The microstructure and magnetic properties of electrodeposited Co–Pt thin films on Ru buffer layer

For high-density magnetic recording media, this study examined the crystal structure and the texture of electrodeposited cobalt–platinum (Co–Pt) films on Ru buffer layer. A 15-nm-thick Co–Pt film exhibited very high out-of-plane coercivity and squareness, which were 6248 Oe and 0.89, respectively. The coercivity, H_c, of Co–Pt films grown on Ru buffer layer decreased significantly with increasing thickness, possibly due to the lattice misfit of 5.4% between Co–Pt and Ru, leading to the decrease of perpendicular magnetic anisotropy (PMA) of Co–Pt films as indicated by the observed hexagonal-closed-packed (HCP) (1 1¯ 0 1) plane of Co–Pt films. According to nano beam diffraction pattern (NBDP), however, Co–Pt film grown on Ru layer of HCP exhibited mixed HCP and FCC phases. Also, cross-sectional TEM image suggests that the high PMA may result from the columnar structure of physically isolated Co–Pt grains with the c-axis perpendicular to the film plane.     

Microstructures and soft magnetic properties of as-deposited Fe–Sm–O thin films

The influences of O₂ partial pressure on saturation magnetization, coercivity and effective permeability of the as-deposited Fe–Sm–O thin films, which were fabricated by RF magnetron reactive sputtering method, were investigated. The nanocrystalline Fe_83.4Sm_3.4O_13.2 thin film fabricated at O₂ partial pressure of 5% exhibited the best magnetic softness with a saturation magnetization of 1.43 MA/m, coercivity of 65.2 A/m and effective permeability of about 2600 in the frequency range from 0.5 to 100 MHz. The electrical resistivity of Fe_83.4Sm_3.4O_13.2 was 130 μΩ cm. The microstructures and electrical resistivity were investigated in this work.     

The high frequency magnetic properties of self assembled Fe–Co–Si–N nanogranular thin films

The effect of a variation in Si and N concentration on the microstructure, crystal structure and high-frequency magnetic properties of Fe–Co–Si–N nanogranular thin films was investigated. The films, prepared by rf magnetron sputtering, consisted of nanosized grains of FeCo as well as a Si and N rich intergranular amorphous phase. The Si concentration had a significant effect on the crystal structure of the FeCo phase. The resistivities of the Fe–Co–Si–N films were significantly enhanced by an increase in Si concentration. The resonant frequency of the Fe–Co–Si–N films could be tuned from 0.45 GHz to 2.1 GHz by controlling Si concentration. The N concentration greatly influenced magnetic properties and the variation in resonant frequency is in agreement with Kittel’s equation.     

Role of electrolyte pH on structural and magnetic properties of Co–Fe films

Co–Fe films were electrodeposited on polycrystalline Titanium substrates from the electrolytes with different pH levels. X-ray diffraction (XRD) was used to study the crystal structure of the films. The XRD patterns showed that the films grown at the pH levels of 3.70 and 3.30 have a mixed phase consisting of face-centred cubic (fcc) and body-centred cubic, while those grown at pH=2.90 have only fcc structure. It was observed that the film composition, by energy dispersive x-ray spectroscopy, contain around 88 at% Co and 12 at% Fe for all films investigated in this study. Morphological observations indicated that all films have grainy structure with the slight change of grain size depending on the electrolyte pH. Magnetoresistance measurements, made at room temperature, showed that all films exhibited anisotropic magnetoresistance, which is affected by the electrolyte pH. From the magnetic measurements made by vibrating sample magnetometer, the saturation magnetization increases as the electrolyte pH decreases. Furthermore, all films have in-plane easy-axis direction of magnetization.     

Synthesis and magnetic properties of Co–Zn magnetic fluid

Co_1−xZn_xFe₂O₄ (with x varying from 0 to 0.7) nanoparticles to be used for ferrofluid preparation were prepared by chemical co-precipitation method. The fine particles were suitably dispersed in transformer oil using oleic acid as the surfactant. The magnetization (M_s) and the size of the particles were measured at room temperature. The magnetization (M_s) was found to decrease with the increase in zinc substitution. The magnetic particle size (D_m) of the fluid was found to vary from 11.19 to 4.25 nm decreasing with the increase in zinc substitution.     

Structure,optical, and magnetic properties of rutile Sn1−xMnxO2 thin films

Sn_1?xMn_xO₂ (x ≤ 0.11) thin films were fabricated by sol–gel and spin-coated method on Si (1 1 1) substrate. X-ray diffraction revealed that single-phase rutile polycrystalline structure was obtained for x up to about 0.078. Evolution of the lattice parameters and X-ray photoelectron spectroscopy studies confirmed the incorporation of Mn³⁺ cations into rutile SnO₂ lattice. Optical transmission studies show that the band gap energy (E_g) broadens with the increasing of Mn content. Magnetic measurements revealed that all samples exhibit room temperature ferromagnetism (RTFM), which is identified as an intrinsic characteristic. Interestingly, the magnetic moment per Mn atom decreases with the increasing Mn content. The origin of RTFM can be interpreted in terms of the bound magnetic polaron model.     

Structure and magnetic properties of Co–Ni–Li ferrites synthesized by citrate precursor method

Nanoparticles of Co_0.5Ni_0.5−2xLi_xFe_2+xO₄ with x ranging from 0.00 to 0.25 in steps of 0.05 were prepared by using citrate precursor method. The microstructure and the magnetic properties of the as-prepared nanosamples and the effect of increasing Li¹⁺ ions on their physical properties were studied. X-ray diffraction (XRD), transmission electron microscopy (TEM), particle size analyzer (PSA), Fourier transform infrared spectroscopy (FTIR) and vibrating sample magnetometer (VSM) were used to investigate the samples. The XRD analysis confirmed the cubic spinel phase formation of the prepared samples, while TEM images and PSA ensure the nanostructural features of them. The FTIR spectra reveal the presence of two prominent absorption bands v₁ and v₂ in the range of 600 and 400 cm⁻¹ which are usually attributed to the tetrahedral and octahedral complexes of the spinel lattice, respectively. The change of v₂ gradually towards lower frequency and the slightly change of v₁ were explained depending on the effect of increasing Li¹⁺ content on the bond length of B-site metal ions and the spin canting of A-site metal ions, respectively. Saturation magnetization and remnant magnetization were found to increase with adding Li¹⁺ ions up to x=0.15 and then to decrease again, while coercivity decreases monotonically by increasing Li¹⁺ ions. The change in magnetic properties by adding Li¹⁺ ions is explained as to be dependent on many factors such as crystallite size, measured density, porosity, expected cation distribution, A–B exchange interactions, and magnetocrystalline anisotropy.     

Electrical and optical properties of a-SexTe100–x thin films

The dc electrical conductivity of as deposited thin films of a-Se_xTe_100?x (x=3, 6, 9 and 12) is measured as a function of temperature range from 298 to 383 K. It is observed that the dc conductivity increases exponentially with the increase in temperature in this glassy system. The value of activation energy calculated from the slope of ln σ_dc vs. 1000/T plot, is found to decrease on incorporation of dopant (Se) content in the Te system. On the basis of pre-exponetial factor (σ₀), it is suggested that the conduction is due to thermally assisted tunneling of the carriers in the localized states near the band edges. The optical absorption measurements show an indirect optical band gap in this system and it decreases on increasing Se concentration. The optical constants (extinction coefficient (k) and refractive index (n)) do change significantly with the photon energy and also with the dopant Se concentration. The decrease in optical band gap may be due to the decrease in activation energy in the present system. It is also found that the real and imaginary parts of dielectric constants show a significant change with the photon energy as well as with the dopant concentration. With large absorption coefficients and compositional dependence of optical band gap and optical constants (n and k), these materials may be suitable for optical disk applications.     

Structural and magnetic properties of nanostructured Mn–Al–C magnetic materials

Pre-alloyed Mn_50+x−yAl_50−xC_y   (x=0$x=0$, 2, 4, 6, 8; y=0$y=0$, 1.7, 3) powders were mechanically milled (MM), and the as-milled powders subsequently annealed at temperatures from 350 to 600 °C to produce the ferromagnetic metastable L1₀-structured τ-phase. Bulk Mn₅₄Al₄₆ specimens were also annealed under the same conditions for comparison. The effects of the Mn concentration and C additions on phase formation, microstructure, magnetic properties, as well as on the magnetization mechanism of the Mn–Al–C alloys were systematically investigated. It was found that the magnetic properties are strongly dependent both on the fraction of the τ-phase and its microstructure. There exists a strong influence of the microstructural refinement, due to the ball milling, on the rate of ε-phase to τ-phase transformation and on the stability of the τ-phase. The kinetics of formation and subsequent decomposition of the magnetic τ-phase were markedly different in the MM and bulk alloys. Both remanence curves and δM plots showed no exchange coupling among the τ-phase nanograins. The mechanism for the magnetization process was determined to be domain wall pinning.     

Structure and properties of DLC–MoS2 thin films synthesized by BTIBD method

Diamond-like carbon (DLC)–MoS₂ composite thin films were synthesized using a biased target ion beam deposition (BTIBD) technique in which MoS₂ was produced by sputtering a MoS₂ target using Ar ion beams while DLC was deposited by ion beam deposition with CH₄ gas as carbon source. The structure and properties of the synthesized films were characterized by X-ray diffraction, X-ray absorption near edge structure (XANES), Raman spectroscopy, nanoindentation, ball-on-disk testing, and corrosion testing. The effect of MoS₂ target bias voltage, ranging from −200 to −800 V, on the structure and properties of the DLC–MoS₂ films was further investigated. The results showed that the hardness decreases from 9.1 GPa to 7 GPa, the Young?s modulus decreases from 100 GPa to 78 GPa, the coefficient of friction (COF) increases from 0.02 to 0.17, and the specific wear rate coefficient (k) increases from 5×10⁻⁷ to 5×10⁻⁶ mm³ N⁻¹ m⁻¹, with increasing the biasing voltage from 200 V to 800 V. Also, the corrosion resistance of the DLC–MoS₂ films decreased with the raise of biasing voltage. Comparing with the pure DLC and pure MoS₂ films, the DLC–MoS₂ films deposited at low biasing voltages showed better tribological properties including lower COF and k in ambient air environment.     

Various properties of sputter-deposited Ta–Ru thin films

This paper discusses several structural, electrical and oxidation characteristics of co-sputtered Ta–Ru alloy films on oxidized Si-substrates. From X-ray examination, the Ta₁Ru₁ phase has formed and dominates in the compositions exceeding 54 at.% Ru content. The resistivity of the Ta–Ru thin films can reach a maximum of ∼320 μΩ cm in the composition range between 35 and 54 at.% Ru. After thermal treatment in air (600°C, 1 h), Ru-rich samples show a less increase in resistivity than Ta-rich ones. The observed preferential oxidation of Ta in the Ta–Ru samples can be further interpreted by thermodynamic calculations. The Ta-rich surface oxide is believed to be responsible for the passivating ability of the Ru atom toward oxidation at high temperatures. This results in the Ru of the metallic state though the oxidation of Ta occurs.     

Optical and magneto-optical properties of Co–SiO<Subscript>x</Subscript> thin films

The optical and magneto-optical properties of hybrid Co–SiO_x systems are studied as a function of Co concentration. The structures were prepared by alternate depositions of SiO_x thin films and layers of 10-nm-diameter Co nanoparticles produced by an Ion Cluster Source. Both optical and magneto-optical constants of the system gradually increase with the amount of Co, though maintaining low optical absorption values in the visible range. The experimental results are well reproduced assuming that the nanoparticles have a cobalt core (7–8 nm in diameter) surrounded by a cobalt oxide shell (1–2 nm thick). The magneto-optical activity versus optical absorption figure of merit of this system is compared with other magneto-optical dielectric systems.     

Nanostructure and thermal-optical properties of vanadium dioxide thin films

A novel nanopolycrystalline structure of vanadium dioxide thin films is deposited on silicon or fused silica substrates by reactive ion sputtering and followed by an annealing. The characteristic analysis shows that the films have a columnar nanostructure with an average grain of 8 nm. The resistivities as a function of ambient temperatures tested by four-point probes for as-deposited films present that the transition temperature for nanostructure of vanadium dioxide films is near 35 ℃ which lowers about 33 ℃ in comparison with the transition temperature at 68 ℃ in its microstructure.     

Structural and magnetic properties of Si1−xGex thin films implanted with Fe ions

A series of Si_1?xGe_x (x = 1, 0.848, 0.591, 0.382, 0.209, 0.064, 0) thin films prepared by ion beam sputtering were implanted with Fe ions to different doses using the metal vapor vacuum arc technique. X-ray absorption fine structure (XAFS) was used to characterize the local microstructure around the Fe atoms in Fe-doped Si_1?xGe_x samples. Structural analysis showed that for annealed samples of Ge-rich thin films (including pure Ge) implanted with low doses of Fe ions, almost all the Fe ions substituted at Ge sites. However, an anti-ferromagnetic Fe₆Ge₅ impurity phase existed in the annealed samples implanted with high doses of Fe. It was also found that the solubility of Fe ions was highest in pure Ge films and that with increasing Si concentration, the solubility decreased. Magnetic analysis showed that for the as-implanted and annealed samples of Ge-rich thin films implanted with Fe ions, room-temperature ferromagnetism was strongest in the pure Ge series of samples and that as the Ge concentration decreased, the ferromagnetism at room temperature weakened. In addition, annealing could increase the number of Fe ions at substitution sites, which resulted in the observed increase in the saturated magnetization after annealing. Experiment and theoretical analysis showed that the ferromagnetism of Fe-doped Ge-rich Si_1?xGe_x thin films samples originated from the s, p–d exchange interactions between the Si_1?xGe_x matrix and those Fe ions which substituted at Ge sites and that the ferromagnetism was mediated by carriers.     

Some optical properties of Ge–S amorphous thin films

Amorphous Ge_xS_1−x films (x=0.27, 0.32, 0.36 and 0.4) were prepared by thermal evaporation. The values of the refractive index, the optical gap and the parameters of the Wemple–DiDomenico single oscillator model were determined. Using Miller's generalized rule the values of the third-order non-linear susceptibility were also estimated. Thermally induced bleaching was observed for films studied. Photobleaching was observed for sulfur rich and nearly stoichiometric films (x=0.27, 0.32) while for a germanium rich film (x=0.4) no response to the illumination was observed. The differences in photobleaching are attributed to the role of p-lone pair states and to an overall network rigidity of the films.     

Structural,electrical and optical properties of sol–gel AZO thin films

Transparent conductive Al-doped zinc oxide (AZO) thin films were prepared by a sol–gel method and their structural, electrical and optical properties were systematically investigated. A minimum resistivity of 4.2 × 10⁻³ Ω cm was obtained for the 650 °C-annealed films doped with 1.0 at.% Al. All films had the preferential c-axis oriented texture according to the X-ray diffraction (XRD) results. Optical transmittance spectra of the films showed a high transmittance of over 85% in the visible region and the optical band gap of the AZO films broadened with increasing doping concentration.