Study of electronic structures for Fe thin films deposited on Si- and C-faces of 4H-SiC substrates by soft X-ray emission spectroscopy

Silicon carbide (SiC) is a candidate material for electronic devices to operate upon crucial environment. Electronic states of silicides and/or carbide/graphite formed in metal/SiC contact system are fundamentally important from the viewpoint of device performance.We study interface electronic structure of iron thin film deposited on silicon (Si)- and carbon (C)-face of 4H-SiC(0 0 0 1) by using a soft X-ray emission spectroscopy (SXES). For specimens of Fe (50 nm)/4H-SiC (substrate) contact systems annealed at 700 and 900 °C, the Si L_2,3 emission spectra indicate different shapes and peak energies from the substrate depending on thermal-treated temperature. The product of materials such as silicides is suggested. Further, from comparison of Si L_2,3 emission spectra between Si- and C-face for the same annealing temperature at 700 °C, it is concluded that the similar silicides and/or ternary materials are formed on the two surfaces. However for those of 900 °C, the film on substrate is composed of the different silicide and/or ternary materials.     

Investigation of Ni/Ta contacts on 4H silicon carbide upon thermal annealing

Nickel and Tantalum thin films with 3:5 thickness ratios were deposited in succession onto 4H-SiC substrate at room temperature. The samples were then heated in situ in vacuum at 650, 800 or 950 °C for 30 min. Glancing angle X-ray diffraction (XRD), Auger electron spectroscopy (AES) and current-voltage (I-V) technique were used for characterising the interfacial reactions and electrical properties. Amorphous Ni-Ta can be formed by solid-state reaction at 650 °C. The minor dissolved Ni in the Ta metal promotes the reaction between Ta and SiC. With increasing annealing temperature up to 950 °C, the dominant carbide changes from Ta₂C to TaC and a layer structure is developed. Electrical measurements show that ohmic contact is formed after annealing at or above 800 °C.     

Study of Ni/Si(1 0 0) solid-state reaction with Al addition

The characteristics of Ni/Si(1 0 0) solid-state reaction with Al addition (Ni/Al/Si(1 0 0), Ni/Al/Ni/Si(1 0 0) and Al/Ni/Si(1 0 0)) is studied. Ni and Al films were deposited on Si(1 0 0) substrate by ion beam sputtering. The solid-state reaction between metal films and Si was performed by rapid thermal annealing. The sheet resistance of the formed silicide film was measured by four-point probe method. The X-ray diffraction (XRD) was employed to detect the phases in the silicide film. The Auger electron spectroscopy was applied to reveal the element profiles in depth. The influence of Al addition on the Schottky barrier heights of the formed silicide/Si diodes was investigated by current-voltage measurements. The experimental results show that NiSi forms even with the addition of Al, although the formation temperature correspondingly changes. It is revealed that Ni silicidation is accompanied with Al diffusion in Ni film toward the film top surface and Al is the dominant diffusion species in Ni/Al system. However, no Ni_xAl_y phase is detected in the films and no significant Schottky barrier height modulation by the addition of Al is observed.     

Epitaxial growth of uniform NiSi2 layers with atomically flat silicide/Si interface by solid-phase reaction in Ni-P/Si(1 0 0) systems

As metal-oxide-semiconductor field-effect transistor (MOSFET) devices are shrunk to the nanometer scale, flat shallow metal/Si electrical contacts must be formed in the source/drain region. This work demonstrates a method for the formation of epitaxial NiSi₂ layers by a solid-phase reaction in Ni-P(8 nm)/Si(1 0 0) samples. The results show that the sheet resistance remained low when the samples were annealed at temperatures from 400 to 700 °C. P atoms can be regarded as diffusion barriers against the supply of Ni to the Si substrate, which caused the formation of Si-rich silicide (NiSi₂) at low temperature. Furthermore, elemental P formed a stable capping layer with O, Ni and Si during the annealing process. A uniform NiSi₂ layer with an atomically flat interface was formed by annealing at 700 °C because of the formation of a Si-Ni-P-O capping layer and a reduction in the total interface area.     

Ta/Ni/Ta multilayered ohmic contacts on n-type SiC

The interface formation, electrical properties and the surface morphology of multilayered Ta/Ni/Ta/SiC contacts were reported in this study. It was found that the conducting behavior of the contacts so fabricated is much dependent on the metal layer thickness and the subsequent annealing temperature. Auger electron spectroscopy (AES) and X-ray diffraction analyses revealed that Ni₂Si and TaC formed as a result of the annealing. The Ni atoms diffused downward to metal/SiC interface and converted into Ni₂Si layer in adjacent to the SiC substrate. The released carbon atoms reacted with Ta atoms to form TaC layer. Ohmic contacts with specific contact resistivity as low as 3 × 10⁻⁴ Ω cm² have been achieved after thermal annealing. The formation of carbon vacancies at the Ni₂Si/SiC interface, probably created by dissociation of SiC and formation of TaC during thermal annealing, should be responsible for the ohmic formation of the annealed Ta/Ni/Ta contacts. The addition of Ta into the Ni metallization scheme to n-SiC restricted the accumulation of carbon atoms left behind during Ni₂Si formation, improving the electrical and microstructure properties.     

Study of electronic states for V thin films deposited on 6H-SiC substrates by soft X-ray emission spectroscopy

Silicon carbide (SiC) is a candidate material for electronic devices to operate upon crucial environment. Electronic states of silicides and/or carbide/graphite formed in metal/SiC contact system is fundamentally important from the view point of device performance.We study interface electronic structure of vanadium (V) thin-film deposited on 6H-SiC(0 0 0 1) Si-face by using a soft X-ray emission spectroscopy (SXES). For specimens of V(38 nm)/6H-SiC (substrate) contact systems annealed at 850 °C, the Si L_2,3 emission spectra indicate different shapes and peak energies from the substrate. The product of materials such as silicides and/or ternary materials is suggested. Similarly, the C Kα emission spectra show the shape and peak energy characteristic of vanadium carbide including substrate 6H-SiC signal.     

Highly reproducible ideal SiC Schottky rectifiers: effects of surface preparation and thermal annealing on the Ni/6H-SiC barrier height

In this work, the effects of surface preparation and thermal annealing on the Ni/6H-SiC Schottky barrier height were studied by monitoring the forward I–V characteristics of Schottky diodes. The ideality factor n and the barrier height _B were found to be strongly dependent on the impurity species present at the metal/SiC interface. The physical mechanism which rules the Schottky barrier formation is discussed by considering the nature of the impurities left from the different surface preparation methods prior to metal deposition. In contrast, nickel silicide/SiC rectifiers (Ni₂Si/6H-SiC), formed by thermal reaction of Ni/6H-SiC above 600 °C, have an almost ideal I–V curve, independent of the surface preparation. Further improvement in the barrier height distribution can be obtained by increasing the annealing temperature to 950 °C. This behaviour is discussed in terms of the silicide phases and the consumption of a SiC layer during the thermal reaction. PACS 73.30.+y; 81.65.Cf; 81.05.Je     

Study of nickel silicide formation on Si(1 1 0) substrate

Nickel silicide formation on Si(1 1 0) and Si(1 0 0) substrate was investigated in this paper. It is confirmed that nickel monosilicide (NiSi) starts to form after 450 °C annealing for Si(1 0 0) substrate, but a higher annealing temperature is required for NiSi formation on Si(1 1 0) substrate, which is demonstrated by X-ray diffraction (XRD) and Raman scattering spectroscopy. The higher formation temperature of NiSi is attributed to the larger Ni₂Si grain size formed on Si(1 1 0) substrate. Ni silicided Schottky contacts on both Si(1 0 0) and Si(1 1 0) substrates were also fabricated for electrical characteristics evaluation. It clearly reveals that the rectifying characteristics of NiSi/n-Si(1 1 0) Schottky contacts is inferior to that of NiSi/n-Si(1 0 0) Schottky contacts, which is attributed to a lower Schottky barrier height and a rougher contact interface. The formation kinetics for nickel silicide on Si(1 1 0) substrate is also discussed in this paper.     

Study on changes in the structure of HfSiO and HfSiON dielectrics with different annealing temperature by photoelectron spectroscopy

We have investigated changes of the structure for HfSiO and HfSiON film with different annealing temperature by photoelectron spectroscopy. Core level photoelectron spectra have revealed the mechanism of metallization reaction at the bottom interface between the HfSiO(N) film and Si substrate under vacuum annealing. Silicidation action occurs by annealing at 850 and 900 °C for HfSiO and HfSiON film, respectively, indicating the incorporation of nitrogen enhances the thermal stability. By annealing at 900 °C, metallization reaction is rapidly promoted for the HfSiO film. For HfSiON film, Hf-nitride clusters or Hf-nitride layer and metal-silicide are formed at the bottom and upper interface, respectively, upon annealing at 950 °C.     

Ultrathin ZrO2 films on Si-rich SiC(0 0 0 1)-(3 × 3): Growth and thermal stability

The growth and thermal stability of ultrathin ZrO₂ films on the Si-rich SiC(0 0 0 1)-(3 × 3) surface have been explored using photoelectron spectroscopy (PES) and X-ray absorption spectroscopy (XAS). The films were grown in situ by chemical vapor deposition using the zirconium tetra tert-butoxide (ZTB) precursor. The O 1s XAS results show that growth at 400 °C yields tetragonal ZrO₂. An interface is formed between the ZrO₂ film and the SiC substrate. The interface contains Si in several chemically different states. This gives evidence for an interface that is much more complex than that formed upon oxidation with O₂. Si in a 4+ oxidation state is detected in the near surface region. This shows that intermixing of SiO₂ and ZrO₂ occurs, possibly under the formation of silicate. The alignment of the ZrO₂ and SiC band edges is discussed based on core level and valence PES spectra. Subsequent annealing of a deposited film was performed in order to study the thermal stability of the system. Annealing to 800 °C does not lead to decomposition of the tetragonal ZrO₂ (t-ZrO₂) but changes are observed within the interface region. After annealing to 1000 °C a laterally heterogeneous layer has formed. The decomposition of the film leads to regions with t-ZrO₂ remnants, metallic Zr silicide and Si aggregates.     

Origin of ohmic behavior in Ni, Ni2Si and Pd contacts on n-type SiC

Ni, Ni₂Si and Pd contacts were prepared on n-type 4H-SiC and annealed in the temperature range of 750-1150 °C. The annealed contacts were analyzed before and after acid etching, and different features were found in unetched and etched contacts. Carbon left on the SiC surface after the acid etching of Ni₂Si contacts annealed at 960 °C was highly graphitized. In nickel contacts, the graphitization of interface carbon began at 960 °C and increased after annealing at higher temperatures. In palladium contacts, the onset of the interface carbon graphitization was observed after annealing at 1150 °C. For all three types of metallization, the minimal values of contact resistivity were achieved only when the sharp first-order peak at 1585 cm⁻¹ and distinct second-order peak at ∼2700 cm⁻¹ related to the presence of graphitized carbon were detected by Raman spectroscopy after the acid etching of contacts. The properties of unannealed secondary contacts deposited onto etched primary contacts were similar to the properties of the primary contacts unless carbon was selectively etched. The results show that ohmic behavior of Ni-based and Pd contacts on n-type SiC originates from the formation of graphitic carbon at the interface with SiC.     

Phosphorous doped Ru film for advanced Cu diffusion barriers

Copper diffusion barrier properties of phosphorous doped Ru film are studied. Phosphorous out-diffusion to Ru from underneath phosphosilicate glass (PSG) layer results in P doped Ru film. The doped Ru film improves copper barrier properties and has excellent thermal stability. XRD graph indicates that there is no copper silicide and ruthenium silicide formations after annealing at 550 °C for 30 min in vacuum. This result is consistant with AES depth profiles which show no Cu, Ru, O and Si inter-diffusion. The phosphorous doped Ru barrier also blocks oxygen's diffusion to copper from the PSG layer. The phosphorous doped Ru film could be an alternative Cu diffusion barrier for advanced Cu interconnects.     

氢氟酸刻蚀对Ni/6H-SiC接触性质的作用

采用浓度为10%的氢氟酸（HF）刻蚀6H-SiC单晶片,研究了HF刻蚀时间对Ni/6H-SiC接触性质的影响．经24?h刻蚀的SiC基片在溅射Ni层后,其接触表现良好线性的电流-电压（I-V）曲线．低于这个腐蚀时间的接触具有明显的势垒,但在大于1000℃快速退火后,也得到了良好线性的I-V曲线．X射线衍射（XRD）和俄歇能谱（AES）深度元素分析表明Ni₂Si和C是快速退火后的主要产物．XRD和低能反射电子能量损失谱表明表层的C 关键词： 欧姆接触 SiC 富碳层 互扩散     

X-ray photoelectron spectroscopy study of NiSi formation on shallow junctions

The influence of boron (B)/arsenic (As) on X-ray photoelectron spectroscopy (XPS) study of NiSi formation on shallow junctions is investigated in this paper. The Ni-silicide film was formed after 30 s soak anneal at 450 °C on ultra shallow p+/n or n+/p junctions. The atomic ratio of Ni/Si profile in depth was probed by XPS and the results show that a uniform NiSi layer forms on B-doped p+/n junction while a non-uniform, Ni-rich silicide layer forms on As-doped n+/p junction. It does not agree with the results of other independent phase identification methods such as X-ray diffraction, Rutherford backscattering spectroscopy, and Raman scattering spectroscopy, which all demonstrate the formation of NiSi on both n+/p and p+/n junctions. Comparing the raw binding energy spectra of Ni and Si for each silicide film, the similar spectra for Ni signals are revealed. But the Si signals with an obviously smaller intensity is found to be responsible for the apparent Ni rich silicide formation on As-doped n+/p junction. It indicates that As atoms in the silicide film can affect the sputtering yield of Ni and Si, while no noticeable effect is observed for B atoms. More As atoms than B atoms segregation into the silicide layer is indeed verified by secondary ion mass spectroscopy. And micro-Raman scattering spectroscopy further confirms that the degree of crystallinity for NiSi on n+/p junction is inferior to that on p+/n junction.     

Photoemission studies of initial oxidation for ultra-thin zinc film on 6H-SiC(0 0 0 1) surface with synchrotron radiation

The thermal oxidation process of metallic zinc on 6H-SiC(0 0 0 1) surface has been investigated by using atomic force microscopy (AFM), synchrotron radiation photoelectron spectroscopy (SRPES) and XPS methods. The AFM images characterize the surface morphology of ZnO film formed during the thermal oxidation and SRPES record the valence band, Si 2p and Zn 3d spectra at different stages. The O 1s peak is recorded by XPS because of the energy limit of the synchrotron radiation. Our results reveal that the silicon oxides layer of SiC substrate can be reduce by hot metallic zinc atom deposition. The oxygen atoms in the silicon oxides are captured by the zinc atoms to form ZnO_x at the initial stage and as a result, the oxidized SiC surface are deoxidized. After the zinc deposition with the final thickness of 2.5 nm, the sample is exposed in oxygen atmosphere and annealed at different temperatures. According to the evolution of peaks integrated intensities, it is considered that the Zn/SiC system will lose zinc atoms during the annealing in oxygen flux at high temperature due to the low evaporation temperature of pure zinc. After further annealing in oxygen flux at higher temperature, the substrate is also oxidized and finally the interface becomes a stable SiC-SiO_x-ZnO sandwich structure.     

Cobalt-induced polycrystalline silicon film growth

Cobalt (Co)-induced crystalline silicon (Si) growth was investigated. The Co catalyst reacted to dc magnetron sputtered Si at 600 °C forming a Co silicide layer. The polycrystalline Si (poly-Si) was epitaxially grown above the Co silicide template, which has a small lattice misfit to Si. Annealing followed to improve the Si crystallinity. X-ray diffraction was performed to trace Co silicide phase formation and transition. The Co-rich silicide phase transitioned to CoSi₂ by annealing. The crystallinity of Si films was identified using reflection absorption Fourier transform-infrared spectroscopy, which detected unique peaks at 689 and 566 cm⁻¹ after the annealing process. The thin poly-Si film was used to fabricate a Schottky diode to prove the electronic quality. A good quality Si thin film was achieved by the metal-induced Si growth.     

The interface reaction of high-k La2Hf2O7/Si thin film grown by pulsed laser deposition

The La₂Hf₂O₇ films have been deposited on Si (1 0 0) substrate by using pulsed laser deposition (PLD) method. X-ray diffraction (XRD) demonstrates that the as-grown film is amorphous and crystallizes after 1000 °C annealing. The interface structure is systematically studied by Synchrotron X-ray reflectivity (XRR), Fourier transform infrared (FTIR) and X-ray photoelectron spectroscopy (XPS). Silicide, silicate and SiO_x formations from interfacial reaction are observed on the surface of the Si substrate in the as-grown film. The impact of silicide formation on the electrical properties is revealed by capacitance-voltage (C-V) measurements. By post-deposition annealing (PDA), silicide can be effectively eliminated and C-V property is obviously improved.     

Effect of substrate temperature on the surface and interface oxidation of NiTi thin films

NiTi shape memory alloy thin films are deposited on pure Cu substrate at substrate ambient temperatures of 300 °C and 450 °C. The surface and interface oxidation of NiTi thin films are characterized by X-ray photoelectron spectroscopy (XPS). After a subsequent annealing treatment the crystallization behavior of the films deposited on substrate at different temperatures is studied by X-ray diffraction (XRD). The effects of substrate temperature on the surface and interface oxidation of NiTi thin films are investigated. In the film surface this is an oxide layer composed of TiO₂. The Ni atom has not been detected on surface. In the film/substrate interface there is an oxide layer with a mixture Ti₂O₃ and NiO in the films deposited at substrate temperatures 300 °C and 450 °C. In the films deposited at ambient temperature, the interface layer contains Ti suboxides (TiO) and metallic Ni.     

Effect of erbium interlayer on nickel silicide formation on Si(1 0 0)

To reveal the influence of erbium interlayer on the formation of nickel silicide and its contact properties on Si substrate, Er(0.5-3.0 nm) and Ni(20 nm) are successively deposited onto Si(1 0 0) substrate and are treated by rapid thermal annealing in pure N₂ ambient. The NiSi formation temperature is found to increase depending on the Er interlayer thickness. The formation temperature of NiSi₂ (700 °C) is not influenced by Er addition. But with 2 nm Er interlayer, the formed NiSi₂ is observed textured with preferred orientation of (1 0 0). During the formation of NiSi, Er segregates to the surface and little Er remains at the NiSi/Si(1 0 0) interface. Therefore, the Schottky barrier height of the formed NiSi/n-Si(1 0 0) contact is measured to be 0.635 ∼ 0.665 eV which is nearly invariable with different Er addition.     

Structural characterization of Ni and Ni/Ti ohmic contact on n-type 4H-SiC

In this study, we report on the structural characterization of Ni layer and Ni/Ti bilayer contacts on n-type 4H-SiC. The resulting Ni-silicides and the redistribution of carbon, after annealing at 950 °C, in the Ni/SiC and the Ni/Ti/SiC contacts are particularly studied by Rutherford Backscattering Spectrometry (RBS) at E_α = 3.2 MeV, nuclear reaction analysis (NRA) at E_d = 1 MeV, scanning electron microscopy (SEM) and Energy Dispersive X-ray Spectrometry (EDS) techniques.