High dielectric constant PrYxOy sensing films electrolyte-insulator-semiconductor pH-sensor for the detection of urea

In this paper, we describe the structural and sensing properties of high-k PrY_xO_y sensing films deposited on Si substrates through reactive co-sputtering. Secondary ion mass spectrometry and atomic force microscopy were employed to analyze the compositional and morphological features of these films after annealing at various temperatures. The electrolyte-insulator-semiconductor (EIS) device incorporating a PrY_xO_y sensing membrane that had been annealed at 800 °C exhibited good sensing characteristics, including a high sensitivity (59.07 mV pH⁻¹ in solutions from pH 2 to 12), a low hysteresis voltage (2.4 mV in the pH loop 7 → 4 → 7 → 10 → 7), and a small drift rate (0.62 mV h⁻¹ in the buffer solution at pH 7). The PrY_xO_y EIS device also showed a high selective response towards H⁺. This improvement can be attributed to the small number of crystal defects and the large surface roughness. In addition, the enzymatic EIS-based urea biosensor incorporating a high-k PrY_xO_y sensing film annealed at 800 °C allowed the potentiometric analysis of urea, at concentrations ranging from 1 to 16 mM, with a sensitivity of 9.59 mV mM⁻¹.     

Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Structure and conductivity of strontium-doped cerium orthovanadates Ce1−xSrxVO4 (0≤x≤0.175)

A-site substituted cerium orthovanadates, Ce_1−xSr_xVO₄, were synthesised by solid-state reactions. It was found that the solid solution limit in Ce_1−xSr_xVO₄ is at x=0.175. The crystal structure was analysed by X-ray diffraction and it exhibits a tetragonal zircon structure of space group I4₁/amd (1 4 1) with a=7.3670 (3) and c=6.4894 (1) Å for Ce_0.825Sr_0.175VO₄. The UV-vis absorption spectra indicated that the compounds have band gaps at room temperature in the range 4.5-4.6 eV. Conductivity measurements were performed for the first time up to the strontium solid solution limit in air and in dry 5% H₂/Ar with conductivity values at 600 °C ranging from 0.3 to 30 mS cm⁻¹ in air to 30-45 mS cm⁻¹ in reduced atmosphere. Sample Ce_0.825Sr_0.175VO₄ is redox stable at a temperature below 600 °C although the conductivity is not high enough to be used as an electrode for solid oxide fuel cells.     

Enzyme mimics of spinel-type CoxNi1−xFe2O4 magnetic nanomaterial for eletroctrocatalytic oxidation of hydrogen peroxide

A series of spinel-type Co_xNi_1−xFe₂O₄ (x = 0, 0.2, 0.4, 0.5, 0.6, 0.8, 1.0) magnetic nanomaterials were solvothermally synthesized as enzyme mimics for the eletroctrocatalytic oxidation of H₂O₂. X-ray diffraction and scanning electron microscope were employed to characterize the composition, structure and morphology of the material. The electrochemical properties of spinel-type Co_xNi_1−xFe₂O₄ with different (Co/Ni) molar ratio toward H₂O₂ oxidation were investigated, and the results demonstrated that Co_0.5Ni_0.5Fe₂O₄ modified carbon paste electrode (Co_0.5Ni_0.5Fe₂O₄/CPE) possessed the best electrocatalytic activity for H₂O₂ oxidation. Under optimum conditions, the calibration curve for H₂O₂ determination on Co_0.5Ni_0.5Fe₂O₄/CPE was linear in a wide range of 1.0 × 10⁻⁸–1.0 × 10⁻³ M with low detection limit of 3.0 × 10⁻⁹ M (S/N = 3). The proposed Co_0.5Ni_0.5Fe₂O₄/CPE was also applied to the determination of H₂O₂ in commercial toothpastes with satisfactory results, indicating that Co_xNi_1−xFe₂O₄ is a promising hydrogen peroxidase mimics for the detection of H₂O₂.     

Crystal chemistry and crystallography of the SrR2CuO5 (R=lanthanides) phases

The crystal chemistry and crystallography of the compounds SrR₂CuO₅ (Sr-121, R=lanthanides) were investigated using the powder X-ray Rietveld refinement technique. Among the 11 compositions studied, only R=Dy and Ho formed the stable SrR₂CuO₅ phase. SrR₂CuO₅ was found to be isostructural with the “green phase”, BaR₂CuO₅. The basic structure is orthorhombic with space group Pnma. The lattice parameters for SrDyCuO₅ are a=12.08080(6) Å, b=5.60421(2) Å, c=7.12971(3) Å, V=482.705(4) Å³, and Z=8; and for the Ho analog are a=12.03727(12) Å, b=5.58947(7) Å, c=7.10169(7) Å, V=477.816(9) Å³, and Z=8. In the SrR₂CuO₅ structure, each R is surrounded by seven oxygen atoms, forming a monocapped trigonal prism (RO₇). The isolated CuO₅ group forms a distorted square pyramid. Consecutive layers of prisms are stacked in the b-direction. Bond valence calculations imply that residual strain is largely responsible for the narrow stability of the SrR₂CuO₅ phases with R=Dy and Ho only. X-ray powder reference diffraction patterns for SrDy₂CuO₅ and SrHo₂CuO₅ were determined.     

Crystal growth and structural investigation of A2BReO6 (A=Sr, Ba; B=Li, Na)

Single crystals of the double perovskite rhenates A₂BReO₆ (A=Sr, Ba; B=Li, Na) were grown out of molten hydroxide fluxes. Single crystals of orange/yellow Ba₂LiReO₆, Ba₂NaReO₆ and Sr₂LiReO₆ were solved in the cubic, Fm-3m space group with a=8.1214(11) Å, 8.2975(3) Å, and 7.9071(15) Å, respectively, while Sr₂NaReO₆ was determined to be monoclinic P2₁/n with a=5.6737(6) Å, b=5.7988(6) Å, c=8.0431(8) Å, and β=90.02(6) °. The cubic structure consists of a rock salt lattice of corner-shared ReO₆ and MO₆ (M=Li, Na) octahedra which, in the monoclinic structure, are both tilted and rotated. A discrepancy exists between the symmetry of Sr₂LiReO₆ indicated by the single-crystal refinement of flux-grown crystals (cubic, Fm-3m) and the symmetry indicated by the powder diffraction data collected on polycrystalline samples prepared by the ceramic method (tetragonal, I4/m). It is possible that the cubic crystals are a kinetic product that forms in small quantities at low temperatures, while the powder represents the more stable polymorph that forms at higher reaction temperature.     

Thermoelectric properties of p-type pseudo-binary (Ag0.365Sb0.558Te)x-(Bi0.5Sb1.5Te3)1−x (x=0-1.0) alloys prepared by spark plasma sintering

In this paper, pseudo-binary (Ag_0.365Sb_0.558Te)_x-(Bi_0.5Sb_1.5Te₃)_1−x (x=0-1.0) alloys were prepared using spark plasma sintering technique, and the composition-dependent thermoelectric properties were evaluated. Electrical conductivities range from 7.9×10⁴ to 15.6×10⁴ Ω⁻¹ m⁻¹ at temperatures of 507 and 318 K, respectively, being about 3.0 and 8.5 times those of Bi_0.5Sb_1.5Te₃ alloy at the corresponding temperatures. The optimal dimensionless figure of merit (ZT) of the sample with molar fraction x=0.025 reaches 1.1 at 478 K, whereas that of the ternary Bi_0.5Sb_1.5Te₃ alloy is 0.58 near room temperature. The results also reveal that a direct introduction of Ag_0.365Sb_0.558Te in the Bi-Sb-Te system is much more effective to the property improvement than naturally precipitated Ag_0.365Sb_0.558Te in the Ag-doped Ag-Bi-Sb-Te system.     

Preparation and photoluminescence properties of RE:Na3La9O3(BO3)8 (RE=Er, Yb) crystals

Using Na₂CO₃-H₃BO₃-NaF as fluxes, transparent RE:Na₃La₉O₃(BO₃)₈ (abbr. RE:NLBO, RE=Er, Yb) crystals have been grown by the top seed solution growth (TSSG) method. The X-ray powder diffraction analysis shows that the RE:NLBO crystals have the same structure with NLBO. The element contents were determined by molar to be 0.64% Er³⁺ in Er:NLBO, 2.70% Yb³⁺ in Yb:NLBO, respectively. The polarized absorption spectra of RE:NLBO have been measured at room temperature and show that both Er:NLBO and Yb:NLBO have a strong absorption bands near 980 nm with wide FWHM (Full Wave at Half Maximum) (21 nm for Er:NLBO and 25 nm for Yb:NLBO). Fluorescence spectra have been recorded. Yb:NLBO has the emission peaks at 985 nm, 1028 nm and 1079 nm and the emission peak of Er:NLBO is at 1536 nm. Spectral parameters have been calculated by the Judd-Ofelt theory for Er:NLBO and the reciprocity method for Yb:NLBO, respectively. The calculated values show that Er:NLBO is a candidate of 1.55 μm laser crystals and Yb:NLBO is a candidate for self-frequency doubling crystal.     

Synthesis and electrical conductivity of perovskite-type PrCo1−xMgxO3

Oxides in the system PrCo_1−xMg_xO₃ (x=0.0, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized by citrate technique and characterized by powder X-ray diffraction and scanning electron microscope. All compounds have a cubic perovskite structure (space group ). The maximum ratio of doped Mg in the system PrCo_1−xMg_xO₃ is x=0.2. Further doping leads to the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃. The substitution of Mg for Co improves the performance of PrCoO₃ as compared to the electrical conductivity measured by a four-probe electrical conductivity analyzer in the temperature range from 298 to 1073 K. The substitution of Mg for Co on the B site may be compensated by the formations of Co⁴⁺ and oxygen vacancies. The electrical conductivity of PrCo_1−xMg_xO₃ oxides increases with increasing x in the range of 0.0-0.2. The increase in conductivity becomes considerable at the temperatures ?673 K especially for x?0.1; it reaches a maximum at x=0.2 and 1073 K. From x>0.2 the conductivity of PrCo_1−xMg_xO₃ starts getting lower. This is probably a result of the segregation of Pr₆O₁₁ in PrCo_1−xMg_xO₃ , which blocks oxygen transport, and association of oxygen vacancies. A change in activation energy for all PrCo_1−xMg_xO₃ compounds (x=0-0.25) was observed, with a higher activation energy above 573 K and a lower activation energy below 573 K. The reasons for such a change are probably due to the change of dominant charge carriers from Co⁴⁺ to Vö in PrCo_1−xMg_xO₃ oxides and a phase transition mainly starting at 573 K.     

Effect of capping and particle size on Raman laser-induced degradation of γ-Fe2O3 nanoparticles

Diol capped γ-Fe₂O₃ nanoparticles are prepared from ferric nitrate by refluxing in 1,4-butanediol (9.5 nm) and 1,5-pentanediol (15 nm) and uncapped particles are prepared by refluxing in 1,2-propanediol followed by sintering the alkoxide formed. X-ray diffraction (XRD) shows that all the samples have the spinel phase. Raman spectroscopy shows that the samples prepared in 1,4-butanediol and 1,5-pentanediol and 1,2-propanediol (sintered at 573 and 673 K) are γ-Fe₂O₃ and the 773 K-sintered sample is Fe₃O₄. Raman laser studies carried out at various laser powers show that all the samples undergo laser-induced degradation to α-Fe₂O₃ at higher laser power. The capped samples are however, found more stable to degradation than the uncapped samples. The stability of γ-Fe₂O₃ sample with large particle size (15.4 nm) is more than the sample with small particle size (10.2 nm). Fe₃O₄ having a particle size of 48 nm is however less stable than the smaller γ-Fe₂O₃ nanoparticles.     

Direct syntheses of Lan+1NinO3n+1 phases (n=1, 2, 3 and ∞) from nanosized co-crystallites

A new direct route for the “bottom up” syntheses of phases in the La_n+1Ni_nO_3n+1 series (n=1, 2, 3 and ∞) has been achieved via single-step heat treatments of nanosized co-crystallized precursors. The co-crystallized precursors were prepared using a continuous hydrothermal flow synthesis system that uses a superheated water flow at ca. 400 °C and 24.1 MPa to produce nanoparticulate slurries. Overall, a significant reduction in time and number of steps for the syntheses of La₃Ni₂O₇ and La₄Ni₃O₁₀ was achieved compared with more conventional synthesis methods, which typically require multiple homogenization and reheating steps over several days.     

Synthesis and characterization of metal substituted AlxCr1−x(acetylacetonate)3 single-source precursors for their application to MOCVD of thin films

A detailed study, involving the synthesis of a single-source precursor containing two metal ions sharing the same crystallographic site, has been undertaken to elucidate the use of such a single-source precursor in a CVD process for growing thin films of oxides comprising these two metals, ensuring a uniform composition and distribution of metal ions. The substituted complexes Cr_1−xAl_x(acac)₃, where acac = acetylacetonate, have been prepared by a co-synthesis method, and characterized using UV–Vis spectroscopy, TGA/DTA measurements, and single crystal X-ray diffraction at low temperature. All the studied compositions crystallize in the monoclinic space group P2₁/c with Z = 4 in the unit cell. It was observed that the ratio (Al:Cr) of the site occupancy for the metal ions, obtained from single crystal refinement, is in agreement with the results obtained from complexometric titrations. All the solid state structures have the metal in an octahedral environment forming six-membered chelate rings. M–O acac bond lengths and disorder in the terminal carbon have been studied in detail for these substituted metal–organic complexes. One composition among these was chosen to evaluate their suitability as a single-source precursor in a LPMOCVD process (low-pressure metal–organic chemical vapour deposition) for the deposition of a substituted binary metal oxide thin film. The resulting thin films were characterized by X-ray diffraction, scanning electron microscopy, and infrared spectroscopy.     

Transport coefficients of titanium-doped Sb2Te3 single crystals

Titanium-doped single crystals (c_Ti=0-2×10²⁰ atoms cm⁻³) were prepared from the elements Sb, Ti, and Te of 5 N purity by a modified Bridgman method. The obtained crystals were characterized by measurements of the temperature dependence of the electrical resistivity, Hall coefficient, Seebeck coefficient and thermal conductivity in the temperature range of 3-300 K. It was observed that with an increasing Ti content in the samples the electrical resistivity, the Hall coefficient and the Seebeck coefficient increase. This means that the incorporation of Ti atoms into the Sb₂Te₃ crystal structure results in a decrease in the concentration of holes in the doped crystals. For the explanation of the observed effect a model of defects in the crystals is proposed. The data of the lattice thermal conductivity were fitted well assuming that phonons scatter on boundaries, point defects, charge carriers, and other phonons.     

Structural, spectroscopic and photoluminescence studies of LiEu(WO4)2−x(MoO4)x as a near-UV convertible phosphor

A series of lithium europium double tungsto-molybdate phosphors LiEu(WO₄)_2−x(MoO₄)_x (x=0, 0.4, 0.8, 1.2, 1.6, 2.0) have been synthesized by solid-state reactions and their crystal structure, optical and luminescent properties were studied. As the molybdate content increases, the intensity of the ⁵D₀→⁷F₂ emission of Eu³⁺ activated at wavelength of 396 nm was found to increase and reach a maximum when the relative ratio of Mo/W is 2:0. These changes were found to be accompanied with the changes in the spectral feature, which can be attributed to the crystal field splitting of the ⁵D₀→⁷F₂ transition. As the molybdate content increases the emission intensity of the 615 nm peak also increases. The intense red-emission of the tungstomolybdate phosphors under near-UV excitation suggests them to be potential candidate for white light generation by using near-UV LEDs. In this study the effect of chemical compositions and crystal structure on the photoluminescent properties of LiEu(WO₄)_2−x(MoO₄)_x is investigated and discussed.     

Structure and magnetic properties of RE2Cu2Cd

The ternary intermetallic compounds RE₂Cu₂Cd (RE=Y, Sm, Gd-Tm, Lu) were synthesized by induction-melting of the elements in sealed tantalum tubes. The samples were characterized by X-ray powder diffraction. The structure of Gd₂Cu₂Cd was refined from single crystal X-ray diffractometer data: Mo₂FeB₂ type, space group P4/mbm, a=756.2(3), c=380.2(3) pm, wR2=0.0455, 321 F² values, 12 variables. The structures are 1:1 intergrowth variants of slightly distorted CsCl and AlB₂ related slabs of compositions RECd and RECu₂. The copper and cadmium atoms build up two-dimensional [Cu₂Cd] networks (257 pm Cu-Cu and 301 pm Cu-Cd in Gd₂Cu₂Cd) which are bonded to the rare earth atoms via short RE-Cu contacts (290 pm in Gd₂Cu₂Cd). Temperature dependent susceptibility measurements of RE₂Cu₂Cd with RE=Gd, Tb, Dy, and Tm show experimental magnetic moments which are close to the free RE³⁺ ion values. The four compounds show ferromagnetic ordering at T_C=116.7(2), 86.2(3), 48.4(1), and 14.5(1) K, respectively, as confirmed by heat capacity measurements. Dy₂Cu₂Cd shows a spin reorientation at T_N=16.9(1) K.     

Complex formation equilibria between Ag(I) and thioureas in n-propanol

Complex formation equilibria between Ag(I) and thiourea or N-alkyl-substituted thioureas have been investigated in n-propanol by potentiometry at 10 °C intervals from 5 to 50 °C. Stepwise formation of tris-coordinated AgL_n (n = 1-3) complexes has been found for the majority of the ligands. ΔH and ΔS values for the complex formation reactions have been evaluated from the dependence of ln β_n on temperature. The alkyl-substituents affect the ligand affinities in different ways in relation with the coordination level n.The reactions are exothermic with few exceptions. Enthalpy favoured complex formation with negative dependence of ΔG on temperature (ΔS > 0) have been found.The enthalpy and entropy changes for the stepwise complex formation equilibria are correlated by two linear compensative relationships with the same isoequilibrium temperature 50-51 °C.     

Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu)

Single crystals of K₃RESi₂O₇ (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were grown from a potassium fluoride flux. Two different structure types were found for this series. Silicates containing the larger rare earths, RE=Gd, Tb, Dy, Ho, Er, Tm, Yb crystallize in a structure K₃RESi₂O₇ that contains the rare-earth cation in both a slightly distorted octahedral and an ideal trigonal prismatic coordination environment, while in K₃LuSi₂O₇, containing the smallest of the rare earths, lutetium is found solely in an octahedral coordination environment. The structure of K₃LuSi₂O₇ crystallizes in space group P6₃/mmc with a=5.71160(10) Å and c=13.8883(6) Å. The structures containing the remaining rare earths crystallize in the space group P6₃/mcm with the lattice parameters of a=9.9359(2) Å, c=14.4295(4) Å, (K₃GdSi₂O₇); a=9.88730(10) Å, c=14.3856(3) Å, (K₃TbSi₂O₇); a=9.8673(2) Å, c=14.3572(4) Å, (K₃DySi₂O₇); a=9.8408(3) Å, c=14.3206(6) Å, (K₃HoSi₂O₇); a=9.82120(10) Å, c=14.2986(2) Å, (K₃ErSi₂O₇); a=9.80200(10) Å, c=14.2863(4) Å, (K₃TmSi₂O₇); a=9.78190(10) Å, c=14.2401(3) Å, (K₃YbSi₂O₇). The optical properties of the silicates were investigated and K₃TbSi₂O₇ was found to fluoresce in the visible.     

Crystal structure and the standard molar enthalpy of formation of a coordination polymer [Cu(nip)(phen)]n

A coordination polymer [Cu(nip)(phen)]_n was hydrothermally synthesized by the reaction of Cu(NO₃)₂ with 5-nitroisophthalic acid and phen. Single-crystal structure analysis showed that the complex crystallized in the monoclinic space group P2₁/c; a = 10.6566(13); b = 12.5931(15); c = 13.0514(16) Å; β = 95.474(2)°, V = 1743.5(4) Å³; Z = 4. The standard molar enthalpy of formation of the complex was determined to be −554 ± 11 kJ mol⁻¹.     

Structure and high-temperature thermoelectric properties of SrAl2Si2

Single crystals of SrAl₂Si₂ were synthesized by reaction of the elements in an aluminum flux at 1000 °C. SrAl₂Si₂ is isostructural to CaAl₂Si₂ and crystallizes in the hexagonal space group P-3m1 (90 K, a=4.1834 (2), c=7.4104 (2) Å, Z=1, R1=0.0156, wR2=0.0308). Thermal analysis shows that the compound melts at ∼1020 °C. Low-temperature resistivity on single crystals along the c-axis shows metallic behavior with room temperature resistivity value of ∼7.5 mΩ cm. High-temperature Seebeck, resistivity, and thermal conductivity measurements were made on hot-pressed pellets. The Seebeck coefficient shows negative values in entire temperature range decreasing from ∼−78 μV K⁻¹ at room temperature to −34 μV K⁻¹ at 1173 K. Seebeck coefficients are negative indicating n-type behavior; however, the temperature dependence is consistent with contribution from minority p-type carriers as well. The lattice contribution to the thermal conductivity is higher than for clathrate structures containing Al and Si, approximately 50 mW cm⁻¹ K, and contributes to the overall low zT for this compound.     

Contrasting oxide crystal chemistry of Nb and Ta:: The structures of the hexagonal bronzes BaTa2O6 and Ba0.93Nb2.03O6

The high-temperature hexagonal forms of BaTa₂O₆ and Ba_0.93Nb_2.03O₆ have P6/mmm symmetry with unit-cell parameters a=21.116(1) Å, c=3.9157(2) Å and a=21.0174(3) Å, c=3.9732(1) Å, respectively. Single crystal X-ray structure refinements for both phases are generally consistent with a previously proposed model, except for displacements of some Ba atoms from high-symmetry positions. The structures are based on a framework of corner- and edge-connected Nb/Ta-centred octahedra, with barium atoms occupying sites in four different types of [0 0 1] channels with hexagonal, triangular, rectangular and pentagonal cross-sections. The refinements showed that the non-stoichiometry in the niobate phase is due to barium atom vacancies in the pentagonal channels and to extra niobium atoms occupying interstitial sites with tri-capped trigonal prismatic coordination. The origin of the non-stoichiometry is attributed to minimisation of non-bonded Ba-Ba repulsions. The hexagonal structure is related to the structures of the low-temperature forms of BaNb₂O₆ and BaTa₂O₆, through a 30° rotation of the hexagonal rings of octahedra centred at the origin.