A Flexible Composite Mechanical Energy Harvester from a Ferroelectric Organoamino Phosphonium Salt

A new binary organic salt diphenyl diisopropylamino phosphonium hexaflurophosphate (DPDP?PF₆) was shown to exhibit a good ferroelectric response and employed for mechanical energy harvesting application. The phosphonium salt crystallizes in the monoclinic noncentrosymmetric space group Cc and exhibits an H‐bonded 1D chain structure due to N?H???F interactions. Ferroelectric measurements on the single crystals of DPDP?PF₆ gave a well‐saturated rectangular hysteresis loop with a remnant (P_r) polarization value of 6 μC cm^?2. Further, composite devices based on polydimethylsiloxane (PDMS) films for various weight percentages (3, 5, 7, 10 and 20 wt %) of DPDP?PF₆ were prepared and examined for power generation by using an impact test setup. A maximum output peak‐to‐peak voltage (V_PP) of 8.5 V and an output peak‐to‐peak current (I_PP) of 0.5 μA was obtained for the non‐poled composite film with 10 wt % of DPDP?PF₆. These results show the efficacy of organic ferroelectric substances as potential micropower generators.     

Piezoelectric Energy Harvesting from a Ferroelectric Hybrid Salt [Ph3MeP]4[Ni(NCS)6] Embedded in a Polymer Matrix

Organic–inorganic hybrid ferroelectrics are an exciting class of molecular materials with promising applications in the area of energy and electronics. The synthesis, ferroelectric and piezoelectric energy harvesting behavior of a 3d metal ion‐containing A₄BX₆ type organic–inorganic hybrid salt [Ph₃MeP]₄[Ni(NCS)₆] ( 1 ) is now presented. P‐E hysteresis loop studies on 1 show a remnant ferroelectric polarization value of 18.71 μC cm^?2, at room temperature. Composite thermoplastic polyurethane (TPU) devices with 5, 10, 15 and 20 wt % compositions of 1 were prepared and employed for piezoelectric energy harvesting studies. A maximum output voltage of 19.29 V and a calculated power density value of 2.51 mW cm^?3 were observed for the 15 wt % 1 ‐TPU device. The capacitor charging experiments on the 15 wt % 1 ‐TPU composite device shows an excellent energy storage performance with the highest stored energies and measured charges of 198.8 μJ and 600 μC, respectively.     

A Flexible Energy Harvester from an Organic Ferroelectric Ammonium Salt

Organic ferroelectrics due to their low cost, easy preparation, light weight, high flexibility and phase stability are gaining tremendous attention in the field of portable electronics. In this work, we report the synthesis, structure and ferroelectric behavior of a two-component ammonium salt 2 , containing a bulky [Bn(4-BrBn)NMe₂]⁺ (Bn=benzyl and 4-BrBn=4-bromobenzyl) cation and tetrahedral (BF₄)⁻ anion. The structural analysis revealed the presence of rich non-classical C−H⋅⋅⋅F and C−H⋅⋅⋅Br interactions in this molecule that were quantified by Hirshfeld surface analysis. The polarization (P) vs. electric field (E) hysteresis loop measurements on 2 gave a remnant polarization (P_r) of 14.4 μC cm⁻² at room temperature. Flexible polymer composites with various (5, 10, 15 and 20) weight percentages (wt%) of 2 in thermoplastic polyurethane (TPU) were prepared and tested for mechanical energy harvesting applications. A notable peak-to-peak output voltage of 20 V, maximum current density of 1.1 μA cm⁻² and power density of 21.1 μW cm⁻² were recorded for the 15 wt% 2 -TPU composite device. Furthermore, the voltage output generated from this device was utilized to rapidly charge a 100 μF capacitor, with stored energies and measured charges of 156 μJ and 121.6 μC, respectively.