接枝共聚法制备二氧化钛/聚（苯乙烯-二乙烯基苯）复合微球

本文以KH560、苯乙烯、马来酸酐为连接组分,将二氧化钛接枝到聚（苯乙烯-二乙烯基苯）微球的表面,成功制备了无孔和多孔纳米复合微球。研究了硅烷偶联剂（KH560）和苯乙烯对二氧化钛在无孔微球表面的分散性和接枝数量以及支撑微球的多孔性质对接枝到微球内部的二氧化钛数量的影响。结果表明,KH560和苯乙烯能够提高二氧化钛在微球表面的分散性和稳定性,使二氧化钛以30-80nm的粒径接枝在微球表面。苯乙烯又能使二氧化钛在无孔微球表面的接枝数量从10.4%增大到20.4%。平均孔径为136nm的多孔微球为支撑微球得到的复合粒子中二氧化钛最高接枝量可达26%,明显高于无孔微球和平均孔径为31nm的多孔微球。     

GO/TiO2-g-C3N4纳米复合材料的制备及可见光催化性能

以水热法制备的20% g-C₃N₄/TiO₂（20%为质量分数）为基,将其与不同质量分数的氧化石墨烯（GO）复合制备出可见光催化性能优良的GO/TiO₂-g-C₃N₄三元复合材料。利用X射线衍射（XRD）、扫描电子显微镜（SEM）、X射线光电子能谱（XPS）、紫外-可见漫反射光谱（UV-Vis DRS）、光致荧光光谱（PL）、瞬态光电流响应等分析测试手段对样品的结构、形貌和光电性能进行表征。研究了不同质量分数GO的加入对GO/TiO₂-g-C₃N₄在可见光下降解亚甲基蓝（MB）溶液的影响。结果表明： g-C₃N₄/TiO₂与GO复合后,锐钛矿相TiO₂颗粒形成小团簇附着在g-C₃N₄和GO片层表面,且当GO含量为15%时,TiO₂形成的团簇最小,对可见光的吸收最多且光生电子-空穴对的复合率最低。可见光照射下,15% GO/TiO₂-g-C₃N₄复合材料对MB的降解率在3 h内可达98.4%,且其降解速率常数（0.022 4 min^-1）分别是纯TiO₂（0.001 5 min^-1）和g-C₃N₄/TiO₂（0.002 5 min^-1）的15倍和9倍。     

Visible Light Photocatalytic Activity of Pt/N‐TiO2 towards Enhanced H2 Production from Water Splitting

Present work mainly focuses on experimental investigation to improvement of hydrogen production by water photoelectrolysis. An experimental facility was designed and constructed for visible light photocatalysis. A series of N‐TiO₂ photocatalysts impregnated with platinum on the surface of N‐TiO₂ were prepared. Hydrogen production upon irradiating aqueous Pt/N‐TiO₂ suspension with visible light was investigated. The shift in excitation wavelength of TiO₂ was 380 nm improved the yield of hydrogen production by N‐TiO₂ and Pt/N‐TiO₂. We used a 400 W mercury arc lamp combined with a 400 nm cutoff filter eliminating all the wavelengths under 400 nm. Pt/N‐TiO₂ material was characterized with TPR, reflective UV/Visible spectroscopy and TEM. The best hydrogen production rate obtained for this setup for N/Ti = 10, 0.05 wt% Pt/N‐TiO₂, through water splitting was about 772 μmolh^?1g^?1.     

A Facile method to Prepare Monodispersed CdS/SiO2 Composite Microspheres and Investigation on Their Photocatalytic Properties

This article presents a facile method to prepare CdS/SiO₂ composite microspheres and their good catalytic properties. In our method, monodispersed SiO₂ particles bearing amino groups (–NH₂) were synthesized at first and then used as carriers to load nanosized CdS particles to form CdS/SiO₂ composite microspheres. With the addition of CdAc₂ solution to the SiO₂ dispersion, Cd²⁺ was attracted to the surfaces of the SiO₂ particles through coordination interaction, and then thioacetamide was added to the dispersion. By heating, S^2? released and reacted with the Cd²⁺, CdS/SiO₂ composite microspheres were obtained accordingly. The photocatalytic properties of the as‐prepared composite microspheres were investigated as well. It was found that the composite microspheres have excellent photocatalytic activities for the degradation of dyes comparing with the commercial P‐25 TiO₂ catalysts. After using and recycling for three times, the photocatalytic performance still remained very well.     

Visible‐light‐driven self‐cleaning SERS substrate of silver nanoparticles and graphene oxide decorated nitrogen‐doped titania nanotube array

Graphene oxide (GO) and silver nanoparticles (Ag NPs) sequentially decorated nitrogen‐doped titania nanotube array (N‐TiO₂ NTA) had been designed as visible‐light‐driven self‐cleaning surface‐enhanced Raman scattering (SERS) substrate for a recyclable SERS detection application. N‐TiO₂ NTA was fabricated by anodic oxidation and then doping nitrogen treatment in ammonia atmosphere, acting as a visible‐light‐driven photocatalyst and supporting substrate. Ag/GO/N‐TiO₂ NTA was prepared by decorating GO monolayer through an impregnation process and then depositing Ag NPs through a polyol process on the surface of N‐TiO₂ NTA, acting as the collection of organic molecule and Raman enhancement. The SERS activity of Ag/GO/N‐TiO₂ NTA was evaluated using methyl blue as an organic probe molecule, revealing the analytical enhancement factor of 4.54 × 10⁴. Ag/GO/N‐TiO₂ NTA was applied as active SERS substrate to determine a low‐affinity organic pollutant of bisphenol A, revealing the detection limit of as low as 5 × 10^?7 m . Ag/GO/N‐TiO₂ NTA could also achieve self‐cleaning function for a recycling utilization through visible‐light‐driven photocatalytic degradation of the adsorbed organic molecules. Ag/GO/N‐TiO₂ NTA has been successfully reused for five times without an obvious decay in accuracy and sensitivity for organic molecule detection. The unique properties of this SERS substrate enable it to have a promising application for the sensitive and recyclable SERS detection of low‐affinity organic molecules. Copyright © 2016 John Wiley & Sons, Ltd.     

Facile Preparation and Lithium Storage Properties of TiO2@Graphene Composite Electrodes with Low Carbon Content

Over the past decade, TiO₂/graphene composites as electrodes for lithium ion batteries have attracted a great deal of attention for reasons of safety and environmental friendliness. However, most of the TiO₂/graphene electrodes have large graphene content (9–40 %), which is bound to increase the cost of the battery. Logically, reducing the amount of graphene is a necessary part to achieve a green battery. The synthesis of TiO₂ nanosheets under solvothermal conditions without additives is now demonstrated. Through mechanical mixing TiO₂ nanosheets with different amount of reduced graphene (rGO), a series of TiO₂@graphene composites was prepared with low graphene content (rGO content 1, 2, 3, and 5 wt %). When these composites were evaluated as anodes for lithium ion batteries, it was found that TiO₂+3 wt % rGO manifested excellent cycling stability and a high specific capacity (243.7 mAh g^?1 at 1 C; 1 C=167.5 mA g^?1), and demonstrated superior high‐rate discharge/charge capability at 20 C.     

Study on the fabrication and photovoltaic property of TiO2 mesoporous microspheres

Titanium dioxide mesoporous microspheres with high surface area was successfully prepared by a facile one-step hydrothermal approach using polyethylene glycol (PEG, MW 200) as the soft template. Study shows that ∼15 nm TiO₂ nanoparticles was assembled into ∼1.1 μm mesoporous microspheres. The Brunauer-Emmett-Teller surface area of TiO₂ microsphere is up to 137 m²/g. TiO₂ mesoporous microspheres were fabricated onto the surface of fluorine-doped tin oxide glass and used as the photoanode of dye-sensitized solar cells, which exhibits an open circuit photovoltage of 0.80 V and an overall conversion efficiency of 6.6%. Owing to the enhanced dye loading and light-harvesting efficiency, a 26% improvement in the overall conversion efficiency was achieved when compared with the commercial Degussa P₂₅ nanoparticles.     

简易模板剂法制备多级介孔TiO2微球及其在染料敏化太阳能电池中的性能

采用模板剂法一步合成分级结构的介孔TiO₂微球, 考察了烷基胺类模板剂中烷基链长度对介孔TiO₂微球合成及性能影响. 将其应用于染料敏化太阳能电池的光阳极半导体薄膜中, 得到了9.5%-10.1%的高能量转换效率. X射线衍射(XRD)、物理吸附仪(BET)、扫描电镜(SEM)等的分析结果表明: 分级结构介孔TiO₂微球的晶相为纯锐钛矿型; 介孔TiO₂微球表面粗糙, 的纳米粒子堆积形成, 使微球具有介孔性质和较适宜的比表面积. 介孔TiO₂微球堆积形成了利于物质扩散的通道并具有良好的光散射效果; 同时微球介孔粗糙表面保证了染料的大量吸附, 从而提高了电池的光电流. 通过电化学阻抗分析结果验证了分等级结构介孔TiO₂微球光阳极有利于电解液的传输和物质扩散的优异性能.     

Porous TiO2 Nanotubes with Spatially Separated Platinum and CoOx Cocatalysts Produced by Atomic Layer Deposition for Photocatalytic Hydrogen Production

Efficient separation of photogenerated electrons and holes, and associated surface reactions, is a crucial aspect of efficient semiconductor photocatalytic systems employed for photocatalytic hydrogen production. A new CoO_x/TiO₂/Pt photocatalyst produced by template‐assisted atomic layer deposition is reported for photocatalytic hydrogen production on Pt and CoO_x dual cocatalysts. Pt nanoclusters acting as electron collectors and active sites for the reduction reaction are deposited on the inner surface of porous TiO₂ nanotubes, while CoO_x nanoclusters acting as hole collectors and active sites for oxidation reaction are deposited on the outer surface of porous TiO₂ nanotubes. A CoO_x/TiO₂/Pt photocatalyst, comprising ultra‐low concentrations of noble Pt (0.046 wt %) and CoO_x (0.019 wt %) deposited simultaneously with one atomic layer deposition cycle, achieves remarkably high photocatalytic efficiency (275.9 μmol h⁻¹), which is nearly five times as high as that of pristine TiO₂ nanotubes (56.5 μmol h⁻¹). The highly dispersed Pt and CoO_x nanoclusters, porous structure of TiO₂ nanotubes with large specific surface area, and the synergetic effect of the spatially separated Pt and CoO_x dual cocatalysts contribute to the excellent photocatalytic activity.     

Coaxial Electrospinning Method for the Preparation of TiO2@CdS/PVA Composite Nanofiber Mat and Investigation on its Photodegradation Catalysis

TiO₂/PVA composite nanofiber mat was prepared via an electrospinning technology. SH‐TiO₂‐SiO₂ hybrid particles and PVA solution were injected through a coaxial syringe, yielding a composite nanofiber mat. The as‐prepared SH‐TiO₂‐SiO₂/PVA composite nanofiber mat was immersed in Cd²⁺ cation solution and S^2? anion solution in turn. Thus, yellow TiO₂@CdS/PVA composite nanofiber mats were prepared. By adjusting the number of times a mat was immersed in the Cd²⁺ and S^2? solutions, different amounts of CdS particles attaching to the mats were obtained. Both SH‐TiO₂‐SiO₂/PVA and TiO₂@CdS/PVA composite nanofiber mats were employed to catalyze the photodegradation of a model dye, methylene blue. The photodegradation performance could be greatly enhanced by the introduction of CdS particles anchoring onto TiO₂ particles. The photodegradation efficiency reached 99.2% within 180 min. Also, the nanofiber mat could be recycled and reused at least 10 times. The photodegradation efficiency of TiO₂@CdS/PVA composite nanofiber mats remained 68.8% for 10 cycles.     

Facile synthesis of polyaniline/TiO2/graphene oxide composite for high performance supercapacitors

The polyaniline/TiO₂/graphene oxide (PANI/TiO₂/GO) composite, as a novel supercapacitor material, is synthesized by in situ hydrolyzation of tetrabutyl titanate and polymerization of aniline monomer in the presence of graphene oxide. The morphology, composition and structure of the composites as-obtained are characterized by SEM, TEM, XRD and TGA. The electrochemical property and impedance of the composites are studied by cyclic voltammetry and Nyquist plot, respectively. The results show that the introduction of the GO and TiO₂ enhanced the electrode conductivity and stability, and then improved the supercapacitive behavior of PANI/TiO₂/GO composite. Significantly, the electrochemical measurement results show that the PANI/TiO₂/GO composite has a high specific capacitance (1020 F g⁻¹ at 2 mV s⁻¹, 430 F g⁻¹ at 1 A g⁻¹) and long cycle life (over 1000 times).     

Preparation and characterization of SiO2/TiO2 composite microspheres with microporous SiO2 core/mesoporous TiO2 shell

SiO₂/TiO₂ composite microspheres with microporous SiO₂ core/mesoporous TiO₂ shell structures were prepared by hydrolysis of titanium tetrabutylorthotitanate (TTBT) in the presence of microporous silica microspheres using hydroxypropyl cellulose (HPC) as a surface esterification agent and porous template, and then dried and calcined at different temperatures. The as-prepared products were characterized with differential thermal analysis and thermogravimetric (DTA/TG), scanning electron microscopy (SEM), X-ray diffraction (XRD), nitrogen adsorption. The results showed that composite particles were about 1.8 μm in diameter, and had a spherical morphology and a narrow size distribution. Uniform mesoporous titania coatings on the surfaces of microporous silica microspheres could be obtained by adjusting the HPC concentration to an optimal concentration of about 3.2 mmol L⁻¹. The anatase and rutile phase in the SiO₂/TiO₂ composite microspheres began to form at 700 and 900 °C, respectively. At 700 °C, the specific surface area and pore volume of the SiO₂/TiO₂ composite microspheres were 552 and 0.652 mL g⁻¹, respectively. However, at 900 °C, the specific surface area and pore volume significantly decreased due to the phase transformation from anatase to rutile.     

Doping of TiO2–GO and TiO2–rGO with Noble Metals: Synthesis,Characterization and Photocatalytic Performance for Azo Dye Discoloration

The nanocomposites of titania coupled with graphene oxide (GO) and reduced graphene oxide (rGO), respectively, were prepared by homogeneous hydrolysis with urea. Graphene was obtained by effect of high‐intensity cavitation field on natural graphite in the presence of strong aprotic solvents in pressurized ultrasonic reactor. The morphology of TiO₂–GO and TiO₂–rGO composites was assessed by scanning electron microscopy and atomic force microscopy. The nitrogen adsorption–desorption was used for determination of surface area (BET) and porosity. Raman and IR spectroscopy were used for qualitative analysis and diffuse reflectance spectroscopy was employed to estimate band‐gap energies. Further enhancement of the photocatalytic activity was attained by codoping of composites with noble metals—Au, Pd and Pt. The photocatalytic activity of TiO₂–GO and TiO₂–rGO were assessed by photocatalytic decomposition of Orange II dye in an aqueous slurry under UV and visible light irradiation. The photocatalytic activity of noble metals codoped samples was determined with decomposition of Reactive Black 5 azo dye.     

Porous Molybdenum‐Based Hybrid Catalysts for Highly Efficient Hydrogen Evolution

We have synthesized a porous Mo‐based composite obtained from a polyoxometalate‐based metal–organic framework and graphene oxide (POMOFs/GO) using a simple one‐pot method. The MoO₂@PC‐RGO hybrid material derived from the POMOFs/GO composite is prepared at a relatively low carbonization temperature, which presents a superior activity for the hydrogen‐evolution reaction (HER) in acidic media owing to the synergistic effects among highly dispersive MoO₂ particles, phosphorus‐doped porous carbon, and RGO substrates. MoO₂@PC‐RGO exhibits a very positive onset potential close to that of 20 % Pt/C, low Tafel slope of 41 mV dec^?1, high exchange current density of 4.8×10^?4 A cm^?2, and remarkable long‐term cycle stability. It is one of the best high‐performance catalysts among the reported nonprecious metal catalysts for HER to date.     

Synthesis of CuAPTPP-TDI-TiO2 Conjugated Microspheres and its Photocatalytic Activity (cited: 1)

The metal complex 5-(4-aminophenyl)-10,15,20-triphenylporphyrin copper (CuAPTPP) was covalently linked on the surface of TiO₂ microspheres by using toluene disocyanate (TDI) as a bridging bond unit. The hydroxyl group (-OH) of TiO₂ microspheres surface and the amino group (-NH₂) of CuAPTPP reacted respectively with the active -NCO groups of TDI to form a surface conjugated microsphere CuAPTPP-TDI-TiO₂ that was confirmed by FT-IR spectra. The CuAPTPP-TDI-TiO₂ microspheres were characterized with UV-visible, elemental analysis, XRD, SEM, and UV-Vis diffuse reflectance spectra. The effect of amounts of linked TDI on the performance of photocatalytic microspheres was discussed, and the optimal molar ratio of TDI:TiO₂ was established. The photocatalytic activity of CuAPTPP-TDI-TiO₂ was evaluated using the photocatalytic degradation of methylene blue (MB) under visible-light irradiation. The results showed that, TDI, as a bond unit, was used to form a steady chemical brigdging bond linking CuAPTPP and the surface of TiO₂ microspheres, and the prepared catalyst exhibited higher photocatalytic activity under visible-light irradiation for MB degradation. The degradation rate of 20 mg/L MB could reach 98.7% under Xe-lamp (150 W) irradiation in 120 min. The degradation of MB followed the first-order reaction model under visible light irradiation, and the rate constant of 5.1×10^-2 min^-1 and the half-life of 11.3 min were achieved. And the new photocatalyst can be recycled for 4 times, remaining 90.0% MB degradation rate.     

Preparation of magnetic Fe3O4/TiO2/Ag composite microspheres with enhanced photocatalytic activity

The novel three-component Fe₃O₄/TiO₂/Ag composite mircospheres were prepared via a facile chemical deposition route. The Fe₃O₄/TiO₂ mircospheres were first prepared by the solvothermal method, and then Ag nanoparticles were anchored onto the out-layer of TiO₂ by the tyrosine-reduced method. The as-prepared magnetic Fe₃O₄/TiO₂/Ag composite mircospheres were applied as photocatalysis for the photocatalytic degradation of methylene blue. The results indicate that the photocatalytic activity of Fe₃O₄/TiO₂/Ag composite microspheres is superior to that of Fe₃O₄/TiO₂ due to the dual effects of the enhanced light absorption and reduction of photoelectron–hole pair recombination in TiO₂ with the introduction of Ag NPs. Moreover, these magnetic Fe₃O₄/TiO₂/Ag composite microspheres can be completely removed from the dispersion with the help of magnetic separation and reused with little or no loss of catalytic activity.     

Synthesis of Bi-doped TiO2 Nanotubes and Enhanced Photocatalytic Activity for Hydrogen Evolution from Glycerol Solution

Bi‐doped TiO₂ nanotubes with variable Bi/Ti ratios were synthesized by hydrothermal treatment in 10 mol·L^?1 NaOH (aq.) through using Bi‐doped TiO₂ particles derived from conventional sol‐gel method as starting materials. The effects of Bi content on the morphology, textural properties, photo absorption and photocatalytic activity of TiO₂ nanotubes were investigated. The scanning electron microscopy (SEM), transmission electron microscopy (TEM), X‐ray diffraction (XRD) and X‐ray photoelectron spectroscopy (XPS) observations of the obtained samples revealed the formation of titanate nanotube structure doped with Bi, which exists as a higher oxidation state than Bi³⁺. Bi‐doping TiO₂ nanotubes exhibited an extension of light absorption into the visible region and improved photocatalytic activities for hydrogen production from a glycerol/water mixed solution as compared with pure TiO₂ nanotubes. There was an optimal Bi‐doped content for the photocatalytic hydrogen production, and high content of Bi would retard the phase transition of titanate to anatase and result in morphology change from nanotube to nanobelt, which in turn decreases the photocatlytic activity for hydrogen evolution.     

Titanium dioxide/graphene oxide composite and its application as an anode material in non-flammable electrolyte based on ionic liquid and sulfolane

A composite of aminosilane-grafted TiO₂ (TA) and graphene oxide (GO) was prepared via a hydrothermal process. The TiO₂/graphene oxide-based (TA/GO) anode was investigated in an ionic liquid electrolyte (0.7 M lithium bis(trifluoromethanesulfonyl)imide (LiNTf₂)) in ionic liquid (N-methyl-N-propylpyrrolidinium bis(trifluoromethanesulfonyl)imide (MPPyrNTf₂)) at room temperature and in sulfolane (1 M lithium hexafluorophosphate (LiPF₆) in tetramethylene sulfolane (TMS)). Scanning and transmission electron microscopy (SEM and TEM) observations of the anode materials suggested that the electrochemical intercalation/deintercalation process in the ionic liquid electrolyte with vinylene carbonate (VC) leads to small changes on the surface of TA/GO particles. The addition of VC to the electrolyte (0.7 M LiNTf₂ in MPPyrNTf₂ + 10 wt.% VC) considerably increases the anode capacity. Electrodes were tested at different current regimes in the range 5–50 mA g^?1. The capacity of the anode, working at a low current regime of 5 mA g^?1, was ca. 245 mA g^?1, while a current of 50 mA g^?1 resulted in a capacity of 170 mA g^?1. The decrease in anode capacity with increasing current rate was interpreted as the result of kinetic limits of electrode operation. A much lower capacity was observed for the system TA/GO│1 M LiPF₆ in TMS + 10 wt.% VC│Li.     

Porous Si-Cu3Si-Cu Microsphere@C Core–Shell Composites with Enhanced Electrochemical Lithium Storage

Low-cost Si-based anode materials with excellent electrochemical lithium storage present attractive prospects for lithium-ion batteries (LIBs). Herein, porous Si-Cu₃Si-Cu microsphere@C composites are designed and prepared by means of an etching/electroless deposition and subsequent carbon coating. The composites show a core–shell structure, with a porous Si/Cu microsphere core surrounded by the N-doped carbon shell. The Cu and Cu₃Si nanoparticles are embedded inside porous silicon microspheres, forming the porous Si/Cu microsphere core. The microstructure and lithium storage performance of porous Si-Cu₃Si-Cu microsphere@C composites can be effectively tuned by changing electroless deposition time. The Si-Cu₃Si-Cu microsphere@C composite prepared with 12 min electroless deposition delivers a reversible capacity of 627 mAh g⁻¹ after 200 cycles at 2 A g⁻¹, showing an enhanced lithium storage ability. The superior lithium storage performance of the Si-Cu₃Si-Cu microsphere@C composite can be ascribed to the improved electronic conductivity, enhanced mechanical stability, and better buffering against the large volume change in the repeated lithiation/delithiation processes.     

Template‐free Fabrication of Hierarchical Macro‐/mesoporous N‐doped TiO2/graphene Oxide Composites with Enhanced Visible‐light Photocatalytic Activity

Hierarchical macro‐/mesoporous N‐doped TiO₂/graphene oxide (N‐TiO₂/GO) composites were prepared without using templates by the simple dropwise addition mixed solution of tetrabutyl titanate and ethanol containg graphene oxide (GO) to the ammonia solution, and then calcined at 350 °C. The as‐prepared samples were characterized by scanning electron microscopy (SEM), Brunauer‐Emmett‐Teller (BET) surface area, X‐ray diffraction (XRD), Raman spectroscopy, X‐ray photoelectron spectroscopy (XPS), and UV‐Vis absorption spectroscopy. The photocatalytic activity was evaluated by the photocatalytic degradation of methyl orange in an aqueous solution under visible‐light irradiation. The results show that N‐TiO₂/GO composites exhibited enhanced photocatalytic activity. GO content exhibited an obvious influence on photocatalytic performance, and the optimal GO addition content was 1 wt%. The enhanced photocatalytic activity could be attributed to the synergetic effects of three factors including the improved visible light absorption, the hierarchical macro‐mesoporous structure, and the efficient charge separation by GO.