Germanium growth on Br-terminated Si(1 0 0)

The consequences of Ge deposition on Br-terminated Si(1 0 0) were studied with scanning tunneling microscopy at ambient temperature after annealing at 650 K. One monolayer of Br was sufficient to prevent the formation of Ge huts beyond the critical thickness of 3 ML. This is possible because Br acts as a surfactant whose presence lowered the diffusivity of Ge adatoms. Hindered mobility was manifest at low coverage through the formation of short Ge chains. Further deposition resulted in the extension and connection of the Ge chains and gave rise to the buildup of incomplete layers. The deposition of 7 ML of Ge resulted in a rough surface characterized by irregularly shaped clusters. A short 800 K anneal desorbed the Br and allowed Ge atoms to reorganize into the more energetically favorable “hut” structures produced by conventional Ge overlayer growth on Si(1 0 0).     

Electronic structure study of reconstructed Au-SiC(0 0 0 1) surfaces

A study of surface and interface properties of reconstructed Au-SiC(0 0 0 1) surfaces is reported. Two reconstructions were prepared on SiC(0 0 0 1), a √3 × √3R30° and a Si-rich 3 × 3, before Au deposition and subsequent annealing at different temperatures. For the Si-rich 3 × 3 surface the existence of three stable reconstructions 2√3 × 2√3R30°, 3 × 3 and 5 × 5 are revealed after deposition of Au layers, 4-8 Å thick, and annealing at progressively higher temperatures between 500 and 950 °C. For the 2√3 surface two surface shifted Si 2p components are revealed and the Au 4f spectra clearly indicate silicide formation. The variation in relative intensity for the different core level components with photon energy suggests formation of an ordered silicide layer with some excess Si on top. Similar core level spectra and variations in relative intensity with photon energy are obtained for the 3 × 3 and 5 × 5 phases but the amount of excess Si on top is observed to be smaller and an additional weak Si 2p component becomes discernable.For the √3 surface the evolution of the core level spectra after Au deposition and annealing is shown to be distinctly different than for the Si-rich 3 × 3 surface and only one stable reconstruction, a 3 × 3 phase, is observed at similar annealing temperatures.     

Structural phase transitions in Au thin films on Si (1 1 0): An in situ temperature dependent transmission electron microscopy study

We present a review on the formation of gold silicide nanostructures using in situ temperature dependent transmission electron microscopy (TEM) measurements. Thin Au films of two thicknesses (2.0 nm and 5.0 nm) were deposited on Si (1 1 0) substrate under ultra-high vacuum (UHV) conditions in a molecular beam epitaxy (MBE) system. Also a 2.0 nm thick Au film was deposited under high vacuum condition (with the native oxide at the interface of Au and Si) using thermal evaporation. In situ TEM measurements (for planar samples) were made at various temperatures (from room temperature, RT to 950 °C). We show that, in the presence of native oxide (UHV-MBE) at the interface, high aspect ratio (≈15.0) aligned gold silicide nanorods were observed. For the films that were grown with UHV conditions, a small aspect ratio (∼1.38) nanogold silicide was observed. For 5.0 nm thick gold thin film, thicker and lesser aspect ratio silicides were observed. Selected area diffraction pattern taken at RT after the sample for the case of 5.0 nm Au on Si (1 1 0)-MBE was annealed at 475 °C show the signature of gold silicide formation.     

Formation and characterization of the Cu2O overlayer on Zn-terminated ZnO(0 0 0 1)

Low-energy electron diffraction, X-ray photoelectron spectroscopy and synchrotron-radiation-excited angle-resolved photoelectron spectroscopy have been used to characterize Cu-oxide overlayers on the Zn-terminated ZnO(0 0 0 1) surface. Deposition of Cu on the ZnO(0 0 0 1)-Zn surface results in the formation of Cu clusters with (1 1 1) top terraces. Oxidation of these clusters by annealing at 650 K in O₂ atmosphere (1.3 × 10⁻⁴ Pa) leads to an ordered Cu₂O overlayer with (1 1 1) orientation. Good crystallinity of the Cu₂O(1 1 1) overlayer is proved by energy dispersion of one of Cu₂O valence bands. The Cu₂O(1 1 1) film exhibits a strong p-type semiconducting nature with the valence band maximum (VBM) of 0.1 eV below the Fermi level. The VBM of ZnO at the Cu₂O(1 1 1)/ZnO(0 0 0 1)-Zn interface is estimated to be 2.4 eV, yielding the valence-band offset of 2.3 eV.     

Ga-induced superstructures on the Si(1 1 1) 7 × 7 surface

Monolayer Ga adsorption on Si surfaces has been studied with the aim of forming p-delta doped nanostructures. Ga surface phases on Si can be nitrided by N₂⁺ ion bombardment to form GaN nanostructures with exotic electron confinement properties for novel optoelectronic devices. In this study, we report the adsorption of Ga in the submonolayer regime on 7 × 7 reconstructed Si(1 1 1) surface at room temperature, under controlled ultrahigh vacuum conditions. We use in-situ Auger electron spectroscopy, electron energy loss spectroscopy and low energy electron diffraction to monitor the growth and determine the properties. We observe that Ga grows in the Stranski-Krastanov growth mode, where islands begin to form on two flat monolayers. The variation in the dangling bond density is observed during the interface evolution by monitoring the Si (LVV) line shape. The Ga adsorbed system is subjected to thermal annealing and the residual thermal desorption studied. The difference in the adsorption kinetics and desorption dynamics on the surface morphology is explained in terms of strain relaxation routes and bonding configurations. Due to the presence of an energetic hierarchy of residence sites of adatoms, site we also plot a 2D phase diagram consisting of several surface phases. Our EELS results show that the electronic properties of the surface phases are unique to their respective structural arrangement.     

Mechanisms of preferential adsorption on the Si(1 1 1)7 × 7 surface

The surface relaxation mechanisms governing the preferential adsorption of metal atoms onto the faulted half-cells of a 7 × 7 reconstructed Si(1 1 1) surface are studied by rate equations and kinetic Monte Carlo simulations. The versatility of these mechanisms to control the formation of quasi-perfect 2D arrays of metal clusters is revealed via the optimization of the deposition/annealing conditions as a function of operating mechanisms, the Si(1 1 1)7 × 7 energy landscape, and the thermal stability of the created clusters. The influence on the formation process of such nanoarrays of the balance between kinetic limitations, which are especially relevant on Si(1 1 1)7 × 7, and thermodynamic tendencies is discussed.     

Nanostructure formation aided by self-organised Bi nanolines on Si(0 0 1)

We provide a mini review of recent theoretical investigations of nanostructure formation aided by self-organised Bi nanolines on the Si(0 0 1) surface. It is suggested that hydrogen-passivated single-domain Si(0 0 1) produced by the formation of defect-free, hundreds of nm long, and 1.2-1.5 nm wide Bi nanolines provides an appealing template with preferential sites for adsorption of other elements. Based on ab initio pseudopotential calculations it is suggested that using the Bi nanoline template it should be possible to grow the following structures: mixed Ge-Si dimer structures on the Si(0 0 1) terrace between two neighbouring Bi nanolines; small In nanoclusters along the nanoline; and line and cluster structures of Fe atoms with novel electronic and magnetic properties.     

Structural analysis of the c(4 × 2) reconstruction in Si(0 0 1) and Ge(0 0 1) surfaces by low-energy electron diffraction

The c(4 × 2) structures in (0 0 1) surfaces of Si and Ge have been studied by low-energy electron diffraction (LEED). Using a proper cleaning method for the Si surface, we were able to observe clear c(4 × 2) LEED patterns up to incident energy of ∼400 eV as well as the Ge surface. Extensive experimental intensity-voltage curves allowed us to optimize the asymmetric dimer model up to the eighth layer (including the dimer layer) in depth in the dynamical LEED calculation. Optimized structural parameters are almost the same for the Si and Ge except for the height of the buckled-up atom of the asymmetric dimer. For the Ge surface, the structural parameters are in excellent agreement with those obtained by a previous theoretical calculation. The tilt angle and bond length of the dimer are 18 ± 1 (19 ± 1)° and 2.4 ± 0.1 (2.5 ± 0.1) Å for the Si(0 0 1) (Ge(0 0 1)), respectively.     

Perturbation of Ge(1 1 1) and Si(1 1 1)√3α-Sn surfaces by adsorption of dopants

We test the response of the √3 × √3α reconstructions formed by 1/3 monolayer of tin adatoms on silicon and germanium (1 1 1) surfaces upon doping with electrons or holes, using potassium or iodine as probes/perturbers of the initial electronic structures. From detailed synchrotron radiation photoelectron spectroscopy studies we show that doping with either electrons or holes plays a complimentary role on the Si and Ge surfaces and, especially, leads to complete conversion of the Sn 4d two-component spectra into single line shapes. We find that the low binding energy component of the Sn core level for both Si and Ge surfaces corresponds to Sn adatoms with higher electronic charge, than the Sn adatoms that contribute to the core level high binding energy signal. This could be analyzed as Sn adatoms with different valence state.     

Interaction of Ag and O on W(1 1 0) studied by scanning tunneling microscopy

The structural changes of Ag films on W(1 1 0) upon coadsorption of oxygen have been studied by scanning tunneling microscopy. The exposure of one monolayer Ag to oxygen leads to a phase separation into an Ag bilayer and patches of O-covered W(1 1 0). The effective Ag island thickness increases linearly with oxygen exposure. For Ag submonolayer-islands the onset of the bilayer formation is delayed, the induction period increases with the available free W area. We conclude that the steps of the transport process are (1) dissociation of oxygen on W and on the Ag islands, (2) site exchange of atomic oxygen with Ag atoms predominantly at the island edges - while on W(1 1 0) the oxygen is immobile, (3) diffusion of the displaced Ag atoms to the island edges where they are incorporated into the monolayer and (4) initiation of Ag bilayer formation, once the W(1 1 0) is saturated with O. This indicates an unexpected activity of the Ag monolayer on W(1 1 0) towards oxygen dissociation. In case of a reversed deposition sequence, where submonolayer quantities of Ag are adsorbed on an oxygen-precovered W(1 1 0) surface, growth of Ag clusters is observed. The distribution of cluster size and cluster height depends critically on the spatial order within the predeposited oxygen overlayer - it is obvious that the oxygen overlayer on the W surface acts as a structured template for preferential Ag nucleation.     

New tetramer structures in the initial process of Si homoepitaxial growth on Si (0 0 1)

We have studied the interaction between Si ad-dimers in the initial process of Si homoepitaxial growth on Si (0 0 1) surface by molecular dynamics simulations using the Stillinger-Weber potential. The interactions determine the formation of larger clusters from diffusing dimers. We show different pathways for the formation of multiple-dimer clusters and propose two new tetramer structures (T_BB and T_CC) formation by two diffusing dimers interacting. These tetramer structures have been found to be energetically stable with respect to isolated ad-dimers. Moreover, their local bonding configuration is very similar to the B-type step edge which is known to be the favored adsorption site for epitaxial growth. The proposed tetramers may play a crucial role as the nucleus of the new epitaxial layer on Si (0 0 1).     

Structural study of Si(1 1 1)-6 × 1-Ag surface using surface X-ray diffraction

The surface structure of Si(1 1 1)-6 × 1-Ag was investigated using surface X-ray diffraction techniques. By analyzing the CTR scattering intensities along 00 rod, the positions of the Ag and reconstructed Si atoms perpendicular to the surface were determined. The results agreed well with the HCC model proposed for a 3 × 1 structure induced by alkali-metals on a Si(1 1 1) substrate. The heights of the surface Ag and Si atoms did not move when the surface structure changed from Si(1 1 1)-√3 × √3-Ag to Si(1 1 1)-6 × 1-Ag by the desorption of the Ag atoms. From the GIXD measurement, the in-plane arrangement of the surface Ag atoms was determined. The results indicate that the Ag atoms move large distances at the phase transition between the 6 × 1 and 3 × 1 structures.     

Growth of (√3 × √3)-Ag and (1 1 1) oriented Ag islands on Ge/Si(1 1 1) surfaces

We have studied the growth of Ag on Ge/Si(1 1 1) substrates. The Ge/Si(1 1 1) substrates were prepared by depositing one monolayer (ML) of Ge on Si(1 1 1)-(7 × 7) surfaces. Following Ge deposition the reflection high energy electron diffraction (RHEED) pattern changed to a (1 × 1) pattern. Ge as well as Ag deposition was carried out at 550 °C. Ag deposition on Ge/Si(1 1 1) substrates up to 10 ML has shown a prominent (√3 × √3)-R30° RHEED pattern along with a streak structure from Ag(1 1 1) surface. Scanning electron microscopy (SEM) shows the formation of Ag islands along with a large fraction of open area, which presumably has the Ag-induced (√3 × √3)-R30° structure on the Ge/Si(1 1 1) surface. X-ray diffraction (XRD) experiments show the presence of only (1 1 1) peak of Ag indicating epitaxial growth of Ag on Ge/Si(1 1 1) surfaces. The possibility of growing a strain-tuned (tensile to compressive) Ag(1 1 1) layer on Ge/Si(1 1 1) substrates is discussed.     

Effects of electronic confinement and substrate on the low-temperature growth of Pb islands on Si(1 0 0)-2 × 1 surfaces

The growth of Pb films on the Si(1 0 0)-2 × 1 surface has been investigated at low temperature using scanning tunneling microscopy. Although the orientation of the substrate is (1 0 0), flat-top Pb islands with (1 1 1) surface can be observed. The island thickness is confined within four to nine atomic layers at low coverage. Among these islands, those with a thickness of six layers are most abundant. Quantum-well states in Pb(1 1 1) islands of different thickness are acquired by scanning tunneling spectroscopy. They are found to be identical to those taken on the Pb(1 1 1) islands grown on the Si(1 1 1)7 × 7 surface. Besides Pb(1 1 1) islands, two additional types of Pb islands are formed: rectangular flat-top Pb(1 0 0) islands and rectangular three-dimensional (3D) Pb islands, and both their orientations rotate by 90° from a terrace to the adjacent one. This phenomenon implies that the structures of Pb(1 0 0) and 3D islands are influenced by the Si(1 0 0)-2 × 1 substrate.     

Self-assembly of 2,6-dimethylpyridine on Cu(1 1 0) directed by weak hydrogen bonding

Sequential stages of formation of a self-assembled monolayer of flat-lying 2,6-dimethylpyridine molecules on a single crystal Cu(1 1 0) surface have been observed by low-temperature scanning tunneling microscopy (LT-STM). At an adsorption temperature of 10 K, all of the molecules are randomly distributed at low coverage upon adsorption. The isolated molecules align their molecular axes parallel to the 〈0 0 1〉 azimuth of the Cu lattice. The nitrogen atom in the molecule is located at the four-fold hollow site. Upon annealing to 100 K, the molecules associate to form head-to-head dimers. The dimer units involve a pair of weak hydrogen bonds between methyl group-hydrogen atoms and N moieties on adjacent molecules, forming a core structure for further growth. In a later stage of self-assembly, single head-to-tail weak hydrogen bonds between ring C-H bonds and N moieties form in chains on the periphery of the central cores, leading to larger domains with a c(6 × 2) overlayer structure.     

Configuration of pentacene (C22H14) films on Si(1 0 0)-2 × 1 studied by NEXAFS

Pentacene films on Si(1 0 0)-(2 × 1) surface at 300 K were investigated using near edge X-ray absorption fine structure (NEXAFS) at the carbon K-edge. NEXAFS spectra show that pentacene molecules are chemisorbed on the Si(1 0 0)-(2 × 1) surface for monolayer with flat-laying and predominantly physisorbed on the Si(1 0 0)-(2 × 1) surface for multilayer films with an upright molecular orientation. Absorption angle of pentacene molecules were measured through π^∗ transition. The angles between the double bond and the silicon surface were 35-55°, 65° and 76° at monolayer, 24 and 48 nm pentacene deposited on the Si(1 0 0) surface, respectively. We observed that the intermediate flat-laying phase is favored for monolayer coverage, while the films of molecules standing perpendicular to the Si(1 0 0) surface are favored for multilayer coverage.     

Study of nickel silicide formation on Si(1 1 0) substrate

Nickel silicide formation on Si(1 1 0) and Si(1 0 0) substrate was investigated in this paper. It is confirmed that nickel monosilicide (NiSi) starts to form after 450 °C annealing for Si(1 0 0) substrate, but a higher annealing temperature is required for NiSi formation on Si(1 1 0) substrate, which is demonstrated by X-ray diffraction (XRD) and Raman scattering spectroscopy. The higher formation temperature of NiSi is attributed to the larger Ni₂Si grain size formed on Si(1 1 0) substrate. Ni silicided Schottky contacts on both Si(1 0 0) and Si(1 1 0) substrates were also fabricated for electrical characteristics evaluation. It clearly reveals that the rectifying characteristics of NiSi/n-Si(1 1 0) Schottky contacts is inferior to that of NiSi/n-Si(1 0 0) Schottky contacts, which is attributed to a lower Schottky barrier height and a rougher contact interface. The formation kinetics for nickel silicide on Si(1 1 0) substrate is also discussed in this paper.     

STM image visualization of Si(1 1 1) 7 × 7 surface (graphic simulation and implementation)

The possibilities of graphic STM image simulation of a clean Si(1 1 1) 7 × 7 surface at atomic level are indicated. The presented procedure takes into account various types of deformation on the surface near the Fermi level in order to classify them and explain their origin. It also gives a clear hint to insert relevant physical phenomena in a suggested analysis. This goal is achieved exploiting the results of DAS (dimmer adatom stacing fault) model by means of standard mathematical programmes. A clean Si(1 1 1) 7 × 7 surface is considered as the representative example, but similar evaluation is possible for another non-metal and metal surfaces.     

Layer-resolved photoelectron diffraction from Si(0 0 1) and GaAs(0 0 1)

Photoelectron diffraction in the layer-resolved mode brings more detailed information about local atomic arrangement than is obtained in the standard mode. This is demonstrated in crystals with diamond and zinc-blende structures, both for unpolarized photon excitation as well as for circularly polarized excitation. The full angular distributions of photoemission intensities are evaluated for large atomic clusters representing ideally truncated surfaces of Si(0 0 1) and GaAs(0 0 1). Highly structured layer-resolved patterns enable a more detailed understanding of the standard mode outcomes. Photoelectron intensities from atomic layers placed at different depths under the crystal surface provide direct evidence about electron attenuation and its anisotropy in crystals.     

Sulphur overlayers on the Au(1 1 0) surface: LEED and TPD study

The adsorption and desorption of sulphur on the clean reconstructed Au(1 1 0)-(1 × 2) surface has been studied by low energy electron diffraction, Auger electron spectroscopy and temperature programmed desorption. The results obtained show a complex behaviour of the S/Au(1 1 0) system during sulphur desorption at different temperatures. Two structures of the stable ordered sulphur overlayer on the Au(1 1 0) surface, p(4 × 2) and c(4 × 4), were found after annealing the S/Au(1 1 0) system at 630 K and 463 K, respectively. The corresponding sulphur coverage for these overlayers was estimated by AES signal intensity analysis of the Au NOO and S LMM Auger lines to be equal to 0.13 ML and 0.2 ML, respectively. Both sulphur structures appear after removing an excess of sulphur, which mainly desorbs at 358 K as determined from TPD spectra. Furthermore, it was not possible to produce the lower coverage p(4 × 2) sulphur structure by annealing the c(4 × 4) surface. In the case of the p(4 × 2) S overlayer on the Au(1 1 0)-(1 × 2) surface it is proposed that the sulphur is attached to “missing row” sites only. The c(4 × 4) S overlayer arises via desorption of S₂ molecules that are formed on the surface due to mobility of sulphur atoms after a prolonged anneal.