Growth of high quality a-plane GaN epi-layer on r-plane sapphire substrates with optimization of multi-buffer layer

Nonpolar (1 1–2 0) a-plane GaN films have been grown using the multi-buffer layer technique on (1–1 0 2) r-plane sapphire substrates. In order to obtain epitaxial a-plane GaN films, optimized growth condition of the multi-buffer layer was investigated using atomic force microscopy, high resolution X-ray diffraction, and transmission electron microscopy measurements. The experimental results showed that the growth conditions of nucleation layer and three-dimensional growth layer significantly affect the crystal quality of subsequently grown a-plane GaN films. At the optimized growth conditions, omega full-width at half maximum values of (11–20) X-ray rocking curve along c- and m-axes were 430 and 530 arcsec, respectively. From the results of transmission electron microscopy, it was suggested that the high crystal quality of the a-plane GaN film can be obtained from dislocation bending and annihilation by controlling of the island growth mode.     

A study on structural formation and optical property of wide band-gap Be0.2Zn0.8O layers grown by RF magnetron co-sputtering system

Wide band-gap BeZnO layers were grown on Al₂O₃ (0 0 0 1) substrate using radio-frequency magnetron co-sputtering. The rate of Be_xZn_1−xO crystallized as a hexagonal structure was x=0.2. From the X-ray photoelectron spectroscopy measurement, the O–Zn bonds relating the crystal structure and the Be–O bonds related to the deviation of the stoichiometry in the BeZnO layer were caught at 530.4 and 531.7 eV in the O 1s spectrum, respectively. Thus, the observance on the Be 1s peak of 113.2 eV associated with the bonding Be–O indicates that the sputtered Be atoms are substituted for the host-lattice site in ZnO. This Be–O bonding shows a relatively low intense and broadening spectrum caused by large fluctuation of Be content in the BeZnO layer. From the photoluminescence and transmittance measurement, the free exciton and the neutral donor-bound exciton (D⁰, X) emissions were observed at 3.7692 and 3.7313 eV, respectively, and an average transmittance rate over 95% was achieved in a wide ultraviolet (UV)–visible region. Also, the binding energy for the (D⁰, X) emission was extracted to be 37.9 meV. Through the wide band-gap material BeZnO, we may open some possibilities for fabricating a ZnO-based UV light-emitting diode to be utilized as a barrier layer comprised of the ZnO/BeZnO quantum well structure and/or an UV light emitting material itself.     

Investigation of nonpolar (1 1 2¯ 0) a-plane ZnO films grown under various Zn/O ratios by plasma-assisted molecular beam epitaxy

Structural and optical properties of nonpolar a-plane ZnO films grown with different II/VI ratios on r-plane sapphire substrates by plasma-assisted molecular beam epitaxy were investigated. Even by increasing the II/VI ratio across the stoichiometric flux condition a consistent surface morphology of striated stripes along the ZnO 〈0 0 0 1〉 direction without any pit formation was observed, which is contrary to polar c-plane ZnO films. Root mean square surface roughness, full width at half maximum values of X-ray rocking curves, defect densities, and photoluminescence were changed with the II/VI ratio. The sample grown with stoichiometric flux condition showed the lowest value of rms roughness, the smallest threading dislocation and stacking fault densities of ∼4.7×10⁸ cm⁻² and ∼9.5×10⁴ cm⁻¹, respectively, and the highest intensity of D^oX peak. These results imply that the stoichiometric flux growth condition is suitable to obtain superior structural and optical properties compared to other flux conditions.     

Enhancement of near-band edge photoluminescence of ZnO thin films by employing MgF2 buffer layer

ZnO/MgF₂/ZnO sandwich structure films were fabricated. The effects of a buffer layer on structure and optical properties of ZnO films were investigated by X-ray diffraction, photoluminescence, optical transmittance and absorption measurements. Measurement results showed that the buffer layer had the effects of improving the quality of ZnO films and releasing the residual stresses in the films. The near-band edge emissions of ZnO films deposited on the MgF₂ buffer layer were significantly enhanced compared with those deposited on bare substrate due to the smaller lattice mismatch between MgF₂ and ZnO than that between fused silica and ZnO.     

Influence of oxygen/argon ratio on structural,electrical and optical properties of Ag-doped ZnO thin films

Ag-doped ZnO (ZnO:Ag) thin films were deposited on quartz substrates by radio frequency magnetron sputtering technique. The influence of oxygen/argon ratio on structural, electrical and optical properties of ZnO:Ag films has been investigated. ZnO:Ag films gradually transform from n-type into p-type conductivity with increasing oxygen/argon ratio. X-ray photoelectron spectroscopy measurement indicates that Ag substitutes Zn site (Ag_Zn) in the ZnO:Ag films, acting as acceptor, and being responsible for the formation of p-type conductivity. The presence of p-type ZnO:Ag under O-rich condition is attributed to the depression of the donor defects and low formation energy of Ag_Zn acceptor. The I–V curve of the p-ZnO:Ag/n-ZnO homojunction shows a rectification characteristic with a turn-on voltage of ∼7 V.     

Hydrothermal growth of ZnO nanorods on a-plane GaN/sapphire template

ZnO nanorod arrays are grown on a-plane GaN template/r-plane sapphire substrates by hydrothermal technique. Aqueous solutions of zinc nitrate hexahydrate and hexamethylenetetramine were employed as growth precursors. Electron microscopy and X-ray diffraction measurements were carried out for morphology, phase and growth orientation analysis. Single crystalline nanorods were found to have off-normal growth and showed well-defined in-plane epitaxial relationship with the GaN template. The 〈0 0 0 1〉 axis of the ZnO nanorods were observed to be parallel to the 〈1 0 1¯ 0〉 of the a-plane GaN layer. Optical property of the as-grown ZnO nanorods was analyzed by room temperature photoluminescence measurements.     

On the isothermal closed space sublimation growth of CdSe using a mixed source for selenium

The use of a selenium–tellurium (SeTe) mixed source in the isothermal close space sublimation growth of CdSe epilayers is considered. The epitaxial growth was performed in flowing helium by sequential exposures of the substrate to vapors of the mixed SeTe source and elemental cadmium at temperatures within 350–410 °C. In spite of the mixed source (proposed to decrease the partial pressure of Se), tellurium incorporation was small and CdSe_xTe_(1−x) (x∼0.98) epilayers were obtained. X-ray diffraction reciprocal space mapping shows the existence of hexagonal inclusions mainly on the (1 1 1) facets of the cubic phase. Material deposition on areas of the graphite crucible exposed to the sources, contamination of the Cd source and large growth rates suggest the existence of a selenium transport process via graphite. This transport might be the result of the combination of selenium deposition on graphite with a subsequent activated desorption of selenium under cadmium exposure. It affects Cd source purity and growth kinetic bringing on a modification of the usual atomic layer deposition regimen; however, a reproducible growth rate of the epilayers was obtained.     

Optimization of hydrothermal growth ZnO Nanorods for enhancement of light extraction from GaN blue LEDs

In this study, we report on the enhancement in the light extraction efficiency of GaN blue LEDs topped with ZnO nanorods. The ZnO nanorods were grown by a two-step hydrothermal synthesis with pre-coated ZnO nanoparticles under optimized condition to give the appropriate size and quality, giving an increase in the light output efficiency of 66%. This improvement is attributed to the optimal rod size and spacing with improved thermal dissipation as compared to light extraction from plain GaN surface. During the ZnO growth on the LEDs, 0.55 M of NH₃ was added and the ZnO sample was later annealed at 475 °C in N₂ ambient, to drive out interstitial oxygen atoms from the tetrahedral unstable site. As a result, a high ratio of UV to orange defect band emission was achieved. The two-step growth of ZnO nanorods on GaN LEDs was effective in generating array of ZnO nanorods which serve as reflector to enhance light extraction from LEDs.     

InGaN growth with various InN mole fractions on m-plane ZnO substrate by metalorganic vapor phase epitaxy

We have demonstrated In_xGa_1−xN epitaxial growth with InN mole fractions of x=0.07 to 0.17 on an m-plane ZnO substrate by metalorganic vapor phase epitaxy for the first time. The crystalline quality of the epilayers was found to be much higher than that of epilayers grown on a GaN template on an m-plane SiC substrate.     

Structural and infrared properties of zinc oxide film and nanowires

The structural and infrared properties of the highly (00.2) oriented ZnO film, randomly grown Au-catalyzed ZnO nanowires (NWs) and vertically aligned self-catalyzed ZnO NWs were compared. In the XRD analysis, (0 0 2) diffraction intensity of self-catalyzed ZnO NWs was enhanced mainly attributed to the preferential growth of NWs in [0 0 0 1] as compared to the ZnO film and the randomly grown Au-catalyzed ZnO NWs. The high UV-to-green emission ratio of self-catalyzed ZnO NWs in room temperature PL measurement indicates that they had a better crystal quality as compared to Au-catalyzed ZnO NWs and ZnO film. Infrared spectroscopy has been used to characterize these films and nanowires too. The phonon peak 407 cm⁻¹ which related to the transverse optical (TO) vibrations perpendicular to the optical axis was observed in the IR reflectivity measurements on the highly c-oriented ZnO film. The IR peaks that appeared in the 550–580 cm⁻¹ region of the spectra of the specimens could be assigned to the ZnO NWs as it was not observed in the ZnO film. These peaks were observed in the 550–580 cm⁻¹ region in both s- and p-polarized light for the randomly grown Au-catalyzed ZnO NWs. In contrast, the IR peak at 580 cm⁻¹ was clearly shown in p-polarized light but not in the s-polarized light for vertically aligned ZnO NWs. This indicated that the vibration was polarized along the vertically aligned ZnO NWs. The (00.2) orientation of the ZnO specimens could be identified by comparing the p- and s-polarized IR spectra.     

Growth of epitaxial ZnO films on Si (1 1 1) substrates with Cr compound buffer layer by plasma-assisted molecular beam epitaxy

Single crystalline ZnO film was grown on (1 1 1) Si substrate through employing an oxidized CrN buffer layer by plasma-assisted molecular beam epitaxy. Single crystalline characteristics were confirmed from in-situ reflection high energy electron diffraction, X-ray pole figure measurement, and transmission electron diffraction pattern, consistently. Epitaxial relationship between ZnO film and Si substrate is determined to be (0 0 0 1)_ZnO‖(1 1 1)_Si and [1 1 2¯ 0]_ZnO‖[0 1 1]_Si. Full-width at half-maximums (FWHMs) of (0 0 0 2) and (1 0 1¯ 1) X-ray rocking curves (XRCs) were 1.379° and 3.634°, respectively, which were significantly smaller than the FWHMs (4.532° and 32.8°, respectively) of the ZnO film grown directly on Si (1 1 1) substrate without any buffer. Total dislocation density in the top region of film was estimated to be ∼5×10⁹ cm⁻². Most of dislocations have a screw type component, which is different from the general cases of ZnO films with the major threading dislocations with an edge component.     

Chemically assisted vapour transport for bulk ZnO crystal growth

A chemically assisted vapour phase transport (CVT) method is proposed for the growth of bulk ZnO crystals. Thermodynamic computations have confirmed the possibility of using CO as a sublimation activator for enhancing the sublimation rate of the feed material in a large range of pressures (10⁻³ to 1 atm) and temperatures (800–1200 °C). Growth runs in a specific and patented design yielded single ZnO crystals up to 46 mm in diameter and 8 mm in thickness, with growth rates up to 400 μm/h. These values are compatible with an industrial production rate. N type ZnO crystals (μ=182 cm²/(V s) and n=7 10¹⁵ cm⁻³) obtained by this CVT method (Chemical Vapour Transport) present a high level of purity (10–30 times better than hydrothermal ZnO crystals), which may be an advantage for obtaining p-type doped layers ([Li] and [Al] <10⁺¹⁵ cm⁻³). Structural (HR-XRD), defect density (EPD), electrical (Hall measurements) and optical (photoluminescence) properties are presented.     

Study of the ZnO crystal growth by vapour transport methods

The crystal growth of ZnO by vapour transport is classically made with the assistance of additional species that produce a gaseous mixture, the role of which remains often uncertain in the transport and growth process. Initially, in order to study the mass transport process, a numerical simulation is made to analyse which are the requirements to have an effective transport. As the pressure of each gaseous species is generally unknown, the numerical study has been performed for different total pressures. It is found that, if congruent and equilibrium conditions are assumed at the sublimation and crystallisation interfaces, effective growth conditions can only be attained for a narrow range of total pressures. Nevertheless, it is well known that ZnO growth by vapour transport is possible for a wide range of pressures of gaseous species. As a consequence, partial pressures higher than the equilibrium ones must be present in order to justify the experimental results. We suggest that the thermal decomposition of ZnO is given by an activated process. The analysis of different mechanisms that could justify the activated decomposition, in accord with a systematic set of growth experiments, suggests that some additional species in the growth of ZnO by vapour transport promote the generation of an additional Zn pressure. This zinc pressure would act autocatalytically inducing O₂ and Zn partial pressures higher than the equilibrium ones and promoting thermal decomposition. The above-cited set of experimental growth experiences, that include the presence of C, Zn, Fe, Cu and H₂, will be analysed and interpreted according to this approach.     

Rate-determining process in chemical vapor deposition of SiC on off-axis -SiC

Homoepitaxial growth on off-axis α-SiC at reduced pressures in a horizontal cold-wall chemical vapor deposition (CVD) system operating at has been investigated. The growth rate was found inversely proportional to the square root of total pressure or the partial pressure of H₂, a carrier gas. A model to explain the experimental results is proposed, where the rate-determining process in CVD is competition between Si species and hydrogen atoms for C (carbon) dangling bonds at SiC step edges.     

Tip-growth mode and base-growth mode of Au-catalyzed zinc oxide nanowires using chemical vapor deposition technique

Tip-growth and base-growth modes of Au-catalyzed zinc oxide nanowires (ZnO NWs) were synthesized on Au-film pre-deposited silicon substrates using Chemical Vapor Deposition (CVD) technique. The diameter of tip-growth Au-catalyzed ZnO NWs was proportional to the Au film thickness, whereas the areal density of these NWs was inversely proportional to the Au film thickness. It would be more appropriate to explain the growth of Au-catalyzed ZnO NWs by a combination of Vapor–Liquid–Solid and Vapor–Solid (VLS–VS) mechanisms instead of the conventional VLS mechanism, regardless of tip-growth or base-growth mode of Au-catalyzed ZnO NWs. The competition between the VLS and VS mechanism in the effectiveness of capturing the adsorbed Zn and O atoms would determine the final morphology of ZnO NWs. In addition, Au catalyst promoted the growth rate of NWs as compared to the self-catalyzed ZnO NWs.     

A route to single-crystalline ZnO films with low residual electron concentration

Single-crystalline ZnO films have been grown on a-plane sapphire in plasma assisted molecular beam epitaxy by introducing a high-temperature ZnO buffer layer. The residual electron concentration of the films can be lowered to 1.5×10¹⁶ cm⁻³, comparable with the best value ever reported for ZnO films grown on a rare and costly substrate of ScAlMgO₄. A 3×3 reconstruction has been observed on the films grown in this route, which reveals that the films have very smooth surface. X-ray phi-scan spectrum of the films shows six peaks with 60° intervals, and two-dimensional X-ray diffraction datum indicates the single-crystalline nature of the films. Low temperature photoluminescence spectrum of the films shows a dominant free exciton emission and five phonon replicas, confirming the high quality of the films.     

Cracking assisted nucleation in chemical vapor deposition of silicon nanoparticles on silicon dioxide

Deposition of sub-monolayer silicon on SiO₂/Si(1 0 0) greatly facilitates nucleation in subsequent thermal chemical vapor deposition (CVD) of silicon nanoparticles. Sub-monolayer seeding is accomplished using silicon atoms generated via disilane decomposition over a hot tungsten filament. The hot-wire process is nonselective towards deposition on silicon and SiO₂, is insensitive to surface temperature below 825 K, and gives controlled coverages well below 1 ML. Thermal CVD of nanoparticles at 1×10⁻⁴ Torr disilane and temperatures ranging from 825 to 925 K was studied over SiO₂/Si(1 0 0) surfaces that had been subjected to predeposition of Si or were bare. Seeding of the SiO₂ surface with as little as 0.01 ML is shown to double the nanoparticle density at 825 K, and densities are increased twenty fold at 875 K after seeding the surface with 30% of a monolayer.     

Extended defects in CdZnTe crystals: Effects on device performance

We explored some unique defects in a batch of cadmium zinc telluride (CdZnTe) crystals, along with dislocations and Te-rich decorated features, revealed by chemical etching. We extensively investigated these distinctive imperfections in the crystals to identify their origin, dimensions, and distribution in the bulk material. We estimated that these features ranged from 50 to 500 μm in diameter, and their depth was about ∼300 μm. The density of these features ranged between 2×10² and 1×10³ per cm³. We elaborated a model of them and projected their effect on charge collection and spectral response. In addition, we fabricated detectors with these defective crystals and acquired fine details of charge-transport phenomena over the detectors’ volume using a high-spatial resolution (25 μm) X-ray response mapping technique. We related the results to better understand the defects and their influence on the charge-transport properties of the devices. The role of the defects was identified by correlating their signatures with the findings from our theoretical model and our experimental data.     

Decisive role of Au layer on the oriented growth of ZnO nanorod arrays via a simple aqueous solution method

Vertically aligned arrays of ZnO nanorod were synthesized on the Au/SiO₂/Si(1 0 0) substrate by a simple aqueous solution growth process, without pre-prepared ZnO seed layer. For comparison, glass and SiO₂/Si were also used as substrates, and the results show that the Au layer plays a decisive role in orienting the growth of the ZnO nanorod. The effects of other growth parameters, including Zn²⁺ concentration and growth time, on morphology, density, and orientation of the ZnO nanostructure were also studied and with longer reaction time, a new structure namely ZnO nanotip was obtained. Moreover, the growth mechanism of ZnO nanorod arrays grown on the Au/SiO₂/Si substrate was proposed.     

Synchrotron X-ray diffraction studies of heteroepitaxial ZnO films grown by pulsed laser deposition

Heteroepitaxial ZnO films were grown by pulsed laser deposition on various substrates such as GaN-buffered C-Al₂O₃, C-Al₂O₃, A-Al₂O₃, and R-Al₂O₃. The epitaxy nature of the films was investigated mainly by synchrotron X-ray diffraction. The results showed that the GaN interlayer plays a positive role in growing an unstrained, well-aligned epitaxial ZnO film on the basal plane of Al₂O₃. Importantly, the ZnO film grown on R-Al₂O₃ has two differently aligned domains. The dominant (1 1 0) oriented domain has much better alignment in the in-plane direction than the minor portion of (0 0 1) oriented domain, while in the out-of-plane direction the two domains have almost the same mosaic distribution.