Sputtered deposited nanocrystalline ZnO films: A correlation between electrical, optical and microstructural properties

Zinc oxide thin films were prepared by dc (direct current) and rf (radio frequency) magnetron sputtering on glass substrates. ZnO films produced by dc sputtering have a high resistance, while the films produced using rf sputtering are significantly more conductive. While the conductive films have a compact nodular surface morphology, the resistive films have a relatively porous surface with columnar structures in cross section. Compared to the dc sputtered films, rf sputtered films have a microstructure with smaller d spacing, lower internal stress, higher band gap energy and higher density. Dependence of conductivity on the deposition technique and the resulting d spacing , stress, density, band gap, film thickness and Al doping are discussed. Correlations between the electrical conductivity, microstructural parameters and optical properties of the films have been made. PACS 73.25.+i; 81.15.cd; 81.05.ys     

Simulation of the HAZ and magnetic properties of laser cut non-oriented electrical steels

An attempt has been made to simulate the heat-affected zone observed in laser cut samples in order to investigate the influence of laser cutting on the magnetic properties of electrical steels. The thermal cycles, after experimental calibration, are calculated from the Rosenthal modeling. The cycles have been reproduced in massive samples in order to characterize both the microstructure and the magnetic properties of high- and low-alloyed silicon steels. Results show the harmful effect of the bainite and the thermal stresses on the magnetic properties.     

Effect of the rapid heating on the magnetic properties of non-oriented electrical steels

Measurements of the bulk magnetic properties for two non-oriented electrical steels after a rapid heating are reported. A deterioration of the magnetic properties was observed for the fully processed non-oriented grade and an improvement for the semi-processed non-oriented grade. This publication emphasizes the effects due to the competition between the increase of the grain size and the appearance of thermal stresses during the rapid heating on the magnetic properties of the steels.     

Effect of deformation and annealing on the microstructure and magnetic properties of grain-oriented electrical steels

The effect of plastic deformation and subsequent annealing on the magnetic properties and microstructure of a grain-oriented (GO) electrical steel has been studied. True strain (ε) from 0.002 to 0.23 was applied by rolling in two directions, rolling (RD) and transverse (TD). The deterioration of power losses varies according to the direction of deformation. Annealing the strained material—at 800 °C/2 h—leads to a recrystallization and restored magnetic properties. The main components of annealed-textures are around 15–35° from those of deformed-textures for both RD and TD. Rolling along {1 1 0} 〈0 0 1〉 direction leads to the development of deformation twins.     

Preisach modelling of nonlinear response in electrically biased lead zirconate titanate-based piezoceramics

The alteration of the high-field electrical permittivity (nonlinear response) of PZT-based ceramics when an electrical bias field is applied is reported in this work. Large differences are observed between soft and hard PZT behaviours. While in soft PZT a bias field does not modify the nonlinear behaviour, a notable dependence is verified in hard PZT. The Preisach model is satisfactorily used to describe experimental results. A distribution function containing the first terms of the Maclaurin development series of a function composed by two Gaussian-like functions of different amplitudes is proposed. The model gives a satisfactory explanation for the fact that the permittivity depends not only on the amplitude of the applied electric field, but also on the bias field, both for soft and hard ceramics and for poled or unpoled samples.     

Microstructure,texture and magnetic properties of strip-cast 1.3% Si non-oriented electrical steels

In this work, the evolution of microstructure, texture and magnetic properties of non-oriented 1.3% silicon steel processed using the twin-roll strip casting was investigated, especially under different solidification structures. A number of microstructures about the as-cast strips show that the initial solidification structure of casting a strip can be controlled by the melt superheats. The microstructures with the average grain size of ∼100–400 μm can be obtained in strips when the melt superheats are from 20 to 60 °C. A nearly random, diffuse, homogeneous texture under a low melt superheat, but comparatively developed {100} oriented grains are formed under a high melt superheat through the cast strip thickness. The relatively low core loss and high magnetic induction can be obtained in the cold rolled and annealed sheets when increasing the initial grain size of cast-strip. The textures in annealed sheets with coarse initial grain size are characterized by the relatively strong Goss component and {001} fiber but weak γ-fiber component, which lead to the high permeability.     

Helium effects on the microstructural evolution of reactor irradiated ferritic and austenitic steels

Abstract

Microstructural evolution in neutron irradiated austenitic stainless steels and Cr-Mo ferritic steels is reviewed. Important highlights are: (1) there is a strong correlation between precipitation and void evolution in austenitic steels; (2) helium affects precipitate evolution in austenitic steels, but observations indicate no effect on precipitation in ferritic steels; (3) helium has a pronounced effect on the cavity evolution of the two steel types. Helium effects are explained in terms of the interrelationship between microstructural evolution and point-defect annihilation processes. In stainless steel, three relative regimes of microstructural behavior for different helium generation rate-displacement rate ratios are recognized: (1) “low” He/dpa ratio, where helium effects on the radiation-induced microstructural evolution are negligible or develop slowly, (2) “medium” He/dpa ratio, where helium effects strongly enhance the microstructural changes, and (3) “high” He/dpa ratio, where helium effects are limited to the early development of a high density of fine bubbles which interfere with other radiation-induced microstructural changes, but allow enhanced thermal microstructural evolution to take place instead. The extensive data on austenitic steels fall within these regimes. Ferritic steels are known to be highly resistant to void swelling without helium. It is suggested that enhanced cavity formation due to helium in ferritic steels makes higher swelling a potential concern for fusion reactor applications.     

Effect of initial grain size on texture evolution and magnetic properties in nonoriented electrical steels

The magnetic properties of nonoriented electrical steels are influenced by the grain size and crystallographic texture. The technologies used to control the grain size in nonoriented electrical steels are approaching their limits. However, there is still some room for improvement of the magnetic properties through texture control. Hot-band annealing is known to be one of the most effective processing stages for texture modification. In this study, two types of initial grain sizes prior to cold rolling are obtained by different hot-band annealing. The effect of initial grain size on texture evolution and magnetic properties in nonoriented electrical steels containing 2% Si is examined. The specimens having different initial grain sizes have significantly different textures in the cold-rolled state and the annealed state. During the recrystallization stage, new grains formed in the coarse-grained specimens have stronger Goss but weaker γ-fibre texture than those in the fine-grained specimens. During the grain growth after complete recrystallization, the coarse-grained specimens still have weaker γ-fibre texture than the fine-grained specimens. The magnetic induction of the coarse-grained specimens is always higher at the same temperature than that of the fine-grained specimens. The core loss of the coarse-grained specimens is lower at the same temperature than that of fine-grained specimens. However, the improvement of the core loss becomes less pronounced as the annealing temperature increases.     

Effects of sulfur content and slab reheating temperature on the magnetic properties of fully processed nonoriented electrical steels

The effects of sulfur content and slab reheating temperature on the magnetic properties of four fully processed nonoriented electrical steels have been investigated. Four slabs of nonoriented electrical steels with sulfur content in the range of 0.0006–0.0126 wt% were reheated to 1100, 1200, and 1300 °C, respectively. Then, they were hot rolled and annealed at 700 °C, cold rolled at the same condition and annealed at 820 °C in the salt bath furnace for 1 min to simulate continuous annealing. The ac core loss, dc hysteresis loss, and ac and dc permeability were measured at 15 kG inductions. It was found that the amount of inclusions in the hot-rolled bands increased with increasing slab reheating temperature and increasing sulfur content in steels. After final annealing, grain sizes of cold-rolled steel sheets decreased with increasing sulfur content and increasing slab reheating temperature. The main preferred orientations in the final annealed steel sheets were (0 1 1) 〈1 0 0〉 and (1 1 1) 〈u v w〉 γ fiber texture. Steel sheets containing 0.0032 and 0.0060 wt% sulfur developed a more stronger (0 1 1)〈1 0 0〉 texture than other steel sheets. However, steel sheets containing 0.0126 wt% sulfur had the weakest (1 1 1)〈u v w〉 texture during slab reheating at temperatures higher than 1200 °C. Both ac core loss and dc hysteresis loss increased with increasing slab reheating temperature and increasing sulfur content in steel sheets. Both ac and dc permeability decreased with increasing slab reheating temperature and increasing sulfur content in steel sheets. If sulfur content decreased from 0.0060 to 0.0032 wt%, there were great improvements in ac core loss, dc hysteresis loss, and ac and dc permeability. However, eddy current loss was almost independent of the sulfur content and slab reheating temperature.     

Effects of deposition temperatures and annealing conditions on the microstructural, electrical and optical properties of polycrystalline Al-doped ZnO thin films

Al-doped ZnO (AZO, ZnO:Al₂O₃ = 98:2 wt%) films are deposited on different substrates by an RF magnetron sputtering and subsequently annealed at three different conditions to investigate the microstructural, electrical, and optical properties. X-ray diffraction and scanning electron microscope results show that all the samples are polycrystalline and the samples rapid-thermal-annealed at 900 °C in an N₂ ambient contain larger grains compared to the furnace-annealed samples. It is shown that the sample deposited at room temperature on the sapphire gives a resistivity of 5.57 × 10⁻⁴ Ω cm when furnace-annealed at 500 °C in a mixture of N₂:H₂ (9:1). It is also shown that the Hall mobility vs. carrier concentration (μ-n) relation is divided into two groups, depending on the annealing conditions, namely, either rapid-thermal annealing or furnace annealing. The relations are described in terms of either grain boundary scattering or ionized impurity scattering mechanism. In addition, the samples produce fairly high transmittance of 91-96.99% across the wavelength region of 400-1100 nm. The optical bandgaps of the samples increase with increasing carrier concentration.     

Magnetic and microstructural properties of the Ti-doped Barium hexaferrite

A study of the magnetic and microstructural properties of the M-type Ti⁴⁺-doped Barium hexaferrite according to the stoichiometric formulation BaFe_{(12−(4/3)x)}Ti_xO₁₉ with x=0, 0.6, 0.8 and 1.0, has been reported. The XRD and magnetic analysis show a variation of the host lattice parameters and a decrease in the values of remnant magnetization and magnetic anisotropy with Ti⁴⁺ content. The behavior of magnetic properties of materials is explained by the combined effect of the coherent rotation of the magnetic domains and the replacements of Fe³⁺ by Ti⁴⁺ ions in the octahedral and tetrahedral sites.     

Some chemical and microstructural factors influencing creep cavitation resistance of austenitic stainless steels

Creep cavitation in materials is greatly influenced by trace elements. To enhance creep cavitation resistance, the chemical composition of 304, 321, 347 austenitic stainless steels was modified with the addition of minute amounts of boron and cerium. The addition of boron and cerium to type 304 stainless steel led to an increase in its creep rupture life with an associated decrease in creep rupture ductility. The addition of boron and cerium to the titanium-containing 321 steel and niobium-containing 347 steel was found to increase their creep rupture life and ductility. Creep cavitation was highly suppressed in the 347 and 321 steels with the addition of boron and cerium. The chemistry of the grain boundary and creep cavity surface was analyzed by Auger electron spectroscopy. Extensive sulphur segregation was observed on the grain boundary and cavity surface of the steels without boron and cerium addition and even in the 304 steel containing boron and cerium. In the boron- and cerium-containing 347 and 321 steels, respectively, segregation of elemental boron and the BN compound on the cavity surface were observed. These segregations reduced cavity growth rate substantially in these steels and BN segregation was found to be more effective in reducing cavity growth rate than boron segregation. Cerium acts as a getter for soluble sulphur in the steels by precipitation of ceriumoxysulfide (Ce₂O₂S) to facilitate the segregation of boron on the cavity surface.     

Effect of annealing prior to cold rolling on magnetic and mechanical properties of low carbon non-oriented electrical steels

The effects of annealing prior to cold rolling on the microstructure, magnetic and mechanical properties of low-C grain non-oriented (GNO) electrical steels have been investigated. The grain structure of hot-rolled electrical steel strips is modified by annealing at temperatures between 700 and 1050 °C. Annealing at temperatures less than the ferrite to austenite+ferrite transformation temperature on heating (Ac₁) causes a marginal effect on the grain size. However, annealing in the intercritical region at temperatures between Ac₁ and Ac₃ (the ferrite+austenite to austenite transformation temperature on heating) causes rapid decarburization and development of large columnar ferrite grains free of carbide particles. This microstructure leads, after cold rolling and a fast annealing treatment, to carbide free, large ferrite grain microstructures with magnetic and mechanical properties superior to those observed typically in the same steel in the industrially fully processed condition. These results are attributed to the increment in grain size and to the {1 0 0} fiber texture developed during the final annealing at temperatures up to 850 °C. Annealing at higher temperatures, T>Ac₃, results in a strong {1 1 1} fiber texture and an increase of the quantity of second phase particles present in the microstructure, which lead to a negative effect on the final properties. The results suggest that annealing prior to cold rolling offers an attractive alternative processing route for the manufacture of fully processed low C GNO electrical steels strips.     

Effect of substrate temperature and annealing temperature on the structural, electrical and microstructural properties of thin Pt films by rf magnetron sputtering

Influence of both substrate temperature, T_s, and annealing temperature, T_a, on the structural, electrical and microstructural properties of sputtered deposited Pt thin films have been investigated. X-ray diffraction results show that as deposited Pt films (T_s = 300, 400 °C) are preferentially oriented along (1 1 1) direction. A little growth both along (2 0 0) and (3 1 1) directions are also noticed in the as deposited Pt films. After annealing in air (T_a = 500-700 °C), films become strongly oriented along (1 1 1) plane. With annealing temperature, average crystallite size, D, of the Pt films increases and micro-strain, e, and lattice constant, a₀, decreases. Residual strain observed in the as deposited Pt films is found to be compressive in nature while that in the annealed films is tensile. This change in the strain from compressive to tensile upon annealing is explained in the light of mismatch between the thermal expansion coefficients of the film material and substrate. Room temperature resistivity of Pt films is dependant on both the T_s and T_a of the films. Observed decrease in the film resistivity with T_a is discussed in terms of annihilation of film defects and grain-boundary. Scanning electron microscopic study reveals that as the annealing temperature increases film densification improves. But at an annealing temperature of ∼600 °C, pinholes appear on the film surface and the size of pinhole increases with further increase in the annealing temperature. From X-ray photoelectron spectroscopic analysis, existence of a thin layer of chemisorbed atomic oxygen is detected on the surfaces of the as deposited Pt films. Upon annealing, coverage of this surface oxygen increases.