Interfacial effects in organophilic montmorillonite–poly(ϵ‐caprolactone) nanocomposites

In the last few years much progress has been made in the development of hybrid polymer–inorganic filler nanocomposites. Nevertheless, many questions remain. The comprehension of the structure and the interactions at the polymer–nanofiller interface are crucial to foresee and control the properties of nanocomposites. Because of the high surface ratio of the inorganic nanofiller, the interface is expected to have a prevailing role in determining the nanocomposite properties. In this study we use X‐ray photoelectron spectroscopy (XPS) as a tool for the surface characterization of an organophilic montmorillonite/poly(ε‐caprolactone) exfoliated nanocomposite. The XPS core levels of the nanocomposite have been compared with those obtained from its precursors, and analyzed as reference compounds to evaluate eventual differences attributable to the polymer–nanofiller interfacial interactions. The XPS investigation has allowed us to propose a qualitative model of possible interface interactions between poly(ε‐caprolactone) and the organo‐modified montmorillonite. The model is substantiated by Fourier transform infrared spectroscopy (FTIR). © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3907–3919, 2004     

Complexation of linear and poly(ethylene oxide)‐grafted poly(methacryl oxyethyl trimethylammonium chloride) with poly(ethylene oxide‐block‐sodium methacrylate)

The interactions between oppositely charged polyelectrolytes were studied in saline aqueous solutions as functions of the temperature and the salt and polymer concentrations. The polyanion was a diblock copolymer composed of a poly(ethylene oxide) block and a poly(sodium methacrylate) block. Two polycations were used, the homopolymer poly(methacryl oxyethyl trimethylammonium chloride) and its poly(ethylene oxide)‐grafted analogue. By dynamic light scattering and turbidity measurements, it was observed that the salt concentration, temperature, and counterion size had a significant effect on the formation of the polymer complexes in aqueous solutions. At a fixed salt concentration and a fixed temperature, it was possible to form completely soluble complexes of an ionic polymer in aqueous solutions between poly(ethylene oxide)‐grafted poly(methacryl oxyethyl trimethylammonium chloride)and the polyanion with a poly(ethylene oxide) block at a 1:1 anion/cation ratio. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1904–1914, 2003     

Poly(thieno[3,4‐b]‐1,4‐oxathiane) and poly(3,4‐ethylenedioxythiophene‐co‐thieno[3,4‐b]‐1,4‐oxathiane)/poly(styrene sulfonic sodium): Preparation,characterization, and optoelectronic performance

In this work, the asymmetrical analog of 3,4‐ethylenedioxythiophene (EDOT), thieno[3,4‐b]‐1,4‐oxathiane (EOTT), was synthesized and chemically polymerized first in aqueous solution using poly(styrene sulfonic sodium) (PSS) as the polyelectrolyte to yield poly(thieno[3,4‐b]‐1,4‐oxathiane) (PEOTT)/PSS. As‐formed film exhibited low electrical conductivity (～10^?4 S/cm). Alternatively, EOTT together with EDOT (in different molar ratio of 1:1 and 1:5) was copolymerized and the polymer poly(EOTT‐co‐EDOT)/PSS had electrical conductivity of 10^?1 S/cm. After dimethyl sulfoxide (DMSO) treatment, the electrical conductivity was enhanced to 10⁰ S/cm; however, the conductivity of the above homopolymer was reduced (～10^?5 S/cm). Raman spectroscopy was used to interpret conductivity enhancement or reduction after DMSO treatment. The conductivity decrease of PEOTT/PSS compared to poly(EOTT‐co‐EDOT)/PSS may arise from the conformational change of PEOTT backbone from the quasi‐planar to the distorted planar mode induced by PSS^–/PSSH through ionic interaction. Kinetic studies revealed that the copolymer had high coloration efficiencies (375 cm²/C), low switching voltages (?0.8 to +0.6 V), decent contrast ratios (45%), moderate response time (1.0 s), excellent stability, and color persistence. An electrochromic device employing poly(3‐methylthiophene) and poly(EOTT‐co‐EDOT)/PSS as the anode and cathode materials was also studied. From these results, poly(EOTT‐co‐EDOT)/PSS would be a promising candidate material for organic electronics. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 2285–2297     

Control of doctor‐blade coated poly (3,4‐ethylenedioxythiophene)/poly(styrenesulfonate) electrodes shape on prepatterned substrates via microflow control in a drying droplet

We demonstrated a simple patterning method for the deposition of polymer electrodes such as poly(3,4‐ethylenedioxythiophene)/poly(styrenesulfonate) (PEDOT/PSS). We made use of the difference in wettability between hydrophobic surfaces and hydrophilic surfaces to make the patterns. However, the patterns made with our patterning method created undesirable ring‐like stains, which were caused by the outward flow of the solute within the PEDOT/PSS solution drop. To achieve homogenous device performance, we proposed a simple process for removing this ring‐like stain by making the surface tension gradient with dual solvent system in the PEDOT/PSS solution drop. Because this surface tension gradient causes the inward flow of the solute within the PEDOT/PSS solution drop, the ring‐like stain is removed. Finally, we confirmed the potential of our patterning method for polymer electrodes such as the PEDOT/PSS by fabricating pentacene thin‐film transistors (TFTs) and measuring the electrical properties of the pentacene TFTs. © 2011 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 49: 1590–1596, 2011     

Preparation of poly(3, 4‐ethylenedioxythiophene)/poly(styrene sulfonate) (PEDT/PSS) composite and its applications in anti‐static coating

Poly(3, 4‐ethylenedioxythiophene)/poly(styrene sulfonate) (PEDT/PSS) composite is prepared by solution polymerization at room temperature in the presence of 3, 4‐ethylenedioxythiophene as the monomer, PSS as the doping agent, potassium supersulfate (KPS) as the oxidant, and deionized water as the solvent. The color of the PEDT/PSS solution is dark blue and its solid content is 2.2%, its pH value is 1.5. By mixing alcohols, polar organic solvents, adhesives, and so on into PEDT/PSS solution, the anti‐static coating solution is prepared. The coating is conducted by bar‐coating (20 µm) at 40% relative humidity and 20°C. The influence of the content of each component on the coating surface resistivity is discussed, and a reasonable volume content of each component is obtained. The obtained coating has low surface resistivity (1 × 10⁶ Ω), excellent water resistance, and high transmittance of visible light together with a wide range of potential applications. Copyright © 2009 John Wiley & Sons, Ltd.     

Simultaneous synthesis of silver nanoparticles and poly(2,5‐dimethoxyaniline) in poly(styrene sulfonic acid)

Silver nanoparticles were formed in situ along with poly(2,5‐dimethoxyaniline) (PDMA) in an interconnected network matrix (reactor), comprising the electronic conductive polymer, PDMA, and a polyelectrolyte, poly(styrene sulfonic acid) (PSS), through the simultaneous reduction of Ag⁺ ions and polymerization of 2,5‐dimethoxyaniline. In situ ultraviolet‐visible spectroscopy showed that peaks corresponding to the plasmon resonance of silver nanoparticles at 411 nm and the polaronic transition of PDMA at 438 nm provided evidences for the simultaneous formation of silver nanoparticles and PDMA. Transmission electron microscopy and size distribution analysis revealed the presence of spherical silver nanoparticles with an average diameter of 12 nm in the composite. X‐ray photoelectron spectroscopy showed that the amine units in PDMA changed to imine units upon the formation of silver nanoparticles. A comprehensive mechanism for the formation of the PDMA‐PSS‐Ag nanocomposite is proposed. A 10‐fold increase in the conductivity was noticed for the PDMA–PSS–Ag nanocomposite (1 S/cm) in comparison with the PDMA–PSS composite (0.1 S/cm). © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3843–3852, 2006     

The grafting of acrylamide onto poly(ε‐caprolactone) and poly(1,5‐dioxepan‐2‐one) using electron beam preirradiation. III. The grafting and in vitro degradation of chemically crosslinked poly(1,5‐dioxepan‐2‐one)

Acrylamide was graft polymerized onto the surface of a chemically crosslinked and amorphous biodegradable polyester, poly(1,5‐dioxepan‐2‐one). Electron beam irradiation at a dose of 5 Mrad was used to generate the initiating species in the polyester. The degradation behavior in vitro at pH 7.4 and 37°C in a phosphate buffer solution was studied for untreated, irradiated, and acrylamide‐grafted polymer. Differences in weight loss performance were observed between virgin and treated polymers. The acrylamide‐grafted poly(1,5‐dioxepan‐2‐one) was totally degraded after 43 weeks as compared to 48 weeks for the irradiated and 55 weeks for the virgin polymer. On the other hand, the treated polymers showed a higher resistance to degradation in terms of weight loss during the intermediate part of the degradation, i.e., between about 5 and 35 weeks. After this period, the irradiated and particularly the acrylamide grafted poly(1,5‐dioxepan‐2‐one) degraded much more rapidly than the virgin polymer. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1659–1663, 1999     

Stretchable and flexible resistive behavior of poly(3,4‐ethylenedioxythiophene):Poly(styrenesulfonate) thin film on ultra‐low modulus polydimethylsiloxane with trench‐type roughness

This study investigates the resistive behavior of rod‐coated micrometer thick films of poly(3,4‐ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) on ultra‐low modulus (120– 130 kPa) polydimethylsiloxane (PDMS) substrate having scratch or microtrench‐type roughness patterns. On average, the films were found to remain electrically functional up to 23% axial strain with an average increase of three times in the value of the normalized resistance. The films were also found to remain conductive up to bending diameter of 4 mm with an average increase of 1.12 times their initial resistance. The rod‐coated PEDOT:PSS films on ultra‐low modulus PDMS having microtrench‐type roughness were also found to remain functional even after 1000 bending cycles at a bending diameter of 4 mm and even smaller with an increase in resistance that was on average 1.15 times their initial resistance. The films were found to fail firstly by cracking and thereby debonding from the substrate under the application of axial strain. On the other hand, the films exhibit no delamination under bending strains. The results from this investigation suggest that the polymer–polymer laminate has potential applicability in stretchable and flexible electronics and related applications. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 226–233     

Smectic structures in electrochemically prepared poly(3,4‐ethylenedioxythiophene) films

Sub‐micrometer layers of electrochemically prepared methyl‐ and decyl‐substituted poly(3,4‐ethylenedioxythiophene) (PEDOT) carrying perchlorate counterions have been examined with grazing incidence X‐ray diffraction with synchrotron radiation. The materials were found to be partially crystalline, and the data could be ascribed to a model of sheets of π‐π stacked polymer chains with a smectic ordering of these sheets. An unsubstituted PEDOT sample with the polymeric polystyrenesulfonic acid as a counterion was also investigated and turned out to be essentially amorphous. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 945–952, 2003     

Helicity induction on a poly(phenylacetylene) derivative bearing aza‐18‐crown‐6 ether pendants in water

A stereoregular poly(phenylacetylene) bearing the bulky aza‐18‐crown‐6 ether as the pendant (poly‐ 1 ) formed a predominantly one‐handed helical conformation upon complexation with various chiral compounds, such as amino acids, peptides, aminosugars, amines, and amino alcohols in water. The complexes exhibited an induced circular dichroism (ICD) in the UV–visible region of the polymer main chain. Therefore, poly‐ 1 can be used as a novel probe for determining the chirality of chiral compounds in water. The assay of 19 common free L ‐amino acids gave the same ICD sign at 0 °C except for L ‐phenylalanine. The effects of pH, temperature, guest concentration, and organic solvent content on the ICD during the complexation of poly‐ 1 with chiral compounds were also investigated. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1004–1013, 2003     

Investigation of polymer–solvent interactions in poly(styrene sulfonate) thin films

The swelling behavior of acid form poly(styrene sulfonate) (PSS‐H) thin films were investigated using in situ spectroscopic ellipsometry (SE) to probe the polymer–solvent interactions of ion‐containing polymers under interfacial confinement. The interaction parameter (χ), related to the polymer and solvent solubility parameters in the Flory–Huggins theory, describes the polymer‐solvent compatibility. In situ SE was used to measure the degree of polymer swelling in various solvent vapor environments, to determine χ for the solvent‐PSS‐H system. The calculated solubility parameter of 40–44 MPa^1/2 for PSS‐H was determined through measured χ values in water, methanol, and formamide environments at a solvent vapor activity of 0.95. Flory–Huggins theory was applied to describe the thickness‐dependent swelling of PSS‐H and to quantify the water‐PSS‐H interactions. Confinement had a significant influence on polymer swelling at low water vapor activities expressed as an increased χ between the water and polymer with decreasing film thickness. As the volume fraction of water approached ～0.3, the measured χ value was ～0.65, indicating the water interacted with the polymer in a similar manner, regardless of thicknesses. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2017 , 55, 1365–1372     

Raman spectroscopic investigation of the phase behavior and phase transitions in a poly(methyl methacrylate)‐carbon dioxide system

Laser Raman spectroscopy, in conjunction with an optical high‐pressure cell, was used to investigate the poly(methyl methacrylate)‐carbon dioxide system. The Raman shifts associated with carbon dioxide molecules in the gas phase and those dissolved in the polymer were used to derive sorption kinetics of carbon dioxide and the carbon dioxide‐induced phase changes in the polymer. Measurements were made in the temperature and pressure ranges in which this system is known to exhibit retrograde vitrification behavior. The Raman results on the sorption kinetics and on the onset of plasticization were in agreement with those obtained by gravimetric and calorimetric techniques, respectively. This technique provides a versatile and rapid way of characterizing polymer‐gas systems and information that so far has been obtainable only through painstaking and time‐consuming techniques. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 2214–2217, 2003     

Synthesis and characterization of fluorinated poly(amide imide)s derived from 1,4‐bis(2′‐trifluoromethyl‐4′‐trimellitimidophenoxy)benzene and aromatic diamines

A series of fluorinated poly(amide imide)s were prepared from 1,4‐bis(2′‐trifluoromethyl‐4′‐trimellitimidophenoxy)benzene and various aromatic diamines [3,3′,5,5′‐tetramethyl‐4,4′‐diaminediphenylmethane, α,α‐bis(4‐amino‐3,5‐dimethyl phenyl)‐3′‐trifluoromethylphenylmethane, 1,4‐bis(4′‐amino‐2′‐trifluoromethylphenoxy)benzene, 4‐(3′‐trifluoromethylphenyl)‐2,6‐bis(3′‐aminophenyl)pyridine, and 1,1‐bis(4′‐aminophenyl)‐1‐(3′‐trifluoromethylphenyl)‐2,2,2‐trifluoroethane]. The fluorinated poly(amide imide)s, prepared by a one‐step polycondensation procedure, had good solubility both in strong aprotic solvents, such as N‐methyl‐2‐pyrrolidinone, dimethylacetamide, dimethylformamide, dimethyl sulfoxide, and cyclopentanone, and in common organic solvents, such as tetrahydrofuran and m‐cresol. Strong and flexible polymer films with tensile strengths of 84–99 MPa and ultimate elongation values of 6–9% were prepared by the casting of polymer solutions onto glass substrates, followed by thermal baking. The poly(amide imide) films exhibited high thermal stability, with glass‐transition temperatures of 257–266 °C and initial thermal decomposition temperatures of greater than 540 °C. The polymer films also had good dielectric properties, with dielectric constants of 3.26–3.52 and dissipation factors of 3.0–7.7 × 10^?3, and acceptable electrical insulating properties. The balance of excellent solubility and thermal stability associated with good mechanical and electrical properties made the poly(amide imide)s potential candidates for practical applications in the microelectronics industry and other related fields. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1831–1840, 2003     

Crystal structure of poly(ω‐pentadecalactone)

The crystal structure of poly(ω‐pentadecalactone) (PPDL) synthesized by enzyme‐catalyzed polymerization was determined by full‐profile refinement. A pseudo‐orthorombic monoclinic unit cell with dimensions a = 7.49(1), b = 5.034(9), and c = 20.00(4)Å (fiber axis), and α = 90.06(4)° hosts two monomeric units belonging to polymer chains with opposite orientation, according to the P2₁ space‐group symmetry. A close similarity to the crystal structure of poly(?‐caprolactone) was evident. However, the even number of backbone atoms in the monomer unit of PPDL leads to a lower crystal symmetry. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1009–1013, 2003     

Library synthesis and characterization of 3‐aminopropyl‐terminated poly(dimethylsiloxane)s and poly(ϵ‐caprolactone)‐b‐poly(dimethylsiloxane)s

Libraries of 3‐aminopropyl‐terminated poly(dimethylsiloxane) (APT–PDMS) and poly(?‐caprolactone)–poly(dimethylsiloxane)–poly(?‐caprolactone) (PCL—PDMS–PCL) triblock copolymers were synthesized. Preliminary experiments were carried out to select an appropriate catalyst and route for the poly(dimethylsiloxane) synthesis, and trial experiments were conducted to verify the successful synthesis of the intended polymer compositions. Then, a series of APT–PDMS oligomers were synthesized with an automated combinatorial high‐throughput synthesis system to cover a molecular weight range of 2500–50,000 g/mol. Trial PCL—PDMS–PCL triblock copolymers were synthesized with the automated reactor system and characterized in detail with rapid gel permeation chromatography, high‐throughput Fourier transform infrared, nuclear magnetic resonance, and differential scanning calorimetry. Finally, two library synthesis experiments were carried out in which the lengths of both the poly(dimethylsiloxane) and poly(?‐caprolactone) blocks in the PCL—PDMS–PCL triblock copolymers were varied. The results obtained from these experiments demonstrated that it was possible to synthesize libraries of well‐defined APT–PDMS oligomers and PCL—PDMS–PCL triblock copolymers with an automated high‐throughput system. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4880–4894, 2006     

Synthesis and opto‐electrical properties of dendron‐containing poly(2,3‐diphenyl‐1,4‐phenylenevinylene) derivatives

A new series of poly(2,3‐diphenyl‐1,4‐phenylenevinylene) derivatives containing dendritic side groups were synthesized. Different generations of dendrons were integrated on the pendant phenyl ring to investigate their effect on optical and electrical properties of final polymers. Homopolymers can not be obtained via the Gilch polymerization because of sterically bulky dendrons. By controlling the feed ratio of different monomers during polymerization, dendron‐containing copolymers with high molecular weights were obtained. The UV–vis absorption and photoluminescent spectra of the thin films are pretty close; however, quantum efficiency is significantly enhanced with increasing the generation of dendrons. The electrochemical analysis reveals that hole‐injection is also improved by increasing dendritic generation. Double‐layer light‐emitting devices with the configuration of ITO/PEDOT:PSS/polymer/Ca/Al were fabricated. High generation dendrons bring benefit of improved device performance. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 3440–3450, 2007     

Study of the self‐diffusion of poly(ethylene glycol)s in poly(vinyl alcohol) aqueous systems

We have measured the self‐diffusion coefficients of a series of oligo‐ and poly(ethylene glycol)s with molecular weights ranging from 150 to 10,000, in aqueous solutions and gels of poly(vinyl alcohol) (PVA), using the pulsed‐gradient spin‐echo NMR techniques. The PVA concentrations varied from 0 to 0.38 g/mL which ranged from dilute solutions to polymer gels. Effects of the diffusant size and polymer concentration on the self‐diffusion coefficients have been investigated. The temperature dependence of the self‐diffusion coefficients has also been studied for poly(ethylene glycol)s with molecular weights of 600 and 2,000. Several theoretical models based on different physical concepts are used to fit the experimental data. The suitability of these models in the interpretation of the self‐diffusion data is discussed. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 2396–2403, 1999     

Dehydrogenation of poly(1,3‐cyclohexadiene)–polystyrene binary block copolymers

The dehydrogenation of poly(1,3‐cyclohexadiene)–polystyrene binary block copolymers obtained by anionic copolymerization with alkyllithium/amine systems was investigated for the first time. The dehydrogenation of the poly(1,3‐cyclohexadiene) block, which was composed of 1,2‐cyclohexadiene (1,2‐CHD) and 1,4‐cyclohexadiene (1,4‐CHD) units, was strongly affected by the polymer chain structure. The existence of 1,2‐CHD units prevented the dehydrogenation of the poly(1,3‐cyclohexadiene) block in the binary block copolymer. The rate of dehydrogenation was fast on a long sequence of 1,4‐CHD units, whereas it was relatively slow for 1,2‐CHD/1,4‐CHD (≈1/1) unit sequences. The bonding of the polystyrene block to the polymer chain effectively improved not only the rate of dehydrogenation of a long sequence of 1,4‐CHD units but also that of the polymer chain with a high content of 1,2‐CHD units. The dehydrogenation of a poly(1,3‐cyclohexadiene) block containing a small number of 1,2‐CHD units progressed via step‐by‐step reactions. The dehydrogenation of a long sequence of 1,4‐CHD units proceeded as the first step. Subsequently, in the second step, the 1,2‐CHD/1,4‐CHD (≈1/1) unit sequences remaining in the polymer chain were dehydrogenated. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3526–3537, 2006     

A novel aromatic–aliphatic copolyester consisting of poly(1,4‐dioxan‐2‐one) and poly(ethylene‐co‐1,6‐hexene terephthalate): Preparation,thermal, and mechanical properties

A novel multiblock aromatic–aliphatic copolyester poly(ethylene‐co‐1,6‐hexene terephthalate)‐copoly(1,4‐dioxan‐2‐one) (PEHT‐PPDO) was successfully synthesized via the chain‐extension reaction of dihydroxyl teminated poly(ethylene‐co‐hexane terephthalate) (PEHT‐OH) with dihydroxyl teminated poly(1,4‐dioxan‐2‐one) (PPDO‐OH) prepolymers, using toluene‐2,4‐diisocyanate as a chain extender. To produce PEHT‐OH prepolymer with an appropriate melting point which can match the reaction temperature of PEHT‐OH prepolymer with PPDO‐OH prepolymer, 1,6‐hexanediol was used to disturb the regularity of poly(ethylene terephthalate) segments. The chemical structures and molecular weights of PEHT‐PPDO copolymers were characterized by ¹H NMR, FTIR, and GPC. The DSC data showed that PPDO‐OH segments were miscible well with PEHT‐OH segments in amorphous state and that the crystallization of copolyester was predominantly contributed by PPDO segments. The TGA results indicated that the thermal stability of PEHT‐PPDO was improved comparing with PPDO homopolymer. The novel aromatic–aliphatic copolyesters have good mechanical properties and could find applications in the field of biodegradable polymer materials. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2828–2837, 2010     

Structural changes of silver polymer electrolytes: Comparison between poly(2‐ethyl‐2‐oxazoline) and poly(N‐vinyl pyrrolidone) complexes with silver salt

The difference between the polymer matrices of poly(2‐ethyl‐2‐oxazoline) (POZ) and poly(N‐vinyl pyrrolidone) (PVP) does not have a significant effect on the facilitated propylene transport and propylene solubility in 1:1 polymer/silver salt complex membranes, according to our previous work. In this article, its origin is investigated in terms of both microstructures of silver polymer electrolytes and the coordinative interaction of silver ion with polymer and with the counteranion. Initially different microstructures of POZ and PVP become similar to each other upon dissolving a large amount of silver salt, as evidenced by propane transport properties, specific volume, and Bragg d‐spacing. The dissolution of the silver salt in the polymer solvent strongly depends on the coordinative interaction between silver ion and carbonyl oxygen of POZ and PVP. Thus, the structural similarity upon dissolving silver salts in POZ and PVP is primarily determined by the coordinative interaction between silver ion and carbonyl oxygen, which was confirmed by theoretical structure calculation based on density functional theory and by IR and Raman spectroscopy. Therefore, facilitated olefin transport for silver polymer electrolyte membranes does not strongly depend on the polymeric matrix at high silver concentrations. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 232–237, 2004