Structure and Ionic Conductivity of Bi6Cr2O15, a New Structure Type Containing (Bi12O14)n Columns and CrO4 Tetrahedra

Powder samples of the Cr⁶⁺-containing compound Bi₆Cr₂O₁₅ were prepared by solid state reaction of Bi₂O₃ and Cr₂O₃ in air at 650°C. The structure was solved and refined using high-resolution neutron powder diffraction data in space group Ccc2, with anisotropic thermal displacement parameters a=12.30184(5), b=19.87492(7), and c=5.88162(2) Å, V=1438.0 ų, and 126 variables to R_F=1.8%. Bi₆Cr₂O₁₅ exhibits a new structure type that contains (Bi₁₂O₁₄)⁸ⁿ⁺_n columns, of the kind previously found only for phases isotypic with Bi₁₃Mo₄VO₃₄. Each column is surrounded by eight CrO²⁻₄ tetrahedra. The ionic conductivity of Bi₆Cr₂O₁₅ was determined by impedance measurements to be 3.5×10⁻⁵ (Ω cm)⁻¹ at 600°C.     

The study of Bi3B5O12: synthesis, crystal structure and thermal expansion of oxoborate Bi3B5O12

The paper presents a new data on the crystal structure, thermal expansion and IR spectra of Bi₃B₅O₁₂. The Bi₃B₅O₁₂ single crystals were grown from the melt of the same stoichiometry by Czochralski technique. The crystal structure of Bi₃B₅O₁₂ was refined in anisotropic approximation using single-crystal X-ray diffraction data. It is orthorhombic, Pnma, a=6.530(4), b=7.726(5), c=18.578(5) Å, V=937.2(5) Å³, Z=4, R=3.45%. Bi³⁺ atoms have irregular coordination polyhedra, Bi(1)O₆ (d(B-O)=2.09-2.75 Å) and Bi(2)O₇ (d(B-O)=2.108-2.804 Å). Taking into account the shortest bonds only, these polyhedra are considered here as trigonal Bi(1)O₃ (2.09-2.20 Å) and tetragonal Bi(2)O₄ (2.108-2.331 Å) irregular pyramids with Bi atoms in the tops of both pyramids. The BiO₄ polyhedra form zigzag chains along b-axis. These chains alternate with isolated anions [B₂^IVB₃^IIIO₁₁]⁷⁻ through the common oxygen atoms to form thick layers extended in ab plane. A perfect cleavage of the compound corresponds to these layers and an imperfect one is parallel to the Bi-O chains. The Bi₃B₅O₁₂ thermal expansion is sharply anisotropic (α₁₁≈α₂₂=12, α₃₃=3×10⁻⁶ °C⁻¹) likely due to a straightening of the flexible zigzag chains along b-axis and decreasing of their zigzag along c-axis. Thus the properties like cleavage and thermal expansion correlate to these chains.     

Crystal chemistry and crystallography of the Aurivillius phase Bi5AgNb4O18

Bi₅AgNb₄O₁₈ is a new phase, which was discovered during the phase equilibrium study of the Bi₂O₃-Ag₂O-Nb₂O₅ system. Bi₅AgNb₄O₁₈ was prepared at 750°C and is stable in air up to its melting temperature of 1160.1±5.0°C (standard error of estimate). Results of a Rietveld refinement using neutron powder diffraction confirmed that Bi₅AgNb₄O₁₈ is isostructural with Bi₃TiNbO₉, Bi₅NaNb₄O₁₈, and Bi₅KNb₄O₁₈. The structure was refined in the orthorhombic space group A2₁am, Z=2, and the lattice parameters are a=5.4915(2) Å, b=5.4752(2) Å, c=24.9282(8) Å, and V=749.52(4) Å³. The structure can be described as the m=2 member of the Aurivillius family, (Bi₂O₂)²⁺ (A_m−1B_mO_3m+1)²⁻ (where A=Bi and B=Ag, Nb), which is characterized by perovskite-like (A_m−1B_mO_3m+1)²⁻ slabs regularly interleaved with (Bi₂O₂)²⁺ layers. The octahedral [NbO₆] units are distorted with Nb-O distances ranging from 1.856(4) to 2.161(2) Å and the O-Nb-O angles ranging from 82.6(3)° to 98.5(3)°. These octahedra are tilted about the a- and c-axis by about 10.3° and 12.4°, respectively. Ag was found to substitute exclusively into the Bi-site that is located in the layer between the two distorted [NbO₆] units. Although the Ag substitutes into the Bi-site with the Bi:Ag ratio of 1:1, the existence of a superlattice was not detected using electron diffraction. A comparison of (Bi₂O₂)²⁺(A_m−1Nb_mO_3m+1)²⁻ structures (where A=Ag, Na, and K) revealed a relation between the pervoskite tolerance factor, t, and structural distortion. The reference pattern for Bi₅AgNb₄O₁₈ has been submitted to the International Centre for Diffraction Data (ICDD) for inclusion in the Powder Diffraction File.     

Mechanochemical-thermal preparation and structural studies of mullite-type Bi2(GaxAl1−x)4O9 solid solutions

A series of Bi₂(Ga_xAl_1−x)₄O₉ solid solutions (0≤x≤1), prepared by mechanochemical processing of Bi₂O₃/Ga₂O₃/Al₂O₃ mixtures and subsequent annealing, was investigated by XRD, EDX, and ²⁷Al MAS NMR. The structure of the Bi₂(Ga_xAl_1−x)₄O₉ solid solutions is found to be orthorhombic, space group Pbam (No. 55). The lattice parameters of the Bi₂(Ga_xAl_1−x)₄O₉ series increase linearly with increasing gallium content. Rietveld refinement of the XRD data as well as the analysis of the ²⁷Al MAS NMR spectra show a preference of gallium cations for the tetrahedral sites in Bi₂(Ga_xAl_1−x)₄O₉. As a consequence, this leads to a far from random distribution of Al and Ga cations across the whole series of solid solutions.     

Bi2−xLnxWO6: a novel layered structure type related to the Aurivillius phases

The crystal structure of Bi_0.7Yb_1.3WO₆ (a representative of the isomorphous series Bi_2−xLn_xWO₆; 0.3<x<1.3, for most lanthanides) has been determined. Contrary to previous suggestions, this structure type (space group A2; a=8.1070(3) Å, b=3.7048(2) Å, c=15.8379(8) Å, β=103.548(4)°) contains layers of stoichiometry WO₄, containing WO₆ octahedra sharing both edges and corners. These layers alternate with fluorite-like (Bi/Yb)₂O₂ sheets; this is a novel and unexpected arrangement and contrasts dramatically with the purely corner-sharing octahedral WO₄-layer in the parent Aurivillius phase Bi₂WO₆.     

Synthesis and structural analysis of Bi2−ySryIr2O7, a new pyrochlore solid solution

This paper presents a study of the synthesis and structural properties of the new pyrochlore-type Bi_2−ySr_yIr₂O₇ series. Ten compositions with 0.0≤y≤0.9 were prepared by solid-state reaction with thermal treatments at 873, 1073 and 1323 K under atmospheric pressure conditions. Structural refinements from X-ray powder diffraction data by the Rietveld method show that all compounds of the Bi_2−ySr_yIr₂O₇ solid solution crystallize in a α-pyrochlore structure. The main structural difference when bismuth is substituted by strontium concerns the x position of the O1 (x, ?, ?). This substitution significantly increases the Bi/Sr-O1 distance and diminishes the Ir-O1 distance; this implies that the Ir-O1-Ir bond angle increases. With the Sr substitution, the IrO₆ local configuration goes from a flattened trigonal antiprism, y<0.5, to an elongated one, y>0.5, passing through an octahedral array, y∼0.5. The electrical consequences of these structural changes observed in this system are qualitatively explained with electronic structure calculations, this behavior agrees very well with those observed in other pyrochlore systems A₂M₂O₇ (A=rare earth cations or Tl⁺, Pb²⁺, or Bi³⁺, and M=Ru or Ir).     

Structure and crystal chemistry of fluorite-related Bi38Mo7O78 from single crystal X-ray diffraction and ab initio calculations

The floating-zone furnace method was used to synthesize single crystals of the fluorite-related δ-Bi₂O₃-type phase Bi₃₈Mo₇O₇₈ for the first time. Single crystal synchrotron X-ray diffraction data, in conjunction with ab initio (density functional theory) calculations, were used to solve, optimize, and refine the 5×3×3 commensurate superstructure of fluorite-type δ-Bi₂O₃ in Pbcn (a=28.7058(11) Å, b=16.8493(7) Å and c=16.9376(6) Å, Z=4, R_F=11.26%, wR_I=21.67%). The structure contains stepped channels of Mo⁶⁺ in tetrahedral environments along the b axis and chains of Mo⁶⁺ in octahedral environments along the ac plane. The role of the stepped channels in oxide ion conduction is discussed. The simultaneous presence of both tetrahedral and octahedral coordination environments for Mo⁶⁺, something not previously observed in Mo⁶⁺-doped δ-Bi₂O₃-type phases, is supported by charge balance considerations in addition to the results of crystallographic and ab initio analysis.     

Synthesis, Structures, and Thermal Expansion of the La2W2−xMoxO9 Series

The La₂W_2−xMo_xO₉ series has been synthesized by the ceramic method. An alternative synthesis using microwave radiation is also reported. La₂W₂O₉ has two polymorphs and the low-temperature phase (α) transforms to the high-temperature form (β) at 1077°C. The influence of the W/Mo substitution in this phase transition has been investigated by DTA. The β structure for x≥0.7 compositions can be prepared as single phase at any cooling rate. The β phase for 0.3≤x≤0.7 compounds can be prepared as single phase by quenching, whereas a mixture of α and β phases is obtained by slow cooling. The W/Mo ratio in both coexisting phases is different with the β-phase having a higher Mo content. The x=0.1 and 0.2 compounds have been prepared as mixtures of phases. The room temperature structure of β-La₂W_1.7Mo_0.3O₉ has been analyzed by the Rietveld method in P2₁3 space group. The final R-factors were R_WP=9.0% and R_F=5.6% with a structure similar to that of β-La₂Mo₂O₉. Finally, the thermal expansion of both types of structures has been determined from a thermodiffractometric study. The thermal expansion coefficients were 2.9×10⁻⁶ and 9.7×10⁻⁶°C⁻¹ for α-La₂W₂O₉ and β-La₂W_1.2Mo_0.8O₉, respectively.     

Crystal structure and ionic conductivity of the series A2Bi24Mo8X2O68 (A = Ca, Sr and Ba and X = Cr and W) in the Bi2O3?MoO3 system

A series of A₂Bi₂₄Mo₈X₂O₆₈ compounds, Ca₂Bi₂₄Mo₈Cr₂O₆₈ (CBMC), Sr₂Bi₂₄Mo₈Cr₂O₆₈ (SBMC), Pb₂Bi₂₄Mo₈Cr₂O₆₈ (PBMC) and Ba₂Bi₂₄Mo₈W₂O₆₈ (BBMW) have been synthesized by the solid-state method and characterized by single crystal X-ray diffraction. The compounds index into the monoclinic P2/c system with a=11.687(4) ?, 5.784(2) ?, 24.728(9) ?, 101.911(6)°, Z=1; 11.673(6) ?, 5.775(3) ?, 24.670(2) ?, 101.757(8)°, Z=1; 11.638(3) ?, 5.790(1) ?, 24.655(6) ?, 101.716(4)°, Z=1 and 11.718(6) ?, 5.818(3) ?, 24.716(12) ?, 101.835(9)°, Z=1 for CBMC, SBMC, PBMC and BBMW, respectively. The structures were solved by direct methods and refined to R indices of 0.081, 0.065, 0.080 and 0.079 respectively. These compounds are isostructural with Bi₂₆Mo₁₀O₆₉ and the structure consists of columns of [Bi₁₂O₁₄] along the b-axis, surrounded by Mo/Cr/WO₄ tetrahedra. a.c. impedance studies indicate higher values of ionic conductivity for the tungsten-substituted compounds. Supplementary material The crystal data of CBMC, SBMC, PBMC and BBMW have been deposited at the Fachinformationszentrum Karlsruhe (FIZ) with the numbers CSD 415143, CSD 415145, CSD 415144 and CSD 415142, respectively.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

Synthesis crystal structure and ionic conductivity of Ca0.5Bi3V2O10 and Sr0.5Bi3V2O10

Two new compounds Ca_0.5Bi₃V₂O₁₀ and Sr_0.5Bi₃V₂O₁₀ have been synthesized in the ternary system: MO-Bi₂O₃-V₂O₅ system (M=M²⁺). The crystal structure of Sr_0.5Bi₃V₂O₁₀ has been determined from single crystal X-ray diffraction data, space group and Z=2, with cell parameters a=7.1453(3) Å, b=7.8921(3) Å, c=9.3297(3) Å, α=106.444(2)°, β=94.088(2)°, γ=112.445(2)°, V=456.72(4) Å³. Ca_0.5Bi₃V₂O₁₀ is isostructural with Sr_0.5Bi₃V₂O₁₀, with, a=7.0810(2) Å, b=7.8447(2) Å, c=9.3607(2) Å, α=106.202(1)°, β=94.572(1)°, γ=112.659(1)°, V=450.38(2) Å³ and its structure has been refined by Rietveld method using powder X-ray data. The crystal structure consists of infinite chains of (Bi₂O₂) along c-axis formed by linkage of BiO₈ and BiO₆ polyhedra interconnected by MO₈ polyhedra forming 2D layers in ac plane. The vanadate tetrahedra are sandwiched between these layers. Conductivity measurements give a maximum conductivity value of 4.54×10⁻⁵ and 3.63×10⁻⁵ S cm⁻¹ for Ca_0.5Bi₃V₂O₁₀ and Sr_0.5Bi₃V₂O₁₀, respectively at 725 °C.     

A novel 1D organic-inorganic hybrid based on alternating heteropolyanions [GeMo12O40] and isopolyanions [Mo6O22]

A novel one-dimensional (1D) coordination polymer [{Cu(2,2′-bpy)}₆(Mo₆O₂₂)][GeMo₁₂O₄₀]·H₂O (2,2′-bpy=2,2′-bipyridine), which represents the first example of 1D organic-inorganic hybrid based on a Keggin-type heteropolyanion [GeMo₁₂O₄₀]⁴⁻ and an unprecedented isopolyanion [Mo₆O₂₂]⁸⁻, has been hydrothermally synthesized and characterized by single crystal X-ray diffraction. Crystal data: C₆₀H₅₀Cu₆GeMo₁₈N₁₂O₆₃, monoclinic, P2₁/c, a=13.9344(3), b=20.0329(3), c=17.2151(3) Å; β=94.0220(10)°, V=4793.70(15) Å³, T=293(2) K; Z=2.     

Approach to thermal properties and electronic polarizability from average single bond strength in ZnOBi2O3B2O3 glasses

The glass transition temperature (T_g), density, refractive index, Raman scattering spectra, and X-ray photoelectron spectra (XPS) for xZnO-yBi₂O₃-zB₂O₃ glasses (x=10-65, y=10-50, z=25-60 mol%) are measured to clarify the bonding and structure features of the glasses with large amounts of ZnO. The average electronic polarizability of oxide ions (α_O2−) and optical basicity (Λ) of the glasses estimated using Lorentz-Lorenz equation increase with increasing ZnO or Bi₂O₃ content, giving the values of α_O2−=1.963 Å³ and Λ=0.819 for 60ZnO-10Bi₂O₃-30B₂O₃ glass. The formation of BOBi and BOZn bridging bonds in the glass structure is suggested from Raman and XPS spectra. The average single bond strength (B_MO) proposed by Dimitrov and Komatsu is applied to the glasses and is calculated using single bond strengths of 150.6 kJ/mol for ZnO bonds in ZnO₄ groups, 102.5 kJ/mol for BiO bonds in BiO₆ groups, 498 kJ/mol for BO bonds in BO₃ groups, and 373 kJ/mol for BO bonds in BO₄ groups. Good correlations are observed between T_g and B_MO, Λ and B_MO, and T_g and Λ, proposing that the average single bond strength is a good parameter for understanding thermal and optical properties of ZnOBi₂O₃B₂O₃ glasses.     

Structural Characterization of the Complex Perovskites Ba1−xLaxTi1−xCrxO3

The series Ba_1−xLa_xTi_1−xCr_xO₃ (0≤x≤1) was synthesized at 1400°C for about 60 h. Their structure was carefully analyzed by the use of powder X-ray diffraction and Rietveld analysis software GSAS (General Structure Analysis System). Four solid solutions are found in this series: tetragonal solid solution Ba_1−xLa_xTi_1−xCr_xO₃ (0≤x≤0.029), cubic solid solution Ba_1−xLa_xTi_1−xCr_xO₃ (0.0365≤x≤0.600), rhombohedral solid solution Ba_1−xLa_xTi_1−xCr_xO₃ (0.700≤x≤0.873), and orthorhombic solid solution Ba_1−xLa_xTi_1−xCr_xO₃ (0.956≤x≤1). There are corresponding two-phase regions between the adjacent two solid solutions. The detailed lattice parameters are presented. The relationship between the lattice parameters and the composition of the solid solutions is developed.     

Crystal structure, thermal and magnetic properties of Cr2V4O13

Cr₂V₄O₁₃, a tetravanadate of Cr³⁺ has been prepared by repeated heating of stoichiometric amounts of Cr₂O₃ and V₂O₅ and its crystal structure is refined by Rietveld refinement of the powder XRD data. This compound crystallizes in a monoclinic lattice with unit cell parameters: a=8.2651(3), b=9.2997(3), c=14.5215(5) Å, β=102.618(3)°, V=1089.21(6) Å³ and Z=4 (Space group: P2₁/c). The U shaped (V₄O₁₃)⁶⁻ formed by corner connected VO₄ tetrahedra links the Cr₂O₁₀ (dimers of two edge shared CrO₆ octahedra) forming a three dimensional network structure of Cr₂V₄O₁₃. This compound is stable up to 635 °C and peritectically decomposes to orthorhombic CrVO₄ and V₂O₅ above this temperature. A possible long range antiferromagnetic ordering below 10 K is suggested from the squid magnetometry and electron paramagnetic resonance (epr) spectroscopic studies of Cr₂V₄O₁₃.     

Crystal Structure of Pseudorhombohedral InFe1−xTixO3+x/2 (x=2/3)

The structure of pseudorhombohedral-type InFe_1−xTi_xO_3−x/2 (x=2/3) was refined by Rietveld profile fitting. The crystal is a commensurate member of a series in a solution range on InFeO₃-In₂Ti₂O₇ including incommensurate structures. The structure with the unit cell of a=5.9188(1), b=10.1112(2), and c=6.3896(1) Å, β=108.018(2)°, and a space group P2₁/a is the alternate stacking of an edge-shared InO₆ octahedral layer and an Fe/Ti-O plane along c^*. Metal sites on the Fe/Ti-O plane are surrounded by four oxygen atoms on the Fe/Ti-O plane and two axial ones. Electric conductivities of the order 10⁻⁴ S/cm were observed for the samples at 1000 K, while the oxide ion transport number is almost zero as no electromotive force was detected by an oxygen concentration cell.     

Series of compositions Bi2(M′xM1−x)4O9 (M′, M=Al, Ga, Fe; 0≤x≤1) with mullite-type crystal structure: Synthesis, characterization and O/O exchange experiment

Series of compositions Bi₂(M′_xM_1−x)₄O₉ with x=0.0, 0.1,…, 1.0 and M′/M=Ga/Al, Fe/Al and Fe/Ga were synthesized by dissolving appropriate amounts of corresponding metal nitrate hydrates in glycerine, followed by gelation, calcination and final heating at 800 °C for 24 h. The new compositions with M′/M=Ga/Al form solid-solution series, which are isotypes to the two other series M′/M=Fe/Al and Fe/Ga. The XRD data analysis yielded in all cases a linear dependence of the lattice parameters related on x. Rietveld structure refinements of the XRD patterns of the new compounds, Bi₂(Ga_xAl_1−x)₄O₉ reveal a preferential occupation of Ga in tetrahedral site (4 h). The IR absorption spectra measured between 50 and 4000 cm⁻¹ of all systems show systematic shifts in peak positions related to the degree of substitution. Samples treated in ¹⁸O₂ atmosphere (16 h at 800 °C, 200 mbar, 95% ¹⁸O₂) for ¹⁸O/¹⁶O isotope exchange experiments show a well-separated IR absorption peak related to the M-¹⁸O_c-M vibration, where O_c denotes the common oxygen of two tetrahedral type MO₄ units. The intensity ratio of M-¹⁸O_c/M-¹⁶O_c IR absorption peaks and the average crystal sizes were used to estimate the tracer diffusion coefficients of polycrystalline Bi₂Al₄O₉ (D=2×10⁻²² m²s⁻¹), Bi₂Fe₄O₉ (D=5×10⁻²¹ m²s⁻¹), Bi₂(Ga/Al)₄O₉ (D=2×10⁻²¹ m²s⁻¹) and Bi₂Ga₄O₉ (D=2×10⁻²⁰ m²s⁻¹).     

Quaternary selenostannates Na2−xGa2−xSn1+xSe6 and AGaSnSe4 (A=K, Rb, and Cs) through rapid cooling of melts. Kinetics versus thermodynamics in the polymorphism of AGaSnSe4

The quaternary alkali-metal gallium selenostannates, Na_2−xGa_2−xSn_1+xSe₆ and AGaSnSe₄ (A=K, Rb, and Cs), were synthesized by reacting alkali-metal selenide, Ga, Sn, and Se with a flame melting-rapid cooling method. Na_2−xGa_2−xSn_1+xSe₆ crystallizes in the non-centrosymmetric space group C2 with cell constants a=13.308(3) Å, b=7.594(2) Å, c=13.842(3) Å, β=118.730(4)°, V=1226.7(5) Å³. α-KGaSnSe₄ crystallizes in the tetragonal space group I4/mcm with a=8.186(5) Å and c=6.403(5) Å, V=429.1(5) Å³. β-KGaSnSe₄ crystallizes in the space group P2₁/c with cell constants a=7.490(2) Å, b=12.578(3) Å, c=18.306(5) Å, β=98.653(5)°, V=1705.0(8) Å³. The unit cell of isostructural RbGaSnSe₄ is a=7.567(2) Å, b=12.656(3) Å, c=18.277(4) Å, β=95.924(4)°, V=1741.1(7) Å³. CsGaSnSe₄ crystallizes in the orthorhombic space group Pmcn with a=7.679(2) Å, b=12.655(3) Å, c=18.278(5) Å, V=1776.1(8) Å³. The structure of Na_2−xGa_2−xSn_1+xSe₆ consists of a polar three-dimensional network of trimeric (Sn,Ga)₃Se₉ units with Na atoms located in tunnels. The AGaSnSe₄ possess layered structures. The compounds show nearly the same Raman spectral features, except for Na_2−xGa_2−xSn_1+xSe₆. Optical band gaps, determined from UV-Vis spectroscopy, range from 1.50 eV in Na_2−xGa_2−xSn_1+xSe₆ to 1.97 eV in CsGaSnSe₄. Cooling of the melts of KGaSnSe₄ and RbGaSnSe₄ produces only kinetically stable products. The thermodynamically stable product is accessible under extended annealing, which leads to the so-called γ-form (BaGa₂S₄-type) of these compounds.     

Synthesis and crystal structure of Bi6.4Pb0.6P2O15.2: A new polymorph in the series Bi6+xM1−xP2O15+y

Bi_6.4Pb_0.6P₂O_15.2 is a polymorph of structures with the general stoichiometry Bi_6+xM_1−xP₂O_15+y. However, unlike previously published structures that consist of layers formed by edge sharing OBi₄ tetrahedra bridged by PO₄ and TO₆ (T=transition metal) tetrahedra and octahedra the title compound's structure is more complex. It is monoclinic, C2, a=19.4698(4) Å, b=11.3692(3) Å, c=16.3809(5) Å, β=101.167(1)°, Z=10. Single-crystal X-ray diffraction data were refined by least squares on F² converging to R₁=0.0387, wR₂=0.0836 for 7023 intensities. The crystal twins by mirror reflection across (001) as the twin plane and twin component 1 equals 0.74(1). Oxygen ions are in tetrahedral coordination to four metal ions and the O(BiPb)₄ units share corners to form layers that are part of the three-dimensional framework. Eight oxygen ions form a cube around the two crystallographically independent Pb ions. Pb-O bond lengths vary from 2.265(14) to 2.869(14) Å. Pairs of such cubes share an edge to form a Pb₃O₂₀ unit. The two oxygen ions from the unshared edges are part of irregular Bi polyhedra. Other oxygen ions of Bi polyhedra are part only of O(BiPb)₄ units, and some oxygen ions of the polyhedra are also part of PO₄ tetrahedra. One, two, three and or four PO₄ moieties are connected to the Bi polyhedra. Bi-O bond lengths ?3.1 Å vary from 2.090(12) to 3.07(3) Å. The articulations of Pb cubes, Bi polyhedra and PO₄ tetrahedra link into the three-dimensional structure.     

Preparation and crystal structure of [Bi3I(C4H8O3H2)2(C4H8O3H)5]2Bi8I30 containing the novel polynuclear [Bi8I30] anion

Preparation and crystal structure of the novel compound [Bi₃I(C₄H₈O₃H₂)₂(C₄H₈O₃H)₅]₂Bi₈I₃₀ are reported. The title compound is prepared by heating of BiI₃ and diethylene glycol at 413 K in a sealed quartz glass tube filled with argon. Deep red single crystals are grown and applied to perform X-ray powder diffraction and X-ray single-crystal diffraction measurements. The compound crystallizes triclinic with space group P-1: Z=2, a=13.217(1) Å, b=15.277(1) Å, c=22.498(1) Å, α=84.33(1), β=73.18(1), γ=67.48(1). [Bi₃I(C₄H₈O₃H₂)₂(C₄H₈O₃H)₅]₂Bi₈I₃₀ comprises the novel polynuclear [Bi₈I₃₀]⁶⁻ anion and [Bi₃I(C₄H₈O₃H₂)₂(C₄H₈O₃H)₅]³⁺ as the cation. Cation as well as the anion can be assumed to represent intermediates between solid BiI₃ and BiI₃ completely dissolved in diethylene glycol.