MOCVD growth of GaN on Si(1 1 1) substrates using an ALD-grown Al2O3 interlayer

GaN thin films have been grown on Si(1 1 1) substrates using an atomic layer deposition (ALD)-grown Al₂O₃ interlayer. This thin Al₂O₃ layer reduces strain in the subsequent GaN layer, leading to lower defect densities and improved material quality compared to GaN thin films grown by the same process on bare Si. XRD ω-scans showed a full width at half maximum (FWHM) of 549 arcsec for GaN grown on bare Si and a FWHM as low as 378 arcsec for GaN grown on Si using the ALD-grown Al₂O₃ interlayer. Raman spectroscopy was used to study the strain in these films in more detail, with the shift of the E₂(high) mode showing a clear dependence of strain on Al₂O₃ interlayer thickness. This dependence of strain on Al₂O₃ thickness was also observed via the redshift of the near bandedge emission in room temperature photoluminescence (RT-PL) spectroscopy. The reduction in strain results in a significant reduction in both crack density and screw dislocation density compared to similar films grown on bare Si. Screw dislocation density of the films grown on Al₂O₃/Si substrates approaches that of typical GaN layers on sapphire. This work shows great promise for the use of oxide interlayers for growth of GaN-based LEDs on Si.     

Surface and interfacial structure of epitaxial SrTiO3 thin films on (0 0 1) Si grown by molecular beam epitaxy

Effects of relaxation of interfacial misfit strain and non-stoichiometry on surface morphology and surface and interfacial structures of epitaxial SrTiO₃ (STO) thin films on (0 0 1) Si during initial growth by molecular beam epitaxy (MBE) were investigated. In situ reflection high-energy electron diffraction (RHEED) in combination with X-ray diffraction (XRD), atomic force microscopy (AFM), X-ray photoelectron spectrometry (XPS) and transmission electron microscopy (TEM) techniques were employed. Relaxation of the interfacial misfit strain between STO and Si as measured by in situ RHEED indicates initial growth is not pseudomorphic, and the interfacial misfit strain is relaxed during and immediately after the first monolayer (ML) deposition. The interfacial strain up to 15 ML results from thermal mismatch strain rather than lattice mismatch strain. Stoichiometry of STO affects not only surface morphology but interfacial structure. We have identified a nanoscale Sr₄Ti₃O₁₀ second phase at the STO/Si interface in a Sr-rich film.     

Large-size β-Ga2O3 single crystals and wafers

Large-size single crystals of β-Ga₂O₃ with 1 inc in diameter have been grown by the floating zone technique. The stable growth conditions have been determined by the examination of the crystal structure. Wafers have been cut and fine polished in the (1 0 0), (0 1 0) and (0 0 1) planes. These were highly transparent in the visible and near UV, as well as electrically conductive, indicating the potential use of β-Ga₂O₃ as a substrate for optoelectic devices operating in the visible/near UV and with vertical current flow.     

Influence of cooling rate on the liquid-phase epitaxial growth of Zn3P2

We report the liquid-phase epitaxial growth of Zn₃P₂ on InP (1 0 0) substrates by conventional horizontal sliding boat system using 100% In solvent. Different cooling rates of 0.2–1.0 °C/min have been adopted and the influence of supercooling on the properties of the grown epilayers is analyzed. The crystal structure and quality of the grown epilayers have been studied by X-ray diffraction and high-resolution X-ray rocking measurements, which revealed a good lattice matching between the epilayers and the substrate. The supercooling-induced morphologies and composition of the epilayers were studied by scanning electron microscopy and energy dispersive X-ray analysis. The growth rate has been calculated and found that there exists a linear dependence between the growth rate and the cooling rate. Hall measurements showed that the grown layers are unintentionally doped p-type with a carrier mobility as high as 450 cm²/V s and a carrier concentration of 2.81×10¹⁸ cm⁻³ for the layers grown from 6 °C supercooled melt from the cooling rate of 0.4 °C/min.     

CrO2 (1 0 0) and TiO2 (1 0 0) film heteroepitaxy on a BaF2 (1 1 1)/Si (1 0 0) substrate

Multi-domained heteroepitaxial rutile-phase TiO₂ (1 0 0)-oriented films were grown on Si (1 0 0) substrates by using a 30-nm-thick BaF₂ (1 1 1) buffer layer at the TiO₂–Si interface. The 50 nm TiO₂ films were grown by electron cyclotron resonance oxygen plasma-assisted electron beam evaporation of a titanium source, and the growth temperature was varied from 300 to 600 °C. At an optimal temperature of 500 °C, X-ray diffraction measurements show that rutile phase TiO₂ films are produced. Pole figure analysis indicates that the TiO₂ layer follows the symmetry of the BaF₂ surface mesh, and consists of six (1 0 0)-oriented domains separated by 30° in-plane rotations about the TiO₂ [1 0 0] axis. The in-plane alignment between the TiO₂ and BaF₂ films is oriented as [0 0 1] TiO₂ || BaF₂ or [0 0 1] TiO₂ || BaF₂ . Rocking curve and STM analyses suggest that the TiO₂ films are more finely grained than the BaF₂ film. STM imaging also reveals that the TiO₂ surface has morphological features consistent with the BaF₂ surface mesh symmetry. One of the optimally grown TiO₂ (1 0 0) films was used to template a CrO₂ (1 0 0) film which was grown via chemical vapor deposition. Point contact Andreev reflection measurements indicate that the CrO₂ film was approximately 70% spin polarized.     

The photoluminescence of ZnO thin films grown on Si (1 0 0) substrate by plasma-enhanced chemical vapor deposition

High-quality ZnO thin films have been grown on a Si(1 0 0) substrate by plasma-enhanced chemical vapor deposition (PECVD) using a zinc organic source (Zn(C₂H₅)₂) and carbon dioxide (CO₂) gas mixtures at a temperature of 180°C. A strong free exciton emission with a weak defect-band emission in the visible region is observed. The characteristics of photoluminescence (PL) of ZnO, as well as the exciton absorption peak in the absorption spectra, are closely related to the gas flow rate ratio of Zn(C₂H₅)₂ to CO₂. Full-widths at half-maximum of the free exciton emission as narrow as 93.4 meV have been achieved. Based on the temperature dependence of the PL spectra from 83 to 383 K, the exciton binding energy and the transition energy of free excitons at 0 K were estimated to be 59.4 meV and 3.36 eV, respectively.     

Growth of epitaxial ZnO films on Si (1 1 1) substrates with Cr compound buffer layer by plasma-assisted molecular beam epitaxy

Single crystalline ZnO film was grown on (1 1 1) Si substrate through employing an oxidized CrN buffer layer by plasma-assisted molecular beam epitaxy. Single crystalline characteristics were confirmed from in-situ reflection high energy electron diffraction, X-ray pole figure measurement, and transmission electron diffraction pattern, consistently. Epitaxial relationship between ZnO film and Si substrate is determined to be (0 0 0 1)_ZnO‖(1 1 1)_Si and [1 1 2¯ 0]_ZnO‖[0 1 1]_Si. Full-width at half-maximums (FWHMs) of (0 0 0 2) and (1 0 1¯ 1) X-ray rocking curves (XRCs) were 1.379° and 3.634°, respectively, which were significantly smaller than the FWHMs (4.532° and 32.8°, respectively) of the ZnO film grown directly on Si (1 1 1) substrate without any buffer. Total dislocation density in the top region of film was estimated to be ∼5×10⁹ cm⁻². Most of dislocations have a screw type component, which is different from the general cases of ZnO films with the major threading dislocations with an edge component.     

Investigations on the effect of InSb and InAsSb step-graded buffer layers in InAs0.5Sb0.5 epilayers grown on GaAs (0 0 1)

We report the structural and electrical properties of InAsSb epilayers grown on GaAs (0 0 1) substrates with mid-alloy composition of 0.5. InSb buffer layer and InAs_xSb_1−x step-graded (SG) buffer layer have been used to relax lattice mismatch between the epilayer and substrate. A decrease in the full-width at half-maximum (FWHM) of the epilayer is observed with increasing the thickness of the InSb buffer layer. The surface morphology of the epilayer is found to change from 3D island growth to 2D growth and the electron mobility of the sample is increased from 5.2×10³ to 1.1×10⁴ cm²/V s by increasing the thickness of the SG layers. These results suggest that high crystalline quality and electron mobility of the InAs_0.5Sb_0.5 alloy can be achieved by the growth of thick SG InAsSb buffer layer accompanied with a thick InSb buffer layer. We have confirmed the improvement in the structural and electrical properties of the InAs_0.5Sb_0.5 epilayer by quantitative analysis of the epilayer having a 2.09 μm thick InSb buffer layer and 0.6 μm thickness of each SG layers.     

Structural,electrical and optical properties of SnO2 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

SnO₂ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates at different substrate temperatures (500–800 °C) by metalorganic chemical vapor deposition (MOCVD). Structural, electrical and optical properties of the films have been investigated. The films deposited at 500 and 600 °C are epitaxial SnO₂ films with orthorhombic columbite structure, and the HRTEM analysis shows a clear epitaxial relationship of columbite SnO₂(1 0 0)||YSZ(1 0 0). The films deposited at 700 and 800 °C have mixed-phase structures of rutile and columbite SnO₂. The carrier concentration of the films is in the range from 1.15×10¹⁹ to 2.68×10¹⁹ cm⁻³, and the resistivity is from 2.48×10⁻² to 1.16×10⁻² Ω cm. The absolute average transmittance of the films in the visible range exceeds 90%. The band gap of the obtained SnO₂ films is about 3.75–3.87 eV.     

Growth and optical properties of self-frequency-doubling laser crystal Yb:LuAl3(BO3)4

Single crystal of Yb:LuAl₃(BO₃)₄(Yb:LuAB) was grown by the flux method for the first time. The cell parameters of the grown crystal were estimated by X-ray diffraction analysis. The result indicates the symmetry of trigonal space group R32, with lattice parameters a=b=9.26372 Å, c=7.21405 Å, V=536.14 Å³, and Z=4. The absorption and emission spectra of Yb:LuAB crystal at room temperature has also been studied. The fluorescence lifetime for Yb:LuAB crystal is about 1.48 ms. The heat capacity was measured from 25 to 500 °C. Its second harmonic generation efficiency in LuAl₃(BO₃)₄ crystal is 3–4 times that of KDP crystal. These results show that Yb:LuAB crystal would be a potential self-frequency-doubling laser crystal.     

Morphology transition of one-dimensional ZnO grown by metal organic vapour phase epitaxy on (0 0 0 1)-ZnO substrate

Metal organic vapour phase epitaxy (MOVPE) has been used to successfully grow one-dimensional (1D) ZnO deposits on (0 0 0 1)-ZnO substrate. Dimethylzinc–triethylamine and nitrous oxide were used as zinc and oxygen sources, respectively, with nitrogen as the carrier gas. Vertically aligned 1D ZnO structures were observed along the c-axis by using lower VI/II mole ratio R_VI/II<2025 and/or high growth temperatures (Tg>800 °C). The diameter, length, density and the mechanism of formation could be controlled with the growth time. Scanning electron microscopy (SEM) shows different structures, i.e., sharp-top, flat-top and open-top with slim bottom and large-top one-dimensional ZnO. A good structural quality was revealed by X-ray diffraction rocking curve with a full-width at half-maximum (FWHM) varying from 40 to 92 arcsec with increasing growth time.     

Synthesis and characteristics of Na-doped Bi4Ti3O12 thin films on Si substrate

Bi_3.25Na_2.25Ti₃O₁₂ thin films were prepared on p-Si(1 1 1) substrate by a metalorganic solution decomposition (MOSD) method. The structural characteristic and crystallization of the films were examined by X-ray diffraction. The current–voltage characteristic shows ohmic conductivity in the lower voltage range and space-charge-limited conductivity in the higher voltage range. The dielectric constant is 53 at a frequency of 100 kHz at room temperature and the dissipation factor exists at a minimal value of 0.02 at a frequency of 200 kHz. The retention time estimated by measuring capacitance is about 10⁶ s. Nonhysteretic C–V curves at various frequencies were also collected.     

Properties of ZnO films grown on (0 0 0 1) sapphire substrate using H2O and N2O as O precursors by atmospheric pressure MOCVD

In this paper, we compare the properties of ZnO thin films (0 0 0 1) sapphire substrate using diethylzinc (DEZn) as the Zn precursor and deionized water (H₂O) and nitrous oxide (N₂O) as the O precursors, respectively in the main ZnO layer growth by atmospheric pressure metal–organic chemical vapor deposition (AP-MOCVD) technique. Surface morphology studied by atomic force microscopy (AFM) showed that the N₂O-grown ZnO film had a hexagonal columnar structure with about 8 μm grain diameter and the relatively rougher surface compared to that of H₂O-grown ZnO film. The full-widths at half-maximum (FWHMs) of the (0 0 0 2) and () ω-rocking curves of the N₂O-grown ZnO film by double-crystal X-ray diffractometry (DCXRD) measurement were 260 and 350 arcsec, respectively, indicating the smaller mosaicity and lower dislocation density of the film compared to H₂O-grown ZnO film. Compared to H₂O-grown ZnO film, the free exciton A (FX_A) and its three phonon replicas could be clearly observed, the donor-bound exciton A⁰X (I₁₀):3.353 eV dominated the 10 K photoluminescence (PL) spectrum of N₂O-grown ZnO film and the hydrogen-related donor-bound exciton D⁰X (I₄):3.363 eV was disappeared. The electron mobility (80 cm²/V s) of N₂O-grown ZnO film has been significantly improved by room temperature Hall measurement compared to that of H₂O-grown ZnO film.     

Development of m-plane GaN anisotropic film properties during MOVPE growth on LiAlO2 substrates

The anisotropic film properties of m-plane GaN deposited by metal organic vapour phase epitaxy (MOVPE) on LiAlO₂ substrates are investigated. To study the development of layer properties during epitaxy, the total film thickness is varied between 0.2 and 1.7 μm. A surface roughening is observed caused by the increased size of hillock-like features. Additionally, small steps which are perfectly aligned in (1 1 −2 0) planes appear for samples with a thickness of ∼0.5 μm and above. Simultaneously, the X-ray rocking curve (XRC) full width at half maximum (FWHM) values become strongly dependent on incident X-ray beam direction beyond this critical thickness. Anisotropic in-plane compressive strain is initially present and gradually relaxes mainly in the [1 1 −2 0] direction when growing thicker films. Low-temperature photoluminescence (PL) spectra are dominated by the GaN near-band-edge peak and show only weak signal related to basal plane stacking faults (BSF). The measured background electron concentration is reduced from ∼10²⁰ to ∼10¹⁹ cm⁻³ for film thicknesses of 0.2 μm and ∼1 μm while the electron mobilities rise from ∼20 to ∼130 cm²/V s. The mobilities are significantly higher in [0 0 0 1] direction which we explain by the presence of extended planar defects in the prismatic plane. Such defects are assumed to be also the cause for the observed surface steps and anisotropic XRC broadening.     

Heteroepitaxy of CdTe on tilting Si(2 1 1) substrates by molecular beam epitaxy

CdTe(2 1 1)B epilayers were grown on 3 in Si(2 1 1) substrates which misoriented 0–10° toward [1 1 1] by molecular beam epitaxy (MBE). The relationship of X-ray double-crystal rocking curve (XRDCRC) FWHM and deflection angle from CdTe(2 1 1) to Si(2 1 1) was studied. For 4.2–4.5 μm CdTe, the best value of FWHM 83 arcsec was achieved while deflection angle is 2.76°. A FWHM wafer mapping indicated a good crystalline uniformity of 7.4 μm CdTe on tilting Si(2 1 1), with FWHM range of 60–72 arcsec. The shear strains of these epilayers were analyzed, using reciprocal lattice points of symmetric and asymmetric reflections measured by high-resolution multi-crystal multi-reflection X-ray diffractometer (HRMCMRXD). It was found that the shear strain angle of epilayer is effectively reduced by using proper tilting Si(2 1 1) substrate. It was also proved that the lattice parameter of CdTe(2 1 1)B is affected by the shear strain and thermal strain.     

Heteroepitaxial growth of Cu2O thin film on ZnO by metal organic chemical vapor deposition

Cuprous oxide (Cu₂O) thin films were grown epitaxially on c-axis-oriented polycrystalline zinc oxide (ZnO) thin films by low-pressure metal organic chemical vapor deposition (MOCVD) from Copper(II) hexafluoroacetylacetonate [Cu(C₅HF₆O₂)₂] at various substrate temperatures, between 250 and 400 °C, and pressures, between 0.6 and 2.1 Torr. Polycrystalline thin films of Cu₂O grow as single phase with [1 1 0] axis aligned perpendicular to the ZnO surface and with in-plane rotational alignment due to (2 2 0)_Cu2O(0 0 0 2)_ZnO; [0 0 1]_Cu2O[1 2¯ 1 0]_ZnO epitaxy. The resulting interface is rectifying and may be suitable for oxide-based p–n junction solar cells or diodes.     

Structural and optical properties of CuGaSe2 layers grown by the hot wall epitaxy method

Copper gallium selenide (CuGaSe₂, CGS) layers were grown by the hot wall epitaxy method. The optimum temperatures of the substrate and source for growth turned out to be 450 and 610 °C, respectively. The CGS layers were epitaxially grown along the 1 1 0 direction and consisted of Ga-rich components indicating the slight stoichiometric deviations. Based on the absorption measurement, the band-gap variation of CGS was well interpreted by the Varshni's equation. The band-gap energies at low temperatures, however, had a higher value than those of other CGS. It suggests that the band-gap increase is influenced by the slightly Ga-rich composition. From the low-temperature photoluminescence experiment, sharp and intensive free- and bound-exciton peaks were observed. By analyzing these emissions, a band diagram of the observed optical transitions was obtained. From the solar cell measurement, an 11.17% efficiency on the n-CdS/p-CGS junction was achieved.     

Atomic ordering in GaAsSb (0 0 1) grown by metalorganic vapor phase epitaxy

Epitaxial GaAsSb (0 0 1) semiconductor alloys grown by metalorganic vapor phase epitaxy exhibit several spontaneously ordered structures. A superlattice structure with three-fold ordering in the [1 1 0] direction has been previously observed by different groups. CuAu structures with (1 0 0) and (0 1 0) ordering planes have also been reported. The physical origin of CuAu ordering in III–V semiconductors has not yet been explained. In this work we report the effect of growth conditions on CuAu ordering in GaAsSb, including miscut from (0 0 1), growth rate, bismuth surfactant concentration, and growth temperature. These data point to a surface kinetic mechanism not based on dimer strain, but possibly due to one-dimensional ordering at step edges.