Photoluminescence observations of hydrogen incorporation and outdiffusion in ZnO thin films

ZnO thin films were deposited with the addition of H₂ to the reaction gas using the atmospheric-pressure metal organic chemical vapor deposition method. The incorporation and outdiffusion of hydrogen in ZnO films were investigated by comparing the intensity of the hydrogen-related bound-exciton peak (I₄: 3.363 eV) in the photoluminescence spectrum. The intensity of I₄ peak was found to be the strongest in the ZnO film deposited at 680 °C with H₂ present. However, for the ZnO films prepared at the same temperature 680 °C but without H₂ present and at the higher temperature of 900 °C with H₂ present, respectively, the I₄ peak was just a minor shoulder of another bound-exciton peak (I₈: 3.359 eV). The intensity of I₄ peak in the ZnO films deposited with H₂ present was found to decrease with the increasing of annealing temperature. These results suggest that it is difficult for hydrogen to incorporate into ZnO thin films grown at high temperatures even in the hydrogen-present ambient.     

Effect of excimer laser annealing on the properties of ZnO thin film prepared by sol-gel method

Pristine ZnO thin films have been deposited with zinc acetate [Zn(CH₃COO)₂], mono-ethanolamine (stabilizer), and isopropanol solutions by sol-gel method. After deposition, pristine ZnO thin films have been irradiated by excimer laser (λ = 248, KrF) source with energy density of 50 mJ/cm² for 30 sec. The effect of excimer laser annealing on the optical and structural properties of ZnO thin films are investigated by photoluminescence and field emission scanning electron microscope. As-grown ZnO thin films show a huge peak of visible region and a wide full width at half maximum (FWHM) of UV region due to low quality with amorphous ZnO thin films. After KrF excimer laser annealing, ZnO thin films show intense near-band-edge (NBE) emission and weak deep-level emission. The optically improved pristine ZnO thin films have demonstrated that excimer laser annealing is novel treatment process at room temperature.     

Influence of annealing temperature on the properties of ZnO thin films deposited by thermal evaporation

ZnO thin films were deposited by thermal evaporation of a ZnO powder. The as-deposited films are dark brown, rich zinc and present a low transmittance. Then, these films were annealed in air atmosphere at different temperatures between 100 and 400 °C. Their microstructure and composition were studied using XRD and RBS measurements respectively. By increasing the temperature, it was found that film oxidation starts at 250 °C. XRD peaks related to ZnO appear and peaks related to Zn decrease. At 300 °C, zinc was totally oxidised and the films became totally transparent. The electrical conductivity measurement that were carried out in function of the annealing temperature showed the transition from highly conductive Zn thin film to a lower conductive ZnO thin film. The optical gap (E_g) was deduced from the UV-vis transmittance, and its variation was linked to the formation of ZnO.     

Conversion of p-type to n-type conductivity in undoped ZnO films by increasing operating temperature

ZnO thin films with the thickness of about 15 nm on (0 0 0 1) sapphire substrates were prepared by pulsed laser deposition. X-ray photoelectron spectroscopy indicated that both as-grown and post-annealed ZnO thin films were oxygen-rich. H₂ sensing measurements of the films indicated that the conductivity type of both the unannealed and annealed ZnO films converted from p-type to n-type in process of increasing the operating temperature. However, the two films showed different conversion temperatures. The origin of the p-type conductivity in the unannealed and annealed ZnO films should be attributed to oxygen related defects and zinc vacancies related defects, respectively. The conversion of the conductivity type was due to the annealing out of the correlated defects. Moreover, p-type ZnO films can work at lower temperature than n-type ZnO films without obvious sensitivity loss.     

The effect of heat treatment on the physical properties of sol-gel derived ZnO thin films

Zinc oxide (ZnO) thin films were deposited on microscope glass substrates by sol-gel spin coating method. Zinc acetate (ZnAc) dehydrate was used as the starting salt material source. A homogeneous and stable solution was prepared by dissolving ZnAc in the solution of monoethanolamine (MEA). ZnO thin films were obtained after preheating the spin coated thin films at 250 °C for 5 min after each coating. The films, after the deposition of the eighth layer, were annealed in air at temperatures of 300 °C, 400 °C and 500 °C for 1 h. The effect of thermal annealing in air on the physical properties of the sol-gel derived ZnO thin films are studied. The powder and its thin film were characterized by X-ray diffractometer (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure (JCPDS 36-1451) and show the c-axis grain orientation. Increasing annealing temperature increased the c-axis orientation and the crystallite size of the film. The annealed films are highly transparent with average transmission exceeding 80% in the visible range (400-700 nm). The measured optical band gap values of the ZnO thin films were between 3.26 eV and 3.28 eV, which were in the range of band gap values of intrinsic ZnO (3.2-3.3 eV). SEM analysis of annealed thin films has shown a completely different surface morphology behavior.     

Structural characterization of supported nanocrystalline ZnO thin films prepared by dip-coating

Nanocrystalline ZnO thin films prepared by the sol-gel dip-coating technique were characterized by grazing incidence X-ray diffraction (GIXD), atomic force microscopy (AFM), X-ray reflectivity (XR) and grazing incidence small-angle X-ray scattering (GISAXS). The structures of several thin films subjected to (i) isochronous annealing at 350, 450 and 550 °C, and (ii) isothermal annealing at 450 °C during different time periods, were characterized. The studied thin films are composed of ZnO nanocrystals as revealed by analysing several GIXD patterns, from which their average sizes were determined. Thin film thickness and roughness were determined from quantitative analyses of AFM images and XR patterns. The analysis of XR patterns also yielded the average density of the studied films. Our GISAXS study indicates that the studied ZnO thin films contain nanopores with an ellipsoidal shape, and flattened along the direction normal to the substrate surface. The thin film annealed at the highest temperature, T = 550 °C, exhibits higher density and lower thickness and nanoporosity volume fraction, than those annealed at 350 and 450 °C. These results indicate that thermal annealing at the highest temperature (550 °C) induces a noticeable compaction effect on the structure of the studied thin films.     

Post-annealing influence on properties of N-In codoped ZnO thin films prepared by ion beam enhanced deposition method

N-In codoped ZnO thin films were prepared by ion beam enhanced deposition method (IBED) and were annealed in nitrogen and oxygen ambient after deposition. The influence of post-annealing on structure, electrical and optical properties of thin films were investigated. As-deposited and all post-annealed samples showed preferential orientation along (0 0 2) plane. Electrical property studies indicated that the as-deposited ZnO film showed p-type with a sheet resistance of 67.5 kΩ. For ZnO films annealed in nitrogen with the annealing temperature increasing from 400 to 800 °C, the conduction type of the ZnO film changed from p-type to n-type. However, for samples annealed in oxygen the resistance increased sharply even at a low annealing temperature of 400 °C and the conduction type did not change. Room temperature PL spectra of samples annealed in N₂ and in O₂ showed UV peak located at 381 and 356 nm, respectively.     

Low temperature synthesis wide optical band gap Al and (Al, Na) co-doped ZnO thin films

Al-doped ZnO (AZO) and (Al, Na) co-doped ZnO (ANZO) thin films were prepared via sol-gel technique with an annealing process at temperatures between 450 and 550 °C for 60 min in air ambient, and their structural and optical properties have been investigated. The deposited films exhibited hexagonal zinc oxide structure except annealing at 450 °C. For the 500 °C-annealed samples, the surface morphology was analyzed via scanning electron microscopy, Photoluminescence (PL) of different Na content ANZO thin films showed that there were very obvious violet and blue emission bands between 400 and 500 nm, and intensity of which were enhanced with Na content increasing. Transparency of the films was improved along with increasing Na content. The result of UV indicated the absorb bands appeared obviously red shift with Na doping into ZnO, the optical gaps of all films far beyond 3.37 eV of pure ZnO, and gradually decreased with Na content increasing, this is very virtual for improving photoelectricity performance of transparent conduct oxide (TCO) film. The possible origins responsible for structure and optical properties also had been discussed.     

Correlation between microstructure and optical properties of nano-crystalline TiO2 thin films prepared by sol-gel dip coating

Titanium dioxide thin films have been prepared from tetrabutyl-orthotitanate solution and methanol as a solvent by sol-gel dip coating technique. TiO₂ thin films prepared using a sol-gel process have been analyzed for different annealing temperatures. Structural properties in terms of crystal structure were investigated by Raman spectroscopy. The surface morphology and composition of the films were investigated by atomic force microscopy (AFM). The optical transmittance and reflectance spectra of TiO₂ thin films deposited on silicon substrate were also determined. Spectroscopic ellipsometry study was used to determine the annealing temperature effect on the optical properties and the optical gap of the TiO₂ thin films. The results show that the TiO₂ thin films crystallize in anatase phase between 400 and 800 °C, and into the anatase-rutile phase at 1000 °C, and further into the rutile phase at 1200 °C. We have found that the films consist of titanium dioxide nano-crystals. The AFM surface morphology results indicate that the particle size increases from 5 to 41 nm by increasing the annealing temperature. The TiO₂ thin films have high transparency in the visible range. For annealing temperatures between 1000 and 1400 °C, the transmittance of the films was reduced significantly in the wavelength range of 300-800 nm due to the change of crystallite phase and composition in the films. We have demonstrated as well the decrease of the optical band gap with the increase of the annealing temperature.     

Effect of different dopant elements (Al,Mg and Ni) on microstructural,optical and electrochemical properties of ZnO thin films deposited by spray pyrolysis (SP)

In the present work we studied the influence of the dopant elements and concentration on the microstructural and electrochemical properties of ZnO thin films deposited by spray pyrolysis. Transparent conductive thin films of zinc oxide (ZnO) were prepared by the spray pyrolysis process using an aqueous solution of zinc acetate dehydrate [Zn(CH₃COO)₂·2H₂O] on soda glass substrate heated at 400 ± 5 °C. AlCl₃, MgCl₂ and NiCl₂ were used as dopant. The effect of doping percentage (2–4%) has been investigated. Afterwards the samples were thermally annealed in an ambient air during one hour at 500 °C. X-ray diffraction showed that films have a wurtzite structure with a preferential orientation along the (0 0 2) direction for doped ZnO. The lattice parameters a and c are estimated to be 3.24 and 5.20 ?, respectively. Transmission allowed to estimate the band gaps of ZnO layers. The electrochemical studies revealed that the corrosion resistance of the films depended on the concentration of dopants.     

Surface morphology and luminescence characterization of β-FeSi2 thin films prepared by pulsed laser deposition

β-FeSi₂ thin films were prepared on Si (1 1 1) substrates by pulsed laser deposition (PLD) with a sintering FeSi₂ target and an electrolytic Fe target. The thin films without micron-size droplets were prepared using the electrolytic Fe target; however, the surface without droplets was remarkably rougher using the Fe target than using the FeSi₂ target. After deposition at 600 °C and then annealing at 900 °C for 20 h, XRD indicated that the thin film prepared using the Fe target had a poly-axis-orientation, but that prepared using the FeSi₂ target had a one-axis-orientation. The PL spectra of the thin films prepared using the FeSi₂ and Fe targets at a growth temperature of 600 °C and subsequently annealed at 900 °C for 20 h had A-, B- and C-bands. Moreover, it was found that the main peak at 0.808 eV (A-band) in the PL spectrum of the thin films prepared using the FeSi₂ target was the intrinsic luminescence of β-FeSi₂ from the dependence of PL peak energy on temperature and excitation power density.     

Influence of annealing temperature on structural and optical properties of ZnO: In thin films prepared by ultrasonic spray technique

Transparent conducting indium doped zinc oxide was deposited on glass substrate by ultrasonic spray method. The In doped ZnO samples with indium concentration of 3 wt.% were deposited at 300, 350 and 400 °C with 2 min of deposition time. The effects of substrate temperature and annealing temperature on the structural, electrical and optical properties were examined. The DRX analyses indicated that In doped ZnO films have polycrystalline nature and hexagonal wurtzite structure with (0 0 2) preferential orientation and the maximum average crystallite size of ZnO: In before and annealed at 500 °C were 45.78 and 55.47 nm at a substrate temperature of 350 °C. The crystallinity of the thin films increased by increasing the substrate temperature up 350 °C, the crystallinity improved after annealing temperature at 500 °C. The film annealed at 500 °C and deposited at 350 °C show lower absorption within the visible wavelength region. The band gap energy increased from E_g = 3.25 to 3.36 eV for without annealing and annealed films at 500 °C, respectively, indicating that the increase in the transition tail width. This is due to the increase in the electrical conductivity of the films after annealing temperature.     

The gas response enhancement from ZnO film for H2 gas detection

ZnO thin films were prepared by thermal oxidation of Zn metal at 400 °C for 30 and 60 min. The XRD results showed that the Zn metal was completely converted to ZnO with a polycrystalline structure. The sensors had a maximum response to H₂ at 400 °C and showed stable behavior for detecting H₂ gases in the range of 40 to 160 ppm. The film oxidized for 60 min in oxygen flow exhibited higher response than that of the 30 min oxidation which was approximately 4000 for 160 ppm H₂ gas concentration. The sensing mechanism was modeled according to the oxygen-vacancy model.     

Effect of annealing temperature and annealing atmosphere on the structure and optical properties of ZnO thin films on sapphire (0 0 0 1) substrates by magnetron sputtering

ZnO thin films were epitaxially grown on sapphire (0 0 0 1) substrates by radio frequency magnetron sputtering. ZnO thin films were then annealed at different temperatures in air and in various atmospheres at 800 °C, respectively. The effect of the annealing temperature and annealing atmosphere on the structure and optical properties of ZnO thin films are investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), photoluminescence (PL). A strong (0 0 2) diffraction peak of all ZnO thin films shows a polycrystalline hexagonal wurtzite structure and high preferential c-axis orientation. XRD and AFM results reveal that the better structural quality, relatively smaller tensile stress, smooth, uniform of ZnO thin films were obtained when annealed at 800 °C in N₂. Room temperature PL spectrum can be divided into the UV emission and the Visible broad band emission. The UV emission can be attributed to the near band edge emission (NBE) and the Visible broad band emission can be ascribed to the deep level emissions (DLE). By analyzing our experimental results, we recommend that the deep-level emission correspond to oxygen vacancy (V_O) and interstitial oxygen (O_i). The biggest ratio of the PL intensity of UV emission to that of visible emission (I_NBE/I_DLE) is observed from ZnO thin films annealed at 800 °C in N₂. Therefore, we suggest that annealing temperature of 800 °C and annealing atmosphere of N₂ are the most suitable annealing conditions for obtaining high quality ZnO thin films with good luminescence performance.     

Surface characterization and luminescent properties of SrAl2O4:Eu,Dy nano thin films

SrAl₂O₄:Eu²⁺, Dy³⁺ thin films were grown on Si (1 0 0) substrates in different atmospheres using the pulsed laser deposition (PLD) technique. The effects of vacuum, oxygen (O₂) and argon (Ar) deposition atmospheres on the structural, morphological and photoluminescence (PL) properties of the films were investigated. The films were ablated using a 248 nm KrF excimer laser. Improved PL intensities were obtained from the unannealed films prepared in Ar and O₂ atmospheres compared to those prepared in vacuum. A stable green emission peak at 520 nm, attributed to 4f⁶5d¹→4f⁷ Eu²⁺ transitions was obtained. After annealing the films prepared in vacuum at 800 °C for 2 h, the intensity of the green emission (520 nm) of the thin film increased considerably. The amorphous thin film was crystalline after the annealing process. The diffusion of adventitious C into the nanostructured layers deposited in the Ar and O₂ atmospheres was most probably responsible for the quenching of the PL intensity after annealing.     

Influence of temperature annealing on optical properties of SrTiO3/BaTiO3 multilayered films on indium tin oxide

We have prepared SrTiO₃/BaTiO₃ thin films with multilayered structures deposited on indium tin oxide (ITO) coated glass by a sol-gel deposition and heating at 300-650 °C. The optical properties were obtained by UV-vis spectroscopy. The films show a high transmittance (approximately 85%) in the visible region. The optical band gap of the films is tunable in the 3.64-4.19 eV range by varying the annealing temperature. An abrupt decrease towards the bulk band gap value is observed at annealing temperatures above 600 °C. The multilayered film annealed at 650 ° C exhibited the maximum refractive index of 2.09-1.91 in the 450-750 nm wavelength range. The XRD and AFM results indicate that the films annealed above 600 ° C are substantially more crystalline than the films prepared at lower temperatures which were used to change their optical band gap and complex refractive index to an extent that depended on the annealing temperature.     

Electrostatic spray deposited zinc oxide films for gas sensor applications

In this work, thin films of zinc oxide (ZnO) for gas-sensor applications were deposited on platinum coated alumina substrate, using electrostatic spray deposition (ESD) technique. As precursor solution zinc acetate in ethanol was used. Scanning electron microscopy (SEM) evaluation showed a porous and homogeneous film morphology and the energy dispersive X-ray analysis (EDX) confirmed the composition of the films with no presence of other impurities. The microstructure studied with X-ray diffraction (XRD) and Raman spectroscopy indicated that the ZnO oxide films are crystallized in a hexagonal wurtzite phase. The films showed good sensitivity to 1 ppm nitrogen dioxide (NO₂) at 300 °C while a much lower sensitivity to 12 ppm hydrogen sulphide (H₂S).     

Synthesis and photoelectric characterization of delafossite conducting oxides CuAlO2 laminar crystal thin films via sol-gel method

Thin films of delafossite of CuAlO₂ laminar crystals on metal substrates (Ni plates) were prepared by sol-gel processing and subsequent thermal treatment in vacuum. The influence of annealing treatment on surface morphologies and structure of the samples is discussed. Field-emission scanning electron microscope (FESEM) shows the laminar surface architecture of the as-prepared CuAlO₂ thin films. The electrical property of sample was investigated by current-voltage analysis, which indicates that a rectifying junction between CuAlO₂ film and metal substrate is formed and forward current exceeds reverse current by a factor of up to three. Otherwise, the photoelectrochemical characteristics recorded under 250 mW/cm² illumination show that the as-prepared thin film electrode which was annealed at 1150 °C for 4 h in vacuum possesses the highest photocurrent density, which is 0.7 mA/cm² at 0 V vs Ag/AgCl.     

Microstructures, optical and electrical properties of In-doped ZnO thin films prepared by sol-gel method

ZnO and indium-doped ZnO (I_xZO) thin films were prepared on silica-glass substrates by the sol-gel method. The thin films were crystallized at 600 °C and 700 °C for 1 h in 6.9 × 10⁻¹ Torr under pure O₂ atmosphere. The analyzed results were compared to investigate the structural characteristics and optical properties. The surface morphology of the I_xZO films was different from that of the ZnO films, and showed a thin overlay structure. In addition, the crystallization of I_xZO film was depleted at higher crystallized temperatures. From XRD analysis, the ZnO and I_xZO thin films possessed hexagonal structures. Notably, micro-In₂O₃ phases were observed in the I_xZO thin films using EDS. Both of In₂O₃ phases and the crystallization mechanism not only improved the peeling of structure, but also improved the electrical conductivity of I_xZO thin films. For the PL spectrum, the optical property of the I_xZO film was raised at a higher crystallization temperature. Although the In₂O₃ phases reduced the structural defects of I_xZO thin film, the optical effect of the residual In³⁺ was not enhanced completely at higher crystallized temperatures.     

Effects of rapid thermal annealing on structural, magnetic and optical properties of Ni-doped ZnO thin films

XPS depth profiles were used to investigate the effects of rapid thermal annealing under varying conditions on the structural, magnetic and optical properties of Ni-doped ZnO thin films. Oxidization of metallic Ni from its metallic state to two-valence oxidation state occurred in the film annealed in air at 600 °C, while reduction of Ni²⁺ from its two-valence oxidation state to metallic state occurred in the film annealed in Ar at 600 and 800 °C. In addition, there appeared to be significant diffusion of Ni from the bottom to the top surface of the film during annealing in Ar at 800 °C. Both as-deposited and annealed thin films displayed obvious room temperature ferromagnetism (RTFM) which was from metallic Ni, Ni²⁺ or both with two distinct mechanisms. Furthermore, a significant improvement in saturation magnetization (M_s) in the films was observed after annealing in air (M_s = 0.036 μ_B/Ni) or Ar (M_s = 0.033 μ_B/Ni) at 600 °C compared to that in as-deposited film (M_s = 0.017 μ_B/Ni). An even higher M_s value was observed in the film annealed in Ar at 800 °C (M_s = 0.055 μ_B/Ni) compared to that at 600 °C mainly due to the diffusion of Ni. The ultraviolet emission of the Ni-doped ZnO thin film was restored during annealing in Ar at 800 °C, which was also attributed to the diffusion of Ni.