plane) to the film plane and ever maintaining the direction of the applied field perpendicular to that of the transport current. The films grown on an (0 0 1) STO substrate showed identical magnetization properties in two orthogonal crystallographic directions of the substrate, [1 0 0]_S and [0 0 1]_S (in-plane and out-of-plane geometry), which suggests the presence of a multi domain structure within the plane of the film. For such samples, no anisotropic field (hard axis) along de [0 0 1]s direction, i.e., perpendicular to the film-plane could be detected. Nevertheless, a distinguishable temperature dependent out-of-plane anisotropic magnetoresistance (MR) along with strong temperature dependent low field hysteretic MR(H) behavior was detected for the studied films. A negative MR ratio MR(T)=[ρ(μ₀H=9 T; T)−ρ( μ₀H=0 T; T)]/ρ( μ₀H=0 T; T) on the order of a few percent, with maximums of 6% and 4% (right at the Curie temperature, T_C 160 K) was calculated for an in-plane and out-of plane measuring geometry, respectively. In addition there is an equally strong MR effect at low temperatures, which might be related to the temperature dependence of the magnetocrystalline anisotropy together with a magnetization rotation. Both the MR(T) behavior and the achieved values (except for T<30 K) are similar to those obtained on SrRuO₃ films grown on 2° miscut (0 0 1) STO substrates with the current parallel to the field and parallel to the direction, which was identified as the easier axis for magnetization.     

Defect versus nanocrystal luminescence emitted from room temperature and hot-implanted SiO2 layers

Silicon nanocrystals have been synthesized in SiO₂ matrix using Si ion implantation. Si ions were implanted into 300-nm-thick SiO₂ films grown on crystalline Si at energies of 30–55 keV, and with doses of 5×10¹⁵, 3×10¹⁶, and 1×10¹⁷ cm⁻². Implanted samples were subsequently annealed in an N₂ ambient at 500–1100°C during various periods. Photoluminescence spectra for the sample implanted with 1×10¹⁷ cm⁻² at 55 keV show that red luminescence (750 nm) related to Si-nanocrystals clearly increases with annealing temperature and time in intensity, and that weak orange luminescence (600 nm) is observed after annealing at low temperatures of 500°C and 800°C. The luminescence around 600 nm becomes very intense when a thin SiO₂ sample is implanted at a substrate temperature of 400°C with an energy of 30 keV and a low dose of 5×10¹⁵ cm⁻². It vanishes after annealing at 800°C for 30 min. We conclude that this luminescence observed around 600 nm is caused by some radiative defects formed in Si-implanted SiO₂.     

Dielectric and modulus behavior of LiFe1/2Ni1/2VO4 ceramics

The polycrystalline sample of LiFe_1/2Ni_1/2VO₄ was prepared by a standard solid-state reaction technique and confirmed by X-ray diffractometry. LiFe_1/2Ni_1/2VO₄ has orthorhombic crystal structure whose dielectric and electric modulus properties were studied over a wide frequency range (100 Hz–1 MHz) at different temperatures (296–623 K) using a complex impedance spectroscopy (CIS) technique. The frequency and temperature dependence of dielectric constant (ε_r) and tangent loss (tan δ) of LiFe_1/2Ni_1/2VO₄ are studied. The variation of ε_r as a function frequency at different temperatures exhibits a dispersive behavior at low frequencies. The variation of the ε_r as a function of temperature at different frequencies shows the dielectric anomaly in ε_r at 498 K with maximum value of dielectric constant 274.49 and 96.86 at 100 kHz and 1 MHz, respectively. Modulus analysis was carried out to understand the mechanism of the electrical transport process, which indicates the non-exponential type of conductivity relaxation in the material. The activation energy calculated from electric modulus spectra is 0.38 eV.     

Excess molar heat capacity of isobutyric acid–water binary liquid mixtures near and far away from the critical temperature

The heat capacity of the liquid–liquid mixture isobutyric acid–water has been measured for the first time near and far away from its critical point using an adiabatic calorimeter. The measurements were performed at atmospheric pressure, in the one phase region as a function of three temperatures: (1) T − T_C = 0.055 °C, (2) T − T_C = 3.055 °C, (3) T − T_C = 8.055 °C and of the composition X in acid (IA). The heat capacity C_p decreases rapidly when X increases at the used temperatures. Near the critical composition, C_p is not affected by the correlation of the concentration fluctuations.

The molar excess heat capacity of the system under investigation was analysed along the phase diagram and considered as a structural transformation effect.     

Temperature dependence of ESR anisotropy in La7/8Sr1/8MnO3

We report X-ray diffraction, DC-susceptibility, electron spin resonance (ESR), and dilatometry measurements carried out on an La_7/8Sr_1/8MnO₃ single crystal. Thermal expansion was measured along different crystallographic axes using a three-terminal dilatometer. The sharp anomalies observed in the temperature dependence of Δl/l allowed us to locate the Jahn–Teller transition at T_JT=285(1) K. ESR experiments were carried out in the paramagnetic regime from 220 to 570 K, at 9.4 GHz. We measured the ESR line width ΔH_pp(T) with the magnetic field parallel to the crystallographic directions [1 0 0] and [0 0 1], referred to the orthorhombic (Pbnm) axes. We correlate the temperature dependence of ΔH_pp with the structural changes of the lattice.