Visualization of structural rearrangements responsible for temperature-induced shrinkage of amorphous polycarbonate after its deformation at different conditions

Structural rearrangements during the temperature-induced shrinkage of amorphous polycarbonate after its tensile drawing below and above the glass transition temperature, rolling at room temperature, and solvent crazing have been studied with the use of the direct microscopic procedure. This evidence demonstrates that the character of structural rearrangements during the temperature-induced shrinkage of the oriented amorphous polymer is primarily controlled by the temperature and mode of deformation. In the case of the polymer sample stretched above the glass transition temperature, the subsequent temperature-induced shrinkage is shown to be homogeneous and proceeds via the simultaneous diffusion of polymer chains within the whole volume of the polymer sample. When polymer deformation is carried out at temperatures below the glass transition temperature, the subsequent temperature-induced shrinkage within the volume of the polymer sample is inhomogeneous and proceeds via the movement of rather large polymer blocks that are separated by the regions of inelastically deformed polymer (shear bands or crazes).     

NMR study of the tie-chain length distribution in oriented polymers

Wide-line NMR has been used in an investigation of noncrystalline (amorphous) regions in oriented semicrystalline polymers. Nylon 6 was chosen as a model material. The tie-chain length distribution function, the fraction of tie chains in the total number of chains in the crystallite cross section, and the relative number of taut tie chains have been determined. The data on the tie-chain length distribution are used in discussing specific features of vitrification of the amorphous regions in oriented polymers and in prediction macroscopic mechanical properties.     

The amount of immobilized polymer in PMMA SiO2 nanocomposites determined from calorimetric data

For semicrystalline polymers there is an ongoing debate at what temperature the immobilized or rigid amorphous fraction (RAF) devitrifies (relaxes). The question if the polymer crystals are melting first and simultaneously the RAF devitrifies or the RAF devitrifies first and later on the crystals melt cannot be answered easily on the example of semicrystalline polymers. This is because the crystals, which are the reason for the immobilization of the polymer, often disappear (melt) in the same temperature range as the RAF. For polymer nanocomposites the situation is simpler. Silica nanoparticles do not melt or undergo other phase transitions altering the polymer-nanoparticle interaction in the temperature range where the polymer is thermally stable (does not degrade). The existence of an immobilized fraction in PMMA SiO₂ nanocomposites was shown on the basis of heat capacity measurements at the glass transition of the polymer. The results were verified by enthalpy relaxation experiments below the glass transition. The immobilized layer is about 2 nm thick at low filler content if agglomeration is not dominant. The thickness of the layer is similar to that found in semicrystalline polymers and independent from the shape of the nanoparticles. Nanocomposites therefore offer a unique opportunity to study the devitrification of the immobilized fraction (RAF) without interference of melting of crystals as in semicrystalline polymers. It was found that the interaction between the SiO₂ nanoparticles and the PMMA is so strong that no devitrification occurs before degradation of the polymer. No gradual increase of heat capacity or a broadening of the glass transition was found. The cooperatively rearranging regions (CRR) are either immobilized or mobile. No intermediate states are found. The results obtained for the polymer nanocomposites support the view that the reason for the restricted mobility must disappear before the RAF can devitrify. For semicrystalline polymers this means that rigid crystals must melt before the RAF can relax.     

Effect of nanoscale diamondoids on the thermomechanical and morphological behaviors of polypropylene and polycarbonate

Nanoscale MolecularDiamond products (various diamondoid materials), obtained from petrochemical feedstocks, have been investigated as additives for polypropylene and polycarbonate. Three of the homologues of this family (diamantane, triamantane, and the [121]tetramantane isomer) have marginal effects on the thermal and mechanical properties of nonpolar/semicrystalline polypropylene. Mixtures of methylated tetramantane nanofillers also increase the stress–strain behavior of polypropylene composites without significantly impacting their glass transition temperatures. The addition of the selected diamondoids to amorphous/moderately polar polycarbonate increases the polymer tensile modulus significantly with marginal increases in the yield stress. The effects of the selected diamondoids on the thermal stability, crystallinity, and optical properties of polypropylene and polycarbonate are also reported. The results for the mechanical properties show that the selected diamondoids behave as plasticizers in polypropylene, whereas in polycarbonate, they act as antiplasticizers without adversely affecting the optical clarity. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1077–1089, 2007     

Oriented noncrystalline structure in PET fibers prepared with threadline modification process

The development of an oriented noncrystalline phase in a semicrystalline polymer filament has been studied via X-ray scattering. These unique PET fibers contain a relatively high noncrystalline content and also have high tenacity, high modulus, and low breaking elongation. Fiber properties were found to be very responsive to the oriented amorphous phase content. This phase was utilized for interpreting noncrystalline orientation in PET fibers produced by a new extrusion technique. Here, the oriented noncrystalline regions in a series of PET fibers varies from 6% to 63%, depending strongly on the production conditions. In particular, samples produced with a newly developed threadline modification process possess a high content of oriented noncrystalline polymer. Measurements such as dynamic and static mechanical properties have been performed on various samples, and these properties are related to the oriented noncrystalline phase. The results provide direct evidence for the existence of highly oriented noncrystalline material in these unique PET fibers spun with a threadline modification process. © 1996 John Wiley & Sons, Inc.     

半晶聚对苯二甲酸乙二酯中的受限非晶相

当半晶聚对苯二甲酸乙二酯 (PET)的结晶度 (Xwc)处于一定范围内时 ,其物理老化后在差示扫描量热(DSC)曲线上的玻璃化转变区有吸热双峰出现 .通过对此吸热双峰分别与完全非晶试样和具有相当高Xwc 的半晶试样物理老化后在DSC曲线上出现的吸热单峰的比较 ,表明半晶PET中存在两种性质极为不同的非晶区 ,即自由非晶区和受限非晶区 .动态力学热分析 (DMTA)曲线上显示的损耗正切 (tanδ)双峰进一步证实了这两种不同非晶区的存在 .这两种不同非晶区的产生是由于试样中晶粒对非晶相中高分子链段活动性的不同限制作用所致 .研究发现 ,对于由冷结晶得到的半晶试样来说 ,出现两种不同非晶区所需的Xwc 上下限都随结晶温度 (Tc)的升高而增高 .还发现 ,在物理老化过程中 ,虽然非晶相的总量基本保持不变 ,但部分自由非晶区却逐渐转变为受限非晶区 .上述实验结果很好地符合Struik的“扩展玻璃化转变”模型 .     

Increased glass transition temperature in motionally constrained semicrystalline polymers

A large number of experimental results in the literature support and illuminate a model of behavior of chains and chain segments in the amorphous phase of semicrystalline polymers connecting the elevation of the glass transition temperature (T_g) above its normal value to several kinds of motional restrictions imposed on the chains and parts thereof. Accordingly, polymer chain, chain-segment and chain-fragment motions of all kinds comprise one or more torsions around main-chain bonds from one stable conformation to another, known as rotational isomerizations. When impediments are placed in front of thermal fluctuations and larger transversal and longitudinal motions of polymer chains, segments and shorter fragments in the amorphous phase, and the motions are thus restricted, the glass transition temperature is elevated relative to that of the same amorphous phase in the bulk under normal conditions. The obstructions may prevent either the onset of rotational isomerizations or of their completion once started. The completion of the torsional isomerizations and larger motions may be prevented by eliminating the free spaces necessary to accommodate the volumes of the interconverting chain fragments and segments even when they move in concert, or by preventing the creation of such free spaces. Another way to hinder the completion of such motions is by the introduction into the system of many rigid walls and other interfaces with strong attractive interactions with the polymer, that by geometrical constraints and attractive interactions suppress the rotational and larger motions and prevent their completion. Elimination of the necessary free volume is achievable by the application of compressive pressure, while the introduction of rigid attractive walls may be accomplished by the incorporation of crystallites, as in semicrystalline polymers, or by the addition of rigid finely comminuted foreign additives with very large surface areas or confining voids with high tortuosity. It is believed that motional restrictions imposed on the amorphous phase by the growth faces of polymer crystallites, especially in oriented semicrystalline polymers, are more effective than the restrictions imposed by the fold surfaces of these crystallites. The prevention of the onset of rotational isomerizations and larger motions may be achieved by stretching the polymer chains and chain segments in the amorphous phase and, by one means or another, pinning down the taut chains such that essentially all their rotational isomers are in the trans conformation: they cannot interconvert to the gauche conformation since it requires the chain’s end-to-end distance to decrease. Parallel alignment of relatively taut chain-segments may impose additional geometrical restrictions on both the onset and completion of rotational isomeric torsions and, of course, on longer-range motions. In all cases, the T_g of the motionally constrained parts of the amorphous phase, especially in semicrystalline polymers, is expected to rise. It is likely that the characteristic length associated with transversal motions and their suppression is R_c, the spatial distance between entanglements, which is of the same size scale, and may be the same as the tube diameter of the reptation model. Special emphasis was placed in this work on the semicrystalline polymers poly (ϵ-caprolactam) (nylon-6) and poly (ethylene terephthalate) (PET). © 1998 John Wiley & Sons, Ltd.     

How did we find the rigid amorphous phase?

The first experimental evidence of the existence of the rigid amorphous phase was reported by Menczel and Wunderlich [1]: when trying to clarify the glass transition characteristics of the first main chain liquid crystalline polymers [poly(ethylene terephthalate-co-p-oxybenzoate) with 60 and 80 mol% ethylene terephthalate units] [2], the absence of the hysteresis peak at the lower temperature glass transition became evident when the sample of this copolymer was heated much faster than it had previously been cooled. Since this glass transition involved the ethylene terephthalate-rich segments of the copolymer, we searched for the source of the absence of the hysteresis peak in PET. There, the gradual disappearance of the hysteresis peak with increasing crystallinity was confirmed [1]. At the same time it was noted that the higher crystallinity samples showed a much smaller ΔC _p than could be expected on the basis of the crystallinity calculated from the heat of fusion (provided that the crystallinity concept works). Later it was confirmed that the hysteresis peak is also missing at the glass transition of nematic glasses of polymers. When checking other semicrystalline polymers, the sum of the amorphous content calculated from the ΔC _p at the glass transition, and the crystallinity calculated from the heat of fusion was far from 100% for a number of semicrystalline polymers. For most of these polymers, the sum of the amorphous content and the crystalline fraction was 0.7, meaning that ca. 30% rigid amorphous fraction was present in these samples after a cooling at 0.5 K min⁻¹ rate. Thus, the presence of the rigid amorphous phase was confirmed in five semicrystalline polymers: PET, Nylon 6, PVF, Nylon 66 and polycaprolactone [1]. Somewhat later poly(butylene terephthalate) and bisphenol-A polycarbonate [3] were added to this list.     

Dielectric relaxation of poly(phenylene sulfide) containing a fraction of rigid amorphous phase

The dielectric relaxation behavior of poly(phenylene sulfide), PPS, has been investigated from room temperature to 180°C. This study was undertaken to examine the mobility of the amorphous phase through the glass transition region, to determine the contribution that rigid amorphous phase material makes to the relaxation process. Semicrystalline samples contain a fraction of the rigid amorphous phase, which was determined from the heat capacity increment at the glass transition, using degree of crystallinity determined from x-ray scattering. In the dielectric experiment, we measured the temperature and frequency dependence of the real and imaginary parts of the dielectric function. ε″ vs. ε′ was used to determine the dielectric relaxation intensity, δε = ε_s–ε∞, at temperatures above the glass transition. For amorphous PPS, δε decreases as temperature increases, while for all semicrystalline PPS, δε increases with temperature. The ratio of semicrystalline intensity to amorphous intensity determines the total fraction of dipoles which are already relaxed at a given temperature. Results indicate that more and more rigid amorphous phase material relaxes as the temperature is increased. This provides the first evidence that rigid amorphous phase material in PPS contains chains that possess different levels of molecular mobility. Finally, to the temperature of the loss peak maximum, at a given frequency, we assign the value of the dielectric T_g. For both melt and cold crystallization, the dielectric T_g systematically decreases as the crystallization temperature increases, and as the fraction of rigid amorphous phase decreases.     

Thermally stimulated current and DSC studies of the broadened glass transition in liquid crystalline polymers

The high sensitivity of the thermally stimulated current, thermal sampling (TS) method is emphasized in a study of the breadth of the glass transition in several liquid-crystalline polymers (LCPs). Differential scanning calorimetry (DSC) was performed on all samples to further quantify the glass transition regions. For “random” copolyester LCPs with widely varying degrees of crystallinity, including highly amorphous samples, very broad glass tran-sition regions were observed. One semicrystalline alternating copolyester and a series of semicrystalline azomethine LCPs were studied as examples of structurally regular polymers. These exhibited relatively sharp glass transitions more comparable to ordinary isotropic amorphous or semicrystalline polymers. The broad glass transitions in the random copolyesters are attributed to structural heterogeneity of the chains. In one example of a moderate-crystallinity random copolyester LCP (Vectra), glass transitions ranging up to ca. 150°C in breadth were determined by the thermal sampling (TS) method and DSC. In other lower crystallinity copolyester LCPs, the main glass transition temperature as determined by DSC was comparable to that determined by TSC although cooperative relaxations of a minor fraction of the overall relaxing species were detected well below the main T_g, by the TS method and not by DSC. Rapid quenches from the isotropic melt to an isotropic glass were possible with one LCP. The anisotropic and isotropic glassy states for this LCP were found to have the same breadth of the glass transition as was determined by the TS method, although TSC and DSC show that T_g is shifted downward by ca. 15°C in the anisotropic glass as compared to the isotropic glass. © 1993 John Wiley & Sons, Inc.     

Biodegradable poly(alkylene succinate) blends: Thermal behavior and miscibility study

New binary blends composed of poly(ethylene succinate) and poly(propylene succinate) or poly(ethylene succinate) and poly(butylene succinate) were prepared. Both PESu/PPSu and PESu/PBSu systems belong to semicrystalline/semicrystalline pairs. The miscibility and crystallization behavior was investigated using differential scanning calorimetry (DSC), wide angle X‐ray diffraction (WAXD), and polarizing light microscopy (PLM). Blends of PESu and PPSu exhibited a single composition dependent glass transition temperature over the entire range of composition, indicating that the system is miscible. The melting point depression of the high melting temperature component, PESu, was analyzed according to the Nishi‐Wang equation. A negative polymer–polymer interaction parameter was obtained, indicating that the blends are thermodynamically miscible in the melt. The two components crystallized sequentially when the blends were cooled rapidly to a low temperature. DSC traces of PESu/PBSu blends after quenching showed two distinct composition dependent glass transition temperatures between those of the neat polymers, showing that the polymers are partially miscible. The amorphous PESu/PBSu blends in the intermediate compositions showed three cold‐crystallization peaks, indicating the influence of mixing. The crystallization rates of PBSu were reduced and those of PESu were increased. WAXD showed reduced crystallinity and peak broadening in the patterns of the blends of intermediate compositions, while no spherulites could be detected by PLM. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 584–597, 2006     

Blends of polycarbonate and acrylic polymers: Crystallization of polycarbonate

The microstructure of amorphous polymer blends has been extensively studied in the past, but now there is a growing interest for polymer blends where one or more of the components can crystallize. In this study we investigate such blends, namely miscible polycarbonate (PC)/acrylic blends. Using small angle X-ray scattering (SAXS) measurements, combined with atomic force microscopy (AFM), electron microscopy (SEM), and optical microscopy, we demonstrate that the amorphous acrylic component mostly segregates inside the spherulites between the lamellar bundles (interfibrillar segregation). Varying the PC molecular weight or the mobility of the amorphous component (by changing its molecular weight and T_g) does not change the mode of segregation. So far qualitative predictions of the mode of segregation in semicrystalline polymer blends have been proposed using the δ parameter (the ratio between the diffusion coefficient D of the amorphous component in the blend and the linear crystallization rate G), introduced by Keith and Padden. Our results suggest that other parameters have to be considered to fully understand the segregation process. © 1998 John Wiley & Sons, Inc. J. Polym. Sci. B Polym. Phys. 36: 2197–2210, 1998     

Reorganization of the structures,morphologies, and conformations of bulk polymers via coalescence from polymer–cyclodextrin inclusion compounds

Bulk poly(ethylene terephthalate) (PET) and bisphenol A polycarbonate (PC) samples have been produced by the coalescence of their segregated, extended chains from the narrow channels of the crystalline inclusion compounds (ICs) formed between the γ‐cyclodextrin (CD) host and PET and PC guests, which are reported for the first time. Differential scanning calorimetry, Fourier transform infrared, and X‐ray observations of PET and PC samples coalesced from their crystalline γ‐CD‐ICs suggest structures and morphologies that are different from those of samples obtained by ordinary solution and melt processing techniques. For example, as‐received PC is generally amorphous with a glass‐transition temperature (T_g) of about 150 °C; when cast from tetrahydrofuran solutions, PC is semicrystalline with a melting temperature (T_m) of about 230 °C; and after PC/γ‐CD‐IC is washed with hot water for the removal of the host γ‐CD and for the coalescence of the guest PC chains, it is semicrystalline but has an elevated T_m value of about 245 °C. PC crystals formed upon the coalescence of highly extended and segregated PC chains from the narrow channels in the γ‐CD host lattice are possibly more chain‐extended and certainly more stable than chain‐folded PC crystals grown from solution. Melting the PC crystals formed by coalescence from PC/γ‐CD‐IC produces a normal amorphous PC melt that, upon cooling, results in typical glassy PC. PET coalesced from its γ‐CD‐IC crystals, although also semicrystalline, displays a T_m value only marginally elevated from that of typical bulk or solution‐crystallized PET samples. However, after the melting of γ‐CD‐IC‐coalesced PET crystals, it is difficult to quench the resultant PET melt into the usual amorphous PET glass, characterized by a T_g value of about 80 °C. Instead, the coalesced PET melt rapidly recrystallizes during the attempted quench, and so upon reheating, it displays neither a T_g nor a crystallization exotherm but simply remelts at the as‐coalesced T_m. This behavior is unaffected by the coalesced PET sample being held above T_m for 2 h, indicating that the extended, unentangled nature of the chains in the noncrystalline regions of the coalesced PET are not easily converted into the completely disordered, randomly coiled, entangled melt. Apparently, the highly extended, unentangled characters of the PC and PET chains in their γ‐CD‐ICs are at least partially retained after they are coalesced. Initial differential scanning calorimetry, thermogravimetric analysis, Fourier transform infrared, and X‐ray observations are described here. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 992–1012, 2002     

Characterization,processing, and properties of an aromatic poly (ether ketone)

Poly(oxy-1,3-phenylenecarbonyl-1,4-phenylene), mPEK, was synthesized in a methane sulfonic acid/phosphorus pentoxide medium through the polycondensation of 3-phenoxybenzoic acid. The polymer was soluble at room temperature in strong acids and common organic solvents. Differential scanning calorimetry on mPEK indicated a glass transition temperature of 132°C and no detectable crystal melting behavior. The polymer was thermo-oxidatively stable up to 420°C in air as determined by thermogravimetric analysis. Thermal degradation resulted in a crosslinked polymer. Compression molding was successfully applied to consolidate mPEK powder into bulk specimens without causing degradation. Tensilefractured surfaces of the consolidated specimens were examined by scanning electron microscopy which strongly indicated adequate fusion of mPEK powder but also disclosed microvoids of uniform size, shape, and distribution. X-ray scattering revealed that mPEK powder was amorphous and that the consolidated mPEK specimens were structurally isotropic as well as amorphous. The bulk specimen density was determined to be 1.29 ± 0.01 g/cm³ and the three-dimensionally isotropic bulk tensile properties were shown to be 4.10 ± 0.10 GPa (modulus), 0.07 ± 0.01 GPa (strength), and 0.021 ± 0.006 (elongation at break). Tensile properties of the amorphous mPEK specimens compared favourably with literature values of state-of-the-art semicrystalline thermoplastics. Crystaline phases could be realized for mPEK by melt-processing, or precipitating from a solvent.     

The influence of draw-induced structural changes on the activity of a semicrystalline polymer-supported catalyst

The activity of a solid, polymer-supported catalyst (a semicrystalline polyethylene film containing grafted, sulfonated styrene) was shown to be altered by cold drawing. The catalytic activity was measured by a test reaction, the dehydration of isopropyl alcohol to give propylene. Catalytic reaction rates were measured with variously drawn films clamped in a differential flow reactor operated at 100°C and 1 atm. The catalytic activity increased with the elongation of the polymer up to a draw ratio of 2.5; the activity decreased upon further drawing. The drawn films were characterized by x-ray diffraction, dynamic mechanical measurements, electron microscopy, birefringence, and density measurements. Since no evidence was found for the formation of surface sites by creation of microcracks, the changes in activity are attributed to modifications in the polymer structure induced by drawing. The kinetics of the catalytic reaction and the data giving percentage crystallinity and crystalline and amorphous orientation factors suggest that, in the undrawn polymer, the catalytically active ? SO₃H groups form a hydrogen-bonded network, which is excluded from the crystalline regions. Initial elongation partially breaks up the network, allowing more ? SO₃H groups to bond to alcohol and become catalytically engaged. Elongation beyond a draw ratio of 2.5 leads to a separation of ? SO₃H groups greater than that required for the formation of the reaction intermediate, which involves the alcohol hydrogen bonded to several ? SO₃H groups. The combined results of the catalytic kinetics experiments and structural characterizations imply that the preliminary deformation response of the semicrystalline polymer occurs predominantly within the noncrystalline regions and is accommodated by the rigid slip and tilting of crystal lamellae. The hydrogen bonding among the ? SO₃H groups in the noncrystalline regions hinders lamellar breakup and suppresses the formation of highly aligned fibrillar morphologies.     

Temperature modulated calorimetry and dielectric spectroscopy in the glass transition region of polymers

The results from temperature modulated DSC in the glass transition region of amorphous and semicrystalline polymers are described with the linear response approach. The real and the imaginary part of the complex heat capacity are discussed. The findings are compared with those of dielectric spectroscopy. The frequency dependent glass transition temperature can be fitted with a VFT-equation. The transition frequencies are decreased by 0.5 to 1 orders of magnitude compared to dielectric measurements. Cooling rates from standard DSC are transformed into frequencies. The glass transition temperatures are also approximated by the VFT-fit from the temperature modulated measurements. The differences in the shape of the curves from amorphous and semicrystalline samples are discussed.Dedicated to Professor Bernhard Wunderlich on the occasion of his 65th birthday     

Dielectric signature of a dead layer in ultrathin films of a nonpolar polymer

Extremely thin films of poly(styrene) (h相似文献   

Anomalous enhanced mobility in a semicrystalline random poly(butylene isophthalate/butylene adipate) copolyester.

An anomalous enhancement of the segmental dynamics upon crystallization is observed by analyzing the dielectric relaxation of a random copolymer formed by stiff aromatic and flexible aliphatic co-monomeric units. The corresponding aliphatic homopolymer is characterized by a low glass transition temperature. The results show that the characteristic self-confinement inherent to semicrystalline polymer systems, which significantly slows down the segmental dynamics as compared to that of pure amorphous ones, is not only avoided but pushed in the opposite direction. Although the effect formally resembles that observed in liquids confined within non-interacting environments, X-ray measurements have shown that the origin in the present case must be sought in an enrichment of the amorphous phase with the most flexible co-monomer upon crystallization.     

The competition between crystallization and demixing in polymer blends. IV. Detection of composition inhomogeneities around growing spherulites

In polymer blends of an amorphous and a semicrystalline component, the crystallization kinetics and the resulting morphology are heavily determined by the diffusion ability of the whole chains and by the dwelling site of the amorphous polymer. Depending on the relative rates of spherulite growth and chain diffusion, radial composition profiles around the growing spherulites and a gradual increase of the melt bulk composition can develop. The resulting change in composition, particularly at the crystallization front, causes a corresponding temporal variation of the spherulite growth rate. In the present article, two experimental techniques are introduced to prove the existence and to determine the course of these concentration profiles. They are based on the composition dependences of the spherulite growth rate and the number density of primary nuclei. Their efficiency is demonstrated by measurements on PVDF/PEA blends. The blend composition at the crystal growth front was found to change by absolute 25%, and the width of the profile can amount to up to 70 μm. © 1996 John Wiley & Sons, Inc.