Structural, optical and morphological studies on laser ablated nanostructured WO3 thin films

Thin films of tungsten trioxide (WO₃) are prepared by reactive pulsed laser deposition (PLD) technique on glass substrates at three different substrate temperatures (T_s). The structural, morphological and optical properties of the deposited films are systematically studied using X-ray diffraction (XRD), grazing incidence X-ray diffraction (GIXRD), micro-Raman spectroscopy, scanning electron microscopy (SEM), atomic force microscopy (AFM) and UV-VIS spectrophotometry techniques. X-ray diffraction analysis reveals that crystalline WO₃ films can grow effectively even at 300 K at an oxygen pressure of 0.12 mbar. All the films deposited at various T_s exhibit mixed oxide phase consisting of orthorhombic and triclinic phase of tungsten oxide with a preferred orientation along (0 0 1) lattice plane reflection. Micro-Raman results are consistent with X-ray diffraction findings. The SEM analysis shows that deposited films are porous and crystalline grains are of nano-metric dimension. The effect of T_s on mean surface roughness studied by AFM analysis reveals that mean surface roughness decreases with increase in T_s. The optical response of WO₃ layers measured using UV-VIS spectrophotometry is used to extract the optical constants such as refractive index (n), extinction coefficient (k) and optical band gap (E_g), following the method of Swanepoel.     

Effect of substrate temperature on structural, optical and electrical properties of pulsed laser ablated nanostructured indium oxide films

Nanocrystalline indium oxide (INO) films are deposited in a back ground oxygen pressure at 0.02 mbar on quartz substrates at different substrate temperatures (T_s) ranging from 300 to 573 K using pulsed laser deposition technique. The films are characterized using GIXRD, XPS, AFM and UV-visible spectroscopy to study the effect of substrate temperature on the structural and optical properties of films. The XRD patterns suggest that the films deposited at room temperature are amorphous in nature and the crystalline nature of the films increases with increase in substrate temperature. Films prepared at T_s ≥ 473 K are polycrystalline in nature (cubic phase). Crystalline grain size calculation based on Debye Scherrer formula indicates that the particle size enhances with the increase in substrate temperature. Lattice constant of the films are calculated from the XRD data. XPS studies suggest that all the INO films consist of both crystalline and amorphous phases. XPS results show an increase in oxygen content with increase in substrate temperature and reveals that the films deposited at higher substrate temperatures exhibit better stoichiometry. The thickness measurements using interferometric techniques show that the film thickness decreases with increase in substrate temperature. Analysis of the optical transmittance data of the films shows a blue shift in the values of optical band gap energy for the films compared to that of the bulk material owing to the quantum confinement effect due to the presence of quantum dots in the films. Refractive index and porosity of the films are also investigated. Room temperature DC electrical measurements shows that the INO films investigated are having relatively high electrical resistivity in the range of 0.80-1.90 Ωm. Low temperature electrical conductivity measurements in the temperature range of 50-300 K for the film deposited at 300 K give a linear Arrhenius plot suggesting thermally activated conduction. Surface morphology studies of the films using AFM reveal the formation of nanostructured indium oxide thin films.     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.     

Effect of substrate temperature on the structural, optical and electrical properties of dc magnetron sputtered tantalum oxide films

dc reactive magnetron sputtering technique was employed for deposition of tantalum oxide films on quartz and silicon substrates by sputtering of pure tantalum target in the presence of oxygen and argon gases under various substrate temperatures in the range 303-973 K. The variation of cathode potential with the oxygen partial pressure was systematically studied. The influence of substrate temperature on the chemical binding configuration, crystal structure and optical properties was investigated. X-ray photoelectron spectroscopic studies indicated that the films formed at oxygen partial pressures ≥1 × 10⁻⁴ mbar were stoichiometric. The Fourier transform infrared spectroscopic studies revealed that the films formed up to substrate temperatures <673 K showed a broad absorption band at 750-1000 cm⁻¹ and a sharp band at 630 cm⁻¹ indicated the presence of amorphous phase while at higher substrate temperatures the appearance of bands at about 810 and 510 cm⁻¹ revealed the polycrystalline nature. The effect of substrate temperature on the electrical characteristics of Al/Ta₂O₅/Si structure was investigated. The dielectric constant values were in the range 17-29 in the substrate temperature range of 303-973 K. The current-voltage characteristics showed modified Poole-Frenkel conduction mechanism with a tendency for reduction of the compensation level. The optical band gap of the films decreased from 4.44 to 4.25 eV and the refractive index increased from 1.89 to 2.25 with the increase of substrate temperature from 303 to 973 K.     

High temperature annealing effect on structure, optical property and laser-induced damage threshold of Ta2O5 films

Ta₂O₅ films were deposited by conventional electron beam evaporation method and then annealed in air at different temperature from 873 to 1273 K. It was found that the film structure changed from amorphous phase to hexagonal phase when annealed at 1073 K, then transformed to orthorhombic phase after annealed at 1273 K. The transmittance was improved after annealed at 873 K, and it decreased as the annealing temperature increased further. The total integrated scattering (TIS) tests and AFM results showed that both scattering and root mean square (RMS) roughness of films increased with the annealing temperature increasing. X-ray photoelectron spectroscopy (XPS) analysis showed that the film obtained better stoichiometry and the O/Ta ratio increased to 2.50 after annealing. It was found that the laser-induced damage threshold (LIDT) increased to the maximum when annealed at 873 K, while it decreased when the annealing temperature increased further. Detailed damaged models dominated by different parameters during annealing were discussed.     

Highly conductive and transparent laser ablated nanostructured Al: ZnO thin films

Al doped ZnO thin films are prepared by pulsed laser deposition on quartz substrate at substrate temperature 873 K under a background oxygen pressure of 0.02 mbar. The films are systematically analyzed using X-ray diffraction, atomic force microscopy, micro-Raman spectroscopy, UV-vis spectroscopy, photoluminescence spectroscopy, z-scan and temperature-dependent electrical resistivity measurements in the temperature range 70-300 K. XRD patterns show that all the films are well crystallized with hexagonal wurtzite structure with preferred orientation along (0 0 2) plane. Particle size calculations based on XRD analysis show that all the films are nanocrystalline in nature with the size of the quantum dots ranging from 8 to 17 nm. The presence of high frequency E₂ mode and longitudinal optical A₁ (LO) modes in the Raman spectra suggest a hexagonal wurtzite structure for the films. AFM analysis reveals the agglomerated growth mode in the doped films and it reduces the nucleation barrier of ZnO by Al doping. The 1% Al doped ZnO film presents high transmittance of ∼75% in the visible and near infrared region and low dc electrical resistivity of 5.94 × 10⁻⁶ Ω m. PL spectra show emissions corresponding to the near band edge (NBE) ultra violet emission and deep level emission in the visible region. Nonlinear optical measurements using the z-scan technique shows optical limiting behavior for the 5% Al doped ZnO film.     

Influence of post-deposition annealing on the structural,optical and electrical properties of Li and Mg co-doped ZnO thin films deposited by sol–gel technique

Lithium (Li) and magnesium (Mg) co-doped zinc oxide (ZnO) thin films were deposited by sol–gel method using spin coating technique. The films were deposited on glass substrates and annealed at different temperatures. The effects of annealing temperature on the structural, optical and electrical properties of the deposited films were investigated using X-ray diffraction (XRD), Ultraviolet–Visible absorption spectra (UV–VIS), photoluminescence spectra (PL), X-ray photo electron spectroscopy (XPS) and Hall measurements. XRD patterns indicated that the deposited films had a polycrystalline hexagonal wurtzite structure with preferred (0 0 0 2) orientation. All films were found to exhibit a good transparency in the visible range. Analysis of the absorption edge revealed that the optical band gap energies of the films annealed at different temperatures varies between 3.49 eV and 3.69 eV. Room temperature PL spectra of the deposited films annealed at various temperatures consist of a near band edge emission and visible emission due to the electronic defects, which are related to deep level emissions, such as oxide antisite (O_Zn), interstitial zinc (Zn_i), interstitial oxygen (O_i) and zinc vacancy (V_Zn) which are generated during annealing process. The influence of annealing temperature on the chemical state of the dopants in the film was analysed by XPS spectra. Ion beam analysis (Rutherford back scattering) experiments were performed to evaluate the content of Li and Mg in the films. Hall measurements confirmed the p-type nature of the deposited films.     

Photosensitivity of nanocrystalline ZnO films grown by PLD

We have studied the properties of ZnO thin films grown by laser ablation of ZnO targets on (0 0 0 1) sapphire (Al₂O₃), under substrate temperatures around 400 °C. The films were characterized by different methods including X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and atomic force microscopy (AFM). XPS analysis revealed that the films are oxygen deficient, and XRD analysis with θ-2θ scans and rocking curves indicate that the ZnO thin films are highly c-axis oriented. All the films are ultraviolet (UV) sensitive. Sensitivity is maximum for the films deposited at lower temperature. The films deposited at higher temperatures show crystallite sizes of typically 500 nm, a high dark current and minimum photoresponse. In all films we observe persistent photoconductivity decay. More densely packed crystallites and a faster decay in photocurrent is observed for films deposited at lower temperature.     

Radio-frequency assisted pulsed laser deposition of nanostructured WOx films

The synthesis of tungsten oxide films with large surface area is promising for gas sensing applications. Thin WO_x films were obtained by radio-frequency assisted pulsed laser deposition (RF-PLD). A tungsten target was ablated at 700 and 900 Pa in reactive oxygen, or in a 50% mixed oxygen-helium atmosphere at the same total pressure values. Corning glass was used as substrate, at temperatures including 673, 773 and 873 K. Other deposition parameters such as laser fluence (4.5 J cm⁻²), laser wavelength (355 nm), radiofrequency power (150 W), target to substrate distance (4 cm), laser spot area (0.7 mm²), and number of laser shots (12,000) were kept fixed. The sensitivity on the deposition conditions of morphology, nanostructure, bond coordination, and roughness of the obtained films were analyzed by scanning and transmission electron microscopy, micro-Raman spectroscopy, and atomic force microscopy.     

Effect of thermal annealing on the structure and microstructure of TiO2 thin films

Nanostructured TiO₂ thin films have been prepared through chemical route using sol-gel and spin coating techniques. The deposited films were annealed in the temperature range 400–1000°C for 1 h. The structure and microstructure of the annealed films were characterized by GAXRD, micro-Raman spectroscopy and AFM. The as-deposited TiO₂ thin films are found to be amorphous. Micro-Raman and GAXRD results confirm the presence of the anatase phase and absence of the rutile phase for films annealed up to 700°C. The diffraction pattern of the film annealed at 800 to 1000°C contains peaks of both anatase and rutile reflections. The intensity of all peaks in micro-Raman and GAXRD patterns increased and their width (FWHM) decreased with increasing annealing temperature, demonstrating the improvement in the crystallinity of the annealed films. Phase transformation at higher annealing temperature involves a competition among three events such as: grain growth of anatase phase, conversion of anatase to rutile and grain growth of rutile phase. AFM image of the asdeposited films and annealed films indicated exponential grain growth at higher temperature.      

Ferromagnetism in MnxGe1−x films prepared by magnetron sputtering

Mn_xGe_1−x thin films were prepared by magnetron sputtering with a substrate temperature of 673 K and subsequently annealed at 873 K. The X-ray diffraction (XRD) measurements showed that all samples had a single Ge cubic structure. No films showed clear magnetic domain structure under a magnetic force microscope (MFM). Atom force microscope (AFM) measurements showed that the films had an uniform particle size distribution, and a columnar growth pattern. X-ray photoelectron spectroscopy (XPS) measurements indicated that the valences of both Mn and Ge atoms increase with the Mn concentration. The resistance decreased with increasing temperature, suggesting that the films were typical semiconductors. Magnetic measurements carried out using a Physical Property Measurement System (PPMS) showed that all samples exhibited ferromagnetism at room temperature. There was a small concentration of Mn₁₁Ge₈ in the films, but the ferromagnetism was mainly induced by Mn substitution for Ge site.     

Influence of temperature annealing on optical properties of SrTiO3/BaTiO3 multilayered films on indium tin oxide

We have prepared SrTiO₃/BaTiO₃ thin films with multilayered structures deposited on indium tin oxide (ITO) coated glass by a sol-gel deposition and heating at 300-650 °C. The optical properties were obtained by UV-vis spectroscopy. The films show a high transmittance (approximately 85%) in the visible region. The optical band gap of the films is tunable in the 3.64-4.19 eV range by varying the annealing temperature. An abrupt decrease towards the bulk band gap value is observed at annealing temperatures above 600 °C. The multilayered film annealed at 650 ° C exhibited the maximum refractive index of 2.09-1.91 in the 450-750 nm wavelength range. The XRD and AFM results indicate that the films annealed above 600 ° C are substantially more crystalline than the films prepared at lower temperatures which were used to change their optical band gap and complex refractive index to an extent that depended on the annealing temperature.     

Seebeck and magnetoresistive effects of Ga-doped ZnO thin films prepared by RF magnetron sputtering

In this paper, Ga-doped ZnO (GZO) films were deposited on glass substrates at different substrate temperatures by RF magnetron sputtering. The effect of substrate temperature on the structural, surface morphological properties, Seebeck and magnetoresistive effects of GZO films was investigated. It is found that the GZO films are polycrystalline and preferentially in the [0 0 2] orientation, and the film deposited at 300 °C has an optimal crystal quality. Seebeck and magnetoresistive effects are apparently observed in GZO films. The thermoelectromotive forces are negative. Decreasing substrate temperature and annealing in N₂ flow can decrease carrier concentration. The absolute value of the Seebeck coefficient increases with decreasing carrier concentration. The maximal absolute value of Seebeck coefficient is 101.54 μV/K for the annealed samples deposited at the substrate temperature of 200 °C. The transverse magnetoresistance of GZO films is related to both the magnetic field intensity and the Hall mobility. The magnetoresistance increases almost linearly with magnetic field intensity, and the films deposited at higher substrate temperature have a stronger magnetoresistance under the same magnetic field, due to the larger Hall mobility.     

Effect of substrate temperature on the surface and interface oxidation of NiTi thin films

NiTi shape memory alloy thin films are deposited on pure Cu substrate at substrate ambient temperatures of 300 °C and 450 °C. The surface and interface oxidation of NiTi thin films are characterized by X-ray photoelectron spectroscopy (XPS). After a subsequent annealing treatment the crystallization behavior of the films deposited on substrate at different temperatures is studied by X-ray diffraction (XRD). The effects of substrate temperature on the surface and interface oxidation of NiTi thin films are investigated. In the film surface this is an oxide layer composed of TiO₂. The Ni atom has not been detected on surface. In the film/substrate interface there is an oxide layer with a mixture Ti₂O₃ and NiO in the films deposited at substrate temperatures 300 °C and 450 °C. In the films deposited at ambient temperature, the interface layer contains Ti suboxides (TiO) and metallic Ni.     

Optical properties of single-phase β-FeSi2 films fabricated by electron beam evaporation

Single-phase semiconducting iron disilicide (β-FeSi₂) films on silicon substrate were fabricated by electron beam evaporation (EBE) technique. For preventing the oxidation of Fe film, silicon/iron/silicon sandwich structure films with different thickness of silicon and iron were deposited and then annealed at different temperatures. X-ray diffraction (XRD), Raman and Fourier transform infrared spectroscopy (FTIR) measurements were carried out to study the phase distribution and crystal quality of the films. Single-phase β-FeSi₂ with high crystal quality was achieved after annealing at 800 °C for 5 h. An apparent direct bandgap E_g of approximately 0.85-0.88 eV was observed in the β-FeSi₂ films. It is considered that the silicon/iron/silicon sandwich structure is suited for formation of single-phase β-FeSi₂ with high crystal quality.     

Reversible wettability of nanostructured ZnO thin films by sol-gel method

Nanostructured ZnO thin films were deposited on Si(1 1 1) and quartz substrate by sol-gel method. The thin films were annealed at 673 K, 873 K, and 1073 K for 60 min. Microstructure, surface topography, and water contact angle of the thin films have been measured by X-ray diffractometer, atomic force microscopy, and water contact angle apparatus. XRD results showed that the ZnO thin films are polycrystalline with hexagonal wurtzite structure. AFM studies revealed that rms roughness changes from 2.3 nm to 7.4 nm and the grain size grow up continuously with increasing annealing temperature. Wettability results indicated that hydrophobicity of the un-irradiated ZnO thin films enhances with annealing temperature increase. The hydrophobic ZnO surfaces could be reversibly switched to hydrophilic by alternation of UV illumination and dark storage (thermal treatment). By studying the magnitude and the contact angle reduction rate of the light-induced process, the contribution of surface roughness is discussed.     

Effect of annealing on thermal stability and morphology of pulsed laser deposited Ir thin films

Iridium (Ir) thin films, deposited on Si (1 0 0) substrate by pulsed laser deposition (PLD) technique using Ir target in a vacuum atmosphere, were annealed in air ambient and the thermal stability was investigated. The crystal structure and surface morphology of Ir thin films before and after being annealed were studied by X-ray diffraction, Raman scattering, scanning electron microscope, and atomic force microscopy. The results showed that single-phase Ir thin films with (1 1 1) preferred orientation could be deposited on Si (1 0 0) substrate at 300 °C and it remained stable below 600 °C, which showed a promising bottom electrode of integrated ferroelectric capacitors. Ir thin films got oxidized to IrO₂ at temperatures from 650 to 800 °C.     

Effect of annealing on electrical resistivity of rf-magnetron sputtered nanostructured SnO2 thin films

Tin oxide (SnO₂) thin films were deposited by radio frequency (RF) magnetron sputtering on clean corning glass substrates. These films were then annealed for 15 min at various temperatures in the range of 100-500°C. The films were investigated by studying their structural and electrical properties. X-ray diffraction (XRD) results suggested that the deposited SnO₂ films were formed by nanoparticles with average particle size in the range of 23-28 nm. XRD patterns of annealed films showed the formation of small amount of SnO phase in the matrix of SnO₂. The initial surface RMS roughness measured with atomic force microscopy (AFM) was 25.76 nm which reduces to 17.72 nm with annealing. Electrical resistivity was measured as a function of annealing temperature and found to lie between 1.25 and 1.38 mΩ cm. RMS roughness and resistivity show almost opposite trend with annealing.     

Investigation of annealing effects on the laser-induced damage threshold of amorphous Ta2O5 films

Ta₂O₅ films were deposited using the conventional electron beam evaporation method and then annealed at temperatures in the range 373-673 K. Chemical composition, scattering and absorption were examined by X-ray photoelectron spectroscopy (XPS), total integrated scattering (TIS) measurement and the surface thermal lensing (STL) technique, respectively. The laser-induced damage threshold (LIDT) was assessed using the output from an Nd:YAG laser with a pulse length of 12 ns. The results showed that the improvement of the LIDT after annealing was due to the reduced substoichiometric and structural defects present in the film. The LIDT increased slightly below 573 K and then increased significantly with increase in annealing temperature, which could be attributed to different dominant defects. Moreover, the root mean square (RMS) roughness and scattering had little effect on the LIDT, while the absorption and the LIDT were in accord with a general relation.     

The influence of substrate temperature and annealing on the properties of pulsed laser-deposited YIG films on fused quartz substrate

Yttrium iron garnet (YIG) thin films were deposited on fused quartz substrate at different substrate temperatures (T_s) varying from room temperature (RT) to 850 °C using pulsed laser deposition (PLD) technique. All the films in the as-deposited state were X-ray amorphous and non-magnetic at RT. The film deposited at RT after annealing at temperatures T_a?700 °C showed both X-ray peaks and the magnetic order. The films deposited at higher T_s (500–850 °C) and then annealed at 700 °C resulted in better-quality films with higher 4πM_s value. The highest value of magnetization was for the sample deposited at 850 °C and annealed at 700 °C, which is 68% of the bulk 4πM_s value.