Superconductivity in Ba2−xSrxYCu3Oz prepared at GPa

The compounds Ba_1.4Sr_0.6YCu₃O_z (7.0≤z<7.4) were synthesized at 2 GPa to clarify the effect of high temperature and pressure on the superconducting properties. The structure as observed by powder X-ray diffraction was tetragonal for z≥7.2, and orthorhombic or tetragonal for z<7.1. It has been revealed that high-pressure syntheses suppress the superconductivity in the compounds with z<7.1. Recovery of the superconducting properties occurs above z≥7.2. The effect of Sr substitution on the superconducting properties was also studied. The magnitude of diamagnetism at 5–30 K decreases monotonically from −0.003 to −0.0002 emu/g Oe with increasing x in Ba_2−xSr_xYCu₃O_z (x≥1.2).     

Oxygen nonstoichiometry and phase transitions of the neodymium-rich Nd1+xBa2−xCu3Oz solid solution

On the basis of chemical, thermal analysis and Cu K-edge X-ray absorption measurements, oxygen content in the Nd_1+xBa_2−xCu₃O_z solid solution was determined between 1000°C in air and 400°C in oxygen for x=0.05–0.9 compositions. It has been observed that the oxygen nonstoichiometry Δz of the Nd_1+xBa_2−xCu₃O_7+x/2−Δz solid solution decreases 2–2.5 times for a large substitution (Δz≈0.3–0.33 for x=0.9), despite of the acclaimed higher total oxygen content. The difference in nonstoichiometry is explained by a higher average value of the copper oxidation state (ACV), which is vital for the solid solution with large x even at elevated temperatures (ACV≈2–2.05 for x>0.3 at 1000°C, PO₂=0.21 atm). On the contrary, the ACV after complete oxygenation is almost constant (about 2.25–2.3) for the whole series. The x-dependence of the oxygen content is not monotonous and structural phase transitions can be observed at x=0.3 and x=0.6, as confirmed by the X-ray diffraction and the Raman scattering spectroscopy. The first well-known transition is connected with the oxygen disorder due to the Nd substitution for Ba at random Ba-sites. In the present work, it is proved by the apical oxygen mode broadening in Raman spectra. Ordering of the Nd and Ba atoms with a subsequent orthorhombic distortion of the lattice may occur even at 1000°C in air due to the second transformation at x≈0.6. The invariable orthorhombicity of the Nd-rich solid solution with x>0.6 is not caused by the oxygen absorption as in the x=0.05 case. Existence of high- and low-temperature orthorhombic modifications of this solid solution has been observed for the first time. Finally, a tentative 3D (z–x–T) diagram is suggested for the Nd_1+xBa_2−xCu₃O_z solid solution up to 1000°C in air, including the new x=0.6–0.9 region.     

Nax/2Bi1−x/2MoxV1−xO4 and Bi1−x/3MoxV1−xO4 New Scheelite-related phases

New Scheelite-related solid solutions of the compositions Na_x/2Bi_1−x/2Mo_xV_1−xO₄ (0≤x≤1) and Bi_1−x/3 Mo_xV_1−xO₄(0≤x≤0.2) have been synthesised by the substitution of Na and Mo at the A and B sites respectively of the ABO₄ type ferroelastic BiVO₄. The phases were characterised using chemical analysis, powder X-ray diffraction, scanning electron microscopy, EDAX, and Raman spectroscopy. While almost a continuous solid solution is obtained for the series Na_x/2Bi_1−x/2Mo_xV_1−xO₄, the absence of Na at the A-site results only in a narrow stability region for the other series, Bi_1−x/3 Mo_xV_1−xO₄ where 0≤x≤0.2. Raman spectra of selected samples at room temperature also suggest that vanadium and molybdenum atoms are disordered at the tetrahedral sites.     

Structural and compositional analysis of InBixAsySb(1−x−y) films grown on GaAs(0 0 1) substrates by liquid phase epitaxy

The growth of epitaxial InBi_xAs_ySb_(1−x−y) layers on highly lattice mis-matched semi-insulating GaAs substrates has been successfully achieved via the traditional liquid phase epitaxy. Orientation and single crystalline nature of the film have been confirmed by X-ray diffraction. Scanning electron micrograph shows abrupt interface at micrometer resolution. Surface composition of Bi(x) and As(y) in the InBi_xAs_ySb_(1−x−y) film was measured using energy dispersive X-ray analysis and found to be 2.5 and 10.5 at.%, respectively, and was further confirmed with X-ray photoelectron spectroscopy. Variation of the composition with depth of the film was studied by removing the layers with low current (20 μA) Ar⁺ etching. It was observed that with successive Ar⁺ etching, In/Sb ratio remained the same, while the As/Sb and Bi/Sb ratios changed slightly with etching time. However after about 5 min etching the As/Sb and Bi/Sb ratios reached constant values. The room temperature band gap of InBi_0.025As_0.105Sb_0.870 was found to be in the range of 0.113–0.120 eV. The measured values of mobility and carrier density at room temperature are 3.1×10⁴ cm² V⁻¹ s⁻¹ and 8.07×10¹⁶ cm⁻³, respectively.     

Magnetization measurements of Fe1−xCoxSi

Magnetization measurements are made in pulsed magnetic fields up to 200 kOe at 4.2 K and up to 100 kOe at various temperatures on the alloys Fe_1−xCo_xSi. In the paramagnetic region of x<0.05 or x0.7, we expected a metamagnet transition at high field but no remarkable change of magnetization is observed.     

Influence of Nd substitution on the superconducting properties of ceramics in the 2212 system Bi2−wPbwSr2−xCa1−yNdx+yCu2O8+z

In the system Bi_2−wPb_wSr_2−xCa_1−yNd_x+yCu₂O_8+z different fractions of Nd are substituted on either Sr of Ca sites in order to introduce intrinsic insulating pinning centres. It is shown that a Nd concentration around x or y = 0.2 is likewise favourable with an average Nd---Nd distance in the range of the coherence length in the a, b-plane. However, clear evidence of flux pinning is only present for charge compensation with Pb²⁺. A simultaneous substitution of the Bi-based 2212 superconductor with moderate amounts of Nd³⁺ and Pb²⁺ improves the superconducting properties by strengthening the flux pinning forces.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

Ferromagnetic Zr1−xMnxCo2 laves phase compounds

Structure and magnetic properties of the Zr_1−xMn_xCo_2+δ alloys were studied for 0 x <0.7, δ=0, 0.45. The cubic C15 Laves phase structure shows Mn solubility up to x≈0.4. The other Laves phase with the hexagonal C36 structure found for x0.5 apparently has a small region of Mn solubility in the vicinity of Zr_0.4Mn_0.6Co₂. Though the parent Mn-free compounds are known to be paramagnetic, the Mn-substituted alloys show ferromagnetic behavior with the Curie temperatures up to 625 K and the room-temperature saturation magnetization of about 100 emu/g. The onset of ferromagnetism with the Mn substitution for Zr may be caused by polarization of itinerant 3d electrons, like it was earlier supposed for the off-stoichiometric ZrCo_2+δ. The universal composition dependencies of the intrinsic magnetic properties for different δ can be obtained, if plotted against the amount of zirconium atoms missing in its sublattice. The room-temperature anisotropy with the noticeable anisotropy field of 24 kOe and the 1 1 0 easy magnetization direction laying in a basal plane was found in the hexagonal Zr_0.5Mn_0.5Co₂.     

Effective Ru moment in RuSr2Eu2−xCexCu2O10 from high-temperature magnetic susceptibility

We have made high-temperature (250 K<T<800 K) DC susceptibility measurements in the compounds RuSr₂Eu_2−xCe_xCu₂O₁₀ for x=0.6,0.8, and 1.0 in order to determine the Ru effective magnetic moment. After carefully subtracting all contributions to the magnetic susceptibility except that of the Ru ions, we have been able to fit the Ru susceptibility with a law χ_Ru=χ₀+C_Ru/(T−Θ_Ru). We have found that the Ru effective moment falls between the values expected for Ru⁵⁺ in spin states and . We have also found a dependence of μ_eff(Ru) and Θ_Ru with the Ce content x.     

Superconductivity and crystallographic properties of La2 − xMxCuO4 − δ (M = Na, K)

Superconductivity and crystallographic properties of La_{2 − x}M_xCuO_{4 − δ} (M = Na, K) are studied. In the La_{2 − x}M_xCuO_{4 − δ} system, superconductivity is detected for x 0.2. Oxygen content analysis shows that the system has more oxygen vacancies than the La_{2 − x}Sr_xCuO_{4 − δ} system. These oxygen vacancies may reduce the hole concentration, and high Na-doping is needed to produce superconductivity. In the La_{2 − x}K_xCuO_{4 − δ} system, superconductivity is observed for the first time. Resistivity and magnetic susceptibility measurements show that T_c(onset) is 40 K and the Meissner volume fraction is about 4% for x = 0.7. The system changes from orthorhombic to a tetragonal K₂NiF₄ structure at x ≈ 0.3 and only tetragonal samples show superconductivity.     

A spectroscopic ellipsometric investigation of new critical points of Zn1−xMnxS epilayers

Zn_1−xMn_xS epilayers were grown on GaAs (1 0 0) substrates by hot-wall epitaxy. X-ray diffraction (XRD) patterns revealed that all the epilayers have a zincblende structure. The optical properties were investigated using spectroscopic ellipsometry at 300 K from 3.0 to 8.5 eV. The obtained data were analyzed for determining the critical points of pseudodielectric function spectra, (E) = ₁(E) + i₂(E), such as E₀, E₀ + Δ₀, and E₁, and three E₂ (Σ, Δ, Γ) structures at a lower Mn composition range. These critical points were determined by analytical line-shapes fitted to numerically calculated derivatives of their pseudodielectric functions. The observation of new peaks, as well as the shifting and broadening of the critical points of Zn_1−xMn_xS epilayers, were investigated as a function of Mn composition by ellipsometric measurements for the first time. The characteristics of the peaks changed with increasing Mn composition. In particular, four new peaks were observed between 4.0 and 8.0 eV for Zn_1−xMn_xS epilayers, and their characteristics were investigated in this study.     

Magnetic properties of the pyrite type FexCo1−x−yNiyS2 system

The magnetic phase diagram of the Fe_xCo_1−x−yNi_yS₂ system was determined. Ferromagnetic (F)-, antiferromagnetic (AF )- and paramagnetic (P) phases were found. In the triangular diagram, the F-phase appears along the CoS₂-FeS₂ line, the AF-phase around NiS₂ and the P-phase between the F- and AF-phases. Discussions are given on the F-phase.     

Effect of Pr and Ca substitution on superconductivity in Y(1−x−yPrxCay)Ba2Cu3O7−δ

Pr substituted at constant Ca concentration for Y in (Y_1−x−yPr_xCa_y)Ba₂Cu₃O_7−δ superconductors have been prepared under identical conditions and the temperature dependence of the electrical resistivity of these samples are measured. The resistively determined values of T_c decrease linearly with increasing x (0 ≤ x ≤ 0.2) for constant y = 0.10 and 0.15 which provides convincing evidence that the suppression of superconductivity by Pr is mainly due to magnetic pair breaking. The suppression of superconductivity can also be correlated to the observed changes in oxygen content determined by iodometric analysis and to the average Cu-valences. However, it is found that the observed suppression of T_c cannot be compensated by appropriate hole doping with Ca.     

Characterization of nonstoichiometric nickel manganite spinels NixMn3−x□3δ/4O4+δ by temperature programmed reduction

Cation deficient spinels Ni_xMn_3−x□_3δ/4O_4+δ (0≤x≤1) have been prepared by thermal decomposition of mixed oxalates Ni_x/3Mn_(3−x)/3(C₂O₄)·nH₂O in air at 623 K. They have been characterised by temperature programmed reduction (TPR) under H₂, the reaction being followed by gravimetric and powder X-ray diffraction measurements. It has been shown that TPR proceeds in several steps. The first steps correspond to the loss of nonstoichiometric oxygen leading to the formation of a stoichiometric oxide. During the following stages the manganese cations are reduced, causing the spinel structure to be destroyed, and the formation of solid solution of NiO in a cubic MnO. Subsequently, Ni²⁺ cations undergo a reduction to metallic nickel, and, finally, a mixture of nonstoichiometric MnO_1−δ and metallic nickel is formed. These oxides contain a high level of vacancies which vary with the nickel content with a maximum of δ≈1 near x=0.6. This nonstoichiometry is ascribed both to the presence of Ni³⁺ and excess of Mn⁴⁺.     

Non-Fermi liquid regimes in U1−xMxPd2Al3(M=Y,Th)

The temperature-composition (T–x) phase diagram and NFL characteristics in the electrical resistivity ρ(T), specific heat C(T), and magnetic susceptibility χ(T) at low temperatures for the systems U_1−xM_xPd₂Al₃ (M=Y,Th) are described. The T–x phase diagram, the NFL characteristics, and the underlying mechanism for the NFL behavior are distinctly different for M=Y³⁺ and Th⁴⁺, apparently reflecting the difference in valence of the M atom substituents, and suggesting that U is tetravalent in these two systems.     

Charge ordering in the electron doped Ca1−xYxMnO3 manganites

Structural studies on the electron doped Ca_1−xY_xMnO₃ are presented. At 300 K, orthorhombic O-phase was observed in all cases, associated to low electric resistivity and high Curie–Weiss temperature. For samples with x>0.07, structural phase transitions to more distorted orthorhombic and monoclinic phases were found at T<170K. In these phases only weak ferromagnetic interactions were observed.     

Normal-state transport properties of Ba1−xKxBiO3 crystals

The normal-state transport properties of Ba_1−xK_xBiO₃ crystals with a wide range of potassium compositions (0≤x≤0.62) were studied. Although the host material BaBiO₃ has a monoclinic structure, the system changes from a monoclinic to an orthorhombic structure with a small doping of potassium (0≤x<0.35) and behaves similar to a doped semiconductor, without exhibiting superconductivity. In the composition range, holes are majority carriers in the transport phenomena. When x exceeds a critical value (0.35), the system goes into a cubic superconducting phase with a single metallic band. The vicinity of the critical composition transport phenomena is easy to understand assuming the existence of two conducting channels that are made up of metallic and semiconducting phases. Maximum T_c exceeding 30 K was observed at x0.4, where carrier density was at its maximum. Overdoping with potassium suppresses superconductivity. In the metallic composition of x>0.45, transport seems to correlate with the phonon mode with an energy distribution of 15–43 meV.     

Positive linear magnetoresistance in Fex–C1−x composites

A large positive magnetoresistance (MR) has been found in micro-sized Fe_x–C_1−x composites. At a magnetic field of 5 T, the Fe_0.2–C_0.8 composite has the largest MR, 53.8% and 190% at room temperature and at 5 K, respectively. The magnetic field dependence of the MR can be described approximately as MR∝Bⁿ, and the value of exponent n is determined by the Fe weight concentration and temperature, ranging from 1/4 to 6/4. It appears that Fe_x–C_1−x has a linear field dependence of the positive MR at different temperatures. The possible mechanism for the positive MR is discussed.     

Magnetic properties of Gd2Fe14−xCoxB compounds

The magnetization of magnetically-aligned Gd₂Fe_14−xCo_xB samples with x = 0, 2, 4, 6, 8.4, 11.2 and 14 has been measured at 4.2 K in fields up to 14 T and the anisotropy fields have been derived. The effect of substitution of Co for Fe on the magnetic properties of Gd₂Fe₁₄B has been investigated.     

NMR study of coexistence of ferro- and antiferromagnetism in (Zr1−xNbx)Fe2

The magnetic phase diagram has been investigated in the C14 type (Zr_1−xNb_x)Fe₂ with x0.7 from ⁹³Nb NMR and magnetization measurements. In the compound with x = 0.825 a first order-like transition has been found to occur around 25 K from a canted state with the ferromagnetic moment in the basal plane to a ferromagnetic state with decreasing temperature.