Study on the superconducting composite material formation in the system Bi2Sr2CaCu2O8+x/Al-containing phases

Phase evolution in the Bi---Sr---Ca---Cu---Al---O system was studied. Two Al-containing phases BiSr_1.5Ca_0.5Al₂O_z and (Sr_1−xCa_x)₃Al₂O₆ (x = 0.4 − 0.45) were determined to be chemically compatible with Bi_2.18Sr₂CaCu₂O_8+x (Bi-2212) at temperatures of the samples processing. The phase equilibria in the title system were investigated above the solidus temperature. The BiSr_1.5Ca_0.5Al₂O_z was found to be in equilibrium only with the melt and the (Sr_1−xCa_x)₃Al₂O₆ phase. This latter aluminate equilibrated with Ca,Sr cuprates, CaO, the Cu-free phase, and the liquid. The melting and solidification in Bi-2212, doped with the aluminate, corresponded to the reversible reaction Bi-2212 + BiSr_1.5Ca_0.5Al₂O_z ↔ (Sr_1−xCa_x)₃Al₂O₆ + liquid. Two sets of superconducting composite materials with initial compositions Bi-2212 + nBiSr_1.5Ca_0.5Al₂O_z and Bi-2212 + m(Sr_1−xCa_x)₃Al₂O₆ were prepared by solidification from the partial melt. The former material was composed mostly of large Bi-2212 lamellas separated by the BiSr_1.5Ca_0.5Al₂O_z phase, which destroyed superconducting links between Bi-2212 grains. The latter material consisted of a Bi-2212 polycrystalline matrix with high concentration of small (ca. 3 μm) grains of (Sr_1−xCa_x)₃Al₂O₆ imbedded in Bi-2212 lamellas. The Bi-2212 + m(Sr_1−xCa_x)₃Al₂O₆ materials displayed a trend to enhance flux pinning at T = 60 K with the increase of aluminate phase content.     

Short-range order and F ion diffusion inside the Pb1 − xAlxF2 + x solid solution Part I: F-NMR investigation

A ¹⁹F-NMR investigation of the Pb_{1 − x}Al_xF_{2 + x} (0 ≤ x ≤ 0.12) solid solution and of the ordered Pb₉Al₂F₂₄ phase is undertaken as a function of temperature. Several F⁻ ion groups become progressively mobile at the NMR time scale at increasing temperature, the first, (F_i)_pb and (F_n)_pb, are located in the surroundings of Pb²⁺ cations, the second ones, (F_rd)_AI and (F_ra)_Al, in that of Al³⁺ cations. Four types of fluoride ions are distinguished in the ¹⁹F-NMR spectra of rigid lattice at low temperature (T = 175 K) and the distribution of fluoride ions among the four sites is determined by deconvolution of the spectra registered. The sites occupied by the (F_n)_pb anions are identified with the normal anionic sites of the fluorite network, the others with different interstitial sites.     

Short-range order and F ion diffusion inside the Pb1 − xAlxF2 + x solid solution Part II: Al NMR investigation and proposal of clustering process

A ²⁷Al nuclear magnetic resonance (NMR) investigation at room temperature of the Pb_{1 − x}Al_xF_{2 + x} (0 ≤ x ≤ 0.12) solid solution and of the ordered Pb₉Al₂F₂₄ phase is carried out. Two different types of aluminium ions are identified and their ratio is determined as a function of x. A clustering process based on the formation of column clusters, more and more extended when x increases, is proposed on the basis of results issued from the ¹⁹F (Part I) and ²⁷Al NMR investigations.     

Crystal structure, electrical and magnetic properties of La1 − xSrxCoO3 − y

The crystal structure and properties of La_{1 − x}Sr_xCoO_{3 − y} with strontium contents ranging from x = 0.1 to x = 0.7 have been studied. The lattice parameters were measured as a function of temperature (4.2–400 K) and the crystal structure was found to change from rhombohedral (at low temperatures and values of x) to cubic. While LaCoO₃ is paramagnetic the oxides in the composition range 0.2 < x < 0.6 are soft ferromagnets. The strontium additions are compensated by the formation of Co⁴⁺ (cobalt ions with one positive effective charge, Co_Co^.) and oxygen vacancies (V_o^..). From the results it is concluded that the relative importance of oxygen vacancies increases with increasing temperature and decreasing oxygen activity. As a result the concentration of electronic charge carriers — and the resultant electrical conductivity — decrease with increasing temperature. The defect structure is discussed and it is concluded that defect associations — probably between oxygen vacancies and strontium ions — and formation of microdomains of perovskite-related phases are important aspects of the overall structure of these perovskite phases.     

Synthesis and superconducting properties of the infinite-layer compounds Sr1−xLnxCuO2(Ln=La, Nd, Sm, Gd)

Infinite-layer-type superconductors Sr_1−xLn_xCuO₂ are synthesized under high pressure of 3 GPa for Ln=Sm, Gd as well as for Ln=La, Nd. Their chemical and superconducting properties are systematically studied as functions of doping concentration and the kind of lanthanide ion. As a result, it is demonstrated that the variation of these properties with doping concentration is similar for all the examined Ln³⁺ ions. The solubility limit lies at x ≈ 0.10. CuO₂ sheets are expanded with increasing x, while their spacing decreases. The T_c onset determined by magnetic measurements remains constant for any doping concentration; only the Meissner fraction increases with increasing x.     

Ramans study of Y1−xPrxBa2Cu3O7−δ and YB2Cu3−xZnxO7−δ single crystals

Single crystals with known T_c values of Y_1−xPr_xBa₂Cu₃O_7−δ (Y---Pr1:2:3) and YBa₂Cu_3−xZn_3−xZn_xO_7−δ (Y---Zn1:2:3) systems are studied by Raman measurements. The Raman spectra for (Y---Pr1:2:3) single crystals show that the frequencies of Ba and O_z modes increase as the Pr content increases. The results are consistent with the hole-localization scheme proposed for the suppression of superconductivity in the polycrystalline Y---Pr1:2:3 systems. On the other hand, in the Y---Zn1:2:3 system, all the Raman modes do not change in frequencies. However, the FWHM of the Cu(2) mode increases with the decrease of T_c, indicating strong scattering of charge carriers by the substituted Zn ions in the CuO₂ planes. The induced disorder in the CuO₂ planes may be related with suppression of T_c in the Y---Zn1:2:3 system. Thus, the suppression mechanism in the Y---Zn1:2:3 systems seems to be different from that in the Y---Pr1:2:3 systems.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

Synthesis and characterization of the Aurivillius phases Bi2 − xPbxSr1 − xNdxNb2O9

The n = 2 Aurivillius phase Bi_{2 − x}Pb_xSr_{1 − x}Nd₂O₉ was successfully synthesized as a ceramic material over the whole range of simultaneous, charge compensated substitution x = 0–1.0. Structural investigations were performed by Rietveld refinement applying different space groups Fmmm and A2₁am, and additionally by X-ray absorption spectroscopy (EXAFS) on the Nd L_III-edge, confirming the accommodation of Nd on the atomic sites of Sr, which implies the substitution of Bi³⁺ by the isoelectronic Pb²⁺. The ferroelectric transition temperature T_c = 270 °C of the substituted powders with x = 0.4 and 1.0 is distinctly reduced compared to the unsubstituted sample with T_c = 450 °C. In temperature resolved powder X-ray diffraction patterns no structural phase transition could be detected.     

Nax/2Bi1−x/2MoxV1−xO4 and Bi1−x/3MoxV1−xO4 New Scheelite-related phases

New Scheelite-related solid solutions of the compositions Na_x/2Bi_1−x/2Mo_xV_1−xO₄ (0≤x≤1) and Bi_1−x/3 Mo_xV_1−xO₄(0≤x≤0.2) have been synthesised by the substitution of Na and Mo at the A and B sites respectively of the ABO₄ type ferroelastic BiVO₄. The phases were characterised using chemical analysis, powder X-ray diffraction, scanning electron microscopy, EDAX, and Raman spectroscopy. While almost a continuous solid solution is obtained for the series Na_x/2Bi_1−x/2Mo_xV_1−xO₄, the absence of Na at the A-site results only in a narrow stability region for the other series, Bi_1−x/3 Mo_xV_1−xO₄ where 0≤x≤0.2. Raman spectra of selected samples at room temperature also suggest that vanadium and molybdenum atoms are disordered at the tetrahedral sites.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Oxygen nonstoichiometry and phase transitions of the neodymium-rich Nd1+xBa2−xCu3Oz solid solution

On the basis of chemical, thermal analysis and Cu K-edge X-ray absorption measurements, oxygen content in the Nd_1+xBa_2−xCu₃O_z solid solution was determined between 1000°C in air and 400°C in oxygen for x=0.05–0.9 compositions. It has been observed that the oxygen nonstoichiometry Δz of the Nd_1+xBa_2−xCu₃O_7+x/2−Δz solid solution decreases 2–2.5 times for a large substitution (Δz≈0.3–0.33 for x=0.9), despite of the acclaimed higher total oxygen content. The difference in nonstoichiometry is explained by a higher average value of the copper oxidation state (ACV), which is vital for the solid solution with large x even at elevated temperatures (ACV≈2–2.05 for x>0.3 at 1000°C, PO₂=0.21 atm). On the contrary, the ACV after complete oxygenation is almost constant (about 2.25–2.3) for the whole series. The x-dependence of the oxygen content is not monotonous and structural phase transitions can be observed at x=0.3 and x=0.6, as confirmed by the X-ray diffraction and the Raman scattering spectroscopy. The first well-known transition is connected with the oxygen disorder due to the Nd substitution for Ba at random Ba-sites. In the present work, it is proved by the apical oxygen mode broadening in Raman spectra. Ordering of the Nd and Ba atoms with a subsequent orthorhombic distortion of the lattice may occur even at 1000°C in air due to the second transformation at x≈0.6. The invariable orthorhombicity of the Nd-rich solid solution with x>0.6 is not caused by the oxygen absorption as in the x=0.05 case. Existence of high- and low-temperature orthorhombic modifications of this solid solution has been observed for the first time. Finally, a tentative 3D (z–x–T) diagram is suggested for the Nd_1+xBa_2−xCu₃O_z solid solution up to 1000°C in air, including the new x=0.6–0.9 region.     

The crystal structure of (Pb0.5Cd0.5)Sr2 (Y1−xCax)Cu2O7

The crystal structures of (Pb_0.5Cd_0.5)Sr₂YCu₂O₇, (Pb_0.5Cd_0.5)Sr₂(Y_0.6Ca_0.4)Cu₂O₇ and (Pb_0.5Cd _0.5)Sr₂(Y_0.5Ca_0.5)Cu₂O₇ have been refined by the Rietveld method for the X-ray diffraction data. The refinement results indicate that both Pb and Cd atoms in the (Pb, Cd)O layers and O(3) atoms are displaced from their ideal sites, and that there is a complicated occupation in the (Pb, Cd)O layers, i.e., other cations, such as Sr²⁺, Cu²⁺ and Ca²⁺, can occupy the (Pb, Cd) site for these samples. This may be the reason why the lattice constants do not vary monotanically with the calcium content, and why there exist broad superconducting transitions in the system (Pb_0.5Cd_0.5)Sr₂(Y_1−xCa_x)Cu₂O₇. The refinement results also indicate that, as the calcium content increases, the O(2) atoms move close to the CuO₂ planes and far from the (Pb, Cd)O layers. Thus, the increase of calcium content results in charge transfer from the charge reservoir layer (Pb, Cd)O to the CuO₂ planes. This result is consistent with the bond valence sums of the Cu ions in the CuO₂ planes.     

Characterization of Ce1−xZrxO2 thin films prepared by pyrolytic spray technique

It was demonstrated that spray pyrolysis can be used to prepare Ce_1−xZr_xO₂ thin films with x between 0 and 1. The composition of these films was determined by electron probe microanalysis (EPMA), and the crystalline structure by X-ray diffraction (XRD) and Raman spectroscopy (RS). Cyclic voltammetry (CV) was performed in an electrolyte of propylene carbonate with 1 M LiClO₄. Films with high Zr content were incapable of charge exchange of Li⁺ ions. In the contrast, films with high Ce content were found to be able to insert/extract large charge densities of Li⁺ ions. They also remained transparent during Li⁺ intercalation.     

Effective Ru moment in RuSr2Eu2−xCexCu2O10 from high-temperature magnetic susceptibility

We have made high-temperature (250 K<T<800 K) DC susceptibility measurements in the compounds RuSr₂Eu_2−xCe_xCu₂O₁₀ for x=0.6,0.8, and 1.0 in order to determine the Ru effective magnetic moment. After carefully subtracting all contributions to the magnetic susceptibility except that of the Ru ions, we have been able to fit the Ru susceptibility with a law χ_Ru=χ₀+C_Ru/(T−Θ_Ru). We have found that the Ru effective moment falls between the values expected for Ru⁵⁺ in spin states and . We have also found a dependence of μ_eff(Ru) and Θ_Ru with the Ce content x.     

Influence of Nd substitution on the superconducting properties of ceramics in the 2212 system Bi2−wPbwSr2−xCa1−yNdx+yCu2O8+z

In the system Bi_2−wPb_wSr_2−xCa_1−yNd_x+yCu₂O_8+z different fractions of Nd are substituted on either Sr of Ca sites in order to introduce intrinsic insulating pinning centres. It is shown that a Nd concentration around x or y = 0.2 is likewise favourable with an average Nd---Nd distance in the range of the coherence length in the a, b-plane. However, clear evidence of flux pinning is only present for charge compensation with Pb²⁺. A simultaneous substitution of the Bi-based 2212 superconductor with moderate amounts of Nd³⁺ and Pb²⁺ improves the superconducting properties by strengthening the flux pinning forces.     

Luminescence from Si-Si1−xGex/Si1−yCy-Si structures

Near band edge photoluminescence has been obtained from Si_1−yC_y quantum well (QW) and neighboring Si_1−xGe_x/Si_1−yC_y double QW (DQW) structures. Enhanced no-phonon recombination is observed from the DQW structures and it is attributed to a breaking of the k-selection rule in the presence of the heterointerface. The luminescence persists for measurement temperatures up to 30–50 K and the intensity exhibits a quenching behavior with an activation energy equal to 8–20 meV. In electroluminescence only recombination in the Si_1−xGe_x layer has been observed from neighboring Si_1−xGe_x and Si_1−yC_y DQW structures.     

Synthesis, crystal structure and inelastic neutron scattering in the infinite-layer compounds Sr1−xNdxCuO2

For the first time large samples of the nominal composition Sr_1−xNd_xCuO₂ (x=0.07, 0.15) 10 g in mass each have been prepared using a high-pressure technique. Neutron-diffraction and X-ray measurements have shown that the main phase in the samples obtained is of the infinite-layer structure which has been refined in the tetragonal P4/mmm space group. Both samples are not superconducting. Inelastic neutron scattering has been employed to search for crystalline-electric-field transitions in these compounds. The observed low-energy spectra exhibit one inelastic line of magnetic origin at 18 meV, comparable in energy with a crystalline-electric-field excitation in the high-T_c superconductor NdBa₂Cu₃O_x.     

Niobium based tetragonal tungsten bronzes as potential anodes for solid oxide fuel cells: synthesis and electrical characterisation

In this paper we report studies on a range of niobate based tungsten bronzes, with a view to analysing their potential as anode materials in SOFCs. Six systems were studied, (Sr_1−xBa_x)_0.6Ti_0.2Nb_0.8O₃, Sr_0.6−xLa_xTi_0.2+xNb_0.8−xO₃, (Sr_0.4−xBa_x)Na_0.2NbO₃, (Ba_1−xCa_x)_0.6Ti_0.2Nb_0.8O₃, Ba_0.5−xA_xNbO₃ (A=Ca, Sr), and Ba_0.3NbO_2.8, and the electrical conductivities were examined over a range of oxygen partial pressures (10⁻²⁰–1 bar). All the systems showed good conductivity in low oxygen partial pressures, with values as high as 8 S cm⁻¹ at 930°C (P(O₂)=10⁻²⁰ bar). As the oxygen partial pressure was raised the conductivity dropped showing in most cases an approximate [P(O₂)]^−1/4 dependence and good re-oxidation kinetics. Of all the samples studied the (Sr_1−xBa_x)_0.6Ti_0.2Nb_0.8O₃ and (Ba_1−xCa_x)_0.6Ti_0.2Nb_0.8O₃ systems appear most promising for potential use as anode materials in SOFCs.     

Magnetic properties and percolation threshold in diluted B-spinel ZnCr2xAl2−2xS4: a study through high-temperature expansions

By making use of high-temperature series expansions (HTSE) of the correlation functions, we study the thermal and disorder variation of the short-range order (SRO) in the particular B-spinel ZnCr_2xAl_2−2xS₄. We developed the HTSE for the q-dependent static structure factor S(q) to the order 6 in reciprocal temperature including both the nearest- and next-nearest-neighbour interactions J₁ and J₂, respectively. Respecting the experimental fact that the broad diffuse peak of the neutron is situated at the particular wave vector q₀=[0 0 0.79] and is insensitive to the temperature for a given ratio of dilution x, we have estimated the thermal variation of J₁ and J₂ in the case of the pure compound.

The bond percolation threshold x_p of the ZnCr_2xAl_2−2xS₄ is determined by studying the disorder variation of the correlation length ξ. The x_p is considered as the concentration at which ξ vanishes. The obtained values are x_p=0.27 when only J₁ is considered and 0.23 when both J₁ and J₂ are taken into account.     

Characterization and cathode performance of Li1 − xNi1 + xO2 prepared with the excess lithium method

Samples of Li_{1 − z}Ni_{1 + x}O₂ with various x values were synthesized and their electrochemical properties, phase transitions, and ordering phenomena were investigated comparatively. In order to synthesize samples with a small x value, an excess lithium was used as a starting material to compensate for lithium loss during the calcination process. A stoichiometric sample with a large reversible capacity of more than 200 mAh g⁻¹ is also described.