Magnetic properties and static-dynamic magnetostrictive characteristics for SmFe2/Fe exchange-coupled multilayers

Giant magnetostrictive SmFe₂/Fe exchange-coupled multilayers were fabricated by ion beam sputtering deposition on glass substrates. The effects of SmFe₂/Fe exchange coupling action and vacuum annealing on soft-magnetic property and static-dynamic magnetostrictive characteristics of SmFe₂/Fe multilayers were investigated. The results showed that the soft-magnetic, static-dynamic magnetostrictive characteristics were greatly improved by SmFe₂/Fe exchange coupling action and proper vacuum annealing treatment temperature. Compared with that of SmFe₂ single film, the coercivity in the direction of easy magnetization axis for SmFe₂/Fe exchange-coupled multilayers exhibited a greater decrease. Better soft-magnetic properties were achieved (H_c=2.54 kA/m, M_s=120.38 emu/g, and M_r/M_s=0.21) after vacuum annealing at certain temperature. The magnetostrictive coefficient for SmFe₂/Fe exchange-coupled multilayers was about 135 ppm at 16 kA/m magnetic field. At first order resonant frequency (99.2 Hz), the amplitude peak-peak value for the as-deposited SmFe₂/Fe exchange-coupled multilayers was 46 μm. After the vacuum annealing treatment at 250 °C, the amplitude peak-peak value increased to 650 μm.     

Magnetic dynamics of charge ordered Nd0.80Na0.20MnO3 compound

The magnetic dynamics of charge ordered Nd_0.8Na_0.2MnO₃ compound was studied by measuring the temperature variation of magnetization for different magnetic fields up to 7 T and, the field variation of magnetization at different temperatures down to 5 K. This sample exhibits a charge-ordering transition at 180 K, followed by a weak ferromagnetic (FM) transition at around 100 K and a spin glass like transition below 40 K. Suppression of charge-ordering and spin glass like transition and increase in FM T_C were observed with an increase in magnetic field. A reversible metamagnetic transition above a threshold field (H_f) of 4.5 T was observed at 130 K, followed by a saturation magnetization of 3.2 μ_B/f.u. However at 5 K, an irreversible field induced first order phase transition from charge ordered state to FM state was observed at H_f=5 T. For comparison, the temperature and field variations of magnetization were studied on a FM compound from the same series with the composition Nd_0.90Na_0.10MnO₃. A clear FM transition with a T_C of 113 K and a saturation magnetization of 4.3 μ_B/f.u was observed.     

Magnetic and magneto-transport properties of double perovskite Ba2−xSrxFeMoO6 system

The structural magnetic and magneto-transport properties of double perovskite system Ba_2−xSr_xFeMoO₆ (0?x?1.0) prepared in bulk polycrystalline form are reported in this paper. X-ray diffraction analysis showed that samples are single phase and the lattice constants decreases with increase in the Sr content. The degree of Fe-Mo ordering has been found decreasing in the series with an increase in the Sr content. Parent compound Ba₂FeMoO₆ exhibits saturation magnetic moment value of 3.54 μ_B/f.u. at 85 K in a magnetic field of 6000 Oe. Temperature dependence of resistivity shows metallic behavior for all the samples. The magneto-resistance (MR) of the compound with x=0.4 is higher than that of the other samples. At room temperature this system shows a saturation magnetization value of 1.73 μ_B/f.u. and MR value of 7.08% (1 T). The observed variations in the structural and magnetic properties are attributed to the change of chemical pressure due to the substitution of Sr in place of Ba. The effect of antisite disorder (ASD) defects on magneto-transport properties is studied in more detail.     

Iron isotope effect on Tc in optimally-doped (Ba,K)Fe2As2 (Tc = 38 K) and SmFeAsO1−y (Tc = 54 K) superconductors

We report the iron isotope effect on a transition temperature (T_c) in an optimally-doped (Ba,K)Fe₂As₂ (T_c = 38 K) and SmFeAsO_1−y (T_c = 54 K) superconductors. In order to obtain the reliable isotope shift in T_c, twin samples with different iron isotope mass are synthesized in the same conditions (simultaneously) under high-pressure. We have found that (Ba,K)Fe₂As₂ shows an inverse iron isotope effect α_Fe = −0.18 ± 0.03 while SmFeAsO_1−y shows a small iron isotope effect α_Fe = −0.02 ± 0.01, where the isotope exponent α is defined by T_c ∼ M^−α (M is the isotopic mass). The results show that α_Fe changes in the iron-based superconductors depending on the system. The distinct iron isotope effects imply the exotic coupling mechanism in the iron-based superconductors.     

Effect of Mn on the magnetic properties of Fe3B/Nd2Fe14B nanocomposites

The magnetic properties of Nd_4.5Fe_77−xMn_xB_18.5 (x=0, 1 and 2) nanocomposites prepared by the crystallization of amorphous precursors were investigated. Addition of Mn is found to decrease the crystallization temperature of the amorphous ribbons. The intrinsic coercivity _iH_c and maximum energy product (BH)_max increase from 2.6 kOe and 9.1 MGOe for x=0 to 3.1 kOe and 10.3 MGOe for x=1, respectively, and the remanence ratio M_r/M_s increases from 0.70 to 0.72. The effect of Mn on Curie temperature T_C and the thermal stability of M_r and _iH_c were also studied. ⁵⁷Fe Mössbauer spectra have been recorded for x=0, 1 and 2 ribbons at room temperature and site preference of the Mn atoms in Fe₃B and Nd₂Fe₁₄B phases is discussed using the Mössbauer spectroscopy.     

Synthesis,magnetic and electrical transport properties of magnetoresistance material Sr2FeMoO6 by microwave sintering

Magnetoresistance material Sr₂FeMoO₆ with double perovskite structure was synthesized by microwave sintering method using SrCO₃, Fe₂O₃ and MoO₃ as raw materials, with MnO₂ for microwave absorber. The phase structure, magnetic and electrical transport properties were investigated by X-ray powder diffraction (XRD) and vibrating-sample magnetometer. XRD analysis shows that the as-synthesized sample is Sr₂FeMoO₆ with tetragonal crystal structure and I4/mmm space group. The unit cell parameters are a=0.5587 nm, c=0.7894 nm, volume=0.2464 nm³. The calculated grain size of the sample is 31.62 nm, which is obtained by the Scherrer formula using the diffraction data. Magnetism testing results show that the sample Sr₂FeMoO₆ is ferromagnetic with the magnetic transition temperature of about 380 K. Under 1.0 T magnetic field, the saturation and spontaneous magnetization of Sr₂FeMoO₆ is 1.25 μ_B/f.u. and 1.00 μ_B/f.u. at room temperature. The magnetoresistance ratio of the sample is 28%. Electrical transport properties testing results indicate that the sample exhibits typical semiconductor behavior. The conductive mechanism of Sr₂FeMoO₆ is highly dependent on temperature: within the temperature range of 100–300 K, the mechanism is attributed to the small polaron variable-range hopping model; while it is ascribed to the adiabatic small polaron model within the temperature range of 80–100 K.     

Neutron scattering study on CeAgAs2

CeAgAs₂, an HfCuSi₂ like layered pnictide, orders antiferromagnetically at T_N=6.2(1) K. The ordering process was monitored in neutron diffraction experiments in the temperature range 10 K≥T≥3.5 K. At T=4 K the lattice parameters are a=5.7438(1) Å, b=5.7696(1) Å and c=21.0067(2) Å. The diffraction pattern of the antiferromagnetic phase with a propagation vector k=[0,0,0] point towards ferromagnetically ordered moments in Ce layers stacked along [001], the individual layers are coupled antiferromagnetically with a +− −+type sequence. The alignment of moments within the Ce layers cannot be determined reliably from the experimental data so that two different structure models are discussed. The proposed metamagnetic transition was confirmed by diffraction experiments applying an external magnetic field at T<T_N. In the interval 4 K≤T≤6 K, a relatively small field of μ₀H≈0.3 T suffices to fully suppress the antiferromagnetic ordering. The effect is completely reversible yet subject to hysteresis: After switching off the external field at any T<T_N the magnetic reflections gain their original intensity within several 10 min indicating the restoring of the antiferromagnetic phase.     

The structural and magnetic properties of Ni2Mn1−xBxGa Heusler alloys

The influence of the substitution of manganese by boron on the crystal structure and magnetic properties of Ni₂Mn_1−xB_xGa Heusler alloys with 0?x?0.5 has been investigated using X-ray diffraction, thermal expansion, resistivity, and magnetization measurements. The samples with concentrations x<0.25 were found to be of single phase and belonged to the cubic L2₁ crystal structure at room temperature. Crystal cell parameters of the alloys decreased from 5.830 to 5.825 Å with increasing boron concentration (x) from 0 to 0.25. The alloys were ferromagnetically ordered at 5 K and the saturation magnetization decreased with increasing boron concentration. The ferromagnetic ordering and structural transition temperatures for 0?x?0.3 have been observed and the phase (x−T) diagram of the Ni₂Mn_1−xB_xGa system was constructed. The phase (x−T) diagram indicates that the ground state of Ni₂Mn_1−xB_xGa alloys belongs to ferromagnetic martensitic, premartensitic, and austenitic phases in x?0.12, 0.12<x?0.18, and 0.18<x?0.3, respectively. The relative influence of cell parameters and electron concentrations on the phase diagram is discussed.     

Effects of indium doping on the superconducting properties of YBa2Cu3Oy sintered compounds and thin films

We investigated the effects of indium doping on the superconducting properties of YBCO sintered samples and thin films. In₂O₃-doped YBCO and YBa₂Cu_3−xIn_xO_y sintered samples showed a gradual decrease in the critical temperature (T_c) with increasing indium content; however, a T_c value above 80 K was maintained even up to 30 vol.% addition and x = 0.4, respectively. Ba₃Cu₃In₄O₁₂ was detected by X-ray diffractometry and energy-dispersive X-ray spectroscopy as a reaction product for both sintered samples. The normalized J_c under a magnetic field of 0.1 T showed a maximum at x = 0.3. Indium-doped YBCO films prepared by pulsed laser deposition showed a similar dependence of T_c on indium content as the sintered samples.     

Magnetic phase transitions in Nd7Rh3 single crystal

Magnetic phase transitions in rare earth intermetallic compound Nd₇Rh₃ have been investigated using a single crystal. Measurement results of magnetization, magnetic susceptibility, specific heat, and electrical resistivity reveal that Nd₇Rh₃ has two magnetic phase transitions at T_N=34 K, T_t2=9.1 K and a change of the magnetic feature at T_t1=6.8 K in the absence of an external magnetic field. Antiferromagnetic orderings exist in all the three magnetic states; a large magnetic anisotropy between the c-axis and the c-plane is observed. In the magnetic phase below T_t2, an irreversible field-induced magnetic phase transition takes place in the c-plane; after removing external magnetic field, a coexistence state of ferro- and antiferromagnetic ordering or a ferrimagnetic state having a remanent magnetization M_R is stabilized. The M_R decays to a certain value for several hours after the first process; a magnetic field cooling effect was also observed in the c-plane below T_t2. In the antiferromagentic state above T_t2, the irreversibility disappears and an ordinary antiferromagnetic state takes place. As the origin of this phenomenon, a kind of martensitic structural transition that is observed in Gd₅Ge₄ can be considered.     

Microstructures and multiferroic properties of textured Bi0.8La0.2FeO3 thin films

La-substituted BiFeO₃, Bi_0.8La_0.2FeO₃, thin films were fabricated on Pt/Ti/SiO₂/Si substrates by pulsed laser deposition. X-ray diffraction and high-resolution transmission electron microscope were used to analyze the structures of the films. The results show the films fabricated under optimized growth condition are (0 1 2) textured. X-ray photoemission spectroscopy results indicate that the oxidation state of Fe ion is Fe³⁺ in the films without detectable Fe²⁺. The films show low leakage current and excellent dielectric characters. Multiferroic properties with a remnant ferroelectric polarization of 5.2 μC/cm² and a remanent magnetization of 0.02 μ_B/Fe were established. These results have some implications for further research.     

Synthesis, structural and magnetic properties of the nanocomposite Fe63B23Nd7Y3Nb3Cr1 magnets

The Fe₆₃B₂₃Nd₇Y₃Nb₃Cr₁ nanocomposite magnets in the form of sheets have been prepared by copper mold casting technique. The phase evolution, crystal structure, microstructural and magnetic properties have been investigated in the as-cast and annealed states. The as-cast sheets show magnetically soft behaviors which become magnetically hard by thermal annealing. The optimal annealed microstructure was composed of nanosize soft magnetic α-Fe (19-29 nm) and hard magnetic Nd₂Fe₁₄B (45-55 nm) grains. The best hard magnetic properties such as intrinsic coercivity, _jH_c of 1119 kA/m, remanence, B_r of 0.44 T, magnetic induction to saturation magnetization ratio, M_r/M_s=0.61 and maximum energy product, (BH)_max of 55 kJ/m³ was obtained after annealing at 680 °C for 15 min. The annealing treatment above 680 °C results in non-ideal phase grains growth, which degrade the magnetic properties.     

Low temperature synthesis and superconducting properties of polycrystalline T′-(La,Sm)2CuO4

La_2−xSm_xCuO_4+δ with the Nd₂CuO₄ structure was synthesized by precipitation from fused alkaline hydroxide, CsOH, at 400 °C. The as-sintered polycrystalline samples showed no diamagnetic signal, but after post-annealing in vacuum of ≈10⁻⁸ atm at 650–700 °C, the samples with x = 0.1 and 0.3 exhibited superconductivity at T_c on = 25 K. The volume fraction of the superconducting phase estimated from the slope of the Zero-Field-Cooled magnetization data was over 30% for x = 0.3, which confirmed that the La_1.7Sm_0.3CuO_4+δ is a bulk superconductor.     

Gigantic uniaxial pressure effect in single crystals of iron-based superconductors

In order to elucidate the anisotropic pressure effect on superconductivity in an iron-based superconductor, magnetization measurements have been performed in Ba(Fe_0.92Co_0.08)₂As₂ single crystals under uniaxial pressures applied along the c-axis. Gigantic T_c suppression, dT_c/dP_//c = −15 K/GPa, was observed when the anisotropic deformation with the a-expansion and c-compression was induced by the c-pressure, which should be compared with dT_c/dP < +1 K/GPa in the isotropic pressure case. This suggests that the a-axis (c-axis) compression has a positive (negative) contribution to T_c.     

Elastic and electronic properties of YNi2B2C under pressure from first principles

The elastic and electronic structure properties of YNi₂B₂C under pressure are investigated by performing the generalized gradient approximation (GGA) and local density approximation (LDA) correction scheme in the frame of density functional theory (DFT). The pressure dependences of the normalized lattice parameters a/a₀ and c/c₀, the ratio c/a, and the normalized primitive volume V/V₀ of YNi₂B₂C are also obtained. The lattice constants and bulk modulus obtained are in agreement with the available experimental and other theoretical data. We have also studied the pressure dependences of elastic properties. It is found that, as pressure increases, the elastic constants C₁₁, C₃₃, C₆₆, C₁₂, and C₁₃ increase, the variation of elastic constant C₄₄ is not obvious. Moreover, our compressional and shear wave velocities V_L=6.99 km/s and V_S=3.67 km/s as well as the Debye temperature Θ=549.7 K at 0 GPa compare favorably with the available experimental data. The pressure dependences of band structures, energy gap and density of states are also investigated.     

Second harmonic generation in transparent microcrystalline α-CdGa2S4-containing chalcogenide glass ceramics

Transparent glass ceramics were prepared by heat treating of the as-prepared 80GeS₂ · 10Ga₂S₃ · 10CdI₂ glass at 370 °C (T_g + 15 °C) for 72 h (labeled as GGCd10-370). The existence of α-CdGa₂S₄ crystal in GGCd10-370 glass ceramics has been testified by XRD and Raman spectroscopy. Using the typical Maker fringe technique, SHG was observed in the original transparent GGCd10-370 glass ceramics successfully, which is mainly ascribed to the α-CdGa₂S₄ nonlinear optical microcrystal. And the SH intensity is almost 0.8 times larger than that of the standard quartz reference. It can be also deduced that the thickness of crystalline layer is a little larger than the coherent length, l_c ≈ 2.7 μm.     

High temperature ferromagnetism of the vacuum-annealed (In1−xFex)2O3 powders

(In_1−xFe_x)₂O₃ (x = 0.02, 0.05, 0.2) powders were prepared by a solid state reaction method and a vacuum annealing process. A systematic study was done on the structural and magnetic properties of (In_1−xFe_x)₂O₃ powders as a function of Fe concentration and annealing temperature. The X-ray diffraction and high-resolution transmission electron microscopy results confirmed that there were not any Fe or Fe oxide secondary phases in vacuum-annealed (In_1−xFe_x)₂O₃ samples and the Fe element was incorporated into the indium oxide lattice by substituting the position of indium atoms. The X-ray photoelectron spectroscopy revealed that both Fe²⁺ and Fe³⁺ ions existed in the samples. Magnetic measurements indicated that all samples were ferromagnetic with the magnetic moment of 0.49-1.73 μ_B/Fe and the Curie temperature around 783 K. The appearance of ferromagnetism was attributed to the ferromagnetic coupling of Fe²⁺ and Fe³⁺ ions via an electron trapped in a bridging oxygen vacancy.     

Synthesis, structure and magnetic properties of the new double perovskite Ca2CrSbO6

The title double perovskite has been synthesized by solid-state reaction in air. The crystal structure has been studied from powder X-ray diffraction data. Rietveld fits to the pattern show that this compound has a monoclinic symmetry [a=5.4932(3) Å, b=5.4081(3) Å, c=7.6901(5) Å, β=90.0022(1)°, at 300 K] defined in the space group P2₁/n, where the Cr and Sb cations are almost completely ordered in the B-sublattice of the perovskite structure. Magnetic susceptibility and magnetization measurements show that this compound behaves as a Curie-Weiss paramagnet at high temperatures with μ_eff=3.53(1) μ_B and θ_P=8 K, and exhibits a robust ferromagnetic component below the ordering temperature of T_C=13 K, with a saturation magnetization of 2.36 μ_B/f.u. at 5 K. To our knowledge, this is the first example of a ferromagnetic double perovskite containing a non-magnetic element, such as Sb, occupying one half of the B positions of the perovskite structure.     

Magnetic ordering in CeMnCuSi2

Temperature and field-dependent magnetization measurements on polycrystalline CeMnCuSi₂ reveal that the Mn moments in this compound exhibit ordering with a ferromagnetic (FM) component ordered instead of the previously reported purely antiferromagnetic (AFM) ordering. The FM ordering temperature, T_c, is about 120 K and almost unchanged with external fields up to 50 kOe. Furthermore, an AFM component (such as in a canted spin structure) is observed to be present in this phase, and its orientation is modified rapidly by the external magnetic field. The Ce L₃-edge X-ray absorption result shows that the Ce ions in this compound are nearly trivalent, very similar to that in the heavy fermion system CeCu₂Si₂. Large thermomagnetic irreversibility is observed between the zero-field-cooled (ZFC) and field-cooled (FC) M(T) curves below T_c indicating strong magnetocrystalline anisotropy in the ordered phase. At 5 K, a metamagnetic-type transition is observed to occur at a critical field of about 8 kOe, and this critical field decreases with increasing temperature. The FM ordering of the Mn moments in CeMnCuSi₂ is consistent with the value of the intralayer Mn–Mn distance R^a_Mn–Mn=2.890 Å, which is greater than the critical value 2.865 Å for FM ordering. Finally, a magnetic phase diagram is constructed for CeMnCuSi₂.     

Synthesis,crystal structure and magnetic properties of Yb8Ag18.5Al47.5, Yb2Pd2Cd and Yb1.35Pd2Cd0.65

We report the synthesis of three new Yb-based compounds, Yb₈Ag_18.5Al_47.5 (Yb₈Cu₁₇Al₄₉-type, tetragonal tI74–I4/mmm), Yb₂Pd₂Cd (Mo₂B₂Fe-type, tetragonal tP10-P4/mbm) and Yb_1.35Pd₂Cd_0.65 (MnCu₂Al-type, cubic cF16–Fm3¯m). The crystal symmetry of these compounds has been determined and the complete structural characterisation carried out by single crystal and powder diffraction techniques. Two symmetry in-equivalent sites are available for the Yb ions in Yb₈Ag_18.5Al_47.5 and Yb_1.35Pd₂Cd_0.65. The 4f levels of the Yb ions are appreciably hybridised in Yb₈Ag_18.5Al_47.5 and to a lesser extent in Yb₂Pd₂Cd as inferred from the magnetisation and heat capacity data. Signatures of heavy fermion behaviour are observed in the heat capacity data of Yb₂Pd₂Cd in which the heat capacity, C/T, increases at low temperatures attaining a value of ≈600 mJ/mol K² at 1.8 K. The electrical resistivity of Yb₂Pd₂Cd follows a linear variation with temperature, T, between 1.4 and 5 K, thus indicating a possible non-Fermi liquid behaviour. In contrast, Yb ions are trivalent in Yb_1.35Pd₂Cd_0.65 and order magnetically near 1.4 K.