Crystallinity and morphology dependent luminescence of Li-doped Y2−xGdxO3:Eu thin film phosphors

The influence of lithium doping on the crystallization, the surface morphology, and the luminescent properties of pulsed laser deposited Y_2−xGd_xO₃:Eu³⁺ thin film phosphors was investigated. The crystallinity, the surface morphology, and the photoluminescence (PL) of films depended highly on the Li-doping and the Gd content. The relationship between the crystalline and morphological structures and the luminescent properties was studied, and Li⁺ doping was found to effectively enhance not only the crystallinity but also the luminescent brightness of Y_2−xGd_xO₃:Eu³⁺ thin films. In particular, the incorporation of Li and Gd into the Y₂O₃ lattice could induce remarkable increase in the PL. The highest emission intensity was observed Li-doped Y_1.35Gd_0.6O₃:Eu³⁺ thin films whose brightness was increased by a factor of 4.6 in comparison with that of Li-doped Y₂O₃:Eu³⁺ thin films.     

Photoluminescence properties of Sr1-xSi2O2N2: Eux as green to yellow-emitting phosphor for blue pumped white LEDs

This study evaluated potential applications of green to yellow-emitting phosphors (Sr_1−xSi₂O₂N₂: Eu²⁺_x) in blue pumped white light emitting diodes. Sr_1-xSi₂O₂N₂: Eu²⁺_x was synthesized at different Eu²⁺ doping concentrations at 1450 °C for 5 h under a reducing nitrogen atmosphere containing 5% H₂ using a conventional solid reaction method. The X-ray diffraction patterns of the prepared phosphor (Sr_1-xSi₂O₂N₂: Eu²⁺_x) were indexed to the SrSi₂O₂N₂ phase and an unknown intermediate phase. The photoluminescence properties of these phosphors (Sr_1−xSi₂O₂N₂: Eu²⁺_x) showed that the samples were excited from the UV to visible region due to the strong crystal field splitting of the Eu²⁺ ion. The emission spectra under excitation of 450 nm showed a bright color at 545-561 nm. The emission intensity increased gradually with increasing Eu²⁺ doping concentration ratio from 0.05 to 0.15. However, the emission intensity decreased suddenly when the Eu²⁺ concentration ratio was >0.2. As the doping concentration of Eu²⁺ was increased, there was a red shift in the continuous emission peak. These results suggest that Sr_1-xSi₂O₂N₂: Eu₂⁺_x phosphor can be used in blue-pumped white light emitting diodes.     

Effects of Mn substitution of Co and Fe in spinel CoFe2O4 thin films

Effects of Mn substitution for Co and Fe on the structural and magnetic properties of inverse-spinel CoFe₂O₄ have been investigated. Mn_xCo_1−xFe₂O₄ and Mn_yCoFe_2−yO₄ thin films were prepared by a sol–gel method. The observed increase of the lattice constant of Mn_xCo_1−xFe₂O₄ indicates that Mn²⁺ ions substitute the octahedral Co²⁺ sites. Conversion electron Mössbauer spectroscopy data indicate that a fraction of octahedral Co²⁺ ions exchange sites with tetrahedral Fe³⁺ ions through Mn doping. Vibrating-sample magnetometry data exhibit a large increase of saturation magnetization for both Mn_xCo_1−xFe₂O₄ and Mn_yCoFe_2−yO₄ films compared to that of the CoFe₂O₄ film. Such enhancement of magnetization can be explained in terms of a breaking of ferrimagnetic order induced by the Co²⁺ migration.     

Room-temperature ferromagnetism in Sn1−xMnxO2 nanocrystalline thin films prepared by ultrasonic spray pyrolysis

Sn_1−xMn_xO₂ (x=0.01-0.05) thin films were synthesized on quartz substrate using an inexpensive ultrasonic spray pyrolysis technique. The influence of doping concentration and substrate temperature on structural and magnetic properties of Sn_1−xMn_xO₂ thin films was systematically investigated. X-ray diffraction (XRD) studies of these films reflect that the Mn³⁺ ions have substituted Sn⁴⁺ ions without changing the tetragonal rutile structure of pure SnO₂. A linear increase in c-axis lattice constant has been observed with corresponding increase in Mn concentration. No impurity phase was detected in XRD patterns even after doping 5 at% of Mn. A systematic change in magnetic behavior from ferromagnetic to paramagnetic was observed with increase in substrate temperature from 500 to 700 °C for Sn_1−xMn_xO₂ (x=0.01) films. Magnetic studies reveal room-temperature ferromagnetism (RTFM) with 3.61×10⁻⁴ emu saturation magnetization and 92 Oe coercivity in case of Sn_1−xMn_xO₂ (x=0.01) films deposited at 500 °C. However, paramagnetic behavior was observed for the films deposited at a higher substrate temperature of 700 °C. The presence of room-temperature ferromagnetism in these films was observed to have an intrinsic origin and could be obtained by controlling the substrate temperature and Mn doping concentration.     

Hydrothermal synthesis and structural characterization of (1−x)α-Fe2O3-xSnO2 nanoparticles

Structural and morphological characteristics of (1−x)α-Fe₂O₃-xSnO₂ (x=0.0-1.0) nanoparticles obtained under hydrothermal conditions have been investigated by X-ray diffraction (XRD), transmission Mössbauer spectroscopy, scanning and transmission electron microscopy as well as energy dispersive X-ray analysis. On the basis of the Rietveld structure refinements of the XRD spectra at low tin concentrations, it was found that Sn⁴⁺ ions partially substitute for Fe³⁺ at the octahedral sites and also occupy the interstitial octahedral sites which are vacant in α-Fe₂O₃ corundum structure. A phase separation of α-Fe₂O₃ and SnO₂ was observed for x≥0.4: the α-Fe₂O₃ structure containing tin decreases simultaneously with the increase of the SnO₂ phase containing substitutional iron ions. The mean particle dimension decreases from 70 to 6 nm, as the molar fraction x increases up to x=1.0. The estimated solubility limits in the nanoparticle system (1−x)α-Fe₂O₃-xSnO₂ synthesized under hydrothermal conditions are: x≤0.2 for Sn⁴⁺ in α-Fe₂O₃ and x≥0.7 for Fe³⁺ in SnO₂.     

Structural and electrical transport properties of ZnxFe3−xO4 thin film deposited on Si (1 1 1) by pulsed-laser deposition

Polycrystalline thin films of Fe_3−xZn_xO₄ (x = 0.0, 0.01 and 0.02) were prepared by pulsed-laser deposition technique on Si (1 1 1) substrate. X-ray diffraction studies of parent as well as Zn doped magnetite show the spinel cubic structure of film with (1 1 1) orientation. The order–disorder transition temperature for Fe₃O₄ thin film with thickness of 150 nm are at 123 K (Si). Zn doping leads to enhancement of resistivity by Zn²⁺ substitution originates from a decrease of the carrier concentration, which do not show the Verwey transition. The Raman spectra for parent Fe₃O₄ on Si (1 1 1) substrate shows all Raman active modes for thin films at energies of T_2g¹, T_2g³, T_2g², and A_1g at 193, 304, 531 and 668 cm⁻¹. It is noticed that the frequency positions of the strongest A_1g mode are at 668.3 cm⁻¹, for all parent Fe₃O₄ thin film shifted at lower wave number as 663.7 for Fe_2.98Zn_0.02O₄ thin film on Si (1 1 1) substrate. The integral intensity at 668 cm⁻¹ increased significantly with decreasing doping concentration and highest for the parent sample, which is due to residual stress stored in the surface.     

Synthesis and electrochemical performances of Li4Ti4.95Al0.05O12/C as anode material for lithium-ion batteries

Spinel compounds Li₄Ti_5−xAl_xO₁₂/C (x=0, 0.05) were synthesized via solid state reaction in an Ar atmosphere, and the electrochemical properties were investigated by means of electronic conductivity, cyclic voltammetry, and charge-discharge tests at different discharge voltage ranges (0-2.5 V and 1-2.5 V). The results indicated that Al³⁺ doping of the compound did not affect the spinel structure but considerably improved the initial capacity and cycling performance, implying the spinel structure of Li₄Ti₅O₁₂ was more stable when Ti⁴⁺ was substituted by Al³⁺, and Al³⁺ doping was beneficial to the reversible intercalation and deintercalation of Li⁺. Al³⁺ doping improved the reversible capacity and cycling performance effectively especially when it was discharged to 0 V.     

Ferroelectric properties of Bi3.25−x/3La0.75Ti3−xNbxO12 films prepared by pulsed laser deposition

Bi₄Ti₃O₁₂ (BiT), Bi_3.25La_0.75Ti₃O₁₂ (BLT), Bi_4−x/3Ti_3−xNb_xO₁₂ (BTN) and Bi_3.25−x/3La_0.75Ti_3−xNb_xO₁₂ (BLTN) thin films have been prepared by pulsed laser deposition. BTN and BLTN films exhibit a maximum in the remanent polarization P_r at a Nb content x=0.018. At this Nb content, the BLTN film has a P_r value (25 μC/cm²) that is much higher than that of BiT and a coercive field similar to that of BiT. The polarization of this BLTN film is fatigue-free up to 10⁹ switching cycles. The high fatigue resistance is mainly due to the substitution of Bi³⁺ ions by La³⁺ ions at the A site and the enhanced P_r arises largely from the replacement of Ti⁴⁺ ions by Nb⁵⁺ ions at the B site. The mechanisms behind the effects of the substitution at the two sites are discussed.     

Investigation of spectroscopic properties and thermal stability of Er/Yb-co-doped Bi2O3-B2O3-Ga2O3 glasses

A series of Er³⁺/Yb³⁺-co-doped 60Bi₂O₃-(40−x) B₂O₃ -xGa₂O₃ (BBGA x=0, 4, 8, 12, 16 mol%) glasses have been prepared. The absorption spectra, emission spectra, fluorescence lifetime of Er³⁺:⁴I_13/2 level and thermal stability were measured and investigated. Three Judd-Ofelt intensity parameters Ω_t (t=2,4,6) (Ω₂=(4.67-5.93)×10⁻²⁰ cm², Ω₄=(1.50-1.81)×10⁻²⁰ cm², Ω₆=(0.92-1.17)×10⁻²⁰ cm²) of Er³⁺ ions were calculated by Judd-Ofelt theory. It is found that the Ω₆ first increases with the increase of Ga₂O₃ content from 0 to 8 mol% and then decreases, which is mainly affected by the number of non-bridging oxygen ions of the glass network. The high peak of stimulated emission cross-section () of Er³⁺: ⁴I_13/2→⁴I_15/2 transition were obtained according to McCumber theory and broad full width at half maximum (FWHM=69-76 nm) of the ⁴I_13/2→⁴I_15/2 transition of Er³⁺ ions were measured. The results indicate that these new BBGA glasses can be used as a candidate host material for potential broadband optical amplifiers.     

Structural characterization and ytterbium spectroscopy in Sc2O3 nanocrystals

Ytterbium-doped scandium oxide nanocrystals measuring less than 25 nm with compositions of Sc_2−xYb_xO₃ (x=0.001-1) were prepared using the modified Pechini method. The Yb:Sc₂O₃ nanocrystals were obtained by calcination at low temperature such as 1073 K for 2 h. X-ray powder diffraction (XRD) and transmission electronic microscopy (TEM) were used to perform the structural characterization of nanocrystals; these studies indicated that the nanocrystals have high crystalline quality with cubic structure and Ia3¯ space group. The morphology and particle size were studied using electron microscopy. A detailed study of the effect of the nanodimension and the ytterbium concentration on the spectroscopic characteristics of Yb³⁺ as an active ion was carried out in terms of optical absorption, optical emission and fluorescence decay time at room and low temperature.     

Electrical properties of neodymium doped CaBi4Ti4O15 ceramics

Neodymium doped bismuth layer structure ferroelectrics (BLSFs) ceramics CaBi_4−xNd_xTi₄O₁₅ (x=0, 0.25, 0.50, 0.75) were prepared by solid-state reaction method. X-ray diffraction pattern showed that single phase was formed when x=0-0.75. The refined lattice parameters showed that a (b) axes decrease at x=0.25 and increase with more Nd³⁺ dopant. The effects of Nd³⁺ doping on the dielectric and ferroelectric properties of CaBi₄Ti₄O₁₅ ceramics are studied. Nd³⁺ dopant decreased the Curie temperature linearly, and the dielectric loss, tan δ, as well. The remnant polarization of Nd³⁺ doped CaBi₄Ti₄O₁₅ ceramics was increased by 80% at x=0.25, while more Nd³⁺ dopant decreased the remnant polarization. CaBi_3.75Nd_0.25Ti₄O₁₅ ceramics had the largest piezoelectric constant d₃₃. The structure and properties of CaBi_4−xNd_xTi₄O₁₅ ceramics showed that Nd³⁺ may occupy different crystal locations when Nd³⁺ content x is less than 0.25 and more than 0.50.     

Phase transformation behavior and dielectric characteristics of BaTi1−x(Al1/2Nb1/2)xO3 (0.01≤x≤0.40) ceramics

Microstructure, phase transformation behavior and dielectric properties of BaTi_1−x(Al_1/2Nb_1/2)_xO₃ (0.01≤x≤0.40) ceramics were investigated. A high level of (Al_1/2Nb_1/2)⁴⁺ substitution for Ti⁴⁺ ions was not conducive to the stability of the perovskite structure and resulted in the formation of BaAl₂O₄. As x was increased, lattice constants and unit cell volume decreased, reached a minimum at x=0.10 and then increased. The BaTi_1−x(Al_1/2Nb_1/2)_xO₃ ceramics at room temperature experienced a transformation from ferroelectric to paraelectric phase with increasing (Al_1/2Nb_1/2)⁴⁺ concentration. Meanwhile, permittivity of the BaTi_1−x(Al_1/2Nb_1/2)_xO₃ ceramics was markedly reduced, while Q value was slightly increased. Frequency dispersion of dielectric peak was obviously increased as x was increased from 0.01 to 0.10. It is of great interest that a dielectric abnormity represented by a broad dielectric peak at 200-400 K was observed for the composition with x=0.40.     

Luminescent properties of stabled hexagonal phase Sr1−xBaxAl2O4:Eu (x=0.37-0.70)

Stabled hexagonal phase Sr_1−xBa_xAl₂O₄:Eu²⁺ (x=0.37-0.70) was prepared by solid-state method. Result revealed that the structure behavior of the SrAl₂O₄:Eu²⁺ calcined at 1350 °C in a reducing atmosphere for 5 h strongly depended on the Ba²⁺ concentration. With increasing Ba²⁺ concentration, a characteristic hexagonal phase can be observed. When 37-70% of the strontium is replaced by barium, the structure of the prepared sample is pure hexagonal. Photoluminescence and excitation spectra of the samples with different x and doped with 2% Eu²⁺ were investigated. Changes in the emission spectra were observed in the two different phases. The green emission at 505 nm from Eu²⁺ was found to be quite strong in the hexagonal phase. The intensity and peak position of the green luminescence from Eu²⁺ changed with increasing content of Ba²⁺. The strongest green emission was obtained from Sr_0.61Ba_0.37Al₂O₄:Eu²⁺. The decay characteristics of Sr_1−xBa_xAl₂O₄:Eu²⁺ (x=0.37-0.70) showed that the life times also varied with the value of x. Furthermore, the emission colors and decay times varying with x could be ascribed to the variation of crystal lattice.     

Raman spectra of Ba6−3xSm8+2xTi18O54 solid solution

Raman spectra of Ba_6−3xSm_8+2xTi₁₈O₅₄ solid solution were investigated as the function of x and sintering time. Reasonable explanations were provided about the Raman shifts and their intensities at 1013, 590, 751, 280, 232 cm⁻¹. 1013 cm⁻¹ demonstrates the existence of BaCO₃ phase in solid solution, 590 cm⁻¹ is the symmetric stretching mode of the basal oxygens of the octahedral; 280 and 232 cm⁻¹ are the symmetric stretching modes resulted from the tilt of octahedral when large cation sites are Sm³⁺ and Ba²⁺. The shoulder peak appearing around 302 cm⁻¹ is related to the vacancy produced by the unequal valence of Sm³⁺ and Ba²⁺.     

Synthesis and characterization of novel red emitting nanocrystal Gd6WO12:Eu phosphors

Novel nanosized Gd₆WO₁₂:Eu³⁺ phosphors were synthesized via a co-precipitation reaction. The crystal structure and morphology of the phosphors were characterized by using X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). It was found that the resultant powders show a regular and sphere-like shape with average particle size of 60 nm. Intrinsic red emission originating from Eu³⁺ was observed while excited at the W⁶⁺→O²⁻ and Eu³⁺→O²⁻ charge transfer bands or f-f absorption bands. The color coordinates of the phosphors were calculated to be x=0.625, y=0.375. The concentration dependence of the luminescence was studied, and optimum doping concentration for obtaining maximum emitting intensity was confirmed to be around 12 mol%. It was also found that the electric dipole-dipole interaction plays an important role for quenching luminescence of Eu³⁺.     

Luminescence and chromaticity of alkaline earth aluminate MxSr1−xAl2O4:Eu (M: Ca,Ba)

In order to prepare fluorescent material for UV-LED used as illumination light source, two series of Eu²⁺ doped (1 mol%) alkaline earth aluminate phosphors Ca_xSr_1−xAl₂O₄ and Ba_xSr_1−xAl₂O₄ were prepared. The crystal structure, relative quantum efficiency(Qr), peak wavelength(λ_p), color tuning and chromaticity were investigated by XRD patterns and photoluminescence (PL) on samples prepared by solid solution system (s series) and powder mixing system (m series) respectively. For the s series, the synthesized Ca_xSr_1−xAl₂O₄:Eu²⁺ powders show that the structure transforms from monoclinic to hexagonal at x?0.5, and λ_p increases from 442.3 to 529.7 nm with decreasing x. For the Ba_xSr_1−xAl₂O₄:Eu²⁺ system, the structure transforms from monoclinic to hexagonal at x?0.3, and λ_p decreases from 520.5 to 502.2 nm continuously from x=0 to 1. The shift in λ_p could be explained by the crystal field effect, which is affected by different coulomb attractive forces due to the various fraction of alkaline earth cation in the host lattice. Different phosphor properties prepared by either solid solution or powder mixing methods were characterized by chromaticity measurements for both reflective and transmissive modes.     

Effect of Bi2O3 on EPR, optical transmission and DC conductivity of vanadyl doped alkali bismuth borate glasses

Glasses with composition xBi₂O₃·(30−x)M₂O·70B₂O₃ (M=Li, Na) containing 2 mol% V₂O₅ have been prepared over the range 0≤x≤15 (x is in mol%). The electron paramagnetic resonance spectra of VO²⁺ of these glasses have been recorded in the X-band (≈9.3 GHz) at room temperature (RT≈300 K). Spin Hamiltonian parameters, g_∥, g_⊥, A_∥, A_⊥, dipolar hyperfine coupling parameter, P, and Fermi contact interaction parameter, K, have been calculated. The molecular orbital coefficients, α² and γ², have been calculated by recording the optical transmission spectra. In xBi₂O₃·(30−x)Li₂O·70B₂O₃ glasses there is decrease in the tetragonality of the V⁴⁺O₆ complex for x up to 6 mol% whereas for x≥6 mol%, tetragonality increases. In xBi₂O₃·(30−x)Na₂O·70B₂O₃ glasses there is increase in the tetragonality of the V⁴⁺O₆ complex with increasing x. The 3d_xy orbit expands with increase in Bi₂O₃:M₂O ratio. Values of the theoretical optical basicity, Λ_th, have also been reported. The DC conductivity increases with increase in temperature. The order of conductivity is 10⁻⁵ ohm⁻¹ m⁻¹ at low temperature and 10⁻³ ohm⁻¹ m⁻¹ at high temperature. The DC conductivity decreases and the activation energy increases with increase in Bi₂O₃:M₂O ratio.     

Properties of vanadium-doped SrBi4Ti4O15 ferroelectric ceramics

Using the standard solid-state reaction method, several vanadium-doped ferroelectric ceramics of type SrBi_4−x/3Ti_4−xV_xO₁₅ (SBTV−x) were synthesized. The vanadium doping content, x, rangs from 0.00 to 0.06. The crystal structure of SrBi₄Ti₄O₁₅ is not affected by V-doping. The electric breakdown voltage of the samples increases with V content. Meanwhile, V-doping results in a notable enlargement of remnant polarization (2P_r). The 2P_r of STBV−0.03 reaches a very large value, which is over 50 μC/cm² and is nearly twice greater than that at zero doping. The Curie temperatures of V-doped samples decrease slightly in comparison with that of SrBi₄Ti₄O₁₅. V-doping can improve the electric properties of SrBi₄Ti₄O₁₅ without sacrificing its thermal stableness.     

Chemical pressure effect in CeFeAs1−xPxO0.95F0.05

We investigate the chemical pressure effect due to P doping in the CeFeAs_1−xP_xO_0.95F_0.05(0≤x≤0.4) system. The compound CeFeAsO_0.95F_0.05 without P doping is on the boundary between antiferromagnet (AFM) and superconductor. The AFM order of Ce³⁺ local moments causes a significant reentrance behavior in both resistivity and magnetic susceptibility. Upon P doping, T_c increases and reaches a maximum of 21.3 K at x=0.15, and then it is suppressed to lower temperatures. Meanwhile, the AFM order of Ce³⁺ ions remains nearly the same in the whole doping range (0≤x≤0.4). Our experimental results suggest a competition between superconductivity and Kondo effect in the Ce 1111 system.     

Ferromagnetism of epitaxially grown CaRu1−xMxO3 (M=Ti, Mn) films

Epitaxial thin films of CaRu_1−xM_xO₃ (M=Ti, Mn) were fabricated on a (0 0 1)-SrTiO₃ substrate by spin-coat method using organometallic solutions (metal alkoxides). Results of X-ray diffraction and transmission electron microscopy indicate that the epitaxial films were grown pseudomorphically so as to align the [0 0 l] axis of the CaRu_1−xM_xO₃ films perpendicular to the (0 0 1) plane of the SrTiO₃ substrate. Ferromagnetism and metal-insulator transition are induced by the substitution of transition metal ions. The occurrence of ferromagnetism was explained qualitatively assuming a TiRu₆ cluster model for CaRu_1−xTi_xO₃ film and a mixed valence model for CaRu_1−xMn_xO₃ film. Ferromagnetism was also observed for layered CaRuO₃/CaMnO₃ film and CaRuO₃/CaMnO₃/CaRuO₃/CaMnO₃ multilayer film and the magnetism was explained by an interfacial exchange interaction model with magnetic Mn³⁺, Mn⁴⁺, and Ru⁵⁺ ions.