Improvement of refrigerant capacity of La0.7Ca0.3MnO3 material with a few percent Co doping

The influence of first and second order magnetic phase transitions on the magnetocaloric effect (MCE) and refrigerant capacity or relative cooling power (RCP) of La_0.7Ca_0.3MnO₃ and La_0.7Ca_0.3Mn_0.95Co_0.05O₃ materials has been investigated. Large low-field-induced magnetic entropy changes are observed in La_0.7Ca_0.3MnO₃ and La_0.7Ca_0.3Mn_0.95Co_0.05O₃ materials. The La_0.7Ca_0.3MnO₃ material experiences a large entropy change with a first-order magnetic phase transition at the Curie temperature, T_C. On the other hand, La_0.7Ca_0.3Mn_0.95Co_0.05O₃ displays a smaller entropy change with a second order phase transition. While a first-order magnetic transition material induces a larger MCE (7.528 J/kg K at 5 T) at T_C, this is limited to a narrow temperature range, resulting in a relatively small RCP (218 J/kg), while the Co-doped second-order magnetic transition material induces a smaller MCE (7.14 J/kg K for 5 T), but it is spread over a broader temperature range, resulting in a larger RCP (308 J/kg). The maximum magnetoresistance (MR, defined as ρ(0)/ρ(H)-1) under a field of 5 T is about 206% and 333% for La_0.7Ca_0.3MnO₃ and La_0.7Ca_0.3Mn_0.95Co_0.05O₃, respectively. The refrigeration capacity (RCP) is enhanced in La_0.7Ca_0.3Mn_0.95Co_0.05O₃ (by about 41%) due to small changes from Co doping. The magnetocaloric features of these materials at lower magnetic fields (MCE=3.163 for La_0.7Ca_0.3Mn_0.95Co_0.05O₃ and 4.63 J/kg K for La_0.7Ca_0.3MnO₃ at 1 T), and the high RCP and MR can provide some ideas for exploring novel magnetic refrigerants that can operate with permanent magnets rather than superconducting ones as the magnetic field source.     

Influence of Dy addition on the magnetocaloric effect of La0.67Ca0.33Mn0.9V0.1O3 ceramics

The influence of partial substitution of La by Dy on the magnetocaloric response of (La_1−xDy_x)_0.67Ca_0.33Mn_0.9V_0.1O₃, where x=0.03, 0.15 and 0.25 is studied. Rietveld refinement of X-ray diffraction pattern using GSAS method shows that the compounds adopt the orthorhombic structure with Pnma space group. The systematic change in lattice parameters and magnetic phase transition indicates the substitution effect of Dy. From the magnetization isotherms at different temperatures, magnetic entropy change close to their respective transition temperatures (T_C) has been evaluated. The maximum value of entropy change near T_C is found to be about 4.8 J/kg K at 187.5 K for LCMVDy_0.03, 2.45 J/kg K at 107.5 K for LCMVDy_0.15 and 2.15 J/kg K at 92.5 K for LCMVDy_0.25 at 4 T. Dy addition produces a reduction in T_C and in magnitude of the magnetic entropy change. Even though the entropy change decreases with increasing Dy substitution the refrigerant temperature range, ΔT, is found to be 10 K for LCMVDy_0.03, 31 K for LCMVDy_0.15 and 35 K for LCMVDy_0.25 compounds [90%] at 4 T. The field dependence of the magnetic entropy change is also analyzed showing the power law dependence, ΔS_M∞Hⁿ where n=0.75(2) for LCMVDy_0.03, n=0.80(4) for LCMVDy_0.15 and n=0.92(8) for LCMVDy_0.25 compounds at their respective transition temperatures. The relative cooling power and its field dependance are also analyzed.     

Magnetocaloric effect in R2Fe17 (R=Sm,Gd, Tb,Dy, Er)

A series of R₂Fe₁₇ (R=Sm, Gd, Tb, Dy, Er) have been synthesized. The magnetocaloric effect (MCE) of these compounds has been investigated by means of magnetic measurements in the vicinity of their Curie temperature. The Curie temperature of Er₂Fe₁₇ is 294 K. The maximum magnetic entropy change of Er₂Fe₁₇ under 5 T magnetic field is ∼3.68 J/kg K. In the R₂Fe₁₇ (R=Sm, Gd, Tb, Dy, Er) system, the maximum magnetic entropy change under 1.5 T magnetic field is 1.72, 0.89, 1.32, 1.59, 1.68 J/kg K corresponding to their Curie temperature (400, 472, 415, 364, 294 K), respectively.     

Anisotropic and large low-field magnetic entropy change in a La4/3Sr5/3Mn2O7 single crystal

We have studied the magnetocaloric effect (MCE) in a bilayered La_4/3Sr_5/3Mn₂O₇ single crystal with applied field along both ab-plane and c-direction. Due to the quasi-two-dimensional structure, the crystal exhibits a strong anisotropy in the MCE. The difference of magnetic entropy change between two crystallographic directions depends on external magnetic fields and has a maximum of 2 J/kg K. A large low-field magnetic entropy change, reaching 3.2 J/kg K for a magnetic field change of 15 kOe, is observed when the applied field is along ab-plane. This large low-field magnetic entropy change is attributed to the rapid change of magnetization in response to external magnetic fields in the easy magnetizing plane.     

Effect of monovalent metal substitution on the magnetocaloric effect of perovskite manganites Pr0.5Sr0.3M0.2MnO3 (M=Na,Li, K and Ag)

The influence of monovalent doping on the magnetocaloric effect (MCE) and refrigerant capacity or relative cooling power (RCP) of Pr_0.5Sr_0.3M_0.2MnO₃ (M=Na, Li, K and Ag) materials has been investigated. A large magnetocaloric effect was inferred over a wide range of temperature around the second order paramagnetic–ferromagnetic transition. The maximum magnetic entropy changes (ΔS_M) reached 1.8, 2.2, 1.6 and 2.1 J/kg K and the relative cooling power (RCP) approached 58.9, 59.3, 69.6 and 54.6 J/kg for Na, Li, K and Ag doped materials in the magnetic change of 15 kOe, respectively. According to the results determined by the Maxwell relation, the magnetic entropy change fits well with the Landau theory of phase transition above T_C for Pr_0.5Sr_0.3Li_0.2MnO₃. The large magnetic entropy change induced by low magnetic field suggested that these materials are beneficial for practical applications.     

Effect of Sn-doping on the structural,magnetic and magnetocaloric properties of La0.67Ba0.33Mn1−xSnxO3 compounds

Magnetocaloric effect (MCE) in fine-grained perovskite manganites of the type La_0.67Ba_0.33Mn_1−xSn_xO₃ (x=0.05, 0.1 and 0.15) were prepared by the solid-state method. The prepared samples remain single phase and exhibit paramagnetic to ferromagnetic phase transition (T_C) at 340, 325 and 288 K for x=0.05, 0.1 and 0.15, respectively. From the measured magnetization data of La_0.67Ba_0.33Mn_1−xSn_xO₃ compounds as a function of field (2 T), the associated magnetic entropy change close to their respective Curie temperatures and the relative cooling power (RCP) have been determined. Large MCE has been obtained in all samples and |ΔS_M|_max reached the highest value of 2.49 J/kg K at T_C (288 K) for the sample x=0.15, with H=2 T.     

Large reversible magnetocaloric effect in spinel MnV2O4 with minimal Al substitution

Magnetocaloric effect of MnV_1.95Al_0.05O₄ was studied by the magnetization and heat capacity measurements. MnV_1.95Al_0.05O₄ is a cubic spinel structure with ferromagnetism of second order in nature and performs reversible magnetic entropy around the magnetic transition temperature. The large magnetic entropy changes −ΔS_M∼5.2 and 8.2 J/kg K and the adiabatic temperature changes ΔT_ad∼1.5 and 2.6 K are revealed for the magnetic field changes of 2 and 4 T near the Curie temperature (T_C) of 59.6 K, respectively. The relative cooling power (RCP) are about 82.2 and 177.2 J/kg K for magnetic field changes 2 and 4 T, respectively. Compared with the parent compound, although the −ΔS_M and ΔT_ad become smaller, the refrigeration working temperature span and the RCP have been improved.     

Metamagnetic transition and magnetocaloric effect in charge-ordered Pr0.68Ca0.32−xSrxMnO3 (x=0, 0.1, 0.18, 0.26 and 0.32) compounds

In this study, magnetic and magnetocaloric properties of Pr_0.68Ca_0.32−xSr_xMnO₃ (x=0, 0.1, 0.18, 0.26 and 0.32) compounds were investigated. X-ray results indicated that all the samples have a single phase of orthorhombic symmetry. The orthorhombic unit cell parameters increase with the increase in Sr content. Large negative magnetic entropy changes (−26.2 J/kg K at 38 K and 5 T for x=0 and −6.5 J/kg K at 83 K and 6 T for x=0.1) were attributed to ultrasharp metamagnetic transitions. The peak value of ΔS_m decreased from −4.1 J/kg K for x=0.18 sample to −2.4 J/kg K for x=0.32 at 1 T magnetic field.     

Magnetocaloric effect and multifunctional properties of Ni–Mn-based Heusler alloys

The studies of magnetocaloric properties, phase transitions, and phenomena related to magnetic heterogeneity in the vicinity of the martensitic transition (MT) in Ni–Mn–In and Ni–Mn–Ga off-stoichiometric Heusler alloys are summarized. The crystal structure, magnetocaloric effect (MCE), and magnetotransport properties were studied for the following alloys: Ni₅₀Mn_50−xIn_x, Ni_50−xCo_xMn₃₅In₁₅, Ni₅₀Mn_35−xCo_xIn₁₅, Ni₅₀Mn₃₅In₁₄Z (Z=Al, Ge), Ni₅₀Mn₃₅In_15−xSi_x, Ni_50−xCo_xMn_25+yGa_25−y, and Ni_50–xCo_xMn_32−yFeyGa₁₈. It was found that the magnetic entropy change, ΔS, associated with the inverse MCE in the vicinity of the temperature of the magneto-structural transition, TM, persists in a range of (125-5) J/(kg K) for a magnetic field change ΔH=5 T. The corresponding temperature varies with composition from 143 to 400 K. The MT in Ni₅₀Mn_50−xIn_x (x=13.5) results in a transition between two paramagnetic states. Associated with the paramagnetic austenite-paramagnetic martensite transition ΔS=24 J/(kg K) was detected for ΔH=5 T at T=350 K. The variation in composition of Ni₂MnGa can drastically change the magnetic state of the martensitic phase below and in the vicinity of TM. The presence of the martensitic phase with magnetic moment much smaller than that in the austenitic phase above TM leads to the large inverse MCE in the Ni₄₂Co₈Mn_32−yFeyGa₁₈ system. The adiabatic change of temperature (ΔT_ad) in the vicinity of TC and TM of Ni₅₀Mn₃₅In₁₅ and Ni₅₀Mn₃₅In₁₄Z (Z=Al, Ge) was found to be ΔT_ad=−2 K and 2 K for ΔH=1.8 T, respectively. It was observed that |ΔT_ad|≈1 K for ΔH=1 T for both types of transitions. The results on resistivity, magnetoresistance, Hall resistivity in some In-based alloys are discussed.     

Magnetic/structural diagram, chemical composition-dependent magnetocaloric effect in self-doped antipervoskite compounds Sn1−xCMn3+x (0≤x≤0.40)

The effects of Mn substitutions on the crystal structure, magnetic properties, and magnetocaloric effect (MCE) of antiperovskite Sn_1−xCMn_3+x (0≤x≤0.40) have been investigated detailedly. Both the Curie temperature (T_C) and the magnetizations at 40 kOe decrease with increasing x firstly for x≤0.10, and then increase with increasing x further. The type of magnetic transition changes from first-order to second-order around x=0.10 with increasing x. Chemical composition-dependent MCE is also studied around T_C. With increasing x, the maximal magnetic entropy changes decrease and the magnetic phase transitions broaden. Accordingly, the relative cooling power (RCP) increases with increasing x, reaching the largest values of ∼0.56 J/cm³ (∼75 J/kg) and ∼1.66 J/cm³ (∼221 J/kg) with the magnetic changes of 20 kOe and 48 kOe, respectively. Considering the large RCP, inexpensive, and innoxious raw materials, these serial samples Sn_1−xCMn_3+x are suggested to be potential room-temperature magnetic refrigerant materials.     

Structural,magnetic and magnetocaloric properties of AMn1−xGaxO3 compounds with 0≤x≤0.2

Structural, magnetic and magnetocaloric properties of manganites series with the AMn_1−xGa_xO₃ (A=La_0.75Ca_0.08Sr_0.17 and x=0, 0.05, 0.1 and 0.2) composition have been investigated to shed light on Ga-doping influence. Solid-state reaction method was used for preparation. From XRD study, all samples are found single phase and crystallize in the orthorhombic structure with the Pnma space group. The variation of the magnetization M vs. temperature T, under an applied magnetic field of 0.05 T, reveals a ferromagnetic–paramagnetic transition for all samples. The experimental results indicate that T_C decreases from 336 to 135 K with increasing Ga substitution. Magnetocaloric effect (MCE) was estimated, in terms of isothermal magnetic entropy change (−ΔS_M), using the M(T, μ₀H) data and employing the thermodynamic Maxwell equation. The maximum entropy change and Relative Cooling Power (RCP) show non-monotonic behaviors with increasing the concentration of Gallium. In fact, the maximum value of ΔS_Mmaxof AMn_1−xGa_xO₃ for x=0.00 and 0.2 samples is found to be, respectively, 2.87 and 1.17 J/kg/K under an applied magnetic field change of 2 T. For the same applied magnetic field (μ₀H=2 T), the RCP values are found to vary between 97.58 and 89 J/kg.     

Magnetic properties and room-temperature magnetocaloric effect in the doped antipervoskite compounds Ga1−xAlxCMn3 (0≤x≤0.15)

We report the effects of Al doping on the structure, magnetic properties, and magnetocaloric effect of antiperovskite compounds Ga_1−xAl_xCMn₃ (0≤x≤0.15). Partial substitutions of Al for Ga enhance the Curie temperature (from 250 K for x=0.0 to 312 K for x=0.15) and the saturation magnetization. On increasing the doping level x, the maximum values of the magnetic entropy change (−ΔS_M) decreases while the temperature span of −ΔS_M vs. T plot broadens. Furthermore, the relative cooling power (RCP) is also studied. For 20 kOe, the RCP value tends to saturate at a high doping level (for x=0.12, 119 J/kg at 296 K). However, at 45 kOe, the RCP value increases quickly with increasing x (for x=0.15, 293 J/kg at 312 K). Considering the relatively large RCP and inexpensive raw materials, Ga_1−xAl_xCMn₃ may be alternative candidates for room-temperature magnetic refrigeration.     

Structure, magneto-structural transitions and magnetocaloric properties in Ni50−xMn37+xIn13 melt spun ribbons

Melt spun Ni_50−xMn_37+xIn₁₃ (2≤x≤5) ribbons were investigated for the structure, microstructure, magneto-structural transitions and inverse magnetocaloric effect (IMCE) associated with the first-order martensitic phase transition. The influence of excess Mn in Ni site (or Ni/Mn content) on the martensite transition and the associated magnetic and magnetocaloric properties are discussed. It was found that with the increase in Mn content, the martensitic transition shifted from 325 to 240 K as x is varied from 2 to 4, and the austenite phase was stabilized at room temperature. The x=5 ribbon did not show the martensitic transition. For the x=3 ribbon, the structural and magnetic transitions are close together unlike in the x=4 ribbon in which they are far (∼60 K) apart. The zero field cooled and field cooled curves support the presence of exchange bias blocking temperature due to antiferromagnetic interactions in the ribbons. A large change in the magnetization between the martensite and austenite phases was observed for a small variation in the Ni/Mn content, which resulted in large IMCE. A large positive magnetic entropy change (ΔS_M) of 32 J/kg K at room temperature (∼ 300 K) for a field change of 5 T with a net refrigeration capacity of 64 J/kg was obtained in the Ni₄₇Mn₄₀In₁₃ ribbon.     

Field-induced structural transition and the related magnetic entropy change in Ni43Mn43Co3Sn11 alloy

Magnetic properties and magnetic entropy change ΔS were investigated in Heusler alloy Ni₄₃Mn₄₃Co₃Sn₁₁. With decreasing temperature this alloy undergoes a martensitic structural transition at T_M=188 K. The incorporation of Co atoms enhances ferromagnetic exchange for parent phases. Austenitic phase with cubic structure shows strong ferromagnetic behaviors with Curie temperature T_C^A at 346 K, while martensitic phase shows weak ferromagnetic properties. An external magnetic field can shift T_M to a lower temperature at a rate of 4.4 K/T, and a field-induced structural transition from martensitic to austenitic state takes place at temperatures near but below T_M. As a result, a great magnetic entropy change with positive sign appears. The size of ΔS reaches 33 J/kg K under 5 T magnetic field. More important is that the ΔS displays a table-like peak under 5 T, which is favorable for Ericsson-type refrigerators.     

Magnetocaloric properties of (La0.67−xGdx)Sr0.33MnO3 polycrystalline nanoparticles

In this paper, magnetic property and magnetocaloric effect (MCE) in nanoparticles perovskite manganites of the type (La_0.67−xGd_x)Sr_0.33MnO₃ (x=0.10, 0.15, 0.20) synthesized by using an amorphous molecular alloy as precursor have been reported. From the magnetic measurements as function of temperature and magnetic applied field, we have discovered that the Curie temperature (T_C) of the prepared samples is found to be strongly dependent on Gd content. The Curie temperature of samples is 358.4, 343.2, and 285.9 K for x=0.1, 0.15, and 0.2, respectively. A large magnetocaloric effect close to T_C has been observed with a maximum of magnetoentropy change in all the samples, ∣ΔS_M∣_max of 1.96 and 4.90 J/kg K at 2 and 5 T, respectively, for a substitution rate of 0.15. In addition, the maximum magnetic entropy change observed for samples with different concentration of Gd, exhibits a linear dependence with the applied high magnetic field. These results suggest that (La_0.67−x Gd_x)Sr_0.33MnO₃ (x=0.10, 0.15, 0.20) compounds could be a suitable candidate as working substance in magnetic refrigeration near room temperature.     

The influence of the sintering temperature on the structural and the magnetic properties of doped manganites: La0.95Ag0.05MnO3 and La0.75Ag0.25MnO3

La_1−xAg_xMnO₃ samples were synthesized by standard sol-gel method with Ag concentrations of x=0.05 and 0.25. The samples from each concentration were pressed and sintered at 1000, 1200 and 1400 °C for 24 h in air for a systematic study. They were examined structurally by Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM) with Energy Dispersive Spectroscopy (EDS) and X-ray Diffraction (XRD) and magnetically by Magnetic Properties Measurements System (MPMS). AFM and SEM analyses show that surface morphology changes with Ag concentration and sintering temperature (T_S). It was observed that high temperature sintering leads Ag to leave material as determined from EDS analyses. XRD spectra exhibited that the crystal structure changes with Ag concentration while showing pronounced change with the sintering temperature. From the magnetic measurements, the Curie temperatures (T_C) and the isothermal magnetic entropy changes (−ΔSM) were calculated. It was observed that T_C increases with Ag concentration and decreases with T_S. The maximum −ΔSM was calculated to be 7.2 J/kg K under the field change of 5 T for the sample sintered at 1000 °C with x=0.25.     

Magnetic entropy change in perovskite manganites La0.6Pr0.1Pb0.3MnO3 with double metal-insulator peaks

Following the double metal-insulator peaks found in series of perovskite manganites La_0.7−xPr_xPb_0.3MnO₃ (x=0, 0.05, 0.1), the magnetic entropy change of La_0.6Pr_0.1Pb_0.3MnO₃ was carefully investigated as a representative. The maximum magnetic entropy change (ΔS_H=−1.7 J/kg K at 300 K) and the expanded refrigerant capacity (about 123.8 J/kg) had been obtained under 10 kOe magnetic field variation, though the double peak of maximum magnetic entropy change had not occurred since the comparative faint magnetic signal from the Pr ions inhomogeneity existed in the octahedral frame submerged in the strong magnetic signal originated from the dominating octahedral frame both in the double exchange mechanism, but the width at half maximum in the magnetic entropy change comparatively broadened.     

Magnetic entropy change in GdCo13−xSix intermetallic compounds

The magnetic entropy change in GdCo_13−xSi_x (x=3.8, 4, 4.1, and 4.2) intermetallic compounds has been investigated by means of magnetic measurements in the vicinity of their Curie temperature. It was found that the magnetic ordering temperatures decrease from 60 K at x=3.8 to 28 K for x=4.2. The magnetic entropy change is calculated from isothermal magnetization versus magnetic field at various temperatures using the Maxwell relation. As a result, the maximum magnetic entropy changes of the investigated compounds, at their Curie temperatures, decrease from 11.5 J/kg K for x=4.2 to 6.86 J/kg K for x=3.8 in a field change of 0-3 T, whereas it decreases from 5.13 J/kg K for x=4.2 to 2.60 J/kg K for x=3.8 in a field change of 0-1 T. Moreover, the maximum value of the magnetic entropy change obtained at a higher field for GdCo_13−xSi_x with x=4 (23.75 J/kg K at 5 T) is comparable to that of various types of compounds with a cubic NaZn₁₃-type structure. Finally, the maximum of the magnetic entropy change is found to decrease with increasing Si content.     

Magnetocaloric properties in the Cr-doped La0.7Sr0.3MnO3 manganites

Single-phase polycrystalline samples of La_0.7Sr_0.3Mn_1-xCr_xO₃ with nominal composition of x=0.00, 0.20, 0.40 and 0.50 were prepared by a conventional solid-state reaction method in air. Investigations of magnetization were carried out in the temperature range 5-400 K and magnetic field range 0-8 T. It was found that the Curie temperature T_C decreases with increasing x and the maximum magnetic entropy change (−ΔS_M) for x=0.20 is ∼1.203 and ∼2.653 J/kg K, respectively for 2 and 6 T magnetic field near the temperature of 280 K.     

Structural, magnetic and magnetocaloric properties of La0.7−xEuxBa0.3MnO3 perovskites

Polycrystalline perovskite manganites La_0.7−xEu_xBa_0.3MnO₃(x=0.05, 0.1 and 0.15) were prepared by sol-gel method. The prepared samples remain single phase with a perovskite structure, revealed by X-ray diffraction. The structure refinement of La_0.7−xEu_xBa_0.3MnO₃(x=0.05, 0.1 and 0.15) samples was performed in the hexagonal setting of the R3¯c space group. The dependence of magnetization M on applied magnetic field H and temperature T was measured carefully near the Curie temperature T_C for all the samples. With the increasing Eu content, both the unit cell volume and Curie temperature T_C of 298 K has been detected with a maximum of magnetic entropy |ΔS_M^max| for the La_0.7−xEu_xBa_0.3MnO₃ with x=0.15, reaching a value of 2.3 J/kg K when a magnetic field of 10 kOe was applied and the relative cooling power (RCP) is 46 J/kg. These results suggest that the material may be a suitable candidate as working substance in magnetic refrigeration near room temperature.