水溶性荧光CdSe量子点的合成及其在指纹显现中的应用

Water-soluble fluorescent CdSe quantum dots(QDs) were synthesized by using Se、Na₂SO₃ and CdCl₂ as precursors and mercaptoacetic acid(TGA) as modifier. The effects of refluxing time and initial pH values of the reaction on the particle size and fluorescence intensity of CdSe QDs were studied. The XRD、HRTEM and fluorescent spectroscopy were employed to characterize these samples. It is found that CdSe QDs with crystalline size of 2～3 nm are homogeneously distributed in the organic matrix. The maximum fluorescence absorption and emission peak of CdSe QDs solution are at 450 nm and 562 nm, respectively. The fingerprint details on the surface of smooth objects were clearly developed with CdSe QDs solution under irradiation of UV lights.     

水溶性的高荧光CdTe/CdSeⅡ型核壳量子点的合成与表征

用L-半胱氨酸(L-cysteine)作为稳定剂,以制备的CdTe量子点为核模板,水相合成了具有近红外发光的Ⅱ型核壳CdTe/CdSe半导体量子点。实验考察了合成温度,核模板的尺寸和组分比等因素对合成高质量的CdTe/CdSe量子点的影响。用紫外-可见吸收和荧光光谱研究了合成的量子点的光学性质。在优化的合成条件下,荧光发射光谱在586～753nm范围连续可调,荧光量子产率高达68%;通过X-射线衍射(XRD),X射线光电子能谱(XPS)和透射电镜(TEM)对合成的Ⅱ型核壳CdTe/CdSe量子点进行了结构和形貌表征。     

CdSe包覆层数对水溶性CdTe/CdSe (II型)核壳量子点的光学特性和微观结构的影响

在水相合成的CdTe量子点的体系中通过分批次加入新鲜配制的NaHSe和CdCl2溶液,制备出了CdSe包覆层数不同的CdTe/CdSe核壳量子点,并着重考察了CdSe包覆层数对CdTe/CdSe核壳量子点的光学特性以及微观结构的影响.与CdTe量子点相比,CdSe单层包覆的CdTe/CdSe核壳量子点的吸收峰和荧光发射峰出现明显红移;随着CdSe包覆层数的增多,CdTe/CdSe核壳量子点吸收光谱的覆盖范围向长波方向扩展,荧光发射峰强度逐步下降,荧光寿命大幅延长,体现出Ⅱ型核壳量子点的特征.X射线衍射(XRD)分析表明,随着CdSe包覆层数的增多,CdTe/CdSe核壳量子点的粉末衍射峰由CdTe衍射峰位置逐步向CdSe衍射峰位置靠近.CdTe/CdSe核壳量子点因其延伸到近红外区域的宽吸收特性致使其在太阳电池领域具有重要的应用前景.     

水溶性InP/ZnS量子点的合成及其在指纹显现中的应用

以磷化锌、氯化铟为原料,以十二烷胺为溶剂,在150～200℃下合成了InP量子点,通过相转移和紫外光照得到了巯基乙酸修饰的水溶性InP/ZnS量子点.利用X射线衍射仪、透射电镜、高分辨透射电镜、荧光光谱仪等分析了不同温度下合成的量子点的粒径、形貌、荧光性能及指纹显现效果.结果表明,合成的InP和InP/ZnS量子点为球...     

室温水相合成CdTe/CdS核/壳结构量子点

开发了一种以聚乙烯吡咯烷酮为分散剂和稳定剂经条件温和的室温水相合成光谱可调的水溶性CdTe/CdS核/壳结构量子点的方法:向新鲜制备的CdTe量子点溶液中加入硫源,继续反应即可生成CdS壳层,通过控制硫源的浓度即可控制CdS壳层厚度,从而调节光谱性质和增强稳定性.采用XRD、TEM、HRTEM、荧光光谱以及紫外-可见光...     

CdSe量子点/核壳结构的制备及在敏化太阳能电池中的应用进展

综述了CdSe量子点和核-壳型量子点的制备及其在敏化太阳能电池方面的应用进展.     

CdTe/CdS核壳量子点与蛋白质荧光标记

利用连续离子层吸附技术合成了水溶性的CdTe／CdS核壳量子点．通过CdS壳层的包覆,量子点的量子效率由原来的15％（裸核）提高到38％（核壳）,这种核壳结构量子点的化学和光学性质具有更好的稳定性,可以用于生物标记．本文采取共价连接与静电吸附两种方法,实现了量子点的生物标记,电泳技术已证明,应用这种量子点成功地实现了对蛋白质分子的生物标记．通过对量子点与蛋白质偶联前后的荧光光谱分析,发现量子点与蛋白质作用后荧光增强是由于蛋白质对量子点进行了表面修饰,从而降低了表面缺陷引起的非辐射跃迁几率所致．通过共价连接量子点的荧光峰位红移,主要是由于偶极-偶极相互作用引起的;量子点与蛋白质静电吸附作用引起的荧光峰位蓝移主要起因于量子点表面电荷量的降低．     

CdTe/ZnSe核壳量子点免疫层析试纸条检测克伦特罗的研究

采用巯基丁二酸作为表面修饰剂,水相法合成水溶性的CdTe/ZnSe核壳量子点,然后在N-羟基琥珀酰亚胺(NHS)的作用下,将CdTe/ZnSe核壳量子点与抗克伦特罗多克隆抗体(Anti-CLE pAb)连接。通过凝胶电泳和斑点杂交实验,验证CdTe/ZnSe核壳量子点与Anti-CLE pAb连接成功,并且CdTe/ZnSe-Anti-CLE pAb偶联物能识别克伦特罗-BSA抗原(CLE-BSA)。光谱分析表明,量子点与抗体连接后荧光增强,荧光峰位从628nm红移至635nm。将合成的CdTe/ZnSe-Anti-CLE pAb偶联物作为指示克伦特罗(CLE)分子的荧光标记物,制备出一种用于检测CLE的免疫层析试纸条,其最低检测量可达1μg/L。与ELISA法的对比实验表明,此试纸条能应用于CLE残留的快速检测。     

化学合成荧光量子点在指纹显现中的应用

简要阐述了量子点的光学特性、制备方法及其在指纹显现中的应用。重点介绍了Ⅱ~Ⅵ族的CdS基、CdTe基、CdSe基、ZnSe基量子点和Ⅲ~Ⅴ族的InP量子点的化学合成、修饰及其在指纹显现中的研究进展,最后介绍了第Ⅳ族C、Si量子点的研究现状,并对其在指纹显现中的潜在应用作了展望。     

油胺/油酸稳定的CdSe量子点的绿色合成

以液体石蜡为高温反应溶剂,油酸和油胺为混合稳定剂,利用高温热解法一步合成了高质量的CdSe量子点。通过紫外-可见吸收光谱、荧光发射光谱、红外光谱和X射线衍射等手段对量子点的光学性质和结构进行了表征。结果表明,油胺/油酸混合表面活性剂稳定的量子点吸收光谱峰形更尖锐,荧光发射光谱半峰宽更窄。反应温度和反应时间均对量子点的生长过程和光学性质有明显影响,220℃下反应15 min,荧光量子产率可达26%。得到的CdSe量子点为立方晶型,表面同时包覆了油酸和油胺,具有良好的光稳定性。该方法无需使用三烷基膦,价廉环保,且合成的CdSe量子点性质稳定、性能优越,有利于其在分析检测领域中的应用。     

微波辐射法制备水溶性CdTe/ZnS量子点及其与司帕沙星的作用

以巯基乙酸为稳定剂,通过微波加热在水溶液中制备了CdTe/znS量子点.研究了pH值、反应时间、反应温度和cdTe/s<'2->浓度比等合成条件对cdTe量子点荧光光谱的影响.以CdTe/ZnS量子点为探针,探讨了喹诺酮类抗生素司帕沙星与量子点的荧光猝灭作用,结果表明,在最佳实验条件下,其线性范围为0.05～3.00μg/mL,线性相关系数为0.9954,检出限为0.01μg/mL,可将CdTe/ZnS量子点荧光探针用于司帕沙星的测定.     

Probing cytotoxicity of CdSe and CdSe/CdS quantum dots

Toxicities of CdSe and CdSe/CdS quantum dots(QDs) synthesized by ultrasound-assisted methods were investigated in vitro and in vivo.Five human cell lines were used to assess the cytotoxicity of as-prepared CdSe and CdSe/CdS by assays of MTT viability,red blood cell hemolysis,flow cytometry,and fluorescence imaging.The results show that these QDs may be cytotoxic by their influence in S and G2 phases in cell cycles.The cytotoxicity of QDs depends on both the physicochemical properties and related to target cells.     

Aqueous synthesis of CdSe and CdSe/CdS quantum dots with controllable introduction of Se and S sources

A new and convenient route is developed to synthesize CdSe and core-shell CdSe/CdS quantum dots(QDs) in aqueous solution.The gaseous precursors,H2Se and H2S,generated on-line by reducing SeO 3 2à with NaBH 4 and the reaction between Na 2 S and diluted H2SO 4,are used to form high-quality CdSe and CdSe/CdS QDs,respectively.The synthesized water-soluble CdSe and CdSe/CdS QDs possess high quantum yield(3% and 20%) and narrow full-width-at-half-maximum(43 nm and 38 nm).The synthesis process is easily reproducible with simple apparatus and low-toxic chemicals,and can be readily extended to the large-scale aqueous synthesis of QDs.     

Use of CdSe/ZnS core-shell quantum dots as energy transfer donors in sensing glucose

In the present work, CdSe/ZnS core-shell quantum dots were synthesized and conjugated with enzymes, glucose oxidase (GOD) and horseradish peroxidase (HRP). The complex of enzyme-conjugated QDs was used as QD-FRET-based probes to sense glucose. The QDs were used as an electron donor, whereas GOD and HRP were used as acceptors for the oxidation/reduction reactions involved in oxidizing glucose to gluconic acid. Electron transfer between the redox enzymes and the electrochemical reduction of H₂O₂ (or O₂) occurred rapidly, resulting in an increase of the turnover rate of the electron exchange between the substrates (e.g. glucose, H₂O₂ and O₂) and the enzymes (GOD, HRP), as well as between the QDs and the enzymes. The transfer of non-radiative energy from the QDs to the enzymes resulted in the fluorescence quenching of the QDs, corresponding to the increase in the concentration of glucose. The linear detection ranges of glucose concentrations were 0–5.0 g/l (R = 0.992) for the volume ratios of 10/5/5, 0.2–5.0 g/l (R = 0.985) for the volume ratios of 10/5/3 and 1.0–5.0 g/l (R = 0.982) for the volume ratios of 10/5/0. Temperature (29–37 °C), pH (6–10) and some ions (NH₄⁺, NO₃⁻, Na⁺, Cl⁻) had no interference effect on the glucose measurement.     

高量子产率水溶性CdTe量子点的制备与表征

以巯基乙酸(HSCH2 COOH,TGA)为稳定剂,在水相中合成高量子产率CdTe量子点(QDs),产率达68%.用紫外.可见分光光度计、荧光分光光度计、红外光谱仪、透射电子显微镜等对制备的样品进行表征.结果表明:CdTe Ods紫外吸收峰及荧光发射峰均随回流时间延长而红移,即粒径在不断增大;荧光发射峰窄而对称,表明QDs分散性好、大小较均一,半峰宽随回流时间延长而逐渐变宽,表明粒径在增大的同时粒径分布范围也变宽;从TEM及紫外.可见光谱推算,可知其粒径约为3 nm;红外光谱图说明作为稳定剂的巯基乙酸对QDs表面起到修饰作用.     

Optimized Synthesis and Fluorescence Spectrum Analysis of CdSe Quantum Dots

An optimized synthesis route was applied for controlling the preparation of CdSe quantum dots (QDs) in an aqueous solution. Some key factors which influencing the properties of CdSe QDs, such as initial pH, stabilizers, ratio of precursor, etc. were investigated. The size, shape, crystal structure, and optical property of CdSe QDs were also characterized by TEM, XRD, UV-Vis, and fluorescence (FL) spectra. The result showed that high-quality cubic CdSe QDs with 3 nm were obtained. The experiments also confirmed that thioglycolic acid (TGA), under the conditions of weak acid, is a better stabilizer than others. The ratio of [Cd²⁺] to [SeSO₃ ^2?] played an important role in the formation of CdSe QDs. The mechanisms about the influence factors were also presented.     

柠檬酸盐稳定的水溶性CdSe量子点的合成及表征

以柠檬酸三钠为稳定剂在水溶液中合成了水溶性CdSe量子点,用X射线粉末衍射、透射电镜、紫外-可见吸收光谱和荧光发射光谱对CdSe量子点的结构、形貌及其荧光性质进行了表征.结果表明合成的CdSe量子点为立方闪锌矿结构,呈球形,分散性良好,平均尺寸约为2.6nm,具有窄且对称的荧光发射光谱,半峰宽为45nm.     

Spectroscopy and femtosecond dynamics of type-II CdTe/CdSe core-shell quantum dots.

Syntheses of CdTe/CdSe type-II quantum dots (QDs) using CdO and CdCl2 as precursors for core and shell, respectively, are reported. Characterization was made via near-IR interband emission, transmission electron microscopy (TEM), energy dispersive spectroscopy (EDX), and X-ray diffraction (XRD). Femtosecond fluorescence upconversion measurements on the relaxation dynamics of the CdTe core (in CdTe/CdSe) emission and CdTe/CdSe interband emission reveal that as the size of the core increases from 5.3, 6.1 to 6.9 nm, the rate of photoinduced electron separation decreases from 1.96, 1.44 to 1.07 x10(12) s(-1). The finite rates of the initial charge separation are tentatively rationalized by the small electron-phonon coupling, causing weak coupling between the initial and charge-separated states.