Low Density Self-Assembled InAs/GaAs Quantum Dots Grown by Metal Organic Chemical Vapour Deposition

The self-assembled InAs quantum dots （QDs） on GaAs substrates with low density （5×10^8 cm^-2） are achieved using relatively higher growth temperature and low InAs coverage by low-pressure metal-organic chemical vapour deposition. The macro-PL spectra exhibit three emission peaks at 1361, 1280 and 1204nm, corresponding to the ground level （GS）, the first excited state （ES1） and the second excited state （ES2） of the QDs, respectively, which are obtained when the GaAs capping layer is grown using triethylgallium and tertiallybutylarsine. As a result of micro-PL, only a few peaks from individual dots have been observed. The exciton-biexciton behaviour was clearly observed at low temperature.     

Growth and characterization of InAs quantum dots with low-density and long emission wavelength

The growth parameters affecting the deposition of self-assembled InAs quantum dots （QDs） on GaAs substrate by low-pressure metal-organic chemical vapor deposition （MOCVD） are reported. The low-density InAs QDs （- 5 × 10^8cm^-2） are achieved using high growth temperature and low InAs coverage. Photoluminescence （PL） measurements show the good optical quality of low-density QDs. At room temperature, the ground state peak wavelength of PL spectrum and full-width at half-maximum （FWHM） are 1361 nm and 23 meV （35 nm）, respectively, which are obtained as the GaAs capping layer grown using triethylgallium （TEG） and tertiallybutylarsine （TBA）. The PL spectra exhibit three emission peaks at 1361, 1280, and 1204 nm, which correspond to the ground state, the first excited state, and the second excited state of the ODs, respectively.     

Extremely Low Density InAs Quantum Dots with No Wetting Layer

Extremely low density InAs quantum dots （QDs） are grown by molecular beam droplet epitaxy. The gallium deposition amount is optimized to saturate exactly the excess arsenic atoms present on the GaAs substrate surface during growth, and low density InAs/GaAs QDs （4× 10^6 cm^-2） are formed by depositing 0.65 monolayers （MLs） of indium. This is much less than the critical deposition thickness （1.7 ML）, which is necessary to form InAs/GaAs QDs with the conventional Stranski-Krastanov growth mode. The narrow photoluminescence linewidth of about 24 meV is insensitive to cryostat temperatures from IO K to 250K. All measurements indicate that there is no wetting layer connecting the QDs.     

双层堆垛长波长InAs/GaAs量子点发光性质研究

研究了双层堆垛InAs/GaAs/InAs自组织量子点的生长和光致发光(PL)的物理性质。通过优化InAs淀积量、中间GaAs层厚度以及InAs量子点生长温度等生长条件,获得了室温光致发光1391～1438nm的高质量InAs量子点。研究发现对量子点GaAs间隔层实施原位退火、采用Sb辅助生长InGaAs盖层等方法可以增强高密度(2×1010 cm-2)InAs量子点的发光强度,减小光谱线宽,改善均匀性和红移发光波长。     

近红外波段InAs量子点结构与光学特性

采用分子束外延技术,分别在480,520℃的生长温度下,制备了淀积厚度2.7ML的InAs/GaAs量子点。用原子力显微镜对样品进行形貌测试和统计分布。结果表明,在相应的生长温度下,量子点密度分别为8.0×10¹⁰,5.0×10⁹cm^-2,提高生长温度有利于获得大尺寸的量子点,并且量子点按高度呈双模分布。结合光致发光谱的分析,在480℃的生长条件下,最近邻量子点之间的合并导致了量子点尺寸的双模分布;而在525℃的生长温度下,In偏析和InAs解析是形成双模分布的主要原因。     

Structural and optical properties of high-density (>10/cm) InAs QDs with varying Al(Ga)As matrix layer thickness

We have obtained high-density (>10¹¹/cm²) InAs quantum dot (QD) structures by using an Al(Ga)As matrix layer. With increase of the AlAs matrix layer thickness, the density of QDs increases a little and the luminescence intensity emitted from InAs QDs decreases. We have used a thin GaAs insertion layer (IL) for the reason of keeping InAs QDs from an aluminum intermixing towards QDs. As the thickness of GaAs IL increases, the density of QDs decreases slightly due to the reduction of the roughness of an AlAs matrix layer. However, the luminescence intensity increases with increase in the thickness of GaAs IL resulting from the efficient blocking of an aluminum intermixing towards QDs.     

High-density and narrow size-distribution InAs quantum dots formed by a modified two-step growth

We develop a modified two-step method of growing high-density and narrow size-distribution InAs/GaAs quantum dots (QDs) by molecular beam epitaxy. In the first step, high-density small InAs QDs are formed by optimizing the continuous deposition amount. In the second step, deposition is carried out with a long growth interruption for every 0.1 InAs monolayer. Atomic force microscope images show that the high-density ($\sim $5.9$\times $10$^{10}$\,cm$^{ - 2})$ good size-uniformity InAs QDs are achieved. The strong intensity and narrow linewidth (27.7\,meV) of the photoluminescence spectrum show that the QDs grown in this two-step method have a good optical quality.     

High-density and narrow size-distribution InAs quantum dots formed by a modified two-step growth

We develop a modified two-step method of growing high-density and narrow size-distribution InAs/GaAs quantum dots (QDs) by molecular beam epitaxy. In the first step, high-density small InAs QDs are formed by optimizing the continuous deposition amount. In the second step, deposition is carried out with a long growth interruption for every 0.1 InAs monolayer. Atomic force microscope images show that the high-density ($\sim $5.9$\times $10$^{10}$\,cm$^{ - 2})$ good size-uniformity InAs QDs are achieved. The strong intensity and narrow linewidth (27.7\,meV) of the photoluminescence spectrum show that the QDs grown in this two-step method have a good optical quality.     

Broadband light emitting from multilayer-stacked InAs/GaAs quantum dots

We report the effect of the GaAs spacer layer thickness on the photoluminescence(PL) spectral bandwidth of InAs/GaAs self-assembled quantum dots(QDs).A PL spectral bandwidth of 158 nm is achieved with a five-layer stack of InAs QDs which has a 11-nm thick GaAs spacer layer.We investigate the optical and the structural properties of the multilayer-stacked InAs/GaAs QDs with different GaAs spacer layer thicknesses.The results show that the spacer thickness is a key parameter affecting the multi-stacked InAs/GaAs QDs for wide-spectrum emission.     

InAs/AlAs quantum dots with InGaAs insertion layer: dependence of the indium composition and the thickness

We have systematically studied the effect of an In_xGa_1−xAs insertion layer (IL) on the optical and structural properties of InAs quantum dot (QD) structures. A high density of 9.6×10¹⁰ cm⁻² of InAs QDs with an In_0.3Ga_0.7As IL has been achieved on a GaAs (1 0 0) substrate by metal organic chemical vapor deposition. A photoluminescence line width of 25 meV from these QDs has been obtained. We attribute the high density and high uniformity of these QDs to the use of the IL. Our results show that the InGaAs IL is useful for obtaining high-quality InAs QD structures for devices with a 1.3 μm operation.     

Sb-mediated growth of high-density InAs quantum dots and GaAsSb embedding growth by MBE

Self-assembled InAs quantum dots (QDs) with high-density were grown on GaAs(0 0 1) substrates by antimony (Sb)-mediated molecular beam epitaxy technique using GaAsSb/GaAs buffer layer and InAsSb wetting layer (WL). In this Sb-mediated growth, many two-dimensional (2D) small islands were formed on those WL surfaces. These 2D islands provide high step density and suppress surface migration. As the results, high-density InAs QDs were achieved, and photoluminescence (PL) intensity increased. Furthermore, by introducing GaAsSb capping layer (CL), higher PL intensity at room temperature was obtained as compared with that InGaAs CL.     

InAs/GaAs单量子点中电子/空穴自旋弛豫

利用分子束外延制备了三种类型量子点样品,它们分别是:未掺杂样品、n型Si调制掺杂样品和p型Be调制掺杂样品。在5 K温度下,采用共聚焦显微镜系统,测量了单量子点的光致发光谱和时间分辨光谱, 研究了单量子点中三种类型激子(本征激子、负电荷激子和正电荷激子)的电子/空穴自旋翻转时间。它们的自旋翻转时间常数分别为: 本征激子的自旋翻转时间约16 ns, 正电荷激子中电子的自旋翻转时间约2 ns, 负电荷激子中空穴的自旋翻转时间约50 ps。     

1.5 μm emission from InAs quantum dots with InGaAsSb strain-reducing layer grown on GaAs substrates

InGaAsSb strain-reducing layers (SRLs) are applied to cover InAs quantum dots (QDs) grown on GaAs substrates. The compressive strain induced in InAs QDs from the GaAs is reduced due to the tensile strain induced by the InGaAsSb SRL, because the lattice constant of InGaAsSb is closer to InAs lattice constant than that of GaAs, resulting in a significant red shift of photoluminescence peaks of the InAs QDs. The emission wavelength from InAs QDs can be controlled by changing the Sb composition of the InGaAsSb SRL. The 1.5 μm band emissions were achieved in the sample with an InGaAsSb SRL whose Sb compositions were above 0.3. The calculation of the electron and the hole wave functions using the transfer matrix method indicates that the electron and the hole were localized around InAs QDs and InGaAsSb SRL.     

Effect of thermal annealing in the microstructural and the optical properties of uncapped InAs quantum dots grown on GaAs buffer layers

The effect of thermal annealing on self-assembled uncapped InAs/GaAs quantum dots (QDs) has been investigated using transmission electron microscopy (TEM) and photoluminescence (PL) measurements. The TEM images showed that the lateral sizes and densities of the InAs QDs were not changed significantly up to 650 °C. When the InAs/GaAs QDs were annealed at 700 °C, while the lateral size of the InAs QDs increased, their density decreased. The InAs QDs disappeared at 800 °C. PL spectra showed that the peaks corresponding to the interband transitions of the InAs QDs shifted slightly toward the high-energy side, and the PL intensity decreased with increasing annealing temperature. These results indicate that the microstructural and the optical properties of self-assembled uncapped InAs/GaAs can be modified due to postgrowth thermal annealing.     

Ordered InAs Quantum Dots with Controllable Periods Grown on Stripe-Patterned GaAs Substrates

GaAs （001） substrates are patterned by electron beam lithography and wet chemical etching to control the nucleation of lnAs quantum dots （QDs）. InAs dots are grown on the stripe-patterned substrates by solid source molecular beam epitaxy. A thick buffer layer is deposited on the strip pattern before the deposition of InAs. To enhance the surface diffusion length of the In atoms, InAs is deposited with low growth rate and low As pressure. The AFM images show that distinct one-dimensionally ordered InAs QDs with homogeneous size distribution are created, and the QDs preferentiMly nucleate along the trench. With the increasing amount of deposited InAs and the spacing of the trenches, a number of QDs are formed beside the trenches. The distribution of additional QDs is long-range ordered, always along the trenchs rather than across the spacing regions.     

InAs/GaAs量子点1.3 μm单光子发射特性

采用双层耦合量子点的分子束外延生长技术生长了InAs/GaAs量子点样品,把量子点的发光波长成功地拓展到1.3 μm.采用光刻的工艺制备了直径为3 μm的柱状微腔,提高了量子点荧光的提取效率.在低温5 K下,测量得到量子点激子的荧光寿命约为1 ns;单量子点荧光二阶关联函数为0.015,显示单量子点荧光具有非常好的单光子特性;利用迈克耳孙干涉装置测量得到单光子的相干时间为22 ps,对应的谱线半高全宽度为30 μeV,且荧光谱线的线型为非均匀展宽的高斯线型.     

Controlling the spontaneous emission rate of single quantum dots in a two-dimensional photonic crystal

We observe large spontaneous emission rate modification of individual InAs quantum dots (QDs) in a 2D photonic crystal with a modified, high-Q single-defect cavity. Compared to QDs in a bulk semiconductor, QDs that are resonant with the cavity show an emission rate increase of up to a factor of 8. In contrast, off-resonant QDs indicate up to fivefold rate quenching as the local density of optical states is diminished in the photonic crystal. In both cases, we demonstrate photon antibunching, showing that the structure represents an on-demand single photon source with a pulse duration from 210 ps to 8 ns. We explain the suppression of QD emission rate using finite difference time domain simulations and find good agreement with experiment.     

CdTe量子点荧光猝灭法测定微量铅

以CdTe量子点作为荧光探针,基于荧光猝灭法对铅进行了定量检测,考察了缓冲溶液体系、量子点浓度、反应时间等多种因素的影响。实验结果表明,在pH 7.5的0.2mol/L Na2HPO4-NaH2PO4缓冲液中,反应时间为10min,铅浓度为2.0×10-6—3.5×10-5mol/L范围时,其线性回归方程为ΔF=26.35+11.47C(×10-6mol/L),相关系数和检出限分别为0.9991和1.8×10-8mol/L。该方法灵敏度高,为铅的测定提供了新的方法。     

Formation process for and strain effect in InAs quantum dots grown on GaAs substrates by using molecular beam epitaxy

Reflection high-energy electron diffraction (RHEED) and atomic force microscopy (AFM) measurements were used to investigate the dependences of the formation process and the strain on the As/In ratio and the substrate temperature of InAs quantum dots (QDs) grown on GaAs substrates by using molecular beam epitaxy. The thickness of the InAs wetting layer and the shape and the size of the InAs QDs were significantly affected by the As/In ratio and the substrate temperature. The strains in the InAs layer and the GaAs substrate were studied by using RHEED patterns. The magnitude in strain of the InAs QDs formed at a low substrate temperature was larger than that in InAs QDs grown at high substrate temperature. The present results can help to improve the understanding of the formation process and the strain effect in InAs QDs.     

Optical properties of 1.3-μm InAs/GaAs quantum dots grown by metal organic chemical vapor deposition

The optical properties of self-assembled InAs quantum dots （QDs） on GaAs substrate grown by metalorganic chemical vapor deposition （MOCVD） are reported. Photoluminescence （PL） measurements prove the good optical quality of InAs QDs, which axe achieved using lower growth temperature and higher InAs coverage. At room temperature, the ground state peak wavelength of PL spectrum and full-width at half-maximum （FWHM） are 1305 nm and 30 meV, respectively, which are obtained as the QDs are finally capped with 5-nm In0.06Ga0.94As strain-reducing layer （SRL）. The PL spectra exhibit two emission peaks at 1305 and 1198 nm, which correspond to the ground state （GS） and the excited state （ES） of the QDs, respectively.