Annealing induced microstructural evolution of electrodeposited electrochromic tungsten oxide films

A significant influence of microstructure on the electrochromic and electrochemical performance characteristics of tungsten oxide (WO₃) films potentiostatically electrodeposited from a peroxopolytungstic acid (PPTA) sol has been evaluated as a function of annealing temperature. Powerful probes like X-ray diffractometry (XRD), transmission electron microscopy (TEM), UV-vis spectrophotometry, multiple step chronoamperometry and cyclic voltammetry have been employed for the thin film characterization. The as-deposited and the film annealed at 60 °C are composed of nanosized grains with a dominant amorphous phase, as well as open structure which ensues from a nanoporous matrix. This ensures a greater number of electroactive sites and a higher reaction area thereby manifesting in electrochromic responses superior to that of the films annealed at higher temperatures. The films annealed at temperatures ≥250 °C are characterized by a prominent triclinic crystalline structure and a hexagonal phase co-exists at temperatures ≥400 °C. The deleterious effect on the electrochromic properties of the film with annealing is ascribed to the loss of porosity, densification and the increasing crystallinity and grain size. Amongst all films under investigation, the film annealed at 60 °C exhibits a high transmission modulation (ΔT ∼ 68%) and coloration efficiency (η ∼ 77.6 cm² C⁻¹) at λ = 632.8 nm, charge storage capacity (Q_ins ∼ 21 mC cm⁻²), diffusion coefficient (6.08 × 10⁻¹⁰ cm² s⁻¹), fast color-bleach kinetics (t_c ∼ 275 s and t_b ∼ 12.5 s) and good electrochemical activity, as well as reversibility for the lithium insertion-extraction process upon cycling. The remarkable potential, which the film annealed at 60 °C has, for practical “smart window” applications has been demonstrated.     

Effects of annealing temperature on the structural and photoluminescence properties of nanocrystalline ZrO2 thin films prepared by sol-gel route

Highly transparent nanocrystalline zirconia thin films were prepared by the sol-gel dip coating technique. XRD pattern of ZrO₂ thin film annealed at 400 °C shows the formation of tetragonal phase with a particle size of 13.6 nm. FT-IR spectra reveal the formation of Zr-O-Zr and the reduction of OH and other functional groups as the temperature increases. The transmittance spectra give an average transmittance greater than 80% in the film of thickness 262 nm. Photoluminescence (PL) spectra give intense band at 391 nm and a broad band centered at 300 nm. The increase of PL intensity with elevation of annealing temperature is related to reduction of OH groups, increase in the crystallinity and reduction in the non-radiative related defects. The luminescence dependence on defects in the film makes it suitable for luminescent oxygen-sensor development. The “Red shift” of excitation peak is related to an increase in the oxygen content of films with annealing temperature. The “Blue shift” of PL spectra originates from the change of stress of the film due to lattice distortion. The defect states in the nanocrystalline zirconia thin films play an important role in the energy transfer process.     

Planar quarter wave stacks prepared from chalcogenide Ge-Se and polymer polystyrene thin films

Planar quarter wave stacks based on amorphous chalcogenide Ge-Se alternating with polymer polystyrene (PS) thin films are reported as Bragg reflectors for near-infrared region. Chalcogenide films were prepared using a thermal evaporation (TE) while polymer films were deposited using a spin-coating technique. The film thicknesses, d∼165 nm for Ge₂₅Se₇₅ (n=2.35) and d∼250 nm for polymer film (n=1.53), were calculated to center the reflection band round 1550 nm, whose wavelengths are used in telecommunication. Optical properties of prepared multilayer stacks were determined in the range 400-2200 nm using spectral ellipsometry, optical transmission and reflection measurements. Total reflection for normal incidence of unpolarized light was observed from 1530 to 1740 nm for 8 Ge-Se+7 PS thin film stacks prepared on silicon wafer. In addition to total reflection of light with normal incidence, the omnidirectional total reflection of TE-polarized light from 8 Ge-Se+7 PS thin film stacks was observed. Reflection band maxima shifted with varying incident angles, i.e., 1420-1680 nm for 45° deflection from the normal and 1300-1630 nm for 70° deflection from the normal.     

The effect of heat treatment on the physical properties of sol-gel derived ZnO thin films

Zinc oxide (ZnO) thin films were deposited on microscope glass substrates by sol-gel spin coating method. Zinc acetate (ZnAc) dehydrate was used as the starting salt material source. A homogeneous and stable solution was prepared by dissolving ZnAc in the solution of monoethanolamine (MEA). ZnO thin films were obtained after preheating the spin coated thin films at 250 °C for 5 min after each coating. The films, after the deposition of the eighth layer, were annealed in air at temperatures of 300 °C, 400 °C and 500 °C for 1 h. The effect of thermal annealing in air on the physical properties of the sol-gel derived ZnO thin films are studied. The powder and its thin film were characterized by X-ray diffractometer (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure (JCPDS 36-1451) and show the c-axis grain orientation. Increasing annealing temperature increased the c-axis orientation and the crystallite size of the film. The annealed films are highly transparent with average transmission exceeding 80% in the visible range (400-700 nm). The measured optical band gap values of the ZnO thin films were between 3.26 eV and 3.28 eV, which were in the range of band gap values of intrinsic ZnO (3.2-3.3 eV). SEM analysis of annealed thin films has shown a completely different surface morphology behavior.     

Annealing temperature influence on electrical properties of ion beam sputtered Bi2Te3 thin films

Ion beam sputtering process was used to deposit n-type fine-grained Bi₂Te₃ thin films on BK7 glass substrates at room temperature. In order to enhance the thermoelectric properties, thin films are annealed at the temperatures ranging from 100 to 400 °C. X-ray diffraction (XRD) shows that the films have preferred orientations in the c-axis direction. It is confirmed that grain growth and crystallization along the c-axis are enhanced as the annealing temperature increased. However, broad impurity peaks related to some oxygen traces increase when the annealing temperature reached 400 °C. Thermoelectric properties of Bi₂Te₃ thin films were investigated at room temperature. The Bi₂Te₃ thin films, including as-deposited, exhibit the Seebeck coefficients of −90 to −168 μV K⁻¹ and the electrical conductivities of 3.92×10²-7.20×10² S cm⁻¹ after annealing. The Bi₂Te₃ film with a maximum power factor of 1.10×10⁻³ Wm⁻¹ K⁻² is achieved when annealed at 300 °C. As a result, both structural and transport properties have been found to be strongly affected by annealing treatment. It was considered that the annealing conditions reduce the number of potential scattering sites at grain boundaries and defects, thus improving the thermoelectric properties.     

Solution processed amorphous InGaZnO semiconductor thin films and transistors

Amorphous indium gallium zinc oxide (a-IGZO) semiconductor thin films and transistors were deposited on alkali-free glasses by the sol–gel route. The atomic ratio of In:Ga:Zn in the solution was 0.7:0.3:1. In this study, the effects of annealing temperature on the structural, surface condition, optical transmittance, and electrical resistivity of a-IGZO semiconductor thin films were investigated. GIXRD measurements and TEM-NBD analysis indicated that all annealed IGZO thin films had an amorphous phase structure. The dried IGZO sol–gel films annealed at a temperature higher than 425 °C had a flat surface and exhibited high transparency (>89%) in the visible region. According to results from TGA, FT-IR and XPS, the residual organic compounds in the dried IGZO sol–gel films were completely removed at the annealing temperatures higher than 450 °C. Therefore, we chose the 450 °C annealed thin film as the active channel layer in the bottom-gate, bottom-contact (BGBC) thin-film transistor (TFT) in the present study. Current–voltage (I–V) characteristics of the 450 °C annealed a-IGZO TFT revealed that it operated in n-type behavior with a positive threshold voltage (enhancement mode).     

Structural, compositional, thermal resistant and hydro-oleophobic properties of fluorine based block-co-polymer films on quartz substrates by wet chemical process

Crack free and smooth surfaces of poly [4,5-difluoro 2,2-bis (trifluoromethyl)-(1,3 dioxole)-co-tetrafluoroethylene] (TFE-co-TFD) thin films have been deposited by wet chemical dip coating technique on polished quartz and glass slide substrates. The deposited films have been subjected to annealing at different temperatures ranging from 100 to 500 °C for 1 h in argon atmosphere. The elemental composition of the as-deposited (xerogel) thin film as well as film annealed at 400 °C was measured by X-ray photoelectron spectroscopy and observed that there was no change in the composition of the film. X-ray diffraction pattern revealed the amorphous behaviour of both as-deposited and film annealed at 400 °C. Surface morphology and elemental composition of the films have been examined by employing scanning electron microscopy attached with energy dispersive X-ray analyser, respectively. It was found that as the annealing temperature increased from 100 to 400 °C, nano-hemisphere-like structures have been grown, which in turn has shown increase in the water contact angle from 122^o to 148^o and oil (peanut) contact angle from 85° to 96°. No change in the water contact angle (122°) has been observed when the films deposited at room temperature were heated in air from 30 to 80 °C as well as exposed to steam for 8 days for 8 h/day indicating thermal stability of the film.     

Effects of post-thermal treatments on morphological and optical properties of NiO/Ni(OH)2 thin films synthesized by solution growth

Room temperature deposition of PVP capped nanostructured NiO/Ni(OH)₂ thin film, the morphological and optical characterizations by solution growth technique are reported. The nanostructured thin films which were deposited on optical glass substrates were annealed at different temperatures and then subjected to structural, morphological and optical characterizations. X-ray diffraction measurements of the films revealed that higher temperatures during the thermal treatment enhanced the crystallinity of the thin films. The SEM surface micrographs show non-interconnected uniformly deposited fibre-like structures with approximate lengths between 400 and 1200 nm. The optical band gap energy roughly decreased from about 2.7 eV to about 2.2 eV with thermal treatment. The absorbance of the thin films annealed at 300 and 400 °C was as high as 90% in the visible region of the electromagnetic spectrum. These materials could be useful in solar thermal conversion processes.     

Improved dielectric properties of (Pb,Ca)TiO3 thin films prepared by metal-organic decomposition method

(Pb,Ca)TiO₃ (PCT) thin films have been deposited on Pt/Ti/SiO₂/Si substrate by metal-organic decomposition (MOD) technique. The film processing parameters such as drying and annealing temperatures have been optimized to obtain good-quality PCT films. Compositional analysis of the film has been studied by X-ray photoelectron spectroscopy (XPS). The effect of the annealing temperature on the crystalline structure, microstructure and electrical properties have been investigated by X-ray diffraction, atomic force microscopy (AFM) and impedance analyzer, respectively. Amorphous PCT films form at 350 °C and crystallize in the perovskite phase following the isothermal annealing at ?650 °C for 3 h in oxygen ambient. Typical tetragonal structure of the PCT film is evidenced from X-ray diffraction pattern. The grain size in the PCT films increases with an increase in annealing temperature. Significant improvement in the dielectric constant value is observed as compared to other reported work on PCT films. The observed dielectric constant and dissipation factor at 100 kHz for 650 °C annealed PCT films are 308 and 0.015, respectively. The correlation of the film microstructural features and electrical behaviors is described.     

Effect of annealing temperature on the optical and electrical properties of amorphous As45.2Te46.6In8.2 thin films

The optical absorption of the As-prepared and annealed As_45.2Te_46.6In_8.2 thin films are studied. Films annealed at temperatures higher than 453 K show a decrease in the optical energy gap (E_o). The value of E_o increases from 1.9 to 2.43 eV with increasing thickness of the As-prepared films from 60 to 140 nm. The effect of thickness on high frequency dielectric constant (?_∞) and carrier concentration (N) is also studied. The crystalline structures of the As_45.2Te_46.6In_8.2 thin films resulting from heat treatment of the As-prepared film at different elevated temperatures is studied by X-ray diffraction. An amorphous-crystalline transformation is observed after annealing at temperatures higher than 453 K. The electrical conductivity at low temperatures is found due to the electrons transport by hopping among the localized states near the Fermi level. With annealing the films at temperatures higher than 473 K (the crystallization onset temperature) for 1 h, the electrical conductivity increases and the activation energy decreases, which can be attributed to the amorphous-crystalline transformations.     

Thin porous Ni-YSZ films as anodes for a solid oxide fuel cell

Porous Ni-YSZ (YSZ—yttria-stabilized zirconia) films were fabricated by reactive co-sputtering of a Ni and a Zr-Y target, followed by sequentially annealing in air at 900 °C and in vacuum at 800 °C. The Ni-YSZ films comprised small grains and pores that were tens of nanometers in size. The porous Ni-YSZ films were used as an anode on one side of a YSZ electrolyte disc and a La_0.7Sr_0.3MnO₃ thick film was used as a cathode on the other side of the disc to form solid oxide fuel cells (SOFCs). The voltage-current curves of the SOFCs with single- and a triple-layered porous anodes were measured in a single-chamber configuration, in a mixture of CH₄ and air (CH₄:O₂ volume ratio=2:1). The maximum power density of the SOFC using the single-layered porous Ni-YSZ thin films as the anode was 0.38 mW cm⁻², which was lower than that of 0.76 mW cm⁻², obtained using a screen-printed Ni-YSZ thick anode. The maximum power density of the SOFC with a thin anode was increased, but varied between 0.6 and 1.14 mW cm⁻² when a triple-layered porous Ni-YSZ anode was used.     

Effect of annealing temperature on the microstructure and optical–electrical properties of Cu–Al–O thin films

We have successfully prepared Cu–Al–O thin films on silicon (100) and quartz substrates by radio frequency (RF) magnetron sputtering method. The as-deposited Cu–Al–O film is amorphous in nature and post-annealing treatment in argon ambience results in crystallization of the films and the formation of CuAlO₂. The annealing temperature plays an important role in the surface morphology, phase constitution and preferred growth orientation of CuAlO₂ phase, thus affecting the properties of the film. The film annealed at 900 °C is mainly composed of CuAlO₂ phase and shows smooth surface morphology with well-defined grain boundaries, thus exhibiting the optimum optical–electrical properties with electrical resistivity being 79.7 Ω·cm at room temperature and optical transmittance being 80% in visible region. The direct optical band gaps of the films are found in the range of 3.3–3.8 eV depending on the annealing temperature.     

Close space vapor transport method for Bi2Te3 thin films deposition: Influence of the type of substrate

Bismuth telluride thin films have been grown by close space vapor transport (CSVT) technique as a function of substrate temperature (T_sub). Both N- and P-type samples can be obtained by this method which is a relatively simple procedure, which makes the method interesting for technological applications. The samples were deposited onto amorphous glass and polycrystalline CdTe film substrates in the substrate temperature range 300-425 °C, with a fixed gradient between source and substrate of 300 °C. The influence of the type of substrate and substrate temperature in the CSVT chamber on the physical properties of the films is presented and discussed.     

Influence of temperature annealing on optical properties of SrTiO3/BaTiO3 multilayered films on indium tin oxide

We have prepared SrTiO₃/BaTiO₃ thin films with multilayered structures deposited on indium tin oxide (ITO) coated glass by a sol-gel deposition and heating at 300-650 °C. The optical properties were obtained by UV-vis spectroscopy. The films show a high transmittance (approximately 85%) in the visible region. The optical band gap of the films is tunable in the 3.64-4.19 eV range by varying the annealing temperature. An abrupt decrease towards the bulk band gap value is observed at annealing temperatures above 600 °C. The multilayered film annealed at 650 ° C exhibited the maximum refractive index of 2.09-1.91 in the 450-750 nm wavelength range. The XRD and AFM results indicate that the films annealed above 600 ° C are substantially more crystalline than the films prepared at lower temperatures which were used to change their optical band gap and complex refractive index to an extent that depended on the annealing temperature.     

Improvement of electrical properties of Sr-modified (Pb,Ca)TiO3 thin films grown by soft chemistry route

Strontium and calcium-modified lead titanate (Pb_0.70Ca_0.15Sr_0.15)TiO₃ soft chemistry-derived thin films were prepared on platinum-coated silicon substrate by spin-coating method. Investigations were made on the structure, surface morphology and electrical properties of the film. The results by XRD and FE-SEM showed that the film exhibits a pure tetragonal perovskite phase and an average grain size of about 50-60 nm, respectively. Electrical measurements of a metal-ferroelectric-metal type capacitor exhibited a stable and switchable electrical polarization in the film. The structure of the Au/PCST/Pt capacitor showed well-saturated hysteresis loops at an applied voltage of 300 kV/cm with remanent polarization and coercive field values of 22 μC/cm² and 100 kV/cm, respectively. At 100 kHz, the dielectric constant and the dielectric loss of the (Pb_0.70Ca_0.15Sr_0.15)TiO₃ thin film with thickness 240 nm were 528 and 0.05, respectively.     

Role of growth temperature and oxygen partial pressure on the structural and electrical properties of pulsed laser deposited La1−xSrxnO3−δ thin films

The paper presents the fabrication and characterization of La_0.65Sr_0.35MnO_3−δ (LSMO) polycrystalline thin films deposited directly on Si (1 0 0) substrates using pulsed laser deposition technique. Various deposition parameters like substrate temperature and oxygen partial pressure have been varied systematically to obtain stoichiometric, crack-free films with smooth surface morphology having nearly monodisperse grain size distribution. The substrate temperature variation from 600 to 800 °C had profound effects on the microstructure and topography of the deposited film, with optimum result being obtained at 700 °C. The variation of partial pressure of oxygen controls the deposition kinetics as well as the stoichiometry of the film in terms of oxygen vacancy, which influences the magnetic and electrical transport properties of the manganate films. The microstructure and crystallinity of the deposited films have been studied using X-ray diffraction, scanning electron microscopy and atomic force microscopy. A correlation between the oxygen stoichiometry and micro-structural and transport properties of the deposited films has been obtained.     

Application of nickel oxide nanoparticles in electrochromic materials

This study presents the application of NiO nanoparticles in electrochromic materials field. The monodisperse NiO nanoparticles ranged from 5 to 8 nm were synthesized by hot-injection method and the NiO films were prepared by dip-coating technique on ITO glass. The structure, electrochemical as well as optical performance was investigated systematically. NiO films composing of nanoparticles maintained the porous microstructure and exhibited excellent electrochromic performance. It was clear that the film annealed at 300 °C exhibited the highest electrochemical activity and improved transmittance modulation (?T), while maintaining faster response time.     

The Al-doping and post-annealing treatment effects on the structural and optical properties of ZnO:Al thin films deposited on Si substrate

Al-doped ZnO (ZnO:Al) thin films with different Al contents were deposited on Si substrates using the radio frequency reactive magnetron sputtering technique. X-ray diffraction (XRD) measurements showed that the crystallinity of the films was promoted by appropriate Al content (0.75 wt.%). Then the ZnO:Al film with Al content of 0.75 wt.% was annealed in vacuum at different temperatures. XRD patterns revealed that the residual compressive stress decreased at higher annealing temperatures. While the surface roughness of the ZnO:Al film annealed at 300 °C became smoother, those of the ZnO:Al films annealed at 600 and 750 °C became rougher. The photoluminescence (PL) measurements at room temperature revealed a violet, two blue and a green emission. The origin of these emissions was discussed and the mechanism of violet and blue emission of ZnO:Al thin films were suggested. We concluded that the defect centers are mainly ascribed to antisite oxygen and interstitial Zn in annealed (in vacuum) ZnO:Al films.     

Structural, optical and electrochromic properties of nickel oxide thin films grown from electrodeposited nickel sulphide

Nickel oxide thin films were grown onto FTO-coated glass substrates by a two-step process: electrodeposition of nickel sulphide and their thermal oxidation at 425, 475 and 525 °C. The influence of thermal oxidation temperature on structural, optical, morphological and electrochromic properties was studied. The structural properties undoubtedly revealed NiO formation. The electrochromic properties were studied by means of cyclic voltammetry. The films exhibited anodic electrochromism, changing from a transparent state to a coloured state at +0.75 V versus SCE, i.e. by simultaneous ion and electron ejection. The transmittance in the coloured and bleached states was recorded to access electrochromic quality of the films. Colouration efficiency and electrochromic reversibility were found to be maximum (21 mC/cm² and 89%, respectively) for the films oxidized at 425 °C. The optical band gap energy of nickel oxide slightly varies with increase in annealing temperature.     

Influence of annealing temperature on the structural, optical and mechanical properties of ALD-derived ZnO thin films

ZnO thin films grown on Si(1 1 1) substrates by using atomic layer deposition (ALD) were annealed at the temperatures ranging from 300 to 500 °C. The X-ray diffraction (XRD) results show that the annealed ZnO thin films are highly (0 0 2)-oriented, indicating a well ordered microstructure. The film surface examined by the atomic force microscopy (AFM), however, indicated that the roughness increases with increasing annealing temperature. The photoluminescence (PL) spectrum showed that the intensity of UV emission was strongest for films annealed at 500 °C. The mechanical properties of the resultant ZnO thin films investigated by nanoindentation reveal that the hardness decreases from 9.2 GPa to 7.2 GPa for films annealed at 300 °C and 500 °C, respectively. On the other hand, the Young's modulus for the former is 168.6 GPa as compared to a value of 139.5 GPa for the latter. Moreover, the relationship between the hardness and film grain size appear to follow closely with the Hall-Petch equation.