Syntheses and properties of the Fe-Co/Fe3O4 ferrites

The Fe alloy-ferrite composites Fe-Co/Fe₃O₄ are synthesized by using disproportion of Fe (II) and reduction of Co (II) by Fe⁰ in a concentrated and boiling KOH solution. The Fe alloy and ferrites are prepared in aqueous solution without any templet and surfactants at low temperature. Their structures and magnetic properties are investigated by X-ray diffractometer (XRD) and vibrating sample magnetometer (VSM). From the results of XRD, it is shown that the samples have b.c.c and f.c.c structure of Fe, and the spinel structures of the ferrite before calcinations; the samples have b.c.c and spinel structures after calcinations at 300 °C; and the samples have only f.c.c structure and the spinel structures calcined at 500 °C.     

Fabrication and characterization of magnetic Fe3O4-CNT composites

Carbon nanotubes (CNTs) decorated with magnetite nanoparticles on their external surface have been fabricated by in situ solvothermal method, which was conducted in benzene at 500 °C with ferrocene and CNTs as starting reagents. The as-prepared composites were characterized using XRD, FTIR, SEM and TEM. It has been found that the amount of magnetite nanoparticles deposited on the CNTs can be controlled by adjusting the initial mass ratio of ferrocene to CNTs. The Fe₃O₄-CNT composites display good ferromagnetic property at room temperature, with a saturation magnetization value (M_s) of 32.5 emu g⁻¹ and a coercivity (H_c) of 110 Oe.     

Nanoparticles of the giant dielectric material, CaCu3Ti4O12 from a precursor route

A method of preparing the nanoparticles of CaCu₃Ti₄O₁₂ (CCTO) with the crystallite size varying from 30 to 200 nm is optimized at a temperature as low as 680 °C from the exothermic thermal decomposition of an oxalate precursor, CaCu₃(TiO)₄(C₂O₄)₈·9H₂O. The phase singularity of the complex oxalate precursor is confirmed by the wet chemical analyses, X-ray diffraction, FT-IR and TGA/DTA analyses. The UV-vis reflectance and ESR spectra of CCTO powders indicate that the Cu(II) coordination changes from distorted octahedra to nearly flattened tetrahedra (squashed) to square-planar geometry with increasing annealing temperature. The HRTEM images have revealed that the evolution of the microstructure in nanoscale is related to the change in Cu(II) coordination around the surface regions for the chemically prepared powder specimens. The nearly flattened tetrahedral geometry prevails for CuO₄ in the near surface regions of the particles, whereas square-planar CuO₄ groups are dominant in the interior regions of the nanoparticles. The powders derived from the oxalate precursor have excellent sinterability, resulting in high-density ceramics which exhibited giant dielectric constants upto 40,000 (1 kHz) at 25 °C, accompanied by low dielectric loss <0.07.     

Effect of chromium substitution in Ca4Mn3O10

Ca₄Mn_3−xCr_xO₁₀ compounds were synthesized in order to investigate the role of an isoelectronic substitution in the layered manganite. Induced structural changes are mainly described as a distortion of the two types of octahedra in the n=3 RP structure. The results indicate that Cr³⁺ is not the only significant valence state for chromium ions. Electrical and magnetic characterization allow to conclude that chromium does not favour the double exchange mechanism in these compounds.     

Immiscibility in the Fe3O4-FeCr2O4 spinel binary

A recent thermodynamic model of mixing in spinel binaries, based on changes in cation disordering (x) between tetrahedral and octahedral sites [Am. Mineral. 68 (1983) 18, 69 (1984) 733], is investigated for applicability to the Fe₃O₄-FeCr₂O₄ system under conditions where incomplete mixing occurs. Poor agreement with measured consolute solution temperature and solvus [N. Jb. Miner. Abh. 111 (1969) 184] is attributed to neglect of: (1) ordering of magnetic moments of cations in the tetrahedral sublattice antiparallel to the moments of those in the octahedral sublattice and (2) pair-wise electron hopping between octahedral site Fe³⁺ and Fe²⁺ ions. Disordering free energies (ΔG_D), from which free energies of mixing are calculated, are modeled by

     

Magnetic susceptibility of vanadium garnets NaPb2Co2V3O12 and NaPb2Ni2V3O12

Vanadium garnets NaPb₂Co₂V₃O₁₂ and NaPb₂Ni₂V₃O₁₂ have been successfully synthesized. The X-ray diffraction experiments indicate that these compounds have the garnet structure of cubic symmetry of space group with the lattice constant of 12.742 Å (NaPb₂Co₂V₃O₁₂) and 12.666 Å (NaPb₂Ni₂V₃O₁₂), respectively. The magnetic susceptibility of NaPb₂Ni₂V₃O₁₂ shows the Curie-Weiss paramagnetic behavior between 4.2 and 350 K. The effective magnetic moment μ_eff of NaPb₂Ni₂V₃O₁₂ is 3.14 μ_B due to Ni²⁺ ion at A-site and the Weiss constant is −3.67 K (antiferromagnetic sign). For NaPb₂Co₂V₃O₁₂, the simple Curie-Weiss law cannot be applicable. The ground state is the spin doublet and the first excited state is spin quartet , according to Tanabe-Sugano energy diagram on the basis of octahedral crystalline symmetry. This excited spin quartet state just a bit higher than ground state influences strongly the complex temperature dependence of magnetic susceptibility for NaPb₂Co₂V₃O₁₂.     

Electrochemical properties of carbon-coated LiFePO4 synthesized by a modified mechanical activation process

Carbon-coated lithium iron phosphate (LiFePO₄/C) composites were synthesized by conventional mechanical activation (MA) process and also by a modified MA process. Phase-pure particles were obtained of ∼100 nm size with a nano-meter thick web of carbon surrounding the particles. The composite prepared by the modified MA process shows good performance as cathode material in lithium cells at room temperature. A high performance was achieved at 0.1 C-rate with >96% utilization of the active material. A stable cycle performance even at higher C-rates was achieved with a cathode that has a total carbon content of only 12 wt%. The use of the modified MA process to synthesize LiFePO₄/C has promise to be an efficient process to decrease the total carbon content of the cathode, resulting in the enhanced energy density.     

Magnetotransport coefficients of Sm0.55Sr0.45MnO3

Measurements of resistivity, magnetization, Seebeck coefficient in 0 and 1.5 T and Nernst coeffecient in 0.3, 0.9 and 1.8 T as a function of temperature on a polycrystalline sample Sm_0.55Sr_0.45MnO₃ are presented. The data demonstrate that an increase in both the carrier density and the mobility of the charge carriers is responsible for the observed colossal magnetoresistance in this compound.     

Aqueous synthesis and enhanced photocatalytic activity of ZnO/Fe2O3 heterostructures

We report a facile synthesis of ZnO/Fe₂O₃ heterostructures based on the hydrolysis of FeCl₃ in the presence of ZnO nanoparticles. The material structure, composition, and its optical properties have been examined by means of transmission electron microscopy, scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and diffuse reflectance UV–visible spectroscopy. Results obtained show that 2.9 nm-sized Fe₂O₃ nanoparticles produced assemble with ZnO to form ZnO/Fe₂O₃ heterostructures. We have evaluated the photodegradation performances of ZnO/Fe₂O₃ materials using salicylic acid under UV-light. ZnO/Fe₂O₃ heterostructures exhibited enhanced photocatalytic capabilities than commercial ZnO due to the effective electron/hole separation at the interfaces of ZnO/Fe₂O₃ allowing the enhanced hydroxyl and superoxide radicals production from the heterostructure.     

Solution-combusting preparation of mono-dispersed Mn3O4 nanoparticles for electrochemical applications

Manganese oxide (Mn₃O₄) nanoparticles with average diameter of 15 nm were prepared using alcohol solution of manganese chloride as starting material via a facile solution-combusting method. The flame core zone was chosen to prepare mono-dispersed and high crystalline products, which were employed to modify glassy carbon electrode and detect dopamine via cyclic voltammetry. The results exhibited excellent electrochemical sensitivity. A linear relationship between the concentration of dopamine and its oxidation peak current was obtained by differential pulse voltammetry, which will find wide application in the biological detection.     

Thermal stability of A-site ordered PrBaMn2O6 manganites

The crystal structure and electromagnetic properties as well as thermal stability of the A-site ordered PrBaMn₂O₆ manganites have been investigated. These samples have been prepared by using ‘two-steps’ synthesis mode. They have tetragonal structure with no tilt of MnO₆ octahedra and show ferromagnetic metal to paramagnetic semiconductor transition. The most significant structural feature of the A-site ordered manganites is that the MnO₂ sublattice is sandwiched by two types of rock-salt layers PrO and BaO. The different degree of Pr and Ba ions in the A-sublattice is revealed. The A-site ordered PrBaMn₂O₆ sample with maximum degree of the A-site order demonstrates ferromagnetic metallic to paramagnetic insulating transition with the Curie point ∼320 K. The A-site disordered Pr_0.50Ba_0.50MnO₃ sample is ferromagnetic metal below T_C≈140 K. The cation order in these compounds is stable in air up to 1300 °C. For the partly A-site ordered samples the magnetic and electronic phase separation is observed. The magnetotransport properties of the A-site ordered manganites treated under different conditions are discussed in terms of the superexchange interactions and A-site order degree.     

Magnetic and rheological properties of monodisperse Fe3O4 nanoparticle/organic hybrid

Fe₃O₄ nanoparticle/organic hybrids were synthesized via hydrolysis using iron (III) acetylacetonate at ∼80 °C. The synthesis of Fe₃O₄ was confirmed by X-ray diffraction, selected-area diffraction, and X-ray photoelectron spectroscopy. Fe₃O₄ nanoparticles in the organic matrix had diameters ranging from 7 to 13 nm depending on the conditions of hydrolysis. The saturation magnetization of the hybrid increased with an increase in the particle size. When the hybrid contained Fe₃O₄ particles with a size of less than 10 nm, it exhibited superparamagnetic behavior. The blocking temperature of the hybrid containing Fe₃O₄ particles with a size of 7.3 nm was 200 K, and it increased to 310 K as the particle size increased to 9.1 nm. A hybrid containing Fe₃O₄ particles of size greater than 10 nm was ferrimagnetic, and underwent Verwey transition at 130 K. Under a magnetic field, a suspension of the hybrid in silicone oil revealed the magnetorheological effect. The yield stress of the fluid was dependent on the saturation magnetization of Fe₃O₄ nanoparticles in the hybrid, the strength of the magnetic field, and the amount of the hybrid.     

Microwave-assisted synthesis of Fe3O4 nanorods and nanowires in an ionic liquid

Without using inert gas to prevent the oxidation of Fe²⁺, Fe₃O₄ nanorods and nanowires have been successfully synthesized via a microwave-assisted ionic liquid method (MAIL). Compared to the traditional methods, the whole reaction process can be carried out more easily and faster. Our result shows that temperature and time of microwave heat played important roles in the formation of Fe₃O₄ with different morphologies. These products were characterized by X-ray powder diffraction (XRD), transmission electron microscopy (TEM), thermogravimetric analysis (TG) and FT-IR spectra.     

Superparamagnetic-like behavior and spin-orbit coupling in (Co,Zn)RE4W3O16 tungstates (RE=Nd, Sm, Eu, Gd, Dy and Ho)

Magnetic susceptibility measurements carried out on (Co,Zn)RE₄W₃O₁₆ compounds revealed a disordered state of magnetic moments above 4.2 K for all compounds under study, and a weak response to magnetic field and temperature for ZnSm₄W₃O₁₆ and ZnEu₄W₃O₁₆ samples. The temperature independent component of magnetic susceptibility has a negative value for ZnGd₄W₃O₁₆ and a positive one for the rest of the tungstates, indicating a domination of van Vleck contribution. The magnetization isotherms of majority of the tungstates under study revealed both spontaneous magnetic moments and hysteresis characteristic for the superparamagnetic-like behavior with blocking temperature T_B∼30 K, except for ZnEu₄W₃O₁₆. Fitting procedure of the Landé factor revealed that the stronger the orbital contribution, the weaker the superparamagnetic effect, namely for ZnRE₄W₃O₁₆. In case of CoRE₄W₃O₁₆ a significant participation of the Co²⁺ moment in the spontaneous magnetization was observed.     

A novel strategy to synthesize cobalt hydroxide and Co3O4 nanowires

Cobalt hydroxide ultra fine nanowires were prepared by a facile hydrothermal route using hydrogen peroxide. This method provides a simple, low cost, and large-scale route to produce β-cobalt hydroxide nanowires with an average diameter of 5 nm and a length of ca. 10 μm, which show a predominant well-crystalline hexagonal brucite-like phase. Their thermal decomposition produced highly uniform nanowires of cobalt oxide (Co₃O₄) under temperature 500 °C in the presence of oxygen gas. The produced cobalt oxide was characterized by X-ray diffraction, transmission electronic microscopy, and selected-area electron diffraction. The results indicated that cobalt oxide nanowires with an average diameter of 10 nm and a length of ca. 600 nm have been formed, which show a predominant well-crystalline cubic face-centered like phase.     

Mössbauer study of Zn0.4Cu0.6Fe1.2Cr0.8O4

Zn_0.4Cu_0.6Fe_1.2Cr_0.8O₄ has been studied by Mössbauer spectroscopy, SQUID magnetometry, and X-ray diffraction. The crystal is found to have a cubic spinel structure with the lattice constant The iron ions are in ferric states and occupy both the tetrahedral (A) and octahedral (B) sites; the fractions of the iron ions at the A-sites and B-sites are 0.52 and 0.34, respectively. While spin orderings are collinear at higher temperatures, spin canting begins to appear around 25 K and increases with decreasing temperature; the canting angle at 4.7 K reaches up to 27°. Debye temperatures of the tetrahedral and octahedral sites are determined to be 339 and 335 K, respectively.     

Immiscibility in the NiFe2O4-NiCr2O4 spinel binary

The solid solution behavior of the Ni(Fe_1−nCr_n)₂O₄ spinel binary is investigated in the temperature range 400-1200 °C. Non-ideal solution behavior, as exhibited by non-linear changes in lattice parameter with changes in n, is observed in a series of single-phase solids air-cooled from 1200 °C. Air-annealing for 1 year at 600 °C resulted in partial phase separation in a spinel binary having n=0.5. Spinel crystals grown from NiO, Fe₂O₃ and Cr₂O₃ reactants, mixed to give NiCrFeO₄, by Ostwald ripening in a molten salt solvent, exhibited single-phase stability down to about 750 °C (the estimated consolute solution temperature, T_cs). A solvus exists below T_cs. The solvus becomes increasingly asymmetric at lower temperatures and extrapolates to n values of 0.2 and 0.7 at 300 °C. The extrapolated solvus is shown to be consistent with that predicted using a primitive regular solution model in which free energies of mixing are determined entirely from changes in configurational entropy at room temperature.     

EPR investigations of oxidation effects in (V1−xMox)2−δO3

Electron paramagnetic resonance (EPR) investigations has been carried out on the new family of molybdenum doped vanadium sesquioxides (V_1−xMo_x)_2−δO₃. The oxidation effects were monitored from the rate of paramagnetic V⁴⁺ created when the sample is exposed to the air. The effects of the oxidation time, sample temperature, and annealing at 1000 °C under a diluted hydrogen atmosphere on the EPR signal features are analyzed. The V⁴⁺ concentration in the oxidized samples is determined and the relaxation effects driven by the conduction electrons are pointed out from the thermal behaviour of the EPR line features. EPR spectra of all the oxidized samples also reveal a small ferromagnetic contribution strongly correlated with the V⁴⁺ content.     

Field-induced microwave absorption in Fe3O4 nanoparticles and Fe3O4/polyaniline composites synthesized by different methods

Three kinds of nanoscale powders containing Fe₃O₄ nanoparticles (NPs) have been studied by ferromagnetic resonance (FMR): (i) Fe₃O₄ NPs grown and then covered with polyaniline (PANI), (ii) unclad Fe₃O₄ NPs, and (iii) Fe₃O₄ NPs grown “in situ” with the PANI. In every case, there is no low field microwave absorption, rather a single FMR line is observed. However, the half-power widths are of order of 1 kOe presumably due to a distribution of internal fields. For type I particles with a low concentration (below 40%) of Fe₃O₄, the observed resonance fields (H_r) are close to those expected for spheres with negligible magnetocrystalline anisotropy. For all other cases, H_r values are significantly lower. Such shortfalls can be roughly understood by invoking dipolar interactions between the grains, stresses frozen in grains during manufacture (method III), as well as anisotropy fields when the specimens are prepared in an aligning field.     

Photophysical and enhanced daylight photocatalytic properties of N-doped TiO2/g-C3N4 composites

N-doped TiO₂/C₃N₄ composite samples were synthesized by heating the mixture of the hydrolysis product of TiCl₄ and C₃N₄ at different weight ratios. The samples were characterized by X-ray diffraction (XRD), Raman spectrum, UV–vis absorption spectrum, photoluminescence spectrum, X-ray photon electron spectrum (XPS) and surface photovoltage spectrum (SPS). The XRD and Raman results indicate that the introduction of C₃N₄ could inhibit the formation of rutile TiO₂. The composite samples show slight visible light absorption due to the introduction of C₃N₄. The XPS result reveals that some amount of nitrogen is doped into TiO₂, and C₃N₄ exists in the composite sample. The intensities of the SPS signal in the composite samples decrease with the rise in the amount of C₃N₄ in the samples. The photocatalytic activity was evaluated from the Rhodamine B (RhB) degradation under fluorescence light irradiation. The composite samples show significantly enhanced photocatalytic activities and the RhB self-sensitized photodegradation in this system was observed by measuring the photocurrent in the dye sensitized solar cell using the composite as the working electrode.