A Co‐MOF with a (4,4)‐connected binodal two‐dimensional topology: synthesis,structure and photocatalytic properties

The Co‐MOF poly[[diaqua{μ₄‐1,1,2,2‐tetrakis[4‐(1H‐1,2,4‐triazol‐1‐yl)phenyl]ethylene‐κ⁴N:N′:N′′:N′′′}cobalt(II)] benzene‐1,4‐dicarboxylic acid benzene‐1,4‐dicarboxylate], {[Co(C₃₄H₂₄N₁₂)(H₂O)₂](C₈H₄O₄)·C₈H₆O₄}_n or {[Co(ttpe)(H₂O)₂](bdc)·(1,4‐H₂bdc)}_n, (I), was synthesized by the hydrothermal method using 1,1,2,2‐tetrakis[4‐(1H‐1,2,4‐triazol‐1‐yl)phenyl]ethylene (ttpe), benzene‐1,4‐dicarboxylic acid (1,4‐H₂bdc) and Co(NO₃)₂·6H₂O, and characterized by single‐crystal X‐ray diffraction, IR spectroscopy, powder X‐ray diffraction (PXRD), luminescence, optical band gap and valence band X‐ray photoelectron spectroscopy (VB XPS). Co‐MOF (I) shows a (4,4)‐connected binodal two‐dimensional topology with a point symbol of {4⁴·6²}{4⁴·6²}. The two‐dimensional networks capture free neutral 1,4‐H₂bdc molecules and bdc^2? anions, and construct a three‐dimensional supramolecular architecture via hydrogen‐bond interactions. MOF (I) is a good photocatalyst for the degradation of methylene blue and rhodamine B under visible‐light irradiation and can be reused at least five times.     

Synthesis,structure and photocatalytic degradation of organic dyes of a copper(II) metal–organic framework (Cu–MOF) with a 4‐coordinated three‐dimensional CdSO4 topology

Metal–organic frameworks (MOFs) have attracted much interest in the fields of gas separation and storage, catalysis synthesis, nonlinear optics, sensors, luminescence, magnetism, photocatalysis gradation and crystal engineering because of their diverse properties and intriguing topologies. A Cu–MOF, namely poly[[(μ₂‐succinato‐κ²O:O′){μ₂‐tris[4‐(1,2,4‐triazol‐1‐yl)phenyl]amine‐κ²N:N′}copper(II)] dihydrate], {[Cu(C₄H₄O₄)(C₂₄H₁₈N₁₀)]·2H₂O}_n or {[Cu(suc)(ttpa)]·2H₂O}_n, (I), was synthesized by the hydrothermal method using tris[4‐(1,2,4‐triazol‐1‐yl)phenyl]amine (ttpa) and succinate (suc^2?), and characterized by IR, powder X‐ray diffraction (PXRD), luminescence, optical band gap and valence band X‐ray photoelectron spectroscopy (VB XPS). Cu–MOF (I) shows a twofold interpenetrating 4‐coordinated three‐dimensional CdSO₄ topology with point symbol {6⁵·8}. It presents good photocatalytic degradation of methylene blue (MB) and rhodamine B (RhB) under visible‐light irradiation. A photocatalytic mechanism was proposed and confirmed.     

Enhanced Photocatalytic Activity of MIL‐125 by Post‐Synthetic Modification with CrIII and Ag Nanoparticles

NH₂‐MIL‐125, [Ti₈O₈(OH)₄(bdc‐NH₂)₆] (bdc^2?=1,4‐benzene dicarboxylate) is a highly porous metal–organic framework (MOF) that has a band gap lying within the ultraviolet region at about 2.6 eV. The band gap may be reduced by a suitable post‐synthetic modification of the nanochannels using conventional organic chemistry methods. Here, it is shown that the photocatalytic activity of NH₂‐MIL‐125 in the degradation of methylene blue under visible light is remarkably augmented by post‐synthetic modification with acetylacetone followed by Cr^III complexation. The latter metal ion extends the absorption from the ultraviolet to the visible light region (band gap 2.21 eV). The photogenerated holes migrate from the MOF’s valence band to the Cr^III valence band, promoting the separation of holes and electrons and increasing the recombination time. Moreover, it is shown that the MOF’s photocatalytic activity is also much improved by doping with Ag nanoparticles, formed in situ by the reduction of Ag⁺ with the acetylacetonate pendant groups (the resulting MOF band gap is 2.09 eV). Presumably, the Ag nanoparticles are able to accept the MOF’s photogenerated electrons, thus avoiding electron–hole recombination. Both, the Cr‐ and Ag‐bearing materials are stable under photocatalytic conditions. These findings open new avenues for improving the photocatalytic activity of MOFs.     

High Compression‐Induced Conductivity in a Layered Cu–Br Perovskite

We show that the onset pressure for appreciable conductivity in layered copper‐halide perovskites can decrease by ca. 50 GPa upon replacement of Cl with Br. Layered Cu–Cl perovskites require pressures >50 GPa to show a conductivity of 10^?4 S cm^?1, whereas here a Cu–Br congener, (EA)₂CuBr₄ (EA=ethylammonium), exhibits conductivity as high as 2×10^?3 S cm^?1 at only 2.6 GPa, and 0.17 S cm^?1 at 59 GPa. Substitution of higher‐energy Br 4p for Cl 3p orbitals lowers the charge‐transfer band gap of the perovskite by 0.9 eV. This 1.7 eV band gap decreases to 0.3 eV at 65 GPa. High‐pressure X‐ray diffraction, optical absorption, and transport measurements, and density functional theory calculations allow us to track compression‐induced structural and electronic changes. The notable enhancement of the Br perovskite's electronic response to pressure may be attributed to more diffuse Br valence orbitals relative to Cl orbitals. This work brings the compression‐induced conductivity of Cu‐halide perovskites to more technologically accessible pressures.     

The Effect of pH Values on the Synthesis,Microstructure and Photocatalytic Activity of Ce‐Bi2O3 by a Two‐Step Hydrothermal Method

In this study, the effect of pH values on the microstructure and photocatalytic activity of Ce‐Bi₂O₃ under visible light irradiation was investigated in detail. In alkaline condition (e.g. pH = 9), the as‐prepared Ce‐Bi₂O₃ exhibited an agglomerated status and mesoporous structures without a long‐range order. While in weak acid condition (e.g. pH = 5), the Ce‐Bi₂O₃ exhibited a best morphology with irregular nanosheets. Correspondingly, it possessed largest surface area (24.641 m² g^?1) and pore volume (9.825E‐02 cm³ g^?1). These unique nanosheets can offer an attachment for pollutant molecules and reduce the distance of electron immigration from inner to surface, thus facilitating the separation of photoelectron and hole pairs. Compared with the pure Bi₂O₃, the band gap of Ce‐Bi₂O₃ prepared at different pH was much lower. Among them, the band gap of Ce‐Bi₂O₃ (pH of 5) was lowest (2.61 eV). Ce‐Bi₂O₃ (pH of 5) exhibited as tetragonal crystal with the bismuth oxide in the form of the composites, which could reduce the band gap width or suppress the charge‐carrier recombination, subsequently possessing great photocatalytic activity for acid orange II under visible light irradiation. After 2 h degradation under visible light, the degradation rate of acid Orange II was up to 96.44% by Ce‐Bi₂O₃ prepared at pH 5. Overall, it can be concluded that the pH values had effects on the microstructure and photocatalytic activity of Ce‐Bi₂O₃ catalysts.     

A Polypyridyl‐Based Layered Complex as Dual‐Functional Co‐catalyst for Photo‐Driven Organic Dyes Degradation and Water Splitting

With the ever‐increasing concerns on environmental pollution and energy crisis, it is of great urgency to develop high‐performance photocatalyst to eliminate organic pollutants from wastewater and produce hydrogen via water splitting. Herein, a polypyridyl‐based mixed covalent Cu^I/II complex with triangular {Cu₃} and rhombic {Cu₂Cl₄} subunits alternately extended by mixed SCN^– and Cl^– heterobridges [Cu₄(DNP)(SCN)Cl₄]_n ( 1 ) [DNP = 2,6‐bis(1,8‐naphthyridine‐2‐yl)pyridine] was solvothermally synthesized and employed as a dual‐functional co‐photocatalyst. Resulting from a narrowed band‐gap of 1.07 eV with suitable redox potential and unsaturated Cu^I/II sites, the complex together with H₂O₂ can effectively degrade Rhodamine B and methyl orange up to 87.4 and 88.2 %, respectively. Meanwhile, the complex mixed with H₂PtCl₆ can also accelerate the photocatalytic water splitting in the absence of a photosensitizer with the hydrogen production rate of 27.5 μmol · g^–1 · h^–1. These interesting findings may provide informative hints for the design of the multiple responsive photocatalysts.     

Synthesis of the Dy: SrMoO4 with High Photocatalytic Activity under Visible Light Irradiation

Dysprosium (Dy)‐doping SrMoO₄ (with different molar ratio of Dy/Sr = 0/100, 10/100, 15/100 and 20/100) have been synthesized by high temperature thermal decomposition of metal–organic salt in organic solvent with a high boiling point. Their structures, morphology, and optical properties were characterized by X‐ray diffraction (XRD), high‐resolution tuning electron microscopy ((HR)TEM), X‐ray photo‐electron spectroscopy (XPS), and UV–vis diffuse reflectance spectroscopy (UV–vis DRS). Using this method, the pure phase, nano‐size, and low band gap of SrMoO₄ sample are obtained. The results shows that the size of as‐synthesized SrMoO₄ nanoparticles was about 200 nm. The band gap of Dy‐doped SrMoO₄ ranges from 3.76–3.90 eV, and decreases with increasing Dy concentration. The photocatalytic performance of as‐syntheszied products were determined from the degradation of methylene blue (MB) by UV–vis light irradiation. The 15 mol%Dy‐doped SrMoO₄ sample shows the best performance for photocatalytic degradation of methyl blue of nearly 100% in 120 min under visible irradiation, which is higher than most of those reported before. The present work is meaningful for revealing the underlying mechanism in photocatalyst and improving the photocatalytic performance.     

On‐surface Synthesis of a Semiconducting 2D Metal–Organic Framework Cu3(C6O6) Exhibiting Dispersive Electronic Bands

A 2D metal–organic framework (2D‐MOF) was formed on a Cu(111) substrate using benzenehexol molecules. By means of a combination of scanning tunneling microscopy and spectroscopy, X‐ray photoelectron spectroscopy and density‐functional theory, the structure of the 2D‐MOF is determined to be Cu₃(C₆O₆), which is stabilized by O–Cu–O bonding motifs. We find that upon adsorption on Cu(111), the 2D‐MOF features a semiconductor band structure with a direct band gap of 1.5 eV. The O–Cu–O bonds offer efficient charge delocalization, which gives rise to a highly dispersive conduction band with an effective mass of 0.45 m_e at the band bottom, implying a high electron mobility in this material.     

Syntheses,Crystal Structures,and Photocatalytic Activities of Three Copper Coordination Polymers Based on Bis(1H‐imidazol‐4‐yl)benzene/3‐(2‐Pyridyl)pyrazole

Three copper(II) coordination polymers (CuCPs), namely, [Cu_0.5(1,4‐bib)(SO₄)_0.5]_n ( 1 ), {[Cu(1,3‐bib)₂(H₂O)] · SO₄ · H₂O}_n ( 2 ), and [Cu(bpz)(SO₄)_0.5]_n ( 3 ), were assembled from the reaction of three N‐donors [1,4‐bib = 1,4‐bis(1H‐imidazol‐4‐yl)benzene, 1,3‐bib = 1,3‐bis(1H‐imidazol‐4‐yl)benzene, and Hbpz = 3‐(2‐pyridyl)pyrazole] with copper sulfate under hydrothermal conditions. Their structures were determined by single‐crystal X‐ray diffraction analyses and further characterized by elemental analyses (EA), IR spectroscopy, powder X‐ray diffraction (PXRD), and thermogravimetric analyses (TGA). Structure analyses reveal that complex 1 is a 3D 6‐connected {4¹² · 6³}‐ pcu net, complex 2 is a fourfold 3D 4‐connected 6⁶‐ dia net, whereas complex 3 is a 1D snake‐like chain, which further expanded into 3D supramolecular architectures with the help of C–H ··· O hydrogen bonds. Moreover, the photocatalytic tests demonstrate that the obtained CuCPs are photocatalysts in the degradation of MB with the efficiency is 86.4 % for 1 , 75.3 % for 2 , and 91.3 % for 3 after 2 h, respectively.     

(1‐Butyl‐4‐methyl‐pyridinium)[Cu(SCN)2]: A Coordination Polymer and Ionic Liquid

The compound (C₄C₁py)[Cu(SCN)₂], (C₄C₁py=1‐Butyl‐4‐methyl‐pyridinium), which can be obtained from CuSCN and the ionic liquid (C₄C₁py)(SCN), turns out to be a new organic–inorganic hybrid material as it qualifies both, as a coordination polymer and an ionic liquid. It features linked [Cu(SCN)₂]^? units, in which the thiocyanates bridge the copper ions in a μ_1,3‐fashion. The resulting one‐dimensional chains run along the a axis, separated by the C₄C₁py counterions. Powder X‐ray diffraction not only confirms the single‐crystal X‐ray structure solution but proves the reformation of the coordination polymer from an isotropic melt. However, the materials shows a complex thermal behavior often encountered for ionic liquids such as a strong tendency to form a supercooled melt. At a relatively high cooling rate, glass formation is observed. When heating this melt in differential scanning calorimetry (DSC) and temperature‐dependent polarizing optical microscopy (POM), investigations reveal the existence of a less thermodynamically stable crystalline polymorph. Raman measurements conducted at 10 and 100 °C point towards the formation of polyanionic chain fragments in the melt. Solid‐state UV/Vis spectroscopy shows a broad absorption band around 18 870 cm^?1 (530 nm) and another strong one below 20 000 cm^?1 (<500 nm). The latter is attributed to the d(Cu^I)→π*(SCN)‐MLCT (metal‐to‐ligand charge transfer) transition within the coordination polymer yielding an energy gap of 2.4 eV. At room temperature and upon irradiation with UV light, the material shows a weak fluorescence band at 15 870 cm^?1 (630 nm) with a quantum efficiency of 0.90(2) % and a lifetime of 131(2) ns. Upon lowering the temperature, the luminescence intensity strongly increases. Simultaneously, the band around 450 nm in the excitation spectrum decreases.     

Synthesis,characterization and photocatalytic application of TiO2/magnetic graphene for efficient photodegradation of crystal violet

A magnetized nano‐photocatalyst based on TiO₂/magnetic graphene was developed for efficient photodegradation of crystal violet (CV). Scanning electron microscopy, X‐ray diffraction, energy‐dispersive X‐ray spectroscopy and elemental mapping were used to characterize the prepared magnetic nano‐photocatalyst. The photocatalytic activity of the synthesized magnetic nano‐photocatalyst was evaluated using the decomposition of CV as a model organic pollutant under UV light irradiation. The obtained results showed that TiO₂/magnetic graphene exhibited much higher photocatalytic performance than bare TiO₂. Incorporation of graphene enhanced the activity of the prepared magnetic nano‐photocatalyst. TiO₂/magnetic graphene can be easily separated from an aqueous solution by applying an external magnetic field. Effects of pH, magnetized nano‐photocatalyst dosage, UV light irradiation time, H₂O₂ amount and initial concentration of dye on the photodegradation efficiency were evaluated and optimized. Efficient photodegradation (>98%) of the selected dye under optimized conditions using the synthesized nano‐photocatalyst under UV light irradiation was achieved in 25 min. The prepared magnetic nano‐photocatalyst can be used in a wide pH range (4–10) for degradation of CV. The effects of scavengers, namely methanol (OH^? scavenger), p‐benzoquinone (O₂^?? scavenger) and disodium ethylenediaminetetraacetate (hole scavenger), on CV photodegradation were investigated.     

硼铈共掺杂纳米TiO2光催化降解三氯杀螨醇和菊酯类农药

采用溶胶-凝胶法在钛酸丁酯水解过程引入硼酸、硝酸铈,制备具有光催化活性的硼铈共掺杂纳米二氧化钛（TiO2）,经XRD、TEM、FT-IR、UV-Vis-DRS表征晶体结构,在日光灯照射下,光催化降解三氯杀螨醇、高氟氯氰菊酯、氟戊菊酯农药。结果表明：硼铈共掺杂的TiO2只有锐钛矿型,而纯的或掺铈的TiO2有含有锐钛矿型、金红石相和少量板钛矿型,UV-Vis-DRS测定结果表明硼铈共掺杂的TiO2禁带宽度变小,硼铈共掺杂的TiO2在可见光区吸光度高于掺杂铈和不掺杂的TiO2,在420nm~850nm有强的吸收;在同样光照下对三氯杀螨醇、高氟氯氰菊酯、氟戊菊酯的降解试验证明硼铈共掺杂纳米TiO2的光催化活性高于不掺杂或只掺杂铈的TiO2。     

Synthesis,Structure, and Physical Properties of 5,7,14,16‐Tetraphenyl‐8:9,12:13‐bisbenzo‐hexatwistacene

A novel compound, 5,7,14,16‐tetraphenyl‐8:9,12:13‐bisbenzo‐hexatwistacene ( TBH ), has been successfully synthesized through a retro‐Diels–Alder reaction. Single‐crystal structure analysis indicated that TBH has a twisted configuration with a torsion angle of 27.34°. The HOMO–LUMO gap of TBH calculated from the difference between the half‐wave redox potentials (E_1/2^ox=+0.40 eV and E_1/2^red=?1.78 eV) is 2.18 eV, which is in good agreement with the band gap (2.19 eV) derived from the UV/Vis absorption data. In addition, organic light‐emitting devices using TBH as emitter have been fabricated. The results revealed that TBH is a promising red light‐emitting candidate for applications in organic light‐emitting diodes.     

Sol‐Gel Synthesis and Photocatalytic Study of Visible Light Active N‐Doped KSbWO6

KSbWO₆ was prepared by sol‐gel method. N‐doped KSbWO₆ (KSbWO_6–xN_x) was obtained by heating KSbWO₆ and urea at 400 °C. Both the compounds are characterized by powder X‐ray diffraction (XRD), TEM, SEM‐EDS, X‐ray photo electronic spectroscopy (XPS), and UV/Vis diffuse reflectance spectroscopy (UV‐DRS). A shift in the peak positions of powder XRD and XPS spectra was observed. The band gap energy (E_g) of KSbWO₆ and N‐doped KSbWO₆ was obtained from their diffused reflectance spectra.E_g was reduced from 3.17 eV to 2.56 eV upon nitrogen doping in KSbWO₆. The reduction of the E_g is attributed to the lifting of valence band of N‐doped KSbWO₆, due to the mixing of O 2p states with N 2p states. The photocatalytic activity of both the samples was studied by degradation of methylene blue (MB). The nitrogen doped KSbWO₆ shows higher photocatalytic activity compared to that of KSbWO₆.     

Synthesis,Characterization and Photocatalytic Activity of Mg‐Impregnated ZnO–SnO2 Coupled Nanoparticles

ZnO–SnO₂ nanoparticles were prepared by coprecipitation method; then Mg, with different molar ratios and calcination temperatures, was loaded on the coupled nanoparticles by impregnation method. The synthesized nanoparticles were characterized by X‐ray diffraction (XRD), field emission scanning electron microscopy (FESEM), energy dispersive X‐ray spectroscopy (EDX), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), and Brunauer–Emmett–Teller (BET) techniques. Based on XRD results, the ZnO–SnO₂ and Mg/ZnO–SnO₂ nanoparticles were made of ZnO and SnO₂ nanocrystallites. According to DRS spectra, the band gap energy value of 3.13 and 3.18 eV were obtained for ZnO–SnO₂ and Mg/ZnO–SnO₂ nanoparticles, respectively. BET analysis revealed a Type III isotherm with a microporous structure and surface area of 32.051 and 49.065 m² g^?1 for ZnO–SnO₂ and Mg/ZnO–SnO₂, respectively. Also, the spherical shape of nanocrystallites was deduced from TEM and FESEM images. The photocatalytic performance of pure ZnO–SnO₂ and Mg/ZnO–SnO₂ was analyzed in the photocatalytic removal of methyl orange (MO). The results indicated that Mg/ZnO–SnO₂ exhibited superior photocatalytic activity to bare ZnO–SnO₂ photocatalyst due to high surface area, increased MO adsorption and larger band gap energy. Maximum photocatalytic activity of Mg/ZnO–SnO₂ nanoparticles was obtained with 0.8 mol% Mg and calcination temperature of 350°C.     

Synthesis of W‐doped TiO2 by low‐temperature hydrolysis: Effects of annealing temperature and doping content on the surface microstructure and photocatalytic activity

A series of tungsten‐doped Titania photocatalysts were synthesized using a low‐temperature method. The effects of dopant concentration and annealing temperature on the phase transitions, crystallinity, electronic, optical, and photocatalytic properties of the resulting material were studied. The X‐ray patterns revealed that the doping delays the transition of anatase to rutile to a high temperature. A new phase W_yTi_1‐yO₂ appeared for 5.00 wt% W‐TiO₂ annealed at 900 °C. Raman and diffuse reflectance UV–Vis spectroscopy showed that band gap values decreased slightly up to 700 °C. X‐ray photoelectron spectroscopy showed that surface species viz. Ti³⁺, Ti⁴⁺, O^2?, oxygen‐vacancies, and adsorbed OH groups vary depending on the preparation conditions. The photocatalytic activity was evaluated via the degradation of methylene blue using LED white light. The degradation rate was affected by the percentage of dopants. The best photocatalytic activity was achieved with the sample labeled 5.00 wt% W‐TiO₂ annealed at 700 °C.     

Dye degradation studies of Mo‐doped TiO2 thin films developed by reactive sputtering

TiO₂ thin films with various Mo concentrations have been deposited on glass and n‐type silicon (100) substrates by this radio‐frequency (RF) reactive magnetron sputtering at 400°C substrate temperature. The crystal structure, surface morphology, composition, and elemental oxidation states of the films have been analyzed by using X‐ray diffraction, field emission scanning electron microscopy, atomic force microscopy, and X‐ray photoelectron spectroscopy, respectively. Ultraviolet‐visible spectroscopy has been used to investigate the degradation, transmittance, and absorption properties of doped and undoped TiO₂ films. The photocatalytic degradation activity of the films was evaluated by using methylene blue under a light intensity of 100 mW cm⁻². The X‐ray diffraction patterns show the presence of anatase phase of TiO₂ in the developed films. X‐ray photoelectron spectroscopy studies have confirmed that Mo is present only as Mo⁶⁺ ions in all films. The Mo/TiO₂ band gap decreases from ~3.3 to 3.1 eV with increasing Mo dopant concentrations. Dye degradation of ~60% is observed in Mo/TiO₂ samples, which is much higher than that of pure TiO₂.     

A three‐dimensional cadmium coordination polymer based on 1,4‐bis(1,2,4‐triazol‐1‐yl)but‐2‐ene and benzene‐1,3,5‐tricarboxylic acid

The Cd^II three‐dimensional coordination poly[[[μ₄‐1,4‐bis(1,2,4‐triazol‐1‐yl)but‐2‐ene]bis(μ₃‐5‐carboxybenzene‐1,3‐dicarboxylato)dicadmium(II)] dihydrate], {[Cd₂(C₉H₄O₆)₂(C₈H₁₀N₆)]·2H₂O}_n , (I), has been synthesized by the hydrothermal reaction of Cd(NO₃)₂·4H₂O, benzene‐1,3,5‐tricarboxylic acid (1,3,5‐H₃BTC) and 1,4‐bis(1,2,4‐triazol‐1‐yl)but‐2‐ene (1,4‐btbe). The IR spectrum suggests the presence of protonated carboxylic acid, deprotonated carboxylate and triazolyl groups. The purity of the bulk sample was confirmed by elemental analysis and X‐ray powder diffraction. Single‐crystal X‐ray diffraction analysis reveals that the Cd^II ions adopt a five‐coordinated distorted trigonal–bipyramidal geometry, coordinated by three O atoms from three different 1,3,5‐HBTC²⁻ ligands and two N atoms from two different 1,4‐btbe ligands; the latter are situated on centres of inversion. The Cd^II centres are bridged by 1,3,5‐HBTC²⁻ and 1,4‐btbe ligands into an overall three‐dimensional framework. When the Cd^II centres and the tetradentate 1,4‐btbe ligands are regarded as nodes, the three‐dimensional topology can be simplified as a binodal 4,6‐connected network. Thermogravimetric analysis confirms the presence of lattice water in (I). Photoluminescence studies imply that the emission of (I) may be ascribed to intraligand fluorescence.     

Enhanced visible‐light‐driven photocatalytic activity of F doped reduced graphene oxide ‐ Bi2WO6 photocatalyst

The reduced graphene oxide‐Bi₂WO₆ (rGO‐BWO) photocatalysts with the different R_F/O values (molar ratio of the F molar mass and the O's molar mass of Bi₂WO₆) had been successfully synthesized via one‐step hydrothermal method. The F‐doped rGO‐BWO samples were characterized by X‐ray diffraction patterns (XRD), field‐emission scanning electron microscopy (FE‐ESEM), transmission electron microscopy (TEM), Brunauer–Emmett–Teller surface area (BET), X‐ray photoelectron spectroscopy (XPS) and UV–vis diffuse reflectance spectra (DRS). The results indicate that F^? ions had been successfully doped into rGO‐BWO samples. With the increasing of the R_F/O values from 0 to 2%, the evident change of the morphology and the absorption edges of F‐doped rGO‐BWO samples and the photocatalytic activities had been enhanced. Moreover, the photocatalytic activity of F‐doped rGO‐BWO with R_F/O = 0.05 were better than rGO‐BWO and the other F‐doped rGO‐BWO under 500 W Xe lamp light irradiation. The enhanced photocatalytic activity can be attributed to the morphology of the intact microsphere that signify the bigger specific surface area for providing more possible reaction sites for the adsorption–desorption equilibrium of photocatalytic reaction, the introduction of F^? ions that may cause the enhancement of surface acidity and creation of oxygen vacancies under visible light irradiation, the narrower band gap which means needing less energy for the electron hole pair transition.