Preparation of LiNi0.5Mn0.5O2 cathode materials by urea hydrolysis coprecipitation

Layered LiNi_0.5Mn_0.5O₂ has been successfully synthesized via urea hydrolysis coprecipitation method. Well-crystallized LiNi_0.5Mn_0.5O₂ was obtained after calcinations of coprecipitation precursors and lithium salts at 450 °C for 3 h and following 900 °C for 10 h in air. Both the precursors and LiNi_0.5Mn_0.5O₂ powders show an agglomerated secondary structure with crystalline particles inside. The quasi-spherical morphology of the precursors was maintained during the calcinations. The first charge and discharge capacities of as-prepared LiNi_0.5Mn_0.5O₂ were 200 and 165mAh/g respectively. The discharge capacity of about 160mAh/g was retained after 10cycles for as-prepared samples.     

Synthesis of nanocrystalline Zn0.5Mn0.5Fe2O4 via in situ polymerization technique

Nanocrystalline Zn_0.5Mn_0.5Fe₂O₄ was synthesized through the pyrolysis of polyacrylate salt precursors prepared via in situ polymerization of the metal salts and acrylic acid. The pyrolysis behavior of the polymeric precursors was studied by use of thermal analysis. The as-obtained product was characterized by powder X-ray diffraction (XRD), transmission electron microscope (TEM), electron diffraction (ED) pattern, scanning electron microscopy (SEM) and electron dispersive X-ray (EDX) analysis. The results revealed that the particle size is in the range of 15–25 nm for Zn-Mn ferrites with good crystallinity. Magnetic properties of the sample at 300 K were measured using a vibrating sample magnetometer, which showed that the sample exhibited characteristics of superparamagnetism.     

Effect of sintering temperature and the particle size on the structural and magnetic properties of nanocrystalline Li0.5Fe2.5O4

Sintering temperature and particle size dependent structural and magnetic properties of lithium ferrite (Li_0.5Fe_2.5O₄) were synthesized and sintered at four different temperatures ranging from 875 to 1475 K in the step of 200 K. The sample sintered at 875 K was also treated for four different sintering times ranging from 4 to 16 h. Samples sintered at 1475 K have the cubic spinel structure with a small amount of α-Fe₂O₃ (hematite) and γ-Fe₂O₃ (maghemite). The samples sintered at≤1275 K do not show hematite and maghemite phases and the crystals form the single phase spinel structure with the cation ordering on octahedral sites. Particle size of lithium ferrite is in the range of 13-45 nm, and is depend on the sintering temperature and sintering time. The saturation magnetization increased from 45 to 76 emu/g and coercivity decreases from 151 to 139 Oe with an increase in particle size. Magnetization temperature curve recorded in ZFC and FC modes in an external magnetic field of 100 Oe. Typical blocking effects are observed below about 244 K. The dielectric constant increases with an increase in sintering temperature and particle size.     

Magnetotransport properties of epitaxial Pr0.5Ca0.5MnO3 films grown by a solution technique

Epitaxial Pr_0.5Ca_0.5MnO₃ films have been synthesized on (0 0 1) SrTiO₃ substrate using a chemical solution deposition technique and two-step post-annealing process. The zero field resistivity of the films shows semiconducting behavior and a characteristic of charge ordering is observed at 230 K. The resistivity of the 10 nm film did not show any effect with the magnetic field. However, melting of charge ordering was observed for the 120 nm film at an applied magnetic field of 4 T. Large decrease in the resistivity of the 120 nm film (<100 K) resulted in magnetoresistance of nearly −100% at 75 K.     

Magnetic properties of La-substituted NiFe2O4 via egg-white precursor route

Nano-sized NiFe_2−xLa_xO₄ ferrites (x=0.00, 0.01, 0.02, 0.03, 0.04, 0.5, 0.07 and 0.09) were synthesized for the first time by using metal nitrate and egg-white extract in aqueous medium. The ferrites were characterized by DTA-TG, XRD, TEM, FT-IR and VSM techniques. The thermal decomposition behavior revealed that the precursors were completely decomposed at about 420 °C. TEM image shows agglomerated nanoparticles with crystallite sizes agrees well with that estimated by XRD measurement. XRD patterns show a secondary phase of LaFeO₃ besides the cubic structure of the La-substituted ferrites. The lattice parameters, X-ray density and crystallite size were found to increase with the increasing La content. The VSM measurement exhibited a ferromagnetic property for all the samples at room temperature. With increasing La, M_s was found to decrease while H_c increased. The decrease in the saturation magnetization is attributed to the paramagnetic properties of lanthanum, which prefer to substitute iron present in the octahedral sites. The increase in the coercivity is due to either the stronger magnetocrystalline anisotropy induced by La substitution or the change in the crystallite size.     

Influence of epitaxial growth on phase competition in Pr0.5Sr0.5MnO3 films

A series of Pr_0.5Sr_0.5MnO₃ (PSMO) films with various thickness were epitaxially grown on substrates of (0 0 1)-oriented (LaAlO₃)_0.3(SrAl_0.5Ta_0.5O₃)_0.7 (LSAT), LaAlO₃ (LAO) and SrTiO₃ (STO), and (0 1 1)-oriented STO using pulse laser deposition. Influence of epitaxial growth on phase competition was investigated. A ferromagnetic metal to antiferromagnetic insulator (FMM-AFI) transition upon cooling is present in both largely compressed situations deposited on LAO (0 0 1) and tensile cases deposited on STO (0 0 1) but absent in little strained films grown on LSAT (0 0 1), indicating that the antiferromagnetic insulating state is favored by strains. On the other hand, the 400 nm films deposited on (0 1 1)-oriented STO as well as LAO substrates show FMM-AFI transition. These results reveal that both the orientation of epitaxial growth and substrate-induced strain affect the FMM-AFI transition.     

Mossbauer, Raman and X-ray diffraction studies of superparamagnetic NiFe2O4 nanoparticles prepared by sol-gel auto-combustion method

Superparamagnetic nickel ferrite single phase nanoparticles with the average crystallite size of ∼9 nm have been synthesized at a low temperature (220 °C) by the sol-gel auto-combustion method. In the present study the as prepared powder was further calcined at different temperatures for 4 h, resulting in nanoparticles of larger size. The nanoparticles exhibited superparamagnetic behavior and changes in cation distribution as revealed by the Mossbauer, Raman and X-ray diffraction studies. The Mossbauer spectra collected at 5 K and under 5 T applied magnetic field showed mixed spinel structure and canted spin order for the nanoparticles, whereas there is collinear spin order with inverse spinel structure for larger particles. The vibrational spectra of the nanoparticles showed a redshift and broadening in the Raman line shape due to confinement effects.     

Preparation and photoluminescence characteristics of Eu-doped MgAl1.8Y0.2O4 nanocrystals

A simple combustion route was employed for the preparation of Eu³⁺-doped MgAl_1.8Y_0.2−xO₄ nanocrystals using metal nitrates as precursors and urea as a fuel in a preheated furnace at 500 °C. The powders thus obtained were then fired at 1000 °C for 3 h to get better luminescent properties. The incorporation of Eu³⁺ activator in these nanocrystals was checked by luminescence characteristics. These nanocrystals displayed bright red color on excitation under 254 nm UV source. The main emission peak was assigned to the transition [⁵D₀→⁷F₂] at 615 nm. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) studies were carried out to understand surface morphological features and the particle size. Crystal structures of the nanocrystals were investigated by the X-ray diffraction (XRD) technique. The crystallite size of the as-prepared nanocrystals was around 29 nm, which was evaluated from the broad XRD peaks. The crystallite size increased to ∼45 nm on further heat treatment at 1000 °C.     

NbTi0.5Ni0.5O4 as anode compound material for SOFCs

NbTi_0.5Ni_0.5O₄ (NTNO) has been prepared using solid state synthesis and investigated as a potential anode material. The oxide form of NTNO has single phase rutile-type structure with tetragonal (P42/mnm) space group. The reduced form is a composite of nano-scaled particles of metallic Ni and Nb_1.33Ti_0.67O₄ phase. Reduced NTNO showed high electronic conductivity up to 280 S.cm^− 1 at 900 °C in reducing atmosphere, but suffers from low CTE equal to 3.78 10^− 6 K^− 1. Studies of NTNO as anode material were carried out in a three electrode - electrochemical half cell configuration under pure humidified H₂ at 900 °C using a 2 mm thick zirconia electrolyte and without any additional current collector material. The results show a reasonable series resistance (R_s) equal to 2.7 Ωcm² (about 50% higher than for metallic gold layers) indicating a good current collection performance for a 10 μm layer of material. The polarization resistance (R_p) was equal to 33 Ωcm² and is attributed to a poor density of three phase boundaries (TPB) and shortage of oxide ion conduction in the anode layer. The results show the potential of NTNO as an anode material, especially after optimization of the microstructure towards the increase of TPB length.     

The effect of different temperature annealing on phase relation of LaFe11.5Si1.5 and the magnetocaloric effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 alloys

The phase relation of LaFe_11.5Si_1.5 alloys annealed at different high-temperature from 1223 K (5 h) to 1673 K (0.5 h) has been studied. The powder X-ray diffraction (XRD) patterns show that large amount of 1:13 phase begins to form in the matrix alloy consisting of α-Fe and LaFeSi phases when the annealing temperature is 1423 K. In the temperature range from 1423  to 1523 K, α-Fe and LaFeSi phases rapidly decrease to form 1:13 phase, and LaFeSi phase is rarely observed in the XRD pattern of LaFe_11.5Si_1.5 alloy annealed at 1523 K. With annealing temperature increasing from 1573  to 1673 K, the LaFeSi phase is detected again in the LaFe_11.5Si_1.5 alloy, and there is La₅Si₃ phase when the annealing temperature reaches 1673 K. There almost is no change in the XRD patterns of LaFe_11.5Si_1.5 alloys annealed at 1523 K for 3-5 h. According to this result, the La_0.8Ce_0.2Fe_11.5−xCo_xSi_1.5 (0≤×≤0.7) alloys are annealed at 1523 K (3 h). The analysis of XRD patterns shows that La_0.8Ce_0.2Fe_11.5xCo_xSi_1.5 alloys consist of the NaZn₁₃-type main phase and α-Fe impurity phase. With the increase of Co content from x=0 to 0.7, the Curie temperature T_C increases from 180 to 266 K. Because the increase of Co content can weaken the itinerant electron metamagnetic transition, the order of the magnetic transition at T_C changes from first to second-order between x=0.3 and 0.5. Although the magnetic entropy change decreases from 34.9 to 6.8 J/kg K with increasing Co concentration at a low magnetic field of 0-2 T, the thermal and magnetic hysteresis loss reduces remarkably, which is very important for the magnetic refrigerant near room temperature.     

Green synthesis and characterization of superparamagnetic Fe3O4 nanoparticles

In this paper, we have first demonstrated a facile and green synthetic approach for preparing superparamagnetic Fe₃O₄ nanoparticles using α-d-glucose as the reducing agent and gluconic acid (the oxidative product of glucose) as stabilizer and dispersant. The X-ray powder diffraction (XRD), X-ray photoelectron spectrometry (XPS), and selected area electron diffraction (SAED) results showed that the inverse spinel structure pure phase polycrystalline Fe₃O₄ was obtained. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) results exhibited that Fe₃O₄ nanoparticles were roughly spherical shape and its average size was about 12.5 nm. The high-resolution TEM (HRTEM) result proved that the nanoparticles were structurally uniform with a lattice fringe spacing about 0.25 nm, which corresponded well with the values of 0.253 nm of the (3 1 1) lattice plane of the inverse spinel Fe₃O₄ obtained from the JCPDS database. The superconducting quantum interference device (SQUID) results revealed that the blocking temperature (T_b) was 190 K, and that the magnetic hysteresis loop at 300 K showed a saturation magnetization of 60.5 emu/g, and the absence of coercivity and remanence indicated that the as-synthesized Fe₃O₄ nanoparticles had superparamagnetic properties. Fourier transform infrared spectroscopy (FT-IR) spectrum displayed that the characteristic band of Fe-O at 569 cm⁻¹ was indicative of Fe₃O₄. This method might provide a new, mild, green, and economical concept for the synthesis of other nanomaterials.     

Influence of boron on the giant magnetocaloric effect of La(Fe0.9Si0.1)13

The influences of boron addition on the phase formation, Curie temperature and magnetic entropy change of the NaZn₁₃-type La(Fe_0.9Si_0.1)₁₃ compound have been investigated. Eight boron containing La(Fe_0.9Si_0.1)₁₃B_x samples were prepared with x=0, 0.03, 0.06, 0.1, 0.2, 0.3, 0.5 and 0.6, respectively. Experimental results show that a small amount of B addition in La(Fe_0.9Si_0.1)₁₃ forms the solid solution NaZn₁₃-type structure phase by substituting B for Si or doping B into interstitial position of the lattice, preserves its giant magnetocaloric effects due to their first-order structural/magnetic transition, as well as increase its Curie temperature T_c slightly. The maximum magnetic entropy changes in the magnetic field change of 0–1.6 T are around 20 J kg^–1 K^–1 for the samples with Boron addition less than 0.3, while improving the Curie temperatures by 2 K.     

Effect of high magnetic field annealing on the microstructure and magnetic properties of Co-Fe layered double hydroxide

The effects of high magnetic field (10 T) on the products obtained by calcination of Co-Fe LDH precursors at different temperatures were investigated. The XRD results indicated that Fe^III substituted for Co^III in Co₃O₄ to yield Co^IICo^IIIFe^IIIO₄ under the calcination of Co-Fe LDH precursors at 400 °C. The products obtained by magnetic field annealing at 400 °C had a porous plate-like morphology, whereas the products without magnetic field annealing were composed of nanoparticles. It was seen that CoFe₂O₄ phase could be formed at low temperature (about 500 °C) under the magnetic field annealing. The grain size of products obtained by magnetic field annealing at 800 °C was larger than that of zero magnetic field. It was found that the saturation magnetization was significantly enhanced after magnetic field annealing, especially at lower temperature (≤600 °C). The possible reason for the effects on the microstructure and magnetic properties of products obtained by magnetic field annealing was discussed.     

Photoluminescence at room temperature in Ba0.5Sr0.5TiO3 ceramics

We present in this paper the experimental results of photoluminescence spectra of Ba_0.5Sr_0.5TiO₃ ceramics. An emission band centered at about 920 nm has been observed at room temperature. When we change the amount of oxygen vacancies in these samples by thermal treatment, these samples show an enhancement of luminescence. Our experimental results indicate that the origin of the photoluminescence is related to the oxygen vacancies in these samples.     

Synthesis and luminescence properties of nanocrystalline Gd2O3:Eu by combustion process

The nanocrystalline Gd₂O₃:Eu³⁺ powders with cubic phase were prepared by a combustion method in the presence of urea and glycol. The effects of the annealing temperature on the crystallization and luminescence properties were studied. The results of XRD show pure phase can be obtained, the average crystallite size could be calculated as 7, 8, 15, and 23 nm for the precursor and samples annealed at 600, 700 and 800 °C, respectively, which coincided with the results from TEM images. The emission intensity, host absorption and charge transfer band intensity increased with increasing the temperature. The slightly broad emission peak at 610 nm for smaller particles can be observed. The ratio of host absorption to O²⁻-Eu³⁺ charge transfer band of smaller nanoparticles is much stronger compared with that for larger nanoparticles, furthermore, the luminescence lifetimes of nanoparticles increased with increasing particles size. The effects of doping concentration of Eu³⁺ on luminescence lifetimes and intensities were also discussed. The samples exhibited a higher quenching concentration of Eu³⁺, and luminescence lifetimes of nanoparticles are related to annealing temperature of samples and the doping concentration of Eu³⁺ ions.     

Structural and electrical properties of (Na0.85K0.15)0.5Bi0.5TiO3 thin films deposited on LaNiO3 and Pt bottom electrodes

(Na_0.85K_0.15)_0.5Bi_0.5TiO₃ thin films were deposited on LaNiO₃(LNO)/SiO₂/Si(1 0 0) and Pt/Ti/SiO₂/Si(1 0 0) substrates by metal-organic decomposition, and the effects of bottom electrodes LNO and Pt on the ferroelectric, dielectric and piezoelectric properties were investigated by ferroelectric tester, impedance analyzer and scanning probe microscopy, respectively. For the thin films deposited on LNO and Pt electrodes, the remnant polarization 2P_r are about 22.6 and 8.8 μC/cm² under 375 kV/cm, the dielectric constants 238 and 579 at 10 kHz, the dielectric losses 0.06 and 0.30 at 10 kHz, the statistic d_33eff values 95 and 81 pm/V. The improved piezoelectric properties could make (Na_1−xK_x)_0.5Bi_0.5TiO₃ thin film as a promising candidate for piezoelectric thin film devices.     

Cu2ZnSnSe4 thin films prepared by selenization of co-electroplated Cu-Zn-Sn precursors

A novel technique for growth of high quality Cu₂ZnSnSe₄ (CZTSe) thin films is reported in our work. The CZTSe thin films were fabricated onto Mo layers by co-electroplating Cu-Zn-Sn precursors followed by annealing in the selenium vapors at the substrate temperature of 550 °C. The morphology and structure of CZTSe thin films were characterized using scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), X-ray diffraction (XRD) and Raman scattering spectrum, respectively. The results revealed that the single phase was in the CZTSe thin films, and the other impurities such as ZnSe and Cu₂SnSe₃ were not existed though they were difficult to distinguish both from EDS and XRD.     

Microwave synthesis of magnetic Fe3O4 nanoparticles used as a precursor of nanocomposites and ferrofluids

Methods to synthesize magnetic Fe₃O₄ nanoparticles and to modify the surface of particles are presented in the present investigation. Fe₃O₄ magnetic nanoparticles were prepared by the co-precipitation of Fe³⁺ and Fe²⁺, NH₃·H₂O was used as the precipitating agent to adjust the pH value, and the aging of Fe₃O₄ magnetic nanoparticles was accelerated by microwave (MW) irradiation. The obtained Fe₃O₄ magnetic nanoparticles were characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and vibrating sample magnetometer (VSM). The average size of Fe₃O₄ crystallites was found to be around 8–9 nm. Thereafter, the surface of Fe₃O₄ magnetic nanoparticles was modified by stearic acid. The resultant sample was characterized by FT-IR, scanning electron microscopy (SEM), XRD, lipophilic degree (LD) and sedimentation test. The FT-IR results indicated that a covalent bond was formed by chemical reaction between the hydroxyl groups on the surface of Fe₃O₄ nanoparticles and carboxyl groups of stearic acid, which changed the polarity of Fe₃O₄ nanoparticles. The dispersion of Fe₃O₄ in organic solvent was greatly improved. Effects of reaction time, reaction temperature and concentration of stearic acid on particle surface modification were investigated. In addition, Fe₃O₄/polystyrene (PS) nanocomposite was synthesized by adding surface modified Fe₃O₄ magnetic nanoparticles into styrene monomer, followed by the radical polymerization. The obtained nanocomposite was tested by thermogravimetry (TG), differential scanning calorimetry (DSC) and XRD. Results revealed that the thermal stability of PS was not significantly changed after adding Fe₃O₄ nanoparticles. The Fe₃O₄ magnetic fluid was characterized using UV–vis spectrophotometer, Gouy magnetic balance and laser particle-size analyzer. The testing results showed that the magnetic fluid had excellent stability, and had susceptibility of 4.46×10⁻⁸ and saturated magnetization of 6.56 emu/g. In addition, the mean size d (0.99) of magnetic Fe₃O₄ nanoparticles in the fluid was 36.19 nm.     

Heat generation ability in AC magnetic field of nano MgFe2O4-based ferrite powder prepared by bead milling

Nanosized MgFe₂O₄-based ferrite powder having heat generation ability in an AC magnetic field was prepared by bead milling and studied for thermal coagulation therapy applications. The crystal size and the particle size significantly decreased by bead milling. The heat generation ability in an AC magnetic field improved with the milling time, i.e. a decrease in crystal size. However, the heat generation ability decreased for excessively milled samples with crystal sizes of less than 5.5 nm. The highest heat ability (ΔT=34 °C) in the AC magnetic field (370 kHz, 1.77 kA/m) was obtained for fine MgFe₂O₄ powder having a ca. 6 nm crystal size (the samples were milled for 6-8 h using 0.1 mm ? beads). The heat generation of the samples was closely related to hysteresis loss, a B-H magnetic property. The reason for the high heat generation properties of the samples milled for 6-8 h using 0.1 mm ? beads was ascribed to the increase in hysteresis loss by the formation of a single domain. Moreover, the improvement in heating ability was obtained by calcination of the bead-milled sample at low temperature. In this case, the maximum heat generation (ΔT=41 °C) ability was obtained for a ca. 11 nm crystal size sample was prepared by crystal growth during the sample calcination. On the other hand, the ΔT value for Mg_0.5Ca_0.5Fe₂O₄ was synthesized using a reverse precipitation method decreased by bead milling.     

Glassy-ferromagnetic behavior in Eu0.5Sr0.5CoO3

Polycrystalline perovskite cobalt oxide Eu_0.5Sr_0.5CoO₃ was prepared by the conventional solid-state reaction method. X-ray powder patterns indicated the prepared samples are pure, cubic perovskite structure (Pm3?m), and with no evidence of any secondary phases. The dc magnetization and ac susceptibility measurements were carried out to investigate the magnetic properties of the sample, and which indicated that cluster-glasses properties are suppressed with the increasing of the coercive field. We denied the possibility of spin-glasses and the existence of the Hopkinson effect in Eu_0.5Sr_0.5CoO₃ through the temperature-dependent ac susceptibility measurements, and explained the magnetic behavior of Eu_0.5Sr_0.5CoO₃ with the competition between magnetic anisotropy and the external magnetic field.