本文报导用磁控离子溅射和后热处理方法在LaAlO3(001)衬底上制作2英寸双面Tl2Ba2CaCu2O8(Tl-2212) 超导薄膜的方法和薄膜的特性.XRD测试表明薄膜具有纯的Tl-2212相和c轴垂直于膜面的织构.衬底两侧薄膜的结晶形貌和超导电性均匀,超导转变温度Tc一般为105 K左右,液氮温度下临界电流密度Jc>2×106A/cm2,10GHz频率下表面电阻最小达到350μΩ,可满足超导微波滤波器实用的需要.     

热处理对MgO基片的表面形貌以及对CeO_2和Tl-2212薄膜生长的影响

研究了MgO基片在高温退火时表面形貌和表面结构的变化,以及它对CeO2缓冲层和Tl-2212超导薄膜生长的影响。原子力显微镜(AFM)研究表明,在流动氧环境中1100℃温度下退火,MgO的表面首先由未退火时的皱褶形貌,演化为光滑表面,随着退火时间的延长,表面形貌最终演化为具有光滑基底的独立生长峰结构。XRD测试表明,通过高温热处理可以大幅度提高MgO基片表面结晶的完整性。在1100℃温度下热处理8小时的MgO基片上可以生长出具有高度c轴取向的CeO2(001)缓冲层。然后在此缓冲层上制备了厚度为500nm的外延Tl-2212超导薄膜,其临界转变温度(Tc)达到108.6K,液氮温度下临界电流密度(Jc)为2.8mA/cm2,微波表面电阻Rs(77K,10GHz)约为360.9μΩ。     

倾斜生长Tl2Ba2CaCu2O8超导薄膜的Ⅰ-Ⅴ曲线及快速反应特性

在10mm长、3mm宽的斜切LaAlO3衬底上制备出不同厚度的Tl2Ba2CaCu2O8(Tl-2212)超导薄膜.对薄膜的Ⅰ-Ⅴ特性进行测量,其临界电流密度小于正常生长的Tl-2212超导薄膜.对薄膜通过脉冲方波进行快速反应特性的测量,结果表明倾斜生长的Tl-2212超导薄膜在一个电压脉冲的作用下,产生宽度仅为μs量级的大电流脉冲,然后变为正常态.这和正常生长的超导薄膜不同,前者没有经过发热和升温的过程.利用这一特性可以制作高速高温超导开关和快速反应限流器等.     

倾斜生长Tl_2Ba_2CaCu_2O_8超导薄膜的I-V曲线及快速反应特性

在10mm长、3mm宽的斜切LaA lO3衬底上制备出不同厚度的Tl2Ba2CaCu2O8(Tl-2212)超导薄膜。对薄膜的I-V特性进行测量,其临界电流密度小于正常生长的Tl-2212超导薄膜。对薄膜通过脉冲方波进行快速反应特性的测量,结果表明:倾斜生长的Tl-2212超导薄膜在一个电压脉冲的作用下,产生宽度仅为μs量级的大电流脉冲,然后变为正常态。这和正常生长的超导薄膜不同,前者没有经过发热和升温的过程。利用这一特性可以制作高速高温超导开关和快速反应限流器等。     

蓝宝石基片上制备双面Tl_2Ba_2CaCu_2O_8超导薄膜

在蓝宝石基片上,以CeO2为缓冲层制备了高质量的双面Tl2Ba2CaCu2O8(Tl-2212)超导薄膜。以金属铈靶作为溅射源生长了c轴取向的CeO2缓冲薄膜,并对CeO2薄膜进行了高温处理,有效改善了其结晶质量和表面形貌。采用两步法制备了双面的Tl-2212超导薄膜。XRD测试显示,薄膜为纯的Tl-2212相,且其晶格c轴垂直于衬底表面。超导薄膜的Tc为106K,Jc(77K,0T)为3.5MA/cm2,微波表面电阻Rs(77K,10GHz)为390μΩ。     

在蓝宝石上生长CeO2 缓冲层的原位双温工艺法及Tl-2212薄膜的技术改进

报道了在蓝宝石衬底上制备CeO₂缓冲层的原位双温工艺法及其对Tl₂Ｂa₂CaCu₂Ｏ₈（Tl-2212）薄膜超导特性的影响．XPS和AFM测试结果表明,采用原位双温工艺法制备缓冲层,具有工艺简单,薄膜表面光滑,衬底材料原子扩散量少等特点．在先驱膜的高温后退火过程中,40 nm厚的CeO₂薄膜就能有效地阻挡衬底材料对超导薄膜底层的扩散．随后制备厚度为530 nm的Tl-2212 关键词： Tl-2212超导薄膜 蓝宝石 氧化铈缓冲层 原位双温工艺法     

不同厚度的MgB_2超薄膜的制备和性质研究

本文报导了利用混合物理化学气相沉积法(Hybrid physical-chemical vapor deposition,HPCVD)在SiC(0001)衬底上制备干净的MgB2超薄膜.在背景气体压强、载气H2流量等条件一定的情况下,改变B2H6流量及沉积时间,制备不同厚度的MgB2超薄膜样品,并研究了超导转变温度Tc、剩余电阻率ρ(42K)、上临界场Hc2等与膜厚的关系.这系列超薄膜生长沿c轴外延,随膜厚度的变小Tc(0)降低,ρ(42K)升高.膜在衬底上的生长遵循Volmer-Weber岛状生长模式.对于10nm厚的膜,Tc(0)~32.4K,ρ(42K)~124.92μΩ·cm,其表面连接性良好,平均粗糙度为2.72nm,上临界磁场Hc2(0K)~12T,零场4K时的临界电流密度Jc~107A/cm2,为迄今为止所观测到的10nm厚MgB2超薄膜的最高Jc值,这也证明了10nm厚的MgB2膜在超导纳米器件上具有很强的应用潜力.     

多层膜外退火方法制备MgB2超导薄膜

报道了利用电子束蒸发的Mg/B多层膜作为前驱体,然后退火制备MgB2薄膜的工作.实验中发现,采用翻转膜面的退火处理方式可以有效地避免降温过程中Mg蒸气在薄膜表面形成的颗粒凝结,由此稳定地实现了面积为10 mm×10mm,均匀、平整的超导薄膜的制备,Tc达35 K,转变宽度为0.8 K,在5 μm×5 μm的区域内薄膜的平均粗糙度小于10 nm.为了便于后续器件制作过程中的微加工工艺,研究了膜厚小于1000 (A)时薄膜的成相规律,发现当样品厚度减薄后,Te会有明显降低.通过调整前驱薄膜中的不同分层厚度,仍可实现转变温度达30 K以上、厚度约600 (A)的MgB2薄膜,在20 K时的临界电流密度为2.4×106 A/cm2.     

2英寸双面Tl-2212超导薄膜

我们采用磁控离子溅射和后热处理的方法,在LaAlO3(001)单晶衬底上制作了2英寸直径的双面Tl-2212超导薄膜.薄膜的表面均匀,结构致密.X-光θ-2θ测试表明,薄膜具有很纯的Tl-2212超导相,并具有c-轴垂直于膜面的织构.电磁测试结果表明,薄膜的超导电性均匀,临界温度Tc大于100K,临界电流密度Jc(77K,0T)约1×106A/cm2, 微波表面电阻Rs(77K,10GHz)约0.5mΩ.     

多层高温超导薄膜研究

文中以LaAlO3为衬底,制作了一层Tl-2212高温超导薄膜,并在薄膜上生长一层较薄的CeO2缓冲层,然后再在上面生长一层Tl-2212高温超导薄膜。经过测量,研究了多层膜结构对超导薄膜临界电流密度的影响。结果显示,在缓冲层的结晶过程中超导薄膜的晶格受到影响,结晶过程中的处理很容易诱导上面一层Tl-2212超导薄膜产生杂相,导致临界电流密度降低。     

Magnetic ordering in HoRu2Si2, HoRh2Si2, TbRh2Si2 and TbIr2Si2 by neutron diffraction

Neutron diffraction study of polycrystalline HoRu₂Si₂, HoRh₂Si₂, TbRh₂Si₂, and TbIr₂Si₂ was performed in the temperature range between 4.2 and 300 K. For HoRu₂Si₂ the magnetic spin alignment of a linear transverse wave mode below the Néel temperature 19 K is observed. This static moment wave is propagating along the b-axis with k=(0, 0.2, 0) and is polarized in the c-axis. The root-mean-square and maximum saturation moments per Ho atom are 9.26 and 13.09μ_B, respectively. HoRh₂Si₂, TbRh₂Si₂ an TbIr₂Si₂ are simple collinear antiferromagnets of +-+- type with Néel temperatures of (27±1), (98±2) and (72±3) K, respectively. For TbRh₂Si₂ and TbIr₂Si₂ magnetic moments are localized on RE ions only and are aligned along the tetragonal axis, while for HoRh₂Si₂ they form an angle ø = (28±3)°.     

μ+SR study of LaNi2As2, URh2Si2 and CeRh2Si2

Muon spin relaxation experiments have been carried out in the paramagnetic and magnetically ordered states of URh₂Si₂ and CeRh₂Si₂. As the magnetic structure of these compounds is well known, these measurements can help to characterise their magnetic properties probed by μSR and to understand the μSR results of the heavy fermion compounds of the same crystallographic family. Our measurements show that the muons occupy two different crystallographic sites. The spectra of URh₂Si₂ and CeRh₂Si₂ in the magnetically ordered states are very different, probably reflecting their different magnetic structures. The spectra obtained on CeRh₂Si₂ are similar to the published spectra of the heavy fermion compound CeCu_2.1 Si₂. Muon spin rotation measurements on LaNi₂As₂ indicate that the muon is diffusing at 150 K.     

13C-selective IRMPD of CBr2F2/Cl2 and CCl2F2/Br2 systems

The CO₂ TEA laser irradiation of CBr₂F₂ in the presence of Cl₂ yielded ¹³C-enriched CBrClF₂ and ¹³C-enriched CCl₂F₂ under selected experimental conditions. As the photolysis proceeded, the ¹³C concentration of CBrClF₂ decreased gradually and that of CCl₂F₂ increased up to 90% or higher. These results can be explained by the mechanism involving the secondary ¹³C-selective IRMPD of the primary product CBrClF₂. On the other hand, the carbon-containing product for a CCl₂F₂/Br₂ system was only CBrClF₂; the further IRMPD of which probably regenerated CBrClF₂ in the presence of Br₂. The decomposition probabilities of ¹²C- and ¹³C-containing molecules in both systems were measured as functions of laser line, laser fluence, and reactant pressures.     

Superconductivity in LaPd_2Bi_2 with CaBe_2Ge_2-type structure

正Since the discovery of superconductivity in LaFeAsO_(1-x)F_x,the high-T_c iron-based superconductors have been extensively studied from both experimental and theoretical viewpoints [1-8]. However, the mechanism of the unconventional superconductivity is still to be resolved. To     

Polar optic phonons in Hg2Cl2 and Hg2Br2

Far infrared (30–430 cm^?1) reflectivity measurements of Hg₂Cl₂ and Hg₂Br₂ single crystals have been performed in polarized light. The spectra, which are in agreement with group-theoretical predictions, were analyzed by the oscillator fitting procedure and Kramers-Kronig method. The results are compared with the existing data from other measurements and the large anisotropy of polar modes is briefly discussed. The polarization vectors of all long-wavelength symmetry modes were determined group-theoretically.     

Magnetostriction of SmMn2Ge2 and GdMn2Ge2 intermetallic compounds

Longitudinal and transverse magnetostrictions of polycrystalline samples of intermetallic compounds RMn₂Ge₂ (R=Sm or Gd) are measured in pulsed magnetic fields up to 250 kOe. It is found that linear magnetostrictive strains of about 10^?3 arise in a temperature range in which the magnetic field causes a change in the magnetic state of a manganese magnetic subsystem. The results obtained are described within the model of a two-sublattice ferrimagnet with a negative exchange interaction in the manganese subsystem in terms of a strong dependence of this interaction on interatomic distances.     

Structural,magnetic and neutron diffraction studies on TbFe2-TbAl2, TbCo2-TbAl2 and HoCo2-HoAl2

Both pseudobinary systems exhibit large homogeneous regions of cubic and hexagonal Laves phases. Ordering tendencies on crystallographic sites between Al and the transition metals are observed in the hexagonal type.Electron transfer to the transition metals quenches their moments so that they become nonmagnetic at high Al concentrations. The peculiarities in the mechanism of magnetization which appear in rare earth dialuminides when Al is replaced by a transition metal have been studied in detail at cryogenic temperatures.The first replacement of Al results in a decrease in saturation moment. Neutron diffraction verifies the low ordered rare earth sublattice moments and reveals the ‘lost part’ as a disordered component. Considerable magnetic hardness develops in certain regions of concentration often connected with spontaneous increases in magnetization with field. All available evidence suggests the presence of unusual domain wall effects to be responsible for this effect. High remanences develop in both the hexagonal and in the cubic structures in the intermediate region. The development of disordered magnetic components is connected either with the disorder on crystallographic sites or changes in the free electron concentration.