Influence of ethylene glycol pretreatment on effectiveness of atmospheric pressure plasma treatment of polyethylene fibers

For atmospheric pressure plasma treatments, the results of plasma treatments may be influenced by liquids adsorbed into the substrate. This paper studies the influence of ethylene glycol (EG) pretreatment on the effectiveness of atmospheric plasma jet (APPJ) treatment of ultrahigh molecular weight polyethylene (UHMWPE) fibers with 0.31% and 0.42% weight gain after soaked in EG/water solution with concentration of 0.15 and 0.3 mol/l for 24 h, respectively. Scanning electron microscopy (SEM) shows that the surface of fibers pretreated with EG/water solution does not have observable difference from that of the control group. The X-ray photoelectron spectroscopy (XPS) results show that the oxygen concentration on the surface of EG-pretreated fibers is increased less than the plasma directly treated fibers. The interfacial shear strength (IFSS) of plasma directly treated fibers to epoxy is increased almost 3 times compared with the control group while that of EG-pretreated fibers to epoxy does not change except for the fibers pretreated with lower EG concentration and longer plasma treatment time. EG pretreatment reduces the water contact angle of UHMWPE fibers. In conclusion, EG pretreatment can hamper the effect of plasma treatment of UHMWPE fibers and therefore longer plasma treatment duration is required for fibers pretreated with EG.     

The aging of atmospheric plasma-treated ultrahigh-modulus polyethylene fibers

The aging effects of atmospheric plasma treatments on UHMPE fibers are studied. UHMPE fibers are treated for 0.5 and 1 min with He/O₂/air gas and for 2 and 4 min with He/air gas by atmospheric pressure plasma on a capacitively coupled device at a frequency of 5 kHz. The samples are tested for fiber/epoxy interfacial shear strength at time intervals of 0, 3, 15 and 30 days after initial plasma treatment. Scanning electron microscopy shows micro-cracks on each set of treated fibers, which is not affected by aging over the 30 day study. Interfacial shear strengths (IFSS) for plasma-treated fibers are 2–3 times as high as that of the control. The IFSS for the plasma treated fibers remains constant up to 15 days and then decreases afterwards. XPS Analysis shows a slight increase in atomic concentration of oxygen and nitrogen for each plasma-treated sample. For the He/O₂/air plasma-treated samples, XPS analysis shows an observable increase in C–OH bonds, C=O bonds and COOH bonds, while for the He/air plasma-treated samples, there is a slight increase in C–OH and O=C–O bonds. After 30 days, a decrease in oxygen content for all plasma-treated samples is manifested.     

The influence of moisture on atmospheric pressure plasma etching of PA6 films

The moisture in the substrate material may have a potential influence on atmospheric pressure plasma treatment. In order to investigate how the existence of moisture affects atmospheric pressure plasma treatment, polyamide 6 (PA6) films were treated by helium, helium/oxygen (O₂) plasmas using atmospheric pressure plasma jet (APPJ) at different moisture regain. The film surfaces were investigated using contact-angle measurements, atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS) to characterize the surfaces. The exposure of PA6 film surfaces to the plasmas led to the etching process on the surfaces and changes in the topography of the surfaces. It was shown that the etching rate and the surface roughness were higher for the 9.33% moisture regain (relative humidity 100%) group than that of the 1.61% moisture regain (relative humidity 10%) group with the same plasma gas and power.     

Surface Modification of Para-Aramid Fiber by Direct Fluorination and its Effect on the Interface of Aramid/Epoxy Composites

Surface modification of a para-aramid fiber (DAFIII) was performed by direct fluorination. The properties of treated and untreated fibers were characterized and compared in detail by mechanical testing, Fourier transform infrared (FTIR) spectroscopy characterization, X-ray photoelectron spectroscopy (XPS) analysis and static contact angle measurements. The results showed that little damage of the fiber occurred after direct fluorine treatment, and the content of polar groups on the fibers surfaces were increased significantly, which resulted in a lower value of contact angle. The interlaminar shear strength (ILSS) of DAFIII fiber/epoxy composites and the tensile strength of NOL-ring specimens increased by 33% and 12%, increasing to 56.2 MPa and 2340 MPa, respectively, which indicated that the interfacial adhesion between the matrix and the aramid fiber was improved significantly by the fluorination treatment. Further tests showed that the durability of the direct fluorination treatment on the aramid fiber was also satisfactory.     

Influence of processing parameters on atmospheric pressure plasma etching of polyamide 6 films

This study is designed to systematically investigate how various factors, such as treatment duration, output power, oxygen gas flux, jet to substrate distance, and moisture regain, influence atmospheric pressure plasma etching rate of polyamide 6 (PA 6) films. The etching rate increased as the output power, oxygen gas flux, and moisture regain increased. As the treatment time increased, the etching rate increased first and then decreased. When the substrate was too close or too far from the nozzle, the etching rate was almost not measurable. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) show an increased surface roughness after the plasma treatment. X-ray photoelectron spectroscopy (XPS) shows a decreased carbon content and an increased oxygen content after the plasma treatment. T-peel strength shows an improved bonding strength between the PA 6 films and an adhesive tape after the plasma treatment.     

Surface modification of a polyamide 6 film by He/CF4 plasma using atmospheric pressure plasma jet

Polyamide 6 (PA 6) films are treated with helium(He)/CF₄ plasma at atmospheric pressure. The samples are treated at different treatment times. The surface modification of the PA 6 films is evaluated by water contact angle, atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). The etching rate is used to study the etching effect of He/CF₄ plasma on the PA 6 films. The T-peel strengths of the control and plasma treated films are measured to show the surface adhesion properties of the films. As the treatment time increases, the etching rate decreases steadily, the contact angle decreases initially and then increases, while the T-peel strength increases first and then decreases. AFM analyses show that the surface roughness increases after the plasma treatment. XPS analyses reveal substantial incorporation of fluorine and/or oxygen atoms to the polymer chains on the film surfaces.     

Modification of surface properties of polyamide 6 films with atmospheric pressure plasma

To investigate the effect of the different plasma gases treatment on the surface modification of atmospheric pressure plasma, polyamide 6 films were treated using pure helium (He), He/O₂ and He/CF₄, respectively. Atomic force microscopy (AFM) showed rougher surface, while X-ray photoelectron spectroscopy (XPS) revealed increased oxygen and fluorine contents after the plasma treatments. The plasma treated samples had lower water contact angles and higher T-peel strength than that of the control. The addition of small amount of O₂ or CF₄ to He plasma increases the effectiveness of the plasma treatment in polymer surface modification in terms of surface roughness, surface hydrophilic groups, etching rate, water contact angle and bonding strength.     

Roles of interfaces between carbon fibers and epoxy matrix on interlaminar fracture toughness of composites

The effect of atmospheric-pressure plasma treatment on high strength PAN-based carbon fibers had been studied in terms of fiber surface energetics and mode I and II interlaminar fracture toughness of unidirectional carbon fibers/epoxy matrix composites. The surface characterization of plasma treated carbon fibers was investigated by X-ray photoelectron spectroscopy (XPS) and contact angles. As a result, the plasma treatment changed the surface properties of the carbon fibers, mainly through formation of oxygen functional groups like hydroxyl, carbonyl, and carboxyl groups. According to contact angle measurements, it was observed that plasma treatment led to an increase in surface free energy of the fibers, mainly due to the increase of its specific component. Fracture toughness test results employing double-cantilever beam (DCB) and end notched flexure (ENF) specimens also showed that the increase in specific components or hydrogen bonding between the –OH groups on carbon fibers and the =O ring in epoxy matrix resins played an important role in improving the degree of adhesion at interfaces, resulting in an increase in the interfacial fracture toughness of the composites studied.     

Atmospheric air-plasma treatment of polyester fiber to improve the performance of nanoemulsion silicone

Influence of atmospheric air plasma treatment on performance of nanoemulsion silicone softener on polyethylene terephthalate fibers was investigated by the use of fourier transform infrared spectroscopy (FTIR), bending lengths (BL), wrinkle recovery angles (WRA), fiber friction coefficient analysis (FFCA), moisture absorbency (MA), scanning electron microscopy (SEM) and reflectance spectroscopy (RS). Results indicated that the plasma pretreatment modifies the surface of fibers and increases the reactivity of substrate toward nanoemulsion silicone. Moisture regain and microscopic tests showed that the combination of plasma and silicone treatments on polyethylene terephthalate can decrease moisture absorption due to uniform coating of silicone emulsion on surface of fibers.     

Surface treatment of aramid fiber by air dielectric barrier discharge plasma at atmospheric pressure

Aramid fiber samples are treated by air dielectric barrier discharge (DBD) plasma at atmospheric pressure; the plasma treatment time is investigated as the major parameter. The effects of this treatment on the fiber surface physical and chemical properties are studied by using surface characterization techniques. Scanning electron microscopy (SEM) is performed to determine the surface morphology changes, X-ray photoelectron spectroscopy (XPS) is analyzed to reveal the surface chemical composition variations and dynamic contact angle analysis (DCAA) is used to examine the changes of the fiber surface wettability. In addition, the wetting behavior of a kind of thermoplastic resin, poly(phthalazinone ether sulfone ketone) (PPESK), on aramid fiber surface is also observed by SEM photos. The study shows that there seems to be an optimum treatment condition for surface modification of aramid fiber by the air DBD plasma. In this paper, after the 12 s, 27.6 W/cm³ plasma treatment the aramid fiber surface roughness is significantly improved, some new oxygen-containing groups such as C-O, CO and OC-O are generated on the fiber surface and the fiber surface wettability is greatly enhanced, which results in the better wetting behavior of PPESK resin on the plasma-treated aramid fiber.     

Preparation of vertically aligned carbon nanotube arrays grown onto carbon fiber fabric and evaluating its wettability on effect of composite

Vertically aligned carbon nanotube (CNT) arrays have been grown onto the carbon fiber fabric using a catalytic chemical vapor deposition (CCVD) method. The as-synthesized CNT arrays are about 20 μm in height, and the nanotube has a mean inner and outer diameter of 2.6 nm, 5.5 nm, respectively. The CNT-grafted carbon fabric shows a hydrophobic property with a contact angle over 145°, and the single CNT-grafted carbon fiber shows a sharp increase of dynamic contact angle in de-ionized water from original 71.70° to about 103°, but a little increase does in diiodomethane or E-51 epoxy resin. However, the total surface energy of carbon nanotube-grafted carbon fiber is almost as same as that of as-received carbon fiber. After CNTs growth, single fiber tensile tests indicated a slight tensile strength degradation within 10% for all different lengths of fibers, while the fiber modulus has not been significantly damaged. Compared with the as-received carbon fibers, a nearly 110% increase of interfacial shear strength (IFSS) from 65 to 135 MPa has been identified by single fiber pull-out tests for the micro-droplet composite, which is reinforced by as-received carbon fiber or CNT-grafted carbon fiber.     

Formation of functional groups on graphite during oxygen plasma treatment

Improved sample wettability was obtained by oxygen plasma functionalization of pyrolytic graphite. The samples were exposed to highly dissociated oxygen plasma with the density of 1 × 10¹⁶ m⁻³, the electron temperature of about 5.5 eV and the density of neutral oxygen atoms of 8 × 10²¹ m⁻³ for 20 s. The surface wettability was measured by a contact angle of water drop. The contact angle dropped from original 112° down to about 1°. The functional groups were detected by XPS analyses. The survey spectrum showed a substantial increase of oxygen concentration on the surface, while high-resolution analyses showed additional oxygen was bonded onto the graphite surface in the form of C-O polar functional group responsible for the increase of the surface energy.     

Surface modification of polytetrafluoroethylene film using single liquid electrode atmospheric- pressure glow discharge

Polytetrafluoroethylene films are treated by room temperature helium atmospheric pressure plasma plumes, which are generated with a home-made single liquid electrode plasma device. After plasma treatment, the water contact angle of polytetrafluoroethylene film drops from 114°to 46°and the surface free energy increases from 22.0 mJ/m2 to 59.1 mJ/m2. The optical emission spectrum indicates that there are reactive species such as O2+ , O and He in the plasma plume. After plasma treatment, a highly crosslinking structure is formed on the film surface and the oxygen element is incorporated into the film surface in the forms of -C-O-C-, -C=O, and -O-C=O groups. Over a period of 10 days, the contact angle of the treated film is recovered by only about 10 , which indicates that the plasma surface modification is stable with time.     

Surface analysis of oxygen plasma treated poly(p-phenylene benzobisoxazole) fibers

The influence of oxygen plasma treatment on surface properties of poly(p-phenylene benzobisoxazole) (PBO) fibers and aging effect of the oxygen plasma modified PBO fiber surfaces were investigated by X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and dynamic contact angle analysis (DCAA), respectively. The results indicated that the oxygen plasma treatment introduced some polar groups to PBO fiber surfaces, enhanced surface roughness and changed surface morphologies of PBO fibers by plasma etching and oxidative reactions. Surface wettability of PBO fibers may be significantly improved by increasing surface free energy of the fibers via oxygen plasma treatment. Aging effect of the oxygen plasma treated PBO fibers showed that the fiber surface wettability degraded in the first several days after the plasma treatment, and it was found to be changeless as the aging time continued as long as 30 days.     

Formation of a high hydrophilic/hydrophobic contrast surface on PET substrates by ECR generated sulfur hexafluoride plasma

High hydrophilic/hydrophobic contrast surfaces on polyethylene terephthalate (PET) substrates were formed by shadow mask technique in electron cyclotron resonance generated sulfur hexafluoride plasma atmosphere. The X-ray photoelectron spectroscopy (XPS) analyses indicate that the unmasked PET surfaces contained a high proportion of the CF₂-CF₂ groups, and therefore were hydrophobic with large water contact angle. However, the surface wettability was found to increase drastically on the masked PET surfaces. This could be resulted from a mass of COF (acid fluoride) compounds observed by XPS on the masked film surfaces. The COF compounds could react with atmospheric moisture to form -COOH groups, which in turn increased the surface wettability. In addition, the surface wetting property of the masked areas was found to change significantly with the plasma treatment time, the mask-to-substrate distance and the storage time after the treatment. The best contract in water contact angle obtained from the treated PET samples was larger than 100° after 168 h of storage.     

Improvement of surface wettability and interfacial adhesion of poly-(p-phenylene terephthalamide) by incorporation of the polyamide benzimidazole segment

In order to investigate the effect of the polyamide benzimidazole group on the surface wettability and interfacial adhesion of fiber/matrix composites, surface features of two kinds of aramid fibers, poly (p-phenylene terephthalamide) fiber (Kevlar-49) and poly-(polyamide benzimidazole-co-p-phenylene terephthalamide) (DAFIII), have been analyzed by X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and contact angle analysis (CAA) system, respectively.The results show that with the incorporation of the polyamide benzimidazole segment, more polar functional groups exist on DAFIII surface. The contact angles of water and diiodomethane on DAFIII surface get smaller. The surface free energy of DAFIII increases to 36.5 mJ/m², which is 2.3% higher than that of Kevlar-49. In addition, DAFIII has a larger rough surface compared with that of Kevlar-49 due to different spinning processes. The interfacial shear strength (IFSS) of DAFIII/matrix composite is 25.7% higher than that of Kevlar-49/matrix composite, in agreement with the observed results from surface feature tests. SEM micrographs of failed micro-droplet specimens reveal a strong correlation between the fracture features and the observed test data.     

Surface modification of polypropylene non-woven fabric using atmospheric nitrogen dielectric barrier discharge plasma

In this paper, a dielectric barrier discharge operating in nitrogen at atmospheric pressure has been used to improve the surface hydrophilic property of polypropylene (PP) non-woven fabric. The changes in the hydrophilic property of the modified PP samples are investigated by the contact angle measurements and the variation of water contact angle is obtained as a function of the energy density; micrographs of the PP before and after plasma treatment are observed by scanning electron microscopy (SEM) and the chemical composition of the PP surface before and after plasma treatment is also analyzed by Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The results show that the surface hydrophilic property of the PP samples is greatly improved with plasma treatment for a few seconds, as evidenced by the fact that the contact angle of the treated PP samples significantly decreases after plasma treatment. The analysis of SEM shows that the surface roughness of the treated PP samples increases due to bonding and etching in plasma processing. The analyses of FTIR and the C1s peak in the high-resolution XPS indicate that oxygen-containing and nitrogen-containing polar functional groups are introduced into PP surface in plasma processing. It can be concluded that the surface hydrophilic property of the modified PP samples has been obviously improved due to the introduction of oxygen-containing and nitrogen-containing polar groups and the increase of the surface roughness on the PP surface.     

Plasma surface treatment of textile fibres for improvement of car tires

A new low-temperature plasma surface modification of advanced polyester tire cord at atmospheric pressure was tested. Plasma surface treatment was performed in the barrier discharge plasmas (BDPs, atmospheric pressure glow discharge (APG) and plasma of gliding are (Glid Arc). The surface properties were characterized by the electron spin resonance spectroscopy (ESR), measurements of the contact angle of various polar and non-polar liquids with polyester cords, H-test, peel test and partially by zeta potential measurements. Further tests have been performed at an industrial testingimpregnation line where the common technology was applied on both plasma treated and untreated fibres. The standard H-test and peel-tests were used to characterize the adhesion of the fibre to usual testingrubbers.     

Interfacial evaluation of single Ramie and Kenaf fiber/epoxy resin composites using micromechanical test and nondestructive acoustic emission

Interfacial shear strength (IFSS) of environmentally friendly natural fiber reinforced polymer composites plays a very important role in controlling their overall mechanical performance. The IFSS of various Ramie and Kenaf fiber/epoxy composites was evaluated using the combination of micromechanical test and nondestructive acoustic emission (AE) to find the optimal conditions for desirable final performance. Dynamic contact angle was measured for Ramie and Kenaf fibers and correlated the wettability properties with interfacial adhesion. Mechanical properties of Ramie and Kenaf fibers were investigated using single-fiber tensile test and analyzed statistically by both unimodal and bimodal Weibull distributions. The effect of clamping on the real elongation for both Ramie and Kenaf fibers was evaluated as well. Two different microfailure modes, axial dedonding and fibril fracture, coming from fiber bundles and single fiber composites (SFC) were observed under tension and compression. They were evaluated optically and also determined by AE and their FFT analysis nondestructively.     

Ultrasonic treatment of aramid fiber surface and its effect on the interface of aramid/epoxy composites

Aramid fiber/epoxy composites have been treated by ultrasound during the winding process to enhance the adhesion. According to the ultrasonic treatment interlaminar shear strength (ILSS) of composites has been greatly improved. Dynamic wetting method, XPS and AFM are used to examine the microscopic properties of resultant composites. The enhanced ILSS is attributed to the ultrasonic cavitation, which improves the wetting between aramid fibers and resins.