A study of the properties and microstructure of Ni81Fe19 ultrathin films with MgO

The anisotropic magnetoresistance (AMR) of a Ta (5 nm)/MgO (3 nm)/Ni₈₁Fe₁₉ (10 nm)/MgO (2 nm)/Ta (3 nm) film with MgO-Nano Oxide Layer (NOL) increases dramatically from 1.05% to 3.24% compared with a Ta (5 nm)/Ni₈₁Fe₁₉ (10 nm)/Ta (3 nm) film without the MgO-NOL layer after annealing at 380 °C for 2 h. Although the MgO destroys the NiFe (1 1 1) texture, it enhances the specular electron scattering of the conduction electrons at the NOL interface and suppresses the interface reactions and diffusion at the Ta/NiFe and NiFe/Ta interfaces. The NiFe (1 1 1) texture was formed after the annealing, resulting in a higher AMR ratio. X-ray photoelectron spectroscope results show that Mg and Mg²⁺ were present in the MgO_x films.     

Exchange bias and negative magnetoresistance in [Co/Bi/Co]/IrMn thin films]

The artificial control of grain-boundary resistance and its contribution to magnetic and magneto-transport properties in [Co(3 nm)/Bi(2.5 nm)/Co(3 nm)]Ir₂₀Mn₈₀(12 nm) thin films that exhibit exchange bias is studied. Transverse magnetoresistance (MR) loops exhibit a negative MR in thin films grown by magnetron sputtering on Si/SiN_x(100 nm) substrates. This negative MR effect is of the giant-MR (GMR) type, although its magnitude is less than 1%. A considerable exchange bias (EB) effect is observed only at lower temperatures, where both, GMR and isothermal magnetization loops exhibit a shift of −600 Oe at 5 K.     

Magnetic properties of nanocrystalline Ni0.7Mn0.3Gd0.1Fe1.9O4 ferrite at low temperatures

Mössbauer spectra and magnetic measurement of Ni_0.7Mn_0.3Gd_0.1Fe_1.9O₄ ferrite were investigated by Oxford MS-500 Mössbauer spectrometer and superconducting quantum interference device (SQUID) magnetometer with a field 5 T. Ni_0.7Mn_0.3Gd_0.1Fe_1.9O₄ nanoparticles have a considerable coercivity of 1040 Oe when the test temperature is reduced to 2 K. Mössbauer spectra show that Ni_0.7Mn_0.3Gd_0.1Fe_1.9O₄ nanoparticles exhibit superparamagnetism at room temperature and ferrimagnetism at 77 K.     

Synthesis and magnetic properties of Au-coated amorphous Fe20Ni80 nanoparticles

Gold-coated nanoparticles of Fe₂₀Ni₈₀ (permalloy) have been synthesized by a microemulsion process. The as-prepared samples consist of ∼5 nm diameter particles of amorphous Fe₂₀Ni₈₀ that are likely encapsulated in B₂O₃. One or more Fe₂₀Ni₈₀@B₂O₃ particles are subsequently encapsulated in 8-20 nm gold nanospheres, as determined by TEM and X-ray powder diffraction (XRD) line broadening. The gold shells were found to be under expansive strain. Magnetic data confirm the existence of a superparamagnetic phase with a blocking temperature, T_B, of ∼33 K. The saturation magnetization, M_S, of the as-prepared, Au-coated sample is ∼65 emu g⁻¹ at 5 K and ∼16 emu g⁻¹ at 300 K. The coercivity, H_C, is ∼280 Oe at 5 K.     

Effect of Co underlayer on soft magnetic properties and microstructure of FeCo thin films

High saturation magnetization soft magnetic FeCo (=Fe₆₅Co₃₅) films were prepared using a thin Co underlayer. The FeCo/Co films exhibited a well-defined in-plane uniaxial anisotropy with easy axis coercivity (H_ce) of 10 Oe and hard axis coercivity (H_ch) of 3 Oe, and a half reduction of H_c with H_ce=4.8 Oe and H_ch=1.0 Oe was obtained when the composition was adjusted to 25 at% Co. The effective permeability of the films remains flat around 250 to 800 MHz. The saturation magnetostriction was 5.2×10⁻⁵ and the intrinsic stress was 0.8 GPa in FeCo single layer, both were slightly reduced by Co underlayer. The Co underlayer changed the preferred orientation of the FeCo films from (2 0 0) to (1 1 0) but more significantly, reduced the average grain size from ∼74 to ∼8.2 nm. It also reduced the surface roughness from 2.351 to 0.751 nm. The initial stage and interface diffusion properties were examined by TEM and XPS.     

Preference orientation and magnetic properties of CoxFe3−xO4 nanocrystalline thin films on quartz substrate

Nanocrystalline spinel ferrite thin films of Co_xFe_3−xO₄ (x=0.3$x=0.3$, 0.5, 0.8, and 1.0) have been prepared by RF sputtering on quartz substrate without a buffer layer at room temperature and annealed at the temperature range from 200 to 600 °C in air. The as-sputtered films exhibit the preferred orientation and the high magnetization and coercivity. After annealing, the preferred orientations become poor, but the magnetization and coercivity increase. The sample with a magnetization of 455 emu/cm³, a coercivity of 2.8 kOe, a remanence ratio of 0.72, and a maximum energy product of 2.4 MGOe has been obtained. The influence of Co ions and annealing temperature on the magnetic properties has been discussed.     

Positive exchange bias in a Ni80Fe20/NixFe1−xO thin-film bilayer

We have measured positive exchange bias in a Ni₈₀Fe₂₀/Ni_xFe_1−xO thin-film nanocrystallite system. A series of solid solution Ni_xFe_1−xO 40 nm thick films capped with 25 nm thick Ni₈₀Fe₂₀ were deposited using a range of %O₂/Ar bombardment energies (i.e. End-Hall voltages). Proper tuning of the deposition conditions results in a Ni₈₀Fe₂₀/Ni_xFe_1−xO (30%O₂/Ar) based bilayer that exhibits a positive exchange bias loop shift of H_ex∼60 Oe at 150 K.     

Structure,magnetic properties and magnetostriction of Fe81Ga19 thin films

The structure, magnetic properties and magnetostriction of Fe₈₁Ga₁₉ thin films have been investigated by using X-ray diffraction analysis, scanning electron microscope (SEM), vibrating sample magnetometer and capacitive cantilever method. It was found that the grain size of as-deposited Fe₈₁Ga₁₉ thin films is 50–60 nm and the grain size increases with increase in the annealing temperature. The remanence ratio (M_r/M_s) of the thin films slowly decreases with increase in the annealing temperature. However, the coercivity of the thin films goes the opposite way with increase in the annealing temperature. A preferential orientation of the Fe₈₁Ga₁₉ thin film fabricated under an applied magnetic field exists along 〈1 0 0〉 direction due to the function of magnetic field during sputtering. An in-plane-induced anisotropy of the thin film is well formed by the applied magnetic field during the sputtering and the formation of in-plane-induced anisotropy results in 90° rotations of the magnetic domains during magnetization and in the increase of magnetostriction for the thin film.     

Magnetic and structural properties of laminated Co65Fe35 films

We report on coercivity mechanisms in Co₆₅Fe₃₅ films. Using a unique High Target Utilisation Sputtering System (HiTUS) sputtering system we have produced a range of samples with controlled grain size in the range 6-30 nm. This has enabled an evaluation of the effects of different seed layers (Ru, Cu, Ta and Mg) and the effects of lamination of the films. We found that in 100 Å single-layer films the coercivity rises abruptly from 29 to 90 Oe with grain size. We found that samples with Cu or Ru seed layers show the largest reduction in coercivity. The effects of lamination are more complex since it leads to a reduction in grain size whereas coercivity increases. We believe this is due to RKKY coupling through the metallic interlayers.     

Influence of milling time on the structural, microstructural and magnetic properties of mechanically alloyed Ni58Fe12Zr10Hf10B10 nanostructured/amorphous powders

This paper investigates structural, microstructural and magnetic properties of amorphous/nanocrystalline Ni₅₈Fe₁₂Zr₁₀Hf₁₀B₁₀ powders prepared by high energy milling. Ball milling of Ni, Fe, Zr, Hf and B leads to alloying of the element powders at 120 h. The results show that at 190 h the amorphous content is at the highest level and the grain size is about 2 nm. The magnetic measurements reveal that the coercivity and the saturation magnetization reach about 20 Oe and 30 emu/g at 190 h and become approximately 5 Oe and 40 emu/g after a suitable heat treatment, respectively.     

The influence of pH and bath composition on the properties of Fe-Co alloy film electrodeposition

Fe-Co films were electrodeposited on ITO glass substrates from the electrolytes with different molar ratio of Co²⁺/Fe²⁺ and different pH values (2.1, 2.9, 3.7, and 4.3) at 25 °C. The properties of Fe-Co alloy films depend on both Co²⁺ and Fe²⁺ concentrations in electrolyte and pH values was studied. The content of Co increases from 40% to 85% as the mole ratio of CoSO₄/FeSO₄ increasing from 0.50/0.50 to 0.90/0.10 in electrolyte and slightly decreases from 77% to 63% as the pH values increasing from 2.1 to 4.3. The X-ray diffraction analysis reveals that the structures of the films strongly depend on the Co content in the binary films. The surface morphologies of the films are influenced by the combined action of composition and phase structure. The saturation magnetization reaches a maximum value of 2974.03 emu/cm³ and coercivity reaches a minimum value of 42.72 Oe of the Fe_0.30Co_0.70. The saturation magnetization reaches a maximum values of 2974.03 emu/cm³ and coercivity reaches a minimum values of 42.72 Oe of the Fe_0.30Co_0.70 at pH = 2.9.     

Simultaneous variations of microstructure and magnetic properties of Ni58Fe12Zr20B10 nanostructure/amorphous alloy prepared by mechanical alloying

This study aims to evaluate magnetic and micro-structural properties of amorphous/nanocrystalline mechanically alloyed Ni₅₈Fe₁₂Zr₂₀B₁₀ powders with ball-milling time up to 190 h. Structural, micro-structural and thermal evaluations of the milled powders were carried out by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and differential scanning calorimetry (DSC) methods. Magnetic properties were also measured by a vibrating sample magnetometer (VSM) instrument. Results showed that the amorphous phase reached maximum value of 95% and the crystallite size was about 3 nm at the end of the milling. Magnetization saturation (M_s) decreased slightly and coercivity (H_c) reached to the highest value at 72 h of the milling time. At the 190 h of milling, the coercivity and saturation magnetization reached 18 Oe and 20 emu/g, respectively. While, after an appropriate amount of heat treatment, these two variables became approximately 2 Oe and 32 emu/g.     

Fabrication, magnetism and high frequency application of exchange-coupled Fe65Co35±2-SiO1.7±0.2 granular films

A series of (Fe₆₅Co_35±2)_x-(SiO_1.7±0.2)_1−x nano-granular films with various metal volume fractions (x) were fabricated by rf sputtering. In a wide range, excellent soft magnetic properties have been achieved. In the x range from 0.7 to 0.48, the films exhibit small coercivity H_c not exceeding 4 Oe and high electrical resistivity ρ up to 1.15 × 10⁴ μΩ cm. And a minimum H_c value of 1.65 Oe was obtained for the sample of x = 0.57 with ρ = 2.86 × 10³ μΩ cm. At a frequency lower than 2.0 GHz, the real part μ′ of complex permeability of this sample is more than 170 and the FMR frequency is as high as 2.6 GHz, implying a high cut-off frequency for high frequency applications. With decreasing Fe₆₅Co_35±2 volume fraction, the resistivity of films increases remarkably and the grain size decreases obviously. At the same time, the coercivity H_c decreases with grain size decreasing, which is consistent with the conclusion resulted from random anisotropy model quoted by Herzer. Study on Henkel plots shows that intergranular ferromagnetic exchange coupling exists among grains and is important for realizing soft magnetic properties.     

Out-of-plane low field anisotropic magnetoresistance in Nd0.51Sr0.49MnO3 thin films

A comparative study of the out-of-plane anisotropic magnetoresistance (AMR) in single crystalline and polycrystalline thin films of phase separated manganite Nd_0.51Sr_0.49MnO₃ has been carried out. On-axis DC magnetron sputtering was used to deposit the single crystalline films (30 and 100 nm in thickness) on single crystal (0 0 1) LaAlO₃ (LAO) and polycrystalline films (100 nm) on (1 0 0) Yttrium-stabilized ZrO₂ (YSZ) substrates. The in-plane and out-of-plane magnetotransport properties of these films differ significantly. A large low field AMR is observed in all the films. AMR shows a peak below the insulator-metal transition temperature in the single crystalline films, while the same increases monotonically in the polycrystalline film. Relatively larger low field AMR (∼20% at T=78 K and H=1.7 kOe) in the polycrystalline films suggests the dominance of the shape anisotropy.     

Structural and magnetoresistive properties of half metallic Co2Mn1−xSi thin films

Polycrystalline Co₂Mn_1−xSi (CMS) thin films with Mn-deficiency can grow on different types of substrates such as MgO (1 0 0) single crystal, α-sapphire (0 0 0 1) and Si coated with SiO₂ either by using V or Ta/Cu as the seed layer. The magnetic property, especially the coercivity of the CMS thin films strongly depends on the crystalline structure and microstructure of the CMS thin film, hence it is affected by the substrate and also the seed layer. Very soft CMS thin film with coercivity of about 20 Oe has been obtained when MgO (1 0 0) is used as the substrate. Magnetic tunnel junctions (with MR ratio of about 9%–18%) by utilizing the CMS as one of ferromagnetic electrodes have been successfully fabricated. The degradation of the magnetoresistive effect of the MTJ after magnetic annealing is attributed to the diffusion of the Mn-atoms into the tunnel barrier during the annealing process.     

Microstructure and microwave permeability of FeCo thin films with Co underlayer

Microstructure, static magnetic properties and microwave permeability of sputtered FeCo films were examined. Fe₆₀Co₄₀ films (100 nm in thickness) deposited on glass substrates exhibited in-plane isotropy and a large coercivity of 161.1 Oe. When same thickness films were deposited on 2.5 nm Co underlayer, well-defined in-plane anisotropy was formed with an anisotropy field of 65 Oe. The sample had a static initial permeability of about 285, maximum imaginary permeability of 1255 and ferromagnetic resonance frequency of 2.71 GHz. Cross-sectional TEM image revealed that the Co underlayer had induced a columnar grain structure with grain diameter of 10 nm in the FeCo films. In comparison, FeCo films without Co underlayer showed larger grains of 70 nm in diameter with fewer distinct vertical grain boundaries. In addition, the Co underlayer changed the preferred orientation of the FeCo from (1 0 0) to (1 1 0). The improvement in soft magnetic properties and microwave behavior originates from the modification of the film microstructure, which can be well understood by the random anisotropy theory.     

Structural and magnetic properties of Co50Ni50 powder mixtures

In the present work, morphological, structural, thermal and magnetic properties of nanocrystalline Co₅₀Ni₅₀ alloy prepared by high energy planetary ball milling have been studied by means of scanning electron microscopy, X-ray diffraction, and differential scanning calorimetry. The coercivity and the saturation magnetization of alloyed powders were measured at room temperature by a vibration sample magnetization. Morphological observations indicated a narrow distribution in the particle and homogeneous shape form with mean average particle size around 130 μm². The results show that an allotropic Co transformation hcp→fcc occurs within the three first hours of milling and contrary to what expected, the Rietveld refinement method reveals the formation of two fcc solid solutions (SS): fcc Co(Ni) and Ni(Co) beside a small amount of the undissolved Co hcp. Thermal measurement, as a function of milling time was carried out to confirm the existence of the hcp phase and to estimate its amount. Magnetic measurement indicated that the 48 h milled powders with a steady state particles size have the highest saturation (105.3 emu/g) and the lowest coercivity (34.5 Oe).     

Preparation and magnetic properties of BaFe12O19/Ni0.8Zn0.2Fe2O4 nanocomposite ferrite

Nanocomposite of hard (BaFe₁₂O₁₉)/soft ferrite (Ni_0.8Zn_0.2Fe₂O₄) have been prepared by the sol–gel process. The nanocomposite ferrite are formed when the calcining temperature is above 800 °C. It is found that the magnetic properties strongly depend on the presintering treatment and calcining temperature. The “bee waist” type hysteresis loops for samples disappear when the presintering temperature is 400 °C and the calcination temperature reaches 1100 °C owing to the exchange-coupling interaction. The remanence of BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite with the mass ratio of 5:1 is higher than a single phase ferrite. The specific saturation magnetization, remanence magnetization and coercivity are 63 emu/g, 36 emu/g and 2750 G, respectively. The exchange-coupling interaction in the BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite is discussed.     

Anomalous Hall effect and perpendicular magnetic anisotropy in Sm28Fe72 and Sm32Fe68 thin films

Sm₂₈Fe₇₂ and Sm₃₂Fe₆₈ films of 100 nm thickness were grown using DC magnetron sputter deposition and their structure, magnetization, electrical and Hall resistance characteristics were investigated. An increase in electrical resistivity from 4.75×10⁻⁶ to 5.62×10⁻⁶ Ω m and from 2.26×10⁻⁶ to 2.84×10⁻⁶ Ω m for Sm₂₈Fe₇₂ and Sm₃₂Fe₆₈ films, respectively, with decrease in temperature from 300 to 40 K is attributed to the strain induced anisotropy that dominates at lower temperatures. The positive extraordinary Hall coefficients (R_S) are observed for both films at 300 and 80 K. The existence of hysteresis indicates that Sm₂₈Fe₇₂ and Sm₃₂Fe₆₈ films possess perpendicular anisotropy at 300 K. Hysteresis loop becomes narrow at 80 K for both Sm₂₈Fe₇₂ and Sm₃₂Fe₆₈ films. Magnetization measurements at 300 K exhibiting small coercive field values of 31 and 49 Oe for Sm₂₈Fe₇₂ and Sm₃₂Fe₆₈ films, respectively, confirm the existence of perpendicular anisotropy at 300 K.     

Soft magnetic properties of NiFe compacted powder alloys

It is known that Ni–Fe based alloys (permalloys) are important soft magnetic materials, which have been widely applied in the field of electronic devices and industry. The most suitable permalloys for application exhibit low value of coercivity and magnetostriction (for about 80 at% Ni), high saturation magnetic induction (for about 50 at% Ni), higher electrical resistivity (for about 35 at% Ni). The aim of this work was to investigate the structure and magnetic properties of _Ni81Fe19${\mathrm{Ni}}_{81}{\mathrm{Fe}}_{19}$ (wt%) compacted powder material in the form of small cylinders.