Synthesis and Structure of the New Ammonium Indium Phosphate (NH4)In(OH)PO4

A new ammonium indium phosphate (NH₄)In(OH)PO₄ was prepared by hydrothermal reaction in the In₂O₃-NH₄H₂PO₄-NH₃/OH system (T=200°C, autogenous pressure, 7 days). The formula (NH₄)In(OH)PO₄ was determined on the basis of chemical and thermal analysis (TG/DSC), X-ray powder diffraction and IR-spectroscopy. (NH₄)In(OH)PO₄ crystallizes in the tetragonal system with space group P4₃2₁2 (No. 96); a=9.4232(1) Å, c=11.1766(1) Å, V=992.45(2) ų; Z=8. The crystal structure was refined by the Rietveld method (R_w=6.35%, R_p=5.10%). The second-harmonic generation study confirmed that structure of (NH₄)In(OH)PO₄ does not have a center of symmetry. The cis-InO₄(OH)₂ octahedra form helical chains, parallel to the c-axis. The In-O-In bonds are nearly equidistant. The chains are interconnected by phosphate tetrahedra and create tunnels containing the NH₄⁺ ions along the c-axis. (NH₄)In(OH)PO₄ is isostructural with RbIn(OH)PO₄.     

Synthesis and crystal structure of a new open-framework iron phosphate (NH4)4Fe3(OH)2F2[H3(PO4)4]: Novel linear trimer of corner-sharing Fe(III) octahedra

A new iron phosphate (NH₄)₄Fe₃(OH)₂F₂[H₃(PO₄)₄] has been synthesized hydrothermally at HF concentrations from 0.5 to 1.2 mL. Single-crystal X-ray diffraction analysis reveals its three-dimensional open-framework structure (monoclinic, space group P2₁/n (No. 14), a=6.2614(13) Å, b=9.844(2) Å, c=14.271(3) Å, β=92.11(1)°, V=879.0(3) Å³). This structure is built from isolated linear trimers of corner-sharing Fe(III) octahedra, which are linked by (PO₄) groups to form ten-membered-ring channels along [1 0 0]. This isolated, linear trimer of corner-sharing Fe(III) octahedra, [(FeO₄)₃(OH)₂F₂], is new and adds to the diverse linkages of Fe polyhedra as secondary building units in iron phosphates. The trivalent iron at octahedral sites for the title compound has been confirmed by synchrotron Fe K-edge XANES spectra and magnetic measurements. Magnetic measurements also show that this compound exhibit a strong antiferromagnetic exchange below T_N=17 K, consistent with superexchange interactions expected for the linear trimer of ferric octahedra with the Fe-F-Fe angle of 132.5°.     

New Gallium Phosphate Frameworks Containing 1,4-Diaminobutane and 1,5-Diaminopentane: [NH3(CH2)xNH3][Ga4(PO4)4(HPO4)] and [NH3(CH2)xNH3][Ga(PO4)(HPO4)] (x=4 and 5)

Two new gallium phosphates, [NH₃(CH₂)₄NH₃][Ga₄(PO₄)₄ (HPO₄)] (I) and [NH₃(CH₂)₄NH₃][Ga(PO₄)(HPO₄)] (II), have been synthesized under solvothermal conditions in the presence of 1,4-diaminobutane and their structures determined using room-temperature single-crystal X-ray diffraction data. Compound (I) (M_r=844.90, triclinic, space group P-1, a=9.3619(3), b=10.1158(3) and c=12.6456(5) Å, α=98.485(1), β=107.018(2) and γ=105.424(1)°; V=1070.39 ų, Z=2, R=3.68% and R_w=4.40% for 2918 observed data [I>3(σ(I))]) consists of GaO₄ and PO₄ tetrahedra and GaO₅ trigonal bipyramids linked to generate an open three-dimensional framework containing 4-, 6-, 8-, and 12-membered rings of alternating Ga- and P-based polyhedra. 1,4-Diaminobutane dications are located in channels bounded by the 12-membered rings in the two-dimensional pore network and are held to the framework by hydrogen bonding. Compound (II) (M_r=350.84, monoclinic, space group P2₁/c, a=4.8922(1), b=18.3638(6) and c=13.7468(5) Å, β=94.581(1)°; V=1227.76 ų, Z=4, R=2.95% and R_w=3.37% for 2050 observed data [I>3(σ(I))]) contains chains of edge-sharing 4-membered rings of alternating GaO₄ and PO₄ tetrahedra constituting a backbone from which hang ‘pendant’ PO₃(OH) groups. Hydrogen bonding between the GaPO framework and the diamine dications holds the structure together. A previously reported phase, [NH₃(CH₂)₄NH₃][Ga₄(PO₄)₄(HPO₄)] (V), structurally related but distinct from its stoichiometric equivalent, (I), has been prepared as a pure phase by this method. Two further materials, [NH₃(CH₂)₅NH₃][Ga₄(PO₄)₄(HPO₄)] (III) (tricli- nic, lattice parameters from PXD: a=9.3565(4), b=5.0156(2) and c=12.7065(4) Å, α=96.612(3), β=102.747(4) and γ=105.277(3)°) and [NH₃(CH₂)₅NH₃][Ga(PO₄)(HPO₄)] (IV) (M_r=364.86, monoclinic, space group P2₁/n, a=4.9239(2), b=13.2843(4) and c=19.5339(7) Å, β=96.858(1)°; V=1268.58 ų, Z=4, R=3.74% and R_w=4.44% for 2224 observed room-temperature data [I>3(σ(I))]), were also prepared under similar conditions in the presence of 1,5-diaminopentane. (III) and (IV) are structurally related to, yet distinct from (I) and (II) respectively.     

A new sodium hydroxygallophosphate containing tetrameric gallium units: Na3[Ga4O(OH)(H2O)(PO4)4]·H2O

A new sodium hydroxygallophosphate, Na₃Ga₄O(OH)(H₂O)(PO₄)₄·H₂O, has been prepared by hydrothermal synthesis. Its structure has been determined from a single-crystal X-ray diffraction study. It crystallizes in the P2₁/c space group with the cell parameters a=9.445(2) Å, b=9.028(1) Å, c=19.209(3) Å, β=102.08(2), V=1603.4(4) Å³. Its three-dimensional framework can be described from PO₄ monophosphate groups sharing their apices with original Ga₄O₁₆(OH)(H₂O) tetrameric building units, which result from the assembly of one GaO₄ tetrahedron, one GaO₅ trigonal bipyramid and two octahedra: GaO₅(OH) and GaO₄(OH)(H₂O). The sodium cations and one water molecule are located in tunnels running along b.     

Hydro(solvo)thermal synthesis and structural characterization of a new organically templated gallophosphate: [H3N(CH2)2NH3]1/2·[Ga5 (PO4)4(OH)4]

A new three-dimensional open-framework gallophosphate: [H₃N(CH₂)₂NH₃]_1/2·[Ga₅ (PO₄)₄(OH)₄] has been prepared by hydro(solvo)thermal synthesis in presence of ethylenediamine (en) as structure-directing agent. Its structure was determined by means of single-crystal X-ray diffraction analysis with the following crystal data: monoclinic space group C2/m, a=10.1604(9) Å, b=12.0085(15) Å, c=7.1892(7) Å, β=90.797(6)°, V=877.08(16) Å³, Z=2, R₁=0.0264, wR₂=0.0764. The total numbers of measured reflections and unique reflections were 3508 and 1300, respectively. It is built up from a new secondary building unit (SBU) Ga₄P₄O₂₀(OH)₄, in which Ga atoms exhibit distorted trigonal bipyramidal coordination and P atoms are in tetrahedral coordination. The SBU Ga₄P₄O₂₀(OH)₄ are linked into a layer by bridge oxygen atoms. The GaO₄(OH)₂ octahedra link the layers into a three-dimentional framework. Diprotonated ethylenediamine was found in the channel of the framework. The material was characterized by IR spectroscopy, ¹H NMR spectra, thermogravimetric and differential thermal analyses and elemental analysis.     

Synthesis and characterization of a cadmium germanium phosphate CdGe(OH)3PO4 with an open framework

A new three-dimensional (3D) framework cadmium germanium phosphate, CdGe(OH)₃PO₄ was synthesized by solvothermal methods. The crystal structure of CdGe(OH)₃PO₄ was established by single-crystal X-ray diffraction: CdGeH₃O₇P, Orthorhombic, Cmca, a=7.1415(7) Å, b=10.9034(1) Å, c=13.1098(1) Å, Z=8, R₁=0.0365 (F²>2σ(F²) and wR₂=0.0985 (all data). The framework of CdGe(OH)₃PO₄ is built by a mixed network of GeO₆, CdO₆ octahedra and PO₄ tetrahedra, which are linked to form a 3-membered ring (3-MR). The GeO₆ and CdO₆ octahedra share common vertexes and edges, respectively, to form one-dimensional (1D) Ge-O-Ge and Cd-O-Cd chains, which are further connected forming corrugated Ge-O-Cd layers. The layers are linked by PO₄ tetrahedra, leading to a 3D open-framework structure with 3- and 6-MR channels.     

A sodium gallophosphate with an original tunnel structure: NaGa2(OH)(PO4)2

A new sodium gallophosphate, NaGa₂(OH)(PO₄)₂, has been obtained by hydrothermal synthesis under autogeneous pressure at 473 K. It crystallizes in the P2₁/n space group with the cell parameters a=8.9675(8) Å, b=8.9732(5) Å, c=9.2855(7) Å, β=114.812(6)°, V=678.2 Å³ (Z=4). In its original three-dimensional framework, monophosphate groups share their apices with [Ga₄O₁₆(OH)₂] tetrameric units, which are built from two GaO₅(OH) octahedra and two GaO₄(OH) trigonal bipyramids. The sodium cations are located in tunnels running along a, whereas the tunnels running along b are empty.     

A Vanadium (V) Hydroxymonophosphate Hydrate with a “Tape-Like” structure: K3(VO2)2PO4PO3OH·H2O

A new vanadium (V) hydroxymonophosphate hydrate, K₃(VO₂)₂PO₄PO₃OH·H₂O, with a “tape-like” structure has been synthesized. This compound crystallizes in the space group P2₁/c with a=5.099(1) Å, b=29.168(3) Å, c=8.115(1) Å, β=91.65(1)°. Its structure consists of [V₂P₂O₁₁OH]_∞ ribbons built up of corner-sharing VO₅ pyramids, PO₄, and PO₃OH tetrahedra, interleaved with K⁺ ions and H₂O molecules. In spite of its unidimensional character, this structure forms pentagonal tunnels. Relationships with frameworks involving tetragonal tunnels are studied.     

Hydrothermal Synthesis, Single-Crystal Structure Analysis, and Solid-State NMR Characterization of Zn2(OH)0.14(3)F0.86(3)(PO4)

The zinc fluoro phosphate Zn₂F(PO₄) has been produced by hydrothermal synthesis employing hydrofluoric acid as a mineralizer in a H₂O or D₂O medium. A single-crystal X-ray synchrotron diffraction analysis of Zn₂F(PO₄) shows that the zinc fluoro phosphate is monoclinic, a=9.690(1), b=12.793(1), and c=11.972(1) Å, β=108.265(1)°, space group P2₁/c, No. 14, Z=16. Reflections hkl with k=2n+1 are weak but significant and the structure shows pseudosymmetry. Zn₂F(PO₄) has the wagnerite-type M₂F(XO₄) structure with four Zn atoms each coordinated to four O atoms and one F atom while four other Zn atoms are coordinated to four O atoms and two F atoms. A difference Fourier map, calculated from the single-crystal X-ray data, shows additional electron density close to the four fluorine atoms, indicating a possible partial substitution of F⁻ by OH⁻ ions. This is unambiguously confirmed by ³¹P-{¹H} cross-polarization magic-angle spinning (MAS) and by ¹H/²H MAS NMR spectroscopy. The narrow line width observed for the ¹H resonance and the unique set of ²H quadrupole coupling parameters (obtained for the Zn₂F(PO₄) sample using D₂O as medium) show that ¹H/²H is present as OH(D) groups rather than as water of crystallization in the structure. Quantitative ¹H MAS NMR analysis shows that the composition of the sample is Zn₂(OH)_0.14(3)F_0.86(3)(PO₄). The high-speed ¹⁹F MAS NMR spectrum exhibits two resolved resonances with equal intensity, which are ascribed to an overlap of resonances from the four distinct fluorine sites in Zn₂(OH)_0.14(3)F_0.86(3)(PO₄).     

Four new hydroxymonophosphates with closely related intersecting tunnels structures: The series AM(PO3(OH))2 with A=Rb, Cs; M=Fe, Al, Ga, In

The family of hydroxymonophosphates of generic formula AM^III(PO₃(OH))₂ has been revisited using hydrothermal techniques. Four new phases have been synthesized: CsIn(PO₃(OH))₂, RbFe(PO₃(OH))₂, RbGa(PO₃(OH))₂ and RbAl(PO₃(OH))₂. Single crystal diffraction studies show that they exhibit two different structural types from previously observed other phases with A=H₃O, NH₄, Rb and M=Al, V, Fe. The “Cs-In” and “Rb-Fe” phosphates crystallize in the triclinic space group , with the cell parameters a=7.4146(3) Å, b=9.0915(3) Å, c=9.7849(3) Å, α=65.525(3)°, β=70.201(3)°, γ=69.556(3)° and V=547.77(4) Å³ (Z=3) for CsIn(PO₃(OH))₂ and a=7.2025(4) Å, b=8.8329(8) Å, c=9.4540(8) Å, α=65.149(8)°, β=70.045(6)°, γ=69.591(6)° and V=497.44(8) Å³ (Z=3) for α-RbFe(PO₃(OH))₂. The “Rb-Al” and “Rb-Ga” phosphates crystallize in the Rc space group, with a=8.0581(18) Å and c=51.081(12) Å (V=2872.5(11) Å³ and Z=18) for RbAl(PO₃(OH))₂ and a=8.1188(15) Å and c=51.943(4) Å (V=2965(8) Å and Z=18) for RbGa(PO₃(OH))₂. These two structural types are closely related. Both are built up from M^IIIO6 octahedra sharing their apices with PO₃(OH) tetrahedra to form [M₃(PO₃OH)₆] units, but the latter exhibits a different configuration of their tetrahedra. The three-dimensional host-lattices result from the connection of the [M₃(PO₃OH)₆] units and they present numerous intersecting tunnels containing the monovalent cations.     

The crystal structure, thermal behaviour and ionic conductivity of a novel lithium gadolinium polyphosphate LiGd(PO3)4

Crystal structure and ionic conductivity of lithium gadolinium polyphosphate, LiGd(PO₃)₄, were investigated. Single crystals of the title compound have been grown by a flux technique. The structure of this novel phosphate was determined by single crystal X-ray diffraction techniques. LiGd(PO₃)₄ is isotypic with LiNd(PO₃)₄. It crystallizes in the monoclinic space group C2/c with the unit cell parameters a=16.386(2), b=7.059(3), c=9.677(2) Å, β=126.12(1)°, V=904.2(4) Å³ and Z=4. The structure refined from 967 independent reflections leads to R₁=0.0167 and wR₂=0.0458. The lattice of LiGd(PO₃)₄ is built of twisted zig-zag chains running along with the b direction and make up of PO₄ tetrahedra sharing two corners, connected to the GdO₈ and LiO₄ polyhedra by common oxygen atoms to form a three-dimensional framework. Differential and thermogravimetric thermal analysis are given. The thermal curve of this compound was recorded and interpreted in agreement with impedance measurements. The ionic conductivity has been measured on pellet of the polycrystalline powder and evaluated as a function of temperature. This phase showed the conductivity of 2×10⁻⁶ and 2×10⁻⁴ Ω⁻¹ cm⁻¹ at 682 and 951 K, respectively.     

Synthesis and Structure of a New Layered Zincophosphate Zn6(PO4)5(HPO4)·C8N5H28·5H2O, Intercalated with Quintuply Protonated Tetraethylenepentamine

A new two-dimensional zinc phosphate Zn₆(PO₄)₅(HPO₄)·C₈N₅H₂₈·5H₂O has been synthesized hydrothermally using tetraethylenepentamine (TEPA) as structure-directing agent and its structure was determined by means of single-crystal X-ray diffraction. The title compound crystallizes in the orthorhombic system, space group Pca2₁ (No.29) with lattice parameters a=18.6286(12) Å, b=8.0804(5) Å, c=22.5019(15) Å, V= 3387.1(4) ų, Z=4, R₁=0.0389 and wR₂=0.0862 [4042 observed reflections with I>2σ(I)]. The structure involves a network of ZnO₄, PO₄, and PO₃(OH) tetrahedra forming macroanionic inorganic layers with eight-membered apertures. The charge compensation is achieved by the quintuply protonated TEPA molecule in interlamellar space, which interact with the inorganic layers via hydrogen bonding.     

Sr10[(PO4)5.5(BO4)0.5](BO2): Growth and crystal structure of a strontium phosphate orthoborate metaborate closely related to the apatite-type crystal structure

Single crystals of the strontium phosphate orthoborate metaborate, Sr₁₀[(PO₄)_5.5(BO₄)_0.5](BO₂), were grown from the melt and investigated by X-ray diffraction (space group , No. 147; a=9.7973(8) Å, c=7.3056(8) Å, V=607.29(10) Å³, Z=1). The crystal structure is closely related to apatite and contains linear metaborate groups, [BO₂]⁻ (point group D_∞h, B-O=1.284(11) Å) taking positions within the channels running along the three-fold inversion axis. Strontium sites are found to be fully occupied while [PO₄]³⁻ tetrahedra are partially replaced by [BO₄]⁵⁻ groups.     

Crystal structures of lazulite-type oxidephosphates TiTi3O3(PO4)3 and M4Ti27O24(PO4)24 (M=Ti, Cr, Fe)

Single crystals of the oxidephosphates Ti^IIITi^IV₃O₃(PO₄)₃ (black), Cr^III₄Ti^IV₂₇O₂₄(PO₄)₂₄ (red-brown, transparent), and Fe^III₄Ti^IV₂₇O₂₄(PO₄)₂₄ (brown) with edge-lengths up to 0.3 mm were grown by chemical vapour transport. The crystal structures of these orthorhombic members (space group F2dd ) of the lazulite/lipscombite structure family were refined from single-crystal data [Ti^IIITi^IV₃O₃(PO₄)₃: Z=24, a=7.3261(9) Å, b=22.166(5) Å, c=39.239(8) Å, R₁=0.029, wR₂=0.084, 6055 independent reflections, 301 variables; Cr^III₄Ti^IV₂₇O₂₄(PO₄)₂₄: Z=1, a=7.419(3) Å, b=21.640(5) Å, c=13.057(4) Å, R₁=0.037, wR₂=0.097, 1524 independent reflections, 111 variables; Fe^III₄Ti^IV₂₇O₂₄(PO₄)₂₄: Z=1, a=7.4001(9) Å, b=21.7503(2) Å, c=12.775(3) Å, R₁=0.049, wR₂=0.140, 1240 independent reflections, 112 variables). For Ti^IIITi^IVO₃(PO₄)₃ a well-ordered structure built from dimers [Ti^III,IV₂O₉] and [Ti^IV,IV₂O₉] and phosphate tetrahedra is found. The metal sites in the crystal structures of Cr₄Ti₂₇O₂₄(PO₄)₂₄ and Fe₄Ti₂₇O₂₄(PO₄)₂₄, consisting of dimers [M^IIITi^IVO₉] and [Ti^IV,IV₂O₉], monomeric [Ti^IVO₆] octahedra, and phosphate tetrahedra, are heavily disordered. Site disorder, leading to partial occupancy of all octahedral voids of the parent lipscombite/lazulite structure, as well as splitting of the metal positions is observed. According to Guinier photographs Ti^III₄Ti^IV₂₇O₂₄(PO₄)₂₄ (a=7.418(2) Å, b=21.933(6) Å, c=12.948(7) Å) is isotypic to the oxidephosphates M^III₄Ti^IV₂₇O₂₄(PO₄)₂₄ (M^III: Cr, Fe). The UV/vis spectrum of Cr₄Ti₂₇O₂₄(PO₄)₂₄ reveals a rather small ligand-field splitting Δ_o=14,370 cm⁻¹ and a very low nephelauxetic ratio β=0.72 for the chromophores [Cr^IIIO₆] within the dimers [Cr^IIITi^IVO₉].     

Syntheses and crystal structures of two new hydrated borates, Zn8[(BO3)3O2(OH)3] and Pb[B5O8(OH)]·1.5H2O

Two new hydrated borates, Zn₈[(BO₃)₃O₂(OH)₃] and Pb[B₅O₈(OH)]·1.5H₂O, have been prepared by hydrothermal reactions at 170 °C. Single-crystal X-ray structural analyses showed that Zn₈[(BO₃)₃O₂(OH)₃] crystallizes in a non-centrosymmetric space group R32 with a=8.006(2) Å, c=17.751(2) Å, Z=3 and Pb[B₅O₈(OH)]·1.5H₂O in a triclinic space group P1¯ with a=6.656(2) Å, b=6.714(2) Å, c=10.701(2) Å, α=99.07(2)°, β=93.67(2)°, γ=118.87(1)°, Z=2. Zn₈[(BO₃)₃O₂(OH)₃] represents a new structure type in which Zn-centered tetrahedra are connected via common vertices leading to helical ribbons _∞¹[Zn₈O₁₅(OH)₃]¹⁷⁻ that pack side by side and are further condensed through sharing oxygen atoms to form a three-dimensional _∞³[Zn₈O₁₁(OH)₃]⁹⁻ framework. The boron atoms are incorporated into the channels in the framework to complete the final structure. Pb[B₅O₈(OH)]·1.5H₂O is a layered compound containing double ring [B₅O₈(OH)]²⁻ building units that share exocyclic oxygen atoms to form a two-dimensional layer. Symmetry-center-related layers are stacked along the c-axis and held together by interlayer Pb²⁺ ions and water molecules via electrostatic and hydrogen bonding interactions. The IR spectra further confirmed the existence of both triangular BO₃ and OH groups in Zn₈[(BO₃)₃O₂(OH)₃], and BO₃, BO₄, OH groups as well as guest water molecules in Pb[B₅O₈(OH)]·1.5H₂O.     

Solvothermal synthesis of an open-framework zinc chlorophosphate, [C8N4H26][Zn3Cl(HPO4)3(PO4)], with a layer structure

A solvothermal reaction of ZnO, HCl, H₃PO₄, and N,N′(3-bisaminopropyl)-1,2-ethylenediamine (BAPEN) in diethyleneglycol at 160°C yields a new zinc chlorophosphate, [C₈N₄H₂₆][Zn₃Cl(HPO₄)₃(PO₄)], I. The structure comprises ZnO₄, ZnO₃Cl, HPO₄ and PO₄ tetrahedral units connected through their vertices giving rise to a layered structure with 10-membered apertures. The position of the Zn and P atoms gives rise to double-four ring like building unit with one Zn missing. The fully protonated amine molecules occupy the inter-lamellar region and interacts with the framework through N-H?O hydrogen bonds. Crystal data: M=792.85, orthorhombic, space group=Pca2₁ (no. 29), a=9.8410(2), b=15.0912(2), c=16.1220(4) Å, V=2394.32(8) Å³, Z=4, ρ_calc=2.199 g cm⁻³, μ(MoKα)=3.443 mm⁻¹, R₁=0.0520, wR₂=0.1256 and S=1.054.     

Hydrothermal synthesis, thermal, structural, spectroscopic and magnetic studies of the Mn5−xCox(HPO4)2(PO4)2(H2O)4 (x=1.25, 2, 2.5 and 3) finite solid solution

The Mn_5−xCo_x(HPO₄)₂(PO₄)₂(H₂O)₄ (x=1.25, 2, 2.5, 3) finite solid solution has been synthesized by mild hydrothermal conditions under autogeneous pressure. The phases crystallize in the C2/c space group with Z=4, belonging to the monoclinic system. The unit-cell parameters obtained from single crystal X-ray diffraction are: a=17.525(1), b=9.0535(6), c=9.4517(7) Å, β=96.633(5) ° being R1=0.0436, wR2=0.0454 for Mn75Co25; a=17.444(2), b=9.0093(9), c=9.400(1) Å, β=96.76(1) ° being R1=0.0381, wR2=0.0490 for Mn60Co40; a=17.433(2), b=8.9989(9), c=9.405(1) Å, β=96.662(9) ° being R1=0.0438, wR2=0.0515 for Mn50Co50 and a=17.4257(9), b=8.9869(5), c=9.3935(5) Å, β=96.685(4) ° being R1=0.0296, wR2=0.0460 for Mn40Co60. The structure consists of a three dimensional network formed by octahedral pentameric entities (Mn,Co)₅O₁₆(H₂O)₆ sharing vertices with the (PO₄)³⁻ and (HPO₄)²⁻ tetrahedra. The limit of thermal stability of these compounds is, approximately, 165 °C, near to this mean temperature the phases loose their water content in two successive steps. IR spectra show the characteristic bands of the water molecules and the phosphate and hydrogen-phosphate oxoanions. The diffuse reflectance spectra are consistent with the presence of MO₆ octahedra environments in slightly distorted octahedral geometry, except for the M(3)O₆ octahedron which presents a remarkable distortion and so a higher Dq parameter. The mean value for the Dq and B-Racah parameter for the M(1),(2)O₆ octahedra is 685 and 850 cm⁻¹, respectively. These parameters for the most distorted M(3)O₆ polyhedron are 825 and 880 cm⁻¹, respectively. The four phases exhibit antiferromagnetic couplings as the major magnetic interactions. However, a small spin canting phenomenon is observed at low temperatures for the two phases with major content in the anisotropic-Co(II) cation.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

A rare multi-coordinate tellurite, NH4ATe4O9·2H2O (ARb or Cs): The occurrence of TeO3, TeO4, and TeO5 Polyhedra in the same material

Two new tellurites, NH₄RbTe₄O₉·2H₂O and NH₄CsTe₄O₉·2H₂O have been synthesized and characterized. The compounds were synthesized hydrothermally, in near quantitative yields, using the alkali metal halide, TeO₂, and NH₄OH as reagents. The iso-structural materials exhibit layered, two-dimensional structural topologies consisting of TeO_x (x=3, 4, or 5) polyhedra separated by NH₄⁺, H₂O, Rb⁺ or Cs⁺ cations. Unique to these materials is the presence of TeO₃, TeO₄, and TeO₅ polyhedra. Thermogravimetric and infrared spectroscopic data are also presented. Crystal data: NH₄RbTe₄O₉·2H₂O: Monoclinic I2/a (no. 15), a=18.917(3) Å, b=6.7002(11) Å, c=21.106(5) Å, β=101.813(2)°, V=2618.5(9) Å³, Z=8; NH₄CsTe₄O₉·2H₂O: Monoclinic I2/a (no. 15), a=18.9880(12) Å, b=6.7633(4) Å, c=21.476(2) Å, β=102.3460(10)°, V=2694.2(3) Å³, Z=8.     

Hydrothermal synthesis, structural characterization and magnetic studies of the new pillared microporous ammonium Fe(III) carboxyethylphosphonate: [NH4][Fe2(OH){O3P(CH2)2CO2}2]

The preparation by hydrothermal reaction and the crystal structure of the iron(III) carboxyethylphosphonate of formula [NH₄][Fe₂(OH){O₃P(CH₂)₂CO₂}₂] is reported. The green-yellow compound crystallizes in the monoclinic system, space group Pc(n.7), with the following unit-cell parameters: a=7.193(3) Å, b=9.776(3) Å, c=10.17(4) Å and β=94.3(2)°. It shows a typical layered hybrid organic-inorganic structure featuring an alternation of organic and inorganic layers along the a-axis of the unit cell. The bifunctional ligand [O₃P(CH₂)₂CO₂]³⁻ is deprotonated and acts as a linker between adjacent inorganic layers, to form pillars along the a-axis. The inorganic layers are made up of dinuclear Fe(III) units, formed by coordination of the metal ions with the oxygen atoms originating from the [O₃P−]²⁻ end of the carboxyethylphosphonate molecules, the oxygen atoms of the [−CO₂]⁻ end group of a ligand belonging to the adjacent layer and the oxygen atom of the bridged OH group. Each Fe(III) ion is six-coordinated in a very distorted octahedral environment. Within the dimer the Fe-Fe separation is found to be 3.5 Å, and the angle inside the [Fe(1)-O(11)-Fe(2)] dimers is ∼124°. The resulting 3D framework contains micropores delimited by four adjacent dimers in the (bc) planes of the unit cell. These holes develop along the a-direction as tunnel-like pores and [NH₄]⁺ cations are located there. The presence of the μ-hydroxo-bridged [Fe(1)-O(11)-Fe(2)] dimers in the lattice is also responsible for the magnetic behavior of the compound at low temperatures. The compound contains Fe³⁺ ions in the high-spin state and the two Fe(III) ions are antiferromagnetic coupled. The J/k value of −16.3 K is similar to those found for other μ-hydroxo-bridged Fe(III) dimeric systems having the same geometry.