A study on magnetoelastic properties of Tb3 (Fe28−xCox) V1.0 (x=0, 3, 6) compounds

In this work, The magnetoelastic properties of polycrystalline samples of Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) intermetallic compounds are investigated by means of linear thermal expansion and magnetostriction measurements in the temperature range of 77–515 K under applied magnetic fields up to 1.5 T. The linear thermal expansion increases with the Co content. The well-defined anomalies observed in the linear thermal expansion coefficients for Tb₃ (Fe_28−xCo_x) V_1.0 (x=0, 3, 6) compounds are associated with the magnetic ordering temperature for x=0 and spin reorientation temperatures for x=3, 6. Below transition temperatures, the value of the longitudinal magnetostriction (λ_Pa) at 1.6 T increases with Co content.     

Magnetic structure of the La3NiGe2-type Tb3NiGe2 and Mn5Si3-type Tb5NixGe3−x (x=0 and 0.3)

We present a neutron powder diffraction investigation of the magnetic structure of La₃NiGe₂-type Tb₃NiGe₂ and Mn₅Si₃-type Tb₅Ni_xGe_3−x (x=0, 0.3) compounds. It is found that below∼135 K Tb₃NiGe₂ exhibits a commensurate b-collinear ferrimagnetic ordering with C_2h′={1, m_z, 1′×2_z, 1′×1?} magnetic point group. The Mn₅Si₃-type Tb₅Ge₃ and Tb₅Ni_0.3Ge_2.7 compounds are found to present a flat spiral type antiferromagnetic ordering at 85 and ≥89 K, respectively. The Ni for Ge substitution is found to decrease the flat spiral ordered magnetic unit cell from a×a×40c of Tb₅Ge₃ (below 40 K) down to a×a×5c for Tb₅Ni_0.3Ge_2.7 (below ∼10 K).     

Effect of Fe substitution on magnetocaloric effect in La0.7Sr0.3Mn1−xFexO3 (0.05≤x≤0.20)

We have studied the effect of Fe substitution on magnetic and magnetocaloric properties in La_0.7Sr_0.3Mn_1−xFe_xO₃ (x=0.05, 0.07, 0.10, 0.15, and 0.20) over a wide temperature range (T=10-400 K). It is shown that substitution by Fe gradually decreases the ferromagnetic Curie temperature (T_C) and saturation magnetization up to x=0.15 but a dramatic change occurs for x=0.2. The x=0.2 sample can be considered as a phase separated compound in which both short-range ordered ferromagnetic and antiferromagnetic phases coexist. The magnetic entropy change (−ΔS_m) was estimated from isothermal magnetization curves and it decreases with increase of Fe content from 4.4 J kg⁻¹ K⁻¹ at 343 K (x=0.05) to 1.3 J kg⁻¹ K⁻¹ at 105 K (x=0.2), under ΔH=5 T. The La_0.7Sr_0.3Mn_0.93Fe_0.07O₃ sample shows negligible hysteresis loss, operating temperature range over 60 K around room temperature with refrigerant capacity of 225 J kg⁻¹, and magnetic entropy of 4 J kg⁻¹ K⁻¹ which will be an interesting compound for application in room temperature refrigeration.     

Magnetocaloric effects in (Gd1−xTbx)Co2

The structures and magnetocaloric effects of (Gd_1−xTb_x)Co₂ (x=0, 0.25, 0.4, 0.5, 0.6, 0.7, 0.8, and 1) pseudobinary compounds were investigated by X-ray powder diffraction and magnetic properties measurement. The results show that the T_c of the alloy is near room temperature when X=0.6. The magnetic entropy changes of the compounds increase from 1.7 to 3.6 J/kg K with increasing the content of Tb under an applied field up to 2 T. All the compounds exhibit second order magnetic change. As a result, the values of their ΔS_M are lower than that of some large magnetocaloric effect materials.     

The effect of Mn substitution on thermoelectric properties of Ca3MnxCo4−xO9 at low temperatures

The effects of partial substitution of Mn for Co on the thermoelectric properties of Ca₃Mn_xCo_4−xO₉ (x=0, 0.03, 0.9), prepared by sol-gel process, were investigated at the temperatures from 380 K down to 5 K. The results indicate that the substitution of Mn for Co results in increase in thermopower at temperatures >∼80 K, and substantial (23-31% at 300 K) decrease in lattice thermal conductivity in the whole temperature range investigated. The temperature behavior of ZT suggests that Ca₃Mn_xCo_4−xO₉ with light Mn substitution would be a promising candidate for high-temperature thermoelectric applications.     

Magnetostriction, Curie temperature and microstructure of Tb0.29(Dy1−xPrx)0.71Fe1.97 oriented alloys

The Tb_0.29(Dy_1−xPr_x)_0.71Fe_1.97 (x=0, 0.1, 0.2 and 0.3) alloys were prepared by directional solidification method. The orientation, magnetostriction λ, Curie temperature T_c and microstructure of alloys were characterized by XRD, standard resistant strain gauge technique, VSM and SEM-EDS. The results reveal that the alloys have a preferred orientation of 〈1 1 0〉 and 〈1 1 3〉 direction when x>0. With the increase in Pr content, the T_c of alloys decreases gradually and the non-cubic phase appears, resulting in the decline of λ dramatically, from 1935.2×10⁻⁶ for x=0 to 695.9×10⁻⁶ for x=0.3 at a compressive stress of 6 MPa and a magnetic field of H=240 kA m⁻¹.     

Room temperature magnetic entropy change and magnetoresistance in La0.70(Ca0.30−xSrx)MnO3:Ag 10% (x=0.0−0.10)

The magnetic and magnetocaloric properties of polycrystalline La_0.70(Ca_0.30−xSr_x)MnO₃:Ag 10% manganite have been investigated. All compositions are crystallized in single phase orthorhombic Pbnm space group. Both, the insulator–metal transition temperature (T^IM) and Curie temperature (T_c) are observed at 298 K for x=0.10 composition. Though both T^IM and T_c are nearly unchanged with Ag addition, the MR is increased. The MR at 300 K is found to be as large as 31% with magnetic field change of 1 T, whereas it reaches up to 49% at magnetic field of 3 T for the La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample. The maximum entropy change (ΔS_Mmax) at near its T_c (300.5 K) is 7.6 J kg⁻¹ K⁻¹ upon the magnetic field change of 5 T. The La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample having good MR (31%^1 T, 49%^3 T) and reasonable change in magnetic entropy (7.6 J kg⁻¹.K⁻¹, 5 T) at 300 K can be a potential magnetic refrigerant material at ambient temperatures.     

High temperature ferromagnetism of the vacuum-annealed (In1−xFex)2O3 powders

(In_1−xFe_x)₂O₃ (x = 0.02, 0.05, 0.2) powders were prepared by a solid state reaction method and a vacuum annealing process. A systematic study was done on the structural and magnetic properties of (In_1−xFe_x)₂O₃ powders as a function of Fe concentration and annealing temperature. The X-ray diffraction and high-resolution transmission electron microscopy results confirmed that there were not any Fe or Fe oxide secondary phases in vacuum-annealed (In_1−xFe_x)₂O₃ samples and the Fe element was incorporated into the indium oxide lattice by substituting the position of indium atoms. The X-ray photoelectron spectroscopy revealed that both Fe²⁺ and Fe³⁺ ions existed in the samples. Magnetic measurements indicated that all samples were ferromagnetic with the magnetic moment of 0.49-1.73 μ_B/Fe and the Curie temperature around 783 K. The appearance of ferromagnetism was attributed to the ferromagnetic coupling of Fe²⁺ and Fe³⁺ ions via an electron trapped in a bridging oxygen vacancy.     

Structural and magnetic phase diagram and room temperature CMR effect of La1−xAgxMnO3

The study of the structural and magnetic phase diagram of the manganites La_1−xAg_xMnO₃ shows similarity with the La_1−x′Sr_x′MnO₃ series, involving a metallic ferromagnetic domain at relatively high temperature (≈300 K). The Ag-system differs from the Sr-one by a much smaller homogeneity range (x≤1/6) and the absence of charge ordering. But the most important feature of the Ag-manganites deals with the exceptionally high magnetoresistance (−25%) at room temperature under 1.2 T, that appears for the composition x=1/6. The latter is interpreted as the coincidence of the optimal double exchange condition (Mn³⁺:Mn⁴⁺=2) with T_max=300 K (maximum of the ρ(T) curve in zero field).     

Synthesis, structural and magnetic properties of spin ladder compound Ca1−xCoxCu2O3

MCu₂O₃ (M=Ca and Co) system has two-leg spin ladder structure similar to that of the prototype SrCu₂O₃ system except that the rungs are buckled with an angle of 123° and 105° for CaCu₂O₃ and CoCu₂O₃ compounds, respectively. We have synthesized powder samples of (Ca_1−xCo_x)Cu₂O₃ (x=0.00-1.00) by the solid state reaction method and their structural and magnetic properties have been investigated. All the synthesized compounds crystallize in orthorhombic structure with space group Pmmn. Lattice parameters of (Ca_1−xCo_x)Cu₂O₃ decrease with the increase in Co content. DC magnetic susceptibility χ(T) results of the end products CaCu₂O₃ and CoCu₂O₃ show antiferromagnetic transition (T_N) at 27 and 215 K, respectively. Co doping into (Ca_1−xCo_x)Cu₂O₃ enhances its T_N systematically with increasing Co concentration. The χ(T) of CoCu₂O₃ shows a broad transition with the peak temperature around 215 K and it was found to be field independent up to 90 kOe. The ambiguity concerning the transition was ruled out by recording the temperature dependent X-ray diffraction pattern on CoCu₂O₃ system, which indicated that there is no structural transition in the investigated temperature range of 115-300 K. Further, specific heat measurement on CoCu₂O₃ confirms the magnetic phase transition by the appearance of a sharp peak at 215 K.     

Structure, magneto-structural transitions and magnetocaloric properties in Ni50−xMn37+xIn13 melt spun ribbons

Melt spun Ni_50−xMn_37+xIn₁₃ (2≤x≤5) ribbons were investigated for the structure, microstructure, magneto-structural transitions and inverse magnetocaloric effect (IMCE) associated with the first-order martensitic phase transition. The influence of excess Mn in Ni site (or Ni/Mn content) on the martensite transition and the associated magnetic and magnetocaloric properties are discussed. It was found that with the increase in Mn content, the martensitic transition shifted from 325 to 240 K as x is varied from 2 to 4, and the austenite phase was stabilized at room temperature. The x=5 ribbon did not show the martensitic transition. For the x=3 ribbon, the structural and magnetic transitions are close together unlike in the x=4 ribbon in which they are far (∼60 K) apart. The zero field cooled and field cooled curves support the presence of exchange bias blocking temperature due to antiferromagnetic interactions in the ribbons. A large change in the magnetization between the martensite and austenite phases was observed for a small variation in the Ni/Mn content, which resulted in large IMCE. A large positive magnetic entropy change (ΔS_M) of 32 J/kg K at room temperature (∼ 300 K) for a field change of 5 T with a net refrigeration capacity of 64 J/kg was obtained in the Ni₄₇Mn₄₀In₁₃ ribbon.     

Magnetic entropy change in GdCo13−xSix intermetallic compounds

The magnetic entropy change in GdCo_13−xSi_x (x=3.8, 4, 4.1, and 4.2) intermetallic compounds has been investigated by means of magnetic measurements in the vicinity of their Curie temperature. It was found that the magnetic ordering temperatures decrease from 60 K at x=3.8 to 28 K for x=4.2. The magnetic entropy change is calculated from isothermal magnetization versus magnetic field at various temperatures using the Maxwell relation. As a result, the maximum magnetic entropy changes of the investigated compounds, at their Curie temperatures, decrease from 11.5 J/kg K for x=4.2 to 6.86 J/kg K for x=3.8 in a field change of 0-3 T, whereas it decreases from 5.13 J/kg K for x=4.2 to 2.60 J/kg K for x=3.8 in a field change of 0-1 T. Moreover, the maximum value of the magnetic entropy change obtained at a higher field for GdCo_13−xSi_x with x=4 (23.75 J/kg K at 5 T) is comparable to that of various types of compounds with a cubic NaZn₁₃-type structure. Finally, the maximum of the magnetic entropy change is found to decrease with increasing Si content.     

Large magnetoresistance in low temperature metallic region of manganite compounds (La0.7−2xEux)(Ca0.3Srx)MnO3 (0.05≤x≤0.15)

Magnetoresistance (MR) and magnetization (dc and ac) measurements have been carried out on the manganites, (La_0.7−2xEu_x)(Ca_0.3Sr_x)MnO₃ (0.05≤x≤0.15), in the temperature range of 5-320 K. At 5 K, an unusually large MR of almost 98% is observed in the x=0.15 sample, nearly up to fields of 4-5 T. This large high-field MR occurs in the metallic region, far below the insulator-metal transition temperature, and does not vary linearly with applied field. The unusual magnetoresistance is explained in the light of various possibilities such as phase segregation, cluster spin-glass behavior, etc.     

Synthesis and ferroelectric properties of bismuth layer-structured (Bi7−xSrx)(Fe3−xTi3+x)O21 solid solutions

Bismuth layer-structured (Bi_7−xSr_x)(Fe_3−xTi_3+x)O₂₁ (BSFT) ceramics were synthesized and the ferroelectric properties and crystal structure were investigated. X-ray powder diffraction profiles and refinement of the lattice parameters indicated single phase BSFT was obtained in the composition range 0-1.5. The lattice parameter b of BSFT remained almost constant, while a slight decrease in the lattice parameter a was observed by the Sr and Ti substitution for Bi and Fe, respectively, which indicated an increase in the orthorhombicity. The dependence of the BSFT lattice parameter on temperature implied a phase transition from the orthorhombic to the tetragonal phase, which was in good agreement with the Curie temperature. The remnant polarization P_r, of BSFT was significantly improved by the Sr and Ti substitution for Bi and Fe, and ranged from 9 to 16 μC/cm², although no remarkable variation in the coercive field E_c was observed. As a result, a well-saturated P-E hysteresis loop of BSFT ceramic was obtained at x=0.5 with a P_r of 30 μC/cm at an applied voltage of 280 kV/cm.     

Synthesis and magnetic characterization of cobalt-substituted ferrite (CoxFe3−xO4) nanoparticles

Cobalt-substituted ferrite nanoparticles were synthesized with a narrow size distribution using reverse micelles formed in the system water/AOT/isooctane. Fe:Co ratios of 3:1, 4:1, and 5:1 were used in the synthesis, obtaining cobalt-substituted ferrites (Co_xFe_3−xO₄) and some indication of γ-Fe₃O₄ when 4:1 and 5:1 Fe:Co ratios were used. Inductively coupled plasma mass spectroscopy (ICP-MS) verified the presence of cobalt in all samples. Fourier transform infrared (FTIR) showed bands at ∼560 and ∼400 cm⁻¹, characteristic of the metal–oxygen bond in ferrites. Transmission electron microscopy showed that the number median diameter of the particles was ∼3 nm with a geometric deviation of ∼0.2. X-ray diffraction (XRD) confirmed the inverse spinel structure typical of ferrites with a lattice parameter of a=8.388 Å for Co_0.61Fe_0.39O₄, which is near that of CoFe₂O₄ (a=8.394 Å). Magnetic properties were determined using a superconducting quantum interference device (SQUID). Coercivities higher than 8 kOe were observed at 5 K, whereas at 300 K the particles showed superparamagnetic behavior. The anisotropy constant was determined based on the Debye model for a magnetic dipole in an oscillating field and an expression relating χ′ and the temperature of the in-phase susceptibility peak. Anisotropy constant values in the order of ∼10⁶ erg/cm³ were determined using the Debye model, whereas anisotropy constants in the order of ∼10⁷ erg/cm³ were calculated assuming Ωτ=1 at the temperature peak of the in-phase component of the susceptibility curve as commonly done in the literature. Our analysis demonstrates that the assumption Ωτ=1 at the temperature peak of χ′ is rigorously incorrect.     

Anomalous behavior of ultrasonic properties near 50 K in Rb0.30MoO3 and Rb0.30(Mo1−xVx)O3

Depending on the temperature, the charge density wave (CDW) nonlinear conductivity of the blue bronzes A_0.30MoO₃ (A=K, Rb) shows two different regimes: a strongly damped motion above ∼50 K and motion with almost no damping below ∼50 K. In a search for an elastic signature of this CDW behaviour, we performed ultrasonic measurements on Rb_0.30MoO₃ and Rb_0.30(Mo_1−xV_x)O₃ single crystals between 4 K and 300 K. In Rb_0.30MoO₃, at T∼50 K, upon cooling, a large increase of the sound velocity is observed. The ultrasonic attenuation coefficient shows an increase down to 50 K followed by a plateau. In Rb_0.30(Mo_1−xV_x)O₃ (x=0.4 at%) the anomaly broadens and is shifted towards higher temperatures. The results are discussed in terms of CDW glass.     

Magnetic, electric, and optical functionalities of (PLZT)x(BiFeO3)1−x ferroelectric-ferromagnetic thin films

We have prepared a series of (PLZT)_x(BiFeO₃)_1−x transparent thin films with thickness of 300 nm by a thermal pyrolysis method. Only films with x≦0.10 formed a single phase of perovskite structure. The film where x=0.10 exhibited both ferromagnetic and ferroelectric properties at room temperature with spontaneous magnetization and coercive magnetic fields of 0.0027μ_B and 5500 G, respectively. The remanent electric polarization and coercive electric field for the film where x=0.10 were 3.0 μC/cm² and 24 kV/cm, respectively. Additionally, films with 0.02≦x≦0.10 showed both magneto-optical effects and the second harmonic generation of transmitted light.     

Structural and magnetic properties in Bi1−xRxFeO3 (x=0-1, R=La, Nd, Sm, Eu and Tb) polycrystalline ceramics

A series of rare-earth doped BiFeO₃ samples, Bi_1−xR_xFeO₃ (x=0-1, R=La, Nd, Sm, Eu and Tb), were prepared in this work. X-ray diffraction analysis showed that the structure of rare-earth doped BiFeO₃ was transformed from rhombohedral lattice to orthorhombic one by increasing x. The lattice constants and unit-cell volume decreased with the increasing of the doping content, while both the Néel temperature and magnetization were enhanced. A magnetic phase transition was observed at about 35 K for BiFeO₃. The variation of the magnetization with temperature depended on applied field strength and magnetizing history, which was explained according to the antiferromagnetic exchange interaction between Fe and R sites in Bi_1−xR_xFeO₃(x>0). The magnetocrystalline anisotropy contributed by Fe sublattice gave rise to a large coercivity in Bi_xNd_1−xFeO₃ with an orthorhombic structure.     

Magnetic properties and Griffiths singularity in La0.45Sr0.55 Mn1−xCoxO3

The magnetic properties and the Griffiths singularity were investigated in Mn-site doped manganites of La_0.45Sr_0.55Mn_1−xCo_xO₃ (x=0, 0.05, 0.10 and 0.15) in this work. The parent sample La_0.45Sr_0.55MnO₃ undergoes a paramagnetic-ferromagnetic transition at T_C=290 K and a ferromagnetic-antiferromagnetic transition at T_N=191 K. The doping of Co ions enhances the ferromagnetism and suppresses the antiferromagnetism. The enhanced ferromagnetism results from the fact that the Co doping enhances the Mn³⁺-Mn⁴⁺ double-exchange interaction and induces the Co²⁺-Mn⁴⁺ ferromagnetic superexchange interaction. Detailed investigation on the magnetic behavior above T_C exhibits that the Griffiths singularity takes place in this series of Mn-site doped compounds. The correlated disorder induced by the Co ionic doping, together with the phase competition from the ferromagnetic and the antiferromagnetic interactions among Mn ions, is responsible for the Griffiths singularity.