自然界中三角和斐波纳契数的叶序花样随处可见.通过控制几何条件以及冷却之后产生的应力,这些花样能在Ag内核/SiOx壳层微结构（约10μm大小）上予以实现.在这种内核/壳结构表面上,大小形状十分一致的小球通过自组装是形成斐波纳契数花样（我们观察到5×8, 8×13和13×21三种）还是三角花样,取决于基座面的几何构形.作者工作的意义在于揭示了在适当的几何约束下,自组装形成的花样是总应变能最小的结果.这对叶序花样的形成来源提出了一种非遗传的机理.此外,作者的研究表明,高度有序的、甚至含有内禀缺陷的微结构可以通过应力工程在大面积范围内同时得到.     

ZrO2／SiO2多层膜中膜厚组合周期数及基底材料对残余应力的影响

ZrO₂／SiO₂多层膜由相同沉积条件下的电子束蒸发方法制备而成， 通过改变多层膜中高(ZrO₂)、低(SiO₂)折射率材料膜厚组合周期数的方法，研究了沉积 在熔石英和BK7玻璃 基底上多层膜中残余应力的变化. 用ZYGO光学干涉仪测量了基底镀膜前后曲率半径的变化， 并确定了薄膜中的残余应力. 结果发现，该多层膜中的残余应力为压应力，随着薄膜中膜厚 组合周期数的增加，压应力值逐渐减小. 而且在相同条件下，石英基底上所沉积多层膜中的 压应力值要小于BK7玻璃基底上所沉积多层膜中的压应力值. 用x射线衍射技术测量分析了膜 厚组合周期数不同的ZrO₂／SiO₂多层膜微结构，发现随着周期数增 加，多层膜的结晶程 度增强. 同时多层膜的微结构应变表现出了与所测应力不一致的变化趋势，这主要是由多层 膜中，膜层界面之间复杂的相互作用引起的. 关键词： 2／SiO₂多层膜')" href="#">ZrO₂／SiO₂多层膜 残余应力 膜厚组合周期数     

An oxide/silicon core/shell nanowire metal-oxide semiconductor field-effect transistor

This paper studies an oxide/silicon core/shell nanowire MOSFET(OS-CSNM).Through three-dimensional device simulations,we have demonstrated that the OS-CSNM has a lower leakage current and higher I on /I off ratio after introducing the oxide core into a traditional nanowire MOSFET(TNM).The oxide/silicon OS-CSNM structure suppresses threshold voltage roll-off,drain induced barrier lowering and subthreshold swing degradation.Smaller intrinsic device delay is also observed in OS-CSNM in comparison with that of TNM.     

Synthesis and ignition of energetic CuO/Al core/shell nanowires

Energetic thermites (mixtures of Al and metal oxides), due to their high energy densities, have broad applications in propulsion, thermal batteries, waste disposal, and power generation for micro systems. Reducing the sizes of Al and metal oxides down to the nanoscale has been shown to be effective in increasing their reaction rates and reducing their ignition delays. However, it remains a challenge to create mixtures of Al and metal oxides with nanoscale uniformity. Here we report synthesis and ignition studies on thermites with a new nanostructure, i.e., CuO/Al core/shell nanowires (NWs). The CuO NW cores were synthesized by the thermal annealing of copper films and served as templates for the deposition of Al shells by subsequent sputtering. The advantage of such a core/shell NW structure is that CuO and Al are uniformly mixed at the nanoscale. The onset temperatures of the exothermic reaction of the core/shell NWs were similar to those of nanoparticle (NP)-based thermites in terms of magnitude, insensitivity to equivalence ratios and sensitivity to heating rates. Moreover, the core/shell NW thermites, compared to NP-based thermites, exhibit greatly improved mixing uniformity and reduced activation energy for the thermite reaction.     

Cu/C核/壳纳米结构的气相合成、形成机理及其光学性能研究

采用乙酰丙酮铜为原料, 通过化学气相沉积大批量制备出Cu/C核/壳纳米颗粒和纳米线. 研究结果表明, 通过控制沉积温度可对Cu/C核/壳纳米材料的形貌和结构进行很好的控制. 比如, 沉积温度为400 ℃时可获得直径约200 nm的Cu/C核/壳纳米线, 沉积温度为450 ℃ 时可获得直径约200 nm的Cu/C核/壳纳米颗粒和纳米棒的混合产物, 沉积温度为600 ℃时可获得直径约22 nm的Cu/C核/壳纳米颗粒. 获得的Cu/C核/壳纳米结构是由一个新颖的凝聚机理形成的, 而这种机理不同于著名的溶解-析出机理. 紫外-可见光谱和荧光光谱分析结果表明: Cu/C核/壳纳米线和纳米颗粒均在225 nm处出现Cu的吸收峰, 同时在620 和616 nm处分别出现了纳米线和纳米颗粒的表面等离子共振吸收峰. Cu/C核/壳纳米线在312 和348 nm处、 Cu/C核/壳纳米颗粒在304 和345 nm处出现荧光发射谱峰. 关键词： Cu/C核/壳结构 纳米线 纳米颗粒 光学性能     

Magnetic properties of Ni/Au core/shell studied by Monte Carlo simulations

The magnetic properties of ferromagnetic Ni/Au core/shell have been studied using Monte Carlo simulations within the Ising model framework. The considered Hamiltonian includes the exchange interactions between Ni–Ni, Au–Au and Ni–Au and the external magnetic field. The thermal total magnetizations and total magnetic susceptibilities of core/shell Ni/Au are computed. The critical temperature is deduced. The exchange interaction between Ni and Au atoms is obtained. In addition, the total magnetizations versus the external magnetic field and crystal filed for different temperature are also established.     

小粒径同质/异质壳层结构NaGdF_4:3%Nd~(3+)纳米颗粒的近红外发光特性

采用共沉淀法制备了粒径小于5 nm的六方相NaGdF_4:3%Nd~(3+)纳米颗粒.纳米颗粒表面缺陷会使发光中心产生严重的淬灭,对其表面包覆适当厚度的壳层可以有效地减少发光淬灭,提高发光性能.对NaGdF_4:3%Nd~(3+)核心纳米颗粒分别进行同质和异质包覆并且通过调节核壳比制备了不同壳层厚度的NaGdF_4:3%Nd~(3+)@NaGdF_4和NaGdF_4:3%Nd~(3+)@Na YF4纳米颗粒,研究了不同的壳层厚度对核心纳米颗粒发光的影响,并对两种不同核壳结构纳米颗粒的发光性能进行了对比.在808 nm近红外光激发下,NaGdF_4:3%Nd~(3+)纳米颗粒发射出位于约866,893,1060 nm的近红外发射.与核心纳米颗粒相比,核壳结构的纳米颗粒的荧光强度增强,荧光寿命增长,并且随着壳厚的增加,荧光强度出现先增强后减弱、荧光寿命逐步增长的趋势.与相同条件下同质包覆的NaGdF_4:3%Nd~(3+)@NaGdF_4纳米颗粒相比,异质包覆的NaGdF_4:3%Nd~(3+)@NaYF_4纳米颗粒光谱荧光强度增强,寿命增长.     

Preparation and characterization of core/shell particles with siloxane in the shell

The core/shell particles consisting of polystyrene core and 3-(methacryloxypropyl)-trimethoxysilane (MPS) shell were prepared in the present study by successive seeding polymerization under kinetically controlled conditions and were characterized by particle size analyser, transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). The TEM image indicated that the particles containing organic siloxane presented an evident core/shell structure. Additionally, the study of XPS also revealed that MPS could be grafted onto the surface of polystyrene microspheres and the atomic ratio of C/Si on the surface of the core/shell particles (MPS-40) was very close to the ratio of C/Si in the molecule of MPS. The surface properties of the films produced from the core/shell particles were also investigated by the static contact angle method. Compared with the homopolymer of PS, the core/shell particles were more effective to create hydrophobic surface, so, the introduction of MPS was capable of obvious increase in water repellency.     

Reduced-temperature ordering of FePt nanoparticle assembled films by Fe30Pt70/Fe3O4 core/shell structure

In this paper, Fe30Pt70/Fe3O4 core/shell nanoparticles were synthesized by chemical routine and the layered polyethylenimine （PEI）-Fe30Pt70/Fe3O4 structure was constructed by molecule-mediated self-assembly technique. The dimension of core/shell structured nanoparticles was that of 4nm core and 2 nm shell. After annealing under a flow of forming gas （50%Ar2＋30%H2） for 1 h at or above 400℃, the iron oxide shell was reduced to Fe and diffused to Pt-rieh core, which leaded to the formation of L1. phase FePt at low temperature. The x-ray diffraction results and magnetic properties measurement showed that the chemical ordering temperature of Fe30Pt70/Fe3O4 core/shell nanoparticles assembly can be reduced to as low as 400℃. The sample annealed at 400℃ showed the eoereivity of 4KOe with the applied field of 1.5T. The core/shell structure was suggested to be an effective way to reduce the ordering temperature obviously.[第一段]     

High performance Au/Ag core/shell bipyramids for determination of thiram based on surface‐enhanced Raman scattering

Au/Ag core/shell bipyramids were used as surface‐enhanced Raman scattering (SERS) substrates to determine the thiram. The metallic substrates showed high SERS performance and are very suitable for the analytical sensors. The fabrication and characterization of the Au/Ag core/shell bipyramids were described. The influence of experimental parameters, such as the thickness of Ag shell of the bipyramids, sodium chloride concentration, and pH value on SERS of thiram was examined and optimized. Under the optimum conditions, thiram molecules were effectively adsorbed onto bipyramids and the SERS intensity is proportional to the concentration of thiram in the range of 3.3 to 400.0 ng mL^–1. The corresponding correlation coefficient of the linear equation is 0.997, which indicates that there is a good linear relationship between SERS intensity and thiram concentration. The limit of detection for thiram is 2.0 ng mL^–1. The experimental results indicate that the proposed method is a viable method for determination of thiram. Some environmental water samples were analyzed and the analytical results were satisfactory. Copyright © 2012 John Wiley & Sons, Ltd.     

Synthesis and magnetic properties of carbon-coated Ni/SiO_2 core/shell nanocomposites

A simple method for the synthesis of carbon-coated Ni/SiO2 core/shell nanocomposites is reported. The Ni nanoparticles were coated with silica layers via a combined procedure of sol-gel fabrication and hydrogen reduction prior to carbon coating via acetylene decomposition at an appropriate temperature. It was found that the anti-acid ability of the Ni/SiO2 composites was greatly enhanced after carbon coating. The results of magnetization measurement show that the real part (μ′) of complex permeability of the as-obtained sample is almost independent of frequency, and the imaginary part (μ″) stays small up to a frequency of 1 GHz. The encapsulation of Ni particles with SiO2 results in the rise of Ni nanoparticles resistivity. The outcome is the reduction in effect of eddy current at high frequency, making the real part μ′ almost constant and the imaginary part μ″ very small. Thus, this simple method may be effective for preparing composites of soft magnetic properties, especially in the high-frequency range.     

利用激光烧蚀法制备表面等离子体可调谐的金核银壳层纳米颗粒胶体

利用激光烧蚀方法在水中制备了金核银壳层纳米颗粒胶体,发现这种复合胶体的等离子体振动吸收峰频率会随着激光烧蚀时间的不同而发生改变。利用等离子杂化理论定性解释了共振吸收峰可调谐的物理机制.