Activation of magnesia by hydrogen spillover

Magnesia aerogel activated by hydrogen spillover at 430 °C or at 200 °C becomes a catalyst for the hydrogenation of ethylene. This catalytic activity, observed already at 50 °C, is further enhanced by a treatment in oxygen at 430 °C.

---

, 430 200°C, . 50°C 430°C.

     

Kinetics of Cr(VI) and V(V) oxidation of trans-stilbene and indene

Title reactions are acid catalyzed and strongly dependent on the permittivity of the medium. With Cr(VI) indene reacts faster than trans-stilbene, but with V(V), trans-stilbene reacts faster than indene. The mechanism is discussed.

---

. Cr(VI) , -, V(V) - , . , .

     

Nonisothermal kinetics of zinc oxide nonstoichiometrization

The results obtained by studying zinc oxide non-stoichiometrization are presented. The kinetic parameters values under nonisothermal conditions were calculated too. Both the nonstoichiometric zinc oxide composition and the kinetic parameter values are depending on the generating substances.

---

Zusammenfassung Die Ergebnisse der Untersuchungen der Nichtstöchiometrisierung von Zinkoxid werden vorgeführt.Die Werte der kinetischen Parameter unter nicht-isothermen Bedingungen wurden eben falls berechnet.Sowohl die nichtstöchiometrische Zusammensetzung des Zinkoxids als auch die Werte der kinetischen Parameter hängen von der das Phänomen auslösenden Substanz ab.

---

Résumé On présente les résultats d'une étude sur la formation d'oxyde de zinc non-stchiométrique. Les valeurs des paramètres cinétiques en conditions non-isothermes sont égale ment calculées. La composition de l'oxyde de zinc non-stchiométrique ainsi que les valeurs des paramètres cinétiques dépendent du composé de départ.

---

, , . .

     

Hydrogenolysis of n-butane on Ni-Pd/SiO2 catalysts

Supported Ni-Pd/SiO₂ catalysts of different Ni and Pd composition were studied in n-butane hydrogenolysis. The reaction rate, selectivity towards methane, ethane and propane were determined. On the basis of these data the relationship between the size and composition of the active center and the possibility of surface segregation of one of the components is discussed.

---

Ni-Pd/SiO₂ Ni Pd -. , . .

     

Some remarks about butene-1 transformations on NaHY zeolite

Comments are given on the paper Alternative Interpretation of Infrared Spectra of the Zeolite NaHY+Butene-1 System of Forster and Seelemann /2/. Our previous paper /1/ was partly revised but the usefulness of comprehensive studies by infrared and temperature-programmed desorption methods has been emphasized.

---

: NaHY+-1. [2]. [1] , - .

     

On the mechanism of propylene oxidation over gallium-molybdenum oxide catalysts

The products of selective oxidation are shown to be formed via a stepwise mechanism with participation of surface allylic complexes. A successive transformation of -allyl to -allyl and further to acrolein is possible. The products of complete oxidation may be formed through surface carbonate-carboxylate complexes via either a stepwise mechanism involving the catalyst's oxygen, or a concerted mechanism with the participation of molecular oxygen.

---

, . - -, . - , .

     

Effect of carbon support on the hydrogen sorption of platinum

The hydrogen sorption of carbon-supported platinum catalysts, studied by the potentiodynamic method, differs significantly from that of unsupported platinum. The difference depends on the preparation method and on the nature of the support. Possible explanations are suggested as (i) some kind of interaction between metal and support atoms during impregnation, (ii) high dispersity (amorphous structure) and (iii) hydrogen spillover onto the carbon support.

---

Pt/C, . . (I) , (II) ( ), (III) .

     

Differential scanning calorimetry of chloroquine sulphate exposed to sun,heat and ultraviolet radiation

Chloroquine sulphate, like the phosphate, is an antimalarial formulation widely used in the tropics. The stability of such formulations is therefore of interest in the combat against malaria. A DSC study has been made of the effects of exposure to the sun, heat and UV radiation on the stability of chloroquine sulphate, similarly as performed earlier for chloroquine phosphate. When freshly recrystallized from a water-acetone mixture, chloroquine sulphate exhibits two endothermic peaks, at 169.4° and 204.7°, for the expulsion of crystal water (one molecule) and for the melting process, respectively. The exposure of chloroquine sulphate to the sun, heat and UV radiation leads to splitting of the peak for melting.

---

Zusammenfassung Chloroquine-Sulfat ist ebenso wie das entsprechende Phosphatderivat ein in den Tropen weitverbreitet angewandtes Antimalaria-Präparat. Die Stabilität dieses Präparates hat damit Bedeutung für die Malariabekämpfung. Die vorliegende Arbeit ist eine Erweiterung einer Untersuchung über den Effekt der Einwirkung.von Sonne, Hitze und UV-Strahlen auf die Stabilität von Chloroquine-Phosphat auf Chloroquine-Sulfat. Aus Wasser-Aceton-Mischungen frisch kristallisiertes Chloroquine-Sulfat zeigt zwei endotherme Peaks bei 169,4 und 204,7 °C, die durch Abgabe von Kristallwasser (ein Molekül) bzw. durch den Schmelzvorgang bedingt sind. Wird Chloroquine-Sulfat der Sonne, Wärme oder UV-Licht ausgesetzt, so wird der dem Schmelzvorgang zuzuscheibende Peak aufgespalten.

---

, -, , . . , . , , 169,4 204,7°, , , . , .

     

Composition and properties of the cobalt-molybdenum oxide system

The physico-chemical and catalytic properties of the Co–Mo oxide system have been studied in a wide range of various molybdenum to cobalt ratios. The activity increase at 1.21Mo:Co?11 is assumed to be due to the formation of solid solutions.

---

- Co–Mo- . , - 1,21Mo:Co>11 .

     

Interaction of super-finely dispersed Al powders with water

Interaction of super-finely dispersed Al powders (SFDP) with water is characterized by the presence of a considerable section on the kinetic curves, where the conversion rate is maximum and its degree is as high as =0.5–0.7. It is suggested that the essential factor accounting for the conversion kinetics and the phase composition of its products is the self-heating of Al particles.

---

() , , () 0,5–0,7. , .

     

Effect of CO2 on O2 photo-adsorption on anatase

The presence of CO₂ on TiO₂ affects the process of oxygen photo-adsorption depending on the hydroxylation state of the surface. In dehydroxylated samples CO₂ blocks the formation of O ₃ ^– and O ₂ ^– . On H₂O₂/TiO₂ samples pretreated in the range of 150–200°C it leads to CO₂–O ₂ ^– species.

---

, Cu(II). . .

     

Formation of N-butane in the pyrolysis of ethylene [1]

Yields of n-C₄H₁₀ have been measured from the flow pyrolysis of C₂H₄ at 897 (±7) K. From 77 to 720 Torr the order of n-C₄H₁₀ formation was found to be 2.0±0.3 The rate constant for the reaction, was estimated to be 2.4(±0.6)×10^–4l mol^–1s^–1.

---

-C₄H₁₀ C₂H₄ 897 (±7) . -C₄H₁₀ 77 720 2.0±0.3. 2C₂H₄C₂H₃+C₂H₅ 2,4 (±0,6)×10^{–4 –1–1}.

     

Enthalpies de melange du systeme antimoine-tellure a 909,30 K, 911,85 K et 917,95 K

Thermodynamical data on Sb-Te system at 909,30 K, 911,85 K and 917,95 K. The integral molar enthalpies of formation of liquid Sb-Te alloys were measured at three temperatures by drop calorimetry.Partial molar enthalpies of formation of these alloys, referring to the pure liquid constituants, and enthalpie of formation at 298 K of the compound Sb₄₀₅Te₅₉₅ were deduced.

---

Zusammenfassung Thermodynamische Daten, des Systemes Sb-Te bei 909,30, 911,85 und 917,95 K. Mittels Drop-Kalorimetrie wurden die integralen molaren Bildungsenthalpien von flüssigen Sb-Te Legierungen bei drei verschiedenen Temperaturen gemessen. Die partiellen molaren Bildungsenthalpien dieser Legierungen, bezogen auf die reinen flüssigen Komponenten sowie die Bildungsenthalpie der Verbindung Sb_0.405Te_0.595 bei 298 K wurden abgeleitet.

---

Sb-Te 909,30; 911,85 917,95 . , Sb_0.4050.595 298 .

     

CO/H2 and CO2/H2 reactions with amorphous carbon-metal catalysts

By metal impregnation of selected naturally occurring organic materials followed by controlled carbonization, metal semicoke catalysts can be readily prepared. These catalysts have been tested in the synthesis of hydrocarbons and alcohols from CO/H₂ and CO₂/H₂ mixtures. Fe and Co preparations have been used. Relatively high temperatures are required when using these catalysts, which are quite active for synthesis using CO₂ and H₂. The pressure (5150 kPa) is very favorable both for the synthesis of liquid hydrocarbons (C₅–C₃₀) and alcohols (C₁–C₅).

---

. CO/H₂ CO₂/H₂. Fe Co. , CO₂ H₂. 5150 ) (C₅–C₃₀) (C₁–C₅).

     

Thermoanalytical study of the solid state reaction between hydrated ZnO and Fe2O3

The hydrated oxides which are formed by the addition of ammonium bi-carbonate to a solution of Zn(NO₃)₂ and Fe(NO₃)₃, and drying the precipitates at 110° are zinc hydroxy carbonate(I) and iron(III) oxide gel(II), respectively. A new, derived derivative thermogravimetric curve along with conventional DTA and DTG methods have been used to study the reaction between (I) and (II) in two components system.A mixture of (I) and (II) subjected to grinding yields about 16% zinc ferrite precursor. In a sample prepared by coprecipitation from the mixed nitrate solution and drying at 110°, nearly 70% precursor is formed. The formation of zinc ferrite spinel reported to take place at low temperature in such cases appears to be related with the formation of the precursor, and reactivity and phase transformation temperature in Fe₂O₃.

---

Zusammenfassung Die durch Zugabe von Ammoniumbicarbonat zu einer Lösung von Zn(NO₃)₂ und Fe(NO₃)₃ und Trocknung des Niederschlags bei 110° gebildeten hydratisierten Oxide sind Zinkhydroxycarbonat (I) bzw. Eisen(III)oxidgel (II). Eine neue derivierte derivative thermogravimetrische Kurve wurde gemeinsam mit den konventionellen DTA und DTG Methoden zum Studium der Reaktion zwischen (I) und (II) in Zweikomponentensystemen eingesetzt.Das Gemisch von (I) und (II) ergibt beim Mahlen etwa 16% Zinkferrit »Prekursor«. In einer durch Mitfällung der gemischten Nitrate und Trocknung bei 110° erhaltenen Probe wurde fast 70 % »Prekursor« gebildet. Die Bildung von Zinkferritspinell, über dessen Entstehung in solchen Fällen bei niedrigen Temperaturen berichtet wird, scheint mit der Bildung des »Prekursors« verbunden zu sein, sowie mit der Reaktivität und der Phasenübergangstemperatur in Fe₂O₃.

---

Résumé Les oxydes hydratés formés lors de l'addition du bicarbonate d'ammonium à une solution de Zn(NO₃)₂ et de Fe(NO₃)₂ suivie du séchage du précipité à 110°, sont l'hydroxy-carbonate de zinc(I) et le gel de l'oxyde de fer(III) (II). On a utilisé une nouvelle technique de thermogravimétrie en dérivation, ainsi que les méthodes d'ATD et TGD conventionnelles, pour étudier la réaction entre (I) et (II) dans le système à deux composants.Un mélange de (I) et de (II), soumis au broyage, donne environ 16 p.c. de ferrite de zinc «précurseur», tandis qu'un échantillon préparé par coprécipitation à partir de la solution des nitrates mixtes et séchage à 110°, en donne environ 70 p.c.La formation du spinelle de ferrite de zinc décrite comme ayant lieu, dans des cas similaires, à des températures faibles, paraît être en rapport avec la formation du «précurseur» ainsi qu'avec la réactivité et la température de la transformation de phase de Fe₂O₃.

---

Zn(NO₃)₂ Fe(NO₃)₃, , 110°, , , (I) (II). , , I II . I II, , 16% , . , 110°, 70% , . « » , Fe₂O₃.

     

Effect of the medium on the oxidation of aliphatic monocarboxylic acids

Oxidation rates and k₂/k₆ ratios are given for some acids from propionic to lauric. The k₂/k₆ ratio is shown to be influenced by the electrostatic effect of the solvent. A linear dependence between the isodielectric values of k₂/k₆ and the number of methylene groups in the acid molecules is described.

---

k₂/k₆ . k₂/k₆ k₂/k₆ .

     

The thermal decomposition of thaumasite from Mothae kimberlite pipe,Lesotho, Southern Africa

The endothermic decomposition of thaumasite from Mothae which has been investigated by DTA and TG shows a peak temperature of 138–203°, and reaction orders of 0.45–1.00, depending on the heating rate employed. The activation energy of the reaction was found to be about 19 kcal/mole; the enthalpy is 246 cal/g.The decomposition seems to be divided into one reaction withn=0.90, immediately followed by one withn=1.59. The first reaction is attributed to the loss of H₂O, the second one to the (partial) release of OH and CO₂.

---

Zusammenfassung Die durch DTA und TG überprüfte endothermische Zersetzung von Thaumasit aus Mothae zeigt in Abhängigkeit der angewandten Aufheizgeschwindigkeiten Spitzentemperaturen zwischen 138 und 203° C, sowie Reaktionsordnungen von 0.45 bis 1.00. Die Aktivierungsenergie der Reaktion ergab sich zu 19 Kcal/Mol, die Enthalpie zu 246 cal/g.Die Zersetzung scheint in eine Reaktion vonn=0.90 und eine sofort darauffolgende vonn=1.59 geteilt zu sein. Die erste Reaktion wird dem Verlust von H₂O, die zweite der (teilweisen) Freisetzung von OH und CO₂ zugeschrieben.

---

Résumé La décomposition endothermique de la thaumasite de Mothae a été étudiée par ATD et TG. Suivant la vitesse de chauffage utilisée la température au sommet du pic varie de 138 à 203° C et l'ordre de réaction de 0.45 à 1.00. On a trouvé que l'énergie d'activation s'élevait à 19 kcal, mol^–1 et l'enthalpie à 246 cal. g^–1.Il semble que la décomposition s'effectue suivant une réaction d'ordren=0.90, immédiatement suivie par une autre oùn=1.59. On attribue la première réaction à la perte d'eau et la seconde à la libération (partielle) d'hydroxyles OH et d'anhydride carbonique CO₂.

---

, , 138–203° 0,45–1,00 . , 19 /, - 246 /. , n=0,90, n=1,59. , - OH CO₂.

---

---

The material used for this study has been kindly supplied by Dr. P. H. Nixon, former chief geologist, Department of Mines, Maseru, Lesotho.     

IR and thermal studies on lithium oxomolybdenum(VI) oxalate

A new molybdenum(VI) complex, Li₂[Mo₂O₆(C₂O₄)] · 2 H₂O (LMO), was prepared and characterized by chemical analysis and IR spectral studies. Its thermal decomposition was studied by using TG and DTA techniques. LMO loses its two moles of water between 75 and 170° to give the anhydrous product, which decomposes in three stages between 240 and 380°. The first two stages occur in the temperature ranges 240–280° and 280–305°, to give intermediates with the tentative compositions Li₆[Mo₆O₁₉(C₂O₄)₂] and Li₆[Mo₆O₂₀(C₂O₄)], respectively. In the third stage, which extends up to 380°, Li₆[Mo₆O₂₀(C₂O₄)] decomposes to give the end-product, Li₂Mo₂O₇.

---

Zusammenfassung Ein neuer Molybdän(VI)-Komplex der Formel Li₂[Mo₂O₆(C₂O₄)] · 2 H₂O (LMO) wurde dargestellt und durch chemische Analyse und IR-spektroskopisch charakterisiert. Die thermische Zersetzung dieses Komplexes wurde mittels TG und DTA untersucht. LMO verliert die zwei Wassermoleküle zwischen 75 und 170° unter Bildung des wasserfreien Produktes, das zwischen 240 und 380° in drei Stufen zersetzt wird. Die in den Temperaturbereich von 240–280° und 280–305° verlaufenden ersten zwei Reaktionsschritte ergeben Intermediäre der tentativen Zusammensetzung Li₆[Mo₆O₁₉(C₂O₄)₂] bzw. Li₆[Mo₆O₂₀(C₂O₄)]. In dem sich bis 380° erstreckenden dritten Reaktionsschritt wird Li₆[Mo₆O₂₀(C₂O₄)] unter Bildung des Endproduktes Li₂Mo₂O₇ zersetzt.

---

Li₂[MO₂O₆(C₂O₄] · 2 ₂ . . - 70–170° , , 240–380°. 240–280° 280–305° - Li₆[Mo₆O₁₉(C₂O₄)₂] Li₆[Mo₆O₂₀(C₂O₄)]. - 380° Li₂Mo₂O₇.

---

---

The authors are grateful to Prof. S. N. Tandon, Head of the Chemistry Department, for providing the research facilities.     

On theC p toC v conversion of solid linear macromolecules II

A modification is proposed for the Nernst-Lindemann equation that is used to convert calculated heat capacities at constant pressure (C _p ) to heat capacities at constant volume (C _v ) for solid, linear macromolecules. the constant A₀ per mole of repeating unit in this equation is derived by taking into account the variable number of vibrators excited at different temperatures. With the new equation it is possible to calculateC _p for solid polymers over a wider temperature range. The constant is calculated for solid polymers from experimental thermal expansivity, isothermal compressibility and heat capacity data obtained from the literature. An average value of (3.9±2.4)×10^–3(K mol)/J was obtained for A₀ (new) from data on 22 solid polymers. This average value may be used as a universal constant in case no experimental data on compressibility and expansivity are available for computation ofA ₀. The remaining variation of A₀ (new) with temperature is discussed and example calculations are shown for polyethylene. Effects of premelting and possibly large-amplitude motion are discovered for polyethylene in the temperature range 290 to 410 K.

---

Zusammenfassung Es wurde eine Abänderung der Nernst-Lindemann Gleichung vorgeschlagen, mit deren Hilfe für feste, lineare Makromoleküle errechnete Wärmekapazitäten bei konstantem Druck (C _p ) in Wärmekapazitäten bei konstantem Volumen (C _p ) umgerechnet werden können. Zur Ableitung der molaren Konstanten A₀ in dem sich wiederholenden Teil der Gleichung wurde die variable Anzahl der erregten Schwinger bei verschiedenen Temperaturen berücksichtigt. Mit der neuen Gleichung wird es möglich, dieC _p fester Polymere für einen breiten Temperaturbereich zu errechnen. Die Konstante wurde für die festen Polymere auf Grund des ermittelten thermischen Ausdehnungsvermögens und der isothermen Kompressibilität sowie der der Literatur entnommenen Wärmekapazitätsangaben berechnet. Aus Angaben von 22 festen Polymeren wurde für A₀(neu) ein Durchschnittswert von (3,9±2,4)×10^–3 (K mol)/J erhalten. Verfügt man zur Berechnung von A₀ über keine experimentellen Werte für Kompressibilität und Ausdehnungsvermögen, so kann dieser durchscnittswert als universale Konstante angewendet werden. Die verbleibende Temperaturabhängigkeit von A₀(neu) wird besprochen und Beispielrechnungen für Polyäthylen gegeben. Für Polyäthylen wurden im Temperaturbereich 290 bis 410 K Effekte durch Vorschmelzen und Bewegungen mit großer Amplitude festgestellt.

---

-, (C _p ) (C _v ) , . A ₀ , . C _p . A ₀ , , . 22 , A ₀ () (3,9±2,4)· 10^–3 ·/. A ₀ . A ₀ , . 290–410 .