Dendritic nanowire ultraviolet laser array

Self-organized dendritic crystal growth is explored to assemble uniform semiconductor nanowires into highly ordered one-dimensional microscale arrays that resemble comb structures. The individual ZnO nanowires have uniform diameters ranging from 10 to 300 nm. They are evenly spaced on a stem with a regular periodicity of 0.1-2 micrometer. Under optical excitation, each individual ZnO nanowire serves as a Fabry-Perot optical cavity, and together they form a highly ordered nanowire ultraviolet laser array.     

Ordered networks of ZnO-nanowire hierarchical urchin-like structures for improved dye-sensitized solar cells

Quasi-1D ZnO nanowires (NWs) ordered as patterned 3D hollow hierarchical urchin-like structures have been prepared on transparent conducting substrates by electrodeposition. The ZnO NWs have been grown on self-assembled ordered polystyrene microspheres with electrical charge densities ranging from 5 to 30 C cm(-2) and organized arrays of mono and multi-urchin layers have been built. These layers have been sensitized by the highly absorbing D149 indoline organic dye. The optical characterizations and dye titrations have shown a significant increase in the light scattering and absorption as well as dye loading for the organized structures compared to randomly vertically aligned ZnO NWs grown under the same conditions. The dye-sensitized solar cells (DSSC) prepared using the sensitized layers have been characterized by current-voltage (J-V) measurements, IPCE and by electrochemical impedance spectroscopy. We show that the best performances are obtained for the 3D urchin monolayer structures. The conversion efficiency is increased by up to 4 times compared to their counterparts made of randomly dispersed vertical ZnO NWs. Impedance spectroscopy results show a very fast charge transfer in the ZnO NWs and urchin monolayers and that the electron lifetime is in the 4-14 ms range.     

p-n Heterojunction on ordered ZnO nanowires/polyaniline microrods double array

Recently, there has been growing interest in the design of novel nano- and/or microscaled heterojunctions consisting of two distinctive ordered semiconductor arrays for highly efficient p-n diodes used in optical, optielectronic, and microelectronic devices. Here, we report the attainment of an ordered double array comprising of p-type polyaniline microrods and n-type ZnO nanowires by a controlled electrochemical deposition method. Extensive chemical and physical characterizations have been performed on the fabricated p-n heterojunction. The double-array p-n heterojunction exhibits good rectifying characteristics, the rectification ratio of which exhibits a minimum at an illumination density of 93 mW cm(-2), making it suitable for high-sensitivity photodetectors. This research is expected to open up a new avenue for the development of highly efficient and sensitive p-n heterojunction diodes and possibly serve as the building blocks for future nanoelectronics.     

Lithium niobate nanowires for photocatalytic water splitting

Molecule-based preparation of lithium niobate nanowires was achieved by proper combination of a niobium oxooxalate complex, a structure-directing reagent, and a lithium source. Structural and photophysical properties of the nanowires obtained were characterized by several microscopic and spectroscopic techniques. The nanowire was employed as a photocatalyst for overall water splitting, and H(2) or O(2) evolution reaction from an aqueous solution containing a sacrificial reagent under UV light irradiation to show enhanced photocatalytic properties as compared with a bulky counterpart prepared by a solid state reaction. The factors contributing to the enhancement of the photocatalytic performance were suggested to be an increase in active sites for the photocatalytic reaction in conjunction with a large surface area and a small particle size.     

Zinc nanowires synthesized on a large scale by a simple carbothermal process

Metallic Zn nanowires have been synthesized by a new carbothermal reduction route in which ZnO and Eucalyptus sp. tar pitch were used as source materials. This simple practical procedure was capable of producing Zn nanowires in large quantities without reoxidation. This process was carried out in inert atmosphere, without vacuum or catalyst, at temperatures (800–900 °C) lower than those required in the carbothermal reduction of ZnO with graphite. A comparative study was performed using graphite that is traditionally used as a ZnO reducer, under the same experimental conditions, however, no reaction was observed. The new process involves the pyrolysis of biopitch to obtain a highly reactive coke and the reduction of ZnO with the release of Zn_(v) for the growth of Zn_(s) nanowires. The resulting Zn nanowires were characterized by X-ray diffractometry, energy-dispersive spectroscopy and scanning electron microscopy. Differential thermal analysis and thermogravimetric analysis coupled with infrared analysis techniques were used in an effort to understand the underlying mechanism and establish the best ratio biopitch/ZnO to be used. This paper presents the characterization of the as-synthesized nanowires and discusses the main reactions involved in their production.     

Synthesis of variable-aspect-ratio, single-crystalline ZnO nanostructures

Variable-aspect-ratio (length/diameter), one-dimensional (1-D) ZnO nanostructures (nanorods and nanowires) were prepared in alcohol/water solution by reacting a Zn2+ precursor with an organic weak base, tetramethylammonium hydroxide (Me4NOH). The effect of the experimental parameters (temperature, base concentration, reaction time, and water content) on nucleation, growth, and the final morphology of the ZnO nanostructures was investigated. The low-temperature syntheses (75-150 degrees C) yielded aspect ratios of the 1-D ZnO nanostructures that depended on the water content. The individual ZnO nanorods and nanowires were determined to be perfect, single crystals with their c axes as the primary growth direction.     

Earth‐Abundant Oxygen Evolution Catalysts Coupled onto ZnO Nanowire Arrays for Efficient Photoelectrochemical Water Cleavage

ZnO has long been considered as a model UV‐driven photoanode for photoelectrochemical water splitting, but its performance has been limited by fast charge‐carrier recombination, extremely poor stability in aqueous solution, and slow kinetics of water oxidation. These issues were addressed by applying a strategy of optimization and passivation of hydrothermally grown 1D ZnO nanowire arrays. The length and diameter of bare ZnO nanowires were optimized by varying the growth time and precursor concentration to achieve optimal photoelectrochemical performance. The addition of earth‐abundant cobalt phosphate (Co‐Pi) and nickel borate (Ni‐B) oxygen evolution catalysts onto ZnO nanowires resulted in substantial cathodic shifts in onset potential to as low as about 0.3 V versus the reversible hydrogen electrode (RHE) for Ni‐B/ZnO, for which a maximum photocurrent density of 1.1 mA cm^?2 at 0.9 V (vs. RHE) with applied bias photon‐to‐current efficiency of 0.4 % and an unprecedented near‐unity incident photon‐to‐current efficiency at 370 nm. In addition the potential required for saturated photocurrent was dramatically reduced from 1.6 to 0.9 V versus RHE. Furthermore, the stability of these ZnO nanowires was significantly enhanced by using Ni‐B compared to Co‐Pi due to its superior chemical robustness, and it thus has additional functionality as a stable protecting layer on the ZnO surface. These remarkable enhancements in both photocatalytic activity and stability directly address the current severe limitations in the use of ZnO‐based photoelectrodes for water‐splitting applications, and can be applied to other photoanodes for efficient solar‐driven fuel synthesis.     

ZnO纳米线阵列的电沉积法制备及表征(英文)

利用直流电沉积方法在多孔氧化铝模板的孔洞中生成锌纳米线,在氧气氛围中,于800°C下氧化2h,将氧化铝中的锌氧化成氧化锌.本研究利用氧气氛围进行锌的氧化,大大提高了传统方法的氧化锌纳米线的制备效率.用场发射扫描电子显微镜(FE-SEM)、透射电子显微镜(TEM)和X射线衍射仪(XRD)对其形貌及成分进行表征和分析,结果表明,氧化铝模板的有序孔洞中填充了大尺寸、均匀连续的多晶态氧化锌纳米线.纳米线具有约1000:1的高纵横比,其长度等于氧化铝模板的厚度,直径约为80nm.光致发光(PL)光谱表明,氧化锌纳米线在504nm处有由于氧空位引起的较强蓝绿光发射.这为进一步研究ZnO/AAO组装体发学性质和开发新型功能器件提供了基础.     

P3HT/CdS/TiO2/ZnO一维有序核壳式纳米棒阵列的构制及其在杂化太阳电池中的应用研究

采用恒电位法在铟锡氧化物导电玻璃(ITO)上制备了高度有序一维ZnO纳米棒阵列,将ZnO纳米棒阵列在TiO2溶胶中采用提拉法制备出了一维TiO2/ZnO核壳式纳米棒阵列.在一维TiO2/ZnO核壳式纳米棒阵列上电沉积CdS纳米晶得到一维CdS/TiO2/ZnO核壳式纳米棒阵列,然后在一维CdS/TiO2/ZnO核壳式纳米棒阵列上电沉积聚3-己基噻吩(P3HT)薄膜得到P3HT/CdS/TiO2/ZnO核壳式纳米结构薄膜.以该纳米结构薄膜电极为光阳极制备出新型纳米结构杂化太阳电池,研究了该类电池的光电转换性能,初步探讨了该类电池的工作机理.     

ZnO nanowire arrays coating on TiO2 nanoparticles as a composite photoanode for a high efficiency DSSC

A novel composite photoanode with ZnO nanowire arrays coating on the top of TiO(2) nanoparticles is fabricated, and an efficiency of 4.52% is achieved for the composite cell, far higher than both 0.90% of the ZnO nanowire cell and 3.56% of the TiO(2) nanoparticle cell. The improved efficiency is resulted from the high surface area of nanoparticles, as well as fast electron transport and light scattering effect of nanowires.     

硫化锌与硫化锌/氧化锌异质结纳米线的化学气相沉积法制备与表征

介绍一种利用石墨还原快速制备大量硫化锌纳米线的方法,并分别合成了超晶格型、双轴型、核/壳型的硫化锌/氧化锌异质结纳米线。所合成的硫化锌纳米线存在六方纤锌矿和立方闪锌矿两种晶型,纳米线长度达几十微米,直径在20-50 nm,直径均匀且产量很高。在具有双轴型的硫化锌/氧化锌异质结中,首次发现具有超结构特征的氧化锌。HRTEM分析表明,硫化锌/氧化锌超晶格异质结界面为ZB-ZnS(111)∥ZnO(0001),而核/壳型异质结界面为W-ZnS(0001)∥ZnO(0001),这三个晶面分别为各自晶体的极性面,即所合成的硫化锌/氧化锌异质结中极性面相互平行。对ZnS 和ZnS/ZnO 异质结的生长机制进行了探讨,并对硫化锌纳米线与硫化锌/氧化锌异质结的光学性质进行了分析。     

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

Large-scale arrayed ZnO crystals with a series of novel morphologies, including tower-like, flower-like, and tube-like samples, have been successfully fabricated by a simple aqueous solution route. The morphology and orientation of the obtained ZnO crystal arrays can be conveniently tailored by changing the reactants and experimental conditions. For example, the tower-like ZnO crystal arrays were obtained in a reaction solution system including zinc salt, ammonia, ammonium salt, and thiourea, and the orientation of these tower-like crystals could be controlled by the contents of these reactants. Flower-like ZnO arrays were obtained at lower temperatures, and tube-like ZnO arrays were obtained by ultrasonic pretreatment of the reaction system. The growth mechanism of the tower-like and tube-like ZnO crystals was investigated by FESEM. The results show that tower-like crystals grow layer by layer, while tube-like crystals grow from active nanowires. Ultrasonic pretreatment is proved to be effective in promoting the formation of active nuclei, which have important effects on the formation of the tube-like ZnO crystals. In addition, large-scale arrays of these ZnO crystals can be successfully synthesized onto various substrates such as amorphous glass, crystalline quartz, and PET. This implies this chemical method has a wide application in the fabrication of nano-/microscale devices.     

Sb2S3纳米粒子修饰ZnO纳米片微纳分级结构的光电化学性能

采用恒电位方法,选择氯化钾和乙二胺(EDA)为添加剂,在氧化铟锡(ITO)导电玻璃上制备了高度有序的ZnO纳米片阵列,通过二次电沉积得到了ZnO纳米片上生长纳米棒的微纳分级结构.利用化学浴沉积法在ZnO基底上沉积Sb₂S₃纳米粒子制备出了Sb₂S₃/ZnO纳米片壳核结构和Sb₂S₃/ZnO微纳分级壳核结构.利用扫描电子显微镜(SEM)、X射线衍射(XRD)、紫外-可见(UV-Vis)吸收光谱、瞬态光电流等对其形貌、结构组成和光电化学性能进行了表征和分析.结果表明, Sb₂S₃/ZnO纳米片上生长纳米棒分级壳核结构的光电流明显高于Sb₂S₃/ZnO纳米片壳核结构.在Sb₂S₃/ZnO纳米片壳核结构和Sb₂S₃/ZnO微纳分级壳核结构的基础上旋涂一层P3HT薄膜形成P3HT/Sb₂S₃/ZnO复合结构,以上述复合结构薄膜为光活性层组装成杂化太阳电池,其中, P3HT/Sb₂S₃/ZnO分级壳核结构杂化太阳电池的能量转换效率最高,达到了0.81%.     

Chemical growth of ZnO nanorod arrays on textured nanoparticle nanoribbons and its second-harmonic generation performance

On the basis of the highly oriented ZnO nanoparticle nanoribbons as the growth seed layer (GSL) and solution growth technique, we have synthesized vertical ZnO nanorod arrays with high density over a large area and multi-teeth brush nanostructure, respectively, according to the density degree of the arrangement of nanoparticle nanoribbons GSL on the glass substrate. This controllable and convenient technique opens the possibility of creating nanostructured film for industrial fabrication and may represent a facile way to get similar structures of other compounds by using highly oriented GSL to promote the vertical arrays growth. The growth mechanism of the formation of the ordered nanorod arrays is also discussed. The second-order nonlinear optical coefficient d₃₁ of the vertical ZnO nanorod arrays measured by the Maker fringes technique is 11.3 times as large as that of d₃₆ KH₂PO₄ (KDP).     

Architectural control syntheses of CdS and CdSe nanoflowers, branched nanowires, and nanotrees via a solvothermal approach in a mixed solution and their photocatalytic property

Wurtzite CdS and CdSe nanostructures with complex morphologies such as urchin-like CdS nanoflowers, branched nanowires, and fractal nanotrees can be produced via a facile solvothermal approach in a mixed solution made of diethylenetriamine (DETA) and deionized water (DIW). The morphologies of CdS and CdSe nanocrystals can be easily controlled via tuning the volume ratio of DETA and DIW. Urchin-like CdS nanoflowers made of CdS nanorods are in a form of highly ordered hierarchical structures, while the nanowires are branched nanowires, and the fractal CdS nanotrees are a buildup of branched nanopines. The results demonstrated that solvothermal reaction in a mixed amine/water can access a variety of complex morphologies of semiconductor materials. The photocatalytic activity of CdS particles with different morphologies has been tested by the degradation of acid fuchsine under both UV and visible light, showing that the as-prepared branched CdS nanowires exhibit high photocatalytic activity for degradation of acid fuchsine.     

Pristine and supported ZnO-based catalysts for phenazopyridine degradation with direct solar light

In search for safe techniques to manage waste pharmaceutical compounds drained in water, solar-driven degradation of phenazopyridine (a model drug) was investigated in aqueous media using different ZnO-based catalyst systems. Naked ZnO, CdS-sensitized ZnO (ZnO/CdS) and activated carbon-supported ZnO (AC/ZnO) have been studied. Both naked ZnO and AC/ZnO were highly efficient in mineralizing phenazopyridine, reaching complete removal in ～50 min, with AC/ZnO having the higher edge. The ZnO/CdS system showed lower efficiency, due to screening of light by CdS. Moreover, the tendency of CdS to leach out Cd²⁺ ions discouraged the use of CdS as sensitizer in this work. In both ZnO and AC/ZnO systems, the photo-degradation reaction was induced by the UV tail of the solar light. The visible region, with wavelength longer than 400 nm, failed to induce photo-degradation. The reaction was faster with higher catalyst loading, until a maximum efficiency was reached at a certain concentration. The rate of reaction increased with higher drug concentrations up to a certain limit. The effect of pH value was studied, and the catalysts showed highest efficiencies at pH close to 7. Stability of ZnO to degradation was studied. Both catalyst systems showed lowered efficiencies on recovery and reuse. The results suggest that complete mineralization of waste drugs, commonly dumped in sewage water, with direct solar light is a potentially feasible strategy using the AC/ZnO catalyst.     

Toward highly efficient CdS/CdSe quantum dots-sensitized solar cells incorporating ordered photoanodes on transparent conductive substrates

A series of ordered photoanodic architectures (including ordered TiO(2) nanotube arrays (TNT), ZnO nanorods, ZnO/TiO(2) core/shell nanostructures) for CdS/CdSe sensitized solar cells (QDSCs), were fabricated directly on transparent conductive oxide glasses by a facile sol-gel assisted template process. The morphologies, optical and electrical properties of TNTs and CdS/CdSe co-sensitized TNTs have been demonstrated. The effect of CdSe deposition time on the cell performance was clarified, and the growth mechanism of the CdSe quantum dots on the surface of the TNTs has been proposed as well. Furthermore, the evolution of open-circuit photovoltage (V(oc)) towards CdSe deposition time has been investigated by electrochemical impedance spectroscopy (EIS). A promising light-to-electricity conversion efficiency of up to 4.61% has been achieved with 3 μm long TNT arrays, which is the best record for sandwich-type ordered TNT-based QDSCs.     

Large-area highly-oriented SiC nanowire arrays: synthesis, Raman, and photoluminescence properties

Large-area highly oriented SiC nanowire arrays have been fabricated by chemical vapor reaction using an ordered nanoporous anodic aluminum oxide (AAO) template and a graphite reaction cell. Their microstructures were characterized by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction and high-resolution transmission electron microscopy. The results show that the nanowires are single-crystalline beta-SiC's with diameters of about 30-60 nm and lengths of about 8 microm, which are parallel to each other, uniformly distributed, highly oriented, and in agreement with the nanopore diameter of the applied AAO template. The nanowire axes lie along the [111] direction and possess a high density of planar defects. Some unique optical properties are found in the Raman spectroscopy and photoluminescence emission from oriented SiC nanowire arrays, which are different from previous observations of SiC materials. The growth mechanism of oriented SiC nanowire arrays is also analyzed and discussed.     

Highly ordered chevron-shaped arrays of continuous copper nano-dot lines formed by electroless deposition on hydrogen-terminated Si(111) surfaces

We have succeeded in forming highly ordered chevron-shaped arrays of continuous copper nano-dot lines by electroless deposition on hydrogen-terminated Si(111) (H-Si(111)) surfaces. Detailed investigations have shown that tiny Cu clusters are preferentially formed at step edges when the electroless deposition is carried out in a deoxygenated neutral aqueous solution of a low Cu2+ concentration (less than 10 microM) with pH approximately = 7. This finding was combined with highly ordered step-edge lines on H-Si(111) prepared by the previously reported method of Teflon scratching and NH4F etching, which has led to the above success. The present result indicates that designed ordered metal nanowires can be produced by the electroless deposition method, using H-Si(111) surfaces with well-regulated step lines as a substrate.     

Length‐Dependent Charge Generation from Vertical Arrays of High‐Aspect‐Ratio ZnO Nanowires

Aqueous chemical growth of zinc oxide nanowires is a flexible and effective approach to obtain dense arrays of vertically oriented nanostructures with high aspect ratio. Herein we present a systematic study of the different synthesis parameters that influence the ZnO seed layer and thus the resulting morphological features of the free‐standing vertically oriented ZnO nanowires. We obtained a homogeneous coverage of transparent conductive substrates with high‐aspect‐ratio nanowire arrays (length/diameter ratio of up to 52). Such nanostructured vertical arrays were examined to assess their electric and piezoelectric properties, and showed an electric charge generation upon mechanical compressive stress. The principle of energy harvesting with these nanostructured ZnO arrays was demonstrated by connecting them to an electronic charge amplifier and storing the generated charge in a series of capacitors. We found that the generated charge and the electrical behavior of the ZnO nanowires are strictly dependent on the nanowire length. We have shown the importance of controlling the morphological properties of such ZnO nanostructures for optimizing a nanogenerator device.