Under the photocatalysis of 365 nm ultraviolet radiation, ultrafine TiO2 caused the oxidative damage of Teasy plasmid DNA. The damage was determined by gel-electrophoresis. Then, a different dose of β-CD was added to the reaction, and the damage was restrained. The rate of damage restraining reached 97% when the mass of β-CD was 4 times as that of TiO2. Through UV scan and IR spectroscopy, it was found that the Ti-O of ultrafine TiO2 was bound with -OH of β-CD cavum and the -OH on the surface of ultrafine TiO2 disappeared, so the formation of · OH was controlled. The ultrafine TiO2 has been widely used, but it was determined to be carcinogenic by some research. The protection effect of β-CD to DNA in the molecular level takes a new look on the surface modification of nano particles to decrease the toxic effect.     

碳纳米管/TiO_2复合材料的制备及表征研究

采用溶胶-凝胶法和水热合成法,制备出碳纳米管/TiO2(CNTs/TiO2)复合材料。通过X-射线衍射仪(XRD)、扫描电子显微镜(SEM),紫外-可见漫反射光谱(UV-Vis),荧光光谱(LS)检测CNTs/TiO2的晶型及形貌。结果表明:锐钛矿相TiO2纳米颗粒负载在碳纳米管的管壁上,CNTs/TiO2在紫外-可见光波长范围均有较好的吸收性能。在灭菌灯照射下,以甲基橙溶液为降解目标,CNTs/TiO2复合材料对甲基橙溶液的降解有高的光催化活性,180 min内降解率达到85%以上。     

SO_4~(2-)/TiO_2、PO_4~(3-)/TiO_2、BO_3~(3-)/TiO_2系列固体酸的酸性、结构和晶相的研究

制备了ＳＯ４２－／ＴｉＯ２（Ⅰ）、ＰＯ４３－／ＴｉＯ２（Ⅱ）、ＢＯ３３－／ＴｉＯ２（Ⅲ）系列固体酸。用ＩＲ、Ｒａｍａｎ光谱对该系列固体酸进行结构表征,结果表明ＳＯ４２－与ＴｉＯ２表面的结合为螯合式双配位结构和共价硫酸盐共存,ＰＯ４３－与ＴｉＯ２表面的结合为桥式三配位结构,ＢＯ３３－与ＴｉＯ２表面的结合为单齿单配位结构和螯桥混合式三配位结构共存。用由溶液中正丁胺的吸附等温线测定固体表面酸度的方法测定了样品的酸量,结果表明酸量大小为Ⅰ＞Ⅱ＞Ⅲ。用ＸＲＤ技术对该系列固体酸进行考察,衍射图分析提示该系列固体酸主要都为锐钛矿型晶型,但Ⅰ、Ⅱ、Ⅲ中又各自夹杂其它不同的晶型     

SO2-4/TiO2光催化氧化邻硝基苯酚

采用不同浓度的硫酸溶液浸渍处理TiO2,制得不同SO2-4含量的SO2-4/TiO2光催化剂.考察了光催化剂对邻硝基苯酚溶液的光催化行为.发现SO2-4/TiO2的光催化活性高于TiO2的光催化活性,浸渍液中H2SO4的浓度和焙烧温度对SO2-4/TiO2的催化活性有一定的影响,最佳浸渍H2SO4浓度为0.5 mol·L-1,最佳焙烧温度为500℃.     

MoO3/TiO2 和WO3/TiO2 光催化分子氧氧化甲烷的活性

以Ｓｏｌ－Ｇｅｌ法制备的、表面积和孔径相近的含水ＭｏＯ３／ＴｉＯ２、ＷＯ３／ＴｉＯ２为催化剂,光催化分子氧氧化甲烷,初步研究表明,催化剂的活性高于ＴｉＯ２,且有少量的甲醇生成。     

WC/TiO2纳米复合材料的制备及其电催化性能

以TiCl4为原料, 采用溶胶水解法合成了金红石型纳米TiO2颗粒, 并以其为载体制备了WC/TiO2纳米复合材料. 采用X射线衍射(XRD)、扫描电子显微镜(SEM)和X射线能谱(EDS)等手段分析了WC/TiO2纳米复合材料的晶相组成和表面形貌. 结果显示样品是由WC, TiO2和W组成, 纳米WC颗粒均匀地包覆在TiO2的表面, 并与TiO2构成了WC/TiO2纳米复合材料. 采用循环伏安法和计时电流法研究了WC/TiO2纳米复合材料对硝基苯的电催化性能. 结果表明, WC/TiO2纳米复合材料对硝基苯的电催化活性和电化学稳定性均优于介孔结构碳化钨(meso-WC)和纳米WC颗粒(part-WC).     

超临界流体干燥法制备TiO2／C纳米粒子及光催化性能

以TiCl4为原料,采用溶胶凝胶法结合超临界流体干燥法(SCFD)制备了纳米级TiO2/C复合光催化剂.以苯酚的光催化降解对所得催化剂的催化活性进行了评价.结果表明,纳米TiO2/C复合粒子与单组分TiO2比较,复合粒子光催化活性高于单组分的TiO2,h苯酚降解率高达975 ％,COD为957%.并用XRD、TEM、 UV-Vis和XPS等手段进行了表征,iO2以锐钛矿型形式存在.比较了不同制备方法制得的TiO2/C复合催化剂,得出超临界干燥法制备的光催化剂具有粒径小,比表面积大,分散性好,光催化活性高等特点.     

Thermal decomposition of the carbon nanotube/SiO<Subscript>2</Subscript>precursor powders

Summary TG-DSC-MS (thermogravimetry-differential scanning calorimetry-mass spectrometry) coupling techniques were used to make a simultaneous characterizing study for the thermal decomposition process of the carbon nanotube (CNT)/SiO₂precursor powders prepared by rapid sol-gel method. The thermal stability of the CNT and the SiO₂pure gel were investigated by TG-DSC. The results showed that the oxidation of CNT began from 530 and combusted at about 678°C at the heating rate of 10°C min^-1in air. Moreover, the faster the heating rate, the higher the temperature of CNT combustion. The appropriate calcinations temperature of the CNT/SiO₂precursor powders should be held for 1 h at 500°C.     

TiO2/柚子皮生物质活性炭复合材料的制备和吸附光降解性研究

本文以自制柚子皮生物质活性炭为原料,采用凝胶-溶胶法合成TiO2/柚子皮生物质活性炭复合材料(TiO2/BAC)。对复合材料进行SEM、FTIR、XRD等表征,并研究该复合材料对中性红、亚甲基蓝染料及甲醛的吸附降解性能。结果表明,在复合材料中柚子皮生物质活性炭的添加量为7 g、预吸附时间为2 h时,对染料具有最佳的吸附降解效果,复合材料在循环使用5次后对染料的吸附降解率仍达到了80 %以上。当活性炭的添加量为6 g、复合材料的添加量为2 g时,复合材料对甲醛的吸附降解达到最大,可达61%。表明该复合材料对中性红、亚甲基蓝染料及甲醛具有良好的吸附降解效果,有望用于废水染料的去除和家居甲醛净化。     

AgBr/TiO2复合催化剂:双注法制备及其可见光催化性能

以TiO₂为载体,采用双注法合成了AgBr/TiO₂复合光催化剂.利用X射线衍射仪(XRD)、紫外可见分光光度计(UV-Vis)和扫描电子显微镜(SEM)对AgBr/TiO₂的结构、光吸收、形貌进行了表征.研究了AgBr/TiO₂在可见光下对甲基橙和丁基罗丹明B的光催化活性.结果表明,与TiO₂相比,AgBr/TiO₂的光吸收范围拓展到400—600nm波段,并且随着AgBr负载量的增加,AgBr/TiO₂的可见光吸收强度增强;当AgBr与TiO₂的摩尔比为0.25时,AgBr/TiO₂具有最大催化活性;在相同条件下,AgBr/TiO₂对丁基罗丹明B的降解效果优于甲基橙.     

Pr2O3/TiO2纳米粒子的制备及其US/UV协同催化降解苯酚的研究

以钛酸丁酯为原料,用溶胶-凝胶(Sol-gel)法制备了Pr2O3/TiO2纳米粒子.采用X光衍射仪对粉体的物相进行了表征.样品经500 ℃焙烧2 h后,0.5%(摩尔分数)Pr3 TiO2纳米粉末为单一的锐钛型结构.研究了US(超声波)/UV(紫外光)协同催化氧化水中苯酚的降解效果,考察了超声波声强、溶液pH值、反应温度和催化剂投加量对苯酚降解速率的影响.研究结果表明:US/UV协同催化氧化要比单独超声波或光化学处理效果显著,证实了声光联合技术具有明显的协同效应.     

Ag/TiO2中空纳米纤维光催化材料的制备及表征

以棉花纤维为模板制备了银掺杂的TiO₂中空纳米纤维光催化材料, 利用热重分析(TG)、扫描电子显微镜(SEM)、X光电子能谱(XPS)、X射线衍射(XRD)、Zeta电位、紫外-可见光谱(UV-Vis)和傅立叶变换红外光谱(FT-IR)等技术对该材料的形貌、晶体结构、银的状态等特性进行了表征. 以亚甲基蓝(MB)的脱色降解为模型反应, 考察了银掺杂的样品Ag/TiO₂在不同光源下的光催化性能. 结果表明, 所制得的Ag/TiO₂材料保留了棉花纤维的形貌, 且表面带有大量的负电荷|该Ag/TiO₂材料在太阳光条件下的光催化性能显著高于同条件下TiO₂和同材料在紫外光条件下的, 如Ag/TiO₂在太阳光下1.5 h可使MB溶液的脱色降解率在95%以上, 在TiO₂上2.5 h时不足60%, 低于Ag/TiO₂上0.5 h的结果|在紫外光条件下Ag/TiO₂ 3 h时脱色降解率仅为35%. 连续重复使用5次时Ag/TiO₂仍能保证MB溶液的脱色降解率在90%以上|该纤维光催化材料易于离心分离去除、再利用. 因此, 以棉花为模板制备的Ag/TiO₂中空纳米纤维催化材料是一种无能耗、无污染、高活性的绿色环保型光催化材料.     

Self-crystallized Interlayer Integrating Polysulfide-adsorbed TiO2/TiO and Highly-electron-conductive TiO for High-stability Lithium-Sulfur Batteries

Low-cost lithium sulfur(Li-S)batteries afford preeminent prospect as a next-generation high-energy storage device by virtue of great theoretical capacity.Nevertheless,their applications are restricted by some challenging technical barriers,such as weak cycling stability and low poor-conductivity sulfur loading originated in notorious shuttling effect of polysulfide intermediates.Herein,free of any complicated compositing process,we design an interlayer of carbon fiber paper supported TiO2/TiO to impede the shuttle effect and enhance the electrical conductivity via physical isolation and chemical adsorption.Such a self-crystallized homogeneous interlayer,where TiO2/TiO enables absorbing lithium polysulfides(LiPSs)and TiO plays a key role of high-electron-conductivity exhibited ultrahigh capacities(1000 mA·h/g at 0.5 C and 900 mA·h/g at 1 C)and outstanding capacity retention rate(97%)after 100 cycles.Thus,our design provides a simple route to suppress the shuttle effect via self-derived evolution Li-S batteries.     

TiO2/Ag2O纳米材料的制备及其对甲醛的气敏性能

采用溶胶-凝胶法制备了掺杂Ag的TiO2纳米晶粉体. 用XRD、TEM和BET方法对纳米晶的晶型﹑晶粒大小和表面性能进行了表征. 分析结果显示, 相同条件下掺杂Ag的TiO2比纯TiO2纳米材料具有更大的比表面积. 气敏性能测试结果表明, 掺杂Ag的TiO2传感器对甲醛有较好的灵敏度和更高的选择性.当焙烧温度为500 ℃, 掺杂Ag的摩尔比为5%(n(AgNO3)/n(Ti(OC4H9)4)=5%)时, TiO2对甲醛气体敏感性能最好. 在最佳工作电流124 mA下, 该元件对10 μL·L-1 HCHO的灵敏度S 接近4, 它的响应时间不超过1 s, 恢复时间为9 s.     

YFeO3/TiO2异质结材料的制备及其光催化性能研究

通过研磨-焙烧法制备了YFeO3/TiO2异质结材料,考察了焙烧温度和组分质量含量变化对合成异质结材料的影响;进行了X射线衍射(XRD)、傅里叶红外(FRIR)、紫外-可见漫反射(UV-vis/DRS)、光电子能谱(XPS)等表征并测试了不同样品光催化降解橙黄Ⅱ的活性.结果表明,YFeO3/TiO2复合氧化物不仅具有明显的可见光光响应,而且表现出比单组分相对较高的光催化降解活性.最佳的复合样品为600℃焙烧下,w(TiO2)=0.9的复合样品.复合材料光催化活性的提高可归因于p-YFeO3与n-TiO2间存在的p-n结.     

超临界CO2中模板法制备TiO2/SiO2复合多孔材料

在超临界CO2中以颗粒状活性炭为模板,正硅酸乙酯和钛酸四正丁酯为前驱体制备了TiO2/S iO2复合多孔材料。研究了超临界状态下不同涂层温度和涂层压力对涂层率的影响,当温度为40℃时,压力在22 MPa为该温度的最佳涂层压力;固定压力为22 MPa,涂层温度为70℃为最佳涂层条件。X射线衍射(XRD)的研究结果表明,产物由锐钛矿型TiO2、金红石型TiO2以及结晶的S iO2这3种物质构成。根据产物的N2气吸附-脱附等温线计算,产物的比表面积达到144.44 m2/g,平均孔径为7 nm左右。扫描电子显微镜的分析结果证明,产物在一定程度上实现了对模板的复制,同时透射电子显微镜显示,复合材料的纳米颗粒尺寸具有良好的分散性。     

量子顺电体La1/2Na1/2TiO3纳米晶的制备与谱学表征

用改进硬脂酸溶胶-凝胶法制备了量子顺电体La_1/2Na_1/2TiO₃纳米晶,用差热-热重分析和X射线衍射测试了样品的晶化过程及物相结构,用FTIR和Raman光谱表征了其谱学特性.     

新型CdS/TiO2纳米复合材料的制备及其可见光催化性能研究

采用浸渍法和水热法相结合制备了新型的CdS/TiO₂纳米复合材料,并采用X射线衍射(XRD)、透射电子显微镜(TEM)、UV-Vis吸收光谱(UV-VIS)、电子自旋共振谱(ESR)等对样品进行了表征,XRD、TEM表明所制备的新型CdS/TiO₂粒径小、分散均匀,TiO₂以锐钛矿型存在,CdS以高分散的立方相和六方相存在,对比直接法制备的CdS/TiO₂,新型的CdS/TiO₂对活性艳红X-3B具有明显提高的可见光催化活性;大量的束缚单电子氧空位及电子之间强相互作用是新型CdS/TiO₂可见光催化活性提高的主要原因.     

TiO2表面氧空位对Rup2P/TiO2/ITO薄膜电极光致电荷转移的影响

采用改性的TiCl4水解法制备出三种不同表面性质的TiO2-X(X=5,10,20,X表示加入NaOH的浓度,单位为mo·lL-1)样品.利用(1,10-邻菲咯啉)2-2-(2-吡啶基)苯咪唑钌混配配合物(Rup2P)作为敏化剂,制备出Rup2P/TiO2-5/ITO(铟锡金属氧化物)、Rup2P/TiO2-10/ITO和Rup2P/TiO2-20/ITO表面敏化薄膜电极.测试结果表明三种薄膜电极的光电转换效率Rup2P/TiO2-10/ITO最高,Rup2P/TiO2-20/ITO次之,Rup2P/TiO2-5/ITO最低.利用吸收光谱、表面光电压(SP)谱、荧光光谱和表面光电流作用谱等分析了Rup2P和三种TiO2的能带结构和表面性质;利用光致循环伏安和表面光电流作用谱研究了三种Rup2P/TiO2-X/ITO薄膜电极的光致界面电荷转移过程.结果表明,在光致界面电荷转移过程中,TiO2层表面氧空位对Rup2P/TiO2-X/ITO薄膜电极光致电荷转移产生重要影响.并进一步讨论了Rup2P/TiO2-X/ITO薄膜电极的光电流产生机理.