Structure and low-temperature properties of Ba8Ni6Ge40

Structural, magnetic, heat capacity, electrical and thermal transport properties are reported on polycrystalline Ba₈Ni₆Ge₄₀. Ba₈Ni₆Ge₄₀ crystallizes in a cubic type I clathrate structure with unit cell a=10.5179 (4) Å. It is diamagnetic with susceptibility χ_dia=−1.71×10^-6 emu/g Oe. An Einstein temperature 75 K and a Debye temperature 307 K are estimated from heat capacity data. It exhibits n-type conducting behavior below 300 K. It shows high Seebeck coefficients (−111×10^-6 V/K), low thermal conductivity (2.25 W/K m), and low electrical resistivity (8.8 mΩ cm) at 300 K.     

Magnetic and electrical properties of amorphous Ge1−xCrx thin films grown by low temperature vapor deposition

Amorphous Ge_1−xCr_x thin films are deposited on (1 0 0)Si by using a thermal evaporator. Amorphous phase is obtained when Cr concentration is lower than 30.7 at%. The electrical resistivities are 1.89×10⁻³–0.96×10² Ω cm at 300 K, and decrease with Cr concentration. The Ge_1−xCr_x thin films are p-type. The hole concentrations are 5×10¹⁶–7×10²¹ cm⁻³ at 300 K, and increase with Cr concentration. Magnetizations are 7.60–1.57 emu/cm³ at 5 K in the applied field of 2 T. The magnetizations decrease with Cr concentration and temperature. Magnetization characteristics show that the Ge_1−xCr_x thin films are paramagnetic.     

Effect of substrate temperature on structure and electrical resistivity of laser-ablated IrO2 thin films

IrO₂ thin films were prepared on Si(1 0 0) substrates by laser ablation. The effect of substrate temperature (T_sub) on the structure (crystal orientation and surface morphology) and property (electrical resistivity) of the laser-ablated IrO₂ thin films was investigated. Well crystallized and single-phase IrO₂ thin films were obtained at T_sub = 573-773 K in an oxygen partial pressure of 20 Pa. The preferred orientation of the laser-ablated IrO₂ thin films changed from (2 0 0) to (1 1 0) and (1 0 1) depending on T_sub. With the increasing of T_sub, both the surface roughness and crystallite size increased. The room-temperature electrical resistivity of IrO₂ thin films decreased with increasing T_sub, showing a low value of (42 ± 6) × 10⁻⁸ Ω m at T_sub = 773 K.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

Growth and structure of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 thin films prepared by pulsed laser deposition technique

Bi_0.5(Na_0.7K_0.2Li_0.1)_0.5TiO₃ (BNKLT) thin films were prepared on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition (PLD) technique. The films prepared were examined by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The effects of the processing parameters, such as oxygen pressure, substrate temperature and laser power, on the crystal structure, surface morphology, roughness and deposition rates of the thin films were investigated. It was found that the substrate temperature of 600 °C and oxygen pressure of 30 Pa are the optimized technical parameters for the growth of textured film, and all the thin films prepared have granular structure, homogeneous grain size and smooth surfaces.     

Zn掺杂n型笼合物Ba8Ga16-2xZnxGe30+x的热电传输特性

用高温熔融结合放电等离子烧结法制备了Zn掺杂单相n型Ba₈Ga_16-2xZn_xGe_30+x笼合物,探索了Zn对Ga的取代对其热电传输特性的影响规律.研究结果表明,n型Ba₈Ga_16-2xZn_xGe_30+x化合物的电导率随着x的增加逐渐增 关键词： 热电传输性能 n型笼合物 框架取代     

Laser-induced voltage characteristics of Bi2Sr2Co2Oy thin films on LaAlO3 substrates

We report the laser-induced voltage (LIV) effects in c-axis oriented Bi₂Sr₂Co₂O_y thin films grown on (0 0 1) LaAlO₃ substrates with the title angle α of 0°, 3°, 5° and 10° by a simple chemical solution deposition method. A large open-circuit voltage with the sensitivity of 300 mV/mJ is observed for the film on 10° tilting LaAlO₃ under a 308 nm irradiation with the pulse duration of 25 ns. When the film surface is irradiated by a 355 nm pulsed laser of 25 ps duration, a fast response with the rise time of 700 ps and the full width at half maximum of 1.5 ns is achieved. In addition, the experimental results reveal that the amplitude of the voltage signal is approximately proportional to sin 2α and the signal polarity is reversed when the film is irradiated from the substrate side rather than the film side, which suggests the LIV effects in Bi₂Sr₂Co₂O_y thin films originate from the anisotropic Seebeck coefficient of this material.     

Spray-pyrolysis deposition of LaMnO3 and La1−xCaxMnO3 thin films

Ethylene glycol solutions of La-Mn(II) and La-Ca-Mn(II) citric complexes has been used as a starting material for spray-pyrolysis deposition of LaMnO₃ and La_1−xCa_xMnO₃ thin films on β-quartz, fused quartz, Si(0 0 1) and SrTiO₃(1 0 0) substrates heated during the deposition at 380 °C. At suitable post-deposition heating conditions highly uniform films, 0.1-1 μm in thickness, with good crystal structure were obtained. Highly textured LaMnO₃ films are obtained on SrTiO₃(1 0 0) substrate. Interaction between the layer and Si-containing substrates is observed during the post-deposition heating in static air.     

Epitaxial growth and structural characterization of Pb(Fe1/2Nb1/2)O3 thin films

We have grown lead iron niobate thin films with composition Pb(Fe_1/2Nb_1/2)O₃ (PFN) on (0 0 1) SrTiO₃ substrates by pulsed laser deposition. The influence of the deposition conditions on the phase purity was studied. Due to similar thermodynamic stability spaces, a pyrochlore phase often coexists with the PFN perovskite phase. By optimizing the kinetic parameters, we succeeded in identifying a deposition window which resulted in epitaxial perovskite-phase PFN thin films with no identifiable trace of impurity phases appearing in the X-ray diffractograms. PFN films having thicknesses between 20 and 200 nm were smooth and epitaxially oriented with the substrate and as demonstrated by RHEED streaks which were aligned with the substrate axes. X-ray diffraction showed that the films were completely c-axis oriented and of excellent crystalline quality with low mosaicity (X-ray rocking curve FWHM?0.09°). The surface roughness of thin films was also investigated by atomic force microscopy. The root-mean-square roughness varies between 0.9 nm for 50-nm-thick films to 16 nm for 100-nm-thick films. We also observe a correlation between grain size, surface roughness and film thickness.     

The influence of Co doping on the dielectric, ferroelectric and ferromagnetic properties of Ba0.70Sr0.30TiO3 thin films

Ba_0.70Sr_0.30TiO₃ (BST) thin films doped by Co (BSTC) are fabricated by sol-gel method on a Pt/Ti/SiO₂/Si substrate. A strong correlation is observed among the microstructure, dielectric, ferroelectric, ferromagnetic properties and Co concentration. The dielectric constant of BST thin films can be tailored from 343 to 119 by manipulating the Co concentration. The dielectric loss of BSTC thin films are still kept below 0.020 and the tunability is above 30% at a dc-applied electric field of 500 kV/cm. With increasing Co doping up to 10 mol%, the coexistence of ferromagnetism and ferroelectrics is found. Suitable dielectric constant, low-dielectric loss, and high tunability of this kind of thin films can be useful for potential tunable applications.     

Structural and electronic properties of type-I and type-VIII Ba8Ga16Sn30 clathrates under compression

The total energy and electronic structures for type-I (β phase) and type-VIII (α phase) Ba₈Ga₁₆Sn₃₀ clathrates under hydrostatic pressure have been investigated using density functional theory (DFT) calculations. It was found that the type-VIII phase is more stable than the type-I one at ambient conditions and that β→α phase transition can not occur under hydrostatic pressure. The band structures show that the type-I and type-VIII Ba₈Ga₁₆Sn₃₀ are indirect semiconductors with band gaps of 0.24 eV and 0.19 eV, respectively. The results suggested that type-I clathrate Ba₈Ga₁₆Sn₃₀ has a larger value of the thermoelectric (TE) power than that of type-VIII clathrate. We found that pressure tuning changes the k-point of conduction band minimum (CBM) in the Brillouin zone for β-phase, but it is not the case for α-phase. Furthermore, the results show that the pressure can change the interaction between guest atoms and the host lattice, and consequently results in the decrease of the band gap of β-phase and the increase of the band gap of α-phase, indicating that the pressure effect can play an important role in the magnitude of the TE power.     

Preparation of five-layered Si/SixGe1−x nano-films by RF helicon magnetron sputtering

Five-layered Si/Si_xGe_1−x films on Si(1 0 0) substrate with single-layer thickness of 30 nm, 10 nm and 5 nm, respectively were prepared by RF helicon magnetron sputtering with dual targets of Si and Ge to investigate the feasibility of an industrial fabrication method on multi-stacked superlattice structure for thin-film thermoelectric applications. The fine periodic structure is confirmed in the samples except for the case of 5 nm in single-layer thickness. Fine crystalline Si_xGe_1−x layer is obtained from 700 °C in substrate temperature, while higher than 700 °C is required for Si good layer. The composition ratio (x) in Si_xGe_1−x is varied depending on the applied power to Si and Ge targets. Typical power ratio to obtain x = 0.83 was 7:3, Hall coefficient, p-type carrier concentration, sheet carrier concentration and mobility measured for the sample composed of five layers of Si (10 nm)/Si_0.82Ge_0.18 (10 nm) are 2.55 × 10⁶ /°C, 2.56 × 10¹² cm⁻³, 1.28 × 10⁷ cm⁻², and 15.8 cm⁻²/(V s), respectively.     

Effects of substrates on the structure and dielectric properties of Ba(Sn0.15Ti0.85)O3 thin films

Ba(Sn_0.15Ti_0.85)O₃ (BTS) thin films were grown on Pt(1 1 1)/Ti/SiO₂/Si and LaNiO₃(LNO)/Pt(1 1 1)/Ti/SiO₂/Si substrates by a sol-gel processing technique, respectively. The BTS thin films deposited on annealed Pt(1 1 1)/Ti/SiO₂/Si and annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si substrates exhibited strong (1 1 1) and perfect (1 0 0) orientations, respectively. The BTS thin films grown on un-annealed Pt(1 1 1)/Ti/SiO₂/Si substrates showed random orientation with intense (1 1 0) peak, while the films deposited on un-annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si substrate exhibited random orientation with intense (1 0 0) peak, respectively. The dielectric constant of the BTS films deposited on annealed Pt(1 1 1)/Ti/SiO₂/Si, annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si, un-annealed Pt(1 1 1)/Ti/SiO₂/Si and un-annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si substrates was 512, 565, 386 and 437, respectively, measured at a frequency of 100 kHz. A high tunability of 49.7% was obtained for the films deposited on annealed LNO/Pt(1 1 1)/Ti/SiO₂/Si substrate, measured at the frequency of 100 kHz with an applied electric field of 200 kV/cm. The high tunability has been attributed to the (1 0 0) texture of the films and larger grain sizes.     

Strongly oriented BST films on La0.9Sr1.1NiO4 electrodes deposited on various substrates for integration of high capacitances on silicon

In this study, we demonstrate the successful oriented growth of Ba_0.6Sr_0.4TiO₃(h 0 0)/La_0.9Sr_1.1NiO₄(0 0 l) stacks by pulsed laser deposition on SiO₂/Si for application in integrated capacitances. We show that for specific deposition conditions the La_0.9Sr_1.1NiO₄ layer spontaneously grows along its c-axis both on SiO₂/Si and on Pt/Ti/SiO₂/Si substrates, serving as a template for the subsequent oriented growth of Ba_0.6Sr_0.4TiO₃ (BST). Moreover, as the resistivity of the La_0.9Sr_1.1NiO₄ layer is ∼1 mΩ cm, it also fulfills the function of bottom electrode for integration of perovskite-based capacitors on silicon. This holds the promise of integrating epitaxial BST with very high dielectric constant compared to polycrystalline BST films. Still, preliminary capacitance measurements on Al/BST/La_0.9Sr_1.1NiO₄/SiO₂/Si capacitors indicate that the stack deposition needs further optimization.     

Effect of microstructure of MgO buffer layer on BaTiO3 grown on silicon substrates

MgO ultrathin films were grown on Si(1 0 0) substrates as buffer layers for the growth of ferroelectric BaTiO₃ thin films by laser molecular beam epitaxy (L-MBE). The deposition process of MgO buffer layers grown on silicon was in situ monitored by reflection high-energy electron diffraction (RHEED). The structure of BaTiO₃ films fabricated on MgO buffers was investigated by X-ray diffraction. Biaxially textured MgO was obtained at high laser energy density, but when the laser energy was lowered, MgO buffer was transformed to the form of texture with angular dispersion with the increase of the film thickness. BaTiO₃ films grown on the former buffer were completely (0 0 1) textured, while those on the latter were (0 0 1) preferred orientated. Furthermore, the fabricated MgO buffers and BaTiO₃ films had atomically smooth surface and interface. All these can reveal that the quality of textured MgO buffer is a key factor for the growth of BaTiO₃ films on silicon.     

Microstructure of epitaxial SrRuO3 thin films on MgO substrates

SrRuO₃ thin films have been grown on singular (1 0 0) MgO substrates using pulsed laser deposition (PLD) in 30 Pa oxygen ambient and at a temperature of 400-700 °C. Ex situ reflection high-energy electron diffraction (RHEED) as well as X-ray diffraction (XRD) θ/2θ scan indicated that the films deposited above 650 °C were well crystallized though they had a rough surface as shown by atom force microscopy (AFM). XRD Φ scans revealed that these films were composed of all three different types of orientation domains, which was further confirmed by the RHEED patterns. The heteroepitaxial relationship between SrRuO₃ and MgO was found to be [1 1 0] SRO//[1 0 0] MgO and 45°-rotated cube-on-cube [0 0 1] SRO//[1 0 0] MgO. These domain structures and surface morphology are similar to that of ever-reported SrRuO₃ thin films deposited on the (0 0 1) LaAlO₃ substrates, and different from those deposited on (0 0 1) SrTiO₃ substrates that have an atomically flat surface and are composed of only the [1 1 0]-type domains. The reason for this difference was ascribed to the effect of lattice mismatch across the film/substrate interface. The room temperature resistivity of SrRuO₃ films fabricated at 700 °C was 300 μΩ cm. Therefore, epitaxial SrRuO₃ films on MgO substrate could serve as a promising candidate of electrode materials for the fabrication of ferroelectric or dielectric films.     

Annealing effects on the structural and electrical transport properties of n-type Bi2Te2.7Se0.3 thin films deposited by flash evaporation

N-type Bi₂Te_2.7Se_0.3 thermoelectric thin films with thickness 800 nm have been deposited on glass substrates by flash evaporation method at 473 K. Annealing effects on the thermoelectric properties of Bi₂Te_2.7Se_0.3 thin films were examined in the temperature range 373-573 K. The structures, morphology and chemical composition of the thin films were characterized by X-ray diffraction, field emission scanning electron microscope and energy dispersive X-ray spectroscopy, respectively. Thermoelectric properties of the thin films have been evaluated by measurements of the electrical resistivity and Seebeck coefficient at 300 K. The Hall coefficients were measured at room temperature by the Van der Pauw method. The carrier concentration and mobility were calculated from the Hall coefficient. The films thickness of the annealed samples was measured by ellipsometer. When annealed at 473 K, the electrical resistivity and Seebeck coefficient are 2.7 mΩ cm and −180 μV/K, respectively. The maximum of thermoelectric power factor is enhanced to 12 μW/cm K².     

Luminescence properties of Ge implanted SiO2:Ge and GeO2:Ge films

We have investigated cathodeluminescence (CL) of Ge implanted SiO₂:Ge and GeO₂:Ge films. The GeO₂ films were grown by oxidation of Ge substrate at 550 °C for 3 h in O₂ gas flow. The GeO₂ films on Ge substrate and SiO₂ films on Si substrate were implanted with Ge-negative ions. The implanted Ge atom concentrations in the films were ranging from 0.1 to 6.0 at%. To produce Ge nanoparticles the SiO₂:Ge films were thermally annealed at various temperatures of 600-900 °C for 1 h in N₂ gas flow. An XPS analysis has shown that the implanted Ge atoms were partly oxidized. CL was observed at wavelengths around 400 nm from the GeO₂ films before and after Ge⁻-implantation as well as from SiO₂:Ge films. After Ge⁻-implantation of about 0.5 at% the CL intensity has increased by about four times. However, the CL intensity from the GeO₂:Ge films was several orders of magnitude smaller than the intensity from the 800 °C-annealed SiO₂:Ge films with 0.5 at% of Ge atomic concentration. These results suggested that the luminescence was generated due to oxidation of Ge nanoparticles in the SiO₂:Ge films.     

Multilayer Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3/Bi1.5Zn1.0Nb1.5O7 thin films for tunable microwave applications

Bi_1.5Zn_1.0Nb_1.5O₇/Ba_0.6Sr_0.4TiO₃/Bi_1.5Zn_1.0Nb_1.5O₇ tunable multilayer thin film has been fabricated by pulsed laser ablation and characterized. Phase composition and microstructure of multilayer films were characterized by X-ray diffraction, scanning electron microscopy (SEM) and atomic force microscopy (AFM). The film has very smooth surface with RMS roughness of 1.5-2 nm and grain size of 100-150 nm. Total film thickness has been measure to be 375 nm. The BZN thin films at 300 K, on Pt(1 1 1)/SiO₂/Si substrate showed zero-field dielectric constant of 105 and dielectric loss tangent of 0.002 at frequency of 0.1 MHz. Thin films annealed at 700 °C shows the dielectric tunability of 18% with biasing field 500 kV/cm at 0.1 MHz. The multilayer thin film shows nonferroelectric behavior at room temperature. The good physical and electrical properties of multilayer thin films make them promising candidate for tunable microwave device applications.     

Infrared optical properties of Ba(Zr0.20Ti0.80)O3 and Ba(Zr0.30Ti0.70)O3 thin films prepared by sol-gel method

Ba(Zr_xTi_1−x)O₃ (BZT) (x = 0.20 and 0.30) thin films are deposited on Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrate by sol-gel method. X-ray diffraction patterns show that the thin films have a good crystallinity. Optical properties of the films in the wavelength range of 2.5-12 μm are studied by infrared spectroscopic ellipsometry (IRSE). The optical constants of the BZT thin films are determined by fitting the IRSE data using a classical dispersion formula. As the wavelength increases, the refractive index decreases, while the extinction coefficients increase. The effective static ionic charges are derived, which are smaller than that in a purely ionic material for the BZT thin films.