Room temperature magnetic entropy change and magnetoresistance in La0.70(Ca0.30−xSrx)MnO3:Ag 10% (x=0.0−0.10)

The magnetic and magnetocaloric properties of polycrystalline La_0.70(Ca_0.30−xSr_x)MnO₃:Ag 10% manganite have been investigated. All compositions are crystallized in single phase orthorhombic Pbnm space group. Both, the insulator–metal transition temperature (T^IM) and Curie temperature (T_c) are observed at 298 K for x=0.10 composition. Though both T^IM and T_c are nearly unchanged with Ag addition, the MR is increased. The MR at 300 K is found to be as large as 31% with magnetic field change of 1 T, whereas it reaches up to 49% at magnetic field of 3 T for the La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample. The maximum entropy change (ΔS_Mmax) at near its T_c (300.5 K) is 7.6 J kg⁻¹ K⁻¹ upon the magnetic field change of 5 T. The La_0.70Ca_0.20Sr_0.10MnO₃:Ag_0.10 sample having good MR (31%^1 T, 49%^3 T) and reasonable change in magnetic entropy (7.6 J kg⁻¹.K⁻¹, 5 T) at 300 K can be a potential magnetic refrigerant material at ambient temperatures.     

Effect of Mn-site vacancies on the magnetic entropy change and the Curie temperature of La0.67Ca0.33Mn1−xO3 perovskite

Single-phase polycrystalline samples of La_0.67Ca_0.33Mn_1−xO₃ (x=0.00, 0.02, 0.04, 0.06) have been prepared using the sol-gel method. The structure, magnetocaloric properties and the Curie temperature of the samples with different Mn vacancy concentrations have been investigated. The experimental results show that vacancy doping at the Mn-sites has a significant influence on the magnetic properties of La_0.67Ca_0.33Mn_1−xO₃. The Curie temperature decreases monotonically with increasing the Mn-site vacancy concentration x. A remarkable enhancement of the magnetic entropy change has been obtained in the La_0.67Ca_0.33Mn_0.98O₃ sample. The entropy change reaches |ΔS_M|=3.10 J kg⁻¹ K⁻¹ at its Curie temperature (264 K) under an applied magnetic field H=10 kOe, which is almost the same value as that of pure Gd.     

Structural and magnetic phase diagram and room temperature CMR effect of La1−xAgxMnO3

The study of the structural and magnetic phase diagram of the manganites La_1−xAg_xMnO₃ shows similarity with the La_1−x′Sr_x′MnO₃ series, involving a metallic ferromagnetic domain at relatively high temperature (≈300 K). The Ag-system differs from the Sr-one by a much smaller homogeneity range (x≤1/6) and the absence of charge ordering. But the most important feature of the Ag-manganites deals with the exceptionally high magnetoresistance (−25%) at room temperature under 1.2 T, that appears for the composition x=1/6. The latter is interpreted as the coincidence of the optimal double exchange condition (Mn³⁺:Mn⁴⁺=2) with T_max=300 K (maximum of the ρ(T) curve in zero field).     

Low temperature specific heat of bi-layered manganites La2−2xSr1+2xMn2O7 (x=0.3 and 0.5)

The specific heat (C) of bi-layered manganites La_2−2xSr_1+2xMn₂O₇ (x=0.3 and 0.5) is investigated for the ground state of low temperature excitations. A T^3/2 dependent term in the low temperature specific heat (LTSH) is identified at zero magnetic field and suppressed by magnetic fields for x=0.3 sample, which is consistent with a ferromagnetic metallic ground state. For x=0.5 sample, a T² term is observed and is consistent with a two-dimensional (2D) antiferromagnetic insulator. However, it is almost independent of magnetic field within the range of measured temperature (0.6-10 K) and magnetic field (6 T).     

Hydrothermal synthesis and Magnetocaloric effect of La0.5Ca0.3Sr0.2MnO3

The hydrothermal synthesis and magnetic entropy change for the perovskite manganite La_0.5Ca_0.3Sr_0.2MnO₃ have been studied. The La_0.5Ca_0.3Sr_0.2MnO₃ can be produced as phase-pure, crystalline powders in one step from solutions of metal salts in aqueous potassium hydroxide solution at a temperature of 513 K in 72 h. Scanning electron microscopy shows that the materials are made up of cuboid-shaped particles in typical dimension of 4.0×2.5×1.6 μm. Heat treatment can improve the magnetocaloric effect for the hydrothermal sample. The maximum magnetic entropy change ΔS_M for the as-prepared sample is 0.88 J kg⁻¹ K⁻¹ at 315 K for a magnetic field change of 2.0 T. It increases to 1.52 J kg⁻¹ K⁻¹, near its Curie temperature (317 K) by annealing the sample at 1473 K for 6 h. The hydrothermal synthesis method is a feasible route to prepare high-quality perovskite material for magnetic refrigeration application.     

Magnetic properties and Griffiths singularity in La0.45Sr0.55 Mn1−xCoxO3

The magnetic properties and the Griffiths singularity were investigated in Mn-site doped manganites of La_0.45Sr_0.55Mn_1−xCo_xO₃ (x=0, 0.05, 0.10 and 0.15) in this work. The parent sample La_0.45Sr_0.55MnO₃ undergoes a paramagnetic-ferromagnetic transition at T_C=290 K and a ferromagnetic-antiferromagnetic transition at T_N=191 K. The doping of Co ions enhances the ferromagnetism and suppresses the antiferromagnetism. The enhanced ferromagnetism results from the fact that the Co doping enhances the Mn³⁺-Mn⁴⁺ double-exchange interaction and induces the Co²⁺-Mn⁴⁺ ferromagnetic superexchange interaction. Detailed investigation on the magnetic behavior above T_C exhibits that the Griffiths singularity takes place in this series of Mn-site doped compounds. The correlated disorder induced by the Co ionic doping, together with the phase competition from the ferromagnetic and the antiferromagnetic interactions among Mn ions, is responsible for the Griffiths singularity.     

Structural, magnetic and magnetotransport behavior of La0.7SrxCa0.3−xMnO3 compounds

A systematic investigation of the structural, magnetic and electrical properties of a series of nanocrystalline La_0.7Sr_xCa_0.3−xMnO₃ materials, prepared by high energy ball milling method and then annealed at 900 °C has been undertaken. The analysis of the XRD data using the Win-metric software shows an increase in the unit cell volume with increasing Sr ion concentration. The La_0.7Sr_xCa_0.3−xMnO₃ compounds undergo a structural orthorhombic-to-monoclinic transition at x=0.15. Electric and magnetic measurements show that both the Curie temperature and the insulator-to-metal transition temperature increase from 259 K and 253 K correspondingly for La_0.7Ca_0.3MnO₃ (x=0) to 353 K and 282 K, respectively, for La_0.7Sr_0.3MnO₃ (x=0.3). It is argued that the larger radius of Sr²⁺ ion than that of Ca²⁺ is the reason to strengthen the double-exchange interaction and to give rise to the observed increase of transition temperatures. Using the phenomenological equation for conductivity under a percolation approach, which depends on the phase segregation of ferromagnetic metallic clusters and paramagnetic insulating regions, we fitted the resistivity versus temperature data measured in the range of 50-320 K and found that the activation barrier decreased with the raising Sr²⁺ ion concentration.     

Enhancement of the anomalous Hall effect and spin glass behavior in the bilayered manganite La2−2xSr1+2xMn2O7

The Hall resistivity and magnetization have been investigated in the ferromagnetic state of the bilayered manganite La_2−2xSr_1+2xMn₂O₇ (x=0.36). The Hall resistivity shows an increase in both the ordinary and anomalous Hall coefficients at low temperatures below 50 K, a region in which experimental evidence for the spin glass state has been found in a low magnetic field of 1 mT. The origin of the anomalous behavior of the Hall resistivity relevant to magnetic states may lie in the intrinsic microscopic inhomogeneity in a quasi-two-dimensional electron system.     

Investigation of magnetocaloric effect in La0.45Pr0.25Ca0.3MnO3 by magnetic,differential scanning calorimetry and thermal analysis

We investigated magnetocaloric effect in La_0.45Pr_0.25Ca_0.3MnO₃ by direct methods (changes in temperature and latent heat) and indirect method (magnetization isotherms). This compound undergoes a first-order paramagnetic to ferromagnetic transition with T_C=200 K upon cooling. The paramagnetic phase becomes unstable and it transforms into a ferromagnetic phase under the application of magnetic field, which results in a field-induced metamagnetic transition (FIMMT). The FIMMT is accompanied by release of latent heat and temperature of the sample as evidenced from differential scanning calorimetry and thermal analysis experiments. A large magnetic entropy change of ΔS_m=−7.2 J kg⁻¹ K⁻¹ at T=212.5 K and refrigeration capacity of 228 J kg⁻¹ are found for a field change of ΔH=5 T. It is suggested that destruction of magnetic polarons and growth of ferromagnetic phase accompanied by a lattice volume change with increasing magnetic field is responsible for the large magnetocaloric effect in this compound.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

High temperature ferromagnetism of the vacuum-annealed (In1−xFex)2O3 powders

(In_1−xFe_x)₂O₃ (x = 0.02, 0.05, 0.2) powders were prepared by a solid state reaction method and a vacuum annealing process. A systematic study was done on the structural and magnetic properties of (In_1−xFe_x)₂O₃ powders as a function of Fe concentration and annealing temperature. The X-ray diffraction and high-resolution transmission electron microscopy results confirmed that there were not any Fe or Fe oxide secondary phases in vacuum-annealed (In_1−xFe_x)₂O₃ samples and the Fe element was incorporated into the indium oxide lattice by substituting the position of indium atoms. The X-ray photoelectron spectroscopy revealed that both Fe²⁺ and Fe³⁺ ions existed in the samples. Magnetic measurements indicated that all samples were ferromagnetic with the magnetic moment of 0.49-1.73 μ_B/Fe and the Curie temperature around 783 K. The appearance of ferromagnetism was attributed to the ferromagnetic coupling of Fe²⁺ and Fe³⁺ ions via an electron trapped in a bridging oxygen vacancy.     

Structure, transport and magnetic properties in La2xSr2−2xCo2xRu2−2xO6

The perovskite solid solutions of the type La_2xSr_2−2xCo_2xRu_2−2xO₆ with 0.25≤x≤0.75 have been investigated for their structural, magnetic and transport properties. All the compounds crystallize in double perovskite structure. The magnetization measurements indicate a complex magnetic ground state with strong competition between ferromagnetic and antiferromagnetic interactions. Resistivity of the compounds is in confirmation with hopping conduction behaviour though differences are noted especially for x=0.4 and 0.6. Most importantly, low field (50 Oe) magnetization measurements display negative magnetization during the zero field cooled cycle. X-ray photoelectron spectroscopy measurements indicate the presence of Co²⁺/Co³⁺ and Ru⁴⁺/Ru⁵⁺ redox couples in all compositions except x=0.5. Presence of magnetic ions like Ru⁴⁺ and Co³⁺ gives rise to additional ferromagnetic (Ru-rich) and antiferromagnetic sublattices and also explains the observed negative magnetization.     

Highly cation-deficient manganese perovskite, La1−xMn1−yO3 with x=y

Oxidative (δ>0) nonstoichiometry in the perovskite ‘LaMnO_3+δ’ has been known to be manifested not with O interstitials but rather with cation vacancies of equal amounts at the two cation sites, La and Mn, i.e. La_1−xMn_1−yO₃ with x=y. Here, we report the fabrication of samples with record-high cation-vacancy concentrations (x>0.12 or δ>0.4) by means of a variety of high-pressure oxygenation techniques. Linear (negative) dependence of the cell volume on x was observed within the whole x range investigated, down to 56.9 Å³ (per formula unit) for a sample oxygenated at 5 GPa and 1100 °C using Ag₂O₂ as an excess oxygen source. With increasing degree of cation deficiency in La_1−xMn_1−xO₃, the ferromagnetic transition temperature was found to follow a bell shape with respect to x exhibiting a maximum of ∼250 K about x≈0.1. For moderately oxygenated samples large magnetoresistance effect was evidenced.     

Magnetic disorder induced enhanced magneto-resistance in La0.5Sr0.5Co1−xRuxO3

We observe a sharp increase in negative magneto-resistance ratio up to 40% for x=0.1, in La_0.5Sr_0.5Co_1−xRu_xO₃ which is due to the magnetic disorder induced by an anti-ferromagnetic interaction between Co and Ru ions. We also observe a metal to insulator and a ferromagnetic to anti-ferromagnetic transition for 0≤x≤0.3. Ruthenium (IV) ion disrupts an intermediate spin state of cobalt (Co³⁺:t_2g⁵e_g¹), forcing a double exchange mediated ferromagnetic state to an anti-ferromagnetic spin state for x≥0.2.     

Analysis of magnetic field dependent mobility in ferromagnetic Ga1−xMnxAs layers

The magneto-transport properties of ferromagnetic Ga_1−xMn_xAs epilayers with Mn mole fractions in the range of x≈2.2-4.4% were investigated through Hall effect measurements. The magnetic field-dependent Hall mobility for a metallic sample with x≈2.2% in the temperature range of T=0-300 K was analyzed by magnetic field-dependent mobility model including an activation energy of Mn acceptor level. This model provides outstanding fits to the measured data up to T=300 K. It was found that the acceptor levels with activation energies of 112 meV at B=0 Oe decreased to 99 meV at B=5 kOe in the ferromagnetic region. The decrease in acceptor activation energy was due to the spin splitting of the Mn acceptor level in the ferromagnetic region, and was responsible for increase in carrier concentration.     

The magnetic behavior of La1−xTbxMn2Si2 (0≤x≤0.3) in weak magnetic fields

The structure and magnetic properties of La_1−xTb_xMn₂Si₂ (0≤x≤0.3) were studied by X-ray powder diffraction and DC magnetization measurements. All the compounds crystallize in ThCr₂Si₂-type structure. Substitution of Tb for La led to a linear decrease in the lattice constants and the unit-cell volume. A ferromagnetic phase for x≤0.15, and an antiferromagnetic phase for x=0.3 have been observed at about room temperature, whereas the compounds with x=0.2 and 0.25 exhibit a magnetic phase transition from ferromagnetism to antiferromagnetism.     

Critical behavior and magnetic entropy change in the La0.6Sr0.4Mn0.8Fe0.1Cr0.1O3 perovskite

Critical behavior in the La_0.6Sr_0.4Mn_0.8Fe_0.1Cr_0.1O₃ ceramics was studied using magnetization methods. Results show that the paramagnetic–ferromagnetic transition is of second order. Based on the critical behavior analysis using the Banerjee criterion and the Kouvel–Fisher method, we find the critical exponents: β=0.395±0.010, γ=1.402±0.010, and δ=5.208±0.007, for which the magnetic interaction is satisfied within the three-dimensional Heisenberg model. Results indicate the presence of short-range interactions. The magnetic entropy change (−ΔS_M) reached maximum values of 1.75, 1.45, 1.15, 0.8 and 0.43 J Kg⁻¹ K⁻¹ under a magnetic field variation of 5, 4, 3, 2 and 1 T, respectively. Nevertheless, these (−ΔS_M) values are much low for any potential application at this moment. The nature of this phenomenon is discussed in relation to the characteristics of the magnetic phase transition and critical exponents.     

A variable temperature EPR study of the manganites (La1/3Sm2/3)2/3SrxBa0.33−xMnO3 (x=0.0, 0.1, 0.2, 0.33): Small polaron hopping conductivity and Griffiths phase

Four manganite samples of the series, (La_1/3Sm_2/3)_2/3Sr_xBa_0.33−xMnO₃, with x=0.0, 0.1, 0.2 and 0.33, were investigated by X-band (∼9.5 GHz) electron paramagnetic resonance (EPR) in the temperature range 4-300 K. The temperature dependences of EPR lines and linewidths of the samples with x=0.0, 0.1 and 0.2, containing Ba²⁺ ions, exhibit similar behavior, all characterized by the transition temperatures (T_C) to ferromagnetic states in the 110-150 K range. However, the sample with x=0.33 (containing no Ba²⁺ ions) is characterized by a much higher T_C=205 K. This is due to significant structural changes effected by the substitution of Ba²⁺ ions by Sr²⁺ ions. There is an evidence of exchange narrowing of EPR lines near T_min, where the linewidth exhibits the minimum. Further, a correlation between the temperature dependence of the EPR linewidth and conductivity is observed in all samples, ascribed to the influence of small-polaron hopping conductivity in the paramagnetic state. The peak-to-peak EPR linewidth was fitted to ΔB_pp(T)=ΔB_pp,min+A/Texp(−E_a/k_BT), with E_a=0.09 eV for x=0.0, 0.1 and 0.2 and E_a=0.25 eV for x=0.33. From the published resistivity data, fitted here to σ(T)∝1/T exp(−E_σ/k_BT), the value of E_σ, the activation energy, was found to be E_σ=0.18 eV for samples with x=0.0, 0.1 and 0.2 and E_σ=0.25 eV for the sample with x=0.33. The differences in the values of E_a and E_σ in the samples with x= 0.0, 0.1and 0.2 and x=0.33 has been ascribed to the differences in the flip-flop and spin-hopping rates. The presence of Griffiths phase for the samples with x=0.1 and 0.2 is indicated; it is characterized by coexistence of ferromagnetic nanostructures (ferrons) and paramagnetic phase, attributed to electronic phase separation.     

Structural,magnetic and magnetocaloric properties of AMn1−xGaxO3 compounds with 0≤x≤0.2

Structural, magnetic and magnetocaloric properties of manganites series with the AMn_1−xGa_xO₃ (A=La_0.75Ca_0.08Sr_0.17 and x=0, 0.05, 0.1 and 0.2) composition have been investigated to shed light on Ga-doping influence. Solid-state reaction method was used for preparation. From XRD study, all samples are found single phase and crystallize in the orthorhombic structure with the Pnma space group. The variation of the magnetization M vs. temperature T, under an applied magnetic field of 0.05 T, reveals a ferromagnetic–paramagnetic transition for all samples. The experimental results indicate that T_C decreases from 336 to 135 K with increasing Ga substitution. Magnetocaloric effect (MCE) was estimated, in terms of isothermal magnetic entropy change (−ΔS_M), using the M(T, μ₀H) data and employing the thermodynamic Maxwell equation. The maximum entropy change and Relative Cooling Power (RCP) show non-monotonic behaviors with increasing the concentration of Gallium. In fact, the maximum value of ΔS_Mmaxof AMn_1−xGa_xO₃ for x=0.00 and 0.2 samples is found to be, respectively, 2.87 and 1.17 J/kg/K under an applied magnetic field change of 2 T. For the same applied magnetic field (μ₀H=2 T), the RCP values are found to vary between 97.58 and 89 J/kg.     

Photoluminescence investigation of ferromagnetic Ga1−xMnxN layers with GaN templates grown on sapphire (0 0 0 1) substrates

We have investigated the temperature and composition dependent photoluminescence (PL) spectra in Ga_1−xMn_xN layers (where x ≈ 0.1-0.8%) grown on sapphire (0 0 0 1) substrates using the plasma-enhanced molecular beam epitaxy technique. The efficient PL is peaked in the red (1.86 eV), yellow (2.34 eV), and blue (3.29 eV) spectral range. The band-gap energy of the Ga_1−xMn_xN layers decreased with increasing temperature and manganese composition. The band-gap energy of the Ga_1−xMn_xN layers was modeled by the Varshni equation and the parameters were determined to be α = 2.3 × 10⁻⁴, 2.7 × 10⁻⁴, 3.4 × 10⁻⁴ eV/K and β = 210, 210, and 230 K for the manganese composition x = 0.1%, 0.2%, and 0.8%, respectively. As the Mn concentration in the Ga_1−xMn_xN layers increased, the temperature dependence of the band-gap energy was clearly reduced.