Crystal structure of BaMg2Si2O7 and Eu luminescence

Crystal structure of BaMg₂Si₂O₇ was determined and refined by a combined powder X-ray and neutron Rietveld method (monoclinic, C2/c, no. 15, Z=8, a=7.24553(8) Å, b=12.71376(14) Å, c=13.74813(15) Å, β=90.2107(8)°, V=1266.44(2) Å³; R_p/R_wp=3.38%/4.77%). The structure contains a single crystallographic type of Ba atom coordinated to eight O atoms with C₁ (1) site symmetry. Under 325-nm excitation Ba_0.98Eu_0.02Mg₂Si₂O₇ exhibits an asymmetric emission band around 402 nm. The asymmetric shape of the emission band is likely associated with a small electron-phonon coupling in BaMg₂Si₂O₇. The integrated intensity of the emission band was observed to remain constant over the temperature range 4.2-300 K.     

High-pressure transitions in MgAl2O4 and a new high-pressure phase of Mg2Al2O5

Phase transitions in MgAl₂O₄ were examined at 21-27 GPa and 1400-2500 °C using a multianvil apparatus. A mixture of MgO and Al₂O₃ corundum that are high-pressure dissociation products of MgAl₂O₄ spinel combines into calcium-ferrite type MgAl₂O₄ at 26-27 GPa and 1400-2000 °C. At temperature above 2000 °C at pressure below 25.5 GPa, a mixture of Al₂O₃ corundum and a new phase with Mg₂Al₂O₅ composition is stable. The transition boundary between the two fields has a strongly negative pressure-temperature slope. Structure analysis and Rietveld refinement on the basis of the powder X-ray diffraction profile of the Mg₂Al₂O₅ phase indicated that the phase represented a new structure type with orthorhombic symmetry (Pbam), and the lattice parameters were determined as a=9.3710(6) Å, b=12.1952(6) Å, c=2.7916(2) Å, V=319.03(3) Å³, Z=4. The structure consists of edge-sharing and corner-sharing (Mg, Al)O₆ octahedra, and contains chains of edge-sharing octahedra running along the c-axis. A part of Mg atoms are accommodated in six-coordinated trigonal prism sites in tunnels surrounded by the chains of edge-sharing (Mg, Al)O₆ octahedra. The structure is related with that of ludwigite (Mg, Fe²⁺)₂(Fe³⁺, Al)(BO₃)O₂. The molar volume of the Mg₂Al₂O₅ phase is smaller by 0.18% than sum of molar volumes of 2MgO and Al₂O₃ corundum. High-pressure dissociation to the mixture of corundum-type phase and the phase with ludwigite-related structure has been found only in MgAl₂O₄ among various A²⁺B³⁺₂O₄ compounds.     

K2Mo4O13 phases prepared by hydrothermal synthesis

Hydrothermal synthesis in the K-Mo oxide system was investigated as a function of the pH of the reaction medium. Four compounds were formed, including two K₂Mo₄O₁₃ phases. One is a new low-temperature polymorph, which crystallizes in the orthorhombic, space group Pbca, with Z=8 and unit cell dimensions a=7.544(1) Å, b=15.394(2) Å, c=18.568(3) Å. The other is the known triclinic K₂Mo₄O₁₃, whose structure was re-determined from single crystal data; its cell parameters were determined as a=7.976(2) Å, b=8.345(2) Å, c=10.017(2) Å, α=107.104(3)°, β=102.885(3)°, γ=109.760(3)°, which are the standard settings of the crystal lattice. The orthorhombic phase converts endothermically into triclinic phase at ca. 730 K with a heat of transition of 8.31 kJ/mol.     

Crystal chemistry of Co-doped Zn7Sb2O12

Zn₇Sb₂O₁₂ forms a full range of Co-containing α solid solutions, Zn_7−xCo_xSb₂O₁₂, with an inverse-spinel structure at high temperature. At low temperatures for x<2, the solid solutions transform into the low temperature β-polymorph. For x=0, the β→α transition occurs at 1225±25 °C; the transition temperature decreases with increasing x. At high x and low temperatures, α solid solutions are formed but are non-stoichiometric; the (Zn+Co):Sb ratio is >7:2 and the compensation for the deficiency in Sb is attributed to the partial oxidation of Co²⁺ to Co³⁺. From Rietveld refinements using ND data, Co occupies both octahedral and tetrahedral sites at intermediate values of x, but an octahedral preference attributed to crystal field stabilisation, causes the lattice parameter plot to deviate negatively from the Vegard's law. Sub-solidus compatibility relations in the ternary system ZnO-Sb₂O₅-CoO have been determined at 1100 °C for the compositions containing ?50% Sb₂O₅.     

Transition metal tetramolybdate dihydrates MMo4O13·2H2O (M=Co,Ni) having a novel pillared layer structure

Hydrothermal synthesis in the M/Mo/O (M=Co,Ni) system was investigated. Novel transition metal tetramolybdate dihydrates MMo₄O₁₃·2H₂O (M=Co,Ni), having an interesting pillared layer structure, were found. The molybdates crystallize in the triclinic system with space group P−1, Z=1 with unit cell parameters of a=5.525(3) Å, b=7.058(4) Å, c=7.551(5) Å, α=90.019(10)°, β=105.230(10)°, γ=90.286(10)° for CoMo₄O₁₃·2H₂O, and a=5.508(2) Å, b=7.017(3) Å, c=7.533(3) Å, α=90.152(6)°, β=105.216(6)°, γ=90.161(6)° for NiMo₄O₁₃·2H₂O The structure is composed of two-dimensional molybdenum-oxide (2D Mo-O) sheets pillared with CoO₆ octahedra. The 2D Mo-O sheet is made up of infinite straight ribbons built up by corner-sharing of four molybdenum octahedra (two MoO₆ and two MoO₅OH₂) sharing edges. These infinite ribbons are similar to the straight ones in triclinic-K₂Mo₄O₁₃ having 1D chain structure, but are linked one after another by corner-sharing to form a 2D sheet structure, like the twisted ribbons in BaMo₄O₁₃·2H₂O (or in orthorhombic-K₂Mo₄O₁₃) are.     

Rietveld refinement and photoluminescent properties of a new blue-emitting material: Eu activated SrZnP2O7

A new efficient blue phosphor, Eu²⁺ activated SrZnP₂O₇, has been synthesized at 1000 °C under reduced atmosphere and the crystal structure and photoluminescence properties have been investigated. The crystal structure of SrZnP₂O₇ was obtained via Rietveld refinement of powder X-ray diffraction (XRD) pattern. It was found that SrZnP₂O₇ crystallizes in space group of P2₁/n (no. 14), Z=4, and the unit cell dimensions are: a=5.30906(2) Å, b=8.21392(3) Å, c=12.73595(5) Å, β=90.1573(3)°, and V=555.390(3) Å³. Under ultraviolet excitation (200-400 nm), efficient Eu²⁺ emission peaked at 420 nm was observed, of which the luminescent efficiency at the optimal concentration of Eu²⁺ (4 mol%) was estimated to be 96% as that of BaMgAl₁₀O₁₇:Eu²⁺. Hence, the SrZnP₂O₇:Eu²⁺ exhibit great potential as a phosphor in different applications, such as ultraviolet light emitting diode and photo-therapy lamps.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

Synthesis, Structures, and Thermal Expansion of the La2W2−xMoxO9 Series

The La₂W_2−xMo_xO₉ series has been synthesized by the ceramic method. An alternative synthesis using microwave radiation is also reported. La₂W₂O₉ has two polymorphs and the low-temperature phase (α) transforms to the high-temperature form (β) at 1077°C. The influence of the W/Mo substitution in this phase transition has been investigated by DTA. The β structure for x≥0.7 compositions can be prepared as single phase at any cooling rate. The β phase for 0.3≤x≤0.7 compounds can be prepared as single phase by quenching, whereas a mixture of α and β phases is obtained by slow cooling. The W/Mo ratio in both coexisting phases is different with the β-phase having a higher Mo content. The x=0.1 and 0.2 compounds have been prepared as mixtures of phases. The room temperature structure of β-La₂W_1.7Mo_0.3O₉ has been analyzed by the Rietveld method in P2₁3 space group. The final R-factors were R_WP=9.0% and R_F=5.6% with a structure similar to that of β-La₂Mo₂O₉. Finally, the thermal expansion of both types of structures has been determined from a thermodiffractometric study. The thermal expansion coefficients were 2.9×10⁻⁶ and 9.7×10⁻⁶°C⁻¹ for α-La₂W₂O₉ and β-La₂W_1.2Mo_0.8O₉, respectively.     

XRD and Si MAS-NMR spectroscopy across the β-Lu2Si2O7-β-Y2Si2O7 solid solution

Samples in the system Lu_2−xY_xSi₂O₇ (0?x?2) have been synthesized following the sol-gel method and calcined to 1300 °C, a temperature at which the β-polymorph is known to be the stable phase for the end-members Lu₂Si₂O₇ and Y₂Si₂O₇. The XRD patterns of all the compositions studied are compatible with the structure of the β-polymorph. Unit cell parameters are calculated as a function of composition from XRD patterns. They show a linear change with increasing Y content, which indicates a solid solubility of β-Y₂Si₂O₇ in β-Lu₂Si₂O₇ at 1300 °C. ²⁹Si MAS NMR spectra of the different members of the system agree with the XRD results, showing a linear decrease of the ²⁹Si chemical shift with increasing Y content. Finally, a correlation reported in the literature to predict ²⁹Si chemical shifts in silicates is applied here to obtain the theoretical variation in ²⁹Si chemical shift values in the system Lu₂Si₂O₇-Y₂Si₂O₇ and the results compare favorably with the values obtained experimentally.     

Crystal growth and structural investigation of A2BReO6 (A=Sr, Ba; B=Li, Na)

Single crystals of the double perovskite rhenates A₂BReO₆ (A=Sr, Ba; B=Li, Na) were grown out of molten hydroxide fluxes. Single crystals of orange/yellow Ba₂LiReO₆, Ba₂NaReO₆ and Sr₂LiReO₆ were solved in the cubic, Fm-3m space group with a=8.1214(11) Å, 8.2975(3) Å, and 7.9071(15) Å, respectively, while Sr₂NaReO₆ was determined to be monoclinic P2₁/n with a=5.6737(6) Å, b=5.7988(6) Å, c=8.0431(8) Å, and β=90.02(6) °. The cubic structure consists of a rock salt lattice of corner-shared ReO₆ and MO₆ (M=Li, Na) octahedra which, in the monoclinic structure, are both tilted and rotated. A discrepancy exists between the symmetry of Sr₂LiReO₆ indicated by the single-crystal refinement of flux-grown crystals (cubic, Fm-3m) and the symmetry indicated by the powder diffraction data collected on polycrystalline samples prepared by the ceramic method (tetragonal, I4/m). It is possible that the cubic crystals are a kinetic product that forms in small quantities at low temperatures, while the powder represents the more stable polymorph that forms at higher reaction temperature.     

Magnetic properties of Mn2V2O7 single crystals

Magnetic properties of Mn₂V₂O₇ single crystals are investigated by means of magnetic susceptibility, magnetization, and heat capacity measurements. A structural phase transition of the α-β forms is clearly observed at the temperature range of 200-250 K and an antiferromagnetic ordering with magnetic anisotropy is observed below 20 K. A spin-flop transition is observed with magnetic field applied along the [110] axis of β-Mn₂V₂O₇, of which corresponds to the [001] axis of α-Mn₂V₂O₇, suggesting that the spins of Mn²⁺ ions locate within honeycomb layers which point likely in the [110] direction of β-Mn₂V₂O₇ or the [001] axis of α-Mn₂V₂O₇. However, a rather small jump of magnetization at spin-flop transition suggests a possible partition of crystal to some domains through β-to-α transition on cooling or much complex spin structure in honeycomb lattice with some frustration.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

Synthesis, characterization, and structure determination of the orthorhombic U2(PO4)(P3O10)

β-UP₂O₇ has been synthesized under hydrothermal conditions (θ=500°C, P=200 MPa), using UO₂ and H₃PO₄. β-UP₂O₇ crystallizes in the orthorhombic space group Pn2₁a, with a=11.526 (2) Å, b=7.048 (2) Å, c=12.807 (2) Å and Z=4. Its structure has been determined through direct methods and difference Fourier synthesis and has been refined to R=0.0396. The structure is built on UO₈ polyhedral chains along the b-axis. PO₄³⁻ and P₃O₁₀⁵⁻ groups coexist in the structure and the latter groups form non-linear chains. Cohesion of the structure is made through the linkage of UO₈ chains by PO₄ and P₃O₁₀ groups leading to the formula U₂(PO₄)(P₃O₁₀) instead of β-UP₂O₇. Vibrational and optical spectra confirm the results obtained by X-ray diffraction. DTA-TGA measurements show that the transformation of U₂(PO₄)(P₃O₁₀) to the cubic α-UP₂O₇ occurs at θ=870°C.     

The mercury chromates Hg6Cr2O9 and Hg6Cr2O10—Preparation and crystal structures, and thermal behaviour of Hg6Cr2O9

The basic mercury(I) chromate(VI), Hg₆Cr₂O₉ (=2Hg₂CrO₄·Hg₂O), has been obtained under hydrothermal conditions (200 °C, 5 days) in the form of orange needles as a by-product from reacting elemental mercury and K₂Cr₂O₇. Hydrothermal treatment of microcrystalline Hg₆Cr₂O₉ in demineralised water at 200 °C for 3 days led to crystal growth of red crystals of the basic mercury(I, II) chromate(VI), Hg₆Cr₂O₁₀ (=2Hg₂CrO₄·2HgO). The crystal structures were solved and refined from single crystal X-ray data sets. Hg₆Cr₂O₉: space group P2₁2₁2₁, Z=4, a=7.3573(12), b=8.0336(13), , 3492 structure factors, 109 parameters, R[F²>2σ(F²)]=0.0371, wR(F² all)=0.0517; Hg₆Cr₂O₁₀: space group Pca2₁, Z=4, a=11.4745(15), b=9.4359(12), , 3249 structure factors, 114 parameters, R[F²>2σ(F²)]=0.0398, wR(F² all)=0.0625. Both crystal structures are made up of an intricate mercury-oxygen network, subdivided into single building blocks [O-Hg-Hg-O] for the mercurous compound, and [O-Hg-Hg-O] and [O-Hg-O] for the mixed-valent compound. Hg₆Cr₂O₉ contains three different Hg₂²⁺ dumbbells, whereas Hg₆Cr₂O₁₀ contains two different Hg₂²⁺ dumbbells and two Hg²⁺ cations. The Hg^I-Hg^I distances are characteristic and range between 2.5031(15) and 2.5286(9) Å. All Hg₂²⁺ groups exhibit an unsymmetrical oxygen environment. The oxygen coordination of the Hg²⁺ cations is nearly linear with two tightly bonded O atoms at distances around 2.07 Å. For both structures, the chromate(VI) anions reside in the vacancies of the Hg-O network and deviate only slightly from the ideal tetrahedral geometry with average Cr-O distances of ca. 1.66 Å. Upon heating at temperatures above 385 °C, Hg₆Cr₂O₉ decomposes in a four-step mechanism with Cr₂O₃ as the end-product at temperatures above 620 °C.     

Synthesis, X-ray crystal structure and vibrational spectroscopy of the acidic pyrophosphate KMg0.5H2P2O7·H2O

The hydrated potassium hemimagnesium dihydrogen pyrophosphate KMg_0.5H₂P₂O₇·H₂O was synthesized. It crystallizes in the triclinic system, space group (n. 2), Z=2, with the following unit-cell parameters: a=6.8565(2) Å, b=7.3621(3) Å, c=7.6202(3) Å, α=81.044(2)°, β=72.248(2)°, γ=83.314(3)°, V=360.90(2) Å³. The structure was obtained by single-crystal X-ray diffractometry, and a full-matrix least-squares refinement based on F² gave a final R index of =0.0368 (wR=0.0975), utilizing 1446 observed reflections with I>2σ(I). The crystal packing consists in a three-dimensional network made by layers parallel to ab plane of PO₄ double tetrahedra and MgO₆ octahedra, linked by hydrogen bonds, while K atoms form complex coordination within cavities between tetrahedra and octahedra. The dihydro-pyrophosphate anion (H₂P₂O₇)²⁻ shows bent eclipsed conformation and the Mg²⁺ ion lies on inversion center. No coincidences observed between most of infrared and Raman spectral bands confirmed the centrosymmetric structure of the title compound; the vibrational spectra point to a bent POP bridge angle.     

Synthesis and structural investigation of the compounds containing HF2 anions: Ca(HF2)2, Ba4F4(HF2)(PF6)3 and Pb2F2(HF2)(PF6)

Three new compounds Ca(HF₂)₂, Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) were obtained in the system metal(II) fluoride and anhydrous HF (aHF) acidified with excessive PF₅. The obtained polymeric solids are slightly soluble in aHF and they crystallize out of their aHF solutions. Ca(HF₂)₂ was prepared by simply dissolving CaF₂ in a neutral aHF. It represents the second known compound with homoleptic HF environment of the central atom besides Ba(H₃F₄)₂. The compounds Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) represent two additional examples of the formation of a polymeric zigzag ladder or ribbon composed of metal cation and fluoride anion (MF⁺)_n besides PbF(AsF₆), the first isolated compound with such zigzag ladder. The obtained new compounds were characterized by X-ray single crystal diffraction method and partly by Raman spectroscopy. Ba₄F₄(HF₂)(PF₆)₃ crystallizes in a triclinic space group P1¯ with a=4.5870(2) Å, b=8.8327(3) Å, c=11.2489(3) Å, α=67.758(9)°, β=84.722(12), γ=78.283(12)°, V=413.00(3) Å³ at 200 K, Z=1 and R=0.0588. Pb₂F₂(HF₂)(PF₆) at 200 K: space group P1¯, a=4.5722(19) Å, b=4.763(2) Å, c=8.818(4) Å, α=86.967(10)°, β=76.774(10)°, γ=83.230(12)°, V=185.55(14) ų, Z=1 and R=0.0937. Pb₂F₂(HF₂)(PF₆) at 293 K: space group P1¯, a=4.586(2) Å, b=4.781(3) Å, c=8.831(5) Å, α=87.106(13)°, β=76.830(13)°, γ=83.531(11)°, V=187.27(18) Å³, Z=1 and R=0.072. Ca(HF₂)₂ crystallizes in an orthorhombic Fddd space group with a=5.5709(6) Å, b=10.1111(9) Å, c=10.5945(10) Å, V=596.77(10) Å³ at 200 K, Z=8 and R=0.028.     

Effect of sintering on the ionic conductivity of garnet-related structure Li5La3Nb2O12 and In- and K-doped Li5La3Nb2O12

Garnet-structure related metal oxides with the nominal chemical composition of Li₅La₃Nb₂O₁₂, In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ and K-substituted Li_5.5La_2.75K_0.25Nb₂O₁₂ were prepared by solid-state reactions at 900, 950, and 1000 °C using appropriate amounts of corresponding metal oxides, nitrates and carbonates. The powder XRD data reveal that the In- and K-doped compounds are isostructural with the parent compound Li₅La₃Nb₂O₁₂. The variation in the cubic lattice parameter was found to change with the size of the dopant ions, for example, substitution of larger In³⁺(r_CN6: 0.79 Å) for smaller Nb⁵⁺ (r_CN6: 0.64 Å) shows an increase in the lattice parameter from 12.8005(9) to 12.826(1) Å at 1000 °C. Samples prepared at higher temperatures (950, 1000 °C) show mainly bulk lithium ion conductivity in contrast to those synthesized at lower temperatures (900 °C). The activation energies for the ionic conductivities are comparable for all samples. Partial substitution of K⁺ for La³⁺ and In³⁺ for Nb⁵⁺ in Li₅La₃Nb₂O₁₂ exhibits slightly higher ionic conductivity than that of the parent compound over the investigated temperature regime 25-300 °C. Among the compounds investigated, the In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ exhibits the highest bulk lithium ion conductivity of 1.8×10⁻⁴ S/cm at 50 °C with an activation energy of 0.51 eV. The diffusivity (“component diffusion coefficient”) obtained from the AC conductivity and powder XRD data falls in the range 10⁻¹⁰-10⁻⁷ cm²/s over the temperature regime 50-200 °C, which is extraordinarily high and comparable with liquids. Substitution of Al, Co, and Ni for Nb in Li₅La₃Nb₂O₁₂ was found to be unsuccessful under the investigated conditions.     

Phase relations, crystal chemistry, and dielectric properties in sections of the La2O3-CaO-MgO-TiO2 system

Subsolidus phase equilibria and crystal chemistry were studied for the La₂O₃-MgO-TiO₂ system and for the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃ in the quaternary La₂O₃-CaO-MgO-TiO₂ system. Dielectric properties (relative permittivity and temperature coefficient of resonant frequency, τ_f) were measured at 5-10 GHz and mapped onto the phase equilibria relations to reveal the compositions of temperature-stable (τ_f=0) compounds and mixtures. Phase equilibria relations were obtained by X-ray powder diffraction analysis of approximately 80 specimens prepared by solid-state reactions in air at ∼1450°C. Six ternary phases were found to form in the La₂O₃-MgO-TiO₂ system, including the three previously reported compounds LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, and “La₆MgTi₄O₁₈”; and the new phases La₁₀MgTi₉O₃₄, La₉Mg_0.5Ti_8.5O₃₁, and a perovskite-type solid solution (1−x)LaMg_1/2Ti_1/2O₃-xLa_2/3TiO₃ (0?x?0.5). The phase previously reported as “La₆MgTi₄O₁₈” was found to form off-composition, apparently as a point compound, at La₆Mg_0.913Ti_4.04O₁₈. Indexed experimental X-ray powder diffraction patterns are given for LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, La₆Mg_0.913Ti_4.04O₁₈, La₁₀MgTi₉O₃₄, and La₉Mg_0.5Ti_8.5O₃₁. LaMg_1/2Ti_1/2O₃ exhibits a slightly distorted perovskite structure with ordered B-cations (P2₁/n; a=5.5608(2) Å, b=5.5749(3) Å, c=7.8610(5) Å, β=90.034(4)°). La₅Mg_0.5Ti_3.5O₁₅ (Pm1; a=5.5639(1), c=10.9928(5) Å) and La₆Mg_0.913Ti_4.04O₁₈ (R3m; a=5.5665(1), c=39.7354(9) Å) are n=5 and n=6 members, respectively, of the (111) perovskite-slab series A_nB_n−1O_3n. The new phases La₁₀MgTi₉O₃₄ (a=5.5411(2), b=31.3039(9), c=3.9167(1) Å) and La₉Mg_0.5Ti_8.5O₃₁ (a=5.5431(2), b=57.055(1), c=3.9123(1) Å) are n=5 and n=4.5 members, respectively, of the (110) perovskite-slab series A_nB_nO_3n+2, which exhibit orthorhombic subcells; electron diffraction revealed monoclinic superlattices with doubled c-parameters for both compounds. Extensive perovskite-type solid solutions form in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃. The La₂O₃-MgO-TiO₂ system contains two regions of temperature-stable (τ_f=0) compositions. The quaternary La₂O₃-CaO-MgO-TiO₂ system contains an extensive single-phase perovskite-type volume through which passes a surface of temperature-stable compositions with permittivities projected to be in the 40-50 range. Traces of this surface occur as lines of τ_f=0 perovskite-type phases in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃.