聚乙烯吡咯烷酮/四氧化三铁复合纳米纤维的制备与表征

采用静电纺丝方法制备了聚乙烯吡咯烷酮/四氧化三铁复合纳米纤维, 并用透射电子显微镜(TEM)、X射线衍射(XRD)、热失重分析(TGA)和振动磁力分析进行了表征, 探讨了复合物的结构及其性能.     

THE PREPARATION OF DOXORUBICIN- POLYVINYLPYRROLIDONE-NANOPARTICLES BY INVERSE EMULSION POLYMERIZATION

Doxorubicin-loaded nanoparticles, using doxorubicin (ADM) as model drug and vinylpyrrolidone as matrix, were prepared by inverse emulsion polymerization in the paper. The nanoparticles were characterized by telescope electron microscopy (TEM), laser light scattering technique (LLS) and infrared spectrum (IR). LIS test showed that the optimal prepared ADM-loaded nanoparticles had an average size 18.8nm and a narrow size distribution between 15nm and 32nm, which was consistent with the result obtained by TEM. And IR results indicated that the nanoparticles consisted of ADM and polyvinylpyrrolidone (PVP).     

THE PREPARATION OF DOXORUBICIN-POLYVINYLPYRROLIDONE-NANOPARTICLES BY INVERSE EMULSION POLYMERIZATION

1. INTRODUCTIONNow the application of biodegradable polymeric nanoparticles used as a controlled release dosage form of anticancer drugs has generated great interest. Polymeric nanoparticles usually use macromolecule material as matrix and drug is embedde…     

Fe_3O_4/CdTe/聚氨酯纳米复合物的制备及其性能研究

由共沉淀法和Stober法制备了伯胺基功能化SiO2稳定的Fe3O4磁性纳米粒子Fe3O4@SiO2-NH2;Fe3O4@SiO2-NH2与二异氰酸酯及咪唑阳离子二醇、聚乙二醇的反应使其表面形成阳离子型聚氨酯稳定层;通过阳离子型聚氨酯与CdTe量子点表面修饰的巯基乙酸间的电荷相互作用,制备得到了Fe3O4/CdTe/聚氨酯纳米复合物.用X射线衍射(XRD)、红外吸收光谱(FTIR)、热重分析(TGA)、透射电子显微镜(TEM)、磁强计(VSM)、紫外吸收光谱(UV)、荧光发射光谱(PL)表征了该纳米复合物的结构与性能.结果表明,CdTe量子点均匀地分散在Fe3O4@SiO2磁性纳米粒子周围,所得纳米复合物在溶剂中分散均匀,不团聚,且具有超顺磁性,并保持了CdTe量子点的荧光性能.     

壳核型磁性纳米纤维素微球的超声制备及表征

A kind of cellulose magnetic nanoparticle with a core / shell structure has been prepared by ultrasonic irradiation. Cellulose acts as the shell while Fe3O4 magnetic nanoparticles take the role as the core. Magnetic force microscopy（MFM）with atomic force microscopy（AFM）measurement showed that the size of the magnetic nanoparticles is about 30-50 nm in diameter,while the Fe3O4 core is about 20-30 nm. FT-IR,XRD and MFM was used to provide the chemical and magnetic information of the nanoparticles. The MFM image showed that the nanoparticles separate very well with each other,indicating the cellulose shell produces a good prevention from the aggregation of the Fe3O4 particles. MFM studies also showed two magnetic nanoparticles can form particle-pairs,indicating a weak magneto-dipole interaction between magnetic nanoparticles. It is also found that the average sizes of magnetic nanoparticles have relation to the power of ultrasonic irradiation,and the possible mechanism is discussed.     

Synthesis and characterization of bracelet-like magnetic nanorings consisting of Ag-Fe3O4 bi-component nanoparticles

Stable bracelet-like magnetic nanorings, formed by Ag-Fe(3)O(4) nanoparticles with an average size around 40 nm, have been successfully prepared in large scale by means of reducing Ag(+) and Fe(3+) simultaneously under mild conditions. In the reaction, tiny grains of silver are used as seeds to prompt small Fe(3)O(4) nanoparticles to grow larger, which is essential to enhance the magnetic dipole-dipole interactions, while only superparamagnetic Fe(3)O(4) nanoparticles (about 10 nm in size) can be obtained in the absence of Ag seeds. The XRD, TEM, SAED and the EDS line scan data reveal that these nanoparticles are in the core-shell structure. These magnetic Ag-Fe(3)O(4) nanoparticles assembled into nanorings by magnetic dipole-dipole interactions with a diameter of 100-200 nm. The saturation magnetization of the nanorings is 39.5 emu g(-1) at room temperature. The MRI images indicate that these kind of nanorings have the potential application in diagnostics as a T(2) MRI contrast agent.     

Fe3O4/Polypyrrole/Au nanocomposites with core/shell/shell structure: synthesis, characterization, and their electrochemical properties

Uniform Fe3O4 nanospheres with a diameter of 100 nm were rapidly prepared using a microwave solvothermal method. Then Fe304/polypyrrole (PPy) composite nanospheres with well-defined core/shell structures were obtained through chemical oxidative polymerization of pyrrole in the presence of Fe3O4; the average thickness of the coating shell was about 25 nm. Furthermore, by means of electrostatic interactions, plentiful gold nanoparticles with a diameter of 15 nm were assembled on the surface of Fe3O4/PPy to get Fe3O4/PPy/Au core/shell/shell structure. The morphology, structure, and composition of the products were characterized by transmission electronic microscopy (TEM), scanning electronic microscopy (SEM), X-ray powder diffraction (XRD), and Fourier transform infrared (FT-IR) spectroscopy. The resultant nanocomposites not only have the magnetism of Fe3O4 nanoparticles that make the nanocomposites easily controlled by an external magnetic field but also have the good conductivity and excellent electrochemical and catalytic properties of PPy and Au nanoparticles. Furthermore, the nanocomposites showed excellent electrocatalytic activities to biospecies such as ascorbic acid (AA).     

磁微球负载氯化血红素仿酶催化剂制备及催化降解DMP

采用超声辅助反向共沉淀法制得磁纳米Fe3O4颗粒,然后以磁纳米Fe3O4颗粒为种子采用种子乳液聚合法制得羟基功能化的磁纳米复合物微球,再以三聚氯氰为桥联剂键合氯化血红素制得磁微球负载氯化血红素仿酶催化剂.利用傅里叶变换红外光谱仪（FT-IR）、配置积分球的紫外-可见（UV-Vis）分光光度计、透射电子显微镜（TEM）、热重分析仪（TGA）和振动样品磁强计（VSM）对催化剂进行了表征.结果表明,催化剂粒径大小为10～12 nm,粒度均一,分散性好,在300 K下具有一定顺磁性,饱和磁化强度为21.61 emu/g,磁性物质含量为52.50%.催化剂在紫外光照和H2O2存在下对水中邻苯二甲酸二甲酯（DMP）有较高的氧化降解活性,且重复使用效果较好.     

Size and surface effects of prussian blue nanoparticles protected by organic polymers

Prussian blue (PB) nanoparticles protected by organic polymers such as poly(vinylpyrrolidone) (PVP) and poly(diallyldimethylammonium chloride) (PDDA) were prepared. Different experimental conditions (concentrations of Fe ions and feed ratios of Fe to the polymers) have been investigated to control the size of the PB nanoparticles. For example, the averaged dimensions of the PB nanoparticles were tuned from 12 to 27 nm by use of PVP in the different conditions. Addition of PDDA produced the PB nanoparticles with very small dimensions (5-8 nm) by an effective electrostatic interaction. We found that the surface environments of the PB nanoparticles affect the inherent properties of PB. The shifts of charge transfer (CT) absorptions from Fe(2+) to Fe(3+) in the PB nanoparticles resulted from the surface-protecting polymers. Especially, the PB nanoparticles with the PVP protection show high solubility in a variety of organic solvents and a solvent-dependent CT absorption. Measurement of the magnetic properties of the PB nanoparticles showed unprecedented size-dependency, surface effect, and superparamagnetic properties.     

聚(苯乙烯-马来酸酐)/Fe3O4纳米杂化材料的制备与表征

采用2,2,6,6-四甲基-1-哌啶氧化物(TEMPO)的溴盐对化学共沉淀法制备的Fe3O4纳米粒子进行表面修饰,以该粒子为过氧引发剂,苯乙烯(St)、马来酸酐(MA)为单体,采用"活性"/可控自由基聚合技术在粒子表面原位引发聚合,制备了聚(苯乙烯-马来酸酐)/Fe3O4纳米杂化材料,并对纳米Fe3O4及杂化材料进行了FT-IR、XRD、TGA、TEM和GPC表征。结果表明,所制备的纳米杂化材料的平均粒径约为70 nm,磁性粒子表面的聚合物分子链随着聚合时间的增长而增长。振动样品磁强计测试结果显示,在室温、外加磁场下,该纳米杂化材料呈现超顺磁性,饱和磁化强度随着包覆聚合物量的增加而降低。     

静电纺丝法制备铁酸锌中空纤维及其磁学性能

以锌盐、铁盐和聚乙烯吡咯烷酮(PVP)为原料,通过静电纺丝法先制备PVP/硝酸盐复合纤维,这些复合纤维以5℃·min-1的升温速率加热到500℃并保温3h,最终得到铁酸锌(ZnFe2O4)中空纤维.通过X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)以及振动样品磁强计(VSM)等分析手段对中空纤维的晶体结构、形貌和磁学性能进行了研究.结果显示,ZnFe2O4中空纤维属于尖晶石结构,高温处理后仍能保持一维结构,纤维直径在200-400nm之间,纤维壁由大小为25nm的颗粒堆积而成.室温磁化结果显示制备的ZnFe2O4中空纤维具有超顺磁性,在10kOe的磁化强度为2.03emu·g-1.     

Preparation and properties of poly(acrylic acid) oligomer stabilized superparamagnetic ferrofluid

Ferrofluids, which are stable dispersions of magnetic particles, behave as liquids that have strong magnetic properties. Nanoparticles of magnetite with a mean diameter of 10-15 nm, which are in the range of superparamagnetism, are usually prepared by the traditional method of co-precipitation from ferrous and ferric electrolyte solution. When diluted, the ferrofluid dispersions are not stable if anionic or cationic surfactants are used as the stabilizer. This work presents an efficient way to prepare a stable aqueous nanomagnetite dispersion. A stable ferrofluid containing Fe3O4 nanoparticles was synthesized via co-precipitation in the presence of poly(acrylic acid) oligomer. The mechanism, microstructure, and properties of the ferrofluid were investigated. The results indicate that the PAA oligomers promoted the nucleation and inhibited the growth of the magnetic iron oxide, and the average diameter of each individual Fe3O4 particle was smaller than 10 nm. In addition, the PAA oligomers provided both electrostatic and steric repulsion against particle aggregation, and the stability of dispersions could be controlled by adjusting the pH value of solution. A small amount of Fe2O3 was found in the nanoparticles but the superparamagnetic behavior of the nanoparticles was not affected.     

羧甲基葡聚糖磁性纳米微球的制备及表征

采用超声预处理技术,在羧甲基葡聚糖-水分散体系中,通过化学共沉淀法制备羧甲基葡聚糖磁性复合微球．采用IR,TEM,AFM,XRD和振动样品磁强计方法对产物进行了表征．实验结果表明：超声预处理方法能明显提高复合微球的分散性．制得的复合微球呈球形,分散均匀,平均粒径为100nm．它们具有超顺磁性,室温下磁性饱和磁化强度为35emu·g^-1．     

Prussian blue nanoparticles protected by poly(vinylpyrrolidone)

Prussian blue (PB) nanoparticles protected by poly(vinylpyrrolidone) (PVP) were prepared by mixing aqueous Fe2+, Fe(CN)63-, and PVP solutions together and were characterized by UV-vis, IR, XRPD, and TEM. Averaged dimensions of the nanoparticles were controlled between 12 and 27 nm depending on initial Fe ion concentrations and feed ratios of Fe ion to PVP. Solubility of PB bulk in organic solvents is considerably low; nevertheless, formations of the PB nanoparticles dramatically increase the solubility in a variety of organic solvents. It is noteworthy that the PVP-protected PB nanoparticles stably maintain the cluster formations without further aggregations and dissociation in CHCl3 over 1 month. Measurement of the critical temperature (Tc) where PB nanoparticles exhibit a ferromagnetic property showed a gradual decrease of Tc for the nanoparticles as the particle sizes become smaller. This result could be ascribed to the reduction of the averaged numbers of magnetic interacted neighbors.     

Surface chemistry of nanoscale Fe_3O_4 dispersed in magnetic fluids

The interaction between stabilizers and nanoparticles is one of the important factors to prepare stable magnetic fluids. The magnetic nano-size Fe3O4 core with single domain and the average grain size around 8-12 nm were prepared by chemical precipitation method. The O/Fe molar ratio of the particle surface was measured by X-ray photoelectron spectroscopy (XPS). The heat effects of stabilizers ad- sorption on nanoparticles were measured by solution calorimetry. The excess amount of oxygen was possibly the result of the hydroxygen formed on the surface of the nanoparticles. The heat effects showed that compounds containing carboxyl groups can be adsorbed chemically on magnetite by forming chemical bonds. The other stabilizers involving NH-groups, such as polyethylene-imine, can be adsorbed physically. The exothermic value is about half of the former case.     

Magnetite nanoparticles with tunable gold or silver shell

Fe3O4 nanoparticles with size approximately 13 nm have been prepared successfully in aqueous micellar medium at approximately 80 degrees C. To make Fe3O4 nanoparticles resistant to surface poisoning a new route is developed for coating Fe3O4 nanoparticles with noble metals such as gold or silver as shell. The shell thickness of the core-shell particles becomes tunable through the adjustment of the ratio of the constituents. Thus, the route yields well-defined core-shell structures of size from 18 to 30 nm with varying proportion of Fe3O4 to the noble metal precursor salts. These magnetic nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), FTIR, differential scanning calorimetry (DSC), Raman and temperature-dependent magnetic studies.     

磁性聚苯胺纳米微球的合成与表征

报道了具有核壳结构的Fe3O4-聚苯胺磁性纳米微球的合成方法和表征结果.微球同时具有导电性和磁性能.在优化的实验条件下,可得到饱和磁化强度Ms为55.4 emu/g,矫顽力Hc为62 Oe的磁性微球.微球的导电性随着微球中Fe含量的增加而下降.微球的磁性能则随着Fe含量的增加而增大.Fe3O4磁流体的粒径和磁性聚苯胺微球的粒径均在纳米量级.纳米Fe3O4粒子能够提高复合物的热性能.实验表明,磁流体和聚苯胺之间可能存在着一定的相互作用,但这种相互作用较为复杂,难于研究     

荧光磁性双功能树状分子微球的制备与表征

采用化学共沉淀法, 以FeCl₃·6H₂O和FeSO₄·7H₂O为原料制备了磁性Fe₃O₄纳米颗粒, 采用树状大分子对其进行修饰, 然后通过树状大分子具有的大量空腔及末端丰富的氨基, 经吸附、 键合, 与大量巯基乙酸修饰的CdSe/CdS量子点连接, 得到三代具有荧光磁性双功能的树状分子微球, 并对其进行结构表征与性能测试. 结果表明: 三代复合后的微球的平均粒径分别为15, 34和49 nm; 一代荧光磁性微球的发光性能最佳, 其量子产率达24.1%; 零代荧光磁性微球磁性能最优, 其饱和磁化强度为15.96 A·m²/kg. 这种具有荧光和磁性的双功能纳米复合微粒有望在免疫检测、 靶向治疗、 荧光追踪和磁性分离等方面得到广泛应用.     

磁性Fe_3O_4-聚吡咯纳米微球的合成与表征

报道了具有核壳结构的Fe3O4 聚吡咯磁性纳米微球的合成方法和表征结果 .微球同时具有导电性和磁性能 .在优化的实验条件下 ,可得到饱和磁化强度为 2 3 4emu g ,矫顽力为 45 2Oe的磁性微球 .微球的导电性随着微球中Fe3O4含量的增加而下降 .微球的磁性能则随着Fe3O4含量的增加而增大 .Fe3O4磁流体的粒径和磁性聚吡咯微球的粒径均在纳米量级 .纳米Fe3O4粒子能够提高复合物的热性能 .实验表明 ,磁流体和聚吡咯之间存在着一定的相互作用 ,正是这种相互作用使磁性聚吡咯纳米微球的热稳定性提高 .     

Ultrasmall water-soluble metal-iron oxide nanoparticles as T1-weighted contrast agents for magnetic resonance imaging

Using an improved hydrolysis method of inorganic salts assisted with water-bath incubation, ultrasmall water-soluble metal-iron oxide nanoparticles (including Fe(3)O(4), ZnFe(2)O(4) and NiFe(2)O(4) nanoparticles) were synthesized in aqueous solutions, which were used as T(1)-weighted contrast agents for magnetic resonance imaging (MRI). The morphology, structure, MRI relaxation properties and cytotoxicity of the as-prepared metal-iron oxide nanoparticles were characterized, respectively. The results showed that the average sizes of nanoparticles were about 4 nm, 4 nm and 5 nm for Fe(3)O(4), ZnFe(2)O(4) and NiFe(2)O(4) nanoparticles, respectively. Moreover, the nanoparticles have good water dispersibility and low cytotoxicity. The MRI test showed the strong T(1)-weighted, but the weak T(2)-weighted MRI performance of metal-iron oxide nanoparticles. The high T(1)-weighted MRI performance can be attributed to the ultrasmall size of metal-iron oxide nanoparticles. Therefore, the as-prepared metal-iron oxide nanoparticles with good water dispersibility and ultrasmall size can have potential applications as T(1)-weighted contrast agent materials for MRI.