Magnetic and electrical behavior of La1−xAxMnO3 (A=Li, Na, K and Rb) manganites

With a view to understand the magnetic and electrical behavior of monovalent substituted lanthanum manganites, a series of materials were prepared by sol-gel route by sintering at 1200 °C. The X-ray diffraction data were analyzed using Rietveld refinement technique and it has been found that all the samples were found to crystallize into rhombohedral structure with R3¯c space group. The values of ferro to paramagnetic (T_C) and metal-insulator transition (T_P) temperatures were obtained using ac susceptibility and electrical resistivity data, respectively. It has been found that sodium-, potassium- and rubidium-doped samples exhibit two peaks in the electrical resistivity vs. temperature plots. The observed behavior has been explained on the basis of oxygen deficiency present in the samples. The electrical resistivity data were analyzed using various theoretical models and it has been concluded that the electrical resistivity data in the low-temperature regime (T<T_P) can be explained using the equation ρ_(T)=ρ₀+ρ₂T²+ρ_4.5T^4.5, signifying the importance of the grain/domain boundary, electron-electron and two magnon scattering processes. On the other hand, the high-temperature resisitivity data (T>T_P) were explained using variable range and small polaron hopping mechanisms.     

Study of magnetotransport in double-layered La1.4Ca1.6Mn2O7 manganite: Presence of nano-ferromagnetic domains in paramagnetic matrix

Double-layered manganite La_1.4Ca_1.6Mn₂O₇ has been synthesized using the solid-state reaction method. It had a metal-to-insulator transition at temperature T_M1≈127 K. The temperature dependence of ac susceptibility showed a broad ferromagnetic transition. The two-dimensional (2D)-ferromagnetic ordering temperature (T_C2) was observed as ≈245 K. The temperature dependence of its low-field magnetoresistance has been studied. The low-field magnetoresistance of double-layered manganite, in the temperature regions between T_M1 and T_C2, has been found to follow 1/T⁵. The observed behaviour of temperature dependence of resistivity and low-field magnetoresistance has been explained in terms of two-phase model where ferromagnetic domains exist in the matrix of paramagnetic regions in which spin-dependent tunneling of charge carriers occurs between the ferromagnetic correlated regions. Based on the two-phase model, the dimension of these ferromagnetic domains inside the paramagnetic matrix has been estimated as ∼12 Å.     

Effect of Cr doping in the bilayer manganite La1.4Sr1.6Mn2O7

The effect of Cr doping on magnetic and electrical properties in the bilayer manganites La_1.4Sr_1.6(Mn_1−yCr_y)₂O₇ (y=0-0.1) has been investigated. When y≤0.025, Cr doping enhances the three-dimensional magnetic transition temperature T_C and the insulator-metal transition temperature T_IM as well as decreases the peak resistivity at T_IM, and the saturated magnetization decreases slightly. When y≥0.035, T_IM decreases gradually accompanied by the increase of peak resistivity, but T_C remains nearly constant, and the saturated magnetization decreases heavily. In the whole doping region, the two-dimensional magnetic transition temperature T^? monotonously decreases with an increasing of Cr doping level. These results can be explained by considering different magnetic (including ferromagnetic and antiferromagnetic) interactions between Mn ions and Cr ions.     

Ferromagnetic semiconductor Ge1−x−ySnxMnyTe with phase transformation of ferroelectric type

It is expected that joint existence of ferromagnetic properties and ferroelectric structural phase transition in diluted magnetic semiconductors IV-VI leads to new possibilities of these materials. Temperature of ferroelectric transition for such crystals can be tuned by the change of Sn/Ge ratio. Magnetic susceptibility, Hall effect, resistivity and thermoelectric power of Ge_1−x−ySn_xMn_yTe single crystals grown by Bridgeman method (x=0.083-0.115; y=0.025-0.124) were investigated within 4.2-300 K. An existence of FM ordering at T_C∼50 K probably due to indirect exchange interaction between Mn ions via degenerated hole gas was revealed. A divergence of magnetic moment temperature dependences at T?T_C in field-cooled and zero-field-cooled regimes is obliged to magnetic clusters which are responsible for superparamagnetism at T>T_C≈T_f (freezing temperature) and become ferromagnetic at T_C arranging spin glass state at T<T_f≈T_C. Phase transition of ferroelectric type at T≈46 K was revealed. Anomalous Hall effect which allows to determine magnetic moment was observed.     

Structural and electrical behavior of Pb(Mg1/4Cd1/4Mo1/2)O3 ceramics

Preliminary X-ray structural analysis of polycrystalline Pb(Mg_1/4Cd_1/4Mo_1/2)O₃ ceramics, prepared by a solid-state reaction technique, provides single-phase orthorhombic structure at room temperature. Detailed dielectric studies of the material as a function of temperature reveal a sharp phase transition at temperature T_c=49°C obeying Curie-Weiss behavior. Scanning electron microscope (SEM) studies of the sample show the uniform distribution of grains in the samples. A dielectric anomaly and ferroelectric phase transition observed at 49°C was supported by polarization studies. The activation energy of the sample was calculated from the dielectric data. The variation of dc resistivity with temperature suggests that the compound behaves as a negative temperature coefficient resistor (NTCR).     

Preparation and study of silver added La0.67Ca0.33MnO3 film

La_0.67Ca_0.33MnO₃ (LCMO) and Ag admixed La_0.67Ca_0.33MnO₃ (Ag-LCMO) polycrystalline films have been prepared on SrTiO₃ single crystal (100) substrates by ultrasonic spray pyrolysis technique. These films are characterized using XRD, SEM, and temperature dependence of resistivity (ρ-T) and ac susceptibility (χ-T). The films are having cubic structure with lattice parameters as 3.890 and 3.885 Å for LCMO and Ag-LCMO films, respectively. The peek in ρ-T curve (T_p) and the ferromagnetic transition temperature (T_C) for the Ag-LCMO film is higher than that of LCMO film. The stability of both the films was tested by repeated measurements of its characteristics over a period of one week after several thermal cycling from room temperature to 77 K. In the LCMO film, the peak in the ρ-T curve (T_p) is found to shift towards lower value and conduction noise of the film increases in the subsequent measurements. In the case of Ag-LCMO the value of T_p, T_C and conduction noise of the film did not change even after several measurements. Silver segregating at the grain boundaries in Ag-LCMO polycrystalline film seems to be responsible for improving the characteristics of Ag-LCMO films.     

On the coexistence of spin and lattice polarons in the La0.67−xEuxCa0.33MnO3 CMR system

The electrical and magnetic transport properties of the La_0.67−xEu_xCa_0.33MnO₃ system exhibit lowering of insulator to metal and paramagnetic to ferromagnetic transition temperature (T_C) with the increase of Eu concentration in addition to possessing CMR property. The temperature variation of electrical resistivity and magnetic susceptibility for x=0.21 is found to have two distinct regions in the paramagnetic state for T>T_P; one with the localization of lattice polaron in the high-temperature region (T>1.5T_P) satisfying the dynamics of variable range hopping (VRH) model and the other being the combination of the spin and lattice polarons in the region T_P<T<1.5T_P. The resistivity variation with temperature and magnetic field, the cusp in the resistivity peak and CMR phenomenon are interpreted in terms of coexistence of spin and lattice small polarons in the intermediate region (T_P<T<1.5T_P). The spin polaron energy in the La_0.46Eu_0.21Ca_0.33MnO₃ system is estimated to be 106.73±0.90 meV and this energy decreases with the increase of external magnetic field. The MR ratio is maximal with a value of 99.99% around the transition temperature and this maximum persists till T→0 K, at the field of 8 T.     

The influence of the sintering temperature on the structural and the magnetic properties of doped manganites: La0.95Ag0.05MnO3 and La0.75Ag0.25MnO3

La_1−xAg_xMnO₃ samples were synthesized by standard sol-gel method with Ag concentrations of x=0.05 and 0.25. The samples from each concentration were pressed and sintered at 1000, 1200 and 1400 °C for 24 h in air for a systematic study. They were examined structurally by Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM) with Energy Dispersive Spectroscopy (EDS) and X-ray Diffraction (XRD) and magnetically by Magnetic Properties Measurements System (MPMS). AFM and SEM analyses show that surface morphology changes with Ag concentration and sintering temperature (T_S). It was observed that high temperature sintering leads Ag to leave material as determined from EDS analyses. XRD spectra exhibited that the crystal structure changes with Ag concentration while showing pronounced change with the sintering temperature. From the magnetic measurements, the Curie temperatures (T_C) and the isothermal magnetic entropy changes (−ΔSM) were calculated. It was observed that T_C increases with Ag concentration and decreases with T_S. The maximum −ΔSM was calculated to be 7.2 J/kg K under the field change of 5 T for the sample sintered at 1000 °C with x=0.25.     

Electrical conductivity and low field magnetoresistance in polycrystalline La1−xKxMnO3 pellets prepared by pyrophoric method

Electrical conductivity and magnetoresistance of a series of monovalent (K) doped La_1−xK_xMnO₃ polycrystalline pellets prepared by pyrophoric method have been reported. K doping increases the conductivity as well as the Curie temperature (T_C) of the system. Curie temperature increases from 260 to 309 K with increasing K content. Above the metal-insulator transition temperature (T>T_MI), the electrical resistivity is dominated by adiabatic polaronic model, while in the ferromagnetic region (50<T<T_MI), the resistivity is governed by several electron scattering processes. Based on a scenario that the doped manganites consist of phase separated ferromagnetic metallic and paramagnetic insulating regions, all the features of the temperature variation of the resistivity between ∼50 and 300 K are described very well by a single expression. All the K doped samples clearly display the existence of strongly field dependent resistivity minimum close to ∼30 K. Charge carrier tunneling between antiferromagnetically coupled grains explains fairly well the resistivity minimum in monovalent (K) doped lanthanum manganites. Field dependence of magnetoresistance at various temperatures below T_C is accounted fairly well by a phenomenological model based on spin polarized tunneling at the grain boundaries. The contributions from the intrinsic part arising from DE mechanism, as well as, the part originating from intergrannular spin polarized tunneling are also estimated.     

Low temperature magnetoresistance in La1.32Sr1.68Mn2O7 layered manganite under hydrostatic pressure

The La_1.32Sr_1.68Mn₂O₇ layered manganite system has been studied by the low temperature electrical resistance and magnetoresistance under hydrostatic pressure up to 25 kbar. We have observe both, a Curie temperature (T_C) and a metal-insulator transition (T_MI) at 118 K in the ambient pressure. The applied pressure shifts the T_MI to higher temperature values and induces a second metal-insulator transition (T²_MI) at 90 K, in the temperature dependence of resistivity measurements. Also, the pressure suppresses the peak resistance abruptly at T_C. When an external field of 5 T is applied, we have observed a large negative magnetoresistance of 300% at the transition temperature and a 128% at 4.5 K. However, the increased pressure decreases the magnetoresistance ratio gradually. When the pressure reaches its maximum available value of 25 kbar, the magnetoresistance ratio decreases at a rate of 1.3%/kbar. From our experimental results, the decrease of magnetoresistance ratio with pressure is explained by the pressure induced canted spin state which is not favor for the spin polarized intergrain tunneling in layered manganites.     

Electron transport properties of Co71−xFexCr7Si8B14 (x=0, 2, 3.2, 4, 6,8 and 12 at%) amorphous alloys during devitrification

The investigation addresses the electron transport properties of Co_71−xFe_xCr₇Si₈B₁₄ (x=0, 2, 3.2, 4, 6, 8 and 12 at%) amorphous alloys. The variation in electrical resistivity of as-cast amorphous materials with thermal scanning from room temperature to 1000 K was measured. The CoFe-based alloys revealed an initial decrease in temperature coefficient of resistivity (TCR), a characteristic of spin-wave phenomena in glassy metallic systems. This behaviour in the present alloys was in a sharp contrast to the Co-based amorphous materials that indicate the drop in resistivity much below room temperature. In the studied alloys, the variation in initial TCR values and the full-width at half-maxima determined from X-ray diffraction of as-quenched materials exhibited a similar trend with increasing Fe content, indicating the compositional effect of near neighbouring atoms. After the initial decrease in resistivity, all the alloys indicated a subsequent increase at T_min. The Curie temperature (T_C), which was measured from thermal variation of ac susceptibility showed non-monotonic change with Fe content. In the temperature range between T_min and T_C the relative scattering by electron-magnon and electron-phonon resulted in the non-monotonic change in Curie temperature. At crystallization onset (T_X1) all the alloys except there with X=6, showed a sharp decrease in electrical resistivity which was attributed to ordering phenomena. In contrast to this resistivity decrease, X=6 alloy exhibited a drastic increase in resistivity around T_X1 observed during amorphous to nanocrystalline transformation. Such nanocrystalline state was observed by Transmission electron microscopy.     

Structural,electrical transport,and magnetic properties of Ni1−xZnxFe2O4

Structural, electrical, and magnetic properties of Ni_1−xZn_xFe₂O₄ (x=0.2, 0.4) samples sintered at various temperatures have been investigated thoroughly. The bulk density of the Ni_0.8Zn_0.2Fe₂O₄ samples increases as the sintering temperature (T_s) increases from 1200 to 1300 °C and above 1300 °C the bulk density decreases slightly. The Ni_0.6Zn_0.4Fe₂O₄ samples show similar behavior of changes to that of Ni_0.8Zn_0.2Fe₂O₄ samples, except that the bulk density is found to be the highest at 1350 °C. The DC electrical resistivity, ρ(T)$\rho (T)$, decreases as the temperature increases indicating that the samples have semiconductor-like behavior. As the Zn content increases, the Curie temperature (T_c), resistivity, and the activation energy decrease while the magnetization, initial permeability, and the relative quality factor (Q) increases. A Hopkinson peak is obtained near T_c in the real part of the initial permeability vs. temperature curves. The ferrite with higher permeability has a relatively lower resonance frequency. The initial permeability and magnetization of the samples has been found to correlate with density, average grain sizes. Possible explanation for the observed structural, magnetic, and changes of resistivity behavior with various Zn content are discussed.     

Electronic transport and magnetic studies of La1−xCax−0.08Sr0.04Ba0.04MnO3

Lanthanum based mixed valence manganite system La_1−xCa_x−0.08Sr_0.04Ba_0.04MnO₃ (LCSBMO; x=0.15, 0.24 and 0.33) synthesized through the sol-gel route is systematically investigated in this paper. The electronic transport and magnetic susceptibility properties are analyzed and compared, apart from the study of unit cell structure, microstructure and composition. Second order phase transition is observed in all the samples and significant difference is observed between the insulator to metal transition temperature (T_MI) and paramagnetic (PM) to ferromagnetic (FM) transition temperature (T_C). In contrast to the insulating FM behaviour usually observed in La_1−xCa_xMnO₃ (LCMO) for x=0.15, a clear insulator to metal transition is observed for LCSBMO for the same percentage of lanthanum. The temperature dependent resistivity of polycrystalline pellets, when obeying the well studied law ρ=ρ_o+ρ₂T² for T<T_MI, is observed to differ significantly in the values of ρ_o and ρ₂, with the electrical conductivity increasing with x. The variable range hopping model has been found to fit resistivity data better than the small polaron model for T>T_MI. AC magnetic susceptibility study of the polycrystalline powders of the manganite system shows the highest PM to FM transition of 285 K for x=0.33.     

Ferroelectric properties of Pr6O11-doped Bi4Ti3O12

Praseodymium doped Bi₄Ti₃O₁₂ (BIT) ceramics with composition Bi_2.9Pr_0.9Ti₃O₁₂ (BPT) were prepared by solid state reaction. These samples have polycrystalline Bi-layered perovskite structure without preferred orientation, and consist of well-developed plate-like grains with random orientation. Pr doping into BIT causes a large shift of the Curie temperature (T_C) of the BIT from 675 to 398 °C. At an electric field of 87 kV/cm, the remanent polarization and the coercive field of the BPT ceramics are 30 μC/cm² and 52 kV/cm, respectively. Furthermore, the dielectric permittivity and the dissipation factor of the BPT ceramics are 300 and 0.003 at 1 MHz, 1 V, and room temperature. Ferroelectric properties of the BPT ceramics are superior to V-doped Bi₄Ti₃O₁₂ (∼20 μC/cm² and 80 kV/cm) and (Sr, Ta)-doped Bi₄Ti₃O₁₂ (∼12 μC/cm² and 71 kV/cm) ceramics. In addition, the dense ceramics of praseodymium-doped B₄Ti₃O₁₂ were obtained by sintering at 1100 °C, about 100-200 °C lower than those of the SrBi₂Ta₂O₉ system.     

Structural, magnetotransport and morphological studies of Sb-doped La2/3Ba1/3MnO3 ceramic perovskites

We report here the structural, magnetotransport and morphological studies of Sb-doped La_2/3Ba_1/3Mn_1−xSb_xO₃ perovskite manganites. Pristine material La_2/3Ba_1/3MnO₃ (LBMO) shows two insulator-metal (I-M) transitions in the electrical resistivity-temperature (ρ-T) behavior. While the higher temperature transition (T_P1) at ∼340 K is reminiscent of the usual I-M transition in manganites, the lower temperature transition (T_P2) at ∼250 K has been ascribed to the grain boundary (GB) effects arising out of the ionic size mismatch between the ions present at the rare-earth site (La³⁺ and Ba²⁺). With Sb-doping T_P1 shifts to lower temperatures while T_P2 remains invariant up to 3% and shifts to lower temperature for 5%. Room temperature electrical resistivity and the peak values also increase successively with Sb-doping. Scanning electron micrographs of the samples exhibit a gradual increase in their grain sizes with Sb indicating a gradual decrease in the GB density. Shift of T_P1 with doping is explained on the basis of a competition between double-exchange and super-exchange mechanisms. The overall electrical resistivity increases and the shift in the electrical resistivity hump (T_P2) with Sb-doping is found related to be gradually decreasing GB density and the ensuing lattice strain increase at the GBs. The intrinsic magnetoresistance (MR) gets suppressed and extrinsic MR gets enhanced with Sb-doping. At T>T_P1, the electrical resistivity is found to follow the adiabatic polaron hopping model whereas the electron-magnon scattering is found to dominate in the metallic regime (T<T_P1).     

The effect of transition element doping on the electronic and magnetic properties of La1.4Sr1.6Mn2O7

The effect of transition element (TE=Cr, Fe, Co, Ni, Cu, Zn) doping on the electronic transport and magnetic properties in the bilayer manganite La_1.4Sr_1.6Mn₂O₇ is studied for the same dopant concentration fixed at 2%. Doping does not cause change in structure but different behavior in magnetic and transport properties. Except for Cr, all the other dopings significantly shift the magnetic transition temperature (T_C) to a lower temperature. Associated with such a decrease, the insulator-metal transition temperature (T_IM) decreases and the peak resistivity (ρ_p) at T_IM increases. Cr doping enhances T_C and T_IM as well as decreases ρ_p. Fe doping apparently has a stronger effect than Co and Ni doping. It is also indicated that Cu doping causes an anomalously large increase in ρ_p. These behaviors are compared with those observed in other bilayer manganites such as La_1.2Sr_1.8Mn₂O₇ as well as in La_0.7Ca_0.3Mn_1−xTE_xO₃.     

Double metal-insulator peaks and effect of Sm substitution on magnetic and transport properties of hole-doped La0.85Ag0.15MnO3

La_0.85−xSm_xAg_0.15MnO₃ (x=0−0.2) ceramics were prepared using the conventional solid-state synthesis method to investigate the effect of Sm³⁺ substitution on magnetic and electrical transport properties. Magnetic susceptibility versus temperature measurements showed all samples exhibit ferromagnetic to paramagnetic transition with Curie temperature, T_c decreasing from 283 K (x=0) to 164 K (x=0.2) with increasing Sm³⁺. The observed slope in susceptibility, χ′ versus temperature curves below T_c indicates the possible presence of FM and AFM phases in the metallic region. In addition, a deviation from the Curie-Weiss law above T_c in 1/χ′ versus T curves indicates the existence of a Griffith's phase in the x=0.05−0.2 samples due to the Sm³⁺ ion substitution. The Griffith temperature, T_G was found to decrease from 295 K (x=0.05) to 229 K (x=0.2). Electrical resistivity measurements of the samples in zero field showed transition from metallic behavior to insulating behavior as the temperature was increased. For x=0, two metal-insulator, MI transition peaks were observed at T_p1=282 K and at T_p2=250 K. Both peaks shifted to lower temperatures with the increase in Sm³⁺. The relative resistivity of the first peak to the second peak decreases with increasing Sm³⁺ for x>0.05 while at x=0.2 the T_p1 peak was strongly suppressed. Magnetoresistance, MR was observed to weaken with Sm³⁺ substitution. The metallic region of the ρ(T) curve of the x=0−0.15 samples was fitted to the model of electron-electron and electron-magnon scattering while the insulating region was fitted to the variable range hopping, VRH model. The resistivity behavior indicated that the substitution of Sm³⁺ weakened the double exchange process and enhanced the Jahn-Teller effect. Our results indicated that the T_p1 peak is strongly related to the double-exchange mechanism while the T_p2 peak is suggested to originate from magnetic inhomogeneity.     

The transport properties in Nd0.75Sr1.25CoO4 film: Evidence for polaronic transport

The experiments of electrical resistivity and thermopower on Nd_0.75Sr_1.25CoO₄ film in the temperature range 90 K<T<310 K were carried out. The great difference in the activation energies estimated from thermopower and resistivity, a characteristic of small polarons, is observed, providing strong evidence for polaron-dominated transport mechanism in this material. Furthermore, the activation energy at intermediate-temperature region is larger than that at low-temperature region in resistivity, but it is not observed in thermopower, indicating that the energy for the creation of the carriers is slightly lower at low-temperature region than that at intermediate-temperature region. At the same time, the abrupt drop in the thermopower and the abnormal peak in the differential curve of resistivity indicate that a phase transition between a paramagnetic state and a ferromagnetic state occurs at temperature about 218 K. The positive thermopower in the whole temperature range measured suggests that the carriers are holes in this system.     

Magnetic properties of xNi0.53Cu0.12Zn0.35Fe1.88O4+(1−x)BaTiO3 nanocomposites

The nanocrystalline Ni_0.53Cu_0.12Zn_0.35Fe_1.88O₄ and BaTiO₃ powders were prepared using Microwave-Hydrothermal (M-H) method at 160 °C/45 min. The as synthesized powders were characterized using the X-ray diffraction (XRD) and Transmission Electron Microscope (TEM). The size of the powders that were synthesized using M-H system was found to be ∼30 and ∼50 nm for ferrite phase and ferroelectric phases, respectively. The powders were densified using microwave sintering method at 900 °C/30 min. The ferrite and ferroelectric phases were observed from XRD and morphology of the composites was observed with the Scanning Electron Microscope (SEM).The magnetic hysteresis loops were recorded using the Vibrating Sample Magnetometer (VSM).The frequency dependence of real (μ′) and imaginary (μ″) parts of permeability was measured in the range of 1 MHz-1.8 GHz. The permeability decreases with an increase of BaTiO₃ content at 1 MHz. The transition temperature (T_C) of ferrite was found to be 245 °C. The T_C of composite materials decreases with an increase in BaTiO₃ content.     

Effects of Cr doping in electron-doped manganites La0.9Te0.1MnO3

The effects of Cr doping on Mn sites in the electron-doped manganites La_0.9Te_0.1MnO₃ have been studied by preparing the series La_0.9Te_0.1Mn_1−xCr_xO₃ (0.05≤x≤0.20). Upon Cr doping, both the Curie temperature T_C and magnetization M are suppressed. The resistivity measurements indicate that there exists a weak metal-insulator (M-I) transition for the sample with x=0.05, with an increase in the doping level, the M-I transition disappears and the resistivity increases. Thermopower S(T) exhibits a maximum near T_C for all samples. By fitting the S(T) and ρ(T) curves, it is found that the temperature dependences of both S(T) and ρ(T) in the high temperature paramagnetic (PM) region follow the small polaron conduction (SPC) mechanism for all samples. The fitting parameters obtained imply changes of both the average-hopping distance of the polarons and the polaron concentration with Cr doping in our studied samples. In the case of the thermal conductivity κ(T), the variation of κ(T) is analyzed based on the combined effects due to the suppression of the local Mn³⁺O₆ Jahn-Teller (JT) lattice distortion because of the substitution of Cr³⁺ for Mn³⁺ ions, which results in the increase in κ, and the introduction of the disorder due to Cr-doping, which contributes to the decrease in κ.