δ-MnO2对TiO2光催化降解甲基橙的抑制作用

采用动力学方法研究了在水悬浮液中δ-MnO2颗粒物对P-25 TiO2光催化降解甲基橙活性的影响, 并利用紫外-可见漫反射光谱(DRS)和光致发光光谱(PL)对受δ-MnO2污染前后的TiO2样品进行了表征. 动力学研究结果表明, 在3种不同初始pH值条件下, δ-MnO2对TiO2光催化剂都具有明显的致毒效应, 共存δ-MnO2的浓度越大, 致毒效应越明显. 表征结果表明, 由于δ-MnO2 与TiO2之间的界面接触, 使得TiO2吸收带边蓝移, 紫外光区的吸收强度降低, 光致发光信号(PL)明显减弱. 因此, δ-MnO2导致TiO2的禁带宽度增大, 光利用率降低, 并且是光生电子与空穴的复合中心.     

MnO_2对TiO_2光催化降解苯胺的影响

采用动力学方法研究了MnO2颗粒物对TiO2光催化降解苯胺活性的影响,对比考察了光催化降解过程中苯胺溶液的UV吸收光谱的变化,并用HPLC方法鉴别了中间产物.结果表明,少量MnO2颗粒物就能使TiO2光催化降解苯胺的活性受到明显的抑制,不同结构的二氧化锰致毒效应由大到小的顺序为:δ-MnO2α-MnO2β-MnO2;降解不同时间后溶液的UV吸收光谱的变化也反映了MnO2颗粒物具有同样的致毒效应;MnO2颗粒物不改变TiO2光催化降解苯胺的途径,但对生成中间产物的基元步骤的抑制程度不同。     

三元复合材料K8[Fe（H2O）W11MnO39]/PANI/TiO2的制备及光催化性能

采用静电自组装法制备出三元复合材料K8[Fe（H2O）W（11）MnO（39）]/PANI/TiO2.采用IR,UV,XRD,SEM,XPS和N2吸附-脱附的表征手段对K8[Fe（H2O）W（11）MnO（39）]/PANI/TiO2进行表征,并以龙胆紫为模型,在紫外光照射下,考察了K8[Fe（H2O）W（11）MnO（39）]/PANI/TiO2对龙胆紫染料的光催化性能,确定光催化最佳条件：龙胆紫溶液浓度为5mg/L,pH=3,K8[Fe（H2O）W11MnO39]/PANI/TiO2的用量为10mg,脱色率可达92.93%.     

一维纳米结构MnO2的微波合成及其电化学性能

以在水热条件下合成的纳米结构γ-MnOOH为前驱物, 以K2S2O8为氧化剂, 采用单模式微波加热法制备出一维纳米结构MnO2. 采用XRD和TEM等手段对样品进行了表征. 以在100 ℃下水热合成的γ-MnOOH纳米纤维为前驱物时, 制得α-MnO2纳米纤维; 以在150 ℃下水热合成的γ-MnOOH纳米棒为前驱物时, 制得β-MnO2纳米棒. 分别用α-MnO2纳米纤维和β-MnO2纳米棒作为Li/MnO2电池的正极材料进行恒电流放电实验, 研究结果显示, α-MnO2纳米纤维的放电容量为270.23 mA·h/g, β-MnO2纳米棒的放电容量为186.66 mA·h/g.     

SnO_2/TiO_2纳米管复合光催化剂的性能及失活再生

基于微波水热法和微乳液法合成SnO2/TiO2纳米管复合光催化剂.通过X射线衍射(XRD)、配有能量色散X射线光谱仪(EDX)的透射电镜(TEM)和电化学手段对光催化剂进行表征.以甲苯为模型污染物,考察光催化剂在紫外光(UV)和真空远紫外光(VUV)下的性能及失活再生.结果表明,SnO2/TiO2纳米管复合光催化剂形成三元异质结(锐钛矿相TiO2(A-TiO2)/金红石相TiO2(R-TiO2)、A-TiO2/SnO2和R-TiO2/SnO2异质结),促使光生电子-空穴对的有效分离,提高光催化活性.SnO2/TiO2表现出最佳的光催化性能,UV和VUV条件下的甲苯降解率均达100%,CO2生成速率(k2)均为P25的3倍左右.但由于UV光照矿化能力不足,中间产物易在催化剂表面累积.随着UV光照时间的增加,SnO2/TiO2逐渐失活,20 h后k2由138.5 mg·m-3·h-1下降到76.1 mg·m-3·h-1.利用VUV再生失活的SnO2/TiO2,过程中产生的·OH、O2-·、O(1D)、O(3P)、O3等活性物质可氧化吸附于催化剂活性位的难降解中间产物,使催化剂得以再生,12 h后k2恢复到143.6 mg·m-3·h-1.UV和VUV的协同效应使UV降解耦合VUV再生成为一种可持续的光催化降解污染物模式.     

TiO2/BiNbO4复合光催化剂的制备及降解气相苯性能

采用固相反应法制备出BiNbO4,将其与TiO2耦合,得到TiO2/BiNbO4复合光催化剂。考察了催化剂在紫外光照射下催化降解气相苯的活性。结果表明,TiO2与BiNbO4耦合后催化活性明显提高,其中36%TiO2/BiNbO4紫外光照5 h对苯的降解率是P-25的3.7倍。紫外-可见漫反射谱(UV-Vis DRS)、XRD、XPS和低温氮吸附-脱附等表征结果表明TiO2与BiNbO4的能级匹配,二者之间存在能带协同效应。耦合后的TiO2/BiNbO4的光生电子和空穴能有效分离,从而提高了催化剂催化活性。     

SiO2负载氮掺杂TiO2可见光响应光催化剂的制备及性能

以四氯化钛为钛源,尿素为氮源,采用液相水解-沉淀法制得SiO2负载N掺杂TiO2可见光响应TiO2-xNy/SiO2光催化剂(TSN)。以苯酚为模型物,考察了TSN在可见光区、紫外光区及太阳光下的光催化活性,以及催化剂的使用寿命、分离性能。采用XPS、FTIR、UV-Vis DRS、XRD、TEM和低温氮物理吸附等对催化剂的结构进行表征。结果表明,N以阴离子形式进入TiO2体相并置换晶格中的O,适量N掺杂的TSN在紫外光区、可见光区及太阳光下均表现出较高的活性。SiO2与TiO2界面间有Ti-O-Si键形成,结合牢固。N掺杂在TiO2表面生成Ti-O-N键,形成新的能级结构,使催化剂的吸收红移至450~500 nm,诱发TiO2可见光催化活性。SiO2负载可减小TiO2颗粒平均尺寸,增加催化剂比表面积;同时SiO2负载还可改善催化剂的分离性能,提高催化剂使用寿命。     

负载型TiO2/SBA-15的制备及其光催化还原CO2性能

以羧基改性的SBA-15(COOH/SBA-15)和钛酸四丁酯(TB)为原料,利用COOH/SBA-15表面上高分散的大量羧基将TB锚定,通过溶剂热处理得到高分散负载型TiO2/SBA-15催化剂.产物经XRD,Raman,FT-IR,TEM,N2吸脱附和UV-Vis表征,结果显示:所制备的TiO2/SBA-15催化剂为比表面大、结晶度较高的锐钛矿TiO2,TiO2均匀分散于SBA-15表面,此外,COOH/SBA-15有效抑制了TiO2晶粒的长大.以光催化还原CO2为探针反应,考察了TiO2/SBA-15催化剂在紫外光照射下的光催化性能.结果表明:相比于后处理浸渍法制备的光催化剂,本文制备的TiO2/SBA-15催化剂表现出了高的光催化还原CO2活性,主要产物为甲醇,且TiO2最佳负载量为16.5%,并对相关反应机理做了探讨.     

磁载光催化剂Fe3O4/C/TiO2的制备及对三氯苯酚的降解

以FeCl3为铁源,葡萄糖为碳源,钛酸四丁酯为钛源,采用水热法制备了磁载光催化剂Fe3O4/C/TiO2,用TEM、EDX、VSM、XRD和IR对Fe3O4/C/TiO2的粒径、形貌和物相等进行了表征。研究了该催化剂对三氯苯酚的降解性能,探讨了其重复使用的可能性,用荧光光谱法推测了可能的反应机理。结果表明该材料结合了光催化与可再生的优点,1 g·L-1 Fe3O4/C/TiO2在18 W紫外灯下,50 min内可将三氯苯酚降解97.9%以上,6次循环使用后降解率仍保持在95.1%,降解过程中有羟基自由基生成。     

超临界流体干燥法制备纳米TiO2-SnO2-SiO2复合光催化剂及其光催化性能研究

半导体多相光催化法作为一种污染治理新技术越来越受到人们的重视,在所使用的半导体光催化剂中,TiO2以无毒,催化活性高,价廉,无污染等特点,成为最具有前途的绿色环保型催化剂之一[1],但其自身具有局限性,如禁带宽度大,需在近紫外光下才能激发产生电子空穴对,对太阳光的利用率仅     

浅池型TiO2/ACF光催化降解水中苯酚的研究

为了提高光催化过程的降解速率，本文以涂覆法制得的二氧化钛/活性炭纤维（TiO2/ACF）为光催化剂，300 W(365 nm)高压汞灯为光源，研究了浅池型反应器中苯酚在TiO2/ACF上的光催化降解动力学；探讨了光强度、高压汞灯滤光以及光源种类对降解反应的影响，并对光氧化，光催化和吸附过程进行了比较。结果表明：光氧化对苯酚的降解无效果，光催化降解速率常数与吸附速率常数之比为3.35/1；光强越大，光催化降解速率越快；高压汞灯不滤光时光催化降解速率明显加快，但光催化反应仍遵循准一级反应动力学方程；波长为254 nm紫外杀菌灯的降解效果高于波长为365 nm高压汞灯滤光后的降解效果。     

Preparation and Performances of RuO2/TiO2 Films Photocatalyst Supported on Float Pearls

"RuO2/TiO2 films were deposited on float pearls (FP) by the sol-gel-dipping method. The substrates were coated with RuO2/TiO2 precursor sol, air-dried at 120 oC and further heated at 500 oC to obtain the coupled photocatalyst of RuO2/TiO2 films supported on FP (RuO2/TiO2/FP). The structure of coupled photocatalyst was characterized by SEM, XRD, and FT-IR technique, respectively. The results showed TiO2 has anatase structure and doped RuO2 was highly dispersed on the surface of TiO2 particles as amorphous. The average thickness of RuO2/TiO2 films (3 layers) on FP was determined to be about 1 1m. This study was carried out under the following conditions: volume 60 mL, initial concentration of beta-cypermethrin (BEC) 45 mg/L, pH 6.5, amount of RuO2/TiO2/PF 5 g/L, air flow rate 200 mL/min, reaction time 60 min. The degradation rates of BEC are 88.1% (125 W Hg lamp), 82.8% (8 W UV lamp), and 75.1% (8 W solar lamp), respectively. The photocatalytic degradation of BEC was experimentally demonstrated to follow the Langmuir-Hinshelwood kinetic model, and the reaction rate constant (17.5 mg/(L min)) and the adsorption constant (3.486 L/g) were determined, respectively. It was also found that the RuO2/TiO2 /FP photocatalyst has significantly the visible light photoactivity for degradation of BEC."     

活性炭负载TiO2-Fe3O4磁性光催化剂的制备及性能

采用溶胶-凝胶法制备了易于固液分离的活性炭（AC）负载磁性光催化剂（TiO2-Fe3O4／AC）．样品通过SEM-EDX和X射线衍射法进行表征．通过在紫外光照射下降解亚甲基蓝评价其光催化降解能力．结果表明：负载22％Fe3O4的光催化剂（含20％TiO2和58％AC）的光催化活性最强（120min时亚甲基蓝的降解率达到87％,是纯TiO2的2．7倍）;磁性光催化剂可实现磁分离回收．     

高活性低失活In(OH)3纳米晶光催化剂的制备和表征

采用超声沉淀法从In(NO3)3制备出了In(OH)3纳米晶体, 发现其在254 nm紫外光照射下对苯催化活性和活性稳定性比P25-TiO2高得多.     

铂非均匀掺杂二氧化钛薄膜的光催化性能

采用溶胶-凝胶法制备了铂非均匀掺杂的二氧化钛薄膜, 并用UV-vis分光光度计及电化学工作站表征了薄膜的光吸收性能和光电化学行为, 通过对甲基橙的光催化降解动力学来表征催化剂的光催化活性. 结果表明 Pt非均匀掺杂可以明显增强二氧化钛的光催化活性, 而均匀掺杂的效果较差; Pt非均匀掺杂的最佳量为0.3 mol%. 催化剂薄膜的电化学行为显示: Pt非均匀掺杂二氧化钛薄膜的开路电压高, 交流阻抗小. 并从半导体的PN结原理探讨了Pt非均匀掺杂二氧化钛的催化活性机理.     

Hydrothermal synthesis, structure and photocatalytic property of nano-TiO_2-MnO_2

TiCI4 and MnSO4.H2O as raw materials are hydrolyzed stiochiometrically, following the intermediate of oxide hydrating reacts at 150℃, 0.5 MPa in high-pressure reactor, after filtering, washing and drying, nanometric TiO2-MnO2 (Ti1-xMnxO2) is prepared. The effects of the reaction temperature and time on nanometric TiO2-MnO2 are also discussed. XRD shows that the product is TiO2-MnO2 with amorphous phase. After being sintered at above 780℃, it transfers into Ti1-xMnxO2 with a rutile structure. TEM shows that TiO2-MnO2 is the spherical particle. And the average diameter of the particles is 20 nm. The optical absorbance was determined by UV-265 spec-trophotometer after dispersing the sample in the mixture of water and glycerol with the ratio of 1 : 1 equably. It is found that the nano-material possesses the advantages of both nano-TiO2 and nano-MnO2, and it has strong absorption in the UV and visible region. Photodegradation of dyes in an aqueous solution is investigated using nanometricTiO2-MnO2 as a pho     

异质结型AgI/AgBr/TiO2催化剂的制备及其光催化性能

首先以沉积-沉淀法制备AgBr/TiO₂复合催化剂,然后采用离子交换法制备出新型的异质结型AgI/AgBr/TiO₂光催化剂.利用XRD和UV-Vis对AgI/AgBr/TiO₂光催化剂进行了表征.以甲基橙为染料模型,在可见光条件下(500 W、λ>420 nm)研究了AgI的含量对AgI/AgBr/TiO₂催化活性的影响.结果表明,AgI拓展了催化剂的吸收光谱范围;AgI生成量为AgBr的5%时,AgI/AgBr/TiO₂的催化活性最高.AgI/AgBr异质结的形成有利于光生电子和空穴的分离,提高AgI/AgBr/TiO₂的催化活性.     

在Pd/TiO2上CO的光催化增强效应

在Pd(2％)/TiO2上CO催化氧化的研究中发现：室温下， 以黑光灯（λ=365 nm）照时， CO的氧化活性比暗态显著提高，产生了明显的光催化增强效应（两者速率常数比约为15）.但在TiO2上，无论暗态还是黑光灯（λ=365 nm）照，均无CO氧化反应发生.这可能是由于氧分子解离吸附时的键能减弱，使Pd表面氧原子（或O－）浓度增加和氧原子的溢流（oxygen spillover）两种效应结合产生的.     

钛酸铋系化合物的光催化性能研究

采用化学溶液分解法制备了钛酸铋化合物: Bi₁₂TiO₂₀, Bi₄Ti₃O₁₂和Bi₂Ti₂O₇, 并采用XRD表征了其结构. 用TEM观察发现其平均粒径＞100 nm, UV-Vis漫反射谱测定显示它们在可见光区均呈现极强的吸收特征. 紫外光照射下甲基橙的光催化降解脱色实验表明, 三种钛酸铋化合物均具有较强的光催化活性, 其中, Bi₁₂TiO₂₀的光催化活性最强, 几乎与P-25相同. 钛酸铋化合物光催化性能的不同在于它们具有不同的晶相结构和电子结构.